By In-Hyeok Choi

Currently, spent V2O5–WO3/TiO2 catalysts contribute significant amounts of solid waste following increasing levels of global demand. V2O5–WO3/ TiO2 catalysts usually consist of TiO2 anatase as a supporting oxide, vanadium as a catalytic agent, and other promoters such as tungsten, silicon, and calcium. Although vanadium is the main catalytic agent, a relatively high content of tungsten (WO3, 7–10 wt%) typically exists compared to vanadium (0.5–1.5 wt%). Considering the irreplaceable properties and industrial importance of tungsten, a feasible method for the recycling of spent V2O5–WO3/TiO2 catalyst should be established to utilize it as a secondary source. This paper presents a process to recover tungsten from spent V2O5–WO3/TiO2 catalyst. The processes proposed here involving roasting, decomposition using HCl, ammonia leaching, and crystallization. Within the process, ammonium paratungstate (71 wt% as WO3) is obtained as a final product. The total yield rate of tungsten from feedstock was found to be 96.3%.

By Jorge Alberto Soares Tenório, Denise Crocce Romano Espinosa, Luciana Harue Yamane

"The present work investigated the effect of inoculums volume on bioleaching to recover metals from printed circuit boards using Acidithiobacillus ferrooxidans-LR. Printed circuit boards from obsolete computers were mechanically processed by comminution followed by magnetic separation, and the obtained non-magnetic fraction was used in the bioleaching experiments. A shake-flask study was carried out on the non-magnetic fraction samples using a rotary shaker at 30°C, 170 rpm and different volumes of oxidized culture solution as inoculums (%v/v): 5, 10, 20, 30, 40, 50 e 60. The oxidized culture solution was prepared inoculating pre-adapted bacteria Acidithiobacillus ferrooxidans-LR (5%v/v) in 200mL T&K medium. Leaching in acidic ferric sulphate was also performerd. The analyzed parameters were pH, ferrous iron concentration and metals analysis (AAS). The results showed that using 10%v/v of inoculums were extracted 99,2% of copper and 60% of aluminum by bioleaching. Zinc, lead and tin extraction were not influenced by bacterial leaching and extractions rate were obtained by chemical leaching promoted by acid medium. Ferric iron leaching extracted less copper (35%) than bioleaching. SEM analysis shown surface difference between samples of non-magnetic fraction before treatment and after bioleaching, showing corrosion pits formed by the bacteria contact.IntroductionWaste of electrical and electronic equipments (WEEE) has been target of discussion due to environmental, political and economical issues involved. Around 17 million of computers are discarded annually in the world due to malfunctioning equipment or because technologies become obsolete [1,2]. In contrast, only the central processing unit (CPU) of computers weights around 3kg. From this data, it can be calculated that 51 million kilograms of CPU waste are discarded yearly. This calculation was performed considering only the CPUs, disregarding the cathode ray tubes and liquid crystal displays of monitors [3,4]. Because of the amount that has been accumulated, e-waste has become a global problem but also can be an alternative source to recover valuable materials [5,6]."

Jan 1, 2012

By I. D. Reznik

On blowing nickel matte in a converter without quartz, first the oxidation of metallic iron and a part of FeS occurs without evolving sulfur dioxide, the formed FeO dissolves in a sulphide smelt and form a homogeneous oxysulphide smelt. On further increasing the FeO content, the oxysulphide separates into 2 layers. Based on the laboratory investigation of FeO-(FeS+Fe°) - (Ni3S2+Ni°) ternary phase diagram we have identified the separation region at 1250°C. The boundaries of the separation region have the form of an arc and the composition of the separated oxysulphide layers is defined by the canodes. In the nickel or copper-nickel matte - silicacalcium oxide slag system at 1250°C three layers, namely sulphide, oxysulphide, and slag may be formed. A high slag basicity due to the presence of CaO can serve to enhance the activity of FeO; a low nickel content in the matte corresponds to a high concentration of FeS therein; FeO from slag and FeS from the matte form a homogeneous FeO-FeS solution, i.e. an oxysulphide layer. The investigation on the "Camebaks" apparatus and by the nuclear gamma-ray resonance spectroscopy method of the phase composition in a slowly cooled oxysulphide layer has shown the presence of four phases: wustite, troilite, ferronickel grains, and calcium oxide-silica inclusions. Knowledge of regularities in the oxysulphides formation makes it possible to use them in pyrometallurgy of nickel and cobalt or preventing their formation.

Jan 1, 1997

By Jong-Jip Kim, J. G. Byrne, W. Kim, In-Ok Shim, John E. Flinn

"Two rapid solidification processes for 304 stainless steel were studied: centrifugal atomization (CA) in a helium atmosphere and atomization by exposing argon-containing melt to vacuum (VGA). Positron annihilation and x-ray line broadening measurements of explosively consolidated monoliths were used to clarify microhardness measurements as a function of annealing temperature. Interesting differences in positron response between CA and VGA materials are ascribed to more carbide formation in the CA material than in the VGA material in the 600 0C range. In addition, hot isostatic pressing of the CA material was examined as to the relations between mechanical behavior, pore shape, and relative density. A variable stress concentration factor is introduced into the theory to allow for changing pore shape as relative density increases.IntroductionThere are many potential advantages of rapid solidification processing (RSP), such as a high degree of matrix supersaturation, finely dispersed microstructures, improved chemical homogeneity, and retention of metastable phases, which have been studied extensively. To consolidate rapidly solidified material which is in powder form into useful shapes often requires subjecting the material to elevated temperature for extended periods of time under mechanical forces, as in hot isostatic pressing or hot extrusion. In such cases, some of the characteristics of the rapid-cooling step can be strongly affected. An alternative is dynamic consolidation (1), for example by explosive forming, where the time frame at least is extremely short.In the present work, effects of the consolidation processes of hot isostatic pressing (HIP) and explosive forming in a die are examined. The particular material is 304 stainless steel. The characteristics of both RS and VGA 304 stainless-steel powders were described by Wright, Flinn, and Korth (2) earlier."

Jan 1, 1988

By Clemens Schmetterer, Patrick J. Masset

"The surface tension represents an important property for the modelling of high temperature processes. In this study the surface tension of two Al2O3 – CaO – SiO2 model slags and the influence of the admixture of 5 up to 30 wt.% FeO were studied. The surface tension measurements were carried out using the sessile drop technique on BN substrates under Ar atmosphere (10-6 atm O2) up to 1500 °C.IntroductionThe aim of VIRTUHCON1 is the virtualization of high temperature conversion processes, a task that requires thorough understanding of these processes. In many of these conversion processes slag plays an important role to control the properties of the product, to protect the reactor lining or simply as waste. Slag surface tension is one of the materials properties that is needed for the description of such processes, since it influences the interactions between the components in the reactor, e.g. at the slag – Fe interface in the blast furnace.Surface and interfacial tensions have thus received considerable attention in research, but the number of investigations in this particular pseudo-quaternary system is surprisingly low. Furthermore, the literature data are subject to different measurement conditions and techniques which complicates the data analysis and comparison.The slag atlas [1] offers a compilation of the available literature until 1986 (shown in Table I), but literature search has not revealed more recent studies of this system until now. For example, Elliott and Mounier [2] determined the surface tension of ACSF slags using the double tube maximum bubble pressure technique at 1200 °C. They kept their slags in contact with Cu-S-F mattes, and the slag therefore contained a certain amount of sulphur which acts as a surfactant and lowers the surface tension. The compositions of their slags were scattered over a wide composition range and they did not use a common ACS base mixture for their tests, either. The surface tension values vary between 417 and 446 mN/m, but due to the reasons just mentioned no trend in the measurements can be observed and the influence of FeO admixture on the surface tension cannot be deduced. Further information including the temperature dependence is available from Pavlov et al. [3], Ishchanov and Shushkov [4] and Murav’eva and Kaplun [5]; the diagram on page 446 in Ref. [1] has been drawn from these sources. Both positive and negative temperature coefficients are reported in these works. SiO2 is the only pure constituent that has a positive temperature coefficient [6], but a correlation of the temperature coefficient with the SiO2 content was not found to be conclusive."

Jan 1, 2011

By Y. W. Chung, W. I. Chia

"The interaction of water vapor with single crystal Ni3(Al,Ti) and polycrystalline Ni3Fe, with and without the presence of oxygen, has been studied with Auger electron spectroscopy, photoemission spectroscopy, thermal desorption and isotope exchange. Water dissociates to produce atomic hydrogen above 200 K on both Ni3(Al,Ti) and Ni3Fe surfaces. For Ni3(Al, Ti), the reaction is structure-sensitive. Pre-adsorbed or co-adsorbed oxygen on Ni3(Al,Ti) and Ni3Fe significantly suppresses hydrogen production due to water dissociation. This suppression process occurs more efficiently on Ni3Fe than Ni3(Al, Ti).IntroductionOrdered intermetallic compounds such as aluminides, silicides and titanides are very attractive for structural applications at high temperatures. This is because these intermetallics tend to form adherent oxides in oxidizing environments which protect the base materials from excessive oxidation and corrosion. In addition, they have low density, relatively high melting points and good high-temperature strength. However, the moisture in air severely embrittles many ordered intermetallics such as FeAl [1-3], Fe3A1 [4,5], C03Ti [6,7], (Co,Fe)) V [8], Ni3Si [9], Ni3(Si,Ti) [10], Ni3(AI,Mn) [Ill, and Ni3A1 [12-14], resulting in low 'ductility and brittle fracture at room temperature. Recent studies by Liu and coworkers (see review by George and Liu [15]) provide a qualitative description of the mechanism for this moisture-induced embrittlement. During elongation testing, cracks are formed, thus exposing fresh alloy surfaces. One or more active components of the alloy react with water vapor in the environment to produce atomic hydrogen which penetrates into crack tips and causes hydrogen embrittlement. This is similar to that proposed for moisture-induced embrittlement of aluminum alloys [16]."

Jan 1, 1996

By Maurizio Marezio Bertini

Successful treatment of contaminated sediments was achieved by sparging either 0.5 M NaOH solutions or distilled water with an SO2/O2 gas mixture. Metals such as Cu, Pb, Cr and Cd were successfully removed in a relatively short time. The effect of temperature and pH was investigated. Higher temperatures produced faster and higher recoveries with Pb and Cr more affected to temperature increase than Cu and Cd. The removal of copper, up to 50% percent, was achieved in alkaline solutions through the formation of copper sulfite complexes. The complete removal of metals such as Cu, Pb, Cr and Cd required that part of the treatment be carried out in acidic solutions. A preliminary cost analysis was carried out.

Jan 1, 2003

By Y. Ikeda

Typical electric appliances were dismantled into component pieces to study the recyclability of these discarded goods. Types and weight ratios of these component materials were investigated and characterized. The results showed that if they are dismantled properly, these goods could be classified into several groups of similar materials and/or structures, namely those consisting of single materials, metal-plastic combinations, metal-metal combinations and complex combinations of many different materials. By separating each combination into recyclable materials and isolating hazardous materials, it was found that the final waste for disposal could be reduced and the recycling efficiency could be improved markedly as compared to the conventional shredding method. The metal-metal combinations account for 60% by weight of the total metal contents in electric appliances, and therefore, it becomes important to segregate these metals. For the complex combinations, a process consisting of pyrolytic decomposition of plastic contaminants followed by smelting of the residue is proposed. It is anticipated that nearly zero-emission recycling of electric appliances will be achieved by applying this treatment process.

Jan 1, 1995

By Hu Meilong, Liu Lu, Bai Chenguang

Extracting perovskite from high titanium-bearing blast furnace (BF) slag is a green and potential method to recover the second titanium resource. The non-isothermal crystallization process of perovskite in synthesized high titanium-bearing slag was studied in situ by confocal scanning laser microscope (CSLM) with cooling rate of 20 K/min. The results showed that perovskite was the primary phase formed during cooling process in the titanium-bearing synthesized slag (TiO2=23%). Perovskite started to precipitate at 1719 K and finally presented an orthogonal straight lines morphology.

Jan 1, 2014

By Giulio R. Altoé, Sergio N. Monteiro, Ygor M. Moraes, Rômulo L. Loyola, Frederico M. Margem, Gabriel O. Glória

The tensile properties of DGEBA/TETA epoxy matrix composites reinforced with different amounts of PALF fibers were evaluated. Composites reinforced with up to 30% in volume of long, continuous and aligned PALF fibers were tested in an Instron machine at room temperature. The fracture was analyzed by SEM. This one revealed a weak fiber/matrix interface, which could be responsible for the performance of some properties. The results showed significant changes in the mechanical properties with the amount of PALF fibers.

Jan 1, 2015

By Shijie Wang

In pressure oxidation leaching of copper anode slimes, than 65% of the tellurium is m' cxtraoted during decopperizing. About l0- 15% of the selenium is also dissolved simultane¬ously by severe leach conditions. Current operation for the treatment of the leachate is to constantly recirculate the leach solution through a bed of copper turnings. The tellurium and sele¬nium are precipitated from the leach liquor as copper telluride and copper selenide and sepa¬rated from the solution by filtration. In order to improve the reaction efficiency and reduce the process cost, viz, minimize the copper addition, cut retention time, and reduce the energy consumption; a chemical reducing agent is studied and the cementation process tested in the laboratory. In this paper, the test results are presented and the process chemistry is discussed.

Jan 1, 2003

By Tatsuo Itou

Both sales volume of Aluminum Can and its recycling rate are remarkably increasing here in Japan. In 1993, recycled can volume was 11.78 billion cans ( 116,258 metric tons ) and its recycling rate 57.8 percent. We, MITSUBISHI MATERIALS CORPORATION. the leading manufacturer of aluminum can in Japan and our affiliated companies are very deeply involved in recycling used beverage cans ( U.B.C ) and recycling them back to can stock. In this paper. I would like to present the following; 1. Recent trend of beverage can consumption in Japan. 2. Trend of aluminum can and its recycling rate in Japan. 3. Future of aluminum can business in Japan.

Jan 1, 1995

By QIE Jun-mao, DONG Fang, DENG Hao-hua

The DIL402C thermal dilatometer and STA449C thermal analyzer were employed to test the linear expansion and contraction coefficient，CP and DSC curve of 304 stainless steel. The result showed that the linear expansion coefficient range was 20.9700×10-6～21.5712×10-6 and the linear contraction coefficient range was 21.2528×10-6～21.9471×10-6.The linear expansion and contraction coefficient were higher than other steel grade，so the 304 stainless steel belonged to the crack sensitive steel. Because of the crystal phase transformation occurred during the 1000~1400 ℃,the curve of CP fluctuated obviously and the defects of casting blank occurred easily. Chosen 1414℃ as the liquidus temperature of 304 stainless steel based on the analysis results of DSC. The curve of DSC was unsmooth during 1450～1100℃，the crystal phase transformation occurs and thermal stability of slab was inferior.When the initial solidified shell formed in this temperature range,the thickness of the shell would be nonuniform and the surface defects occurred more easily.

Jan 1, 2015

By Marco Olper

The Italian company Engitec Impianti has developed a new electrochemical technology for the treatment of Electric Arc Furnace (EAF) flue dust generated in steel mini-mills. This process is based on a new and completely different concept from the Waeltz technology applied at present and allows, due to its modular nature, for an erection on the steel producer's site. Engitec Impianti spent US $700.000 constructing a 500 t/y throughput pilot plant at Pittini Group's Ferriere Nord mini-mill in Osoppo, Italy in order to demonstrate the process capabilities and obtain the data for a commercial plant design. The paper describes the pilot plant performances and the engineering criteria for a commercial unit of 10.000 t/y throughput. The feasibility study demonstrates a pay-back period of 3 - 4 years for the commercial plant.

Jan 1, 1995

By Saynbaatar, Gangping Ma, Jianhua Fu, Qiqige, Jinghua Wang

The influence on the performance of foam concrete made by replacing cement with some industrial waste residues was researched in this paper. The result shows that the 7d and 28d compressive strength of foam concrete increases firstly and then decreases with the increasing amount of industrial waste residue. The proper added range is 10%-20% for steel slag, blast furnace slag and coal ash, but, 8% for desulfurized fly ash. With the proper adding ratio, the compressive strength of foam concrete always increased comparing with the pure cement foam concrete. When adding 48% of the compound industrial waste residues, the 28d compressive strength of the foam concrete reached the 2.9MPa which could match the pure cement foam concrete. The results indicates that there is a synergistic effect among the compound industrial waste residue, and this effect is benefit to improving the compressive strength of foam concrete.

Jan 1, 2015

By F. G. Prado

The technology for the extraction of zinc from zinc residues, such as zinc ashes, drosses and metallurgical flue dusts, by way of ammonium chloride solutions is well established, at least at the laboratory and bench scale levels. (3, 4) Zinc is soluble in ammonium chloride solutions in the form of zinc diammine chloride. Its solubility depends upon the concentrations and temperatures employed. The procedure and the equipment required are simple, and they can be applied either to small or large operations. As a by-product, zinc diammine chloride is produced with extremely low impurities in quantities which are stoichiometrically proportional to the zinc removed. The technology has been applied experimentally to galvanized steel residues. The dezincing results, including removal performance, energy and reagents required, and by-products are summarily presented in this paper.

Jan 1, 1992

By Peng Jianping, Feng Naixiang, Di Yuezhong, Wang Yaowu, Pan Xijuan

A vacuum silicon thermal reduction lithium process is developed in present work which used lithium hydroxide, alumina and calcium oxide as raw materials. The process contains two steps, which are that Li5AlO4 clinker is prepared in ambient environment, and that metal lithium is extracted from Li5AlO4 clinker with ferro-silicon alloy as reductant in vacuum. On the basis of thermodynamic analysis and investigative experiments, feasibility of this process is proved. The results show that Li5AlO4 can be generated by calcination lithium hydroxide and alumina, the burning loss is above 31% under the conditions of calicination temperature above 750℃ and time more than 90min. The main phases of calcination product are Li5AlO4 and CaO. When the calcination product is reduced by ferro-silicon alloy in vacuum, the lithium reduction ratio can be over 80% under the conditions of reduction temperature 1200℃ and reduction time 60min.

Jan 1, 2014

By Makiko Takahashi

A tool is being developed to predict and visualize the microstructural evolution of steels during quenching. This tool utilizes experimental data and reference data that are stored in a database to predict the microstructural development. The visualization tool animates qualitative representation of two- dimensional microstructure drawings as well as the quantitative volume fractions of phases present as a function of time. This is achieved by superimposing the Jominy End-Quench test results over the Continuous Cooling Transformation diagram of the alloy. The predicted microstructure is presented through the web browser to maximize the ease of use. In addition, a parallel coordinate system is used to aid in identifying similarities within the data set by presenting the large number of data at a glance. The results for 4140 steel that was quenched in a wide variety of quenchants will be presented to illustrate the prediction and visualization tools. Keywords: Quenching, Microstructure Prediction, Simulation, Data Visualization, Database, Applet, Animation

Jan 1, 2003

By Milton Manrique

The thermal decomposition of ilmenite concentrates in a non-transferred arc; thermal plasma flow reactor was investigated. The plasma torch was operated using argon-helium and argon-nitrogen mixtures as plasma gases. The effect of power, feed rate and particle size was studied. Products were characterized by XRD, SEM, TEM and ICP techniques. Free energy minimization plots were used to predict the thermodynamic behavior of the system under different operating conditions. The results of this investigation showed a significant segregation process where titanium-rich products are collected in the reactor, while iron-rich products are collected in the quenching box and filter. The average size of the product is in the sub- micron range. Titanium nitride was formed and condensed in the reactor zone when using an argon-nitrogen mixture as the plasma gas.

Jan 1, 1998

By Nolberto Moreno Borjas

This paper outlines the detrimental impact that unblended ore can have on the Ni and Co recoveries and the ore slurry density with real data from the Caron low-pressure ammonia leaching process for the Punta Gorda ore. The author briefly discusses the reason for the decrease in slurry density that the process experiences. The lower metal recoveries in the process that are caused by the unblended ore chemical characteristics and variations are shown with a data base statistical analysis drawn from the results obtained from a pilot test, designed with different ore bypassed from the normal process flow and a similar ore from a similar metallurgical treatment. Keywords: Ni-Co Laterite, Caron Process, Ore Blending, Slurry Density, Metal Recovery

Jan 1, 2004