By F. F. Schmidt, H. R. Ogden, E. S. Bartlett

Continuing tantalum alloy development studies have been concerned with a more detailed investigation of promising binary, ternary, and more complex tantalum alloys containing Groups IV-A, V-A, VI -A. VII-A, and VII-A metal additions. A primary objective of these studies was to improve the elevated temperature strength of tantalum with minimum degradation of fabricability and low-temperature ductility by alloying. Several alloys were found to exhibit hot tensile strengths in the excess of 25, 15, and 10 ksi at 2700°, 3000°, and 3500°F, respectively, combined with excellent cryogenic toughness and ductility. Particularly outstanding in this respect are alloys in the system Ta-Mo-W. Ternary parameter curves describing hot-strength, low-temperature ductility, recrystallization temperature, weld ductility, and fabricability are presented for the Ta-Cb-V, Ta-Hf-W, Ta-Mo-Hf, Ta-Mo-V, Ta-Mo-W, and Ta-V-W systems. At present, only four metals qualify for large scale structural applications at temperatures above about 1800°F. These are tungsten, tantalum, molybdenum, and columbium. Research and development work on these refractory metals has progressed to the point where efforts are now primarily directed toward the improvement of high- and low-temperature mechanical properties through alloying. High melting point combined with excellent low-temperature ductility, fabricability, toughness, weldability, and high solubility and tolerance for both substitutional and interstitial solutes are important attributes of tantalum. Conversely, its high density and relative scarcity compared with other refractory metals are the major deterrents to the use of tantalum. Early studies in the Battelle alloy development program established base line data on the mechanical and metallurgical properties of high-purity tantalum.' These studies were extended to include a preliminary investigation of the effects of various alloying elements on the established base properties.2,3 Recent studies involved a more detailed investigation of promising binary alloys containing Cb, Hf, Mo, Os, Re, Ru, and W, and ternary Ta-Cb-V, Ta-Hf-W, Ta-Mo-Hf, Ta-Mo-V, Ta-Mo-W, and Ta-V-W alloys. Results of major importance obtained are given in this article. EXPERIMENTAL PROCEDURES Electron-beam-melted tantalum (Wah Chang) and high-purity alloying elements were consolidated as 150-g ingots by multiple nonconsumable arc melting under a partial atmosphere of helium. Homogeneity of the button ingots was checked radiographically. Alloy buttons measured about 1-1/2 to 1-3/4 in. in diam by about 0.35 and 0.50 in. thick. Nominal alloy compositions were checked on each alloy button by weighing after arc melting. In most instances, weight losses were within 3 pct of the total weight charged. Subsequent chemical analyses on a number of selected alloys showed interstitial contents to range as shown below: Range of Interstitial Content, ppm 0 C N H 25-75 50-100 10-50 1-5 Metallic alloying additions were found to agree well with nominal compositions based on weight change data. Fabrication directly from the cast button to sheet was conducted at low (75° to 900°F), intermediate (1800° to 2000°F), or high (3000°F) temperatures, depending upon alloy content and hardness. Evacuated stainless steel or molybdenum packs were used for fabrication at intermediate and high temperatures, respectively. The temperature required to complete recrystal-lization in one hour was determined by hardness measurements and metallographic observations (longitudinal test sections) after vacuum annealing at 180°F intervals in the range 2010° to 2910°F. All mechanical property evaluations were conducted on recrystallized sheet, nominally 0.04 in. thick. Weldability of the various alloys was screened using manual TIG welding techniques. Bend ductility (bend axis perpendicular to weld axis) was the criterion used for evaluation. Tensile specimens employed 0.200 by 1 in. gage lengths, and bend test specimens measured about 1 by 1/4 in. Low-temperature tensile tests were conducted using a crosshead speed of 0.02 in. per min up to the point of yielding, and 0.05 in. per min to fracture. High-temperature tensile tests were conducted in vacuum using a crosshead speed of 0.01 in. per min

Jan 1, 1963

By Walter Kauzmann

ALL viscous or plastic flow of incompressible matter is the result of shear strain; the changing shape of any body that is being plastically deformed can be completely described in terms of the shear strain occurring at each point in the body.[t] Furthermore, the relative amounts of shear strain occurring in different parts of a body under stress depend upon the relative rates of shear strain at those different points, so that if the dependence of the shear rate of any material on the temperature, shear stress, previous history, etc., were understood, the principles of plastic deformation would be known, and we could calculate how a body made of a given material, having a given shape, and subject to a specified system of forces, would change its shape with time. It may be said, then, that the problem of plasticity resolves itself into, first, the problem of the rates of pure shear processes, and second, the application of what is known about pure shear to actual cases. It is the purpose of this work to investigate the former problem -i.e., the dependence of shear rates on temperature, stress, etc.-from the standpoint of recent developments in the field of chemical-rate theory and with particular reference to the phenomena occurring in the creep of metals and in the plastic flow of crystalline solids in general. It is left for the mechanical engineer, and perhaps the expert in hydrodynamics, to deal with the problem of applications1 RESOLUTION OF MACROSCOPIC SHEAR INTO MICROSCOPIC MOVEMENTS; RESEMBLANCE TO CHEMICAL REACTIONS Just as any large body is made up of many small units, or atoms, so macroscopically observable shear is the result of many microscopic unit shear processes; just as the understanding of the behavior of large bodies demands the understanding of the atoms of which it is made, so the understanding of macroscopic shear demands the understanding of these fundamental unit processes. The study of shear from this "atomistic" point of view has made considerable progress. There has been fairly complete understanding of shear processes in gases for a long time, at least for nonturbulent flow, as a chapter on gaseous viscosity in any text on the kinetic theory of gases will prove. In recent years Andrade2 and Eyring3 have presented important theories for the flow of liquids and amorphous solids. Becker,4 Orowan,5 Taylor,6 Burgers,7 and Kanter8 have considered the

Jan 1, 1941

By C. D. Demond

In reverberatory smelting, fuel is the chief item of expense, as it commonly is in processes using large percentages of it. Hence the most suitable supply is eagerly sought; that is, the supply which, in the end, yields the greatest net profit. The better grades are not infrequently bought, even at an advanced price, because they are apt to be decidedly more economical. High price, of itself, however, is no merit, for freight is generally the largest part of the cost of fuel, and the nearby supply may yield as high efficiency as that from a greater distance. If a poorer grade is reasonably good, and if its cost is low enough to more than offset the decreased technical efficiency, it is of course the more suitable. Any smelting operation depends for both efficiency and economy on raising the furnace atmosphere considerably above the "critical" temperature; that is, above the temperature at which smelting is completed. If this temperature is not exceeded, smelting stops, no matter how much coal is burned; and the real value of a fuel depends on the number of degrees that the temperature is continuously kept above this point. For example, if one fuel maintains 2,500" F. and another only 2,100 F., while the "critical" temperature is 2,000" F., the first is worth at least five times as much as the second, although the increase above atmospheric temperature is only one-fifth more in one case than in the other. This "margin of temperature" above the smelting point is much more significant than the total number of heat units developed from the fuel. The case is parallel to that of water flowing from a pipe. The reservoir may contain a billion gallons of water; but, even though the fluid has come to the nozzle, not a drop will run out, where it can be of practical use, unless the level in the reservoir is higher than the nozzle; and the speed and volume of flow depend on how much higher the level is in the reservoir than at this point. If the temperature in a furnace is not above the critical level there will be no slag to flow over the skimming plate, even though there are enough heat units to bring an unlimited quantity of charge up to the point of slag formation; and just as the value of a water supply for the purpose of putting out a fire depends largely on the effective head, so the difficulties of furnace management

Jan 1, 1915

By B. C. Allen

The solubility of chromium in liquid silver and that of molybdenum and tungsten in liquid tin have been determined by equilibrating Ike Liquid in a crucible of the solule metal. Generally the weight of solute in solulion was delermined both chemically and from crucible weight losses. The resulting weight percent solubilily of chromium in silver as a function of absolule temperature T is given by log w = -6660/T + 4.02 in the range 960° to 1445°C, and that of molybdenlttrl in tin by log w = —5050/T + 1. 79 in the range 1200° to 2200°C. The values appear unaffected by minor changes in solute composition. Calculations aye made of the parlial molar heal and excess entropy of mixing. The estimated solubility of tungsten in tin is 0.001 pct at 2000°C. Evidence is presented that molybdenwm dissolves in tin without compound for mation and that tungsten and tin form W10Sn. RECENT developments in coatings, heat transfer, and brazing require a knowledge of equilibrium solubilities in a variety of systems at elevated temperatures. Of particular interest are solid-liquid interactions in metal systems involving dilute solutions. This investigation was undertaken since little is known about the phase relations or solubility of chromium in liquid silver or of molybdenum and tungsten in liquid tin.1,2 EXPERIMENTAL WORK As indicated in Table I, high-purity metals or those of known impurity levels were used. Crucibles were machined from chromium, molybdenum, and tungsten bar stock 1.3 cm diam and 2.2 cm long. Chromium rod was prepared by arc melting and extruding iodide process crystals.3 The five chromium impurity alloys were in the form of 0.6-cm-diam swaged rod. A Cr-0.06N* alloy was prepared by exposure to NH3 at 1150°C in a closed quartz capsule for 24 hr. Because significant nitrogen was lost during annealing in argon at 1600°C,4 the estimated level was 0.01 pct N. Chromium and Mo,W crucibles were outgassed at 1200" and 1600°C, respectively, at 3 X 10-5 mm. The solvent was placed In crucibles of the solute metal- 6 g Ag in chromium, 0.4 g Ag in the five chromium impurity alloys, and 4 g Sn in Mo,W crucibles. The silver and tin series were outgassed at 900" and 110O°C, respectively, and held at the desired solution temperature in a tantalum resistance furnace under 1.05 atm 99.995 pct Ar. An equilibration time of 0.5 to 1 hr was chosen since 0.3-, I-, and 4-hr anneals at 1235°C for Cr-Ag yielded similar results. Temperatures were measured optically to +10°C under essentially black body conditions which were checked against the melting point of silver. The Cr-Ag and Mo-Sn,W-Sn series were respectively equilibrated at 990° to 1400°C and 1200" to 2000°C. Vaporization losses were generally held to <1 pct by the argon. In the 1800" and 2000°C anneals for 0.5 hr, the crucibles were placed in tightly sealed tantalum cans which kept tin losses to <5 pct. After the anneals, the specimens were furnace-cooled. One anneal was made on small Mo-0.02 C, Mo-0.5Ti-0.lZr, and tungsten crucibles containing tin at 2200°C. The metals were sealed in an electron-beam-welded tantalum can of minimum volume. After the anneal, tin was still present in each crucible, none of which was severely attacked. After equilibration, the saturated solvent metal was selectively removed from the crucible by acid leaching. Weight losses sustained by the crucibles were determined from the initial weight minus the final blank-corrected weight after acid leaching. Chemical analyses were performed on some of the samples. Hot 1:l HNO3-H2O removed silver from chromium with the blank running <0.1 mg or <0.002 pct on measured solubility. Tin was removed from molybdenum and tungsten by hot concentrated HC1 with the respective blanks amounting to -0.004 and -0.0004 pct in the presence of tin. The insoluble residues were weighed and checked for composition. The leaching solutions contained traces of the solute metals which were analyzed by colorimetric methods, Diphenyl Carbazide for chromium, Thiocyanate for molybdenum, and Dithiol for tungsten. The total of the two percentages found from the residue and leaching solution minus the blank gave the desired solubility values. On the basis of annealing empty molybdenum and tungsten crucibles, weight losses due to MoO3 or WO3 volatilization were found to be generally 10.4 mg and affect measured solubilities by <0.01pct. RESULTS AND DISCUSSION Chromium-Silver . Since no intermediate compounds are reported to form in the Cr-An system,&apos; crucible weight losses and chemical analysis of the entire melt should provide reliable measures of the chromium in solution. Values obtained by the two methods are in agreement as shown by the results for unalloyed chromium in Table II and plotted in Fig. 1. Furthermore, the results are consistent with those previously determined by melting equilibrated silver out of the crucible and analyzing calorimetrically for chromium.&apos; On the basis of limited thermal analysis data, the solubility of chromium in silver has been quoted as 8 pct at the monotectic temperature of -1445°C.1 This investigation indicates an extrapolated solubility of 1.38 pct which is believed to be more reliable. At the eu-

Jan 1, 1968

By John S. Johnson, Thomas Fraser

SIZING is the process of separating mixed particles into groups of particles all of the same size, or into groups in which all particles L range between certain definite maximum and minimum sizes. In coal preparation, sizing is generally accomplished by passing the coal over screens. Separation by differential settling in air or water currents has been adapted to the special field of separating very fine sizes, and these processes are in commercial use to a relatively small extent in the coal industry. Separation with screens is a very old industrial practice. Agricola 1 described the use of screens for ore treatment in the middle ages. In the literature of the British coal industry references were made to the screening of coal as early as 1589, but the practice of extensive sizing for the market did not become general until the last half of the nineteenth century. In America, the practice of sizing developed first in the Pennsylvania anthracite region, beginning with the use of rakes2 in the mine working places to recover coarse coal. This mining procedure left the fines in the mine. Preparation outside the mine started with the installation of stationary cast-iron plates with 4 to 6-in. square holes. The run-of-mine coal was dumped upon the platforms, the large pieces of rock were picked out by hand, and the large lumps of coal were broken with hammers. The term "breaker," which still applies to the anthracite-preparation plant, originated with this practice, but the term is no longer descriptive of the entire function of the plant. In 1884, the first power-operated anthracite coal breaker3 was erected by Gideon Bart at his colliery at Wolf Creek near Minersville, Pa. This plant utilized a system of rolls for breaking the coal and revolving screens for sizing. The plant was driven by a steam engine. It could handle

Jan 1, 1943

By W. J. McKenna

The International Smelting Co. concentrator at Tooele, Utah, first operated on a custom basis for the treatment of lead-zinc-iron ores on Nov. 1, 1924, with a capacity of 500 tons per day. On May 1, 1925, the capacity was increased to 1000 tons per day by the addition of another 500-ton section. The concentrator has since operated on the two-section basis, each treating 500 tons per day entirely by flotation. Laboratory and Test Mill In connection with the concentrator, a well-equipped laboratory and small continuous testing plant are maintained. The flotation equipment in the test plant is of both the Callow and Mineral Separations Sub-"A" types, so that actual concentrator conditions may be duplicated as closely as possible. Purchasing of Ore A new shipper usually sends to the plant a 25 to 50-lb. samplc, representative of the ore to be shipped. Batch flotation tests are made on this sample to determine its amenability to the concentrator treatment flowsheet and reagent combinations. The results of these tests, which are accurately correlated with those obtained at the concentrator, both as to grades of products and recoveries, determine the actual value of the ore as submitted in the ore purchasing department&apos;s treatment schedule. Hearty cooperation has existed at all times between the ore purchasing and operating departments in the selection of ores as conccntrator feed. Ores Treated The basic tonnages for mixtures on the two sections come from the Park City and Bingham mining districts. The Park City tonnages arc received by rail and consist of crude ores and gravity mill products. Those from the Bingham district arc received by rail and aerial tramway,

Jan 1, 1928

By George W. Maynard

IN the course of an examination of some of the California hydraulie mines in November last, I visited the property of the Gold Run Ditch and Mining Company, near Dutch Flat, Placer County. This is one of the most important and extensively worked mines in the district. The gold occurs in the characteristic blue gravel, which averages 175 feet in thickness, the lower 40-60 feet being made tip of cement gravel, which resists the action of water, and can only be loosened by blasting. The specimen which I have the pleasure of laying before the members was presented to me by Mr. I. L. Gould, the intelligent superintendent of the mines, who informs me that he found it in the old river channel, about twelve feet above the bedrock. The flattened water-worn nugget of gold, about the size of a kidney-bean, is imbedded in blue cement gravel, around which quartz has crystallized. When found the projecting portion of the nugget was enveloped in quartz, the core of gravel and gold having only been discovered after breaking the lump of quartz. On the quartz there is a shell of cement. The specimen is a remarkable confirmation of the theory of the deposition of quartz from solution. DISCUSSION. DR. T. STERRY HUNT, in commenting upon this occurrence, remarked that it is in accordance with what we already know of the recency of some of the quartz of this region, and cited the microscopic

Jan 1, 1880

By W. A. Backofen, R. L. Fleischer

Single crystal, bicrystal, and polycrystal tensile tests of aluminum at 4.2°K, 77°K, and 300°K have been used to examine the role of grain boundaries in the deformation process. Results indicate that a grain boundary may affect the extent and slope of easy glide. The stage II hardening rate, on the other hand, is independent of the presence or absence of grain boundaries. This conclusion allows the size of the region of multiple slip caused by an incompatible grain boundary to be determined. For the size of bicyystal sample used in this study, multiple slip occurs in about half of the cross section. PREVIOUS studies of the stress-strain characteristics of bicrystals of face-centered-cubic metals have been limited to aluminuml-5 at room temperature. Recent results, however, indicate that the stress-strain curves of single crystals of such metals may be separated into at least three stages6 in which different deformation processes are occurring7 provided testing is done at sufficiently low temperatures.&apos; Since for aluminum a well-defined stage II develops only below room temperature, previous studies have not been able to relate effects of grain boundaries to all of the three stages of deformation. It is therefore to be expected that low-temperature deformation of aluminum single crystals and bicrystals should clarify the effects of grain boundaries on the different processes of deformation. EXPERIMENTAL PROCEDURE Single crystals and bicrystals were grown from the melt by the standard techniqueg with aluminum reported by Alcoa to be 99.993 pct pure. Ridges in the boat were used to guide the grain boundary during growth, assuring that the boundary would bisect the sample.10 The rate of furnace motion during growth was 1.0 cm per hr. During growth zone purification resulted, as evidenced by the ability of the first material to freeze to recrystallize at room temperature following severe deformation. Samples were approximately 4.4 X 6.6 mm in cross section and 103.5 mm in length between grips. Samples were annealed at 635" i 5°C for 40 hr and furnace cooled over a 7-hr period. They were then electropolished in a solution of 5 parts methanol to 1 part perchloric acid at a current density of 15 amp per sq dm for about 30 min at temperatures below 0°C. Tensile testing was performed at 295" (room temperature), 77" (sample in liquid nitrogen), and 4.2"K (sample in liquid helium) on the hard-type machine indicated schematically in Fig. 1. The machine con- sists basically of a tube surrounding a rod; one end of the sample is attached to each member, and the rod is pulled up the tube to extend the sample. The rod is rigidly mounted and is moved vertically by a system described by asinski." The pulling force is measured continuously by an electrical strain gage load cell, and the relative displacement of the tube and rod is also recorded continuously by a soft cantilever beam with electrical strain gages. Maximum stress and strain sensitivities were ±2g per sq mm and * 3-10-5. In all tests the strain rate was approximately 5.10-5 per sec. The thin wires in the tensile apparatus introduce softness, which may be corrected for, however, by measuring load vs displacement with the sample replaced by an elastic member. For loads greater than 15 kg the spring constant is 1.875.106 g per cm. The flexible wires also served to reduce substantially the large shearing forces which may arise in the case of grips having horizontal rigidity.&apos;&apos; As in any gripping system, however, bending moments will arise in the course of deformation by single slip. Engineering stress, s = (load)/(original cross-sectional area), and strain, E = (increase in length)/ (original length), are used for stress-strain curves unless otherwise indicated. Tables list resolved shear stress, T=mo and shear strain ? = dm, where m is the usual Schmid resolved shear stress factor for the primary slip system at the start of deformation. The first group of samples to be described forms an isoaxial set, all of the crystals making up the single crystals or bicrystals having the same tensile axis, the orientation of which is indicated by the cross in Fig. 2. For this orientation the primary slip plane and slip direction make angles of 45 deg with the tensile axis and the Schmid factor m has its maximum possible value of 0.5. Rotations about the tensile axis are indexed by means of an angle 0 between the small-area surface of the samples and the projection of the primary slip direction onto the cross section, as defined in Fig. 3. In single crystals, values of 0 were 0 and 90 deg, while in bicrystals 0 values were (0 deg, 180 deg), (90 deg, 270 deg), and (0 deg, 90 deg) as indicated in Fig. 4.

Jan 1, 1961

By Auguste J. Rosh

The use of titaniferous ores in the blast-furnace has been the subject of much controversy for many years. Divers objections have been raised against them, and, for one cause or another, the verdict

Jan 1, 1893

By F. Keller, J. D. Edwards

THE anodic treatment of aluminum presents problems of scientific as well as of commercial interest.1-3 Of particular interest is the fact that, during the anodic oxidation process, the oxide continues to form at the metal-oxide interface under any oxide previously formed. This has led to speculation as to the mechanism involved in the formation of the relatively thick oxide coatings that are used commercially for decorative or protective purposes. Furthermore, the ability of certain types of oxide coatings to adsorb dyes and other substances has stimulated research to determine the actual structure of these adsorptive coatings. It has been found that anodic oxide coatings on aluminum are composed essentially of aluminum oxide. They are formed by the action of oxygen ions penetrating to the metal surface during the electrolytic oxidation treatment. These coatings can be formed in a number of different electrolytes, as for example, those which contain sulphuric acid, chromic acid, oxalic acid, or boric acid. These are the commonest and most useful electrolytes employed commercially. Except for certain specific conditions of formation, the coatings in general have been found to be amorphous alumina, as far as can be determined by X-ray or electron-diffraction methods. Anodic oxidation processes can be arranged in three rather general classes if they are grouped in relation to the solvent action of the electrolyte on the coating.4 In the first class, the electrolyte has little or no solvent action on the coating that is formed. In general, coatings produced under such circumstances are nonporous and non- adsorptive. In the second class, the electrolyte exerts an appreciable solvent action on the coating. These coatings are porous and adsorptive. Finally, for the third class, the electrolyte tends to dissolve the coating about as rapidly as it is formed. This action produces electrolytic brightening or anodic polishing of the aluminum surface and at most leaves only a very thin film of oxide. The nonporous and nonadsorptive type of oxide film is represented by the coatings that are formed when solutions of boric acid are employed as the electrolyte. It is especially significant that these impervious films are formed in electrolytes that exert little or no solvent action on the coating. Where a boric acid electrolyte is used, the coating tends to form rapidly, with the result that the flow of current is soon reduced to substantially zero. This indicates that the growth of the coating has stopped. As a rule, the thickness of the coating is roughly proportional to the voltage employed for formation and the coatings of this type are exceedingly thin. In an electrolyte of this type, the coating has a high resistance when the aluminum is made anode; consequently, any current that may flow (leakage current) is very

Jan 1, 1944

By John R. Low

A number of cases of low-temperature, intergranu2ar brittle fracture of metals containing small amounts of certain impurities, have now been identified. Some degree of understanding of this phenomenon exists for the simpler binary systems of a metal and a single impurity, but the profound effects of other impurities and alloying elements in modifying this type of behavior remain unexplained. Current research in this area is reviewed and some of the newer techniques of investigation which should make possible a more quantitative study of the structure and composition of grain boundaries in impure metals are described. To indicate the subject matter of this lecture, we may begin by reviewing the experimental observations concerning low-temperature intergranular brittleness in impure metals, particularly those examples in which the embrittlement appears to result from what has been called "equilibrium grain boundary segregation."&apos; These are the systems in which it has been impossible, at least up to now, to detect the presence of any second phase film at the brittle interfaces. When second phase films are present they are usually readily detectable by fractographic methods, often appearing as epitaxial films in geometric or dendritic patterns. An example is shown in Fig. 1 for the case grain boundary carbides in a sensitized stainless steel which failed by intergranular brittle fracture at 78?k2 In contrast to this type of embrittlement there are numerous examples of low-temperature intergranular embrittlement in which the fractographs are essentially featureless, for example, that of an oxygen-embrittled iron shown in Fig. 2. The only second phase particles visible are the small, widely separated, round oxide particles typical of the bulk material. The fracture surface is extremely smooth and the fracture path appears to follow the intergranular interface without deviation. This type of fractograph also implies that crack propagation has occurred without plastic deformation at the crack tip, since localized slip or twinning ahead of the crack would be expected to distort the interface and be readily visible in the fractograph. Such indications are occasionally seen in these fractographs, but are not characteristic. A second example of this type of fractograph is shown in Fig. 3, which is from a temper-embrittled, carbon-free, Fe-Cr-Ni alloy containing Sb, broken at 1OO?C.3 The similarity to the oxygen embrittled iron case will be apparent. In the case of the temper embrittled Cr-Ni ferrite containing antimony, it is possible to remove the embrittlement by suitable thermal treatment. The grain boundaries may then be examined by thin film transmission in the electron microscope for the material in both the nonembrittled condition and in the embrittled condition. Two boundaries are shown in dark-field transmission in Fig. 4, one in the nonembrittled

Jan 1, 1970

By R. W. Heckel

It has been shown previously that the effect of applied pressure on the density of a metal powder may be expressed by a relationship of the form:

Jan 1, 1962

By Yuri D. Tretyakov, Robert A. Rapp

The stoichiometry ranges ofNiOl+y and LiFe,O,-d were established by high-temperatwe electrochemical meas7rements in a stabilized-zirconia electrolyte cell. The results were consistent with doubly ionized cation vacancies in NiO,+y and interstitial lithium or iron ions in . The defect structure of the ternary ferrite was derived from the consideration of equilibration with respect to oxygen between the solid and the gas phase. The absolute magnitudes of defect concentrations were calculated. Pavtial molar enthalpies of oxygen in the compounds were calculated and interpreted in terms of the enthalpy of defect formation in these crystals. NICKEL oxide (NiO,,?) is a metal-deficient, p-type, extrinsic semiconductor whose properties are consistent with a structural model based on the presence of cation vacancies as the predominant ionic defect at sufficiently high temperatures and oxygen activities. A survey of previously reported conductivity studies and the presentation of some more recent conductivity measurements will be given in a later paper.&apos; The absolute magnitude of the equilibrium vacancy concentration in NiO has been reported from combined conductivity and thermogravimetric data of &apos; However, disagreement exists concerning the state of ionization of the nickel vacancies in NiO. Some authors3-&apos; have proposed that the predominant defects in NiO are singly ionized nickel vacancies and positive holes (h&apos;) formed by the reaction where, accorhng to the notation of Kroger and Vink,6&apos;7 Oq represents an oxygen ion on its normal lattice site. Other authors"27E have proposed that doubly ionized nickel vacancies (V{i ) and positive holes are predominant and are formed by the reaction One purpose of the present investigation was to establish the nature of the predominant defect in NiO,+? as well as its equilibrium concentration and thermo-dynamic properties at elevated temperatures and known oxygen activities. To accomplish this purpose, the coulometric titration of oxygen into and out of NiO was accomplished using a galvanic cell involving the calcia-stabilized zirconia electrolyte. The ternary oxide, lithium ferrite (LiFe50,-6) is ferromagnetic and has the inverse spinel structure LiFe,O,-d Thus, in the ideal stoichiometric XY204 lattice, Fe3 ions occupy one-eighth of the tetrahedral (A) sites, and i&apos; and Fe3&apos; ions share at random one-half of the octahedral (B) sites within the fcc sublattice of oxygen ions.g The structure and thermodynamics of the spinel structures have been comprehensively decribed.&apos;-&apos; A recent compilation of literature for lithium ferrite is also available. 15 Oxygen-excess LiFe50sis not expected to exist because both i&apos; and 17e3& ions are in their highest normal valency states (positive hole formation is not favorable). As will be discussed, equilibration of the ferrite crystal with oxygen of a surrounding gaseous phase will result in the introduction of equilibrium concentrations of ionic and electronic defects. In the Results and Discussion section a defect model for LiFe50,-d is proposed. This defect model is tested by high-temperature coulometric titration experiments. EXPERIMENT The oxygen activities in nonstoichiometric NiOl+, (and also LiFe,O,-d) were measured by means of coulometric titration with the high-temperature galvanic cell The critical characteristic of a suitable experimental cell is the complete isolation of the phase to be investigated in a minimum sized chamber which is free from extraneous sources and sinks for oxygen (leakage). Then oxygen is only admitted to the chamber or removed from it in known amounts by coulometric titration, which involves the passage of oxygen ions through the solid electrolyte with electrochemical oxidation and reduction reactions at the platinum contacts to the electrolyte. The experimental cell is shown in Fig. 1. The cap of the cell was the tip from a closed-end alumina tube, which was found to be leak-free from a helium leak-detector test. This alumina cap was about 1.2 cm OD and about 1.5 cm high. A Zircoa calcia-stabilized zirconia tablet (crucible lid) of 1.5 cm diam and 0.3 cm thickness served as the solid electrolyte. A Pyrex ring of about 0.1 cm thickness was placed between the electrolyte and the cap. The electrolyte tablet was painted with platinum paste on the entire outer face and on that part of the inner face which would be within the enclosure; these electrodes were further prepared by heating in air at 1000°C for 2 hr. Nickel oxide powder, listed as 99.999 pct pure, was purchased from Leico Industries, Inc. Pills of the NiO were cold-pressed and sintered at 1050°C for 3 hr in a platinum crucible. This poorly sintered NiO was crushed, and chunks were wrapped in 52-mesh Pt gauze (to catalyze the solid-gas exchange) for place-

Jan 1, 1970

By E. P. Abrahamson II

The effect of transitiorz element bitzary solid solution additions upon the recrystallization temperature of columbium has been investigated. The elements Mn, Fe, Co, Ni, W, Re, and 0s OWY the yecystallization tempel-aturye, while Ti, V, CY, zr, Mo, Ru, Rh, Pd, Hf, Ta, W, Ir, and Pt mise it. A correlation is kloted between the rate of chatzge of recyystallization tewaperature with atomic hercent solute and the free atom electron configuration of the solute element. The work of Abrahamson and Grant1 has indicated a correlation between the free atom ground-state electron configuration and the change in brittle-ductile transition temperature per atomic percent solute in chromium base alloys. A similar correlation was observed for the change in the recrystallization temperature of iron base alloys by Abrahamson and Blakeney and Abrahamson. It was also observed that the limit of rapid change in recrystallization temperature also Correlated with the electronic configuration of the free solute atom. A further study by Abrahamson4 established the generality of the phenomenon by yielding similar results for vanadium base dilute alloys. It has been inferred that a peri- odicity might be expected with changes in the free atom electron configuration of the solvent element. This study is the third set of transition base metal systems to be studied. It is the object of this and further studies on transitional metal systems to detect any systematic variations in the observed correlation which might contribute to the understanding of the electron interactions which are evidently exhibiting themselves. PROCEDURE All alloys were made using 99.9 pct Cb with 0.030 Ta, 0.016 0, 0.0025 H, 0.003 Mo, 0.021 Fe, 0.005 C, and 0.002 N. The solute elements were 99.9 pct pure. According to the published binary phase diagrams5 and metallographic examinations at X750, all additions were in solid solution. The alloys were arc melted and remelted 6 times in the form of cubic 400-g buttons under an argon atmosphere. They were then hot forged at 1200oC to 0.6-in. diameter, annealed for 3 hr at 1200o under argon, and furnace cooled. The specimens were then machined to 0.400 -in. diameter. Grain size was checked and found to remain essentially constant at 150 i 30 grains per sq mm. The specimens were then cold swaged to 0.187-in. diameter, yielding 46 i 1 pct cold work. All alloys were chemically analyzed for the major solute. Analyses of random samples indicated that the impurity content remained at the values of the starting material. Tungsten contamination was held to 0.007 pet.

Jan 1, 1962

By W. M. McKewan

Magnetite pellets were reduced in flowing hydrogen at pressures up to 40 atm over a temperature range of 350° to 500°C. The rate of weight loss of oxygen per unit area of the reaction surface was found to be constant with time at each temperature and pressure. The reaction rate was found to be directly proportional to hydrogen pressure up to 1 atm and to approach a maximum rate at high pressures. The results can be explained by considering the reaction surface to be sparsely occupied by adsorbed hydrogen at low pressures and saturated at high pressures. PREVIOUS investigation1,2 have shown that the reduction of iron oxides in hydrogen is controlled at the reaction interface. Under fixed conditions of temperature, hydrogen pressure, and gas composition, the reduction rate is constant with time, per unit surface area of residual oxide, and is directly proportional to the hydrogen pressure up to one atmosphere. The reduction rate of a sphere of iron oxide can be described3 by the following equation which takes into account the changing reaction surface area: where ro and do are the initial radius and density of the sphere; t is time; R is the fractional reduction; and R, is the reduction rate constant with units mass per area per time. The quantityis actually the fractional thickness of the reduced layer in terms of fractional reduction R. It was found in a previous investigation2 of the reduction of magnetite pellets in H2-H,O-N, mixtures, that the reaction rate was directly proportional to the hydrogen partial pressure up to 1 atm at a constant ratio of water vapor to hydrogen. Water vapor poisoned the oxide surface by an oxidizing reaction and markedly slowed the reduction. The enthalpy of activation was found to be + 13,600 cal per mole. It was also found that the magnetite reduced to meta-stable wüstite before proceeding to iron metal. The following equation was derived from absolute reaction-rate theory4,8 to expfain the experimental data: where Ro is the reduction rate in mg cm-2 min-&apos;; KO contains the conversion units; Ph2 and PH2O are the hydrogen and water vapor partial pressures in atmospheres; Ke is the equilibrium constant for the Fe,O,/FeO equilibrium; Kp is the equilibrium constant for the poisoning reaction of water vapor; L is the total number of active sites; k and h are Boltzmann&apos;s and Planck&apos;s constants; and AF is the free energy of activation. Tenenbaum zind Joseph5 studied the reduction of iron ore by hydrogen at pressures over 1 atm. They showed that increasing the hydrogen pressure materially increased the rate of reduction. This is in accordance with the work of Diepschlag,6 who found that the rate of reduction of iron ores by either carbon monoxide or hydrogen was much greater at higher pressures. He used pressures as high as 7 atm. In order to further understand the mechanism of the reduction of iron oxide by hydrogen it was decided to study the effect of increasing the hydrogen pressure on rebduction rates of magnetite pellets. EXPERIMENTAL PROCEDURE The dense magnetite pellets used in these experiments were made in the following manner. Reagent-grade ferric oxide was moistened with water and hand-rolled into spherical pellets. The pellets were heated slowly to 550°C in an atmosphere of 10 pct H2-90 pct CO, and held for 1 hr. They were then heated slowly to 1370°C in an atmosphere of 2 pct H2-98 pct CO, then cooled slowly in the same atmosphere. The sintered pellets were crystalline magnetite with an apparent density of about 4.9 gm per cm3. They were about 0.9 cm in diam. The porosity of the pellets, which was discontinuous in nature, was akrout 6 pct. The pellets were suspended from a quartz spring balance in a vertical tube furnace. The equipment is shown in Fig. 1. Essentially the furnace consists of a 12-in. OD stainless steel outer shell and a 3-in. ID inconel inner shell. The kanthal wound 22 in. long, 1 1/2, in. ID alumina reaction tube is inside the inconel inner shell. Prepurified hydrogen sweeps the reaction tube to remove the water vapor formed during the reaction. The hydrogen is static in the rest of the furnace. The sample is placed at the bottom of the furnace in a nickel wire mesh basket suspended by nickel wire from the quartz spring. The furnace is then sealed, evacuated, and refilled with argon several times to remove all traces of oxygen. It is then evacuated, filled with

Jan 1, 1962

There&apos;s a right way and a wrong way to store diesel electric systems and similar equipment for generating on-site power, according to James Frankow, service manager for Allis-Chalmers Corp&apos;s Engine Division. In any event, the less storage the better. Many generating sets are stored before installation, especially when new construction is underway. Improper storage, or mothballing, can create initial reliability problems. Therefore; arrange for inside storage with no drastic extremes in temperature or humidity. If engines and alternators are stored in areas other than inside a dirt-free and temperature-controlled building, the unit or engine should be completely covered and protected against the environment. Before covering it with a canvas or with plastic, the unit should first be sealed at the following critical engine openings:

Jan 3, 1978

By M. Cohen, R. J. Teitel

There is considerable interest in beryllium because of its low density (1.84 g per cu cm), high modulus of elasticity (40 X 106 psi), high melting point (1280°C), and special nuclear characteristics. Moreover, it has fair resistance to corrosion and oxidation. However, the purest beryllium known to the authors is relatively brittle at room temperature, and cannot be fabricated readily. The search for improved properties leads naturally to investigations of beryllium alloys and the phase relationships upon which they are based. The present paper is concerned with the alloys of beryllium and iron, primarily from the standpoint of the equilibrium diagram. Iron was selected (1) because of its all-round importance in metallurgy, and (2) because the beryllium-iron system is known to be quite complex. The most recent diagram in the literature is that of Gaev and Sokolov,&apos; and covers only the iron-rich end up to 16 wt pct beryllium. Beryllium markedly restricts the austenitic field, closing the gamma loop at about 0.4 wt pct (3 at. pct). On the other hand, beryllium is soluble in a-ferrite up to a maximum of 7.5 wt pct (34 at. pct) at the eutectic temperature of 1160"C. The eutectic composition lies at 10 wt pct beryllium (42 at. pct) and corresponds to a mixture of or and FeBez (called j3 in the present paper). The solid solubility of beryllium in the a phase decreases with decreasing temperature, and makes precipitation-hardening possible. These findings substantiate the earlier work of Oester-held,2 Wever and Mueller3 and Laissus.4 In addition to the FeBe2 (ß) mentioned above, Misch6 has reported on FeBes, and indicated evidence for another compound containing still more beryllium. A preliminary diagram by Gordon,5 not hitherto published, is given in Fig 1. Besides the phases previously named, there are shown a solid solution of extended range (e), a compound of limited solubility (t), and a high temperature phase (7). Beryllium is designated as 8. The t field contains the compound composition FeBea, and the f phase undoubtedly corresponds to the beryllium-rich compound found by Misch.6 The region around the { phase was proposed by R. J. Teitel based on Gordon&apos;s data. The details of the diagram are self-explanatory. It was the unusual complexity of this system that prompted the authors to undertake the present studies. By the same token, more emphasis was placed on the beryllium-rich than the iron-rich end of the diagram. Exprimental Details RAW MATERIALS The beryllium employed in this investigation was one of the purest grades available. Its chemical analysis after vacuum melting is given in Table 1. The metal assayed 99.4 wt pct beryllium. Vacuum melted electrolytic iron of purity shown in Table 1 was the source of iron.

Jan 1, 1950

By H. C. George

As the basis for a round table discussion of Petroleum Engineering Education for the February, 1930, meeting of the Petroleum Division, A. I. M. E., the following questions were sent to about 60 of the leading engineers and educators in the petroleum industry: 1. Should there be any changes in the curricula of our courses in petroleum engineering to meet the changing demands of the Industry? If so, what changes?] 2. Should courses in petroleum engineering be offered through university extension? 3. Should the universities offer correspondence courses in petroleum engineering? 4. What should be the character of the graduate work offered in petroleum production engineering? 5. Should summer work in the oil fields, on pipe lines, or in oil refineries be required of undergraduates? If so, how much and of what character? The following men replied to the questions: G. B. Corless, Humble Oil & Refining Co., Houston, Texas. J. R. McWilliams, Skelly Oil Co., Tulsa, Okla. W. W. Scott, Humble Oil & Refining Co., Houston, Texas. H. H. Power, Gypsy Oil Co., Tulsa, Okla. L. G. E. Bignell, Oil K. Gas Journal, Tulsa, Okla. E. L. Estabrook, Pan American Petroleum & Transport Co., New York, N. Y. F. P. Donohue, Pan American Petroleum & Transport Co., New York, N. Y. C. 0. Rison, lndian Territory Illuminating Oil Co., Bartlesville, Okla. L. B. Holland, Phillips Petroleum Co., Bartlesville, Okla. H. J. Kemler, Shell Petroleum Corpn., St. Louis, Mo. C. A. Bonine, Pennsylvania State College, State College, Pa. J. 0. Lewis, Dunn & Lewis, Tulsa, Okla. A. G. Heggem, Tulsa, Okla. J. M. Lovejoy, Petroleum Bond & Share Corpn., New York, N. Y. B. B. Boatright, Colorado School of Mines, Golden, Colo. A. C. Ruble, Union Oil Co. of California, Los Angeles, Calif. J. B. Umpleby, Goldelline Oil Corpn., Oklahoma City, Okla. R. S. Knappen, Gypsy Oil Co., Tulsa, Okla. K. C. Heald, Gulf Companies, Pittsburgh, Pa. K. C. Sclater, Exchange National Bank Bldg., Tulsa, Okla. F. G. Tickell, Stanford University, Stanford University, Calif.

Jan 1, 1930

By Francis Lucas

ANY metal which contains even a small percentage of aluminum possesses certain peculiarities of appearance and properties which are exhibited both when the metal is melted and after it solidifies. Pure aluminum, or an alloy containing a small proportion of aluminum, can be melted without flux-except for a layer of charcoal-because a film of aluminum oxide and metal forms at the surface of melted aluminum. Although very thin, this film is air-proof, and it prevents the metal underneath from oxidizing. This oxidized film does not move easily on account of its toughness and high surface tension. One very important point in connection with this process of still casting has not been strongly enough stressed, namely, that the same kind of surface film with the same peculiarities forms over the surface of all melted alloys that contain even a small proportion of aluminum. Experienced foundrymen know how desirable it is to cast aluminum under its "skin" or-under the surface of the film which tends to remain still. In the case of red copper, when in fusion, the surface shows pure copper only. This is due to the fact that liquid copper constantly absorbs the copper oxide which forms on the surface. By closely examining melting copper the oxide can be seen dissolving in the bath, and going into solution just as pulverized sugar dissolves in water. When copper is cast in the open, either in wire bars or cakes, the surface of metal exposed to the air is covered by a film of black, oxide that cannot be absorbed by the metal.

Jan 1, 1927

By George R. Ensminger, E. Heaton Hemingway

During the past year, the Watertown Arsenal has been interested in the occluded gas and oxide content of certain ordnance steels in order to determine, if possible, whether some of the peculiar failures in their physical properties might not be traced to these causes. For the purpose of best accomplishing a study of this nature, it was decided to heat the various samples of steel in a vacuum for definite periods of time at high temperatures and carefully examine the quantity and composition of the gases evolved. By the use of a fused quartz tube fitted with a water-cooled, ground-glass stopper, it was possible to maintain a vacuum at a temperature of 1000" C. for 10 hr. without perceptible leakage being evidenced as measured by a McLeod gage. The silica tube was connected with an evacuating system so constructed that the volatilized gases could be removed from time to time and a low vacuum of 0.0002 to 0.0010 mm. of mercury continuously maintained. At no time during the period of heating or in the removal of the gases did the evacuated system come in contact with rubber stoppers or any rubber connections, making contamination from such a source, impossible. In other words, the only volatile products that could be: obtained must necessarily have come from the steel itself or from the glass and fused quartz system or from the mercury used as a sealing agent. In the carlier experiments, the steel treated was in the form of turnings, but this practice was discarded because the weight&apos;s of the turnings before and after being heated were widely inconsistent,, even when taken from the same piece of steel. This discrepancy developed largely through variation in the amount of metal volatilized with the gases; this metal could always be seen in the form of a ring where it condensed in the cooler portion of the tube in either the amorphous or crystalline condition. Because of the frequency in occurrence and the variation in the manner of deposition, this material was roughly analyzed and found to consist for the most part of iron. At the same time two samples of steel that had been

Jan 1, 1922