By Xiyun Yang, Hui Xu, Xichang Shi, Xiang Xiao

"Rod-like magnetite particles were prepared by precipitation of iron salts with urea under the induction of magnetic field. Temperature and initial Fe3+/Fe2+ ratio have a significant effect on the composition of the product. Magnetite particles change from spherical into rod shape in the presence of a 0.35 T magnetic field, The addition of a small amount of spherical seeds increases the rod-like magnetite particles yield. The seeds are prepared by aging ferrous and ferric solution with sodium hydroxide as precipitator. The aspect ratio of the rod is controlled by varying the volume ratio of seed to iron salt.IntroductionMagnetite, an important member of magnetic materials, has attracted a lot of attentions for its super magnetic properties. The rod-like magnetite particles have high anisotropy and coercive force as well as super magnetic properties compared to other shapes, and are widely used as high magnetic density media, magnetic devices and microwave materials [1-4]. Recent studies have found that magnetic field can direct magnetite growing along easy magnetization axis to get one-dimension particles [5-6]. Chen et al. [7] synthesized single crystalline nanorod magnetite under magnetic field. Wang et al. [8] discovered that magnetite grew along easy-magnetization directions under 0.35T magnetic field. Vereda et al. [9-1 O] found that magnetic field had a dramatic effect on the morphology, inducing the aggregates to line along one direction to form rodlike particles.At present, most of the synthesis methods reported in the literature result in a low yield of rod particles and the aspect ratio are difficult to control. Recently, we developed a seed-mediated growth approach to making rod-like particles in an aqueous solution. The spherical magnetite generated by oxidation serves as a seed. These seeds are then added to a solution containing iron salt and urea, and provide nucleation sites for magnetite rod growth."

Jan 1, 2011

By Tengfei Qi, Liqiang Fan, Huiqing Tang

A new method to process the oolitic high phosphorus iron ore for phosphorus removal has been proposed in this research. It is an integration of direct reduction and melting separation with carbon-containing pellets prepared using biomass char. Experiments of direct reduction were preceded using a tubular furnace and three parameters were investigated and they were reduction temperature, biomass char adding ratio(molar ratio of carbon to oxygen） and atmosphere. Results show that the optimum condition is of reduction temperature is 1373 K, biomass adding ratio 0.9, PCO2/PCO 1.0 and reduction time 15~25 min. Under this condition, the reduced briquettes with a metallization of 75.0~80.0 % and a residual carbon content of 0.69~0.11 wt% could be obtained. Subsequent melting separation experiments were conducted using a Si-Mo high temperature furnace. Results show metal with phosphorus content of about 0.4 mass% could be obtained from the reduced sample.

Jan 1, 2015

By William Petruk

A fully automatic image analysis system that consists of a microprobe, an energy dispersive x-ray analyzer, and an image analyzer was developed at CANME:I' to determine mineral behaviour that affects beneficiation. The interlacing between the instruments permits automatic identification and characterization of minerals in samples of unbroken ore pieces and of mill products. Different types of information are obtained for minerals in samples of unbroken ore pieces than in samples of mill products, and are used differently. For unbroken ore pieces size distributions are determined for discrete mineral grains to predict a grind at which they might be liberated, and other measurements are Irade to predict the percentage of mineral that occurs as nonrecoverable grains. For mill products the minerals are analysed to determine percentages that (1) are free, (2) are likely to be recovered in concentrates, (3) are likely to be lost to tailings, and (4) could be liberated with regrinding. The image analysis data for mill products are processed by a mineral-metals balance program to determine the distributions of free and unliberated mineral grains at each point in a concentrator, pilot plant or bench test. For samples containing trace minerals, such as gold, an automatic search technique is used to scan the entire area of the polished section for the trace mineral grains. The identified trace mineral grains are characterized with regard to size, liberation, and other properties.

Jan 1, 1988

By Kim Verbeken, Evelien Van de Steene, Marc Verhaege, Jeriffa De Clercq

"AbstractThe industry is confronted with stricter discharge levels and an increasing awareness to avoid toxic waste (such as heavy metal containing sludge obtained in physicochemical water treatment) and recover valuable metals. This can be realized by ion exchange or by electrodeposition. Both techniques however show an optimum concentration range to efficiently remove and/or recover metals: electrolysis can recover the metal in its metallic form but suffers from low efficiency when applied to diluted solutions, whereas ion exchange can only be applied economically in the low ppm range.A combination of ion exchange followed by electrodeposition was applied to an industrial wastewater. The strong acidic ion exchange resin was stripped with H2SO4 giving a solution of 9g/L nickel. From this solution, nickel was electrodeposited in an ammonia buffer on a Ti-mesh cathode with high current efficiency. It is shown that organic compounds (surfactants, brighteners, …) present in the industrial wastewater do not influence the recovery process.IntroductionAlmost all rinse waters emerging from metal plating plants are generated during the washing operation of plated materials. These solutions with low metal content must either be recycled within the process or be discarded to the surface water after decreasing their metal content to acceptable levels determined by the local environmental regulations, which become more and more stringent. Today, the most commonly used practice is a physico-chemical treatment (precipitation) and a resin post treatment to meet the standards. A more sustainable approach should use a technology to recover efficiently the metal or metal salt without the production of sludge and the effluent should be consistent with environmental regulations."

Jan 1, 2008

By M. I. Novgorodova

An overview of the systems Au-Ag and Au-Cu is given. The nature and levels of concentration of various elements occurring with native gold is reviewed. The examples cited are mainly from the USSR. The lack of homogeneity within naturally occurring Au-Ag solid solutions is examined.

Jan 1, 1991

By Sebastião Ribeiro, Leonardo Carneiro Sardinha, Alline Sardinha Cordeiro Morais, Carlos Maurício Fontes Vieira, Sergio Neves Monteiro

The glass tube of spent fluorescent lamps is contaminated with mercury, which might be a serious hazard in the case of conventional recycling by melting with other glasses. A possible solution could be its incorporation into a clay body to fabricate common fired ceramics such as bricks and tiles. The objective of this work is to characterize a type of fluorescent lamp glass waste to be incorporated into a clayey ceramic. The characterization was performed in terms of wettability tests to evaluate the interaction between the surface of the clayey ceramic and glass waste as a function of the firing temperature. The results showed that the contact angle decreased with increasing temperature, reaching a value of 79°, at a temperature of 1100°C, but not sufficient to completely wet the ceramic. However, compatible chemical composition and reduction of porosity by the flow of soft glass waste between the clay particles favor the consolidation of the ceramics structure above 900°C.

Jan 1, 2015

By John E. Litz

The Denver Process is a chemical/metallurgical process for treating radioactive or mixed wastes by extraction and concentration of the radioactive and/or hazardous component(s). The process was developed at bench scale, evaluated at pilot scale, and will be implemented at full scale to remediate a low-level radioactive sludge. Six unit operations comprise the process: feed handling, leaching, solvent extraction, electrodeposition, precipitation, and tailing preparation. Unit operation design may be modified to tailor the process for varying feed stock composition. Radioactive or mixed waste is reacted with aggressive reagents in an aqueous phase, solubilizing targeted components. These components are then selectively extracted and concentrated in subsequent steps. Waste solids and solution exit the process as non-hazardous non¬radioactive waste. Dehydration of aqueous waste by submerged combustion eliminates aqueous discharge.

Jan 1, 1994

By Thomas M. Harris

To avoid the escalating cost of disposal of metals-containing wastewater and residues, new wastewater treatments will focus on the recovery of the metals. A combination of ion exchange and electrowinning can produce water suitable for discharge and relatively pure metals. The use of a chelating resin can enhance the selectivity of both the removal process and the elution of metals from the resin. A new, simple method of preparing a variety of chelating resins is being developed. The materials produced by this method exhibit interesting, as well as potentially useful, elution behavior. The performance of one test resin is described.

Jan 1, 1992

By Hong Ro Lee, Seang Suk Cho, Byung Sun Chun, Chang Whan Won

"The preparation of Al203-SiC-TiC composite powders was studied by SHS process using silica (source of Si02) powder instead of Si which is expensive. And, aluminum powder was used as reducing agent of silica and charcoal activated was used as carbon source. Effects of the molar ratio in raw material mixtures and compaction pressure and initial temperature of reactant on the products and combustion process were studied. The most important variable affecting the synthesis of Al203-SiC-TiC was the molar ratio of carbon. The combustion reaction generated in powder state without preheating. But the unreactants exist in the product on all molar ratio. When the preheating temperature is over 400 °C, the combustion reaction was able to be generated in pellet state. Without preheating, the combustion reaction was possible by Ti02 addition. The optimum condition in this system was the molar ratio of Si02:Ti02:Al:C=2.5:0.5:4:3.1. INTRODUCTIONCeramics have demonstrated a capability as a cutting tool, especially in competition with WC-Co cermets (ceramic-metal composites) as inserts for metal turning and milling operation. The advantage of ceramics compared with carbides is retention of high hardness, strength, and chemical inertness to temperatures in excess of 1000 ·c . This allows use of the ceramics at much higher machining speeds than can be tolerated by carbides. However, the ceramics have lower toughness than the carbide materials, and have only been used successfully in the limited operations of turning and milling. There are several classes of cutting tools. The addition of TiC or PSZ, or both, and reinforcement with SiC overcame the poor fracture toughness and thermal-shock resistance that limited Al203 use in the past [1]."

Jan 1, 1998

By Kazuyoshi Shimakage, Shinji Hirai, Kenji Wada

"An amorphous zirconium oxide coating was prepared by the sol-gel process using zirconium tetra-n-butoxide on the surface of aluminum to improve the corrosion resistance to salt, acid and alkaline attacks. The coating films formed on the smooth aluminum substrates under UV-irradiation indicated an excellent corrosion resistance for salt, acid and alkaline attack tests. For example, the corroded area of coating film in salt attack test for 3600ks in the order of sol-gel coating· film< chromate film <boehmite film, and the sol-gel coating film had the best corrosion resistance. The coating film prepared on the coarse aluminum substrate by a boiling treatment after heat treatment at 573K also had greater corrosion resistance, and a water-avid surface appeared a contact angle of approximately 3°.IntroductionAs given in a previous paper1; a composite film consisting of a porous layer of anodically grown aluminum oxide filled with amorphous zirconium oxide and an amorphous zirconium oxide coating layer deposited thereon via the sol-gel process utilizing the dip-coating technique, was prepared to improve the alkaline corrosion resistance of aluminum. The alkaline corrosion resistance of these composite films was increased in the range of 24 to 50 times those of conventional anodic oxide films anodized in sulfuric acid. As a result, it was proved that heat treatment at 573K after dip-coating was an important process to .remove organic component from gel film and to accelerate the densification of coating layer. Furthermore, the effect of ultraviolet (UV) irradiation at ambient temperature on the densification of coating layer was also examined to lower the heat-treatment temperature2.Then, a sol-gel film prepared by UV irradiation at ambient temperature indicated that alkaline corrosion resistance of aluminum was superior in the range of 2.4 times to 2. 6 times that of the conventional composite film heated at 573K."

Jan 1, 2000

By A. V. Tarasov, V. M. Paretsky

"The knowledge of the true phase composition of the liquid slag is a very important problem, mastering of which grants the possibilities for the scientifically founded choosing of the decoppering method of the autogenous smelting slags. The investigation using different methods of the phase composition of the flash quenched autogenous copper melt's slags has shown, that the most effective method of the slags' decoppering during smelting with the white matte production is the flotation of the recrystallized slags. In this work the authors posed the problem to realize the slags quenching with the rates similar to those, which are used in the modem investigations devoted to the flash quenching of the ironcontaining alloys, with the subsequent study of the quenched samples using the Mossbauer spectroscopy methods in order to establish the connection between the liquid slag's structure and the metals losses with the slag."

Jan 1, 2000

By I. B. Scorzelli

The aim of this paper is to make a detailed mineralogical characterization of a typical brazilian xenotime and zircon from the Pitinga Mine using SEMIEDS techniques, On the other hand, superficial pretreatments with HCI, HN03 and HF were done to evaluate the modifications on surface compositions and the morphology of the particles for flotation purposes, The studies showed that both xenotime and zircon present very small inclusions of thorite; zircon is strongly metamictizated given rise to malacon. The HF pretreatment deeply affected the morphology of the particles as well as the surface properties in relation to flotation.

Jan 1, 1996

By Linfeng Zhou, Rong Sun, Guanghui Li, Zhiwei Peng, Tao Jiang

The effects of microwave roasting on separation of rhenium (Re) and molybdenum (Mo) from a molybdenite concentrate have been investigated based on evaluation of the heating characteristics of the concentrate in the microwave field. The results show that a variety of operating variables, namely microwave power, sample weight, sample geometry, roasting temperature, roasting time and atmosphere significantly impact on the volatilization rates of Re and Mo. The optimum conditions for Re-Mo separation are microwave power 1300 W, sample weight 20 g, sample geometry pellets, temperature 600 oC, time 1.5 h, and atmosphere 20%O2. Under these experimental conditions, the volatilization rate of Re reaches 88.12%, while that of Mo is just 5.15%. Microwave-assisted roasting provides an alternative route to separating Re and Mo from molybdenite concentrate.

Jan 1, 2016

By Katsunori Yamaguchi

A new technique for the removal of tramp-elements from steel scrap has been required from the viewpoint of saving energy and protection of environment. In order to obtain fundamental information on the removal of copper, tin and zinc from molten iron, the extraction method by using of phase separation in the liquid Fe-Pb-C system was investigated at 1453K. A mixture of iron, lead and carbon melted in a carbon crucible separates into two phases of lead and iron containing carbon. The compositions on the miscibility gap in the Fe-Pb-C system are 95.4%Fe-4.5%C-0.1 %Pb and 99.9%Pb-0.I%Fe. The distribution ratios of copper, tin and zinc between the lead and the iron phases, Lx [mass%X in molten Pb]/(mass%X in molten Fe), are 2.2, 2.2 and 1.4, respectively. Seventy percent of copper and tin from iron scrap can be eliminated with comparable lead addition. Gold, silver and palladium are enriched in the lead rich phase, on the contrary platinum and rhodium are more distributed to the iron rich phase than to the lead phase.

Jan 1, 2003

By Michael Stelter

Lead alloys are a typical material for anodes in technical electrowinning processes. The life time of those anodes differs from 2 years to more than 5 years in tankhouse practice depending on the type of alloy, the mechanical damaging and last but not least the chemical corrosion in the electrolyte. Different types of alloys, such as PbSb, PbCa, PbAg, PbSnCa or PbAgCa have been developed and used in the past, their rate of corrosion being more or less a philosophic discussion. Comparable investigations on the corrosion behavior in dependence of the concentrations of alloying metals, the grain structure and the mechanical and thermal treatment during production have not been conducted before. In the last years the Institute for Nonferrous Metallurgy and Purest Materials of the TU Bergakademie Freiberg investigated the corrosion behavior of the typical lead alloys for metal electrowinning under comparable conditions. Correlations between different alloys, mechanical treatments like rolling or thermal treatment like annealing to the rate of corrosion were made, leading to the conclusion that grain structure and grain size are of eminent importance for the rate of corrosion in technical electrolytes. From these results new and optimized lead alloy anodes can be produced with an increase in life time of the factor 3 ? 5. The optimized lifetime in terms of corrosion stability can not protect from mechanical damaging in tankhouse practice, but with a careful practice the increase in lifetime can save a lot of money and problems.

Jan 1, 2006

By cheng Peng-fei, TANG Hai-yan, guo Xiao-chen, LI Jing-she, Liang Yong-cang, Zhao Baojun

The origin and evolution of non-metallic inclusions for Al-killed casing steel during EAF-LFVD- CC process were studied by industrial tracer experiments. The formations of Al2O3 and MgO·Al2O3 micro- and macro-inclusions from ladle slag were analyzed by theoretical calculations. The results show that micro-inclusions were formed during deoxidation and temperature decreasing in the process of casting, most of the macro-inclusions come from entrapped ladle and mold slags. In addition, most of the Al2O3 formed were modified into 12CaO·7Al2O3 and 3CaO·Al2O3 inclusions which are liquid at steelmaking temperature. MnS cannot be fully modified to CaS and it was only wrapped outside the alumina or calcium aluminate in the form of (Ca,Mn)S with the amount of Ca-Si wire fed during the test.

Jan 1, 2016

By P. T. Velu, R. G. Reddy

"The use of emf measurements to derive classical thermochemical data has been in use for many years. The reaction associated with electrochemical process is harnessed in a galvanic cell and energy involved measured in terms of electromotive force. The property requirements of sensor electrodes used differ for various aqueous, molten salt and solid electrolyte systems. The electrodes for molten salt electrolytes need special care for construction. This paper describes the studies carried out using an Ag/ AgCI reference electrode. This electrode was used to measure the solubility of compounds in molten salt electrolytes. The results obtained using this electrode are in excellent agreement with the values from chemical analysis method.I. IntroductionThe technique of obtaining a metal from its oxides by electrolysis is more than a century old process now. In these processes, it has been well established that for halide electrolytes, only the dissolved oxides are available for the dissociation at the electrode to release the metal during electrolysis. Therefore, the solubility of metallic oxides in the molten salt electrolytes is an important parameter which determines the economical and technical viability of these processes. The widely used molten salts systems in halides are fluorides and chlorides. The fluoride electrolyte system is used in our present study.The viability of obtaining aluminum alloys by in-situ electrochemical processing has been outlined in our earlier publications[1-8]. Studies on the solubility of various alloying element compounds is a part of our ongoing research efforts for the direct production of Al-Li alloys. As mentioned above, the solubility of lithium oxide and lithium carbonate compounds in molten fluoride electrolyte system have studied using EMF technique. The change in potential of the molten electrolyte was measured by a working electrode against the reference electrode with the addition of lithium compound."

Jan 1, 1997

By R. Vasant Kumar

Measurement and control of trace elements in molten metal are often critical in order to achieve optimum production, refining, alloying or recycling. Solid electrolyte sensors for monitoring oxygen and very recently for hydrogen have made major impact in the metal industry. It has not proved straightforward to develop solid electrolyte sensors for many other elements that can be industrially applied in metal production. Novel self-tuning chemical sensors have been developed by the authors that may open up new technological opportunities. Three such examples will be presented in this paper: (i) a self-selecting oxygen-sulfur dual sensor using a composite beta-alumina/zirconia solid electrolyte; (ii) a copper sensor for liquid matte based upon cusicon solid electrolyte operating in a current reversal mode; and (iii) an aluminium sensor on solid NaCl containing channels of molten NaAlCl4 electrolyte formed by electrochemical charging in molten zinc.

Jan 1, 2006

By H. Ikeda

The new Onahama N0.3 tankhouse was put into operation early in 1973. This new tankhouse, which has a capacity of 90,000 metric ton cathode per year, is distinct in many important respects from conventional tankhouses. The major objectives in design were to simplify the construction and ope- ration for reduction of the costs for labor, interest and depreciation and also to reduce the copper inventory in the tankhouse by the use of conti- nuously-cast anodes. As a result, the investment cost was decreased by approximately 30% and the inventory cost by approximately 600, while the production per unit area of the tankhouse was increased by 80 - 100% as compared with the existing conventional-type tankhouses at Onahama. By abolition of cell inspection and maximum mechanization of materials handling the labor cost was decreased by as much as 80%. On the other hand, the new system has some disadvantages, such as increase in anode scrap ratio and increased cost of anode casting. The No.3 tankhouse system is, however, still at its starting point, while conventional methods have been continuously improved over the past years of operation. It is expected that the innovational ideas behind this system will serve as bases for a more efficient electrolytic refining system in future.

Jan 1, 1976

By Akira Yazawa

In the field of pyrometallurgy, the equilibrium evaluation has recently become easy by use of thermodynamic software, but it is strongly desired to estimate the amounts of non-equilibrium minor components to simulate practical processes. However, simple physico-chemical technique can not be applied to evaluate practical non-equilibrium components for many reasons. As an engineering solution for postulated equilibrium system, the activity coefficient is modified and introduced as the simulation parameter referred to as the "adjustment coefficient." This modified thermodynamic calculations were adopted to various sulfide roasting processes where many solid phases are participating and the system is not necessarily in equilibrium. Successful simulation was realized by assigning suitable adjustment coefficients for minor components which form a pseudo solid solution in the calcine. Some examples from sulfation roasting and dearsenizing roasting were discussed. In the smelting system, the loss of copper in slag is caused by equilibrium and non- equilibrium reasons, that is, chemical dissolution and entrainment of copper in slag. The total copper content of slag was simulated by use of the adjustment coefficient for entrained copper.

Jan 1, 1998