By G. Sachs, G. Espey

It is well known that high residual stresses are created in tubing by the sinking process, in which no internal tool or mandrel is used.l-4 In this process, the wall thickness is usually slightly increased.4,5 In tube drawing with a plug, the residual stresses are gradually reduced with increasing reduction of wall, and, by the conventional approximation methods of stress measurement, no stress is detected in tubing in which the wall reduction is over 50 per cent of the total reduction in cross-sectional area.l,6 It has also been observed that higher stresses are set up by the use of wide-angle dies than by acute dies.? 'he actual stress distribution in drawn tubing has been investigated by a few workers,7"9 but has not been related to the conditions of the drawing process. Some attempts have been made to correlate accelerated cracking tests for stresses in brass products with the magnitude of the circumferential stresses and the condition of the metal. l-10 Materials and Preparation The material used in this experiment was commercial cartridge-brass (70 per cent Cu, 30 per cent Zn) tubing in the straightened and annealed condition.† This tubing was of various outside diameters and had a wall thickness of 0.032 in. It was sunk to 1/2-in. outside diameter by means of an experimental 10,000-lb. hydraulic draw-bench, with a maximum drawing speed of 8 ft. per minute. All dies were of 1/2-in. diameter. Various die materials and contours were used in order to study the effect of die design on residual stresses in the tubing; the specifications for the dies are given in Fig. I. Castor oil was used throughout as lubricant. Chattering occurred in sinking some of the tubing, particularly when dies having the more acute angles were used, but the tubes showing chatter marks did not differ markedly from those with a smooth surface regarding the magnitude of residual stress. The source of the chattering has not yet been revealed. The wall of the tubing becomes thicker during s nking, as previously observed.4,5 The increases in wall thickness were 3, 7 and 9.5 per cent on the average for 6, 20 and 33 per cent reductions in diameter, no effect of the contour being noticeable. The reductions mentioned throughout this investigation do not consider this fact, but are reductions of the outside diameter. For the evaluation of the residual stress two fundamentally different methods were used. The approximation methodl,ll of splitting a certain length of tubing was employed to obtain a bird's-eye view of the effect of various drawing conditions on the circumferential stress measured by the diameter change occurring On splitting. For

Jan 1, 1942

By P. P. Gregory

Natural petroleum gas occurring in the oil-bearing reservoirs is found to exist either as free gas associated with the oil and/or in solution in the oil. In some virgin fields practically no free gas is encountered under the reservoir conditions of pressure and temperature, although in other fields a considerable section of the "pay" horizon is occupied by free gas. In other words, a given oil field may or may not have a gas cap before the exploitation takes place. However, when the reservoir pressure is reduced to a point below the critical saturation pressure by withdrawals of fluids from the producing formation, the gas dissolved in the oil inevitably begins to come out of solution and becomes free gas. Under the controlled methods of production and drilling, a portion of this gas is produced with the oil to the surface and a portion of it remains within the reservoir to accumulate at higher structural levels toward which it migrates by virtue of its low specific gravity. The rate of growth of a gas cap in a given structure depends primarily upon the rate of decline in the reservoir pressure. If the rate of pressure decline is rapid, the gas cap likewise will grow rapidly. On the other hand, shrinkage in the gas-cap area was noted in some fields in which reservoir pressures wereincreasing. Determination of Gas-oil Contact and Thickness of Gas Cap The gas-oil contact can be conveniently located in the process of drilling a well and by electrical logging. However, very little can be found in the petroleum literature concerning methods of predetermining gas-oil contacts in producing reservoirs. Therefore, the writer feels justified in describing briefly a simple, workable, and inexpensive method of determining gas-oil contacts and outlining the limits of gas-cap areas in a field where such knowledge may be essential for efficient production and development operations. The method involves the determination of the following data: (I) Structural data, such as the depth or elevation of the top' of "pay" horizon; (2) reservoir pressures; (3) tubing and casing pressures at the well head; (4) static oil-pressure gradient; (5) static gas-pressure gradient. These data can be secured with a minimum of expense, inasmuch as the

Jan 1, 1938

By H. R. Thresh, A. F. Crawley

THIS paper reports the results of viscosity measurements on cadmium and indium undertaken as part of a continuing program of liquid metals research at the Mines Branch, Department of Energy, Mines and Resources, Ottawa, Canada. For several years this work has continued with support from the Canadian Zinc and Lead Research Committee and the International Lead and Zinc Research Organization. In the literature, existing viscosity data for cadmium are conflicting and for indium are scarce. To achieve reliable viscosity values, further work was deemed desirable. Viscosities were measured using an absolute technique applied to an oscillating closed right cylinder of liquid metal. The apparatus, constructed in this laboratory, and the techniques involved in its use have been described in an earlier paper.' In calculating viscosity coefficients from the experimental data. Roscoe's2 mathematical analysis was used. Because accurate viscosity determinations are dependent on accurate density data, and since the available data in the literature are conflicting, the densities of liquid cadmium and indium were also determined in this laboratory by a pycnometric technique. This increased the control exercised over all the variables contributing to the accuracy of viscosity measurements. For both density and viscosity determinations, cadmium and indium of 99.999 pct purity were used. These materials were obtained from Cominco Ltd. In order to suppress excessive evaporation losses and help prevent oxidation, a technique developed in measuring the viscosity of zinc' was used for cadmium. This involved maintaining an atmosphere of purified hydrogen in the viscosimeter during the rela- tively long periods while the experimental temperature was changed and stabilized between individual determinations of the logarithmic decrement. Then, immediately prior to a decrement measurement. the viscosimeter was rapidly evacuated to a pressure of about 2 X 10-6 torr. On the other hand. with indium. no difficulties arise from vaporization or oxidation. In this case. therefore. the apparatus was held under a constant vacuum of about 2 x 10-6 torr. When all sources of random and systematic error have been evaluated, the technique is considered to yield data accurate within 10.5 pct. The viscosity of cadmium was measured to a maximum temperature of 451.8°C and that of indium to 346.5°C. These temperatures are. respectively. 130° and 190°C above the melting points. Two separate runs were made on indium. The results are given in Table I and, when plotted. yield the smooth curves evident in Figs. 1 and 2. Values of A and C to fit the well-known Andrade1 equation were determined by a regression analysis. The equation is: where n = coefficient of viscosity. i = specific volume. T = temperature in °K Despite its empirical nature. Andrade's equation has been shown by many workers to describe accurately the temperature dependence of viscosity. During the current research program, this equation has been found to fit the data precisely for all the metals and alloys that have been studied.5,6 The A and C' values for cadmium and indium are given in Table 11. Comparing the magnitude of the present data with those of previous workers,7-10 as has been done in Fig. 1, it is evident that the results of Fisher and Phillips10 deviate markedly from the rest. With the exception of one point from Gering and Sauerwald,7 all other data agree within ±2.5 pct. However, the agreement between the present results and the work of Menz and sauerwald9 is especially good over the entire experimental temperature range. Such agreement may be expected since Menz and Sauerwald's

Jan 1, 1970

By H. M. St. John

MAINTAINING a satisfactory structure in brass and bronze castings has always been a foundry problem of great practical importance. While metallurgists and scientific investigators have not entirely ignored this matter, it has received less of their attention than has been given to iron, steel and the wrought copper and aluminum alloys. Investigation in this field has probably been discouraged to some extent by the complicated nature of the alloys involved. Hundreds of alloys are in more or less common use, most of them containing copper, zinc, lead and tin in-widely varying proportions. They also contain appreciable percentages of iron and antimony as impurities, and often phosphorus, which has been added as a deoxidizer and fluidifier. Small amounts of sulfur are usually present. It is not uncommon to find nickel, sometimes in rather substantial quantities. Traces of other metals are frequently present. So complicated and variable a mixture obviously offers difficulties in. any investigation of the various factors that influence the structure and other properties of the casting.

Jan 1, 1930

With one shaft almost completed and another shaft being sunk, the scope of the Saskatchewan potash area is beginning to come into focus. Some 18 companies have reportedly leased more than four million acres to explore potash possibilities. PCA, farthest along, is located about 15 miles southeast of Saskatoon, and IMC has its project underway near Esterhazy in the eastern edge of the province. U. S. Borax and Chemical Corp. is also reported exploring the area. The field lies in the middle Devonian geological formation which was probed by oil companies along the 200-mile area across the province. Extensive examination began after World War II and deep drilling was started a few years later.

Jan 5, 1958

By Henry Mulryan

THE largest and purest known deposit of diatomite is being actively mined and processed 3 ½ miles south of Lompoc, Santa Barbara County, Calif., by the Johns-Manville Products Corporation. The workings FIG. 1-LOCATION OF DIATOMITE DEPOSIT AT LOMPOC. cover 4000 acres, the depth of economically recoverable diatomite being 1000 ft. (Fig. 1). Lompoc, a community of 2500 population, is situated in the Santa Ynez River Valley 10 miles inland from the Pacific Ocean. It is 44 miles

Jan 1, 1936

World Petroleum Consumption. By V. R. GARFIAS AND R. V. WHETSEL. (Trans, vol 107). A tabulation showing world consumption of gasoline, kerosene, gas and fuel oil, lubricants, and miscellaneous petroleum products by counties in the years 1931, 1932 and 1933 , Totals are given; for instance, Cuba consumed 3,998,000 bbl of all petroleum products in 1933, in 1933; the world consumed 1,366,291,000 bbl. of all petroleum products, etc. Domestic Production. Annual Symposium of Petroleum Division, February Meeting, 1934 (Trans, vol. 107. 181 pages.) The symposium consists of reports on petroleum and gas developments and production in the producing states of the United States. This year the statistical information is presented in a new and far more comprehensive form. The reports on domestic production are as follows: Arkansas, by B C Craft; California, by V H. Wilhelm and H. W. Miller, Colorado, by C. E. Shoenfelt, Illinois, by A H Bell, Indiana, by W. N Logan and P. Simpson; Kansas, by Marvin Lee; Kentucky, Ohio and West Virginia, by V. C Smith; Louisi¬ana, by B C Craft, Michigan, by Theron Wasson; Mississippi, by B C Craft; Missouri, by F C Greene, Montana, by H. N Hickey, New Mexico, by C. E Shoen¬felt and D E Winchester, New York, by D. H. Newland, Oklahoma, by L. G. E. Bignell, J 0 Lewis and E. A Hanson, Pennsylvania, by G H Fancher, Tennessee, by L. C Glenn, Central Texas, by R B. Kelly and P R Martin, East Texas, by A R. Denison, Gulf Coast, by L P Teas, North Texas, by H B Fuqua and B. E Thomp¬son; North Central Texas, by J M. Armstrong, Panhandle, by R H Lynn and T. C. Craig, Southwest Texas, by 0. G. Bell; West Texas, by C W. Reith, Utah, by E S Shaw, Wyoming, by J G Bartram.

Jan 1, 1935

By J. R. Vilelia

IN accordance with the custom of this society, we are gathered here, as we have every year since 1924, to honor the memory of the eminent American metallurgist and teacher, Professor Henry Marion Howe. Unlike many of the distinguished metallurgists who have preceded me as a Howe lecturer, I cannot bring to you reminiscences of his personality, for it was not my privilege to be associated with Professor Howe, or to be directly one of his students. Yet, Professor Howe and Professor Albert Sauveur, through the medium of their books, were my first teachers of metallography, as they have been of almost all American metallurgists of my generation. As a teacher, and for many years the acknowledged leader of American metallurgists, he exercised a profound influence in the growth of our science and was held in honor by the men of science of his time. I can speak no words of technical appreciation that will add luster to his fame, for by his prophetic vision, his teachings, and his researches he stands among the immortals in the memory of all metallurgists. In 1926, the third Howe Memorial Lecture was presented by Professor William Campbell' of Columbia University, who entitled it "Twenty-Five Years of Metallography." He took as a starting date for his chronology the turn of the century, which coincided with his arrival from England to work in association with Howe at the Columbia School of Mines. In that informative lecture Professor Campbell enumerated the important advances in metallography achieved during the first quarter of the century, and, it now appears, may have established the custom of reviewing such progress every twenty-five years. The scope of Professor Campbell's lecture was as broad as his metallurgical knowledge, for it embraced a wide portion of the field of metallography, both ferrous and nonferrous. Twenty-five years later, the Howe Memorial Lecture Committee saw fit to assign to me the honor of writing a lecture that would commemorate the work of Henry Marion Howe and would at the same time constitute the 25th anniversary of the lecture by Professor Campbell. The Committee suggested that this lecture might properly be called "Twenty-Five More Years of Metallography," a suggestion that I have adopted. I must confess, however, that I have not followed the precedent established by Campbell and have narrowed the scope of this lecture to an appraisal of those achievements which in my opinion have contributed most to the progress of microscopical metallography during the past twenty-five years. Progress in Metallography The metallographic methods most widely used today, with the exception of the electron microscope, were firmly established more than twenty-five years ago. In general, our specimens were prepared for microscopic examination in those days in much the same manner as they are today. It is true that new details of technique have been introduced from time to time, and that superior equipment is available today, but on the whole, these improvements have been in the nature of refinements, often a matter of personal preference, and none can be considered essential to the attainment of the ultimate goal of the art and science of metallography, which is to reveal the structure of metallic specimens with unequivocal clarity so that they may be interpreted correctly. Mechanical metallographic polishing, which was the only method available in 1926, is still universally practiced and still consists of abrading the metallic specimen with a series of abrasives of increasing fineness until a specular surface is attained. We have now the alternative method of electropolishing, but it is not widely used because, except in a few special cases, its results are inferior to those of competent mechanical polishing. Likewise, most of the etching reagents preferred today were in common use more than twenty-five years ago and were applied in the same manner as they are today. Valuable improvements have been made in the optical and mechanical performance of metallurgical microscopes, but there was no dearth in those days of excellent instruments equipped with achromatic and apochromatic objectives capable of yielding micrographs comparable in quality with the best that we can make today. In fact, it would be a difficult task for any metallographer today to make optical micrographs at magnifications in excess of 3000 diameters that would surpass those made by Lucas more than twenty-five years ago. One of these is shown in Fig. 1. Yet, it is unquestionable that on the whole, the micrographs appearing in the metallurgical literature today are vastly superior to those

Jan 1, 1952

Jan 1, 1925

By A. J. Lanea

INDUSTRIAL MEDICINE bids fair to become one of the most important and highly developed branches of medical science. Mining companies, even in remote districts, have developed large and efficient medical organizations that comprise the best types of physicians and surgeons. Not infrequently, however, company medical departments have been influenced too much by local conditions-including the compensation laws, which differ widely in the various states. The possibilities of industrial medicine are just beginning to be generally understood, and the variations in the organization and aims of medical departments of mining companies are no more pronounced than in industry as a whole. The industrial physician should be as much a part of the organization as any other official and he should know intimately the various types and phases of work in the plant and should look at his work from the viewpoint of the needs and requirements of his particular industry and company. He should not-be on the outside looking in, but on the inside, working hand in hand with the superintendent, manager, foremen, employment director, safety director, and anybody else with whom in his work he might associate. In any industry it is essential that the doctor be-familiar with working conditions. The mine doctor who never goes underground must remain ignorant of the factors causing many of the disorders he treats as well as miss the best opportunity of gaining the respect and cooperation of the men he. serves. If the mine doctor remains unfamiliar with underground working conditions he bars himself from valuable preventive medical work. It is estimated that the time lost by industrial workers, as a whole, because of illness is about four times as great as that lost because of accidents. While the effort to determine the responsibility of working conditions for illness is often futile, there is a wide field, both for study and practice, in the lessening of sickness among industrial workers. The first step in this direction must be a knowledge of the factors involved.

Jan 2, 1921

By David V. Ragone, Richard E. Balzhiser

The liquidus uranium concentration in the U-Bi system is given by the following expression for the temperature range 400° to 800°C: No break was observed in the curve over this temperature range. The partial molar enthalpy change for uranium in the liquidus reaction, UBi2— U + 2Bi, was found to equal 12,300 cal per g mole. Copper produced a continuous decrease in the liguihs uranium concentration at 600°C. The presence of copper in the solvent was observed to affect the uranium activity coefficient according to the following expression: duced no change in the liquidus combosition below 0.6 at. pct Pd. Higher palladium concentrations sharply depressed the uranium concentration. SOLUTE behavior in molten alloys has been shown to be strongly influenced by the presence of additional species. Much attention has been given to such phenomena in iron-base systems where a number of alloying elements and/or impurities are likely to be present in small but significant quantities. Frequently, the interaction of these solutes has altered their thermodynamic behavior to the extent that reaction equilibra are appreciably influenced. Consequently, much of the information available for binary behavior must be reevaluated when additional components are likely to be present. Similar interactions can be expected to occur in bismuth-base solvents. Interest in the use of bismuth solutions of uranium as reactor fuels has stimulated investigators to explore the effect of various elements on the liquidus uranium concentration. Criticality requirements necessitate close control of the uranium concentration which, at the anticipated operating temperature of 500°C, approaches saturation. Consequently, elements which suppress the liquidus concentration could produce serious reactivity problems. Since the fuel solution is cer- tain to contain additives, such as magnesium and zirconium, for corrosion inhibition as well as small concentrations of fission products and corrosion products, a better understanding of the possible interaction phenomena is mandatory. This need stimulated experimental programs at the Brookhaven National Laboratory and elsewhere to determine precisely the liquidus uranium concentration in the bismuth-rich portion of several ternary systems. Early experimental efforts were directed toward an accurate dcmtermination of the U-Bi liquidus over the temperature range from 300' to 800°c. As shown in Fig. 1, the results to date exhibit considerable scatter. The investigations of Bareis,' Teitel,2 Greenwood,3 and Cotterill and hon4 agreed well below 700°c. Greenwood and Teitel extended their studies to higher temperatures but failed to concur in their results. A more recent study by Schweitzer and weekss at Brookhaven National Laboratory between 300' and 725°c, produced values 15 pct lower

Jan 1, 1962

By D. J. Jr. McAdam

RESULTS of a general survey of corrosion-fatigue phenomena at the Naval Engineering Experiment Station were presented in five previous papers.1-5 In these papers references were given to the work of Haigh in 1917.6 The five papers mentioned gave a general survey of the behavior of metals when tested to failure under simultaneous corrosion and cyclic stress. As a result of this survey the fourth paper gave a tentative analysis of the corrosion-fatigue process. According to this analysis, if the initial stress is below the endurance limit but above the corrosion-fatigue limit, the corrosion-fatigue process is divided into two periods. The first period is the formation of pits. As the initial stress is below the endurance limit, the pitting is assumed to be due to corrosion, not to fatigue. The corrosion pitting, however, is not the ordinary pitting of stressless corrosion, but is an accelerated pitting due to the effect of the cyclic stress on the corrosion. As the pit progresses, both the actual stress and the effective solution pressure increase. The increase of actual stress is due to increasing stress concentration at the bottoms of the pits. The increase of effective solution pressure is due to the increase of actual stress. The mutual intensification of stress and solution pressure continues until the actual stress at the bottoms of the pits surpasses the endurance limit. The second period of corrosion-fatigue then begins. In this period the process is merely fatigue accelerated by the corrosion. The cracks advance at a continually accelerated rate until the specimen breaks.

Jan 1, 1930

September 1 to 6, 1918 COMMITTEE IN CHARGE Spencer Penrose, Chairman. George M. Taylor, Vice-Chairman. A. E. Carlton, Chairman. Finance Committee J. Dawson Hawkins, Secretary DENVER COLORADO SPRINGS CRIPPLE CREEK Finance Finance Thomas B. Crowe T. B. Stearns A. E. Canton , E. P. Arthur, Jr. Richard A. Parker Spencer Penrose N. S. Greensfelder T. B. Burbridge George M. Taylor A. E. Carlton. A. L. Blomfield, Treasurer B. F. Hill Arrangement I F. G. Willis Dave G. Miller Registration Norris E. Eads Frank Bulkley Loren C. Lennox 1V. E. Ryan Geo. E. Collins Horace F. Lunt Fred Jones .1. M. Tippett F. D. Smale Entertainment J. H. Haynes F. H. Bostwick Arrangement and Entertainment L. W. Lennox F. E. Shepard George M. Taylor A. L. Blomfield M. R.. Valentine Howland Bancroft J. D. Hawkins Thomas B. Crowe B. P. Morse A. E. Carlton E. P. Arthur J. G. Perry G. H. Clevenger Etienne A. Ritter Ladies Ladies , PUEBLO Mrs. T. B. Stearns, Mrs. C. M. Taylor, Mrs. C. H. Clevenger J. F. Welborn Chairman. Chairman H. B. Carpenter Mrs. C. Loughridge Mrs. S.-Penrose Mrs. A. E. Carlton L. B. Eames Mrs. H. Bancroft Mrs. J. D. Hawkins Mrs. A. L. Blomfield F. Robinson Mrs. G. Bancroft Mrs. L. C. Lennox Mrs. J. M. Tippett . Mrs. W. D. Leonard Mrs. H. F. Lunt -Mrs. E. C. van Diest Mrs. C. Chase Mrs. E. A. Ritter Mrs. AV. Strieby Mrs. F. H. Bostwick Mrs. L. S. Harner Mrs. C. L. Bailey Mrs. F. Bulkley Miss F. Dickerman Mrs. E. P. Shove Mrs. C. L. Tutt Mrs. F. C. Peck Mrs. F. D. Pastorius

Jan 10, 1918

By Louis E. Toth, Alan W. Searcy

A modification of Le Claire's microscopic model for self-diffusion is developed in a form suitable for prediction of activation energies for diffusion in disordered substitutional solutions as well as in pure metals Bonding is considered as a localized interaction, and the energy of bonding between atoms of different types is taken as the arithmetic mean of the energies in the pure elements. The activation energies for vacancy formation and migration in substitutional alloys are shown to depend on the empirical constants developed for self-diffusion when the equations are adjusted for the mole fractions of the two elements. The differences in activation energies between alloys and pure metals are calculated and compared with the experimental differences. MaNY different correlations have been proposed for use in predicting activation energies for self-diffusion or diffusion in dilute alloys. Usually theories for self-diffusion cannot be applied to alloys nor can theories for dilute alloys be satisfactorily adapted to self-diffusion. We present here a correlation scheme which can approximate activation energies for diffusion, vacancy formation, and atom migration in substitutional-alloy systems of any concentration. The activation energy for self-diffusion QD has been correlated to the melting temperature Tm,1, 2 the sublimation energy L,,l the heat of fusion Lf,3 crystal structure, and valence.4 Working with mechanical parameters Le claire5 proposed that the activation energy for vacancy migration Qm could be related to appropriate shear moduli. He also proposed that the activation energy for vacancy formation 62, is proportional to Ls. THEORY We consider that Le Claire's expression for 4, is satisfactory. But an alternate expression for Qm in terms of the bulk modulus is just as satisfactory from a theoretical point of view for the prediction of the energy of vacancy migration in pure metals and can more easily be used for alloys. In order for Qm to be a minimum, not only the moving atom but also adjacent and nearby atoms must undergo distortions. These distortions are neither isotropic as is implied by a correlation with the bulk modulus nor unidirectional as implied by a correlation with a shear modulus, but are complex and multidirectional. A complete analysis in terms of the bulk modulus and all the shear moduli is not yet available. In a first approximation in which only one parameter is used, there is no obvious theoretical reason to prefer the shear modulus over the bulk modulus. The bulk modulus is a much more convenient parameter for use in predicting Qm. Shear moduli are known for less than half of the metallic elements while bulk moduli are usually available. Furthermore, because of the directional dependence of shear moduli, their estimation for alloys appears inherently more difficult than is the estimation of bulk moduli. We assume that the bulk modulus Bs reflects an average value of the shear moduli such that the strain energy at the point of maximum distortion of the lattice during vacancy migration can be expressed as

Jan 1, 1964

By H. N. Thomson

GENERAL. THE Tooele plant of the International Smelting & Refining Co. is situated at the mouth of Pine canyon, Tooele county, Utah. It is connected with the main line of the San Pedro, Los Angeles & Salt Lake railroad by the Tooele Valley railway, and is about 7 miles from Tooele Junction. Fig. 1 is a general view of the plant. FIG. 1.-TOOELE PLANT OF THE INTERNATIONAL SMELTING & REFINING Co. The copper plant has been in operation since July, 1910, and the first blast furnace at the lead plant was blown in on Feb. 29, 1912. The location of the plant was selected on sloping ground with the idea of using gravity to the fullest extent and thus keeping labor at a minimum. Practically the entire plant is constructed of steel, reinforced concrete, and brick. Bingham ores, both lead and copper, are received over the Utah Consolidated Aerial Tramway. The tram buckets, each containing

Jan 7, 1913

By H. C. van Elst

Ultrahigh-speedphotographic and electronic meth-ods were applied to an investigation of details of brittle-fracture propagation in steel. The brittle fractures studied were obtained in steel plate with the aid of a Robertson apparatus. It was found that a brittle fracture proceeds by discrete steps ranging from 30 mm near the stop temperature to less than 2 mm at lower temperatures. The halting FROM prior metallographic observations of brittle fracture in steel' it could be concluded that the distribution of mechanical twins along a brittle fracture was similar to the distribution of mechanical twins induced by explosive deformation. It was therefore assumed that a running brittle fracture created stress waves, cf. Refs. 2-7. An emission of stress waves by a brittle fracture, however, seems only conceivable if the fracture propagates by discrete steps. For this reason a study of the details of times between successive steps drop in this tem-perature region from 20 usec to about 1 psec. The stepwise propagation mechanism is accompanied by an intermittent emission of stress waves of the order of 100 to 200 kg per sq mm. These stress waves seen1 to play an important role in the mechanism of brittle fracture as will be discussed. brittle-fracture propagation was undertaken to investigate the possible determination of the fracture steps and the emitted stress waves associated with the assumed mechanism. The more practical object of this work is the development of a test method for the determination of the ductile-brittle transition in small specimens. This has special advantages for the study of irradiation damage in steel. In this test method, which will be published in a following paper, the stress waves emitted by an actual brittle fracture are reproduced with explosive or electrical means and are then transmitted through small specimens at various temperatures. In the present paper only the results of the brittle-fracture study will be reported.

Jan 1, 1964

By J. L. Snoek

[ ] DISCUSSION J. L, SNOEK*-Stress-induced preferential diffusion in cubic body centered metals in the annealed state provides us with a powerful tool for determining the mobility of interstitially solved atoms as well as their location in the lattice and the exact nature of the distortion brought about in the lattice by their presence. Calculations given by D. Polder31 show that the distortion of the lattice, besides being proportional to the applied stress P, is also proportional to [VC, RT + xVCo] where T, V and Co are the temperature, molar volume of the solvent and molar concentration of the solute respectively and x is a constant describing the mutual interaction energy of the dissolved particles. This calculation obviously is no longer valid if x is negative and the abso¬lute value of xVCo surpasses that of RT. The lattice may then be expected to become tetragonal spontaneously. Such a spontaneous tetragonality seems to have been observed by W. Klemm and L, Grimm for the case of oxygen solved in vanadium.32 Measurements of the internal friction in cold worked iron containing carbon or nitrogen should provide us with information on the mobility as well as the preferential location of these particles in the iron lattice in the cold worked state. The work by T'ing-Sui Kê is a valuable contribution to this problem, The data obtained by T'ing Sui Kê and myself on cold worked samples of iron seem to indicate that carbon and nitrogen in these samples are found either in the normal (1/2 , 0, 0) interstices or in a new preferential position created by the cold working. The latter positions in my opinion can hardly by anything else but the edges of the dislocations. The observed larger distances of diffusion might be explained by assuming that the carbon atoms when freed from a certain dislocation by thermal agitation must diffuse over several atom distances before being caught in another dislocation. The theory however needs working out and no doubt will be much more complicated than the one valid for the annealed state. T'ING-SUI KÊ (author's reply)-It is highly encouraging to read the written discussion given by Dr, Snoek who initiated the theory of stress-induced preferential diffusion in cubic body centered metals in the annealed state, Since the presentation of this paper, the author has done more experimental work on this subject which seems to be able to settle several of the points raised by Dr. Snoek. It has been found that such stress-induced preferential diffusion occurs also in the solid solutions of carbon,33 oxygen,34 and nitrogen35 in tantalum which has a body centered cubic structure. Analysis of the shape of the observed internal friction. peaks indicates that the inter-

Jan 1, 1948

By W. H. Emmons

This paper is the third of a series treating of the relations of ores of the metals to igneous rocks. The first' outlined the general problem; the second2 proposed a classification of lode ores, and showed how the distribution of the deposits is in a certain measure controlled by the contour of the roof of the parent batholith. A number of mining districts were discussed, the examples being selected chiefly from group 2 of the classification. The proposed classification of lode deposits, briefly stated, is as follows: 1. Cryptobatholithic: near hidden batholiths which have not yet been exhumed by erosion. 2. Acrobatholithic: in and near cupolas or domes of batholiths—the high points of larger underlying masses. 3. Epibatholithic: on batholiths, near their rims, but below eroded cupolas, or below the highest points of the roofs. 4. Embatholithic: among closely-spaced outcrops which probably are parts of a single bathohth. The outcrops of invaded rocks predominate. 5. Endobatholithic. in and near roof pendants of large batholiths. The invading rocks predominate. 6. Hypobatholithic: in deeply-eroded batholiths, where even roof pendants have been eroded. Deposits of certain metals on the roofs of the batholiths are much more numerous in some positions than deposits of other metals, and the horizontal zonal arrangements of lodes of different metals are shown characteristically only in certain groups. In a large measure, also, the character of the fracturing and metallization is determined by the position on the roof of the batholith. The disseminated copper ores in porphyry constitute a clearly-defined type. All the deposits of these ores, as far as known, are in group 2. They appear to have been formed only in and around small upward projections of the parent granitic masses, and not low on the walls of the

Jan 1, 1927

By R. E. Reed, R. D. Leggett, Paxton, H. W.

TECHNIQUES have been developed for growing monocrystals and bicrystals of Fe-20 Cr, Fe-20 Cr-20 Ni, and Fe-18 Cr-8 Ni alloys by both the strain-anneal and the Bridgeman techniques. None of the techniques are new but since they are simple and many people have expressed interest, they are described here quantitatively as they could be modified for other single-phase "commercial" materials of high melting point. CRYSTAL GROWTH BY STRAIN ANNEAL Flat tensile specimens with a tapered gage length were initially studied to deduce the approximate critical strain. Normal flat tensile specimens were then used. The optimum procedure for the austenitic steels (Fe-Cr-Ni) deduced from a variety of cold reductions, recrystallization treatments, tensile strain, and growth anneals was as follows: cold reduce 70 pct, recrystallize (after machining tensile specimens) at 1000°C for 1 hr, strain in tension 2.5 pct, and then heat to 1350°C as rapidly as possible. A time of 100 hr at 1350°C is usually sufficient to pro-

Jan 1, 1960

By D. S. Eppelsheimer, D. N. Williams

The cold rolled textures of iodide titanium and of three samples of commercial titanium were examined using the Schulz-Decker Geiger counter technique. The iodide titanium and two of the three samples of commercial titanium showed a (0001) [1010] texture rotated 30' toward the transverse direction about an axis in the rolling direction. The third sample of commercial titanium showed a double texture. THE metals of the hexagonal system tend to deform similarly if the c/a ratios are similar. Thus titanium, zirconium, and beryllium, with c/a ratios of 1.601, 1.590, and 1.570, respectively,l should have similar cold rolled textures. The cold rolled texture of high purity iodide titanium has been described as (0001) [1010] rotated 30" toward the transverse direction about an axis in the rolling direction.' The texture of zirconium has also been reported as (0001) [1010] with a transverse rotation from the ideal position of approximately 30" about an axis in the rolling direction." This texture differs from that reported for titanium however since a continuous spread of (0001) poles toward the transverse direction was reported rather than distinct (0001) maxima 30" from the rolling plane normal. Beryllium has a texture similar to that of zirconium although the angle of transverse rotation of the (0001) poles is much less.' These three metals thus show a common type of cold rolled texture, as yet unexplained, which can be described as (0001) [1010] with various degrees of rotation toward the transverse direction about an axis in the rolling direction. Since titanium showed the greatest degree of rotation from the (0001) [1010] position, the cold rolled texture of titanium was re-examined using a semiquantitative Geiger counter X-ray technique to obtain more accurate experimental data from which a theoretical interpretation of this new type of hex- agonal rolling texture could be developed. The cold rolled textures of iodide titanium and of three samples of commercial titanium were determined. Table 1 gives the analyses of the titanium samples. Experimental Procedure Preparation of Samples: Prior to the final rolling operation each of the samples was given an initial reduction of approximately 50 pct and annealed to remove the gross effects of any previous treatments. Samples were annealed in vacuum, high purity helium, and air to determine whether annealing atmosphere had any effect on the cold rolled textures developed. All samples were annealed 1 hr at 800°C. Grain size determinations were made using the formula, 1.075 in which n is the number of grains counted in an area A (in sq mm) and M is the magnification of the area counted.' This formula gives the diameter between opposite flats assuming hexagonal grains. At least three areas containing more than sixty grains each were counted in each grain size determination. Rockwell B hardness readings were made on the annealed samples. The results of the measurements of

Jan 1, 1954