By M. G. Nicholas

The influence of deformation, relative movement and surface cleanliness on the strength of room -temperature "interparticle" bonds between copper surfaces has been studied. No bonding resulted when clean surfaces were merely pressed together, even under pressures of 50,000 psi. Bonding resulted, however, when clean surfaces were simultaneously pressed and moved relative to each other, some bonding occurring no matter how small the pressure or relative movement. Exposure of the clean surfaces to various chemicals inhibited bonding, none at all being produced by small relative movements. The size of the movements which first produce bonding between exposed surfaces depends on the nature of the chemical, being less than 0.002 in. for cleansing reagents and greater than 0.004 in. for lubricants, water and hydrogen sulfide. It is concluded from the experimental data that the prime requirement for bonding is the dispersal of surface films such as oxides and adsorbed contaminants. THE formation of interparticle bonds during the room-temperature compaction of powder metallurgy components greatly increases the ease of handling in subsequent production operations prior to sintering. The strength of unsintered compacts follows the same general trends as their density and hardness, but quantitative data are extremely Scarce. Quantitative correlation of the data on the overall strength of a compact with that of the individual interparticle bonds is virtually impossible due to the extremely complex geometry of powder compacts. Qualitatively, however, the strengths of unsintered compacts can be correlated with variations in parameters known to influence the extent of cold bonding, and hence interparticle bonding, such as surface cleanliness, relative movement, and deformation of the mating surfaces. Kuzmic and seelig4 found that contamination of powder particle surfaces with lubricants reduced the strength of unsintered iron and copper compacts. Interparticle shear has been shown to promote bonding by Train and Hersey7 while Gregory has shown that die rotation is beneficial. Eilender and schwalbe6 concluded that most bonding occurred during the early stages of pressing iron powder compacts when interparticle shear is one of the principal processes occurring. mile there can be little doubt that these and other factors, such as particle size and shape, affect the extent of interparticle bonding produced by compaction, evaluation of the influence of individual factors is not easy. Particle deformation and relative movement, for example, occur simultaneously during compaction, making any precise measurement of their relative influences difficult. Because of these and other difficulties encountered in studying interparticle bonding in actual powder compacts, the approach adopted in this study was to

Jan 1, 1963

By R. C. Ruder, C. E. Birchenall

The method of decrease in surface activity was used to determine the rates of diffusion of Co" into cobalt and into nickel. Since the absorption curves for cobalt radiation were quite complex under the conditions of these experiments, the effects of geometry and surface preparation on the diffusion results were investigated. The cobalt self-diffusion coefficients obey the equation DCoco = e-61100/RT cm2 per sec. For dilute cobalt diffusing in nickel, DConi, == 1.46 e-/R' cm2 er sec. AS part of the general program to measure the self-diffusion and dilute-solution diffusion rates of the iron-group metals, the diffusion coefficients of cobalt into cobalt and nickel have been measured using the radioactive isotope Co"'. Self-diffusion studies in iron have been previously reported by Birchenall and Mehl.' The technique of measurement used was the decrease in surface activity method described by Steigman, Shockley, and Nix.' It has been determined that scattering of the measured beta radiation by the specimen matrix is significantly influenced by the condition of the surface and the counting geometry. Accurate diffusion coefficients can be calculated from the activity data provided that the specimens have plane diffusion surfaces and that the absorption properties of the emitted radiation are determined under geometrical conditions duplicating with external absorbers the absorption and scattering in a thin film at the specimen surface as nearly as possible. The cobalt used in this research was originally in the form of hydrogen reduced rondels 99.9+ pct pure. The nickel had been prepared by the carbonyl process and was found by spectrographic analysis to contain 0.03 pct Fe, 0.04 pct Co and smaller traces of other metallic elements for a balance purity of 99.9+ pet Ni. Both materials were vacuum melted and cast in rectangular ingots. Specimens 7/8x7/8x1/4 in. were machined from these ingots. The specimens were then ground to 4-0 emery paper and annealed in hydrogen for at least a day at 1200°C. Some of the specimens were used in preliminary experimentation after which their diffusion faces were machined to remove the radioactive material from the previous diffusion experiments. After grinding, the specimens were polished using an electrolytic lapping technique described by Mazia." This lapping was continued until at least 0.005 in. was removed from the diffusion surface. The final surfaces were metallographically smooth except for a few fine scratches caused by the glass cloth. A large percentage of the area was undisturbed as determined by microscopic examination. The grain diameters of the diffusion specimens varied from 0.1 to 5 mm. There were no effects due to grain boundary diffusion in the experiments

Jan 1, 1952

By C. Chiou, D. P. Seraphim

The effect of clustering on the superconducting properties of Al-Zn alloys has been studied by the ballistic induction techniques. The superconducting critical temperature, T,, changes when zinc-rich clusters are formed. The change in T, depends on the concentration and may be positive or negative, but always correlates with an effective decrease in the solute concentration of the alloy. Reversion after clustering effectively returns a 5 at. pct Zn alloy to the quenched state. These methods might be use&lly extended to the Al-Mg system, where X-ray data are difficult to obtain. In very dilute Al-Zn alloys, as in other tin,' indium, aluminum,2 or tantalums base solid solutions, there is a decrease in the superconducting critical temperature, Tc, roughly proportional to the temperature independent resistivity, i.e., -0.2°K per pS2cm. With increasing solute concentration, the T, generally reaches a minimum and then increases4 to a value well above that for the pure solvent. The change of T, with solute concentration follows an empirical formulation involving two constants which correlate with the scattering cross section of the impurities. As will be shown below, the Al-Zn alloys more concentrated than 1or2at. pct do not follow the empiricism, probably because they are unstable even when rapidly quenched.5 However, it seems possible to study at least the later stages of solute clustering by precise measurements of the 1', following various thermal treatments. A few experiments on quenched alloys, aged alloys, and tests on reversion are reported here. The heat treatments selected for obtaining the quenched and aged states were mainly deduced from the work of Dash and Fine.6 For the quenched state, specimens were homogenized at 480°C, quenched to -160°C, and immediately transferred and mounted in liquid nitrogen. Measurements on the superconducting properties and residual resistivities were then made at helium temperatures, after which the specimens were aged at room temperature for 3 to 5 hr, i.e., much longer than the time required for clustering to be essentially completed. The superconducting properties and residual resistivities were once again examined. To reach the reverted state of the A1-5at. pct Zn alloy, the aged specimen was heated for 5 min at 200°C and then tested as above.

Jan 1, 1963

By J. J. Kramer, G. W. Wiener, K. Foster

The effects of the primary grain size and sheet thickness on the secondary growth rates of grains with (100) surface planes were studied in 3 pct Si-Fe sheets. This secondary grain growth was carried out under conditions in which the {100} plane had the lowest surface free energy. The value of the surface energy difference, between the (100) plane and the random matrix planes was found to he only about 3 pct of the grain boundary energy, indicating that most of the driving force for secondary growth is supplzed by grain boundary energy. A method for obtaining cube texture in 3 pct Si-Fe sheets by a secondary recrystallization process has been reported.' It has been demonstrated that a difference in surface free energy between the (100) plane and other planes is responsible for this growth, where the (100) plane has the lowest surface energy. A semiquantitative relation has been derived for secondary grain growth in sheets where primary grain growth has proceeded until the grains have grown through the sheet and the average grain diameter in the plane of the sheet is from one to two times the sheet thickness. Then, the linear growth rate, G, for the secondary grains can be given by where M is the grain boundary mobility, is the grain boundary free energy, is the average primary grain radius, A is the average difference in surface free energy between the (100) plane and planes of other orientations, t is the sheet thickness, and C is a term first proposed by zener6 which acts as a negative driving force, the effect of inclusions in holding up grain boundary motion. Since the problem of grain growth being discussed is under conditions where the matrix grain size is at least equal to the sheet thickness, the radius r is, of course, a function of the sheet thickness. The term B/r is the grain boundary driving force normally associated with inclusion inhibited or texture inhibited secondary recrystallization. Here, however, the term is modified to account for the fact that growth occurs in thin sheets. The term is the additional driving force available because of the difference in surface free energy. The purpose of the present work has been to evaluate the driving force terms of the growth equation by studying growth rates of (100) secondary grains as a function of sheet thickness and primary grain size. From these data it has been possible to determine the relative values of grain boundary energy, surface energy difference, and the inclusion term, C. EXPERIMENTAL PROCEDURE A 3 pct Si-Fe alloy was melted and cast under a helium atmosphere using electrolytic iron and a pure commercial grade of silicon as raw materials. The alloy was hot and cold rolled to a thickness of 0.6 mm, and samples approximately 5 in. long by 1 1/4 in. wide were cut from the cold-rolled sheets. Four different primary grain sizes were obtained

Jan 1, 1963

By Jackson M. Langton

Substantial evidence supports the theory that high-angle faults and overthrusts in the Morenci-Metcalf region were initially caused by a Late Precambrian-Early Paleozoic stress field. These faults were reactivated in Late Paleozoic-Early Mesozoic time which completed the structural framework prior to the Laramide Orogeny. Excluding an interruption by diabase dikes and sills, Paleocene-Eocene magmas invaded the pre-existing structures and became progressively more sialic in composition and nearer to the surface with each subsequent injection. The last sialic intrusion was highly explosive, rendering the country rocks more permeable for hypogene and supergene activity. Widespread dilation, instigated by uplift and subsequent magma intrusion, caused extension to the northwest and southeast. A major locus of hypo gene alteration and mineralization appears to be centered around the south and southeast periphery of the youngest granite porphyry stock. A potassic, sulfide-deficient core is telescoped by a pyritic, phyllic zone which in turn is enveloped by widespread propylitic alteration.

Jan 1, 1974

By C. Ernest Birchenall, Robert F. Mehl

APPLICATION of diffusion laws in the customary form to experimental studies in binary metallic solid solutions has shown the diffusion coefficient to vary with concentration for all systems investigated. The factors determining this variation have not been ascertained. However, the question of whether the diffusion coefficient would become a constant, independent of concentration throughout a single phase if the concentration gradient in the diffusion equation were replaced by an activity gradient has been an attractive subject for speculation. Wagner1 derived an expression for the force acting on a diffusing particle in terms of the chemical potential. This was also the approach chosen by Jost2 in his monograph. From a somewhat different point of view, Eyring3 and his co-workers have used activity gradients when dealing with diffusion in concentrated nonideal solutions. The only actual test with experimental data is that given by Darken,4 though this is more qualitative than quantitative. Many others opposed the application in any way of thermodynamic concepts to kinetic phenomena, including diffusion processes. A rigorous examination of this principle requires good data expressing the relationship between activity and concentration for solid solutions for which reliable diffusion work has been done. The literature provides such information only for the interstitial solution of carbon in gamma iron (austenite) and for the substitutional copper-zinc solutions (alpha brass). Activity data for carbon in austenite at 800°C and 1000°C are available from the recent work of Smiths on the equilibrium of hydrogen-methane and carbon monoxide-carbon dioxide mixtures with gamma iron. Combining these with the diffusion studies of Wells and Mehl6 makes possible a quantitative test for this interstitial solid solution. The vapor-pressure determinations for zinc over brass by Hargreaves7 allowed the calculation of activities in this system over a wide range of temperatures and concentrations. Extensive investigation of diffusion in this substitutional solid solution has been carried out by Rhines and Mehl.8 ACTIVITIES IN BRASS9 If the vapor phase of zinc is assumed to behave as an ideal gas, any solid or liquid solutions that are in equilibrium with the same partial pressure of zinc at the same temperature have the same thermodynamic activity of zinc. In order to assign a numerical value to the activity azn, it is necessary to choose some standard reference state to which an activity value of unity is arbitrarily assigned. It is customary to choose the liquid or solid state of the pure material. Then azn is defined numerically by azn = Pza/Pzn° [I]

Jan 1, 1947

By R. J. Wasilewski

THERMAL expansion of rhenium data have been reported by Agte et al.,&apos; and Medoff and cadoff,&apos; respectively, while the linear expansion coefficient was determined by Sims et Al.3 Denoting expansion coefficients parallel and at right angle to c axis by all and Al respectively, their weighted mean should be equal to dilatometric linear coefficient of a random polycrystalline specimen. The values reported for these coefficients are tabulated below: Since these values are in poor agreement, and because of anomalous expansion behavior observed in titanium 4 and chromium, a rede termination of the axial expansion was carried out. A Unicam 19-cm-diam high-temperature camera was used, with unfiltered CuK radiation. Camera calibration was carried out using at Pt wire standarde at temperatures up to 1100oC, the variation between indicated and true temperature being within the experimental error (estimated at <3oC) above 750o C. Rhenium Johnson Matthey spectrographic standard) was vacuum annealed at 1000 oC prior to X-ray diffraction experiments. Lattice parameters were obtained by least-squares solution using the reflec- tions (1232), (1015), (2024), and (3030) for all the patterns, and the additional reflection (2133) for higher temperature (400°C and above) patterns. The relative expansion data obtained are shown in Fig. 1, lengths of the vertical bars indicating the spread in the parameter values obtained by using various combinations of three spacings from the four or five measured. The data calculated from the equation of Ref. 2 are included for comparison purposes. Several specimens were used to obtain the above data, neither of them showing a significant parameter change after completion of the high temperature runs. Some parameter data and the corresponding expansion coefficients between 25 oC and the measurement temperature are tabulated below. The comparison of the present data with those previously reported shows reasonable agreement with the results of Medoff and cadoff2 within the temperature range covered by them (up to 1000 oC). The a values are appreciably higher throughout most of the investigated temperature range. The basal expansion is—in agreement with their findings—appreciably higher than that in the direction of hexagonal axis. The expansion coefficient, al, however, decreases rather more slowly with temperature than previously reported. The expansion along the c axis up to nearly 1000°C appears in excellent agreement. However, at higher temperatures there is a marked deviation towards higher expansion, reproducible between different specimens. Furthermore, there seems to be some irregularity in the variation of all with temperature, the apparent local minimum and maximum values at 510o and 1024o C, Table II, being well outside the experimental error limits. It must be stressed that the apparent discontinuity in the c parameter expansion is still insufficient to account for the expansion value reported by Agte et al.&apos; since a total expansion of close to 2 pct would

Jan 1, 1962

By J. Nutting, J. W. Cahn

WITH the development of thin film techniques for the direct examination of metals in the electron microscope some new problems in quantitative metallography have become apparent. In order to obtain certain contrast effects in the electron optical image when examining thin films from alloys containing dispersed phases, it is essential to use films of a thickness at least two or three times greater than that of the mean particle diameter of the dispersed phase. From micrographs of such specimens it may be desired to obtain the volume fraction of the dispersed phase and the number of particles of the phase in a unit volume of the matrix. Under these conditions the particles sectioned by

Jan 1, 1960

By H. B. Treweek, V. R. Degner

Current mineral industry trends toward handling the high tonnages of lower grade ore and tailings retreat lead to a continuing need for large volume flotation cells. The benefits which accompany the larger cell flotation circuit include reduced capital cost, less mill floor space, reduced operational complexity, and less maintenance, provided the metallurgical performance and solids suspension capability of the cell are not compromised. This study reviews development considerations pertinent to large mechanical air induction type flotation cells from the standpoint of cell internal hydrodynamic characteristics and metallurgical performance. While the importance of process related factors such as chemical usage, pH control, solids size and loading, and circuit arrangement cannot be denied, this study will emphasize the relationship of cell size (volume), mechanism geometry (impeller diameter), and mechanism operating conditions (rotor speed and submergence), to air transfer, liquid circulation, liquid "rise velocity" and mechanism power draw. Specific hydraulic performance maps for large capacity 300 and 500 cu ft flotation cells will be reviewed in terms of the relationship between the operational variables and the air and liquid flow conditions within the cell. Metallurgical results, obtained under plant operating conditions for 300 and 500 cu ft cells, are included to illustrate the metallurgical performance similarity of flotation cells which follow hydrodynamic scale-up criteria set forth in this investigation.

Jan 1, 1976

By C. W. Davis, R. S. Dean

AMONG naturally occurring inorganic compounds, magnetite has many unusual and interesting properties, and it is the purpose of this paper to call attention to these properties and review possible uses of magnetite that might be based on them; in other words, to see what uses may be found for magnetite as a physical rather than as a chemical entity, as a mineral rather than as an iron ore. The Mineral Physics Studies initiated in the Metallurgical Division of the U. S. Bureau of Mines a few years ago gathered together much information on mineral properties, and they are therefore the principal source of material for this paper. Magnetic Properties Of Magnetite And Possible Uses As A Magnetic Material Magnetite is unique among minerals for its great magnetic susceptibility, approximately one-third that of soft iron, and some magnetites are permanent magnets, or lodestones. The literature contains many measurements of magnetic properties of individual magnetite crystals, but no systematic survey of the effect of mechanical preparation and heat-treatment was available until the recent investigations of the Bureau of which included not only susceptibility but coercive force and remanence as well. For the purpose of orientation, Table 1 gives the magnetic properties of several samples of magnetite and of a few other substances3. This table indicates that when ordinary magnetite is powdered it decreases in susceptibility and increases in coercive force and remanence, approaching the properties of lodestone. The properties of lodestone are in fact probably due to the development of very large internal surface on fine grain size4.

Jan 1, 1937

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

The initiation of localized cracking in hydrogenated high strength steel was dependent on the developmeni of a critical hydrogen conceniration and relatively insensitive to the magnitude of the applied stress. The stress was believed to influence the deluyed failure process by providing the means for grouping the hydrogen. On the basis of an assumed distribution law the observed changes in the lower critical stress as a function of notch acuity, yield strength, and temperature were predictable over a significant range of these variables. THE phenomenological characteristics of delayed failure in high-strength steel have been comprehensively investigated and the behavior has been attributed to the strong embrittling action of hydrogen.1-3 Delayed failure or, as it is also termed, static fatigue, is the most sensitive means of detecting hydrogen embrittlement since it allows the maximum time for hydrogen diffusion during a test.3 The nature of delayed failure cail be aptly described by four parameters which are schematically depicted in Fig. 1. The upper critical stress corresponds to the rupture stress in a conventional notch tensile test. The lower critical stress or static fatigue limit is the stress below which no delayed failure will occur. The incubation period is the time required for the formation of the first crack and the fourth parameter is the failure time. An increase in hydrogen content, notch acuity, or strength level of the material increases the susceptibility for delayed failure by decreasing the lower critical stress, the incubation period, and the time to failure.lY3 A decrease in test temperature prolongs the incubation period in accordance with the lower diffusion rate of hydrogen, and also de-

Jan 1, 1961

In the examination of an undeveloped prospect a decision must be arrived at from an inspection of the outcrops and the exposures in a few shallow pits. Prospects that are offered for sale rarely expose any important quantity of good ore, work having usually been stopped when the immediate exploration no longer yielded favorable results. It should be borne in mind, furthermore, that a great majority of prospects have been examined many times, and if of conspicuous promise, would have been acquired-for development. In most cases the problem for the engineer, therefore, is to discover the traces of a valuable mineralization that has disappeared through solution, or the conditions that indicate the possibility, or probability, of underlying secondary enrichments. The available data being meager, every feature should be the subject of careful study-the condition of the outcrop, the structural relationships, the associations of minerals, the alterations of wall rocks, the chances for underlying enrichments, and so forth, as well as the actual assay value of the material exposed. It is frequently advisable to spend the time and money necessary to have trenches dug at various significant points along a promising outcrop; such exposures, even if the depth attained is slight, often disclose conditions that are not apparent at the actual surface, as for example, the existence of soft minerals and the distribution of the various minerals through the mass of the deposit. Trenches also permit samples to be taken from points that were not accessible during former examinations. Strong, persistent outcrops of uniform width may be taken to indicate the probable size and character of the underlying vein,

Jan 1, 1932

By Wayne E. Tuomi

The mining industry is faced with a pressing problem; that is, to develop more efficient methods of extraction, handling and upgrading-techniques that will do the job faster and better than ever before. New techniques require new machines, or applications of new and improved materials that can be used to modify and improve existing machine and equipment designs. The traditional approach has been to increase productivity by increasing equipment size. Prognostication indicates that the trend toward larger equipment sizes and capacities will continue as one answer to the challenge imposed by future increases in mineral demands. But what is the limit on the continued growth of equipment size? Until about 1930, there was a very definite limit-a limit imposed by the strength of the steels and the power plants then available. The equipment engineer had come to an impasse: even though it was easily possible, for instance, to triple the size of a bucket, it had become impractical to correspondingly enlarge the boom, the counterweight, and the power plant.

Jan 3, 1967

By William B. Phillips

The possible sources of potash salts in the United States have been considered from many points of view during the last several years, but it is only within the last two or three months that the situation has become acute. We import from Germany, the only sourcc of large supply, more than $10,000,000 worth of potash salts annually, and this business has been badly crippled by the European war. If there was ever a time in our industrial existence when the necessity of providing for our own needs was more acute than it is now, we are not aware of it. One has only to study the price lists of chemicals sent out by the large supply houses to see the change wrought within a very short time. Whether or not these prices are to maintain for a considerable time, no one can say; but it appears to be probable that we shall not see prices materially lower for a period of uncomfortable length, to say the least. It is not my purpose at this time to discuss the various sources of supply of potash salts that have been suggested or recommended. Some of them might afford a pleasing relief but all of them combined would not affect the situation seriously. If we are to have our own sources of potash salts, they will have to compare, in some efficient manner, with the sources upon which we have drawn during the last 20 or 30 years; i.e., they must exist in minable quantities. It seems to me to be quite idle to speculate upon our domestic sources of potash if those sources are not of a character similar to those upon which we have so long depended. A few thousand or, perhaps, a few hundred thousand dollars&apos; worth of chemically derived potash may be produced under the stress of present conditions, but when we consider that each year demands more than $10,000,000 worth, we must look to underground sources; we must look to mines similar to the famous Stassfurt and Halle deposits. If we cannot mine potash salts, we shall have to do without them for a while.

Jan 1, 1915

By Lloyd Emory

THE region known as. Guyana or Guiana stretches along the north coast of South America from the mouth of the Orinoco River in Venezuela to the mouth of the Amazon River in Brazil. Politically, it is divided into British, Dutch, and French Guiana, extend¬ ing into Venezuela on the north and into Brazil on the south. Because the area is within the sweep of the northeast trade winds and of approximately the same latitude, plant&apos; and animal life are fairly uniform throughout. The geology is very similar as far as the northern coast is concerned. The drainage is taken care of by a number of large rivers that flow northward directly into the sea. The Courantyne River, which roughly divides the area into half, is the eastern boundary of British Guiana.1 The lower reaches of this river are also the center axis of an ancient bay that at one time indented the coast-line at this point. The old shore-line and, in fact, successive shore-lines can be traced from near the present coast-line in, the northwest district of British-Guiana, south-east and inland, crossing the Essequibo River near Dahli, the Demerara near Christianburg, the Berbice at the mouth of the Kuruduni River and the Courantyne at Vaka-Kuyaha Falls. The line then swings around to the northeast and again approaches the coast near St. Lau-rent in French Guiana. This article will be confined to British Guiana and largely to the valley of the Demerara River, but for geographic names .and topographic details it might, however, apply to Dutch Guiana as well. British Guiana, which comprises about 90,000 sq. mi. and is as large as England, Scotland, and Wales combined, may be divided into three belts, the alluvial belt or coastal plain, the foot-hill area (often spoken of as the sand clay belt), and the hinterland.

Jan 1, 1928

By Herbert H. Kellogg, Nathaniel Arbiter, Arthur F. Taggart

THE experimental work herein described is presented in support of the following broad hypothesis: Conditioning of metals and metallic sulphides by amine collectors involves metathetic reaction at the solid surface between the collector and an oxidized metallic compound, to produce a coating comprising an amine-bearing compound of low solubility in the system. The type of reaction is different in acid and in basic solutions; both types may occur simultaneously in near-neutral pulps. EXPERIMENTAL The experiments comprise contact-angle tests with a variety of metals and metallic sulphides and extraction tests on ground chalcocite. Contact-angle tests were made principally on metals. Covellite paralleled metallic copper in amine solution at pH 8.8 (Table 3) and in alkaline water, but maintained an angle of about 70° in 10-3 HCl solution, where metallic copper lost its angle. The tests with anionic collectors (Table I) indicate that the behavior of metals in general is parallel to that of their minerals in anionic solutions. It is believed that this is generally true with cationic collectors also, but the covellite test is a warning against a broad assumption to this effect. All test specimens were mounted in Transoptic.* All tests in conditioning solution were preceded by a test in distilled water; cleaning and polishing were continued in every case until the angle in water was zero. Subsequent transfers into and out of solutions and test cells were made in such a way as to prevent exposure of the surface to air.1 The amine used was primary laurylamine, Armour and Co., AM-1120. It was used in the form of the hydrochloride, obtained by precipitation with gaseous hydrochloric acid from an ether solution of the amine, and purified by two recrystallizations from ether-alcohol.2 Inorganic and other test reagents were standard laboratory grades. [ ] Temperatures were not controlled; the probable range of test-solution temperatures is 65° t0 80°F.

Jan 1, 1943

By Sidney Powers

INTRODUCTION THIS paper aims to present the results of an investigation concerning gravitative differentiation in lava flows, based on a quantitative microscopic and chemical study of a Triassic basalt from Nova Scotia, and confirmed by data secured from a study of certain Keweenawan ophites. At Cape d&apos;Or, Nova Scotia, near the head of the Bay of Fundy, marine erosion has exposed a series of Triassic basalt flows in which copper has been sought for a number of years. Studies of the thickest flow of the series with regard to volumetric composition, specific gravity, and grain have been made by the junior author, and measurements by students at Tufts College, together with confirmatory observations of the same nature on this and other flows by the senior writer, and chemical analyses made by the Division of Mines, Mines Branch, Ottawa,1 all show differentiation in lava flows comparable to that in intrusive bodies. The work was made possible by the availability of the drill-cores, the property of Tufts College, and emphasizes the desirability of the study of drill-cores from other localities. Measurements of the specific gravities of certain Keweenawan lava flows of -Michigan by the senior author, from material collected in 1915, will be given as a comparison to those of the Cape d&apos;Or flow. It has been found that the specific gravity of drill-cores, or volume per cubic foot, can be readily obtained by measuring their dimensions. This can be done to an accuracy of within 1 per cent. in pieces of core over 100 min. in length by using a micrometer gage for the diameter, and taking the average of six measurements of the diameter; and the average of four measurements of the length made with a finely graduated ruler. Then, after weighing them, the weight in grains per cubic centimeter, or what is practically the same thing, ounces per cubic foot, is obtained. System-

Jan 2, 1916

By A. C. Fraker, H. H. Stadelmaier

WIENER and Bergerl reported the existence of the nitrides Fe3NiN and Fe3PtNwith a cubic L1&apos;2 structure. The present note shows that a similar nitride Fe3PdN can be observed and that the composition range between the iron nitride Fe4N and the nitrides Fe3NiN, Fe3PdN, and Fe3PtN is occupied by single-phase cubic nitrides with structures intermediate between L1&apos; and L1&apos;2. The materials used in this investigation were electrolytic iron of 99.9 pct purity, carbonyl nickel of 99.7 pct purity, sponge platinum of 99.95 pct purity, and palladium sheet of 99.8 pct. purity. Binary alloys of the transition metals were induction-melted in a crucible of fused alumina, powdered, and screened to a particle size of - 200 mesh. The powders were nitrided at 600°C in a gas mixture of ammonia and hydrogen, and the crystal structure was determined with the aid of a Wilson powder camera. The results are compiled in Table I together with information from the paper of Wiener and Berger.1 The compound at the nominal composition Fe3PdN has a diffraction pattern with prominent reflections of a face-centered cubic lattice (h2 + k2+l2 = 3, 4, 8, 11, 12, 16) and weaker superstructure lines (h2 + k2 + 12 = 1, 2, 5, 6, 9, 10, 13, 14). With decreasing palladium content the superstructure lines become weaker and approach the intensity of those of Fe4N. No analysis was made of the intensities, but it can be assumed that the structure is that found by Wiener and Bergerl in Fe3NiN and Fe3PtN, namely L1&apos;2 (perovskite structure) with both palladium and the interstitial nitrogen fully ordered. The dependence of the lattice constant upon the solute atom (Ni, Pd, Pt) content can be explained tolerably well by simple lattice expansion due to subsequent work confirms this suggestion, it will be of significance to order-disorder theory. The author is grateful to Lester Guttman for discussions on this topic.

Jan 1, 1961

By W. C. Maurer

Although millions of feet of rock are drilled annually, the basic drilling mechanisms involved are not well understood. The primary reason for this lack of knowledge is because the basic principles of rock failure are not well understood and rock failure is the primary mechanism in drilling. A better understanding of the drilling mechanisms would enable a more scientific approach to the design and use of drills and bits. The paper reviews several models which have been proposed to explain various aspects of the different drilling methods. These models are described and their limitations and areas of application are discussed. Drilling rate relationships are developed and related to the basic rock failure mechanisms. TYPES OF MECHANICAL DRILLS There are three basic methods of mechanically attacking rock: 1) percussive action, 2) rotary action, and 3) combined rotary-percussive action. A percussion drill applies a force perpendicular to the rock surface and the bit moves into the rock perpendicular to the surface, forming a crater beneath it (Fig. 1). A rotary drill applies a constant thrust to the bit while a torsional force moves the bit parallel to the rock surface, breaking the rock ahead of it. A rotary-percussive drill applies both a rotary force and a percussive force to the bit which moves into the rock at an angle to the surface. The commonly used drills can be classified as: rotary-drag, diamond; percussive-hammer, piston, churn; and combination-rotary-percussive, roller.

Jan 1, 1967

By W. H. Emmons

In 1922 Morey made a series of experiments in which he observed the cooling of a molten system containing H2O, 9.1 per cent; K2O, 17.3 per cent and SiO2, 73.6 per cent. This system was confined in a bomb; it was fluid at 500° C. and exerted no vapor pressure. In cooling to 420° C. a large part of it crystallized and at that temperature much of the water had separated from the crystals and remained as steam, which built up a pressure of 4998 lb. per sq. in., a force sufficient to lift nearly one mile of granite.&apos; If granite, cooling at 600°, expels vapor in the process of crystallization it is reasonable to suppose that a considerably greater vapor pressure would result, and it is thought that the vapor expelled from crystallizing granitic batholiths probably has a pressure sufficient to lift two or three miles of granite. This vapor, collecting near the tops of cupolas of batholiths, is believed to exert sufficient pressure to fracture the hoods and roofs of batholiths above the cupolas. If that is true, one would expect to find that the fracture systems above cupolas are arranged in patterns that depend in part on the shapes of the cupolas. The mechanics of the situation seem to require that conical cupolas should have radial fracture patterns, that bluntly rounded cupolas should have fracture systems that are either irregular or rudely conjugated in plan, and that elongated stocks or cupolas should have fracture systems in which the fractu&apos;res lie nearly parallel to the direction of the elongation of the cupolas. Study of essentially all the cupolas of the earth that have associated important vein-filled fractures shows that this is generally true. This

Jan 1, 1935