By Yonghua Li, Fanling Meng, Weitao Zheng, Xiaodong Wang

The NiTi thin films were deposited onto copper substrates by magnetron sputtering. Tensile tests were carried out on CSS-44100 electron universal test-machine. X-ray diffraction profile Fourier analysis method has been used to study the mechanical properties of deformation NiTi thin films. The surface micrographs of the NiTi thin film were obtained using scanning electron microscopy (SEM). It has been found that the dislocation density and the deformation storage energy density increased with elongation increased. Microhardness was calculated from the dislocation data. The results showed that the microhardness values were not in a good agreement between calculated values and measured values. The oxide layer on the surface of NiTi thin film affects the measured values of microhardness. The Vickers hardness measured values are larger than the calculated values. The experimental results showed that a series of parallel cracks grew in a concerted fashion across the thin film and the cracks were equally spaced.

Jan 1, 2015

By Shengqin Zhang, Yousef Mohassab, Feng Chen, Hong Yong Sohn, Mohamed Elzohiery, Amr Abdelghany

A novel ironmaking process is under development at the University of Utah aimed at producing iron directly from iron oxide concentrate in a flash reactor. This process will reduce hazardous emissions and save energy. The kinetics of magnetite reduction with hydrogen was previously investigated in our laboratory in the temperature range 1150 to 1400 oC at large temperature increments (~100 oC increments). Due to the significant melting that occurs above 1350 oC, the reduction kinetics was measured and analyzed in two distinct temperature ranges of 1150 to 1350 oC and 1350 to 1600 oC (~50 oC increments). Experiments were performed using magnetite concentrate particles of different sizes under various hydrogen partial pressures and residence times. Reduction degrees of more than 90 % were achieved in a few seconds at temperatures as low as 1250 ºC. Different rate expressions were needed to obtain reliable agreement with experimental data.

Jan 1, 2016

By Itavahn Alves da Silva, Jose Dimas de Arruda, Amanda Aparecida Fátima Arruda, da Silva de Souza, Carlos Antonio da Silva, Varadarajan Seshadri, Samuel

The knowledge of the flow field inside a continuous casting mold is essential to improve operational efficiency of the process and also to achieve better inclusion control. Physical modeling, PIV technique and CFD have been employed to assess the velocity distribution in the metal- slag interface region in a slab mold. The analysis of results shows how higher casting velocity and lower immersion depth of submerged nozzle can lead to higher turbulence in the slag-metal interface. The effects of density difference between slag and metal and interfacial tension between the phases have been highlighted.

Jan 1, 2016

By S. C. Sharma

The aluminium matrix composites with ceramic dispersoids can be separated by density difference concept. In the proposed work composite scrap is recycled using an oil fired furnace. The scrap is melted in the furnace and temperature is maintained below 740 degree centigrade. Because of the density difference the lighter dispersoids will float and heavier dispersoids will settle down. The clean melt is separated be removing the floating and settled disperssoils, and then filtering using ceramic filters.

Jan 1, 1995

By Cheng Yan, Yugang Li, Qian Wang, Lizhi Zhang

In continuous casting process, mold powder has lots of metallurgical effects, such as covering the molten steel to prevent liquid steel from oxidation by air, preserving heat for top layer liquid steel, lubricating initial shell and so on. However, mold powder also can deteriorate the quality of final products obviously after the entrapment of mold powder in steel. In the present work, based on the similarity theory the effect of technological parameters on mold powder entrainment was investigated by water model. Experiment was carried out in the water mold using oil and water to simulate slag and steel, respectively. The results showed that increasing casting speed increased the water-oil interfacial fluctuation and entrainment frequency; viscosity of oil also had a great impact on the interface fluctuation and entrainment; water-oil interfacial tension effect the entrainment while not changing the interfacial fluctuation; submergence depth had little impact on entrainment and interfacial fluctuation.

Jan 1, 2015

By G. Cifuentes

When the applied current is interrupted in a copper electrowinning plant, and then is back in operation, the lead anodes tend to corrode. In order to decrease the corrosion, the damage protective ("back up") anodic currents are applied during the period of interruption. The current work aims to establish the effect of the concentrations of sulphuric acid, copper and cobalt on the anode corrosion, to quantify the effect of various anodic protection levels on the anode corrosion and to propose a method to select the appropriate protective current density value.

Jan 1, 1999

By Ioannis Paspaliaris, Dimitrios I. Gerogiorgis, Dimitrios Panias

"Red mud fiberization is a process with remarkable potential, alleviating environmental pressure by transforming an aluminum by-product into mineral wool, thus to various marketable products. A promising mineral wool process is molten slag fiberization via an impinging air jet, which avoids mechanical wear and rotating parts. The molten slag which remains after pig iron casting flows out of a heated ladle orifice at a high temperature (1600 °C) and adjustable flowrate, and forms a free-falling vertical jet which visibly radiates its excessive heat: at a given distance, a high-velocity impinging air jet meets the vertical melt jet perpendicularly (or at an angle), inducing intensive droplet generation, subsequent fiber elongation, collection and processing.This paper focuses on high-fidelity CFD modeling of the molten jet flow under external cooling: the model encompasses all physicochemical phenomena (melt laminar flow, radiative cooling) and considers several temperature-dependent slag transport properties in order to understand which operational degrees of freedom (manipulated variables) are useful to process optimization."

Jan 1, 2012

By C. Lupi

Zinc chloride electrowinning presents difficulties in obtaining smooth, compact and dendrite free deposits with a high current efficiency due to the presence of undesirable metal ions. However, it is hard to define a level of impurities tolerable in zinc deposition, and despite a lot of research in this field, the reaction mechanisms of the undesired metal ions are still not clearly understood. In this study, the influence of Fe, Cd, Co, Ni and Cu additions were investigated, as well as their synergic effect on the zinc electrodeposition process from chloride electrolytes and on the obtained deposit morphology. The tests were all performed in presence of TBACl which reduces the harmful effect of such impurities on the zinc reduction.

Jan 1, 2003

By Yuan Zeping

The Guixi smelter is the first Outokumpu flash smelter in China .It was commissioned on December 31, 1985. Originally, the smelter was designed to produce 90,000 tonnes of copper annually. After the implementation of oxygen enrichment and other modifications, the smelter will reach its anticipated annual capacity of 200,000 tonnes of copper in December 1999. This paper describes the performance of the smelter, the first phase modification project and the second phase expansion project which have made Guixi one of the best copper smelters in the word through the use of existing and innovative technologies.

Jan 1, 1999

By F. A. Fasoyinu

The mechanical properties of yellow brass (C85800), high strength yellow brass (C86300), and high manganese brasses (C99700 and C99750) cast in permanent molds have been studied. The tensile properties as well as fracture and impact toughness of these alloys are strongly dependent on the chemical composition. Alloys and/or compositions exhibiting relatively high zinc equivalent often exhibited high ultimate tensile strength and yield strength with significant reduction in ductility (% elongation). In order to achieve optimum properties with a good balance between strength and ductility, a calculation of the zinc equivalent before alloy preparation can be useful.

Jan 1, 1999

By A. Robles

The main goal of the present work is to propose a viable alternative for selective arsenic elimination from copper smelter flue dust without the need of a global leaching scheme for all the individual components of the flue dust. Using this alternative, the inherent copper recovery problems are avoided. Arsenic precipitation is also considered for regenerating the solution and completing the process cycle. The experimental results for arsenic extraction and precipitation are satisfactory. Concentration of NaOH used was relatively low. The main reason for succeeding in high arsenic extraction and low NaOH consumption is due to the previous water washing of the flue dust. Water washing dissolves much of the iron and copper that are present in certain percentage as sulphate.

Jan 1, 1999

By Ligang Zhang, Wen Chen, Xinghua Liu, Jialin Li, Xiaoyin Liu, Zhenhong Liao

A research-scale fluidization and magnetization roasting device was developed to evaluate a processing option that might offset the complexity and high cost of the conventional magnetization roasting process on siderite. In this study, the operating parameters of the fluidization and magnetization roasting device for siderite were evaluated through cold-flow tests and magnetization roasting tests. The reaction mechanism functions of the fluidized roasting process are revealed with kinetic studies.

Jan 1, 2015

The concepts of capacity and basicity have proved extremely useful in dealing with a wide range of solute species in metallurgical slags, and as a result have been widely applied. These two concepts are reviewed, and it is suggested that the Lewis approach to basicity has much to commend it. In some cases, it appears that the term capacity has been used without due consideration being given to the nature of the solution being formed, or even to whether a true solution was being formed at all. This paper proposes a rigorous definition of capacity, based on the true nature of the solution process in slags and glasses, and briefly reviews the repercussions of this approach on data available in the literature and the limitations which it may impose on future investigations in this area.

Jan 1, 1994

By Shanlu Yang

In this study, laser-GTAW hybrid welding was used to the lap joint of galvanized dual-phase (DP) 980 steel in a gap-free configuration. The effects of welding parameters such as the laser power, the distance between the laser beam and the electrode torch, the arc current on the quality of hybrid welds were fully studied. The reason for the formation of different weld defects arises from the development of the highly-pressurized zinc vapor at the interface of two metal sheets. Experimental results demonstrated that the elongated molten pool introduced by the GTAW can suppress the formation of spatters to some extent. However, the hybrid laser-arc welding process still suffers from a large amount of spatters that degrade the weld quality. Furthermore, it was found that the weld quality was enhanced with the increase in the laser beam-arc distance and welding current.

Jan 1, 2009

By L. A. Kazanbayev

The Chelyabinsk Electrolytic Zinc Plant (CEZP) was commissioned in 1935. Over the elapsed years the Plant capacity has been increased from 10 thousand tons of zinc (1935) to 150 thousand tons of zinc (2005). The paper describes the Plant main achievements in production updating for the last 10 years.

Jan 1, 2006

By John L. Uhrie

Oxide stockpile leaching operations can realize increased copper recovery and decreased acid consumption from in-situ generated acid resulting from the oxidation of intentionally introduced pyrite recovered from mill tailings or other sources. While all oxide leach ores can benefit from pyrite addition, low acid consuming ores can show remarkably increased recovery and net acid generation; however, more highly acid consuming ores will show benefit more exclusively through increased copper recovery. Additional work shows that the value of highly acid consuming ores can be optimized by balancing copper recovery against acid consumption.

Jan 1, 1999

By Gerardo R. F. Alvear, Alistair S. Burrows, Stanko Nikolic, James S. Edwards

"The copper ISASMELT™ process has evolved over more than a quarter of a century and can now be considered mainstream, with single furnaces producing more than 340,000 tpa of copper in matte. The next evolutionary step for the ISASMELT™ technology is to directly challenge the dominance of the Peirce-Smith converter by the implementation of a continuous copper converting process on a commercial scale. The present work describes the status of the continuous converting process – ISACONVERT™.Continuous converting has been performed successfully in pilot scale ISACONVERT™ plants, where operating results have verified the predictions of fundamental research and reinforced the underlying confidence in the design parameters. From a matte feed rate of 250 kg/hr, a calcium ferrite slag and a low-sulfur blister have been produced. Design is now complete for the first commercial application of the ISACONVERT™ process. The present paper describes the status of ISACONVERT™ by summarising results of recent pilot plant tests and describing the first commercial plant design."

Jan 1, 2009

By O. P. Pandey, Rama Arora, Gurmel Singh, Suresh Kumar

The tribological behavior of Dual Particles Size (DPS) rutile reinforced LM13 alloy composite was investigated under varying applied pressure from 125 kPa to 625 kPa at a constant sliding speed of 1.6 m/s. In the present studies, 15 wt.% of rutile particles of different sizes (50-75 μm and 106-125 μm) are reinforced in the Al-12Si alloy (LM13) by liquid metallurgy route. Microhardness of the prepared samples was measured in different phases. Microstructure, wear mechanism and surface morphology of the wear surfaces and debris was observed under optical and scanning electron microscope. The change in wear behavior has been explained with reference to the observed EDS analysis of the wear track and debris. However, an interesting change in wear feature, mild to severe wear transition at critical pressure was noticed in wear behavior of the composite. The Al-DPS composite has immense potential to be used as a component material for tribological applications.

Jan 1, 2015

By Xiangru Chen, Qijie Zhai, Wei Zhang, Haicheng Li, Chao Yang

In this paper, ductile iron material with different content of niobium was prepared by a scientific melting method. Image Analysis Software was used to studied the effect of niobium microalloying on both pearlite content and pearlite lamellar spacing in ductile iron quantitatively. The results showed that the addition of a small amount of niobium could increase the pearlite content and decrease pearlite lamellar spacing of ductile iron effectively.

Jan 1, 2015

By Ho-Sang Sohn

Copper concentrate particles of 200 to 300 mesh size were fed from the top of vertical reaction tube of 2.8 cm ID and 2 m long with an O2-N2 gas mixture. The reaction tube was heated to 900 K to 1100 K. The residence time of the particles in the reaction tube was about 1 second. The copper concentrate particles were very rapidly oxidized and melted down during their descent in the reaction tube. The particle temperature were calculated by combining an un-reacted core model, mass transfer between gas and particles, and heat transfer between gas, particles and tube wall. The particle temperature reached its maximum within a distance of 60 cm from the top of reaction tube, and it attained at 2000 K at higher oxygen partial pressure. The most particles were melted at the oxygen partial pressure above 20 kPa. An appreciable amount of As, Sb and Pb in the concentrate particles was eliminated in the upper portion of the reaction tube and the rate of elimination are explained by the rate of mass transfer of volatilized species through the gas film on the particle surface and the variation of particle temperature during the descent.

Jan 1, 2006