By S. L. Couling, D. J-P. Adenis

i2) twinning in poly crystalline magnesium does not usually occur homogeneously but is concentrated in localized regions or bands inclined at about 45 deg to the stress axis. These bands of twinning are in many ways similar to the Luders bands seen in mild steel alzd Al-Mg alloys. Within a hand the percentage of the volume twinned may approach 100 with no twinning outside the band. Bands are not produced in specimens of grain size a3 x 10-= in. or in samples deformed at temperatures 300°F. Annealing of heavily twinned regions leads to re crystallization textures markedly different from those found in the starting material. The exact preferred orientation appears to depend on the starting grain size, the amount of compres-sive strain and the manner in which it is introduced. MAGNESIUM, with its hexagonal crystal structure, deforms plastically at room temperature by a variety of deformation mechanisms, one of the most important of which is (1012) twinning. In single crystals such twinning occurs on compression parallel to the basal plane or tension perpendicular to it. In wrought polycrystalline magnesium, such as rolled sheet, the preferred orientation is such that almost all the grains have their basal planes nearly parallel to the sheet surface. Therefore, if sheet material is deformed by cold rolling or by tension in the plane of the sheet, deformation of the grains by (1012) twinning is not favored. On the other hand, twins form readily on compression parallel to the plane of the sheet as in a compression test, on the compression side of a bent sample, or at the outer rim of a drawn cup. The first part of this paper deals with the morphology of (1012) twinning in polycrystalline magnesium. Some aspects of this subject were covered by Barrett and ~aller.' Of direct bearing on the work to be reported here are the comments of Jetter' in discussion to Ref. 1. He shows that Mg + 1.5 pct Mn alloy sheet when bent about a transverse axis develops a pattern of transverse bands on the surface of compression. A longitudinal section through the sheet shows that the bands are wedge-shaped and inclined to the rolling direction. The bands were identified as "outcrops of regions in which deformation is localized as the result of the reorientation brought about by (1012) twinning". The second part of the paper treats the recrys-tallization texture of the specimens twinned by compression. Magnesium deformed and then annealed generally recrystallizes with no change in orientation.1'3'4 This statement is true provided that the amount of (1012) twinning occurring during deformation is small. In an isolated observation, Anse15 has shown that, when deformation produces much (1072) twinning, annealing causes new maxima to appear in the pole figure. The second part of the paper elaborates on this point. I) MATERIALS AND PROCEDURES All of the experimental work to be reported was done using the commercial sheet and plate alloy AZ31B (nominal composition: 3 pct Al, 1 pct Zn, 0.4 pct Mn, balance magnesium). This alloy is available commercially in two tempers, -0 (fully annealed) and -H24 (partially annealed), and specimens of both tempers were used in various experiments. The average grain. diameter (AGD) for -0 temper 0.125-in. sheet is about 0.5 x 10- in.; where material of larger grain size was desired, anneals at elevated temperature were used to grow the grains. compression tests were made on a screw-driven "hard" machine. The specimens were clamped in a

Jan 1, 1964

By H. Warlimont

Precipitation of cementite plates from carbon-rich austenite gives rise to localized formation of martensite in the matrix next to the precipitate upon quenching. The growth of this martensite is urmsually restricted. A distinct lattice relationship is found between this martensite and the cementite phase. It is concluded that the martensite is nacleated in the region of lowest carbon concentration at the austenite-cementite integace, with low-energy matching to the cementite lattice. The restriction of the growth of the martensite phase to the vicinity of the cementite plates can be explained by misfit in the austenite -martensite glissile interface and the uphill carbon gradient in the austenite. The investigation was carried out by light- and electron-microscopy and by electron-diffraction of thin foils. THE precipitation of cementite from carbon-rich austenite gives rise to a localized formation of martensite in the matrix next to the precipitate upon quenching. This behavior has been described previously by A. B. Greninger and A. R. Troiano1 for a 1.78 pct C steel ("pseudomorphic martensite"), and by A. Hultgren2 for a Fe-0.99 pct C—5.20 pct Mn steel. By measuring the axial ratio of the martensite phase,' it was found that the carbon content of this martensite was lower than that of the martensite which formed without prior partial transformation to cementite. Therefore, it was concluded that lowering of the carbon concentration in the matrix next to the precipitate raised the M, temperature locally and thus led to nucleation of martensite at the ce-mentite-austenite interface. However, the restriction of the growth of the martensite phase to the vicinity of the cementite plates cannot be explained by localized carbon impoverishment alone. Under ordinary conditions a martensite plate which has been nucleated in a favorable site can continue to grow until it encounters a physical barrier, or until it encounters a compositional barrier in the matrix, where the total free-energy change for the reaction is not negative, since it has been shown by numerous experiments that the activation energy for growth of ordinary martensite is virtually zero.' An investigation was conducted by transmission electron microscopy and electron diffraction to study this extraordinary martensite. It was expected that crystallographic in addition to compo- sitional conditions caused this abnormal mode of martensite formation. MATERIAL AND PROCEDURE An Fe-C-Mn alloy containing 1.15 pct C and 5.1 pct Mn was used for most of the experiments. For metallographic work, specimens 15 by 15 by 3 mm were used. For preparation of thin films, the initial specimen size was 15 by 15 by 0.7 mm. The heat treatment of each specimen consisted of austenitizing for 1/2hr at 1100'~ in an argon atmosphere, subsequent isothermal holding in a lead bath at one of a series of different temperatures, and, finally, quenching into brine at room temperature. For metallographic examination, the specimens were mounted in bakelite (slight tempering effects resulted from the heat in the mounting press) ground, polished, and etched in nital. Thin films for transmission electron microscopy and electron diffraction were obtained by grinding the specimens to approximately 0.2 mm thickness and subsequent electrolytical thinning. The orientation relationships were evaluated from sets of electron micrographs and selected-area electron diffraction patterns of single units of the transformation products and the adjacent matrix. RESULTS In the alloy which was used for the experiments, proeutectoid carbide precipitates over a wide tem-

Jan 1, 1962

By Charles R. Cavanaugh, John F. Elliott

The activity of nickel in liquid Pb-iVi alloys which are rich in lead was measured in the temperature region of 700° to 1100°C by means of the galvanic cell: The electrolyte used was stabilized zirconia. Tlze data were correlated using the a function, and a plot of the temperature coefficient aE/aT All subsequent calculations of the thermodynamic properties are based on these two functions. The activity, activity coefficient, and molar properties of mixing of nickel are reported. Nicke1 shows extreme positive deviations frorn ideality while lead shows a very slight positive deviation in the composition range studied The study of the activity of nickel in liquid Pb-Ni alloys reported herein was undertaken to explore the use of stabilized zirconia, an oxygen-ion electrolyte, with liquid-metal electrodes, and to obtain further information on the thermodynamic properties of the liquid binary Pb-Ni system. The cell The reversible electromotive force of the cell results from the difference in the chemical potential of the oxygen at the two electrodes: po, (left) - p~ (right) = -4E5 [I] The chemical potential of oxygen on the right is fixed by the activity of nickel in the solution and pure solid nickel oxide. That on the left is set by pure solid nickel in equilibrium with pure solid NiO. By definition: Since the chemical potential of nickel is related to the chemical potential of oxygen through the equilibrium constant for the formation of NiO from nickel and oxygen gas, the electromotive force of the cell is also expressed In this case, n is 2, E is the reversible potential of the cell, and 5 is Faraday's constant. The work of Kuikkola and wagnerl and Schmalz-reid2 has shown that the stabilized zirconia electrolyte is essentially an ionic conductor at the oxygen levels encountered in the experimental arrangement of the work, i .e., PG > 10-l7 atm. THE EXPERIMENTS The advantage of this type of reversible cell over those using a liquid electrolyte is the simplicity arising because the electrolyte also functions as one of the containing crucibles. A further simplification was the choice of the Ni (sat.)-NiO electrode as the standard. This permitted a ready check on the behavior of the electrolyte, as the potential of the cell must become zero when the right electrode becomes saturated with nickel, either because of a change of temperature or because of the addition of nickel to the electrode. It also permitted the potentials being measured to lie in the most satisfactory experimental range of 0 to 100 mv. Although it was not theoretically necessary, lead was included in the standard electrode as it assured good contact between the electrode and electrolyte. Cell Design. The general arrangement of the experimental cell assembly is shown in Fig. l(a) and the details of the cell itself are contained in Fig. l(b). The anode lead wire on the interior of the cell was connected to a coil of perforated sheet nickel. Within this coil were nickel oxide pellets which were held beneath the surface of the liquid Pb-Ni alloy. A disc of nickel oxide was held at the bottom of the external crucible (alumina) by means of the thermocouple protection tube. The nickel oxide disc and pellets were compressed dry at 10,000 psi and sintered at approximately 1000°C for an hour in air. A major experimental difficulty of reversible electromotive force cells with liquid electrodes is the selection of suitable materials for connecting

Jan 1, 1964

By M. B. Bever, A. K. Jena

Equations for the heat effects of additions of mixtures of multicomponent phases to a solution have been derived in terms of the enthalpy interaction coefficients. By these equations and the measured composition dependence of the heat effects on addition of mixtures of Ag-Cd solid solutions and elemental gold to liquid tin-rich solutions, values of the enthalpy in-teraction coefficients in tin-rich solutions at 541°K have been obtained. Analysis of these results in terms of the regular solution theory and the quasichemical theory suggests that near the melting point of the solvent association in the solution becomes important. SEVERAL recent papers have discussed the nature of dilute solutions on the basis of measured enthalpy interaction coefficients. l-3 These coefficients contribute to the understanding of the constitution of solutions and can be used for the evaluation of thermo-dynamic data of multicomponent systems. Their experimental determination, however, is laborious. This communication reports values of the enthalpy interaction coefficients of silver, cadmium, and gold in liquid tin-rich solutions obtained from the measured heat effects of additions of mixtures of Ag-Cd solid solutions and elemental gold to liquid tin-rich solutions. These measurements were made in the course of the determination of the heats of formation of Ag-Cd solid solutions reported in a concurrent publication.4 THE HEAT EFFECT OF AN ADDITION TO A SOLVENT This analysis is concerned with the addition of a mixture of multicomponent phases from the temperature To to a solvent of known composition at temperature T. If Nmixture << Nsolvent, where N designates the gram-atoms involved, the heat effect per g-atom of mixture added can be expressed as (HT - HT )i = difference in heat contents of component element i in the mixture at T and To Q = heat effect on solution of the mixture at temperature T Also1 Q = S Xi [2] where ?Hi ,T,x = relative partial enthalpy per g-atom of i in solution at temperature T and composition of the solution x x = average of the atom fractions of the added material in solution before and after the addition The relative partial enthalpy ?Hi per g-atom of an element i in a dilute solution composed of a solvent 1 and the solutes j = 2, ... m is related to the interaction coefficients by the following equation5 ?Hi - ?Hi-?Hi,x1-1 + S n1ixj+ . . . +S...S...S nrixn2... Xnji...Xnmm+... [3] vhere Xj = atom fraction of solute j in the solution nri = the rth order enthalpy interaction coefficients, which can also be represented by the more general designation5 L(i)n2,n3...nm and nj may have any positive integral value or zero. For identification of various rth order interaction coefficients, nri is written as nn2i2,...nij,...nmm. Eqs. [1], [2], and [3] combine to give the following general equation for the heat effect on addition of a small quantity of a mixture to a large quantity of a dilute solution n = _?ga ?Ha,To + ? Xi(HT - HT o)i a. i + ?xi?Hi,X,i?1 + ??xnjixj + . . . + ???. . .?. . .?xinrix2n2. . . xnji. . . xnmm+ . . . [4] The first term on the right-hand side of this equation is the heat of decomposition at the addition temperature of the phases present in the mixture, the second term is the heat required to raise the temperature of

Jan 1, 1970

By H. H. Rachford, D. W. Peaceman

A system of partial differential equations describing miscible displacement of fluids in porous media is derived The system takes into account the influence of gravity, the spatial distribution of permeability, diffusion, and fluid viscosities and densities. A numerical procedure for approximating solutions to the differential systems has been tested for a horizontal two-dimensional geometry. In end-to-end displacements of oil with less-viscous solvents, the numerical solutions exhibited fingering qualitatively similar to that observed in laboratory models. Small random spatial variations in permeability about the mean value are sufficient to initiate fingering. Quantitative comparisons of computed results with laboratory data show good agreement. INTRODUCTION Miscible flooding of oil by solvent is receiving increasing consideration for field use.1-4 Unfortunately, such floods potentially present severe problems in loss of recovery through the by-passing of oil by expensive solvent. Consequently, their economic evaluation requires sound techniques for predicting recovery. The purposes of this work are to present a finite-difference method for calculating the multidimensional displacement of oil by solvent and to investigate the validity of the method by comparing results of calculations with data from displacements in laboratory models.5 The formulation of the method to simulate the model experiments treats a case of limited scope in the description of solvent flooding in the reservoir. The model experiments were carried out with fluids that were assumed to form an incompressible, ideal, two-component system with constant diffusivity. Establishing the validity of the method even in its present form provides a major step toward the goal of quantitatively evaluating individual solvent flooding projects. First, it demonstrates the fea- sibility of calculating the course of displacements which are dominated by an inherent macroscopic instability, i.e., viscous fingering. In addition, the method provides almost the only practical means of examining the effect of the size and extent of reservoir inhomogeneities on the development and propagation of the fingers, taking into account the important influences of diffusion and gravitational segregation. It might be inferred that such studies cannot yield results of practical value because in displacements dominated by macroscopic instability the pattern of finger development and the resulting performance should depend critically on small variations in the geometric distribution of reservoir inhomogeneities. The present method offers the capability inherent in computational techniques of predicting performance reproducibly with any arbitrary distribution of reservoir properties and, as such, provides a means of evaluating the sensitivity of behavior to uncertainties in reservoir definition and, thus, assessing the reliability of prediction of performance. THE PHYSICAL PROBLEM DATA USED FOR QUANTITATIVE TESTS OF CALCULATIONS In this work, a calculation for treating the miscible-displacement process is tested by comparing calculated results with experimental data. The experiments chosen for comparison have been described in detail,5 and the quantitative features are summarized in a later section. Briefly, oil was flooded by solvent of equal density from a thin rectangular channel in Lucite packed with uniform Ottawa sand. Under these conditions, two-dimensional geometry is considered adequate to represent the process. Inasmuch as the present work is concerned with testing of the method by comparison with specific two-dimensional data, the system of equations presented in the succeeding section will be oriented to defining the physical system specifically. THE DIFFERENTIAL EQUATIONS Suppose x, y to be a Cartesian co-ordinate system and define h(x, y) to be the height of a point above a horizontal reference plane. It will be assumed

By M. C. Smith, W. V. Green, D. M. Olsen

The creep-rupture behavior of commercial powder-metallurgy molybdenum rod is reported in the temperature range 1600" to 250O°C, at stresses up to 9000 psi and times up to 1 month. The effects of temperature, stress, and grain growth are discussed. Rupture time is fitted to the Larson-Miller parameter and compared to lower-temperature and higher-stress results reported by pugh.1 BECAUSE of its high melting point, molybdenum should retain useful strength to relatively high temperatures. Combined with its ready availability in the United States, this makes it attractive for many applications in missiles, rockets, and so forth—wherever its susceptibility to oxidation can be tolerated or overcome. The mechanical properties of molybdenum rod in the temperature range —200" to 1540°C have been reported by pugh,&apos; Bechtold,&apos; Parke,3 and Carriker and Guard.4 Madden and chen5 have measured the tensile properties of molybdenum single crystals in vacuum up to about 2500°C. As one further step in evaluating its mechanical usefulness, the constant-load creep-rupture properties of commercial powder-metallurgy molybdenum rod have been investigated in the range 1600" to 2500°C. MATERIAL TESTED Creep specimens were machined from 1/2-in. round commercial molybdenum rod, manufactured from powder by pressing, sintering, and swaging. Spectrochemical analysis of the rod showed "traces" (less than 0.01 pct) of silicon, aluminum, chromium, iron, and zirconium, and "faint traces" (less than 0.001 pct) of manganese, magnesium, cobalt, and nickel. Carbon content was 130 to 200 ppm, nitrogen was 110 to 180 ppm, and oxygen 30 to 35 ppm. A typical microstructure of the as-received rod is shown in Fig. 1. Room temperature tensile properties for five specimens strained at about 0.015 in. per in. per min are shown in Table I. CREEP SPECIMENS USED The specimens used for creep-rupture testing are illustrated in Fig. 2. The 1/4-in.-diam gage section was 3/4 in. long, and terminated at shoulders 5 mils high. These shoulders served as fiducial marks for optical strain measurements. Surface finish on the gage section was 16pin. r.m.s. One specimen, for a "long-time" test described below, was modified by dividing the 3/4-in. gage length into three 1/4-in. long sections with individual diameters of 0.250, 0.230, and 0.210 in., each terminating in a pair of fiducial shoulders. TESTING PROCEDURE The constant-load creep-testing machine used has been described by Smith, Olson, and Brown.6 In it the specimen is held vertically on the axis of a cylindrical tantalum or tungsten heater tube by threaded molybdenum or tungsten grips. Both specimen and grips are heated by radiation from the heater-tube, which is heated by its own electrical resistance. The bottom specimen grip is held at its lower end by a clevis pin. The testing load is applied to the specimen through the upper grip by means of hanging weights, a constant force-multiplication lever system, and a pull rod sealed to the chamber lid by a bellows. The incandescent specimen is viewed by an external optical system through slots in the heater-tube and radiation shielding, and an enlarged image of it is projected on a ground-glass screen. Gage-length measurements are made on this image with a pair of cathetometers. Thorium oxide coatings were applied to the threaded ends of most specimens, to prevent diffusion-welding of specimens to grips during testing. Without such a coating welding usually occurred, and grips were often broken by subsequent efforts to remove the tested specimens.

Jan 1, 1960

By J. E. Spruiell, F. H. Patterson, B. F. Shuler

The microstructures and textures developed by the working of high-purzly thermochemically deposited tungstem sheet have been inuesligated. Greater than 60 pct reduction was required to deslroy the columnar grain structure which existed in the as-deposited sheet. With increasing reductions the texture gradu-ally charged from the initial as-deposited orientation with (100) parallel to the sheet normal to a (100}(011) ideal ovienlation with some spread about the rolling direction. This texture was retained after recrystalli-zation a1 2000°C. THE processes for depositing tungsten by hydrogen reduction of tungsten hexafluoride have been under development for the past several years.1,2 The nature of the deposition process is such that the as-deposited material contains a highly oriented columnar grain structure perpendicular to the deposition substrate. This well-defined columnar structure may be useful in certain applications293 but a wrought or equiaxed structure may be desired for some components such as tubing. Knowledge of the effects of working ther-mochemically deposited (TCD) tungsten is therefore necessary in order to establish the feasibility of obtaining worked and recrystallized microstructures and textures. The details of a recently developed technique for thermochemically depositing flat, uniformly thick tungsten sheet are presented with emphasis on the effects of deformation by rolling on the microstructure and texture. Although no work has been previously reported on the rolling and the annealing textures of TCD tungsten, there have been some determinations of textures for cold-rolled tungsten foil prepared from powder-metal -lurgy billets.4-8 The general description is that of a predominantly lurgy{100}(011) texture, with some spread about the rolling direction as an axis. pugh5 reports data both for cold-rolled and for annealed foil having about 96 pct initial cold work. He observed no change in texture, except for a decrease in the spread, for annealing treatments of 30 min at temperatures up to 1800°C. On annealing at 1900°C, both the low-temperature components plus new components which were described alternately as {001}(320) plus {001)(230) or as {100}(011) ± 12 deg about the sheet normal were observed. Above 1900°C, the new orientation existed alone, and it was stable up to 2500°C, the highest temperature that Pugh investigated. THERMOCHEMICAL DEPOSITION OF TUNGSTEN SHEET High-purity tungsten sheet was reproducibly deposited on the inner walls of a molybdenum mandrel by the thermochemical reaction WFs(g) + 3H2(g) - W(s) + 6HF(g). The mandrel was heated by a five-zone tube furnace which afforded a controllable fixed-temperature profile. Sheets measuring 1+ by 12 in. have been deposited with uniform thicknesses of up to 0.145 m. As shown schematically in Fig. 1, the purified reaction gases were metered into a mixing chamber at a Hz-to-WF6 ratio of 15 and preheated to 350°C. The flow rate of the WF6 was 300 cu cm per min at stp. These gases were directed through a conical injector into the deposition chamber. Inside this chamber hydrogen reduction of the WF6 to pure tungsten metal occurred on the hot walls of the molybdenum mandrel at a total pressure of 5 Torr. Typical temperatures for the five zones in the chamber were, respectively, 565", 540", 550°, 570°, and 590°C. The hydrogen fluorlde generated from the reaction, the excess hydrogen, and some un-reacted WF6 were pumped on through the scavenger

Jan 1, 1968

By C. H. Lee, R. Maddin

The diffusion rates of Ag110 in cylindrical single crystals of 99.99 pct pure silver, which were twisted to a total surface strain of 0.91 during the diffusion anneal at temperatures of 700°, 750°, and 800°C, were measured by sectioning and counting as a function of the strain rates. The ratio of the diffusivities while strain ing occurred (Ds) to those of the unstrained specimens varies linearly with the rate of twisting and attains values of near 100 for some of the rates used. The enhancement of diffusion by straining is inversely proportional to the temperature at which diffusion occurs. The activation energy for diffusion determined from the data plotted as a function of the rate of twisting decreases from 44,090 cal per mole for zero strain, to an asymptotic value of 21,000 cal per mole for the strain rates of 22 x it)"5 see-l. Qualitative explanation for the observations based on the generation of nonequilibrium number of defects by plastic deformation will be discussed. The initial research of Buffington and cohen1 on self-diffusion in a iron under compressive stresses contributed the first quantitative information concerning the effect of applied stresses on diffusion. These results were obtained from radioactive Fe55 plated on one of the horizontal surfaces and compressing the large-grained specimens while the diffusion-anneal was occurring. Enhancement of diffusion of a maximum of seventeen times was observed provided the strain was in the tertiary stage of creep and the rates of straining were at least as fast as rates used in the normal creep test. On the other hand, Darby, Tomizuka, and Balluffi,2 extending silver single crystals up to 30 pct elongation at rates of straining about equal to those used by Buffington and Cohen observed no effect. For the past two and a half years at the University of Pennsylvania, we have been investigating the effect or torsional strains on self-diffusion in silver single crystals. If enhancement is observed as has been reported1 a possible explanation may be based upon the generation of fairly large numbers of point defects and their role in the diffusion process. Hence, since torsion should produce an abundance3 of point defects, an increase in the diffusivity while the crystal is being twisted should easily be measured. EXPERIMENTAL PROCEDURE Our research uses single crystals of silver prepared from 99.99 Ag by the Bridgman method in a dynamic vacuum of less than 25 µ. As grown, they are about 25 cm long by 1.3 cm in diam. The crystals are cut into 7.5 cm lengths with a jeweler&apos;s saw and machined to the shape shown in Fig. 1. The test length of the crystal is machined to a 0.6 cm diam after which the ends are masked and the test section etched heavily in HNO3, and KCN:(NH4),S2Os , solution to remove the effects of machining. The specimen is then annealed in vacuum for 8 to 12 hr at 800°C to remove any residual stresses and also to recrystallize the end sections. The recrystallized ends are necessary since experiments showed that single-crystalline end sections are too soft to transmit the desired torque. Occasionally, recrystalliza-

Jan 1, 1960

By A. M. Sarem

For the performance prediction of multiphase oil recovery processes such as steam stimulation, there is an acute need for three-phase relative permeability data. No fast and simple experimental technique, such as the unsteady state method proposed by Welge for two-phase flow, is available for the three-phase flow. In this paper, an unsteady - state method is presented for obtaining three-phase relative permeability data; this method is as fast and easy as Welge&apos;s method for two - phase flow. Analytical expressions are derived by extension of the Buckley-Leverett theory to three-phase flow to express the saturation at the outflow face for all three phases in terms of the known parameters. It is assumed that the fractional flow and relative permeability of each phase are a function of the saturation of that phase. Other simplifying assumptions made include the neglect of capillary and gravity effects. The effect of saturation history upon relative permeability is acknowledged and attainment of similar saturation history in laboratory and field is recommended. The required experimental work and computations are simple to perform. The test core is presaturated with oil and water, then subjected to gas drive. During the test, required data are the rates of oil, water, and gas production, together with pressure drop and temperature. The ordinary gas-oil unsteady-state relative permeability apparatus can be readily modified to measure the required data. The proposed technique was applied to samples of a Berea and a reservoir core. The effect of saturation history upon relative permeability was studied on one Berea core. It was found that increase in initial water saturation has a similar effect upon three-pbase relative permeability as it does in two-phase flow. INTRODUCTION In the light of increasing demand for three-phase relative permeability data for predicting the performance of thermal and other multiphase-flow recovery processes, a simple and accurate method of experimental determination of such data is extremely desirable. Leverett and Lewis 1 described the simultaneous flow method of obtaining three-phase relative permeability data. However, Caudle et al.2 reported that this method is very time consuming and cumbersome. Corey3 proposed calculating the three-phase relative permeability from measured krg data. Corey&apos;s theory is based on simplified capillary pressure curves,4 assuming a straight line relationship between I/Pc2 and saturation. Also, Corey&apos;s method assumes a preferentially water-wet system. The simplest and quickest method of obtaining three-phase relative permeability data is the unsteady-state method where, for instance, oil and water are displaced by gas. However, in such a test the correlation of average saturation with relative permeability does not give a valid relationship because the rates of oil, water and gas flow in the sample change continuously from the upstream to downstream end. This difficulty in calculating valid relationships was solved by Welge for two-phase flow by deriving an expression for determining the outflow face saturation from Buckley and Leverett frontal advance equations.5,6 In this paper, relations are established to determine the outflow face saturation and relative permeability to all phases in a three-phase flow displacement experiment. PROPOSED METHOD The fundamentals established by Buckley and Leverett5 for two-phase flow were extended to three - phase flow and used as a basis for the derivation of saturation equations. This approach is comparable to Welge&apos;s6 use of Buckley and Leverett theory in arriving at expressions to determine the outflow face saturation of the displacing fluid in a two-phase flow system.

Jan 1, 1967

By M. A. Dayananda

Based on the Kirkendall frame of reference, a method is proposed for the determination of atomic mobilities of all the diffusing species in a multicorn-ponent system with a single diffusion couple. The method is based on an atomic mobility model developed on the concept of negligible interactions among the intrinsic fluxes. It is shown in the model that mobilities can be obtained directly from the cumulative intrinsic fluxes past the Kirkendall interface. The proposed method replaces the need for a prior determination of interdiffusion coefficients far the calculation of mobilities. Relations between intrinsic diffusion coefficients and mobilities are derived and the mobility calculations are illustrated with diffusion data in Cu-Zn-Mn alloys at 850°C. ThE concept of "intrinsic flux" with respect to a fixed lattice was introduced "i Darken1 to explain toa Kirkendall effect2 demonstrated by the motion of inert markers during isothermal diffusion in single-phase binary solid solutions. Based on this concept, intrinsic diffusion studies have been made in various binary metallic systems3,4 employing such a lattice frame of reference, commonly referred to as the Kirkendall interface. Similar approaches, both theoretical and experimental, have been presented5"10 to study intrinsic diffusion in multicomponent systems. Based on the direct integration of Fick&apos;s law extended to multicomponent diffusion, Philibert and Guy8 proposed a method for the determination of intrinsic diffusion coefficients. For an n-component system, this procedure requires an experimental study with (n — 1) diffusion couples, all having their Kirkendall interfaces at the same compositio;, where n(n — 1) intrinsic diffusion coefficients are defined. This technique has been employed for ternary diffusion studies by Dayananda and Grace" and Guy and Leroy.11 A different approach is recommended by Ziebold and Cooper,12 who have derived relations between interdiffusion coefficients and atomic mobilities employing fluxes referred to the local center of volume. Their analysis is based on the simplifying assumption of negligible interactions among intrinsic fluxes. This assumption has been considered satisfactory for dilute solutions.5"7 The use of this analysis for the calculation of mobilities requires an initial determination of interdiffusion coefficients with a set of diffusion couples having intersecting diffusion paths. It is the purpose of this paper to propose a method that would permit a direct determination of mobilities of all components of a multicomponent system from a single diffusion couple. This method is based on a mo- bility model developed with diffusion fluxes referred directly to the Kirkendall interface, generally identified by inert markers. gen erall, like that of Ziebold and Cooper,12 employs the simplifying assumption that the flux of each component relative to a fixed lattice is caused only by the driving force of its own chemical potential gradient. THE KIRKENDALL INTERFACE Inert markers are employed in diffusion couples to locate experimentally the position of the Kirkendall interface. They are initially placed at the weld interface for "sandwich" couples, or at the original vapor-solid interface for vapor-solid couples. Studies of marker motion in binary systems3&apos;4 with both types of couples indicate that markers remain in a plane of constant composition and move with this plane para-bolically with time. Parabolic marker movements were also observed in ternary Cu-Zn-Mn couples by Dayananda and Grace.10 It is reasonable to expect a similar marker behavior even for diffusion couples with a higher number of components.

Jan 1, 1969

By M. A. Dayananda, R. E. Grace, P. F. Kirsch

Ternary diffusion experiments were carried out at 750°C with vapor-solid diffusion couples in single-phase copper-rich Cu-Zn-Sn alloys. The Philibert-Guy method was used to calculate intrinsic diffusion coefficients at compositions corresponding to the plane of inert markers imbedded in the diffusion couples. Inter diffusion coefficients were determined at common composition points of intersecting diffusion paths. Intevdiffusion coefficients were also obtained at compositions corresponding to maxima in the tin concentration pvofiles Relations between the interdiffusion coefficients and the expansion of vapor-solid diffusion couples are described in detail. Such relations permit the calculation of constant interdiffusion coefficients in binary couples from expansion data directly. In ternary couples expansion data provide an additional constraint on the interdiffusion coefficzents. ThE phenomenological analysis of diffusion in ternary solid solutions has been developed extensively, and various approaches taken in the determination of diffusion coefficients have been reviewed recently by Guy et al.&apos; Finite,&apos; semi-infinite,3 and infinite4 diffusion couples have been used in studies of ternary diffusion, but most of the work has been done with infinite diffusion couples. Semi-infinite diffusion couples3 (vapor-solid couples) have been used to determine both intrinsic and interdiffusion coefficients in the Cu-Zn-Mn system, in which two diffusing species, zinc and manganese, were supplied from the vapor phase. If only one component has a sufficiently high vapor pressure to be supplied from a vapor source, vapor-solid diffusion couples may still be used. In this case the boundary conditions at the gas/solid interface may be governed by partial equilibria rather than by virtually complete equilibrium between the phases. In the present work diffusion measurements were carried out at 750°C with vapor-solid couples of Cu-Zn-Sn alloys. Only zinc was transported between the vapor source and the diffusion disks, because the vapor pressures of both copper and tin are at least 108 lower than that of zinc. Both intrinsic and interdiffusion measurements were made at several compositions. A secondary objective was to relate expansion of the diffusion couples with the interdiffusion process. Such measurements for binary couples yield average values of the interdiffusion coefficients over composition increments. In ternary diffusion couples ex- pansion data provide an additional constraint on the interdiffusion coefficients. COMPOSITION-DEPENDENT INTRINSIC AND INTERDIFFUSION COEFFICIENTS As shown by Philibert and GUy5 the determination of intrinsic diffusion coefficients in a ternary system requires two independent diffusion couples containing marker planes with identical composition. In the case of vapor-solid couples such a requirement torresponds to two couples set up with the same vapor source exposed to two diffusion disks of different composition. Inert markers placed initially on the disk surfaces become imbedded during diffusion. If the pair of couples exhibits appreciable marker burial with marker planes of virtually the same composition, the intrinsic diffusion coefficient may be evaluated at the composition of the marker planes. Fig. 1 is a schematic diagram of the concentration of of a Cu-Zn-Sn ternary vapor-solid couple after diffusion of zinc from a vapor source into a binary Cu-Sn alloy. The areas, Ai correspond to the cumulative intrinsic fluxes of the three diffusing species across the marker plane:5 where Ji is the intrinsic flux of component i, t is the diffusion time, and D3i are the intrinsic diffusion coefficients. For the determination of interdiffusion coefficients a pair of diffusion couples with intersecting diffusion paths is needed. At the composition point of intersection (C1, C2) the coefficients are evaluated from the equation:3

Jan 1, 1969

By A. J. May

THE Star shaft is near the north boundary of the group of mining claims belonging to the Ground Hog Unit of the American Smelting and Refining Co., near Vanadium, N. Mex. The shaft bins and surface plant are served by a siding from the Atchison, Topeka and Santa Fe railroad, and this factor of railroad transportation influenced the choice of site. This paper describes the shaft sinking only, and does not cover the surface plant or other parts of the mine or its equipment. Experience with this shaft seems of interest because of the mechanical mucking, good rate of progress, and the costs obtained at the present level of labor and material costs. The shaft has four compartments, as shown in fig. 1. Equipment: Riddell Mucker: The mucking was done by a clamshell bucket and a Riddell mucker, which, as in other shafts sunk with this machine, consisted of a carriage mounted on axles with double flanged wheels that traveled back and forth on a swinging track, parallel to the long axis of the shaft (fig. 2 to 6). Three air motors were mounted on the carriage; one hoisted the clam, one operated the bucket opening and closing device, and the third moved the carriage along the track. The carriage was designed with guide shoes and could be hoisted to the surface in either skip compartment without trouble (fig. 4). During blasting operations the clam was tied on the rails and the carriage was hoisted up a few sets to protect it from flying rock. No attempt was made to hoist the carriage and clam together lest the clam catch in the timbers. The track on which the carriage operated was built of extra heavy 6 in. pipe with 1x2 in. strap welded on top for rails. A 1/2x4 in. angle was welded on the bottom of the 6 in. pipe with a 1 in. round rod welded in the angle for a filler and additional strength. The end or cross pieces of the track which kept the track to gauge, were also made of reinforced, heavy 6 in. pipe and were bolted to the long members on which the carriage traveled (fig. 2 and 3). This section of track was used, instead of heavy railroad rails, for two reasons: (1) this section would bend before it snapped and was much safer for the men in the bottom; and (2) it was a better blasting shield, and protected the timbers better, in fact, only five wall plates were broken by blasting in 1926 ft of shaft, although 150 to 225 lb of 40 pct powder was loaded per round, depending on the ground conditions. The swinging track was supported by four 5/s in. hoisting cables anchored to the end plates. There were also four safety cables fastened two to three sets above the carriage, which would catch the carriage if one of the supporting cables should fail for any reason (fig. 7). Clamshell Buckets: Two clams were used, each of 3/s yard capacity, both manufactured by Blaw Knox, Nos. 662 and 663. The No. 663 clam was 4 in. wider and 5 in. shorter than the No. 662, but seemed to dig and load more satisfactorily. It was easier to hoist and lower when it came up for repair. It did not turn over as easily, had less spill

Jan 1, 1950

By Granville S. Borden

MANY complaints have been filed by mine prospectors, explorers and producers about inequities in mining taxation. They have insisted upon improvement, and in the past 35 years there has been some progress. Many of the best taxation provisions made to date are those contained in the Revenue Act of 1951. Mining economics presents special problems, a fact even recognized by many textbooks. Certain provisions have been made to take care of mining taxation rights, but these have been made by Congressional act and do not represent basic, constitutional, guarantees. Despite special provision, in the form of depletion allowances, there remain injustices. The industry faces the problem of gaining adequate income tax allowances for exploration and development expenditures, operating losses, and bonus and subsidy payments. Problems in mine taxation arose soon after the adoption of the 16th Amendment. This amendment gave Congress the power to impose income taxes. Supreme Court decisions against a number of mining companies held that Congress, under its power to tax income, could tax net operating revenue before depletion allowance was deducted. The court also ruled that the right to deduct depletion is a matter of Congressional permission. There is no statute provision permitting mining stockholders to recover their investment out of dividends while the mine is being operated. The Supreme Court did not recognize that part of mining proceeds are actually amortization of the cost of mineral rights. Both these omissions stem from failure to recognize that by its very nature mining consumes its mineral rights and therefore that a part of gross proceeds are not income but recovery of capital. Suppose a Congress unfriendly to mining interests repeals the provisions that allow deductions for depletion. Under such a situation assume that a corporation buys a mineral deposit for $300,000. They mine the deposit and earn an operating profit of $500,000. At the current rates they would pay a Federal Income tax of in excess of $250,000. This venture results in a loss of $50,000 as shown in the table below. For the example given the absence of depletion provisions in income tax law would turn ore into waste rock, because the word "ore" connotes commercially mineable rock. [ ] In retrospect the conclusion is clear: If the Supreme Court had recognized that a part of mining proceeds represent in reality sales proceeds of mineral rights, then profits derived from such sales would have been taxed at the favorable long-term capital rates, instead of being taxed at the high normal, surtax and excess profits rates. It is a question whether percentage depletion allowances offset this tax situation. History The history of depletion allowances has been one of general improvement. The original act did not include depletion, but an allowance at the rate of 5 pct of gross proceeds was provided in 1913. The Acts of 1916 and 1917 allowed depletion upon cost of property, and in 1918 the law was further changed to permit depletion upon cost, or market value as of date of discovery. In 1932 metal, coal and sulphur properties were permitted to elect depletion in percentages of gross income, limited to 50 pct of net income, in lieu of cost depletion. Shortly thereafter the rule was changed and percentage depletion is now allowable in any case where it is higher than cost depletion. Since 1942 percentage depletion allowances have been extended to cover many nonmetals, and in 1951 the rate for coal mines was increased from 5 to 10 pct of gross income. It is interesting to note that these allowances have been retained, and even

Jan 1, 1952

By Dean Goodermote, Carla S. Stone

I Introduction Coal fuels China. Roughly 70 percent of all commercial energy demand is supplied by domestic coal production and with the recent Chinese opening to the West, the Chinese Coal Industry may figure prominently in the export market as well. Because of the importance of China&apos;s coal industry to the future of China and the Pacific Rim energy balance, this paper reviews the industry and offers some cautious projections for its outlook. II Energy&apos;s Position in the Current Political and Economic Climate Traditionally, Chinese society has been dominated by the policies of its most important government leaders. Deng Xiaoping, Vice Chairman of the Communist Party is the current leader of China. Deng and his proteges are pragmatists. Although China&apos;s government structure is based on Marxist/Leninist tradition, Deng and his followers are promoting experiments with market economics and expanded relationships with Western Countries, which have encouraged foreign investment in China. Energy companies represent just one type of industry that is interested in helping the Chinese to develop their abundant natural resources. Although China&apos;s leadership is committed to a program of economic modernization, that program currently is experiencing what the Chinese government terms "readjustment". Readjustment cuts back in imports due to deficient foreign exchange and deemphasizes heavy industry, while it encourages agricultural and consumer goods output and, most imporant, energy production. Increased Chinese coal and oil production is essential both to fuel industry and, equally important, to provide foreign exchange. If sufficient energy production is not forthcoming, then economic growth will be severely retarded. China&apos;s 1979 per capita GNP of $260 is only slightly better than the weighted average achieved by low income countries of $230. (1) Delays in growth could lead to social unrest, threatening the position of the current leadership. Since there is no institutionalized mechanism for leadership succession and policy continuation, it is reasonable to assume that leadership changes could result in energy policy changes. III Energy Consumption Energy production is important to China&apos;s future economic health as highlighted by the World Bank. If China&apos;s economy grows rapidly, 5 percent to 6 percent during this decade, the Bank noted, a significant energy shortfall could occur as early as 1985. This state of affairs contrasts sharply with China&apos;s current position as a net hydrocarbon exporter. (2) To assure a healthy economic future, China&apos;s leadership is attempting to reduce its rate of increase in energy demand through conservation as well as to boost energy output. A massive conservation promotion program has been underway since 1979 and there is much room for improvement. China&apos;s industrial sector is only about half as energy efficient as is U.S. industry. (3) During the last two decades, each percent of increase in GNP has been accompanied by a 1.8 percent of increase in energy consumption. (4) This compares rather poorly with the United States where a less than one-to-one relationship exists. IV Energy Supply The short term prospects for oil production are uncertain. Production increases were rapid in the 1960&apos;s and early 1970&apos;s, averaging 20 percent annually, but most of this increase came from one field, Daquing. Now that Daquing&apos;s production has peaked and the offshore potential has yet to be developed, petroleum production has maintained a plateau of 2.1 million b/d, at least temporarily, of which approximately 15 percent is exported. (5) Output

Jan 1, 1982

By A. D. Rich

The term "bleaching clay" or "bleaching earth," as used in the oil industries, refers to clays that in their natural state, or after chemical or physical activation, have the capacity for adsorbing coloring matter from oil. There are three common types of bleaching clays: fuller&apos;s earth, activated clays, and activated bauxite. Fuller&apos;s earth, or naturally active clay, is prepared from bentonites (see Chap. 5) that possess natural activity. It is not activated commercially; in fact, earths of this type ordinarily do not respond satisfactorily to acid activation. Fuller&apos;s earth is prepared in pulverized as well as granular form for use in the contacting and percolation processes, respectively. Acid-activated clays also are of bentonitic origin. The basic raw clay, however, is of a type that has a very low natural activity but is highly activable by treatment with mineral acid. Commercial acid-activated clays generally possess several times the decolorizing power (bleaching efficiency) of the best quality of fuller&apos;s earth. The former are prepared commercially only in the pulverized grade because of the difficulties in obtaining a satisfactory granular product, and hence are used only in the contact process. Activated bauxite is made by heat-treating bauxite ore, which in its natural state has very little natural activity. The commercial product is prepared in granular form for use in the percolation process on petroleum oils. For the most part, bleaching clay is used commercially in the decolorization of animal, vegetable and petroleum oils, fats and waxes. It is applied in two ways: (1) by the percolation method and (2) by the contacting method. Percolation refers to the passage of oil through a bed of granular clay whereas contacting refers to direct agitation of oil and pulverized clay followed by removal of the clay from the oil by filtration. In either case, the decolorizing effect is obtained by intimate contact between the liquid oil and the solid adsorbent. Petroleum oils are treated commercially by either the percolation or the contact process. Animal and vegetable oils are treated by the contact process only. Composition The raw clays from which both fuller&apos;s earth and acid-activated clays are prepared are composed of hydrous aluminum silicates containing varying quantities of magnesium, iron, calcium and other elements. These raw materials are usually nonswelling bentonites derived from volcanic ash or lava by weathering and hydrothermal chemical reactions. The bentonites have as their chief mineral constituent montmorillonite, which has the formula [(OH)4Si6A14O20•nH2O], according to Grim. (See Chap. 5, ref. 6, p. 91.) The underlying reasons are not fully known for the natural activity of the fuller&apos;s earth type of clay and its usual failure to further activate with mineral acid in contrast to the natural inactivity of the activatable type of clay. However, it may be said that the bentonites that are responsive to the acid-activation treatment generally have not undergone any drastic metamorphism. The chemical composition is not a reliable means of discrimination between a nonactive, a naturally active, and a nonactive but activable clay, therefore it is not possible to forecast the ultimate quality of a clay on the basis of the raw-clay analysis alone. Table 1 gives typical analyses of representative clays of the foregoing classifications.

Jan 1, 1960

By D. J. Pye

Certain high molecular weight synthetic polymers in very dilute solutions decrease water mobility in porous media 5 to 20 times more than would be expected from the solution viscosity. This indicates that increasing water viscosity to reduce adverse mobility ratios in water floods is economically feasible in many situations. Laboratory results are consistent with accepted theory with respect to improved areal sweep, permeability distribution and displacement efficiencies as would be predicted from the solution mobility measured in the core. The laboratory results have been confirmed by field pilot floods which recovered 80 per cent and 100 per cent more oil than comparative water-flood pilots in fields containing 16 cp and 130 cp oil respectively. Economic analyses based on pilot data indicate the method to be profitable. INTRODUCTION The desirability of improving the water-oil mobility ratio in waterflood-ing operations has long been appreciated, especially for high viscosity crudes. Methods of reducing the oil viscosity by application of heat, gas resaturation and miscible drives have met with some success. Conversely, it has been generally conceded that increasing the water viscosity would also be effective, but the amount of thickening agent required to effect an appreciable increase in viscosity is discouragingly high. The use of such materials as glycerin, sugar, or glycols is completely out of the question economically, so that considerable attention has been given to the use of the much more efficient synthetic water-soluble polymers as viscosity improvers; but even these materials are not economically attractive. If increased water viscosity could be economically realized, marked improvements in areal sweep efficiency, as discussed by Caudle and Wittel and others, would be realized in field operations. Similarly, the improved mobility ratio would bring about increased recoveries by correcting permeability distribution problems as discussed by Stiles2 and Dykstra and Parsons,&apos; and improvements in displacement efficiency would be obtained as recognized by Buckley and Leverett4 and Welge.5 LABORATORY STUDIES THE RESISTANCE EFFECT In the course of research to develop a more efficient water-soluble polymer viscosity builder, we discovered that a very few types of water-soluble polymers exhibited a most unusual and very interesting property not previously observed. Among the earliest materials showing such activity were polymers containing acry-lamide. Fig. 1 shows a typical plot of the solution viscosity vs concentration for one of these polymer solutions as determined in an Ostwald viscometer. As usual, such a plot is an approximate straight line on semi-logarithmic paper. Now, an inspection of Darcy&apos;s law, shows that a viscosity value can also be determined in a formation sample if the pressure, flow rate and permeability are known. If the core permeability is previously determined with wa- ter or brine, then the viscosity of another aqueous fluid may be determined from the equation. The viscosities so determined for glycerin (glycol or polyvinyl alcohol solutions, for example) agree with the viscometer determinations. However, in the case of the water-soluble polymer solutions in which we are interested, the viscosities measured in the formation sample depart very markedly from the viscometer values. A typical relationship for a polymer solution is also shown in Fig. 1. This unusual departure from the expected response is referred to as a resistance property of the polymer and is quantified as "resistance factor". Since the resistance factor R can best be determined in a core under study, the term has been defined on the basis of the ratio of the brine mobility to the polymer solution mobility at residual oil saturation so that:

Jan 1, 1965

By R. Fawley, M. A. Quader, R. A. Dodd

Stacking fault energies and annealing twin frequencies have been measured for austenitic stainless steels having a) constant 20 wt pct Cr and varying nickel contents, and b) constant 20 wt pct Ni and varying chromium contents. The effect of nitrogen has also been studied and, to a lesser extent, so has the effect of carbon. All measured stacking fault energies plot linearly against the corresponding annealing twin frequencies, suggesting that, for constant prior deformation and grain size, twinning frequency can be used to estimate stacking fault energy. Compositions low in nickel possess the lowest fault energy, while the maximum fault energy within the investigated composition range occurs mound 20 pct Cr-20 pct Ni. Nitrogen has practically no effect on stacking fault energy when increased from 0.005 to 0.05 wt pct, although Planar dislocation glide is associated with higher nitrogen contents; this may be a short-range order effect. Carbon may raise the stacking fault energy a little, and causes pronounced dislocation tangling in deformed alloys. The basically different dislocation structures promoted by nitrogen and carbon, respectively, are not associated with large variations in stacking fault energy, and the reason for the difference remains unknown. INTEREST in the dislocation configurations developed in plastically deformed alloys arises principally from a desire for an understanding of mechanisms of plastic deformation and fracture. Comparatively little basic work has been concerned with austenitic stainless steels, although considerable interest has developed in the fundamental aspects of deformation of these alloys since the suggestion that those compositions deforming essentially by planar glide are particularly prone to transgranular stress corrosion cracking.&apos; Certain facts are well-established. An 18 Cr-8 Ni steel (type 304) has a low stacking fault energy which is increased by higher nickel contents, and the structure of these steels when moderately plastically deformed changes concomitantly from planar to less planar to distinctly tangled dislocation configurations. These changes are thought to relate to changes in stacking fault energy, and considerable effort has been expended in measuring stacking fault energies of austenitic stainless steels through the determination of node curvatures2"4 even though the method has limitations due to formula approximations,5 an upper limit of measurement of 50 erg cm-2 at the most,5 and the necessity of an extremely meticulous experimental technique. Therefore, it is not surprising that only qualitative agreement between different investigators is generally to be found.&apos;-&apos; At high energies where node radius measurements are inappropriate, some use has been made of annealing twin frequencies to estimate relative stacking fault energies, although a recent critical evaluation of the method suggests that it should be used cautionsly with due regard to effects of grain size and prior deformation.6 Finally, there is a question as to whether the structures of some deformed steels are due to ordering effects. In particular, the role of nitrogen in promoting planar dislocation motion has been suggested to be due to ordering,&apos; but similar suggestions have been made for steels having low interstitial contents.4 EXPERIMENTAL Small ingots of austenitic stainless steels (-50 g) were prepared from components exceeding 99.99 pct purity, the nickel and chromium being Johnson Matthey "Specpure" metals. Carbon was added as pure graphite, and nitrogen as CrN. The components were accurately weighed, and it was assumed that the final composition was the same as the nominal composition

Jan 1, 1969

By F. D. Rosi, C. A. Dube, B. H. Alexander

WHEN a deformed polpcrystalline metal is heated to a sufficiently high temperature, a recrystallized structure develops which consists of small, essentially stress-free grains. This transformation is referred to as primary recrystallization. Under certain conditions, on prolonged annealing of the specimens, a type of grain coarsening occurs in which a small number of grains commence to grow at various points by devouring the neighboring finegrained primary structure, which, in itself, exhibits a marked stability toward normal grain growth. This grain coarsening process has been referred to by Burgers&apos; as "secondary recrystallization" or "exaggerated grain growth." Although much work has been done on recrystallization and growth processes, present knowledge of the factors which determine the occurrence and growth of secondary grains is inadequate for the advancement of a theory which accounts for the observed characteristics of this recrystallization phenomenon. In this respect, it would be important to make measurements of the velocity of growth of these large secondary grains. The early work of Feitnecht2 on aluminum showed that the size of secondary grains increased with temperature and time, suggesting that such measurements would be possible. More recently, Burgers1 found that the growth velocity of these grains in aluminum was constant over a large time interval, as is generally found for the growth velocity of primary grains in a uniformly deformed test piece.3-5 It is reasonable to expect that the determination of the activation energy of the secondary growth process might lead to a better understanding of the underlying atomic mechanism. This investigation, therefore, is one of a series primarily designed to measure the growth velocity of secondary grains at various temperatures for silver, copper, and aluminum. It is hoped that these studies along with those of orientation relationships, will establish a sound basis for theorizing as to the origin and nature of the secondary transformation. Experimental Procedure The metal used in the present investigation was high-purity silver (999.9 fine), which was supplied in the form of cold-rolled plates 0.250 in. thick. These plates were annealed at 500°C for 1 hr and then straight-rolled to a thickness of 0.04 in. in three reductions of approximately 45 pct, followed in each case by an anneal at 450°C for 1/2 hr. The 0.04 in. sheets were given a final reduction of approximately 50 pct, which resulted in a thickness of 0.02 in., thereby insuring two-dimensional crystal growth. Individual specimens of this material about 1x3 cm were used for all heat treatments, unless otherwise noted. The annealing was carried out under an atmosphere of argon in an Inconel tube furnace whose temperature was controlled to within -+2°C. Metallographic examination of the secondary transformation was accomplished by mechanically polishing the specimens on one side to approximately one half their thickness through 2/0 metallographic emery paper, and then electrolytically polishing in a solution of potassium ferrocyanide and sodium cyanide. With a current density of approximately 20 amp per sq dm, the time required to obtain a satisfactory surface varied from 3 to 5 min. Standard potassium bichromate was used to etch the electrolytically polished surfaces. A heavy etch with this solution produced a sharp contrast between the secondary grains and the fine-grained primary structure, darkening the latter while leaving the large secondary grains bright. All area measurements of the secondary crystals were made with a planimeter on enlarged tracings of the grains.

Jan 1, 1953

By Nicholas J. Grant, Rolf Nordheim, Bill C. Gissen

The system Cb-Re was examined in detail utilizing pure metals, careful melting techniques, and heat treatments. Metallographic and X-my methods were utilized for phase identification. In addition to soli-dus determinations, the composition limits and mode of formation of the intermetallic compounds 0 and X were determined. The binary constitution diagram Cb-Re has been the subject of a number of investigations.&apos;-7 Two intermetallic phases have been described and tentative diagrams have been proposed. It was the aim of this investigation to obtain a complete and more accurate diagram through the use of purer alloys and improved techniques. The diagram worked out by Knapton7 was published after our experiments were concluded. EXPERIMENTAL METHODS The starting materials were Re powder of 99.95 pct purity, supplied by the Chase Brass and Copper Co., and Cb rondelles of 99.6 pct purity, supplied by the Electro Metallurgical Co. Typical analyses are given in Table I. The alloys were prepared from compacted Re powder and Cb rondelles; for critical compositions master alloys were used. The melts varied from 5 to 50 g and were melted nonconsumably in an Heraeus arc furnace, under ti-tanium-gettered laboratory grade argon. It was necessary to invert the buttons and remelt, followed by crushing and further remeltings, the number of which depended on the nature of the fracture of the alloy. The weight of each alloy was carefully checked after each melting operation. It was found that significant weight losses occurred only when loose Re powder was used. These losses amounted to a maximum of 3 wt pct in such instances, but did not occur after the charge was once molten, regardless of the composition. Typical loss of weight after 4 remelts, including crushing, amounted to 0.2 wt pct. Oxygen pickup during successive melting cycles did not appear to be significant, since the weight gain values never exceeded 0.01 wt pct. Control of the composition of the alloys was not too difficult; however, the problem of homogenization was a far greater one. Optimum alloying conditions were finally achieved by a combination of master alloy production and repeated crushing and remelting cycles. The compositions of the alloys utilized to determine the constitution diagram are listed in Table 11. The weight balance method was used ultimately as the sole analytical method, since repeated checks indicated that it was accurate to 0.2 pct, if the weight losses were small. The results were double-checked by a metallographic study of the homogeneity of the samples, since this was presumed to be the more serious factor. Heat treatments at 1200°C or lower were accomplished by sealing the specimens in Vycor tubes, heating in a Globar furnace, followed by air cooling. This was considered to be an adequate quench because of the very low temperatures involved. For temperatures of 1200" to 1900°, alloys were homogenized and heat treated in a tungsten-filament resistance vacuum furnace. From 1900" to 2750" a tantalum-tube resistance furnace was utilized, operating under a vacuum of 105 mm Hg. The temperature measurements up to 1200" were made by means of platinum-platinum 10 pct Rh thermocouples, with an accuracy of 5°C. For temperature measurements greater than 1200°C, optical pyrometers were used. They were calibrated against a standardized instru-

Jan 1, 1962

By H. S. Wang, Y. P. Gupta

Diffusion of zinc and germanium in liquid silver is measured in the temperature range 975" to 1400°C by use of the capillary-reservoir technique. The ex-perinzental results are discussed in terms of the fluctuation and the "hole" theories of liquid diffusion, assunzing the solute as a point charge equal to the difference in the valences of the solute and solvent atoms. The additional coulombic interaction term due to the excess solute charge is evaluated in terms of the Thomas-Fenni approximation. The theoretical and experimental results agree with both the fluctuation and "hole" theories of liquid diffusion. No perceptible effect on solute diffusion in liquid silver of the size difference between the solute and solvent atoms/ions is apparent. DIFFUSION in liquid silver of electropositive solutes indium, tin, antimony, and homovalent gold has been previously reported by Leak and Swalin1 and Gupta,&apos; respectively. These solutes have nearly the same atomic size but differ principally from one another in excess valence (+2, +3, +4, respectively). The observed differences in the temperature dependence and the rate of solute diffusion were explained in terms of an added coulombic interaction between the solute and the solvent atoms. In the case of diffusion of gold in liquid silver, the data were found to be consistent with an effective valence for gold of -0.85, as proposed by Le Claire.3 Recently, Wang and Gupta4 have reported a study of diffusion of ruthenium, iron, and cobalt in liquid silver. The results of diffusion of these solutes and their temperature dependence were found consistent with the hole theories and the fluctuation theories of liquid diffusion, if ruthenium, iron, and cobalt were diffusing in liquid silver with relative valences -2, -1.3, and -0.5, respectively, instead of -3, -3, and -2 as suggested by the relative position of these elements in the Periodic Table of Elements. Furthermore, the predicted valences for these solutes were observed to be consistent with the sparsely available information on the magnetic properties of some of the dilute alloys of copper and silver with these solutes. In theoretical calculations of solute diffusivity, the solute was assumed as a point excess charge equal to the difference in the valences of the solute and solvent atoms. Both the assumption of a point excess solute charge and the use of the Thomas-Fermi approximation to calculate the potential of a solute charge are less precise for the case of electronegative solutes. Therefore, it was not possible to infer from the data on ruthenium, iron, and cobalt an effect, if any, on solute diffusion of the relative differences in either the Period or the size of the solute and solvent atoms or the solute atoms themselves. A study of the diffusion of Period 4 elements, specifically zinc and germanium was, therefore, undertaken since zinc and germanium, respectively, have relative valences of +1 and +3 in liquid silver and the data obtained on diffusion of these solutes could be compared with the available data on diffusion of Period 5 electropositive solutes, indium, tin, and antimony in liquid silver. From such a comparison, it was hoped to learn something about the effect, if any, of the ion size or the structure of the ion core on impurity diffusion in liquid silver. EXPERIMENT The diffusion of tracer zinc and germanium in liquid silver was studied by the capillary reservoir technique, modified adequately for use at high temperatures. In principle, capillaries containing liquid silver

Jan 1, 1970