By George A. Calboreanu

In order to overcome drilling and tapping of high hardness wear resistent material in slurry pumps, most of time mild steel inserts are mounted in the mold and after pouring they become an integrated part of the casting. This process is limiting the size and design possibilities of slurry pumps and efforts were made to drill and tap the hard iron itself. The paper will present practical results obtained in drilling and tapping Cr-Mo wear resistent material with hardness in excess of 700 HBN. The life time of the slurry pump parts used in hazardous waste fuel transportation with high slurry velocity and 15% solid loading some of it being quartz, increased 2.5 to 6 times.

Jan 1, 1996

By den Bulck A. Van

In Europe, 50% of the copper originates from recycling. High-Cu containing scraps are regularly rich in impurities like Fe, Ni, Sn and Pb. Many high-Cu containing scraps are fed directly into anode-furnace casting installations or furnaces with limited refining capability. The impurities levels of the anodes produced in these processes should however remain acceptable for further electro-refining. The distribution of Sn between copper and slag has been investigated for conditions relevant to copper converting. Unlike previous studies, this work focuses on the behavior of Sn relevant to fire refining conditions, which are essential for anode refineries.In this study, liquid Cu–1Sn and CuOx–FeOy–SiO2 slag, with CaO additions, were equilibrated at 1300 °C in vacuum sealed SiO2 ampoules. After metal–slag equilibration, the samples were quenched in water. The composition of the slag and Cu metal was investigated with Electron Probe X-ray Microanalysis. The distribution coefficients of Sn between slag and Cu metal were determined as a function of slag composition.

By Patrick R. Taylor

Sub-micron sized boron carbide powders have been synthesized in a non-transferred arc thermal plasma reactor. Precursors for this synthesis are boric acid or boron oxide powders and methane. The powders produced were characterized in terms of size, shape and purity. Methods to increase the purity of the product were evaluated and included hot water leaching to remove unreacted oxides and controlled temperature, air roasting to remove excess carbon. Theoretical results are also presented on the thermodynamics and mechanisms of the synthesis reactions.

Jan 1, 1994

By Onuralp Yucel, Ahmet Turan, Murat Alkan, Hasan Ozer

SHS (Self-propagating High-temperature Synthesis) is one of the important methods to synthesize B4C powders. The process contains the reaction of boron oxide powders (B2O3) with magnesium reducing agent and carbon black carburizer. SHS products are leached in HCl media to purify synthesized B4C powders in the following step. In the present study, effects of various functional additives (KClO3, KHSO4, MgSO4.7H2O, NaCl, MgO and Na2SO4) in the SHS stage were carried out. Various proportions of the additives were mixed with the initial SHS charge mixtures. Two different molar ratios were employed in the initial SHS mixtures as 1:3:0.8 B2O3:Mg:C and 1:2.5:0.8 B2O3:Mg:C. After the SHS step, HCl leaching process was applied to the SHS products. Filter cakes were dried and characterized by using X-Ray Diffraction Spectroscopy, BET and chemical analysis techniques.

Jan 1, 2015

By Wei Gao, Qing-cai Liu, Cun-fang Lu, Jian Yang, Hinmi Zheng

"The mode of occurrence of sulfur and mercury in 57 Chinese bituminous coals have been examined using X-ray fluorescence spectrometry (XRF), X-ray diffraction (XRD), and Zeeman atomic absorption mercury spectrometer. Mercury levels in coal are related to the geographic location of the coals and types of the coals. A synthesis of result indicated that most likely occurrence modes of mercury in high-sulfur and high-mercury coals are in solid solution in pyrite. Our study from 57 coal samples showed that most values of mercury concentration in coal varied from 100 to 1000 ng/g with an average of approximately 500ng/g, and mathematical model about correlation between mercury and sulfur was gained by mathematical statistics. This is apparent that mercury and sulfur vary concomitantly from coal data (table 3) , the high correlation between them in all coals at confidence of 95% ( a=0.05 ) .1. INTRODUCTIONThere contained about one trillion ton abundant coal resources in China. As a leading level of proven coal reserves in the world, the coals mainly distributed in north China and northwest China, especially in Shanxi, Guizhou, Shanxi provinces and Inner-Mongolia autonomous region. At the same time, China has the largest production and consumption of coal, and has the output of coal nearly accounted for 37 percent of the world's production. Coal-fired power plants are the major source of energy generation in China, and the proportion of coal combustion is up to 75 percent in the total energy configuration. Therefore, the mercury pollution caused by coal-fired has become a topic of wide-spread discussions since 1990. The contamination of mercury of human activities accounted for 10 to 30 percent [1], and the mercury emissions of coal-fired flue gas has made the greatest contribution to the pollution of atmosphere[2] In the past 30 years, the global increasing concentration of mercury pollutant in atmosphere maybe result from coal combustion[2]. The mercury emissions caused by coal-burning has become the main reason of China's mercury pollution, and the characteristics of mercury pollution is closely related to China's energy configuration, additionally, the features of mercury pollution have changed from the point pollution in 1970's to diffused pollution today[3]. Mercury can be found in various types of coals, and it is evaporated into gas phase during the combustion process."

Jan 1, 2011

By B. Q. Li, Y. Shu, K Lynn

"This paper discusses the effects of magnetic field and internal radiation on the melt flow and solidification morphology during solidification processing of oxide crystals for optoelectronic and remote sensing applications. The numerical solution of the integral differential equation characterizing the internal radiation and the magnetohydrodynamic equations describing the magnetic and transport phenomena is obtained by applying the combined discontinuous and continuous finite element method. The results show that both internal radiation and an externally applied magnetic field can have important effects on the melt flow and solidification behavior during the melt processing of oxide materials.IntroductionOptical single crystals are widely used in optical and electronic devices. These crystals are often grown from high temperature oxide melts under strictly controlled conditions. As in the well-known single crystal growth processes for semiconductor wafers, thermal gradient in the melt is a major contributing fuctor to the oxide melt pool. Unlike the semiconductor single crystal growth processes, however, the oxide melt is semitransparent and internal thermal radiation plays an important role in redistributing the thermal energy in the melt pool. Our recent experience with pilot-scale plant measurements also shows that the oxide melt is electrically conducting, although its electrical conductivity is considered much lower than the liquid metal or semiconductor melt.The fact that the oxide melt is absorbing and emitting in the thermal radiation frequency range makes it difficult to study the thermal energy transport in the melt pool. This is because thermal radiation is governed by a hyperbolic differential equation, which is different from those describing the transport processes in liquids. Also, our understanding of how thermal radiation interacts with other transport mechanisms such as convection and conduction is rather limited at point in time, in particular in high temperature oxide melts for optical single crystal processing."

Jan 1, 2004

By Emmanuel N. Zevgolis

In the present work, a reduction roasting experimental study of Greek nickeliferous laterite samples with a gaseous reducing mixture ? CO:N2- is presented. The effect of parameters such as temperature, ore grain size, and composition of the reducing mixture were examined. It is deduced that the reducibility of intermediate type laterite sample, where iron appears mainly in the form of goethite (a-FeOOH), is considerably higher than that of limonitic type laterite samples, where hematite (a-Fe2O3) is the predominant iron mineral phase. The degree of reduction of the limonitic type laterite samples does not exceed 50%, while it reaches 95% in the case of the intermediate-type laterite sample under the same experimental conditions. Increasing the temperature in the range 750-900°C does not considerably favor the reduction of the limonitic type laterites, whereas decrease of ore grain size of the limonitic-type ore samples and more intense reducing conditions increase the reduction. The considerably higher specific surface area values of the intermediate laterite samples, diminishes the effect of the ore grain size and this can be regarded as the critical parameter leading to the higher reducibility of this ore.

Jan 1, 2009

By Cong Wang, Siyang Long, Pengcheng Zhang, Haibin Zuo

The present study describes central segregation of the High-carbon steel billets of 150mm square and its heredity to the following hot-rolled wire rods, whose sizes are 10mm and 6.5mm in diameter separately. The relationship between center segregation of the billets and solute element distribution of rods, the mechanical properties and microstructure of rods were studied experimentally. The results show that segregation index of C is higher than that of Mn. With the increase of central segregation, the stability of the mechanical property of the rods becomes worse. The formation of carbide network and central martensite in the rolled products can be attributed to the heredity of the as-cast central segregation. The 6.5mm-diameter-rod has higher tensile strength than that of 10mm diameter which might be due to bigger reduction ratio. Thermo Mechanical Control Process (TMCP) should be used together with Billet Centersegregation- controlling (BCSC) to improve the overall properties of rolled products effectively.

Jan 1, 2016

By H. C. Roland Kammel

Stannous sulfate electrolytes are widely used nowadays in electrolytic tin production. Characteristic features of this electrolysis process are that dense cathode deposits can only be obtained by additions of organic additives and that so called ?black mud is formed on the anode surface which leads to an increase in cell-voltage. In order to prevent excessive cell-voltages or oxygen evolution the black mud has to be removed periodically. Studies in laboratory scale have been performed about the effect of different organic additives on electrolytic tin deposition and the formation of surface layers on pure and industrial tin anodes. Results reveal that organic addition agents are effective in reducing cathode roughening as well as extending the covering time of the anode ?by black muds.

Jan 1, 1985

By K. Fagerlund

Methods for simulation of settler reactions, matte-slag separation and matte settling in copper flash smelting have been examined. The reaction, separation and settling phenomena of slightly oxidized chalcopyrite samples and cuprous sulfide-magnetite mixtures in fayalite type slags were examined at about 1300°C under inert atmosphere. Two methods based on introduction of molten samples of oxidized chalcopyrite concentrates or synthetic matte-magnetite mixtures onto the surface of molten iron silicate slag were tested. In the first method the samples were water quenched and polished specimens were studied and analysed using light optical microscope, scanning electron microscope, energy dispersive spectrometer. In the second method processes taking place after the introduction of samples onto the slag are followed "in situ" using X-ray transmission image monitoring. Great differences were observed in separation and settling behaviour of low and high grade copper mattes produced as a results of interaction of initial samples and slag.

Jan 1, 1997

By Tiejun Chun, Jian Pan, Deqing Zhu, Zhiyong Ruan

"In this paper, the desulfuration of pyrite cinder pellets was carried out. Phase analysis shows that most sulfur of pyrite cinder exists in the form of elementary sulfur. Most sulfur was removed in preheating stage. 81.25% sulfur was removed and the average SO2 concentration of exhaust gas was 1365ppm when the pellets were preheated at 950oC for 9 min. The final product, assaying 62.42wt%Fe and 0.02wt%S content at 96.88% desulfuration was achieved under the conditions of preheating at 950? for 9 min and roasting at 1200? for 15 min, which can be used as the burden for blast furnace.IntroductionPyrite cinder, as a subsidiary product of sulfuric acid production by roasting of pyrite ores, was solid waste in sulfuric acid enterprises. According to the statistics, the annual production of pyrite cinder is about 15 million tons in China. Besides, there is lots of pyrite cinder deposited for many years [1-3]. The pyrite cinder consumed in the cement and other industries as auxiliary additives only accounts for less 30% of its total discharge and the left is stored in waste pond, occupying much land and polluting environment in China [4-5]. Moreover, pyrite cinder contains iron between 30-63% which can be utilized as a cheap raw material for ironmaking by sintering or pelletizing processes, which can not only prevent pollution but also provide cheap raw materials for ironmaking [6-7]. However, compared to traditional iron ore concentrate, pyrite cinder possesses higher sulfur content."

Jan 1, 2012

By Tetsuro Ohashi, Tooru Matsumiya, Yoshio Abe

"The three-dimensional deformation of a continuously cast slab was modeled into two-dimensional deformation by developing the solidified shell of the slab. The developed solidified shell was divided into rectangular elements. The thermal strain produced as the slab is wi thdrawn over one roll spacing in the casting direction was calculated from the temperature change during that time and the increment of the geometrical unbending strain during the time was calculated from the change in the radius of curvature of the slab by assuming that the neutral axis of bending is located at the mid-thickness of the slab and that the transverse section of the slab is kept in a plane during unbending. These strains were imparted to each element as initial strains. The interaction between the elements and the overall deformation of the solidified shell were analyzed by the finite element method.The analysis was performed on a slab being cast on a machine of the circular arc type with progressive unbending. The following findings were obtained as a result. The effect of unbending is spread in the upstream and downstream directions of the slab by the shear deformation of the narrow and wide faces. As the shear deformation increases, the strain in the unbending zone decreases and the strain outside of the unbending zone increases. The effects of secondary cooling conditions, slab size, radius of caster circular arc section, compression casting, etc., were also analyzed. IntroductionTo develop a method for preventing the internal cracking of continuously cast slabs, it is important to acurately analyze the deformation of the slab and this subject has been extensively investigated. Many researchers, including the present authors, have analyzed slab bulging. (1)- (11) Analysis has also been made of thermal deformation that assumes importance in continuous casting of small-section blooms.(12)-(18) However, unbending deformation, an extremely important subject for continuous casters of the circular arc type, has not been fully analyzed."

Jan 1, 1986

By Pavol Loderer

Mineral froth pumping utilising centrifugal slurry pumps is a major engineering challenge for the end users and pump manufacturers due to the undesirable outcome of unstable pump performance. Most of these challenges occur due to incorrect pump selection and suction tank design. The traditional approach is to oversize the pump for pumping mineral froth. New horizontal slurry froth pump designs offer opportunities to improve the mineral froth with challenging (high) Froth Volume Factor while maintaining high efficiency, long wear life and stable pumping performance. This paper examines the flotation process in detail and how froth pumps are designed to handle this arduous process.

By Susanne Pignolet-Brandom

Reflected light microscopy, and scanning electron microscope energy dispersive spectroscopic analysis and backscatter electron images were used to determine if a "slick dross" with undesirable handling properties has an assemblage of phases distinct from normal dross. This study has found that in the normal dross the most abundant lead phases are lead sulfide and lead metal and the most common copper phases are copper-iron sulfide and copper sulfide. In the slick dross, the most abundant copper phase is copper-lead sulfide and the most common lead phases are copper-lead sulfide and lead sulfide. The resulting mineralogical information has provided additional insight into the causes of the handling problem and the reaction mechanism for the formation of normal and slick dross

Jan 1, 1988

By Tengfei Qi, Liqiang Fan, Huiqing Tang

A new method to process the oolitic high phosphorus iron ore for phosphorus removal has been proposed in this research. It is an integration of direct reduction and melting separation with carbon-containing pellets prepared using biomass char. Experiments of direct reduction were preceded using a tubular furnace and three parameters were investigated and they were reduction temperature, biomass char adding ratio(molar ratio of carbon to oxygen） and atmosphere. Results show that the optimum condition is of reduction temperature is 1373 K, biomass adding ratio 0.9, PCO2/PCO 1.0 and reduction time 15~25 min. Under this condition, the reduced briquettes with a metallization of 75.0~80.0 % and a residual carbon content of 0.69~0.11 wt% could be obtained. Subsequent melting separation experiments were conducted using a Si-Mo high temperature furnace. Results show metal with phosphorus content of about 0.4 mass% could be obtained from the reduced sample.

Jan 1, 2015

By John L. Watson

The dewatering of steel industry waste sludges prior to discard or recycling often presents significant problems due to the fineness of the sludge particles, which may blind the filter medium and/or produce a cake with limited porosity, Several steel plant wastes, such as sludges from BOF and EAF gas cleaning operations exhibit not only a very fine particle size, but also some degree of magnetic character, A novel process has been developed to utilize the magnetic character of such sludges to enhance dewatering through a multi-force operation involving magnetic, chemical and vacuum forces, The process consists essentially of undertaking vacuum filtration of a flocculated sludge in a magnetic field, This is achieved by installing a permanent magnetic in a fixed position on the axis of a vacuum drum filter, thus effecting filtration of magnetic and non- magnetic particles, bound together in flocs, in a magnetic field, Previous tests using a modified laboratory vacuum drum filter treating artificial (magnetite) and industry waste (BF sludge) feeds have demonstrated that filtration capacity may be enhanced significantly with increases of up to 3000/0, An explanation of the mechanisms associated with the enhanced filtration was not obvious, and this research was undertaken to permit the cake formation in the magnetic field to be monitored to provide an insight into the manner in which particles agglomerate to form the cake. These tests revealed that the magnetic field caused magnetic particles to be aligned perpendicular to the filter surface and to form channels through which filtrate could freely pass thus increasing capacity, The effects of various magnetic fields and field strengths on the filtration process were also investigated. A simple computer model was constructed to demonstrate the proposed theory of multi-force dewatering, The model output graphically illustrated the suggested mechanism and confirmed the enhanced capacity of the novel dewatering process,

Jan 1, 1996

By Shuai Wang, Gang-hua Fu, Lu Yang, Yu-feng Guo, Tao Jiang

The fluorine-bearing iron concentrate is one of the refractory raw materials for pelletization, which is mainly used in Baotou iron and steel company with lots of problems, such as narrow roasting temperature range and low compressive strength of products. According to its specific character, the effects of roasting temperature, time on the compressive strength and microstructure of pellets were researched. The results show that low melting substances formed during the roasting was the dominant reason of those problems. High melting substances were added in the roasting to investigate their effects on the roasting properties of fluorine-bearing iron concentrate pellets. Low melting substances were reduced when chromite was added. The compressive strength of products was 3100N/P when the 2% chromite was added at the roasting temperature of 1150 ºC, which was increased 700 N/P compared with the pellets without chromite, and the roasting temperature range was expanded by 170 ºC.

Jan 1, 2016

By George P. Demopoulos

n this study we have sought to highlight the critical linkage between individual reaction kinetic parameters (usually determined in small bench scale experiments) and large continuous reactor performance by focusing on the industrially significant zinc pressure leach process. To this end a comprehensive mathematical model previously developed for the description of this process was employed. In this paper we have examined in particular how small variations in key kinetic parameters impact on the autoclave&apos;s performance, i.e. attainment of autogenous steady-state temperature, zinc conversion and solution chemistry. The reaction parameters studied were: (i) stoichiometry of the marmatite leaching reaction; (ii) the activation energy of the same reaction, E,; (iii) the rate constant of the ferrous to ferric oxidation reaction, k,; and (iv) the apparent equilibrium constant for ferric precipitation, K,. This parameter sensitivity analysis was done under no oxygen mass transfer control limitations. Model predictions were found to be more sensitive to the kinetic parameters under certain conditions than others. The most dramatic finding was the one related to the small amount of sulfate produced during marmatite leaching. In connection to this it was found that the small percentage (< 5 %) of sulfate produced enhances the autothermal operational stability of the autoclave. The need for accurate kinetic parameter determination under conditions similar to those encountered in industrial zinc pressure leaching was demonstrated.

Jan 1, 1999

By Jillian Spindura

This work investigates the carbothermic reduction of the complex sulphide mineral, pentlandite, in the presence of lime. The effects of change in temperature and the use of different carbon sources are studied and the role of these variables on the reducibility of pentlandite mineral is discussed. The microstructures of the heat-treated pellets are examined using X-ray diffraction and scanning electron microscopic techniques. The latter analytical method also allows any variation in the morphology and composition of the metallic phases formed, with temperature, to be considered. The kinetics of the reduction process is studied and the magnitude of the overall activation energy is determined from the plots of percentage reduction versus time.

Jan 1, 1996

By lchiro Aoi, Hideo Nakae, Makoto Yoshida, Makoto Ishino

"The influence 6f gravity on the microstructure of unidirectionally solidified Cu-Pb monotectic, Ag-Si and Fe-C eutectic alloys is studied. In order to examine the influence of gravity in a lg environment, both the upward (opposite to direction of gravity) and downward (direction of gravity) unidirectional solidifications are carried out. The results are as follows: (1) For the upward solidified Ag-Si eutectic alloy, the eutectic Si continuously grows. On the other hand, in the downward solidified Ag-Si alloy, the Si grows discontinuously and disperses into the ex-Ag matrix. (2) No morphological difference in the eutectic growth is observed between the upward and downward solidified Fe-C eutectic alloys. (3) In the case of the upward solidified Cu-Pb monotectic alloy, a banded structure, which consists of Pb-rich layers and Cu-rich layers, is observed. However, such a banded structure -is not observed in the downward specimen. (4) The banded structure is not found in the upward solidified Cu-Pb-0.05 mass % Al and Cu-Pb-0.1 mass % Al alloys. In the Cu-Pb-0.05 mass% Al alloy, a fibrous -L 2 phase grows continuously parallel to the growth direction at low growth rate. Only 500 mass ppm addition of aluminum induces the morphological change of the monotectic L2 phase.IntroductionThe influence of gravity on the solidification of eutectic and monotectic alloys has been investigated in microgravity environments [l-9]. The purpose of these studies was to obtain a homogeneous microstructure of eutectic or monotectic alloys, most of which alloys tend to solidify with macro-segregation under gravity. However, in most of the previous experiments, e.g., in free fall systems, in aircraft or in space laboratories, the growth rate was too high to realize a planar solid/liquid interface. This would be due to the limited time for solidification. Thus, it was difficult to examine the influence of gravity on the planar coupled growth of the eutectic or monotectic alloy. In this study, both the downward U.D.S. (unidirectional solidification by gravity) and upward U.D.S. (opposite direction to gravity) are carried out in order to examine the influence of gravity on the coupled growth in a lg environment [l0, 11]. In the case of the downward U.D.S. using the current Bridgman method, the molten alloy must be confined between the crucible and the solid."

Jan 1, 2000