By Jianjun Wang, Jiaqing Peng, Lingen Luo, Zhenbang li, Yinghe Lin

Copper removal from ferronickel by FeS has been exploring studied. It is found that the decopperizing agent FeS makes the copper removal in ferronickel effectively. The effects of FeS addition amount, carbon content in ferronickel and experimental temperature were investigated. The results showed that the removal rate of copper in ferronickel increased with the amount of FeS increasing. When the dosage of FeS is 20% (mass percentage)，the removal rate of copper can reach higher than 11%. The rate of copper removal rises with the amount of carbon content increasing in ferronickel. When the amount of carbon content is 1.86%, the removal ratio of copper is 41.3%. Higher experimental temperature promotes the copper removal reaction in certain extent. The flux is acidity and weak oxidative can also promote the reaction of copper removal.

Jan 1, 2015

By Shu Bin, Lin Chen, Tian-zu Yang, Wei-feng Liu, Wan-da Bin

"Antimony resources are rich in china, its reserves and productions are ranking the first in the world. The Chinese antimony mineral resources are mainly existed in the form of three types, such as stibnite, antimony-gold ores andjamesonite. The antimonial dust that produced from lead smelting process is an important secondary antimony resource. The different process that was adopted to extract antimony depends on the different raw materials. The process of blast furnace volatilization smelting is mainly used to treat stibnite and antimony-gold ores. But jamesonite is treated by the process of roasting-sintering-blast furnace smelting. And antimonial dust is treated in the reverberatory furnace. Many new technologies that are applied in these traditional antimony smelting processes play important roles, such as deleading agent, antimony white production, air-oxidation method, direct-blowing method, bath smelting technology, and so on. At the same time, the development of antimony smelting technology in china is prospected according to the requirement of the state environmental protection.IntroductionThere are five countries that produce antimony in the world, such as china, Tajikistan, Bolivia, Russia, and South africa, but China is the largest country of antimony production in the world. In the world, the antimony productions of 2008, 2009, and 2010 are 182,000 tons, 154,000 tons, and 167.000 tons respectively, but Chinese antimony productions are 166.000 tons, 140,000 tons, and 150,000 tons respectively. So Chinese antimony production was accounted for more than 89% of the world in 2010. It indicates that China have irreplaceable advantages in antimony resource and production all over the world."

Jan 1, 2013

By Jie Li, Zhongliang Tian, Xun Hu, Kai Zhang, Yanqing Lai, Hongliang Zhang

The Al-Sc Alloys show many advanced properties for a wide range of engineering applications. But the metal Sc must be added into the metal Al in the form of the Al-Sc master alloy, which is usually produced by the thermal reduction process. In this paper, the decomposition voltages of Sc2O3 and Al2O3 in Na3AlF6-K3AlF6-AlF3 melt were calculated based on the Nernst equation. And the Al-Sc master alloy was prepared in the melt at 950°C by electrolysis. The results show that the Al-Sc master alloy can be prepared by the co-deposition of Sc3+ and Al3+ at the cathode if the concentration ratio of Sc2O3 to Al2O3 in the melt is more than 2:1 under the condition of the aluminum electrolysis. SEM and ICP analysis of the product indicates that the Al-Sc master alloy is made of the phase Al and the phase Al3Sc.

Jan 1, 2016

By Xin Zhang, Xu Zhang, Hao Bai, Ning Li

Organic Rankine Cycle (ORC) is an effective technology for low-grade waste heat power generation. In this paper, the thermal-dynamic performance of ORC system, in which low-temperature waste heat (from 40-140oC) is used as heat source, was evaluated with software RefProp8.0. The result indicates that in the range of low temperature, the working fluids like R601, R601a, R600a, R141b, R245fa and R245ca have better thermal performance. Furthermore, pilot-scale experiment using R245fa as working fluid was conducted, which validated the operation of the system for low-grade waste heat recovery. Finally, the economic feasibility of ORC has been analyzed for an ORC system using the waste heat from quenching water of blast furnace slag (80oC). According to the analysis, the project is reasonable in economy because the recovery period of investment is less than 4.2 years and environment-friendly since the CO2 emissions can be reduced by almost 43650.68t annually.

Jan 1, 2016

By Bora Derin

This work deals with the recovery of valuable metals from the ancient copper smelting slags located in Küre-Turkey. In this process, copper and cobalt were recovered in metallic form and/or as their compounds, whereas iron was recovered as magnetic oxide or pigment. Abrasive grit material was produced using reduced final slag. The process stages involved carbothermal reduction in a DC arc furnace, granulation, leaching, chemical precipitation, selective sulfidizing roasting and product preparations. In this paper, the process stages were described as theoretically and experimentally whereas slag and products were characterized in detail.

Jan 1, 2003

By G. L. Watt

Fine sized titanium diboride (TiB2) powders have been synthesized in a thermal plasma reactor. Precursor for the synthesis were rutile, boron oxide, and methane. The effect of plasma gas type, precursor ratio, and input power on the synthesis was studied. The produced powders were characterized by X-ray diffraction and chemical analysis. The purified powders were CIP'd, HIP'd, sintered and characterized for porosity, hardness, and microstructure and the results compared with a commercially available TiB2 powder sample.

Jan 1, 1995

By V. A. Luganav

The behavior of arsenopyrite under heating has been studied by many scientists. It has been already established that under heating at more than 650°c and without air access the arsenopyrite dissociates with the formation of one atom arsenic. Under vacuum the dissociation process begins at 5500C with the formation of elemental arsenic. The residue of dissociation process contains pyrrhotite and throilite. In the presence of pyrite, arsenopyrite dissociates under lower temperature and with a higher velocity than without it. The industrial realization of fool scale processing of arsenic bearing raw materials is possible only by the use of standard equipment and oxygen containing blast. In this view the paper presents the results of the study on the effect of oxygen in the gaseous phase and its addition into the charge of pyrite in the process of arsenopyrite decomposition. Thermodynamic analyses showed that under thermal processing of arsenopyrite in the presence of pyrite and limited quantities of oxygen in the gaseous phase the formation of arsenic sulfides is possible according to the following reactions:

Jan 1, 2003

By Kenneth N. Ham

Hydrometallurgy covers a wide spectrum of areas and its knowledge base is enlarged and enhanced by contributions from many other fields. Dissolution of metals and alloys in aqueous media will be used to illustrate how rich the field of metal extraction can be. Comprehensive understanding of the fundamentals of metal and alloy dissolution in aqueous systems requires creative application of thermodynamic principles, solutions chemistry, ligand complexation theory, electrochemistry, transport phenomena and heterogeneous kinetics. In addition, recent developments in instrumentation in the fields of interfacial phenomena and corrosion have tremendously advanced the field of metal extraction in aqueous system. The close relationship between metal extraction in aqueous systems and various physicochemical phenomena occurring in corrosion and interfacial systems will be discussed and illustrated with examples.

Jan 1, 2002

By Tianzu Yang, Weifeng Liu, Lin Chen, Qingkai Xiao, DUCHAO ZHANG

To solve the problem of low leaching ratio of direct gold cyanide leaching from arsenical refractory gold concentrate, this paper proposed a matte smelting process for gold enrichment in low grade copper matte. The effects of copper content in the mixed material, ratio change in slag type, smelting temperature and reaction time on recovery rate of gold and copper were investigated. The experimental results indicated that the recovery rate of gold increased with the increase of copper content in the mixed materials, temperature and reaction time. It was also noted that the recovery rate of gold and copper were respectively 98.16% and 96.39% when the addition of copper content in the mixed material was 3%, slag type of CaO/SiO2 and FeO/SiO2 were 0.6 and 0.9 in 1250°C and the time of reaction was 40min. Most of the arsenic was oxidized into As2O3 existed in the dust. The results showed that the matte smelting method can achieve efficient recovery of gold from arsenical refractory gold concentrate.

Jan 1, 2016

By Dalene Joalet Steenkamp

Excavation of industrial-scale furnaces allows for the systematic study of reaction sequences by identifying the different reaction zones within the furnace. In 2013, Transalloys excavated a 48 MVA submerged arc furnace that was used for silicomanganese production using the ore-based route. The excavation method was reported elsewhere as was observations made in terms of refractory wear and modes of electrical energy dissipation prior to excavation. The paper presented here, reports on the process reaction zones observed during the excavation and subsequent phase chemical analyses of a number of process samples obtained during the excavation. The zones identified were a loose burden zone, a dry coke-bed zone, a wet coke-bed zone, a hard build-up zone, and an alloy zone. The results are compared to observations made in the excavation of an industrial-scale SAF and a pilot-scale SAF in Norway. The presence of the hard build-up zone below one of the electrodes and absence of a slag zone below all three electrodes are unique features of the SAF excavated at Transalloys.

By Nobuo Takahashi

Effective solvent extraction media have been investigated for purification of rare earths. At first, a quaternary ammonium compound was studied. The counter anions of rare earths and organic dielectric substances were tested to improve separation factors,. And second, crown ethers were selected for extractant. Several diluents of crown-adducts were tested to improve solubility and distribution coefficient as well as the counter anions of rare earths. Especially, in the presence of strong reducing agents, highly selective extraction of europium from other rare earths was observed. The third extactnts were ß -diketones. Presence of organic dielectric substances was very effective to improve separation factors. Though those. three groups of extractants were suitable for mutual separation of light rare earths, alkyl esters of alkyl-phosphonic acids were suitable for mutual separation of heavy rare earths because of their high separation factors. To keep proper pH value was necessary for acidic extractants, so control method of the solution pH was studied with high molecule insoluble amines or salts of those.

Jan 1, 1995

By F. D. S. Marquis

An investigation of the mechanisms of formation of two types of porosity-primary and secondary-their characterization, evolution during processing, and effects on the mechanical behavior (fracture, fatigue, and failure) of 7X50 and 2X24 alloys has been conducted. The mechanisms of formation of three forms of primary or cast porosity were investigated, and each form was characterized: (a) macroscopic shrinkage porosity-MSP); (b) microscopic interdendritic porosity (MIP); and (c) hydrogen gas porosity (HGP) or primary hydrogen porosity (PHP). The mechanisms of formation of four forms of secondary or thermal/thermomechanical porosity were investigated, and each form of porosity was characterized: (a) high temperature oxidation (HTO). internal hydrogen precipitation (IHP), or secondary hydrogen precipitation (SHP); (b) preheating blistering porosity (PBP); (c) eutectic melting porosity (EMP);and, (d) dissolution micro void formation (DMF). The evolution and interactions of the primary and secondary types of porosity (w.ith special emphasis on PHP and SHP) during industrial and laboratory processing and their effects on the fracture and failure behavior of both types of alloys (with special focus on fatigue crack initiation and propagation) were investigated.

Jan 1, 1996

By Matthew John M. Krane, Christopher J. Vreeman, J. David Schloz

"A continuum mixture model of the direct chill casting process is used to model the transport phenomena and solidification behavior in the Direct Chill casting of an Al - 6 wt% Cu billet using Wagstaffs AirslipTM process. The model, which includes the transport of free-floating solid particles, can simulate the effect of a grain refiner on macrosegregation and fluid flow. Numerical predictions of sump profiles and composition and temperature fields are presented. Two 45 cm diameter billets were cast under production conditions with and without grain refiner. Temperature and composition measurements and sump profiles are compared to the numerical results. The comparison shows excellent agreement for the grain refined case. It is believed that an incorrect model assumption prevents good agreement in the non-grain refined billet. IntroductionDirect chill casting is a semi-continuous process in which molten aluminum enters the top of a water-cooled mold, is cooled, and forms a solid ingot drawn out below (Figure l(b)). The molten aluminum begins to solidify due to the cooling effect of the mold wall. As the ingot is withdrawn from the bottom of the mold, water jets impinge on the surface, directly cooling the billet and forming a solid layer around a liquid melt, commonly referred to as the sump.A particular defect that occurs in a wide range of casting processes, including the direct chill (DC) casting of aluminum alloys, is macrosegregation, the uncontrolled redistribution of alloying elements on the scale of the ingot during solidification. Macrosegregation in DC cast ingots can produce non-uniform mechanical properties [l], which affects the behavior of the metal during downstream forming and heat treat operations."

Jan 1, 2001

By Luciano E. Ramírez, Jesús L. Valenzuela, José R. Parga

"An innovative process for removing copper cyanide complexes including silver and zinc from cyanidation circuits has been developed. The technology was based on the inducing the nucleated precipitation of copper and silver in a tube serpentine reactor, using sodium sulfide as the precipitate and sulfuric acid as pH control. The results showed that pH had a great effect on copper cyanide removal efficiency and the optimum pH was about 3 to 3.5. At this pH value copper cyanide removal efficiency could be achieved above 97 and 99 % ,when influent copper concentration ions were 650 and 900 ppm respectively. In this process (sulphidizaton-acidification-recycle-thickening), the cyanide associated with the copper cyanide complexes is released as HCN gas under weakly acidic conditions, allowing it to be recycled back to the cyanidation process as free cyanide. This system was successfully commercial applied at Minera William in Mexico.IntroductionThe recovery of gold and silver from minerals and concentrates with cyanide is an important hydrometallurgical process, which has been studied for more than 124 years. Patented by MacArthur in 1888 [1], the process relies on the fact that gold dissolves in aerated cyanide solutions to produce the gold cyanide complex. The stoichiometry by wich this reaction occurs is known as the Elsner equation as shown here. Silver is accomplished in the same fashion."

Jan 1, 2012

By Yuanbo Zhang, Huanpeng Mi, Guanghui Li, Binjun Liang, Zhiwei Peng, Tao Jiang

Ludwigite ore has not yet been utilized on an industrial scale due to its complex mineralogy and fine mineral dissemination. In this study, sodium salts were employed to enhance the separation of iron and boron by reductive roasting-magnetic separation. It was found that the separation of iron and boron as well as the iron grade and recovery were significantly improved b y the addition of Na2SO4 or Na2CO3. Under the reduction temperature of 1050 °C, reduction time of 60 min and magnetic intensity of 0.1T. Compared with the inexistence of sodium salts, the iron grade and recovery of the magnetic concentrate increased from 83.3% and 88.6% to 93.2% and 95.1%, respectively, by adding 6% Na2CO3. The XRD and microstructure analyses indicated that the iron oxides were transformed into metallic iron and the average metallic iron grains were grown to over 40μm which was beneficial for separation of metallic iron from gangue.

Jan 1, 2016

By Wenjun Duan, Kun Wang, Qingbo Yu, Qin Qin

"A novel oxygen production technology noted chemical looping air separation (CLAS) was introduced and properties of Cu-based oxygen carriers used were investigated. The oxygen carriers were prepared by mechanical mixing. Al2O3, Fe2O3, ZrO2, TiO2 and SiO2 were used as binders during the preparation. XRD patterns show that spine! oxides are formed using Al2O3 and Fe2O3 as binders. Phases of CuO and binders keep stable using ZrO2, TiO2 and SiO2 as binders. BET values of oxygen carriers increase in the order of ZrO2>TiO2>SiO2>Fe2O3>Al2O3. The effects of temperatures, binders, particle sizes and flow rates on reduction/oxidation reaction rates were studied in TG experiments. The reduction reaction rate increases in the order of ZrO2>TiO2>SiO2. The effect of binders on the reactivity of oxidation is not obvious. The reduction and oxidation reaction rates both have the tendencies of increasing with the temperature increasing and with gas flow decreasing. However, the effects of gas flow and particle size are little.IntroductionChemical looping air separation (CLAS) is a novel oxygen production technology. The oxygen carriers used in CLAS release oxygen in reduction reactor and regenerate in the oxidation reactor. Selecting suitable oxygen carriers is the key for CLAS. Oxides of CuO, Mn2O3, Co3O4, Pb3O4, CrO2, SrO2, PdO2 and CeO2 have the property of releasing oxygen at suitable temperature and oxygen partial pressure [1]. Among these oxides, CuO, Mn2O3, Co3O4 are the most common compositions used to prepared oxygen carriers for chemical looping combustion (CLC) or chemical looping with oxygen uncoupling (CLOU) [2-5]. Moreover, thermodynamic calculations and preliminary experiments were carried out on oxides of Cu (CuO/Cu2O), Mn (Mn2O3/Mn3O4) and Co (Co3OJCoO) by Moghtaderi to ascertain their feasibility for CLAS process [6]. CuO has the highest oxygen transport capacity (0.1 g 02/g CuO compared to 0.03 g 02/g Mn2O3 and 0.06 g 02/g Co3O4). However, agglomeration is the biggest issue for copper oxides used at high temperature because of its low melting point (l 450°C for CuO, 1235°C for Cu2O and 1075°C for the mixture of CuO and Cu2O) [7]. In order to improve the capability of anti-sintering and stability ofCuO, binders (ZrO2, MgAl2O4, TiO2, SiO2, Fe2O3, Al2O3, cement) are added during the preparation of Cu-based oxygen carriers [8]. In this paper, the Cu-based oxygen carriers were prepared by mechanical mixing method. TiO2, Al2O3, Fe2O3, ZrO2 and SiO2 were selected as binder. XRD, BET and SEM were used to analyze the phase, surface area and surface morphology of oxygen carrier prepared. The reactivity of oxygen reduction and oxidation of oxygen carriers prepared were investigated in STA409PC thermal analyzer."

Jan 1, 2014

By Shigeatsu Nakazawa

Activities of Bi and In in the Bi-In liquid alloy were measured over the whole range of composition at the temperatures from 850K to 1050K. An alloy was vacuum-sealed in a quartz cell and heated at the temperature of interest. The absorption for 307nm radiation from Bi lamp was measured for Bi atom vapor in the cell. By heating a pure metal as a standard and measuring the absorbance as a function of the temperature, an analytical curve for Bi atom vapor was constructed and used for conversion of the absorbance to the vapor density. Bi activity was determined as the ratio of the Bi atom vapor density over the alloy to that over a pure metal. The same procedure was applied to the In 304nm radiation from In lamp and In activity was determined independently of Bi. Results showed that the liquid Bi-In system behaves like a regular solution.

Jan 1, 2003

By Lori Bassman, Cassandra George, Cullen McMahon, Md. Zakaria Quadir, Michael Ferry

"Complete and accurate analysis of subgrain microstructural features must include three-dimensional information. Three-dimensional electron backscatter diffraction (EBSD) data can be used to characterize these features; however their boundaries first must be determined. This cannot be accomplished simply with pixel-to-pixel misorientation thresholding because many of the boundaries are gradual transitions in crystallographic orientation. Fast Multiscale Clustering (FMC) is an established image processing technique that we have combined with quaternion representation of orientation to segment this kind of data. Segmentation algorithms often have issues handling images with both distinct and subtle boundaries. Our implementation of FMC addresses this by using a novel distance function and statistical analysis to take into account the variance in orientation of each feature. Although FMC was originally a twodimensional image processing algorithm it can be generalized to analyze threedimensional data sets. As an example, a segmentation of microbands in cold-rolled aluminum is presented.IntroductionThree-dimensional electron backscatter diffraction (3D-EBSD) is a method for mapping the local crystallographic orientations of points in a volume. The technique uses a dual beam platform consisting of a focused ion beam (FIB) and SEM with EBSD, where FIB is used for serial sectioning and EBSD for orientation mapping of 2D slices. These 2D slices may then be stacked to create a 3D volumetric data set.Typical uses of such a data set include characterizing the geometries and crystallographic orientations of surfaces between structures in 3D [1-5]. This involves identifying boundaries accurately, either in 2D slices with subsequent 3D reconstruction (as illustrated in Figure 1) or in the 3D data set. All such data sets present the challenges of i) aligning data slices to correct for instrument drift, ii) identifying relevant boundaries, and iii) implementing appropriate smoothing or interpolation algorithms. The focus of this paper is boundary identification."

Jan 1, 2011

By T. Ranki-Kilpinen

In the flash smelting technique, developed by Outokumpu Oyj, off-gases with dust load are directed into the heat recovery boiler (HRB). As the temperature decreases, metallic sulphates become thermodynamically stable. Sulphation of oxidic particles initiates. The release of heat causes an increase in particle temperatures, and soft sulphated particles can stick to the heat transfer surfaces. Dust accretion may form and cause operational problems. The objectives of the project are to study sulphation reaction mechanisms and kinetics of flue- dust particles under HRB conditions, and get more information for the flue-dust treatment possibilities. The sulphation behaviour of synthetic Cu2O particles (37-53 pm) was studied using a fluid-bed reactor of laboratory scale. The experimental parameters in the latest campaign were oxygen and sulphur dioxide contents of 2.5-10 vol-% 02 and 40-60 vol-% SO2 respectively and temperatures of 600-660°C. Samples were examined microscopically (SEM+EDS) and chemical analysis were conducted. The sulphation rate was found to have a maximum at the certain temperature, which was dependent on the gas SO2 content. Regardless of the level of SO2, a rise in oxygen content promoted sulphate formation.

Jan 1, 2002

By I. J. Moon

The reduction behavior of hematite by H2 and H2-CO gas mixtures was investigated to elucidate the reduction mechanism at 800-950 °C. The hematite compacts were made by Cold Isostatic Pressing to produce compacts of uniform shape and size. The compacts were sintered at 1000° C for 30min, and showed a contraction of 29%. Mercury pressure porosimeter was used for measuring the total porosity, pore size distribution and pore surface area of the compacts. Reduction was measured by means of weight-loss technique using Cahn Balance (Model : TG-171, capacity log, accuracy f 10pg). Microscopic examination and X-ray analysis were used to correlate the structure of reduced compacts with the mechanisms of reduction. Neither chemical reaction control nor diffusion control is adequate in describing the complete course of reduction of the hematite compact. The reduction of hematite compacts was initially controlled by the chemical reaction at oxidelmetal interface. The reaction goes through a transition phase .where it is undergoing a mixed control, followed by the diffusion control towards the end of the reduction. The values of apparent activation energies for chemical reaction control were 3.48-8.43 kcal/mol depending on the gas compositions.

Jan 1, 1997