By J. L. Brimhall, R. A. Huggins, M. J. Klein

IN a recent paper1 it was shown that small additions of magnesium, copper, and oxygen decrease the stacking fault probability in plastically deformed silver. Correlation of :X-ray data with measurements of the twinning frequency and metallographic observation of slip lines indicated that this effect may be due to an increase in the relative stacking fault energy. It is the purpose of the present note to report experiments on these alloys of known stacking fault probability that relate to the stacking fault contribution to electron scattering in silver. There has been a considerable amount of disagreement in the literature concerning the contribution of dislocations to electrical resistivity in metals. Calculations relating to the scattering of conduction electrons by the dislocation core, its strain fields, and related effects have been made by several authors.2-5 In addition, experimental work on Cu,3,6-10 Ni,11 and Ni-Co alloys1:! has shown that dislocations in those materials exert an anomalously large effect on resistivity, this effect being related to the presence of extended dislocations. The problem of the scattering due to the stacking fault region between partial dislocations has been treated theoretically using several different procedures.13-'0 The results of these calculations show a wide range of predicted values, from rather large to completely negligible, due to the models and the approximations involved. Almost all of this work has been applied to the specific problem of scattering in copper. The more complete theoretical treatments depend rather critically. on the shape of the Fermi surfaces and the effective mass parameters. The scattering from stacking faults might therefore be expected to vary significantly from one metal to another. Unfortunately, sufficiently accurate information is not available .which would allow one to have any confidence in a theoretical prediction of the scattering in the case of silver. Resistivity measurements were made on small wire specimens of vacuum melted high purity silver and several dilute alloys. These measurements were made at approximately 20°C, with great care being given to temperature measurement and corrections. At such temperatures phonon scattering is significantly greater than imperfection scattering. However, the experimental technique was such that measurements on similarly treated samples were reproducible to better than 2.4 X 10-9 ohm-cm, which was satisfactory for this work. Values of the stacking fault probability and the increase in resistivity after severe plastic deformation are given in Table I. The increases in resistivity resulting from plastic deformation agree quite well with previous work on silver.14,21-26 In addition, it has been previously found that interetitials and vacancies in silver anneal out well below room temperature, so that the residual imperfection scattering in these experiments could be expected to be primarily associated with dislocations;. It is seen from the data in Table I that large changes in stacking fault probability are accompanied by differences in resistivity due to imperfection scattering of only a few percent. If the scattering of conduction electrons by extended dislocations is primarily due to the area of the stacking fault region independent of the stacking fault energy, and not the core and strain fields associated with partial dislocations, the resistivity increase should be proportional to the product of the dislocation density and the stacking fault width, as is the stacking fault probability. Therefore, the imperfection scattering caused by plastic deformation of the alloys should be considerably smaller than that found in the pure silver. Since this was not observed, these results sugegest the possibility that stacking faults do not themselves contribute appreciably to the electrical resistivity of silver deformed at room temperature. An alternative explanation of these observations is that the scattering by the stacking fault is roughly proportional to the stacking fault energy, rather than being determined by the total area of such faults. Sufficient evidence is not yet available to separate these two possibilities. This work was supported by the Office of Naval Research.

Jan 1, 1962

By Stephen G. Wright

Jan 1, 1985

By R. W. Smith

IN the manufacture of portland cement, the basic and fundamental essential is a limestone uniformly rich in calcium carbonate and carrying less than 3 per cent magnesium carbonate. In searching for such a deposit, also having in mind quantity of rock, accessibility and quarrying facilities, the Pacific Coast Cement Co. discovered and developed its present quarry at View Cove on the east coast of Dall Island, Alaska. Dall Island is about 100 miles west of Ketchikan and 650 miles north from Seattle. It is 70 miles in length and 5 to 10 miles in width. The climatic conditions are much more favorable than would be expected. The temperature ranges from zero to 70 degrees. The precipitation is considerably more than at Seattle, although there was less snow during the last season than at Seattle. The island is rugged and mountainous; the vegetation is moss and grass and a large portion is timbered with spruce, hemlock and cedar. Some of this timber has market value. The limestone quarry is about 30 miles north of the extreme southern end of the island. The company acquired 240 acres which contain limestone of remarkable uniformity, the percentage of calcium carbonate being about 95. It is estimated that there is ample recover- able rock on the holdings to supply the cement plant at its maximum capacity for well over 100 years.

Jan 1, 1929

By R. HAYDEN, H. B. HALLOWELL, H. O. Hofman

THE object of refining copper in the reverberatory furnace is to obtain a metal which will have the highest attainable degree of malleability, ductility and electric conductivity, and present at the same time a level surface when it solidifies in the mold after casting. These desirable physical properties are governed by the character of the impurities and the forms in which they are present, by the amount of cuprous oxide retained by the copper, by the quantity of gas held in solid solution, by the casting-temperature, and by the thickness of the casting. The effects of impurities, of cuprous oxide and of gases upon the mechanical properties of copper have been studied by Hampe in his classical paper "Contributions to the Metallurgy of Copper." The most recent research into the effect of metals upon the electrical conductivity of copper is that of Addicks.2 The influence of cuprous oxide upon the electrical conductivity has been investigated by Walker' and Addicks.4 The absorption of gases has received' attention by Hampe,5 Stahl 6 and Heyn.7 The effects of casting-temperature have been noted by Stahl.8

Mar 1, 1907

"With a total value to date of well over $200,000,000.00 for its ore production, the Tintic mining district, which is about 100 miles southwest of Salt Lake City, ranks as one of the three main ore producing areas of Utah. In it are located the biggest silver mines of the country, silver having been the chief metal produced in the camp since its start. Tintic's silver production to date has a total value of over $ 100,000,000, approximately half of the value of the camp's ore production, the balance being roughly divided among lead, gold and copper.Discovery of the camp was made in the late sixties. Lack of transportation and ore reduction facilities delayed extensive development of the area for nearly a decade.In recent years Tintic's ore production has ranged from 350,000 to 400,000 tons annually. In 1 924 the camp produced one-eighth of the silver produced in the nation with an output of 7,729,700 ounces. Its lead production was 77,765,000 pounds and its gold production 26,285 ounces.The known mineralized area of the district is found in a broad syncline striking north and south. The west limb plunges sharply and extends for a distance on its dip of approximately one and a half miles to the trough. The east limb raises gently through a distance of about two miles to the east limit of known mineralization. This general structure is broken by local faulting throughout the district, the local structural conditions playing an important part in the ore deposition. The north end of the fold is obscured by a rhyolite flow and the south end stops against a monzonite stock."

Jan 1, 1925

By Brahm Prakash, R. Schuhmann

Chemical conditions for flotation and nonflotation of quartz with oleic acid as collector and barium, calcium, aluminum, iron, and tin as activators were studied using a simple vacuum-flotation technique in glass-stoppered graduates. The detailed study of barium activation led to an interpretation based on ideal Langmuirian chemisorption.

Jan 1, 1950

By Joseph M. Jacisin

Fatigue tests were conducted on 2017-T4 alumium in alloy in an u1lrcthig.h vacuum of 2 x 10-lo Torr and in air. The vatio of vacuum-to-air faligue life for this ~malerial varied Jrom 3.5:1 at a strain of 2.5 X 1O-3 ill. pegr in. to 8:l at a strum of 3.3 x X ill. per 171. Sotlze pvelivtlinary data were also obtained on the faligue life of the alumirnum alloy in a dvy-nitrogen atmosphere. A dark deposit observed on the fracture surfaces of the aiv-tested specimens was identified as oxides of tr~angarzese and magnesium This observalion, and the close correlalion betaveen results obtained in vaCuum and dry-nitrogen environtments, tend to confirm that air stvongly influences the fatigue mechanism by a covrosion process. THE fatigue life of certain metals is known to increase when the atmospheric pressure is reduced. Gough and Sopwith1-2 postulated that this is due to a joint chemical and mechanical process operating in air at the surface of the metal with oxygen and water vapor playing significant roles. Wadsworth and Hutchings3 observed that aluminum is mainly affected by the presence of water vapor. Very little information is available on the fatigue properties of structural aluminum alloys in a vacuum environment. This report describes work performed on 2017-T4 aluminum alloy in an ultrahigh vacuum (2 x 10-loTorr) and in air. Some preliminary data are also presented on the fatigue life of the alloy in a dry-nitrogen environment. 1) EXPERIMENT 1.1) Test Material. The material tested was commerciaT 2017-T4 aluminum alloy which, in addition to aluminum, has an approximate composition of 4 pct Cu, 1 pct Fe, 0.8 pct Si, 0.5 pct Mg, 0.5 pct Mn, plus smaller amounts of other elements.* Some typical naturally age to a substantially stable condition. Specimens were then machined from these rods and ground to a No. 8 microfinish. In order to minimize variation in material characteristics, specimens were made from rods procured from the same lot. 1.2) Apparatus. The apparatus and test specimen used in the fatigue tests are shown in Fig. 1. The device utilized a single-cantilever beam with rotating-bending loading. Bending stress was applied to the fatigue test specimen by placing a spacer beneath the bearing support, thereby providing a constant deflec-

Jan 1, 1968

By Albert Smith

THE creep properties of metals have as-sumed increasing importance in recent years and many investigations have been made on various phases of the problem. In the past year the annual lectures of the Insti-tute of Metals Division1 and the Iron and Steel Division2 were concerned with this subject, and are excellent reviews. For many years the creep properties of lead and lead alloys have been investigated at the Central Research Laboratories of the American Smelting and Refining Co., and it is hoped that the present paper will contribute knowledge of some of the factors that influ-ence creep. Lead, being a metal that recrys-tallizes readily at room temperature, is an excellent material upon which to investi-gate creep phenomena because of the sim-plicity of the apparatus needed, and it might be expected that results would apply to some extent to elevated-temperature tests of other metals.

Jan 1, 1940

By J. T. Norton, N. J. Grant, I. S., Servi

Coarse grained high purity aluminum was tested in creep at temperatures of 400° to 1200°F to develop subgrain structures. Measurements of subgrain size, distribution, and rotation were made from X-ray diffraction patterns. Subgrain size and distribution were checked metallographically and the size was compared with average slip band spacing. The slip family was determined for several specimens. THE interest and research recently evident abroad in the role of subgrain formation and polygon-ization as a contribution to the creep of metals at elevated temperatures is deserving of greater attention in this country. Such metallic subgrains can be defined as macroblocks existing within the grains. The general observation has been that the macro-blocks which belong to the same grain have a maximum difference in orientation of a few degrees. In spite of the considerable amount of work that has been done since Jenkins and Mellorl observed the "division of existing crystals into smaller units when deformation occurs at an annealing temperature," the subject of subgrain formation is only now receiving truly active discussion and investigation. The existence of subgrains has been revealed by metallographic methods, as in the work of Jenkins and Mellor,1 and by X-ray methods, first applied to this problem by Homes.' Hirst3 and Calnan and Burns4 applied the back-reflection Laue technique to the study of coarse grained specimens. Wood et al.5 and Greenough and Smith' examined the ring obtained with a back-reflection camera for the study of fine grained specimens. In addition to the above, the transmission technique was used by Wood.6 A special technique was developed by Guinier and Tennevin8 in order to improve the resolution. Metallographically, the subgrains have been observed directly on the surface of deformed specimens by Wood et al.,3 or have been made evident on repolished surfaces by applying a suitable etching reagent. The latter technique, first suggested by Lacombe and Beaujard,9 was then improved by Wyon and Crussard.10 Subgrains can be formed in single crystals after small amounts of bending followed by heating after this cold work, or during deformation at elevated temperatures. The first phenomenon was analyzed by Cahn11 for the simple case of pure bending followed by annealing. Cahn suggested a mechanism of subgrain formation based on the dislocation theory and called this phenomenon "polygonization." He extended this mechanism to the more complex case of local bending, such as the bending which may occur when a polycrystalline specimen is deformed in tension. Cahn's suggestion was later found quite consistent with the results obtained by Dunn and Daniels." An explanation has been presented recently regarding the formation of subgrains during deformation at elevated temperatures by Chang and Grant.'" In general, there are two schools of thought on the subject. One, according to Wood et al.,5 is that subgrain formation is a mechanism of deformation which is operative under certain conditions in the same way that the slip process is the mechanism of deformation which is operative under other conditions. The boundaries between the subgrains undergo a viscous flow which contributes substantially to the deformation of the material. The second, according to Cahn,13 Wyon and Crussard,10 and Chang and Grant,18 is that subgrain formation is the effect of simultaneous deformation and annealing and is,

Jan 1, 1953

By J. C. HEILMAN

THE Tri-State district, named from its situation in three States, lies in the northeast corner of Oklahoma, the southeast corner of Kansas and the adjacent part of Missouri east of the common corner of the above States. Production in the past eighty years has come from scattered mines within an area of some 35 miles east and west, by 25 miles north and south, although the actual area of the mined ground is but a small fraction of this territory. The land is leased from the individual land-owners, and the size of the tracts varies from 4.0 to 200 acres, the smaller sized tracts predominating. The leases usually call for a royalty of 7% to 15 per cent of the gross receipts of the concentrates, continuous operation during the life of the lease and specifically set out that no ores can be brought in from a foreign lease for custom milling nor can any ore be removed from the lease for milling. The ownership of the tailings remains with the land-owner.

Jan 1, 1931

By M. E. Straumanis, J. -P. Krumme

In basic ([KOH + KCl] with a total polarity of 2) or acidic (2N H2SO4) electrolytes and at anodic current densities of more thun 2 to 4 ma per sq cnz, n-type GaAs single crystals of lozo resistivity preferentially dissol~je forming etch tunnels with triangular or civc~ilay cross sections and of a width between 0.5 arid 5 p. These etch tunnels are oriented along any one of the four possible (111) directions of GaAs. However, their growth occurs only in one direction of a given (111) whick apparently is determined by the atomic sequence Ga —As (and not the rezlerse) in respect to an individual valence bridge in the crystal. It is concluded from comparison with the cubic lattice structure of GaAs that the etch tunnels represent macroscopic evidence for the tetrahedral bonds and their polar properties. If the anodic current density is increased the tunnel fomation results in the development of a fibrous surface layer consisting of GaAs. The latter separates frorn the substrate (in an anodic s~irface disintegration process) by the growth pressure of an As,0, filnz forming in the interior of the fibrous layer, 100 to 200 µ under the surface, at more than about 50 ma per sq cni. The fibrous GaAs film has the same crystallographic orientation as the substvate and represents a skeleton of the original crystal. Since the etch-tunnel density in a separated GaAs layer is about 108 c?n-', and the etch tunnels develop only along (111) in a given polar direction, it is assurraed tlmt the dislocations have no influence on the growth of these tunnels. ElECTROLYTIC treatment of smooth surfaces of poly- and single-crystalline GaAs at high anodic current densities causes the formation of porous surface layers.' This phenomenon suggests comparison with effects being observed with magnesium,' indium,, gallium,4 and aluminum5 and known as "anodic disintegration". The purpose of the present paper is to explore and to explain the reasons for the formation of such surface layers on GaAs and, in particular, to investigate the influence of the lattice polarity of this III-V compound semiconductor in the (111) direction on the anodic dissolution behavior. GaAs SINGLE CRYSTALS For the experiments described below GaAs single crystals from the Monsanto Co., St. Louis, Mo., were used. Their impurity levels were below 1 ppm and their dopant levels between 1 and 100 ppm. They were grown in (111) using the Czochralski or the gradient-freeze technique. The crystals had n-type conductivity and electric resistivities between 1 and 5 ohm-cm. EXPERIMENTAL The GaAs single-crystal rods were cut perpendicularly to (111) into wafers of about 1 mm thickness using a wire-blade crystal slicer and an aqueous slurry of Sic or a diamond saw. The orientation of the faces of these wafers were checked by Laue back-reflection patterns. If there was a deviation from (111) the faces were abraded under a certain angle using grinding paper and distilled water. The damaged surface layer was removed from each crystal by chemical etching with a mixture of 1HF:1HNO3: 1H20 or 2HF:1HNO3:2HAc (glacial). {110) faces were obtained by mechanical cleavage, producing surfaces which did not require a further treatment. The GaAs wafers were mounted using "alligator" clamps instead of soldered electrical contacts.' Only the bare crystal surfaces were dipped into the electrolyte. The clamps were coated with insulating wax to prevent any contact with the electrolyte. The experiments were carried out in aqueous 2 N H2so4,' or in an aqueous solution of KOH and KCl1 (1 mole KOH + 1 mole KCl in 1000 cu cm solution). Anodic current densities up to several hundred ma per sq cm were applied for periods between 30 sec and 2 hr. For the purpose of investigating the initial steps of disintegration the anodic current density applied never exceeded 20 ma per sq cm. The films which partially separated from the anodic surfaces under high-field conditions were treated with KOH to further their detachment by dissolving the As2O3 formed. The washed and dried films were pasted to strips of filter paper, and Laue pictures were made. The back-reflection patterns obtained were compared with those of the original anode surface before and after anodic dissolution. Furthermore, space reciprocal lattices7 were constructed from asymmetric rotation crystal patternsa which permitted the determination of the crystallographic orientation of the detached films of the corrugated anodic surfaces. The disintegration products were identified from assymmetric powder patterns.8 The polarity of the {111) faces was determined by chemical etching with mixtures of 1HF:1H2O2(30 pct): 2H2O or 1HNO3:2H2O. Different patterns on each of two inverse (111) sides appeared.'-l8 The correlation of these patterns to the Ga{111) or the As(111) side has already been established by the use of light figures,18-20 by X-ray diffraction near the absorption edges of gallium and arsenic,'lmZ4 and by LEED measurements.25 The geometric structure of these surfaces and the interior of the anodically attacked crystals were observed and photographed with a high-power microscope using oil immersion objectives up to magnification of X1720.

Jan 1, 1968

By Burk, Hugh A.

AT THE inception of the cyanide process and its adaptation to the practice of gold and silver metallurgy much difficulty was experienced in applying it to auro-cupriferous ores, both in economy of treatment and recovery of the gold from solution. The presence of copper in the ore effected a high chemical consumption of cyanide during treatment, and in the solvent solution, it retarded the precipitation of the gold on zinc shavings. The coating of the copper on the zinc shavings presented even worse difficulties than the increased cyanide consumption as most ores contain a small amount of copper. This interference of copper led to the use of other precipitating methods and attempts to recover the cyanide which was consumed during ore treatment. Of the other methods used, electrolytic precipitation was the most practical until a better understanding of the application of zinc shavings and zinc dust developed. In September, 1905, a patent entitled, "Method for Recovering Precious Metals from Solution," was granted to Isaac Anderson and Michael Scanton. This method is adaptable to precious metal ores containing a small percentage of copper but has never been extensively used or perfected. The process has

Jan 1, 1925

By M. K. Yen, W. R. Hibbard

Previous studies of plastic deformation of metals have emphasized the important role of bending and constraints during strain under relatively pure stresses.1"5 Some new phenomena such as early conjugate slip6 and polygonization7 are intimately concerned with the relief of bending stresses, the former by slip and the latter by a process analogous to re-crystallization. However, few analyses of the bending deformation of single crystals were found in the literature, and those8,9 are sufficiently previous to the modern interpretations of slip to invite further investigation in this area. The transverse bending mode of testing, using the two-point loading method, was selected because the center portion of the specimen may be considered as under a theoretically pure bending stress with a uniform bending moment. Considerable attention was given to both the lattice distortion and flow characteristics of the crystals during deformation. Experimental Proeedare A specimen under the action of equal and opposite couples at both ends is said to undergo pure bending. The shear and moment diagrams of a specimen under the two-point loading method of transverse bending are shown in Fig 1. The moment over the middle-third of the span is equal to PL/6, and the vertical shear is zero. Fig 2 (A) illustrates the stress distribution in the elastic range on a plane across the middle of the specimen. It can be seen that the normal stress has a maximum value at the extreme surfaces on the tension and compression sides, and decreases proportionately to zero as it approaches the neutral plane. However, when the plastic range is reached, the stress distribution is no longer a straight line relation, but changes in a manner which can be best illustrated as shown in Fig 2(B). The following calculation and stress analysis are mainly in accordance with the works reported by Timoshenkol0 and Kochendörfer.9 From the simple beam formula, the maximum normal stress will occur at the surface of the specimen. For a round specimen with a radius r and for a rectangular specimen with a height 2h and width 2b, the maximum normal stress, Sp, will be given by the following formulas: For round specimen: 2PL Sp = 3pr3 [1] For rectangular specimen: Sn = 8bh2 [2] Since it is reasonable to consider that slip takes place under the same conditions as in uniaxial loading, the resolved shear stress S?, along the operative slip direction will be as follows: For round specimen: 2PL sin x cos ? Sp = 3pr3 sin x cos ? [3] For rectangular specimen: PL S8 = 8bh2 sin x cos ? [4] where X is the angle between the specimen axis and the slip direction and X, the angle between the specimen axis and the major axis of the glide ellipse. It was also reported by Kochenclorfer9 that the critical bending moment, that is, the bending moment exerted on the specimen to initiate slip, should be higher than the value given by the equations stated above. Based

Jan 1, 1950

By Bernhard Blumenthal

A melting process was developed by which high purity electrolytic uranium crystals can be converted into sound ingots without serious contamination. Careful preparation of the crystals, melting in a high vacuum, and directional solidification led to a metal of better than 99.993 wt pct purity. The metallographic examination showed a substantially clean metal with only residual amounts of a second phase which responded to heat treatment. The density of high purity uranium is 19.05 g per cu cm. FOR the study of the fundamental properties of uranium and its alloys, a base metal of high purity is needed, and an investigation was started at Argonne several years ago to examine various methods of preparing high purity uranium. Early success was achieved by the fused salt electrolysis process in preparing high purity metal in crystal form,' and the problem became that of melting the crystals into ingots without contamination. The electrolytic crystals contained a few ppm of heavy metals, less than 15 ppm C, and large quantities of potassium and lithium in the form of trapped fused salt electrolyte. On melting in vacuo in magnesia or urania crucibles, the metal picked up considerable quantities of carbon and some iron, copper, and silicon but lost most of the potassium and lithium. It was not metallographically clean, and much research work was necessary to determine the optimum melting conditions for minimum contamination. This work has resulted in the development of a melting procedure by which sound ingots can be prepared with only a limited contamination by carbon. In the section entitled "Melting of the Electrolytic Metal," the equipment and processes that have been developed for melting the electrolytic crystals are described in detail. The "Metallography" section is devoted to the metallography of high purity uranium, and the section "Density of High Purity Uranium" contains the first property measurement on high purity uranium—a density determination. Melting of the Electrolytic Metal Apparatus—Melting and Vacuum Equipment: Uranium may be melted in either resistance or induction-type electric furnaces. Resistance heating was found to be preferable to induction heating for melting down the electrolytic crystals, for several reasons: Although induction heating permits fast heating, this advantage cannot be utilized when crucibles with limited thermal shock resistance are used. Temperature control of induction-heated melts is poor, and the stirring effect increases the rate of contamination of the melt from the crucible, slag, or the furnace atmosphere; liquation and controlled solidification are difficult to carry out. Because of these objections, resistance heating was chosen. A 10 kw Globar resistance furnace of low heat capacity permitted uniform heating of a uranium charge to its melting point in 45 min. The furnace was insulated with a removable aluminum shield so that, after melting and removal of the shield, the furnace could be quickly cooled to room temperature. The furnace was equipped with an apparatus for directional solidification; see Fig. la. The crucible was suspended in the center of the furnace; and when the melting was complete, the crucible was slowly lowered into the cold end of the furnace tube. Solidification took place upward from the bottom; and when the rate of lowering was small, a sound ingot free from sink holes and shrinkage cavities was produced. To remove the large quantities of gas contained in the electrolytic crystals, melting in a high vacuum is mandatory. While, from the standpoint of contamination, melting in a highly purified argon atmosphere appeared feasible, lithium and potassium removal proved less efficient under such conditions. Also, a vacuum-melted ingot has a cleaner surface than one melted in an inert atmosphere. The vacuum system must be of very high pumping speed and leak tight so that a vacuum of less than 2x10-7 mm Hg is attainable when the system is pumped down cold. The system must have a high pumping speed, so that the pressure maximum which may rise to 1x10-4 mm during heating can be quickly reduced

Jan 1, 1956

By Sheldon P. Wimpfen

EVERYWHERE in mining circles the talk is of this new development of hard faced or insert bits which hints of many changes to come in mining practice and rock drill equipment. In the past fifteen years new equipment has appeared in rapid succession which brought one change after another in rock breaking practice. Detachable bits were an innovation which met with wide success. Blasthole diamond drilling has proven itself. Only recently, fusion piercing was announced as a possible solution to the problem of breaking taconite ores. For several years this interest in new methods has been growing and various experimental usages of tungsten carbides in rotary type rock drilling bits have been partially successful. American experts in rock drilling have been concerned with the subject for ten years but actual commercial practice was begun by European manufacturers and mining companies. At this time nearly every manufacturer of rock drilling bits is working on some type of an insert bit. On the Rand, European manufacturers are testing out various types of insert bits. The problems relating to rock drilling in South Africa vary greatly from ours. The bulk of the drilling there is limited to the 31/2-ft holes that are drilled for breaking the gold bearing reef ore. Rock drilling in most mines is far more diversified. Both drifting and ore breaking call for holes varying in length from 4 ft up to as much as 50 ft and more.

Jan 1, 1947

THE progress in lead smelting practice in the United States during 1930 has been along previously defined lines. Since most of the material treated is high-grade concentrate relatively high in zinc, practically all the plants have been forced to adopt double sintering. This generally results in there being' no matte fall, and most of the copper in the charge is recovered in the furnace dross. The furnace dross is . smelted with. scrap iron and flux .in small reverberatories, giving a shipping matte or speiss high in copper and low in lead. Details of this reverberatory. furnace practice vary at the different plants. There is a decided tendency toward moreintensive filtration of blast- furnace and sinter fume. Bag capacity has been in- creased by using higher pressures and more frequent shaking.

Jan 1, 1931

By Frank L. Hess

BERYLLIUM is demanding more of the limelight, and the output of beryllium copper (containing 2% to~ 3 per cent of beryllium) seems to have grown 60 per cent above that of 1936, which was double that of 1935. There is increasing interest in beryllium-aluminum alloys and small quantities are being marketed at $50 per lb. for the contained beryllium. Other alloys also can be produced. Further price decreases for beryllium copper (now $23 per lb. for the contained beryllium) seem , possible and desirable. No difficulty has been experienced in obtaining beryl and a 'reserve stock has been built up. One supplier heretofore found reliable has offered to furnish 200 tons per month. Supplies during 1937 have come from the Black Hills in South Dakota, Colorado. India, and South America

Jan 1, 1938

By R. Schuhmann, O. W. Moles

at temperatures of 1150°, 1250°, and 1350°C for liquid copper sulphides ranging in composition from saturation with Cu to about 21.5 pct S. From the experimental data, activities of Cu, S, and Cu2S in the melts were calculated. Also, the results furnish a new determination of the location of the curve showing the compositions of Cu-saturoted sulphide melts in the CU-S constitution diagram. THE "white metal" made as an intermediate L product in converting copper matte to blister copper is a matte approximating Cu2S in composition. It has long been known that liquid Cu-S mattes can exist at a given temperature over an appreciable composition range, with S:Cu ratios ranging up from a lower limit corresponding to equilibrium of the matte with a liquid Cu phase. The Cu-saturated matte has somewhat less S than Cu2S, although previous measurements of the compositions of Cu-saturated mattes are not in good agreement.'" As the S:Cu ratio approaches and slightly exceeds that for Cu2S, the partial pressure of sulphur gas over the liquid matte rapidly approaches atmospheric pressure,5 so that Cu-S melts with much more S than Cu2S can be made and handled only in pressure apparatus. Accordingly, the liquid copper sulphides of interest in copper smelting and readily studied experimentally fall in a relatively narrow composi- tion range about Cu2S. The freezing points of Cu-S mattes show a maximum of 1129°C near the composition Cu, dropping to 1105oC for Cu-saturated mattes having less S and dropping under 1100°C for higher S mattes.' Estimates of the sulphur pressure and other thermodynamic properties of liquid Cu,S were made by Kelley; based on extrapolations from equilibrium measurements on solid Cu,S. More recently, Cox and coworkers' studied equilibria in the reaction: Cu,S + H, e 2Cu + H,S over the temperature range 700" to 1250°C. They measured equilibrium H2S:H2 ratios presumably with both the sulphide and the metal phase present, so that their data above the melting point of Cu,S should measure the S pressure of Cu-saturated sulphide melts. The sulphur pressures of liquid copper sulphides of several S:Cu ratios at their freezing points can be estimated from data given by Posnjak, Allen, and Merwin." However, beyond these few data, no systematic study seems to have been made of the relations of sulphur pressure and other chemical properties of liquid copper sulphides to composition and temperature. The measurements of the sulphur pressures of liquid copper sulphides reported in this paper represent a first step in the quantitative study of the chemistry of mattes. Similar work is planned on

Jan 1, 1952

By J. H. Clemes

The process of leaching silver ores with sodium hyposulphite is comparatively new, and published accounts of the details and losses of the process are as yet very few. The following account of a careful series of experiments to determine the actual loss in this process may therefore be acceptable to members of the Institute. The ore treated was highly calcareous, and the principal sulphide present was iron pyrites. Following is an analysis by Professor Price, of San Francisco, of the ore treated : Per cent. Silica,..........15.13 Sulphur,.........13.31 Arsenic,.......... 9.82 Iron............ 17.33 Alumina,..........1.35 Zinc,...........4.92 Lead,..........1.78 Carbonate of lime,..33.78 Magnesia,.......... 2.58 100.00 Ten tons were crushed dry with a 30 X 30 screen = 900 holes per square inch. In order to feel our way with this ore, two experimental or "pilot" charges were roasted. Pilot Charge No. 1. Treated 1000 pounds in a four-hearth reverberatory. 8.30 p.m.—Entered fourth hearth, remaining there one and onehalf hours; sulphur began to burn. 10 p.m.—Changed to third hearth; ore became red-hot half an hour after entering; the fireplace was kept almost destitute of fuel. 2.30 A.M.—Changed to second hearth. Charge continued, giving off a large quantity of sulphurous fume; the fireplace was kept dark.

Jan 1, 1884

By F. C. Bond, J. T. Wang

H. J. Kamack (E. I. du Pont de Nemours & Co., Inc., Wilmington, Del.)—Rittinger's law usually is stated to the following effect: "The work (or energy) consumed in particle size reduction is proportional to the new surface area produced." The law has been stated substantially in this way by Taggart20 Berry21 Dalla Valle22 Coghill and DeVaney,23 Richards and Locke," Gross,25 and many others, and, according to Gaudin,26 was originally expressed by Rittinger in the same form. Consequently there can be little doubt that this is the understanding of the law among most workers in the field of particle size reduction. Bond and Wang, however, express the law in the form "the useful work accomplished . . . ." (italics theirs). The distinction is critical, for in the form used by Bond and Wang the law becomes, as they themselves remark "merely a more or less arbitrary definition of useful work," while in its usual sense the law expresses a physical hypothesis which has been verified experimentally within certain limitations. Considering the way the law has been used, it might be stated more explicitly as follows: "In a given machine operating under a given set of constant operating conditions, the work consumed in the particle size reduction of a given material is proportional to the new surface area produced." Or, as Coghill and deVaney have said,27 "the (Rittinger) law holds only when the tests being compared are made under analogous conditions." There are occasions when the law transcends these limitations; for example, the surface area produced per unit energy consumption for a given material in a ball mill does not vary much over a fairly wide range of operating conditions. But by and large, the surface area production per unit energy consumption will vary with the operating conditions, the type of machine, and the material. The essence of Rittinger's law is that the surface area production per unit energy consumption is independent of the particle size, and this has been verified experimentally by numerous workers for numerous materials, within certain limits. An important limitation is that when one grinds to very small particle sizes, agglomerative forces may tend to interfere with size reduction so that the surface area increases less rapidly than Rittinger's law would predict. Within such limitations, Rittinger's law can be regarded as empirically established. The law has, however, certain theoretical implications, and it seems to be chiefly against these that Bond and Wang direct their criticism. Solids are believed to possess surface energy which is proportional to surface area. Thus, Rittinger's law implies a proportionality between surface energy produced and mechanical energy expended (for a particular material in a particular machine). It does not imply that all or most of the mechanical energy is transformed into surface energy; in fact it is known that most of the mechanical energy is transformed into heat. Bond and Wang assert that most of this heat arises from the damping of elastic vibrations of stressed particles. This may possibly be true for crushing (with which they are chiefly concerned), although in grinding it is probable that much of the heat arises from friction between particles. However, the fact that the surface energy is small compared to the heat energy does not invalidate Rittinger's law, which implies merely that they are proportional. The authors also criticize Rittinger's law on the grounds that "this theory cannot be justified mathematically, since work is the product of force times distance, and the distance factor is ignored," and "energy input must be the product of force times distance, and the Rittinger theory completely ignores large variations in the distance (strain dimension or deformation) throughout which a force must act to produce breakage of different materials." However, the quantities force and distance as such are irrelevant to Rittinger's law, which considers energy input as an integral quantity. The fact that different materials require different forces and strains (hence, different amounts of energy) to break them is incontrovertible but again is irrelevant to Rittinger's law, which, as mentioned before, applies -only to a single material. Even in theory, it would not be expected that the surface area produced per unit energy consumption would be the same for different materials, because the surface energy per unit area is presumably specific to each material. Bond and Wang advance another argument of a

Jan 1, 1952