By M. C. Flemings, P. J. Ahearn

Dendvite morphology of unidirectionally solidified Sn-12 pct Bi alloy was determined with the aid of X-ray and macroetch techniques. Columnar growth direction (growth direction of primary arms) in this alloy is [110]; secondary arms grow in the [lii], [111), and [112] directions. Interstices between [112] dendrite arms fill in during early stages of solidification so that well-defined (110) planes are seen in the final structure (parallel to the heat-flozo direction). Similarly, interslices betweex the [111] secondary arrlls fill in to form (112) planes, and interstices between [1111 ] arms fill in to form (112) planes. DENDRITE morphology in alloys is conveniently studied in unidirectionally solidified castings. In this type of solidification, heat is extracted from a single chill surface of the casting while other surfaces are insulated. Solidification progresses from the chill and results in cast grains that are columnar with the long axis of the grain perpendicular to the chill. Dendrite morphology is conveniently studied by examination of etched surfaces parallel and perpendicular to the chill, as previously described.'" Experimental studies on the growth direction for tin are in general agreement. The major growth direction is [110]:-' although this is altered somewhat by supercooling. In one study, tin dendrites pulled from a supercooled melt had a growth orientation 12 deg away from the [110] direction toward the [002] direction.' This orientation could be changed back to the [110] or close to the [110] direction by changing the tempera- ture gradient in the melt. In a study using autoradio-graphic techniques, (111) directions were shown to be directions of preferred growth in addition to the [110) direction.7 PROCEDURE The samples employed in this study were cut from 12 pct Bi-88 pct Sn castings, 1.5 in. in diam and 3.5 in. tall. The casting procedure consisted of heating the charge to 390°C and then pouring the molten alloy directly into a gypsum sleeve mounted on a massive copper chill. Specimens were cut from the ingot, mounted, polished, and etched with Taffs reagent [FeC13 .6H2O, 2 g; HC1, 5 cu cm;H20, 30 cu cm; CzHaOH (95 pct), 60 cu cm].' The dendritic pattern was clearly visible after etching. Photomicrographs at about 8 and 35 times were taken on surfaces parallel and perpendicular to the chill. Laue back-reflection patterns were obtained from three different columnar grains in a singIe polished face 2 in. from the chill. The cut face was polished and positioned in the beam of a Laue camera, so that diffraction occurred from a single dendritic grain. The resulting diffraction pattern was interpreted to determine crystal log raphic orientation in relation to the heat-flow direction and in relation to microstruc-ture of the given grain. RESULTS Fig. 1 shows a horizontal and vertical section of the columnar structure, at low magnification. Light regions are rich in tin, and darker regions tin-poor; the primary phase is tin-rich a phase. The two sections shown were taken orthogonally from the same metallographic specimen. It is readily seen from Fig. 1 that the dendrites have

Jan 1, 1968

By A. D. Zunkel, A. H. Larson

Equilibrium arsenic contents of Pb-As alloys in contact with PbO-As2O3 slags containing less than 30 mol pct As2O3, were determined at 650°, 700: and 750 C in an inert at?rzosphere. In this temperature range, the arsenic content of the alloy increased with increasing temperature in the single-phase liquid slag region and decreased with increasing temperature in the two-phase slag region and the single-phase solid-solution slag region. The PbO-As2O3 phase diagram below 22 mol pct As2O3 was determined by thertrzal analysis and by application of a log ?As2O3/?PbO vS log XAs2o3 /x3pbO plot determined from the equilibrium actiuity data. The resulting phase diagram was not well-defined since the eutectic temperature was not detected in the thermal analysis experiments, although a region of terminal solid solubility of As2O3 was found. Results from the phase diagram determination are compared with an existing diagram in the literature. THIS experimental investigation is an extension of a study by the authors1 on the slag-metal equilibria in the systems concerned with commercial lead refining processes such as softening and dross fuming. The first part of this investigation was a study of the slag-metal equilibria in the Pb-PbO-Sb2O3 system. The only experimental work previously done on the Pb-PbO-As2O3 system was by Pelzel2,3 in which the phase diagram for the PbO-As2O3 system was determined below 50 wt pct As2O3 and the equilibrium constant for the reaction 3Pb + As2O3 + 3PbO + 2As was determined as a function of temperature. No slag-metal equilibrium data have been determined. It is due to the scarcity of information regarding the Pb-PbO-As203 system that this work was undertaken. This paper describes the determination of the slag-metal equilibria in the Pb-PbO-As203 system by equilibrating Pb-As alloys with PbO-As2O3 slags in an inert atmosphere, the effect of 1 wt pct additions of bismuth and copper on the slag-metal equilibria, and the PbO-As2O3 phase diagram both by thermal analysis and the use of the slag-metal equilibria data. EXPERIMENTAL Materials. The materials used in this investigation were analytical reagent-grade and assayed as follows: 1) 99.8 pct PbO (0.014 pct insoluble in CHJCOOH, 0.02 pct not precipitated by H2S, 0.1 pct CaO, and 0.08 pct SiO2); 2) 99.95 pct As2O3; 3) 99.99 pct Pb; 4) 99.0 pct As; 5) 99.99 pct Cu; and 6) 99.97 pct Bi. Room-temperature X-ray patterns revealed no detectable impurities in any of these materials. Apparatus for Equilibrium and Thermal-Analysis Determinations. The resistance-heated crucible furnace used in this investigation employed nichrome elements and was mounted so that it could be raised to surround the reaction tube during each experiment and, subsequently, lowered. A schematic diagram of the apparatus is shown in Fig. 1. Each charge was heated in a 3+-in.-OD by 31/2-in.-high 416 stainless-steel crucible placed in a 41/4-in.-1D by 18-in.-long fused-silica reaction tube which was closed at one end. On a shoulder around the crucible was placed a 3: -in.-OD by 12-in.-long open-end fused-silica condenser tube. The open end of the reaction tube was covered by a water-cooled brass cap with ports for 1) admitting an inert atmosphere to the system through a stopcock, 2) introducing a stainless-steel, motor-driven, paddle stirrer into the crucible, 3) evacuating the system with a mechanical vacuum pump, and 4) sampling the melt with Vycor sampling tubes. The brass cap was fitted to the open end of the reaction tube with a silicone gasket and collar clamp. The furnace temperature was controlled by a Barber-Coleman Capacitrol controller and a chromel-alumel thermocouple. Due to the corrosiveness of the melt, the controlling thermocouple also served as the measuring thermocouple. The temperature of the melt was calibrated against the controller temperature and was checked periodically during each test with a Vycor-enclosed calibrated chromel-alumel thermocouple. The temperature measurement and control can be considered accurate to ±3°C. Procedure. The charge placed in the crucible for each experiment consisted of 1000 g of Pb-As alloy and 300 g of PbO-As2O3 slag. The crucible was then placed in the reaction tube, the condenser tube was placed on the shoulder of the crucible, the silicone gasket and brass cap were fitted on the open end of the reaction tube, and the entire system was evacuated and filled with argon ten times. After the last flushing, a positive argon pressure of 1 psig was impressed on the system. The furnace was then raised to sur-

Jan 1, 1968

By Shiro Ban-ya, John Chipman

The effects of many alloying eletnents on the acticity coefficient of sulfur in liquid iron have-been studied by the equilibriutn in the reaction Sfin Fe) + Hz = HzS at 1550°C'. Results are expressed in terms of a concentration variable for a nonmetallic or for a substitutional metallic solute. Activity coefficient of sulfur, defined as increased by B, Al, C, Si, Ge, Sn, P, As, Sb, Mo, W, Co, and PI. It is decreased by Cu,Au, Ti. Zr, V, h'b, Ta, Cr, ,23n, and Ni. Irulues oj. the interaction coejficient 0i = 6 In are labulated. The same interactions are expressed also in terms of atom fraction and of weight percent. The thermodynamic properties of sulfur in liquid iron have been fairly well established. Our recent paper1 reported new determinations of activity coefficient up an atom fraction of 0.12 and equations based on a careful review of all published data. The effects of alloying elements on the activity of sulfur have been studied by several investigators,2"11 especially by Morris and Williams for silicon,' by Morris and Buehl for carbon,~ and by Sherman and Chipman for manganese. phosphorus, and al~minum.~ However, the effects of some important alloying elements remain to be determined. The purpose of this investigation was to determine the effects of many alloying elements on the activity of sulfur in Fe-S-j ternary systems. EXPERIMENTAL METHOD This study was based on experimental determination of equilibrium in the reaction at 1550°C: The same apparatus and procedure as described in our previous paper have been retained, and the same corrections were applied for dissociation of H2S. The alumina crucibles used in the experiments consisted of four separate compartments. In a given experimental run. kach of three alumina crucibles held four different samples of about 3 g each which reached equilibrium in the same gas atmosphere and temperature. The charges were made up of electrolytic iron, pure iron sulfide, and desired alloying elements, which were pure metal or master alloys made in the laboratory. The weighed samples were held for 4 to 12 hr in the prepared atmosphere at 1550°C. They were then low- ered to be cooled as quickly as possible. The quenched metal beads were crushed to avoid the errors of segregation in the ingot. The sulfur content was determined gravimetrically and alloy content by appropriate chemical analysis. CALCULATIONS The apparent equilibrium constants of Eq. [I] are expressed as follows from the corrected gas ratios and sulfur concentrations: The term K" is the observed equilibrium constant in any given ternary solution, K' is the value for the Fe-S binary solution. and the limiting value of K' in the infinitely dilute solution is designated by K, which is the true equilibrium constant in Eq. [I]. In the thermodynamic treatment of nonmetallic elements in a metallic solution, it has been suggested1' that the lattice ratio has certain advantages over other variables to express the concentration of solute. In interstitial solid solutions the lattice ratio zj is proportional to the ratio of filled interstitial sites to those which remain unfilled. The equations derived for the activity of the solute using zj as the concentration variable are found also to be applicable to liquid solutions containing nonmetallic solutes when the nonmetal is treated as if it were interstitial. For this purpose we adopt the following definitions: The quantity vj which is negative for interstitial solutes is taken as -1 for nonmetallic and +1 for metallic solutes. For purposes of calculation however ; j may be assigned a value which results in a linear relation such as shown in Figs. 1 to 15. The activity coefficient of sulfur, Qs, and equilibrium constant. K(z). are defined as follows: According to a Taylor series expansion. the logarithm of the activity coefficient of sulfur in Fe-S-j ternary system is: However, the value of 6 In */6zi remains constant through a broad range of dilute solutions and the terms of higher order are negligibly small. As a consequence, Eq. [6] is simplified as follows:

Jan 1, 1970

By R. D. West

Miscible displacenzent recovers all oil in the area contacted by the injected .fluid, whereas water or immiscible gas drives usually leave substantial amounts of oil as residual. However, the Door mobility ratios associated with a gas-driven miscible displacement cause the sweep pattern efficiency to be much lower than that obtained with water flooding. One way in which the sweep eficiency in a miscible displacement process can be increased is by decreasing the mobility behind the flooding front. This can be achieved by injecting water along with the gas which drives the miscible slug. This water reduces the relative permeability to gas in this area and thus lowers the total mobility. The main operating conditions for the simultaneous injection -vrocess are that a zone of gas exists between the miscible slug and the leading edge of the water and that a su,@cient amount of gas be injected with the water to form the pas volume which is being left in the water zone. Laboratory model studies have shown that the ultimate sweep pattern efficiency can be as high as 90 per cent for a five-spot flooding system. If gar alone is used as the driving medium an ultimate sweep-out efficiency of about 60 per cent would be obtained in the same system. I INTRODUCTION The miscible displacement processes are a step towards total oil recovery. Conventional gas or water drives usually leave 25 to 5.0 per cent of the oil as residual in the swept portion of the reservoir. This residual can be eliminated if the oil is driven by a fluid with which it is miscible. At some reservoir conditions natural gas will become miscible with the oil. This is the "high pressure gas process".' More often, the oil does not contain enough light hydrocarbons to cause the gas to become miscible with the oil at reasonable pressures. In these cases a small band of fluid which is miscible both with the oil and gas must be kept between them2. Less than 2 per cent of the reservoir volume of the slug material is needed to keep the displacement miscible. Both processes work in the same manner, recovering all of the oil in the portion of the reservoir contacted by the injected fluids. The only difference is the manner in which the miscibility between the oil and the injected gas is obtained. Previous publications have contained detailed descriptions of these processes.1,2,3,4 However, total displacement of the oil in the swept region does not guarantee an efficient recovery process. The amount of oil to be recovered is also determined by the fraction of the reservoir contacted by the flood. This fraction is largely determined by the mobilities of the fluids. (The fluid mobility is the permeability of the rock to that fluid divided by the fluid's viscosity, k/p). This. dependence of the fraction swept on the mobility ratio has been shown in previous studies. Fig. 1 shows the ultimate fraction swept in a five-spot system as a function of the mobility ratio. The small drawings show the location of the areas left unswept for two different mobility ratios. The ultimate fraction of the reservoir swept is here considered to be attained when the producing stream contains less than 5 per cent oil at reservoir conditions. THE GAS-DRIVEN MISCIBLE DISPLACEMENT Since there is no oil left in the swept region after miscible displacement the mobility in this region is very high. It is often 50 times the mobility in the unswept regions. This means that the fraction of the reservoir contacted by the injected fluid will be less for a gas-driven miscible displacement than for a conventional water or gas drive. For a five-spot injection system, water would contact the entire reservoir volume, and the low pressure gas would contact about 90 per cent of this volume, while a gas-driven miscible displacement would only contact about 65 per cent of the reservoir. This poor sweep efficiency often offsets the benefits obtained through miscible displacement. Fig. 2 shows what the recovery curves for the three processes might look like for a five-spot system. The curves show the fraction of the in-place oil recovered as a function of reser-

By Robert H. Richards

The adaptation of European methods of concentrating ores to suit the conditions of this country has followed the lines that simplify machinery, diminish labor and increase capacity. Noteworthy instances are the substitution of hydraulic classifiers for the last one or two trommels in the series, and the substitution of a distributing-tank for the slimes in the place of the Spitzkasten. The question may be fairly asked, At what point do losses become serious in consequence of these changes? It is to study this question that the investigation herein described has been undertaken. After the losses are located and the methods of stopping them are pointed out, it will then lie with the individual mill to decide whether or not the plans proposed will save suficient value to warrant their adoption. In the discussion of sorting followed by sizing, as the terms are used in this paper, me have to deal with the preparation of slimes by the Spitzkasten for subsequent washing upon the slime-table. The Spitzkasten, or pointed box, is an inverted hollow pyramid, generally of wood, usually with four faces or sides coming together in a point below. The sides can have, according to Rittinger, a minimum angle of slope of 50" with the horizontal. The feed-water carrying fine slimes (less than 0.01 inch, or 0.25 mm. in diameter) for treatment is fed at one end and carefully distributed over the whole width. The outlet is over the opposite end. The water-current passes direct from inlet to outlet, and has usually been regarded as a surface-layer pass-

Jan 1, 1898

By A. J. M. Ross, R. G. Wayland

The Homestake mine is situated in Whitewood mining district, in the northern Black Hills of South Dakota, in the city of Lead, Lawrence County. The entire property, comprising 557 lode claims with a total area of 3343 acres, is held under United States Patent. The older claims were 300 by 1500 ft. under local regulations, the newer ones 600 by 1500 ft. The Homestake was discovered April 9, 1876, by Moses and Fred Manuel, and Jake Harney, who were drawn into the northern hills, from the Custer placer district, by news of the discovery of rich placer deposits in Deadwood Gulch. They located a number of additional lode claims and, in a short time, the whole country was covered with locations. The Manuel brothers built an arrastre the following winter and took out $5000. The next year the Homestake lode was sold to Senator George Hearst and associates, who organized the Homestake Mining Co. Other companies were formed to exploit other groups of claims and at one time fivc companies were operating on this deposit, the Father DeSmet, the Dead-wood-Terra, the Caledonia, the Highland, and the Homestake Mining Co. These companies, however, have been merged into the Homestake Mining Company. The first stamp mill, known as the "Eighty Mill," commenced operation on July 12, 1878, and production has been nearly continuous since that time. Geology The orebodies of the Homestake are found in an intensely folded and altered bed of dolomitic limestone occurring in a series of ancient rocks believed to be of Archean age, belonging to the Keewatin series. The Keewatin series is estimated to be 20,000 ft. thick and is made up essentially of quartz mica schists, garnet schists, quartzites, slates, and some green schists, probably derived from basic igneous rocks. The dolomitic limestone bed has a thickness of 40 to 60 ft. The great width of ore, as much as 400 ft. in some of the stopes, is due to the folding, wherein the bed is repeated. In other cases the bed is stretched and pinched out. Dikes of Tertiary rhyolite cut across the country and, in places, sills overlie the

Jan 1, 1925

By J. Kent Smith

THE object of this investigation was to ascertain the effect of varying percentages of beryllium upon pure copper and the properties of the resultant alloys in their softest condition, the effect of heat hardening on them, and the extents to which these properties could be augmented by different combinations of heat hardening and cold rolling. The data compiled in this paper represent partial results of continuing work done by the writer during the years 1930 and 1931, which was a continuation of the unpublished ground work incepted in the laboratory of the Beryllium Corporation of America by H. B. Pulsifer in the year 1926. A short bibliography on beryllium alloys is appended to this paper. It has, of course, long been known that copper subjected to cold work is hardened and strengthened to a considerable extent, furthermore it had been qualitatively noted in previous experiments that copper-beryllium alloys seemed to take on hardness and strength as the result of cold work at a greater rate even than does plain copper. It was decided therefore to endeavor quantitatively to determine such rate of increase, as also the relative increases by combinations of cold working and heat hardening. The results are summarized in Tables 3, 4 and 5. A preliminary series of experiments had indicated that by an exposure to the heat of 575° F. for 2 1/2 hr. age-hardening of a 2.50 per cent beryllium-copper alloy took place. Slab ingots of nine different beryllium-copper alloys were prepared under identical conditions by means of the addition of a previously prepared 12.5 per cent beryllium-copper alloy to well melted and deoxidized pure copper. The ingots were then reduced by hot rolling to 12 gage (about 0.080 in.). These strips were heated to 1450° F. and quenched in cold water, and thus brought to their softest condition. (See Table 1.) Strips were next "precipitation-hardened" by reheating to a definite temperature. Similar strips to those itemized in Table 1 (which had been quenched from 1450° F.) were reheated for varying periods of time at 575° F. The hardness figures show that a metastable condition, of which the range of stability is dependent entirely upon time at the given temperature, begins to be noted in copper samples containing as little as 0.85 per cent beryllium. It is extremely noticeable in samples containing

Jan 1, 1932

By R. L. Loofbourow

Trends in the metal mining industry were definitely down in 1954. With a record in 1953 of $1.8 billion output, the last year dropped to $1.5 billion, the lowest value since 1950. The decrease in iron ore production alone accounted for at least 10 pct of the decline. PROBABLY more than any previous year, political debates of 1954 marked a new high for the mining industry. Lead and zinc prices gave forth with minor rallies producing no real improvements. An anticipated drop in copper prices never came to be. Early in the year arguments for more free trade versus tariffs to restrict imports were voiced eloquently by Charles P. Taft, president, Committee for a National Trade Policy, and Andrew Fletcher, president, St. Joseph Lead Co.

Jan 3, 1955

By E. Marburg

Most ingots complete solidification vertically rather than transversely. This conclusion is based on complete solidification patterns of big-end-up and big-end-down ingots developed from dumped and split ingots. New mechanisms for segregation in ingots are proposed. Internal soundness in ingots is found to depend upon adequate width of vertical core. A LTHOUGH it has long been recognized that the A internal soundness of ingots is principally been recognizedthatthedependent on the process of solidification, knowledge of this process is still only fragmentary. The mechanisms causing the several types of segregation in ingots, which mechanisms are necessarily related to the solidification process, are not well understood. In absence of a better conception of the solidification process, it seems hardly surprising that mold design varies widely. Guiding principles for mold design are needed. At stake in the improvement of ingot quality are not only improved properties of steel but also appreciably higher yields of sound steel, which would considerably decrease manufacturing costs. In the present study, following a general description of the several types of segregation in ingots, Fig. 1, complete solidification patterns of a big-endup and a big-end-down ingot, including the zones of accelerated solidification, have been reconstructed. In both ingots, a core of vertical solidification extends from the base cone to the hot-top junction. Based on the finding that ingots complete solidification vertically rather than transversely, as has been previously assumed, new mechanisms for segregation in ingots are proposed. Internal soundness in ingots is found to depend upon the width of the vertical core, which in turn depends principally upon the width to height (w/h) ratio of the ingot. Solidification patterns of ingots are of three general types: 1—those in which vertical solidification does not reach the top, 2—those in which vertical solidification just reaches the top of the ingot, and 3—those in which vertical solidification reaches the top some time before transverse solidification would reach the middle of the ingot, so that a vertical core of definite width at the top of the ingot is developed. Axial defects vary characteristically with the solidification pattern. Examples of ingots of each type are presented. Dumped ingot data reported by Nelson' have been used in developing families of curves of transverse and vertical solidification, and in deriving the effect of the w/h ratio upon the solidification pattern. Photographs of many ingots split at Homestead and at Duquesne Works, United States Steel CO., as well as those published by the British Iron and Steel Institute,' have been studied and analyzed. In the interest of brevity, only typical ingots of each type or classification from the above sources have been reproduced. Segregation in Ingots Segregation in ingots falls into three principal classifications: 1—lamellar segregation, as revealed in sulphur prints (Figs. 2 and 3); 2—zone segregation, or broad variations in composition; and 3— interdendritic, or microsegregation. The last class, of minor importance, is not considered here. When liquid metal cools, according to the theory of differential or selective solidification,2 metal of relatively high purity selectively solidifies first. Liquid segregates (principally carbon, phosphorus,

Jan 1, 1954

By J. L. Perry

FOR many years, you and your fellow members of the American Institute of Mining and Metallurgical Engineers have devotedly and ably applied yourselves to the art of making iron and steel. having foremost in your minds the conservation of raw materials, suitable and efficient facilities, economical processes, and improved quality of product. For the past three strenuous years you have contributed wholeheartedly to meeting the problems of increased production. You have conducted scientific and technical investigations and research, recommended experiments. and gathered all the available and valuable information possible to gain the desired objectives. You have had many obstacles and difficulties to overcome. In the early days of your organization, there was some lack of co-operation from the industry itself-perhaps, for example, some failure to recognize the mutual advantages of free exchange of experiences and information. But regardless of any hindrances, you have made many and valuable contribution which have tended to make iron and steel manufacture leas of an art and more of a science.

Jan 1, 1944

By E. P: Mathewson

Discussion of the paper of E. P: Mathewson, presented at the Butte Meeting, August, 1913, and printed in Bulletin No. 78, June, 1913, pp. 1033 to 1037. PROF. JOSEPH W. RICHARDS, South Bethlehem, Pa. :-Speaking to the question of the development of the basic lining, and speaking from a somewhat considerable study of the history of the process, ,I think Mr. Mathewson's conclusion (in the last paragraph. of his paper) is perfectly justified and is very fairly stated. Messrs. Smith and Pierce worked at developing their process for many years ; copper men had been trying their level best to get away from the silica lining of the converters and had uniformly failed. On one page of Mr. Mathewson's paper we read that at the old works of the Anaconda Company, at Anaconda, the experiments " were abandoned on the score of cost and lack of advantages." On the next page, after describing the work of Messrs. Smith and Pierce, we have the statement that the Anaconda Company lined a shell with mangnesite brick and the ?results were excellent." I think Mr. Mathewson's statement that to Smith and Pierce belongs the credit of developing a long-discredited idea, is correct. C. D,. DEMOND, Anaconda, Mont. :-It seems to me that the matter of the lining is important; my impression is that they used tar in their basic lining and that did not seem to be at all successful at Anaconda, but silicate of soda was very successful. MR. RICHARDS :-I did not know that they- had abandoned the use of tar. MR. DEMOND :-I said I thought that was the practice. At Anaconda that was not at all satisfactory in the basic linings. Silicate of soda was very satisfactory and is so.

Jan 11, 1913

By Henry Howe

1. Introduction.-This paper is based in large part on the examination of two rings, shown in section in Fig. 4 to 15, cut from an eroded 14-in. (35.56-cm.) gun, liner, and containing, according to Booth, Garrett, & Blair: Carbon, 0.380 per cent.; manganese, 0.655 per cent.; nickel, 2.810 per cent.; vanadium, 0; chromium, a few hundredths of 1 per cent.; tungsten, 0; molybdenum, 0. These rings were received from Admiral Joseph Strauss, then Chief of Ordnance, U. S. Navy, through the kindness of Mr. Hudson Maxim, Chairman of the Committee on Ordnance and Explosives,, of the U. S. Naval Consulting Board.

Jan 2, 1918

By Carl Benedicks

IT is well known by every one who has had to deal with boiler tubes that these are often seriously affected by a sort of corrosion, occurring as a local pitting, that frequently causes a perforation of the tube in a rather short time. The characteristic appearance of this corrosion is shown in Fig. 1. A very similar corrosion occurs in condenser tubes (Fig. 2).1 A study of the microstructure or local chemical composition of the metal (iron; 70 :30 brass) fails to reveal any cause for this pitting. Of course one might possibly assume the starting point-to be some oxide particle, causing an electrolytic local action, but this in no way explains the continued corrosion, progressing even when the assumed oxide particle must have disappeared. By the excellent work done by the Corrosion Research Committee of the Institute of Metals, and communicated, in October, 1923, to the Institution of Engineers and Shipbuilders in Newcastle-on-tyne, stress was laid on the fact that a content of entangled air has a very obnoxious effect. In the following correspondence, Sir George Goodwin stated that "engineers have, for a long time past, regarded air as the big enemy to be fought against in all questions of corrosion"2 and Kenneth Fraser pointed out that the most vital point is "the avoidance or removal of possibly the chief cause of present day corrosion, i. e. entrapped air and gases brought out of solution."' In their reply, however, the authors state that they had "never for a moment believed that entangled air was responsible for the beginnings of corrosion, and express the opinion that the gradual liberation of air could not account for localized corrosion."4 On consulting the many textbooks on corrosion, as that

Jan 4, 1925

By C. H. Mathewson

COPPER and the copper-base solid solutions readily form twin crystals when plastically deformed at a suitably elevated temperature or annealed after cold deformation. In fact, no feature of the microstructure of these materials is more prominent or characteristic than these straight-sided bands or simple lines of division which sometimes come from groups of thin polysynthetic lamellae, penetrating part way or wholly through the parent grain substance, but often divide the grain into a few or perhaps only two crystallographically related parts. Nearly always the bands as seen in the usual microscopic examination of a specimen come into vivid contrast with the adjacent crystalline material owing to the inherent difference in orientation. Bands which under special conditions of orientation cannot be seen with vertically incident light are often visible under oblique illumination and, when this fails, contrasting effects usually may be obtained by using polarized light. There is no longer any doubt that these synthetic banded structures obtained in the ordinary course of working and annealing are due to twinning of the spinel type which was observed long ago in a number of metals crystallizing in the isometric system.1 It has been customary in metallurgical literature to designate these synthetic twins, which grow into prominence during an annealing process, as "annealing twins" without regard to the actual mode of their formation, which is, indeed, obscure and with scant recognition of the fact that prior deformation is essential, no twins having been observed in metal of known unstrained history. This is questionable; especially in view of. the fact that in a number of metals and minerals, reorientation into the twin configuration is known to occur as a result of a simple shearing mechanism along the recognized twinning planes and the

Jan 1, 1930

By P. B. Baxendell

The performance of a water-drive reservoir having a gas cap depends primarily on the movement of the gar-oil and oil-water contacts. The movement of the contacts during production depends in turn on fluid withdrawals and how the reservoir pressure changes as fluids are produced from the reservoir; that is, on how effectively the aquifer maintains pressure by replacing withdrawals. inasmuch as pressure changes, fluid withdrawals, contact positions, and produced gas-oil and oil-water ratios are interdependent, the analysis and prediction of the performance of a reservoir produced in a given way must take into account this interdependence throughout depletion. This paper presents an analysis which, within the limitations of the assumptions made, yields an engineering approach to predicting future performance based on reservoir pressure and production history. The most significant assumption is the method of extrapolation of future gas-oil and water-oil ratios. The extrapolation procedure smoothly increases both ratios to preselected values as the remaining oil column undergoes a specified decrease in thickness. This preselection is made on the busis of previous field experience in depletion of similar reservoirs under similar conditions. For computing future performance a vdumebic balance L combined with the differential equation defining pressure distribution in the aquifer to obtain positions of water-oil and gas-oil contacts. From these positions are extrapolated produced water-oil and gas-oil ratios. Reservoir performance can be investigated when oil production rates are dependent upon various factors including the performance of the reservoir itself. Examples of practical application of the procedure are included. INTRODUCTION To predict performance of water-drive reservoirs with gas caps and thin oil columns, it is necessary to describe the motions of the fluids within the reservoir during the entire production period to depletion. These motions depend on the pressure changes and on the withdrawal of oil, gas and water. Production of oil from the oil zone primarily causes water to move in to take its place; production of gas from the cap tends to cause oil to migrate into its place. In addition, the volumes of oil and gas remaining in the reservoir depend on changes in the pressure, since a decrease in pressure causes fluid expansion, gas liberation and oil shrinkage. A method of relating the future pressure to total withdrawals is used to describe the motions of fluids within the reservoir under conditions arising in possible modes of production. The analysis is based on two relationships and will reduce the problem to one amenable to digital computation. The first of these concerns the dependence of the pressure distribution in the entire aquifer furnishing the water drive upon the total reservoir withdrawals. This dependence is dictated by the permeability distribution and the extent of the aquifer; at present, such information is most readily obtained from the performance history by means of the resistancecapacitance reservoir analyzer. The second relation involves withdrawals, pressure in the reservoir, and movement of oil, gas, and water within the reservoir. The analysis is subject to certain simplifying assumptions that are necessary to permit solution of the problem. A comparison of the methods of this paper with those presently practiced is pertinent. One method of analysis is to use the reservoir analyzer to predict reservoir behavior based on aquifer characteristics determined from production history. Inasmuch as the total withdrawal rate depends upon the gas-oil and water-oil ratios, which depend in turn upon, among other things, the positions of the gas-oil and water-oil contacts, these ratios must be assumed in advance. In this paper these ratios are, instead, related to the computed positions of gas-oil and water-oil contacts. Thus, our method can be applied to problems in which the oil production rate is limited by produced gas-oil ratio, or to problems in which it is desired to determine the variable gas injection rate that will maintain the gas-oil or water-oil contact stationary. These problems cannot be worked satisfactorily on the analyzer. Another method presently used is based on a paper by Hurst.' Since his procedure is dependent upon using the solution of the heat flow equation, which requires constant permeability within the aquifer, and our procedure recognizes variations of permeability in

By F. D. Patchen

Changes in the properties of partland cement upon the addition of fine-ground silica are discussed. Data were collected from formulations cured for periods up to 60 days at temperatures varying from 180" to 350°F. Compressive strengths, permeabilities and thickening times are compared. It is demonstrated that addition of find-ground silica in proper proportion results in a hydrated cement with superior properties above 230°F; i.e., early compressive strengths are higher and increase with additional curing, permeabilities are significantly lnrver and thickening times are increased. X-ray analysis of hydrated cement samples have been used to determine more fully the complex chemistry of these systems. Dicalcium silicate alpha-hydrate was found in all neat cements cured above 260°F. A 10 weight per cent silica addition produced a maximum amount of this phase. Xonotlite and tobermorite have been identified as hydration products at 320°F in systems containing 35 or more weight per cent silica. Formation of these components appears to be primarily responsible for the gain in strength and reduction of permeability observed after the addition of silica. INTRODUCTION For several years it has been recognized that loss of compressive strength occurs when portland cement is cured at a temperature above 250°F. This phenomenon has been called "strength retrogression". More recently it has been recognized that increased permeability usually is associated with decreased compressive strength at these temperatures. At curing temperatures above 300°F, these factors reach serious proportions. A compressive strength loss of 50 per cent between curing times of 24 hours and 14 days has been reported,' and permeabilities as high as 10 md have been measured in neat cements cured at 320°F for seven days.' Earlier investigators,' although unsuccessful in eliminating strength retrogression, stated ". . . .it appears possible that by the proper selection of additives for cement, strength loss with age at high temperatures can be either eliminated or considerably lessened". One solution suggested was the use of a pozzolanic material, hydrated lime, and a retarder. Menze15 in 1934 discovered that portland cement containing finely divided silica possessed high compressive strengths when the curing temperature was 350°F. The use of such a composition is now an established practice in the manufacture of steam-cured cement blocks. It is reasonable to assume that the same beneficial effect can be used advantageously in high-temperature oilwell cementing operations. Ludwig first mentioned the use of sand for this purpose. Later, a portland cement containing moderate additions of silica flour and retarded with CMHEC, a cellulose derivative. was recommended for high-temperature application." These formulations have been successfully employed in the field."'" This paper presents the results of a research program to test the efficacy of finely ground silica in increasing the compressive strength and reducing the permeability of oilwell cement compositions containing portland cement. Included also are X-ray diffraction patterns of powdered samples which have been used to determine some of the important chemical reactions occurring in these systems. LABORATORY PROCEDURES AND MATERIALS All compressive-strength test specimens were prepared and cured from a slurry in accordance with API RP 10B, with two modifications. A final curing pressure of 5,000 psi was maintained for a one- or three-day period; but, for further curing, pressures were reduced to the vapor pressure of water at the curing temperature. Also, the water content was varied in samples containing silica to maintain the slurry viscosity within a range of 5 to 15 poise as measured on a consistometer. Test specimens at 180°T were cured in a water bath at atmospheric pressure. At higher temperatures the specimens were cured in a steam-jacketed high-pressure curing vessel at 5,000 psi for a one- or three-day period. cubes cured for longer periods were removed from the pressure-curing vessel after 24 hours, sealed in small bombs containing water and placed in an aging oven.

By A. A. Smith, J. S. Smart

THE controlled amounts of phosphorus, arsenic, sulphur or selenium found in commercial coppers perform a variety of highly useful functions. Indeed, a large segment of modem copper technology is essentially dependent upon the presence of one or more of these elements. Consequently, the literature contains many references to their effects but the scope is broad and has been only partly covered. New data are presented herewith directed toward a better understanding of the basic behavior of these elements in copper, with particular emphasis on the composition range 0 to 0.05 per cent. These data are a part of a general program of research on the effects of impurities on the properties of oxygen-bearing and oxygen-free copper, other portions of which have been reported previously.1-2-3 Schematically, the behavior of individual elements is determined from measurements of conductivity and softening temperature,1, 2 and the binary alloys employed are synthesized from high-purity copper in order to eliminate interference from the effects of extraneous impurities. Alloys of selected composition were first prepared in the oxygen-free form by continuously casting the melts in the form of 3/8-in. diameter rod. Oxygen was added subsequently to portions of the alloys, either by remelting or by diffusion at 850°C. from a surface scale. Test wires were drawn one B. and S. number per pass, using four 30-min. 600°C. anneals at o.3125, 0.257, o.204 and o.162 in., and a final cold reduction of 95 per cent t0 0.081 in. Oxygen-bearing slugs made by remelting were hot-rolled to 5/16 in., drawn to 0.162 in., annealed for 30 min. at 600°C. and cold-drawn 95 per cent to 0.081inch. The alloys containing phosphorus, having been compounded very early in the program, were prepared in the form of 5/16-in. rod, and processed to wire with only the last three intermediate anneals listed above, all of these having been conducted in commercial nitrogen. In addition, the conductivity anneals on these alloys were also performed in the same atmosphere, and the small amount of oxygen present as an impurity in the gas resulted in some loss of accuracy at temperatures of 700° to 800°C., as will be shown later. Subsequently, the anneals for all oxygen-free alloys were conducted in hydrogen to prevent oxidation, and purified nitrogen was employed only for oxygen-bearing samples. All conductivity anneals were of one hour duration followed by a rapid quench in 10 per cent H2SO4. EFFECT OF PHOSPHORUS The widespread use of phosphorus as a deoxidant has resulted in universal appreci-

Jan 1, 1945

By E. C. Truesdale

A FEW years ago H. M. Cyr, working in the Research Laboratories of The New Jersey Zinc Co., produced a few pounds of zinc1 of such purity that no other elements were detected in it by spectrographic analysis, using the facilities then available. This zinc contained less than one ten-thousandth of one per cent of metallic impurities.2 During the decade that followed upon the laboratory production of this "spectro-graphically pure" zinc, commercial developments brought about the production of large tonnages of zinc of purity exceeding 99.99 per cent, and today zinc of 99.999 per cent purity is produced and marketed as "chemically pure" zinc. Typical analyses of present supplies of high-purity zinc are given in Table 1. TABLE 1.-Typical Analyses Percentage by Weight Sum of Zinc Pb, Fe, Pb Fe Cd Al Cd Special High Grades 0.007b 0.005b 0.0056 none 0.0106 C.P. (chemically pure) <0.0002 0.0005° 0.000052 S.P. (spectrographically pure).. <0.0002d <0.00005d a A.S.T.M. Standard Specification for Special High Grade Slab Zinc (A.S.T.M. Designation: B 6-37). b Maximum. c Fe chemically determined. Pb and Cd are spectrographically determined. d Differences between composition of C.P. and S.P. zinc are discussed later in this paper. The availability of commercial tonnages of special high-grade zinc has been the basis for the development of the zinc-base die-casting alloy industry which, in the year 1936, consumed one-eighth of the zinc used in the United States for all purposes. This and the C.P. and S.P. grades have given impetus to scientific investigations into the properties of pure

Jan 1, 1939

By Robert Anderson

ROUGHLY, a crack in a casting may be considered, for the moment, to be due to fracture of the alloy resulting from the stress set up by the contraction in volume on passing from the liquid to the solid state. Cracks may be external or surface, internal or deep-seated, or incipient or so-called strain cracks. Draws may appear as depressions, unevenness, and "pinching in" of the surface of a casting. Roughly, draws are due to contraction in volume and are governed largely by the same factors as cracks. A casting may be cracked, however, without being drawn. Shrinkage is a foundry term; it connotes the contraction in volume of a metal or alloy on passing from the liquid to the solid state. Pattern-makers&apos; shrinkage is the total contraction in volume (including liquid, solidification, and solid shrinkage) that occurs when an alloy is poured into a mold. The contraction in volume of aluminum is one of the principal factors affecting the occurrence of cracks, as will be shown later, and the question of shrinkage and its control requires careful study in any treatment of cracking in castings. In the case of, sand and die castings, cracks have been attributed to a number of causes, but in the case of most light aluminum alloys, they are due to the large contraction in volume on freezing and the lack of its regulation or control. The most important factors are: (1) Contraction in volume; (2) composition of alloy; (3) quality of melting charge; (4) design of casting; (5) method of molding; (6) hardness of ramming; (7) method of gating; (8) hardness and characteristics of cores; (9) chills; (10) risers; (11) melting temperatures; (12) furnace used for melting; (13) pouring tempera-tures; (14) inclusions in alloys; (15) hot shortness of alloys; and (16) physical properties of alloys at high temperatures. Of these, the first, second, third, and eleventh to sixteenth involve ascertainable metallurgical facts; the remainder are largely matters of opinion, judgment and technical knowledge of men experienced in the production of castings.

Jan 10, 1921

By Enrique Hauser

FiRE-damp is a mixture of methane with other inert gases or combustible gases. The inert gases in question are carbonic acid, water vapor, nitrogen, etc. The combustible gases are hydrogen, ethane, etc. The study of the properties of fire-damp, therefore, becomes a study of the properties of methane and the influence on its properties of the different gases we have mentioned. Characteristic Properties of Methane 1. Respirability.—Methane being a paraffin is characterized by its weak chemical affinities. Prom the physiological point of view one could substitute it for nitrogen of the air at least momentarily, without experiencing any difficulty in breathing the mixture consisting of 21 per cent. 02 + 79 per cent. CHI. I have tried this on myself, making the gas exhaled from the lungs burn subsequently in a Bunsen burner.&apos; From the chemical point of view, this weak affinity permits the gas to be burned in certain circumstances with hydrogen and oxide of carbon in an oxygenated mixture, with the result that the last two gases achieve only a fractional combustion. This practice has been utilized with success in the methods of analysis which I have perfected and which I describe later in this paper. 2. Retardation of Flashing Point.—A characteristic property of methane is its retardation of flashing point, noted by Davy in 1816 and studied by Mallard and Le Chatelier in 1883.2 Taffanel and Le Floch have recently confirmed these results.8 Let us recall the nature of this retardation: When a mixture of combustible gases with air or with oxygen is

Jan 1, 1916