By P. D. Merica

IN connection with other investigations on the properties and characteristics of chilled iron car wheels, the question as to the best range of annealing temperatures was raised. Chilled-iron wheels are cast with a chill against the tread and the inside of the flange, the remainder being in sand. The composition of the metal is so chosen that under these conditions the tread and inside of the flange will show white iron to a depth of from 5/8 to 7/8 in. (15 to 22 mm.), the remainder of the wheel becoming graphitized or gray. In order to relieve the stresses set up during cooling under such drastic conditions, the wheels are stripped from the mold, while still red hot, piled in a soaking pit, and allowed to cool very slowly from their temperature at stripping. Obviously the most suitable temperature for this annealing is the highest at which no formation of graphite occurs within the white tread and at which the wheels can be stripped from the molds. Inasmuch as no direct determinations have been made of the temperatures at which the' formation, of graphite takes place in white iron of compositions used in car wheels upon annealing, it was considered worth while to determine these temperatures as a means of establishing the maximum temperatures at which the annealing of the wheels may be carried out. In the course of this work, some incidental observations were made which are of interest in connection with the theory of graphitization in white iron. The literature on the subject of the formation of graphite both during cooling at casting and upon annealing is very extensive and can be best studied by reference to a comprehensive discussion of the subject by Hatfield. 1 Perhaps the most important contributions of previous investigation are the following: 1. Whether a given mass of molten iron becomes white, mottled, or gray upon casting, depends on its composition and its rate of cooling through the temperature range of solidification and immediately below.

Jan 7, 1919

By Douglas Bunting

IN THE anthracite fields of Pennsylvania, mine fires occur with more or less regularity and their existence is an ever-present hazard in coal mining. In all probability 90 per cent. of the mine fires can be ascribed directly or indirectly to the ordinary miner's open lamp. Other causes may be smoking, electrical installations, gas explosions, gas feeders, and the communication of fire to the outcrops from ash dumps, culm banks, timber and brush fires. Fires in pump rooms, engine rooms, and barns have been largely eliminated as a result of the Act of .Assembly, approved June 15, 1911, which provides that all inside buildings, including engine rooms, pump rooms, barns etc. shall be constructed of incombustible materials. Smoking of pipes, cigars, and cigarettes should be prohibited in the mines and too much care cannot be exercised in preventing fires by enforcing all rules designed for that purpose. Mine fires that involve underground fighting are invariably dangerous, and all fires, irrespective of the method pursued in extinguishing them, involve property loss and expense. Each fire generally presents a more or less original problem, dependent on the particular conditions. Generally mine fires may be divided into two classes: Those occurring in inaccessible workings and those occurring in accessible workings. The methods pursued in extinguishing or controlling mine fires are as follows: (1) direct attack, (2) smothering by sealing, (3) flushing with silt or other solids, (4) flooding with water, (5) cutting off, (6) surrounding with incombustible materials, (7) digging out by stripping from the surface. Most fires are extinguished in their incipiency by direct attack and failure to extinguish by this method is due to late discovery, lack of water, and facilities for fighting, or improper procedure in the initial attack. Should the method first pursued be unsuccessful, careful consideration should be given in determining next the method to be adopted; then the work should be carried on as rapidly as possible and under the supervision f the most competent persons. Materials and supplies should be fur-

Jan 9, 1921

By A. J. Miller, G. R. Brophy

THE Grossmann principle1 for the calculation of hardenability of steel from composition is attractive because of its simplicity. It postulates that the hardenability of a steel for any particular grain size may be expressed in terms of an ideal critical diameter, which is the product of an ideal critical diameter for a "pure" iron-carbon base multiplied by a succession of factors for each element of composition contained, including the incidentals. It infers that the multiplying factor for a given quantity of an element is constant for all combinations of composition. Grossmann has stated that in the great majority of cases the experimental values of hardenability are found to be well within 10 per cent of the calculated values. The validity of the scheme has been confirmed in principle by Crafts and Lamont2,3 and by Kramer et al .4 Their results differ from the original in the magnitude of the effect of some elements but, since they accepted the product concept and followed its direction, it is to be expected that similar results would be obtained. Crafts and Lamont, in their second paper, recognized that the factor relations for manganese and nickel were not continuously linear, but beyond certain critical amounts increase sharply. Austin, Van Note and Prater5 demonstrated nonlinear relations between hardenability and alloy contents. Their curves for chromium, silicon, manganese and nickel were all convex upward to show decreasing incremental effects. They concluded that Grossmann's factors underevaluate the hardening effect of low percentage additions of these elements, and overevaluate the larger additions. [ ] More recently W. Steven6 has found that the factor method fails when applied to complex steels containing two or three principal alloying elements other than carbon. Multiplying factors derived from his results bear a complex relation to composition and are not constant for a given amount of an element as the base composition varies. C. A. Liedholm7 found that, using either the Grossmann or the Crafts-Lamont multiplying factor values, not only were

Jan 1, 1945

By Richard Bosustow, Van Dyne Howbert

The Presidio mine of The American Metal Co. is situated in the "Big Bend" region, some 45 miles over state highway south of Marfa, a station on the Southern Pacific R.R. It lies 20 miles by road north of the Mexican border, in semidesert surroundings typical of this general section of the United States and the adjoining part of Mexico. All supplies are hauled in by truck from Marfa under contract. The concentrates and precipitates produced by the mill are carried by the same trucks to Marfa, from whence they are shipped, respectively, to the El Paso and Selby plants. History The mine was discovered about the year 1880 and was soon thereafter taken over for development by some army officers stationed at Fort Davis, Texas. It was later operated by the Presidio Mining Co., which treated the ore in a small pan-amalgamation mill from 1883 until 1913, when a cyanide plant was erected which has been in continuous operation ever since. When the present company, a subsidiary of The American Metal Co., Ltd., took over the mine in April, 1926, the ore-bearing zone had been worked for about 2200 ft. to the east of I the outcrops down the dip of the formation, at which point it is at a I vertical depth of 500 ft. below the surface. Up to that time the mine had produced some 1,150,000 tons of ore averaging about 17 oz. silver. After a development campaign the company started milling again in February, 1927. Since then the production has been approximately 4700 tons per month of ore; of which the yearly average grade has varied from 19.7 to 23.2 oz. silver, $0.20 to $0.50 gold, and 2.0 to 2.5 per cent. lead. No other property in this district has ever produced tonnage of any importance.

Jan 1, 1931

By Eugene A. Stephenson, Leon J. Pepperberg

The natural gas industry is essentially a byproduct of the oil industry. When first discovered the gas was usually regarded as a nuisance, and even when found immediately associated with oil, or suspected to be so, it was customary to blow it freely into the air, in the hope that gas would shortly be replaced by a flow of oil. The early methods of production,' transportation, and utilization were neither economical nor efficient; the chief value of gas was based on its use as a fuel, with no regard to (1) its effect. upon the oil with which it was associated, (2) its importance as a lifting agent, or (3) to its possibilities for the manufacture of byproducts. The spread of scientific research among major gas and oil companies, manufacturers, and academic groups, has gradually brought recognition of the fact that many of the technical problems bearing on production, transportation and utilization are common to both the gas and the oil industry. A few of the problems that have received serious study, and from which highly gratifying results have been obtained, are: (1) gas measurement, (2) oil well and gas well capacity tests, (3) elimination of field waste, (4) design of pipe lines and compressor stations, (5) extraction of constituents which might interfere with the normal flow of gas through the line, (6) control of reservoir pressure, (7) estimation of reserves of both oil and gas, (8) control of water encroachment, (9) measurement of factors which influence fluid movement through sands, (10) solubility of gases in oils, (11) effect of dissolved gases upon the properties of the solution. These investigations have demonstrated that almost every problem relating to oil production also involves some phase of natural gas engineering. During the past 15 years the use of experimental methods for the discovery and measurement of obscure, influencing factors, which cannot be determined purely by hydrodynamic or thermodynamic analyses, have contributed much towards the progress made in solving the problems of the oil and gas industries. Most of the experimental work on

Jan 1, 1934

By R. R. Hawkins

PEoperly designed tubing strings make it possible to continue the flowing life of wells beyond the stage where ordinarily they would be put to pumping. Wells no longer able to flow through 2-in. tubing can be made to produce through smaller tubing if conditions within the well are carefully studied and correctly designed strings are installed. In this way, pumping expense may be postponed and in some pools it is within reason that the entire recovery may be obtained by natural flow if maintenance of pressure is practiced. Infrequent tubing changes would be necessary but their cost would be much less than that of installing and maintaining pumping equipment. If small wells are to be made to flow naturally, careful consideration must be given the actual lifting mechanics within the string, so that fairly accurate knowledge of reservoir conditions, especially pressure, is essential. Wells producing between 5 and 25 bbl. daily are classified here as "small wells." Exponential Flow A maximum of the energy contained in the expanding gas must be employed to do useful work if natural flow is to be continued. It is evident that adiabatic expansion would defeat this purpose, therefore the velocity of the gas must be held down to a minimum in order that isothermal expansion may be approached. Of course, true isothermal expansion would not be obtainable in an oil well, hence the use of the term "exponential." 1 Obviously the closer the approach to isothermal expansion, the more efficient the lift. Experiments by the U. 8. Bureau of Mines² have shown that for isothermal expansion to take place in a gas well where water is being produced, a definite relationship exists between the depth of the well and the minimum operating pressure. The latter must be such that the tubing fill-up, if static conditions prevailed, would be equivalent to 14 per cent of the distance between the top of the fluid inside the tubing and the tubing head. It has been observed that variations in this essential ratio

Jan 1, 1932

By C. F. Austin, J. K. Pringle

In view of the many large differences in structure and physical properties between metals, plastics, and most rock materials, a continuing experimental petrodynamics program has been established at the U. S. Naval Ordnance Test Station. Part of this program has been to test the concepts of scabbing and corner fracturing in a typical coarse-grained rock. The results of this experimental program have shown very interesting differences between the formation of fractures in rock and the formation of fractures in other materials such as metals and plastics which are often used as models for rock behavior studies. The gross behavior of coarse-grained brittle solids subjected to impulsive loading has undergone abundant empirical investigation by mining organizations and by mineral research agencies. However, the fundamental response of coarse-grained brittle solids to impulsive loading has received little detailed study in recent years. The various organizations and agencies interested in rock-like brittle materials have broadly applied the stress wave interaction concepts of the impulsive failure of metallic samples to the behavior of granular brittle materials 1,2,3,4,5,6 Using the metallic sample approach for stress wave induced fracturing, an understanding of the fracture behavior of brittle materials which perhaps is not always appropriate has been established in the open literature. An excellent summary of the metallic sample approach is provided by ref. 7 which summarizes the general beliefs prevalent at present regarding the impulsive behavior of brittle solids: "In the blasting process, rock breakage occurs primarily from tensile slabbing, beginning at a free face and proceeding back toward the explosive charge. The tensile waves formed by the reflection of incident compressive waves from two or more free faces will collide in the rock, resulting in large localized tensile stresses. Fractures formed by the interaction of these tensile stresses begin at the apex of the free face planes and progress back into the rock as shown...."

Jan 1, 1964

By E. W. Greene, J. B. Duke

This paper deals with the application of froth flotation techniques to the beneficiation of kaolin clay and phosphate slimes, two very fine particle sized materials. The kaolin problem involves the removal of a small amount of a contaminating mineral (anatase), while the phosphate problem involves the concentration and recovery of a much larger percentage of apatite. Due to these differences, and also different response to flotation, the two problems are discussed in separate parts of the article. An idea of what is meant by "Ultrafine Minerals Or Slimes" as used in the title can be had by an examination of Fig. 1. Particle size distributions are presented for a crude kaolin clay, a coarse fraction and a fine fraction. The crude kaolin as mined was blunged with water, degritted through a 325-mesh Tyler screen, and dispersed with sodium silicate. The dispersed crude was then centrifuged in the laboratory into the coarse and fine fractions shown in the figure. The distribution curves were obtained by the well known sedimentation technique of Casa-grande1 using a long arm centrifuge to obtain equiva- lent spherical diameters down to 0.2 p on the finer fraction. Fig. 1 shows the coarse fraction kaolin to be 50% finer than 3 p, while the crude kaolin is 509 f'lner than 1.4 p, and the fine fraction 50% finer than 0.46~. For comparison 53 p on the horizontal scale would represent Stokesian diameters which would just pass a 325-mesh Tyler screen, taking into consideration the Andreasen sieve correction factor of 1.22 times the screen opening. 2 Another helpful comparison is the surface areas, which in square meters per gram, are 0.044 for 53 p particles, 0.77 for 3p, 1.65 for 1.4 p and 5.0 for 0.46 p particles. Fig. 2 is an electron micrograph of a similar fine fraction kaolin showing the hexagonal plate-like particle shapes.

Jan 1, 1962

By H. W. Morse

MANY of our largest copper deposits contain both sulfide and oxidized copper minerals. The large porphyry mines, with a total copper content of from 1.3 to 2.0 per cent., send to their mills ore with an oxide content of from 0.2 to 0.4 per cent. While the recoveries of the sulfide minerals are considered satisfactory, using modern flotation practice, the recovery of the oxi- dized portion of the copper is small; better recoveries of oxidized copper were made before flotation methods were adopted. Beside the ores containing copper mainly as sulfide, with a small amount of oxidized copper,, many of the large porphyry mines have oxide orebodies, in which the propor-tion of non-sulfide minerals is so high that 2 present methods of treatment are ineffi-cient. In some of the well-known ore-bodies in the Miami-Inspiration district the copper occurs about equally in sulfide and oxidized forms; and the mixing of minerals is complete throughout the ore-body. There is no possibility of mining the sulfides and the oxides selectively. At the New Cornelia mine, however, the oxide, and sulfide ores are sharply separated, per-haps by an ancient water level, so that the oxide ore may be mined and treated in a plant built for that purpose, and the under-lying sulfide ore may be left for treatment in another plant. If copper is to be made from an ore having a total content of 1.5 per cent., it must be concentrated or removed from the ore by some. hydrometallurgical method. Flotation is generally successful for the sulfide minerals and flotation after filming with sulfide seems to work in many cases on the pure carbonate minerals. Callow has given an extensive report on the results of "sulfidizing" flotation on the ores of the. Magma mine.1 Where such ?a 'method can be applied, it ?may be, the best

Jan 9, 1922

By R. E. Reed-Hill, J. L. Martin

Kinking is an important deformation phenomenon in poly crystalline a zirconium. The crjlstallo-gvaphic features of the most important form of kinking have been determined with the aid of twins formed at 77°K in grains previously kinked at high temperatures. It has been .found that the kink-band boundaries correspond to walls of edge dislocations with (1150) Burgers vectors and dislocation lines parallel to (1070). The present observations imply that basal slip is an important secondary-slip mode in polycrystalline zirconium. Previous single-crystal studies13 did not veveal this mode Other evidelzc.e for (0002)(1120) slip is also presented. ThE first studies of kinking in hexagonal metals were made by orowan,1 using single-crystal cadmium wires. He suggested that this was a new de- formation mode in metals, different from ordinary glide or twinning. Next, Hess and Barrett2 studied zinc-crystal rods in compression, and were able to offer an explanation of the phenomenon described by Orowan. They concluded that kinks required no new deformation mechanism and were a special form of deformation band that developed gradually and solely from basal glide. Similar kink bands were then observed by Washburn and parker3 on zinc crystals deformed in tension at low stresses and high temperatures. In titaniun,4 kink bands associated with {1010}<1120> prism slip have been observed in coarse-grained specimens. Magnesium5 and rhenium6 have also been observed to kink in conjunction with their basal- and {1010} prism-slip systems, respectively. Yttrium has (1010) as a predominant slip plane, but no observations of kink bands were reported.7 Since no previous investigations of kink bands in zirconium have apparently been made, this study was proposed. Its aim was to determine the crys-tallographic features of a type of kink band frequently observed in polycrystalline zirconium. EXPERIMENTAL APPARATUS All tests were performed on a type TTC Instron machine. The cross-head speed usually chosen in tension or compression was 0.02 in. per min. Ten-

Jan 1, 1964

By Robert Mehl

RELATIVELY few data have been collected on the rates of diffusion in ternary solid solution systems. In general it does not seem worth while to gather extensive data for such systems until the factors that determine the rates of diffusion in binary systems are better understood. But the rates of diffusion in a ternary system of limited solid solubility, in which the terminal solid solution is in equilibrium with an intermediate phase and may thus be represented as a quasibinary system, represents a case of special interest. In this case, where by reason of the association of the two solute metals in an intermediate phase a special attraction of the two solute atoms may be safely assumed, some interaction of these atoms during simultaneous diffusion in the solvent lattice might be expected. It has frequently been proposed that molecular solid solutions exist in quasibinary and in other ternary (and binary) solid solutions. There is no direct evidence for such solid solutions; arguments based upon the supposed anomaly in certain physical properties1 are hardly important; unexpected density relationships have proved deceptive ;2 suggestions of molecular solid solutions have been made on the basis of solution laws in their application to certain systems, but without result;3 attempts to find lattice parameters in the solid solution Al-MgZn2, which cannot be calculated from the separate effects of magnesium and zinc and might therefore be taken as evidence for a molecular aggregation, have given negative results.4 Fundamentally, methods for the determination of the state of molecu¬lar aggregation in solution depend upon the kinetic behavior of the par-ticles constituting the system. If it could be shown that the two solutes in a quasibinary ternary system diffuse in molecular proportions, despite a radical difference in the separate rates of diffusion of each solute when diffusing alone in the solvent lattice, some basis for the concept of molecu-lar solid solution would be afforded. Freche5 examined the rates of independent and simultaneous diffusion of magnesium and silicon in

Jan 1, 1939

By J. J. Reed

The mines of southeast Missouri&apos;s Lead Belt have been in operation since 1864, almost 100 years. During this period about 10 pct of the total ore available has been left in place as pillars, and this now represents the best ore reserve left to the older mines. St. Joseph Lead Co. has been investigating various plans of pillar recovery for several years. The example to be described is only one possible approach under a specific set of conditions. Conditions vary greatly in the different areas within the Lead Belt, and the same approach would be entirely inadequate in certain other areas, but there are important sections where this system is clearly applicable. Horizon mining is practiced in the Lead Belt, and stopes may vary from 10 ft to well over 100 ft high. Fig. 1 is a plan view of 6100 stope, the area to be discussed. For these mines this is a small stope, only 10 to 12 ft high. Before any plans were drawn up for pillar recovery, three independent estimates of the pillar grades were made by the mine superintendent, the mine captain, and the mine geologist. After these results were averaged, pillars indicated to be of economic grade were marked for removal as shown. At this stage several alternatives were considered: 1) retreat with caving, 2) concrete replacement pillars, and 3) systematic bolting and retreat. A retreating system with caving was not chosen because the roof was known to be too bad even to permit loading a blasted pillar before caving would begin. Concrete replacement pillars would have been too costly and would have required a large crew, bulky materials, and unwieldy equipment. Systematic bolting was chosen as being most acceptable for the following reasons: 1) Limited area and spans were involved. 2) Only minor modifications to the jumbo would be required for bolting. 3) Only a two-man bolting crew would be needed. 4) Only compact bolting materials would be required. 5) The bolting plan could be modified to allow

Jan 1, 1960

By M. E. Wadsworth, K. J. Richards

The oxidation rates of tantalum in various partial pressures of carbon dioxide in the temperature range 700°to 950°C were measured with a thermo-gravimetric balance. Oxidation involved a surface -controlled reaction associated with the formation of a nonprotective layer of Ta2O5. Below about 720°C, there was a change in the rate-determining mechanism, and above 830°C the linear rate was preceded by a complex region of nonlinear oxidation behavior. The linear oxidation of tantalum has been explained quantitatively in terms of carbon dioxide adsorption, followed by a rate-controlling surface reaction. The initial adsorption has been expressed both as an equilibrium process and as a steady-state reaction. The enthalpy for chemisorption of CO, was determined to be -17.3 kcal per mole. The surface-controlled reaction had an activation enthalpy of 40.4 kcal per mole. A considerable amount of interest has been shown in recent years in the oxidation of tantalum and the nature of the oxide film produced. This interest is associated with the increasing demand in our technology for structural materials to withstand high temperatures and corrosive atmospheres. The low oxidation resistance of tantalum has severely restricted its application as a high-strength, high-temperature material. As a fundamental approach to the realization of the full poten- tials of this metal, the kinetics of the oxidation of tantalum in oxygen and air have been extensively studied; however, very little work has been reported on the effect of other gases, including carbon dioxide. According to Miller,&apos; the only reported study of the reaction between tantalum and dry carbon dioxide is a restricted observation by O&apos;Driscoll et al.2 at 8 atm absolute pressure and 500°C. Therefore, this study was made to investigate the reaction of tantalum with carbon dioxide. EXPERIMENTAL MATERIALS AND METHODS The vacuum-annealed tantalum used in this study was obtained from Fansteel Metallurgical Corp. as 0.025-mm-thick sheet stock. This material had less than 0.1 pct total impurities, and the maximum individual impurity concentrations were

Jan 1, 1964

By William F. Brace, Howard R. Pratt, Wayne S. Brown

In many engineering structures, the mechanical properties of large volumes of rock must be considered. Typically, such properties are assumed to be the same as those of small laboratory samples, although it is clear that the laboratory samples do not contain the joints, faults, and other natural planes of weakness of the rock mass. A cheap, convenient testing procedure is needed with which the engineer can more accurately assess the strength and elastic properties of natural jointed rock. As a first step in this direction, a test has been developed capable of determining mechanical properties of large samples in their natural undisturbed state. In the present paper, some preliminary experiments on relatively unjointed material are described. Numerous attempts have been made to measure the deformation modulus of rock masses with varying degrees of success. Rocha (1), Grimm (2), and Alexander (3) have placed flat jacks in a slot in the rock and measured the pressure required to deform the slot. Bonnechere (4) has grouted large flat jacks in granite masses and performed similar experiments using a variety of strain measuring techniques. The U. S. Bureau of Mines has conducted radial jacking tests in which a uniform radial stress is applied to the inside of a tunnel of circular cross section and radial deformation is measured by extensometers located at various depths in the tunnel fall. Plate jack tests (Rocha (5), Shannon and Wilson (6)), pressure chamber tests, and cable jacking tests (Zienkiewicz and Stagg (7)) have all been used to determine in-situ deformation modulus. Several bore hole techniques have also been used to measure rock deformation. These include bore hole jacks (Goodman (8)), bore hole dilatometers using expandable membranes (Menard (9)) and bore hole penetrometers. Most of the above tests except the radial jacking test have an unknown stress distribution and require considerable approximation to calculate a deformation modulus. These approximations include the use of elastic theory for solutions of rigid plates, thick-walled cylinders, etc., and determination of values for Poissons

Jan 1, 1971

By Andrew L. Mular, K. K. Humphreys

Introduction Estimates performed on potential future plants must by their very nature be either order-of-magnitude or budget (preliminary) estimates. Of the three types of estimates recognized by the American National Standards Institute (ANSI Standard Z94.2), order-of-magnitude and budget estimates are the least accurate. Order-of-magnitude estimates have an expected accuracy of plus 50 percent to minus 30 percent. In other words, it is anticipated that actual project cost will be no more than 50 percent above the estimate and no less than 30 percent below the estimate. Budget estimates, or preliminary estimates as they are often called, have an expected accuracy of plus 30 percent to minus 15 percent. The reason that greater accuracy cannot be expected in performing estimates on proposed new facilities is simply that insufficient data is generally available to permit performance of a highly accurate estimate. As stated in ANSI Standard Z94.2, a definitive estimate, i.e., an estimate with an expected accuracy of plus 15 percent to minus 5 percent," . . is an estimate prepared from very defined engineering data . . . (including). . .as a minimum, fairly complete plot plans and elevations, piping and instrument diagrams, one line electrical diagrams, equipment data sheets and quotations, structural sketches, soil data and sketches of major foundations, building sketches and a complete set of specifications." In other words, the engineering of the project must be fairly well underway to permit a definitive estimate to be performed. Such is the case only after the construction decision has been made, all potential alternatives evaluated, and major expenditures committed for a particular course of action. This situation is beyond the scope of this chapter. The chapter is directed to comparison of various technological alternatives for which site specific engineering data is not generally available. Accordingly, such comparisons can be made only by utilizing preliminary or order-of-magnitude estimating techniques.

Jan 1, 1982

By W. C. Lilliendahl, H. W. Highriter

The method developed and used in this laboratory for the production of metallic uranium of such purity that it is ductile and can be cold-worked to fine wire or thin sheet by rolling has already been described1. It consists, briefly, in the electrolysis of potassium uranous fluoride (KUF5) in a molten bath composed of equal parts of sodium and calcium chlorides. The bath is contained in a graphite crucible, electrically heated to about 775° C., the crucible serving as the anode for electrolysis. The uranium deposits in finely divided form mixed with salts upon a molybdenum cathode suspended axially in the crucible. Upon completion of the electrolysis the cathode is removed and cooled, the deposit broken and leached to remove salts. The metal powder is washed with water and dilute acetic acid and dried in vacuo to reduce oxidation. Suitable amounts are then prcssed into pellets and heated in vacuo by high-frequency induction, using a thoria crucible. The uranium melts and flows away from the pellet, leaving a shell, which is largely oxide. In general, this method produced a satisfactory metal, although at times tile uranium was not ductile. The investigations recorded here were made to find the cause of this embrittlement. It was known that the metal generally contained carbon, derived from disintegration of the graphitc crucible in which electrolysis is conducted, in amounts dependent upon the thoroughness of washing the metal powder. Accordingly, analyses of several samples, both ductile and brittle, were made by combustion and absorption of CO² in Ascarite, using air instead of oxygen to reduce the temperaturc and rate of oxidation. Several of these metals were made with special precautions to reduce carbon content. The results show no relationship between ductility and carbon content in the range investigated (Table 1). Microscopic examination of ductile and brittle metals disclosed the presence in the latter of an intergranular constituent, harder than the matrix and less easily oxidizable, which was absent from the ductile material. Rough estimates of the volume of the hard constituent

Jan 1, 1935

By David J. Dunn

GENERAL NOTES Liner Design for Comminution Liners in crushers and mills are the mechanical link between machine and ore. The way liners transfer energy to media and ore determines to large degree the production rate, liner wear rate, maintenance cost, energy use, and availability of the comminution process. Plant capacity and mineral recovery economics, and return on investment, are thus strongly dependent upon these simple, low cost metal shapes of which so much is demanded. The complexity of dynamic relationships between liner configuration, material properties, ore characteristics, and operating parameters defy simplistic generalization. Rules-of-thumb and axioms of years past fall into disuse almost daily as new analytical methods, assisted by computers and sophisticated control systems, are applied to crushing and grinding processes. Recent literature is well supplied with references citing production benefits that improved liner designs produce. This chapter is intended to review especially promising liner designs and material developments and presents cameo case studies showing the benefits derived from their application to comminution circuits (Tables 1,2,4,5,7). Complete discussions of liner design and wear materials are beyond the scope of this chapter. Norman&apos;s comprehensive studies in references (1) and (2) and Mclvor&apos;s analyses of mill speed/configuration effects (3) are especially useful reading for designers and operators of crushing and grinding circuits. Changing trends in ore, product value, and costs of wear materials, interest, labor, and energy, make ongoing evolution of liner design equally important for existing mines and for projects still on the drafter&apos;s board. Original designs supplied as new equipment must, of necessity, be best estimates. These can usually be improved as operating experience replaces engineering forecasts. Advent of new materials or design concepts such as the Angular Spiral Liners (Korpi (4) ) or Norman&apos;s Bimetallic design (2) offer improvement potential that must be evaluated if a given circuit is to be kept competitive versus others making similar products.

Jan 1, 1982

By Orson Shepard

TEXTBOOKS on fire assaying list the following standard methods of assaying sulphide ores: (1) scorification, (2) litharge-niter, (3) soda-iron, (4) roasting, (5) combination wet and fire. The litharge-niter method has proved the most satisfactory, and is the usual method for assaying sulphide ores and concentrates. It gives good results when suitably conducted and when lead buttons of uniform size are produced so that the cupellation temperature can be properly controlled. The main objection to the method is the inconvenience of determining the amount of niter to add to each assay charge to produce lead buttons of suitable size from a set of fusions. For the assay of different materials, the niter requirement varies with the particular sulphide minerals present, the amount of sulphide minerals present, the slag composition, and the rate of heating the charge in the furnace. Except for some materials, so uniform in composition that the same amount of niter can be used in assaying all samples, the amount of niter must be determined for each sample to be assayed. This is done by either: (1) calculation from an estimate of the kind and amount of sul-phide minerals present in the sample, or (2) a preliminary fusion. Some assayers use one method and some the other. The estimation method takes the least time; but much experience is required to obtain close estimates on a wide variety of materials. At best, the sizes of the lead buttons obtained vary considerably. The preliminary fusion method usually gives lead buttons of fairly uniform size, although sometimes there is a variation because the oxidizing power of niter varies a little with the charge. This variation can be eliminated by two preliminary fusions: one to determine the reducing power of the ore, and the other to determine the oxidizing power of niter in the charge. The objection to the prelimi-nary fusion is the extra time and expense involved.

Jan 1, 1939

By R. P. Heuer, Paul M. Tyler

THE literature on refractories, although fairly extensive, is so scattered through books and periodicals as to be difficult of access to the general reader and most of the individual papers serve merely to illuminate some particular phase of the industry. Two general treatises by American authors8.16 are available, also the somewhat older works by a well-known British authority, 12,13 but these make their appeal to the technically minded ceramic engineer. Another small group of publications deals with the use of refractories, mainly in the iron and steel industry.1, 3,5,6,11,15 Raw materials utilized by the refractories industry have been covered by sundry books and articles. For the relatively nontechnical reader and economist, however, there appears to be no single review that purports to describe the industry as a whole. Furnace linings and other products that are classed as "refractories" are designed primarily to withstand high temperatures but this important property is by no means the only requirement; a suitable refractory material must likewise withstand slagging (chemical&apos; action), abrasion (physical wear), and spalling, as well as the various other stresses and physical phenomena induced by heat, of which softening or incipient melting is only one phase. Nevertheless, subject to these highly practical considerations, the definition of a refractory material is based upon temperature resistance. Broadly speaking, any material that shows obvious signs of fusion after being heated slowly to 1500°C (2732°F) cannot be classified as a refractory material. The characteristic properties and requirements of refractory materials are conveniently summarized in Fig 1, prepared on the American Refractories Institute Fellowship at Mellon Institute, Pittsburgh, Pennsylvania. Most of the factors of service and properties of refractories given in this chart are interdependent and are greatly affected in degree by the functions of temperature and time. The factors in the chart are believed to cover the commoner questions.

Jan 1, 1949

By W. C. Lilliendahl, H. W. Highriter

The method developed and used in this laboratory for the production of metallic uranium of such purity that it is ductile and can be cold-worked to fine wire or thin sheet by rolling has already been described1. It consists, briefly, in the electrolysis of potassium uranous fluoride (KUF5) in a molten bath composed of equal parts of sodium and calcium chlorides. The bath is contained in a graphite crucible, electrically heated to about 775° C., the crucible serving as the anode for electrolysis. The uranium deposits in finely divided form mixed with salts upon a molybdenum cathode suspended axially in the crucible. Upon completion of the electrolysis the cathode is removed and cooled, the deposit broken and leached to remove salts. The metal powder is washed with water and dilute acetic acid and dried in vacuo to reduce oxidation. Suitable amounts are then prcssed into pellets and heated in vacuo by high-frequency induction, using a thoria crucible. The uranium melts and flows away from the pellet, leaving a shell, which is largely oxide. In general, this method produced a satisfactory metal, although at times tile uranium was not ductile. The investigations recorded here were made to find the cause of this embrittlement. It was known that the metal generally contained carbon, derived from disintegration of the graphitc crucible in which electrolysis is conducted, in amounts dependent upon the thoroughness of washing the metal powder. Accordingly, analyses of several samples, both ductile and brittle, were made by combustion and absorption of CO² in Ascarite, using air instead of oxygen to reduce the temperaturc and rate of oxidation. Several of these metals were made with special precautions to reduce carbon content. The results show no relationship between ductility and carbon content in the range investigated (Table 1). Microscopic examination of ductile and brittle metals disclosed the presence in the latter of an intergranular constituent, harder than the matrix and less easily oxidizable, which was absent from the ductile material. Rough estimates of the volume of the hard constituent

Jan 1, 1935