By A. G. H. Andersen, A. W. Kingsbury

SILICON bronzes containing iron are used to a considerable extent in industry, under the trade name of P.M.G. alloys. Various classes of wrought alloys fall in the composition range 1.5 to 3.5 per cent silicon, and 0.5 to 2.5 per cent iron. Castings may contain as much as 6 per cent silicon and 3 per cent iron at present. The constitutional diagrams of these alloys are thus of considerable practical importance. Copper-silicon-binary alloys have been thoroughly investigated by a number of workers, the latest reports being those of C. S. Smith1 and of A. G. H. Andersen.2 Although much work has been done on iron-copper alloys,3 recorded investigations on the copper-rich copper-iron binary constitutional diagram are not numerous. Tammann and Oelsen4 determined the solubility limits of iron in copper by means of magnetic measurements, and found that the solubility of iron in copper amounts to a fraction of one per cent at 400°C., increasing slowly to one per cent at 800°C. From 800°C., the solubility increases rapidly and attains 4 per cent at 1100°C. Hanson and Ford,5 using electrical resistivity measurements and the microscope, determined a somewhat different solubility limit. Of earlier X-ray works on the copper-iron system, very little has been published. The work by Bradley and Goldschmidt6 on copper-iron-aluminum alloys includes some information on the copper-iron binary. These investigators conclude that substitution of iron in the copper lattice decreases the spacings, which is contrary to the evidence of the present work. Hanson and West7 have investigated the ternary alloys of copper with iron and silicon. Although their diagrams are valuable contributions to the understanding of these alloys, they did not recognize the kappa phase,12, 7,8 and their diagrams do not everywhere conform to the phase rule. The present work contains a check by means of X-rays of the solid solubility limit of iron in copper, and an X-ray investigation of the ternary-phase diagram, which, owing to present conditions, it became necessary to curtail considerably. PREPARATION OF SAMPLES Castings weighing about 75 grams were melted under vacuum. The charges were made up of ingot iron, copper cathodes from Laurel Hill, and refined silicon supplied by the Electrometallurgical Co. Alundum crucibles were generally used. The exceptions were alloys 77 and 78, which were melted in graphite crucibles. The ingots were annealed at 800°C. for one week, then samples were cut for chemical analysis. Longitudinal sections of the binary alloy ingots were hammered into plates 3 in. thick. Wherever possible, these plates were homogenized at temperatures ensuring

Jan 1, 1942

By C. M. Moncrief, B C. Craft

A bentonite-clay drilling mud when treated with tetrasodium pyroarsenate underwent substantially the same reduction in viscosity and water loss as when treated with the complex phosphates. The complex arsenate showed a slightly higher reversion after heating; the other arsenates showed poor viscosity-reducing properties. Introduction During the past 10 years the chemical control of drilling mud has become of major importance in affecting the successful drilling and working over of wells. The desired properties of drilling mud have been well established, and in obtaining these characteristics there has developed a large market for viscosity-reducing chemicals. Viscosity reduction produced by humic acid, tannic acid, sodium silicate, sodium tannate, Calgon, and the complex phosphates has been described by Loomis, Ford, and Fidiam.l The effects Of treatment with complex phosphates and ammonium PolyPhosPhates on the rheological properties of muds were investigated by Fancher2 and the alkali vanadates have been described by Williams.3 Laboratory Investigations It is the purpose of this paper to point out the effects of arsenates in controlling the viscosity and gelling characteristics of a drilling mud. Viscosities and gel strengths were measured at room temperatures with a Stormer viscosimeter calibrated in centipoises and operated at 600 r.p.m. Water loss was determined at 80°F. with the Baroid low-pressure wall-building tester at a pressure of I00 lb. per sq. in. for 30 min. The hydrogen-ion concentration was measured with a glass electrode. The bentonite-clay suspensions were prepared in the laboratory and allowed to age several days before testing. Members of the Arsenic Group in the periodic Table include arsenic, antimony and bismuth, but this investigation was limited to arsenic. Phosphorus also occurs in Group V of the Periodic system and phosphorus and arsenic form many closely related compounds such as pH3 and AsH3, P2O5 and As2O5, H3PO4 and H3AS04 Samples of tetrasodium pyroarsenate were prepared by fusing c.p. disodium arsenate (Na2HA5O4.7H2O). According to Friend,' this re-forms the ortho-arsenate on dissolution in water. Sodium trihydrodiorthoarsenate was prepared as described by Mellor,5 from arsenic pen-toxide as follows: As2O5 + 3H20 -> 2H3AsO4 2H3AS04 + 3NaOH Na3H3(AsO4)2 .3H20 Sodium dihydrogen orthoarsenateWaHz-As04) was obtained by fusing together equivalent quantities of arsenious Oxide and sodium nitrate, dissolving the residue in water and allowing it to crystallize.

Jan 1, 1946

By C. M. Moncrief

A bentonite-clay drilling mud when treated with tetrasodium pyroarsenate underwent substantially the same reduction in viscosity and water loss as when treated with the complex phosphates. The complex arsenate showed a slightly higher reversion after heating; the other arsenates showed poor viscosity-reducing properties. Introduction During the past 10 years the chemical control of drilling mud has become of major importance in affecting the successful drilling and working over of wells. The desired properties of drilling mud have been well established, and in obtaining these characteristics there has developed a large market for viscosity-reducing chemicals. Viscosity reduction produced by humic acid, tannic acid, sodium silicate, sodium tannate, Calgon, and the complex phosphates has been described by Loomis, Ford, and Fidiam.l The effects Of treatment with complex phosphates and ammonium PolyPhosPhates on the rheological properties of muds were investigated by Fancher2 and the alkali vanadates have been described by Williams.3 Laboratory Investigations It is the purpose of this paper to point out the effects of arsenates in controlling the viscosity and gelling characteristics of a drilling mud. Viscosities and gel strengths were measured at room temperatures with a Stormer viscosimeter calibrated in centipoises and operated at 600 r.p.m. Water loss was determined at 80°F. with the Baroid low-pressure wall-building tester at a pressure of I00 lb. per sq. in. for 30 min. The hydrogen-ion concentration was measured with a glass electrode. The bentonite-clay suspensions were prepared in the laboratory and allowed to age several days before testing. Members of the Arsenic Group in the periodic Table include arsenic, antimony and bismuth, but this investigation was limited to arsenic. Phosphorus also occurs in Group V of the Periodic system and phosphorus and arsenic form many closely related compounds such as pH3 and AsH3, P2O5 and As2O5, H3PO4 and H3AS04 Samples of tetrasodium pyroarsenate were prepared by fusing c.p. disodium arsenate (Na2HA5O4.7H2O). According to Friend,' this re-forms the ortho-arsenate on dissolution in water. Sodium trihydrodiorthoarsenate was prepared as described by Mellor,5 from arsenic pen-toxide as follows: As2O5 + 3H20 -> 2H3AsO4 2H3AS04 + 3NaOH Na3H3(AsO4)2 .3H20 Sodium dihydrogen orthoarsenateWaHz-As04) was obtained by fusing together equivalent quantities of arsenious Oxide and sodium nitrate, dissolving the residue in water and allowing it to crystallize.

Jan 1, 1946

By Ralph Hultgren, David W. Mitchell

MAGNESIUM alloys usually are superheated before casting in order to ensure fineness of grain. Superheat temperatures in common use range from 1600° to 1700°F while the casting temperature, which depends upon the mold shape, is usually 200° to 300°F lower. The process of superheating requires considerable time and seriously shortens the life of the iron pots used. Recently it has been reported' that if acetylene, carbon dioxide or natural gas is bubbled through molten electrolytic A.S.T.M. No. 4 alloy at 1400°F. for 5 min., grain refinement equivalent to that of superheating will take place. Addition of certain solids such as graphite or aluminum carbide accomplishes the same results.2 As will be shown in this paper, it is possible to achieve grain refinement in magnesium casting alloys at low temperatures by mechanical stirring of the molten metal for a short time. This process was developed in the course of research work, supervised by the War Metallurgy Committee under the "Restricted" Project NRC-550, for the Office of Production Research and Development of the War Production Board. This paper, based on that work, has been released for publication by the O.P.R.D. MATERIALS AND METHODS The alloys studied were the most common American sand-casting alloys designated as No. 4 and No. 17 by the American Society for Testing Materials. The magnesium used in these alloys was of both carbothermic3 and electrolytic4 origin. Chemical analyses supplied by the producers are shown in Table I. Each heat consisted of approximately 5 lb. of alloy melted in a Tercod crucible. It was refined by fluxing with Permanente No. 7* refining flux at 1300° to 1350°F. After cooling to 1200' to 1250°F., portions of approximately one pound each were ladled into iron crucibles contained in an electric furnace at about 1250°F. The molten metal was covered with Permanente No. 21† covering flux and then heated to the temperature to be investigated. Normally each of the four portions was given a different treatment. In a typical case one portion was stirred vigorously for 5 min., acetylene gas was passed through a second portion for 5 min., a third portion was superheated to 1600°F for 15 min., then cooled to casting temperature, and the fourth was held for 5 min. at the temperature of stirring or gassing without other treatment. Each portion was then cast into one-inch diameter cylinders in three "nonturbulent" molds of identical shape. One mold was made of cast iron and the other two of baked sand. The cast-iron mold and one of the baked sand molds were heated to 360°F., the other baked sand mold was at room temperature. The freezing times in these molds were

Jan 1, 1945

By Ralph Hultgren, David W. Mitchell

Magnesium alloys usually are superheated before casting in order to ensure fineness of grain. Superheat temperatures in common use range from 1600" to r 7o0°F.; the casting temperature, which depends upon the mold shape, is usually 200° to 300°F. lower. The process of superhcating requires considerable time and seriously shortens the life of the iron pots used. Recently it has been reported1 that if acetylene, carbon dioxide or natural gas is bubbled through molten electrolytic A.S.T.M. No. 4 alloy at 1400°F. for 5 min., grain refinement equivalent to that of superheating will take place. Addition of certain solids such as graphite or aluminum carbide accomplishes the same results? As will be shown in this paper, it is possible to achieve grain refinement in magnesium casting alloys at low temperatures by mechanical stirring of the molten metal for a short time. This process was developed in the course of research work, supervised by the War Metallurgy Committee under the "Restricted' project NRC-550, for the Office of Production Research and Development of the War Production Board. This paper, based on that work, has been released for publication by the O.P.R.D. Materials and Methods The alloys studied were the most common American sand-casting alloys designated as No. 4 and No. 17 by the American Society for Testing Materials. The magnesiun used in these alloys was of both carbothermic3 and electrolytic' origin. Chemical analyses supplied by the producers are shown in Table I. Each heat consisted of approximately 5 lb. of alloy melted in a Tercod crucible. It was refined by fluxing with Permanente No. 7* refining flux at 1300° to 1350°F. After cooling to 1200° to 1250°F., portions of approximately one pound each, were ladled into iron crucibles contained in an electric furnace at about 1250°F. The molten metal was covered with Permanente No. 21 † covering flux and then heated to the temperature to be investigated. Normally each of the four portions was given a different treatment. In a typical case one portion was stirred vigorously for 5 min., acetylene gas was passed through a second portion for 5 min., a third portion was superheated to 1600°F. for 15 min., then . cooled to casting temperature, and the fourth was held for 5 min. at the temperature of stirring or gassing without other treatment. Each portion was then cast into one-inch diameter cylinders in three "nonturbulent" molds of identical shape. One mold was made of cast iron and the other two of baked sand. The cast-iron mold and one of the baked sand molds were heated to 360°F., the other baked sand mold was at room temperature. The freezing times in these molds were

Jan 1, 1945

By A. G. H. Anderson, A. W. Kingsbury

Silicon bronzes containing ken are used to a considerable extent in industry, under the trade name of P.M.G. alloys. Various classes of wrought alloys fall in the composition range 1.5 to 3.5 per cent silicon, and 0.5 to 2.5 per cent iron. Castings may contain as much as 6 per cent silicon and 3 per cent iron at present. The constitutional diagrams of these alloys are thus of considerable practical importance. Copper-silicon-binary alloys have been thoroughly investigated by a number of workers, the latest reports being those of C. S. Smith1 and of A. G. H. Andersen.2 Although much work has been done on iron-copper alloys,3 recorded investigations on the copper-rich copper-iron binary constitutional diagram are not numerous. Tammann and Oelsen4 etermined the solubility limits of iron in copper by means of magnetic measurements, and found that the solubility of iron in copper amounts to a fraction of one per cent at 400°C., increasing slowly to one per cent at 800°C. From 800°C., the solubility increases rapidly and attains 4 per cent at iioo°C. Hanson and Ford,5 using electrical resistivity measurements and the microscope, determined a somewhat different solubility limit. of earlier X-ray works on the copper-iron system, very little has been published. The work by Bradley and Goldschmidt6 on copper-iron-aluminum alloys includes some information on the copper-iron binary. These investigators conclude that substitution of iron in the copper lattice decreases the spacings, which is contrary to the evidence of the present work. Hanson and West? have investigated the ternary alloys of copper with iron and silicon. Although their diagrams are valuable contributions to the understanding of these alloys, they did not recognize the kappa phase,l,2,7,8 and their diagrams do not everywhere conform to the phase rule. The present work contains a check by means of X-rays of the solid solubility limit of iron in copper, and an X-ray investigation of the ternary-phase diagram, which, owing to present conditions, it became necessary to curtail considerably. Preparation of Samples Castings weighing about 75 grams were melted under vacuum. The charges were made up of ingot iron, copper cathodes from Laurel Hill, and refined silicon supplied by the Electrometallurgical Co. Alundum crucibles were generally used. The exceptions were alloys 77 and 78, which were melted in graphite crucibles. The ingots were annealed at 800°C. for one week, then samples were cut for chemical analysis. Longitudinal sections of the binary alloy ingots were hammered into plates 1/8 in. thick. Wherever possible, these plates were homogenized at temperatures ensuring

Jan 1, 1943

By A. W. Fahrenwald

CELL depth has been for many years a controversial question in a flotation-machine performance. In the impeller type of machine, we are really talking about impeller submergence-i.e., the depth in the pulp at which the impeller is required to produce aeration. THE FLOTATION MACHINE A COMPRESSOR A flotation machine can be considered as an air compressor or blower in which the aeration mechanism takes in air under atmospheric pressure[t] (14.7 lb. per sq. in.) and blows it into the pulp (the pulp being the receiver) against a head of 14.7 plus cell depth in feet times 0.4333 lb. per sq. inch. In commercial machines the impeller is submerged in the pulp to depths ranging from about 2 ft. in the smaller machines to as much as 5 ft. in some of the larger ones. In the 2-ft. cell, the hydrostatic head on the impeller is (2 X 1.25 =) 2.50 ft. (assuming a pulp density of 1.25), equal to (2.50 X 0.4333 =) 1.078 lb. per sq. in. For the 5-ft. cell, the hydrostatic head against which the impeller must make air is (5 X 1.25 X 0.4333 =) 2.708 lb. per sq. inch. In the small 2-ft. machine, the volume reduction is (1.078 [-] 0.147 + 0.01078 =) 6.85 per cent and in the large, 5-ft. machine, the volume reduction is (2.708 [=] 0.147 + 0.02708 =) 15.5 per cent. It is obvious that for unit volume of free air intake the larger machine receives a lesser (8.65 per cent less) volume of aeration* than the smaller machine. The bubbles in escaping from the pulp expand and are greater in volume at the surface than at the moment of their formation in the pulp; 7.33 and 18.4 per cent larger, respectively, in the small and large machines. Just how this situation affects flotation is not known. It is interesting to note, however, that the bubbles are smaller in the zone of the coarsest particles and largest in the upper zones of the finer, more easily suspended mineral particles. It would seem that the relationship might be reversed advantageously. The deep cell is at a greater disadvantage in this respect than the shallow cell. Nothing, however, presumably can be done about this situation. The shallow cell is a partial corrective. Not only does the compression ratio of aeration increase with impeller submergence but the hydrostatic head against which the impeller must operate also increases. THE FLOTATION MACHINE AS A PUMP Since, in impeller machines that rely upon their own operation to produce aeration, pulp passes through the im-

Jan 1, 1946

By A. G. H. Anderson, A. W. Kingsbury

Silicon bronzes containing ken are used to a considerable extent in industry, under the trade name of P.M.G. alloys. Various classes of wrought alloys fall in the composition range 1.5 to 3.5 per cent silicon, and 0.5 to 2.5 per cent iron. Castings may contain as much as 6 per cent silicon and 3 per cent iron at present. The constitutional diagrams of these alloys are thus of considerable practical importance. Copper-silicon-binary alloys have been thoroughly investigated by a number of workers, the latest reports being those of C. S. Smith1 and of A. G. H. Andersen.2 Although much work has been done on iron-copper alloys,3 recorded investigations on the copper-rich copper-iron binary constitutional diagram are not numerous. Tammann and Oelsen4 etermined the solubility limits of iron in copper by means of magnetic measurements, and found that the solubility of iron in copper amounts to a fraction of one per cent at 400°C., increasing slowly to one per cent at 800°C. From 800°C., the solubility increases rapidly and attains 4 per cent at iioo°C. Hanson and Ford,5 using electrical resistivity measurements and the microscope, determined a somewhat different solubility limit. of earlier X-ray works on the copper-iron system, very little has been published. The work by Bradley and Goldschmidt6 on copper-iron-aluminum alloys includes some information on the copper-iron binary. These investigators conclude that substitution of iron in the copper lattice decreases the spacings, which is contrary to the evidence of the present work. Hanson and West? have investigated the ternary alloys of copper with iron and silicon. Although their diagrams are valuable contributions to the understanding of these alloys, they did not recognize the kappa phase,l,2,7,8 and their diagrams do not everywhere conform to the phase rule. The present work contains a check by means of X-rays of the solid solubility limit of iron in copper, and an X-ray investigation of the ternary-phase diagram, which, owing to present conditions, it became necessary to curtail considerably. Preparation of Samples Castings weighing about 75 grams were melted under vacuum. The charges were made up of ingot iron, copper cathodes from Laurel Hill, and refined silicon supplied by the Electrometallurgical Co. Alundum crucibles were generally used. The exceptions were alloys 77 and 78, which were melted in graphite crucibles. The ingots were annealed at 800°C. for one week, then samples were cut for chemical analysis. Longitudinal sections of the binary alloy ingots were hammered into plates 1/8 in. thick. Wherever possible, these plates were homogenized at temperatures ensuring

Jan 1, 1943

By R. F. Hehemann, S. T. Zegler

The w phase in zirconium alloys containing more than G pct Nb can form in a difjUsionless manner during quenching or with composition change during aging at temperatures below 550°C. The latter treatment establishes a metastable equilibrium between an w phase containing 5 pct Nb and a ß phase containing 45 pct Nb. The superconducting transition temperat~ire of quenched Z?-10 pct Nb and Zr-15 pct Nb alloys is increased by aging at 375°C and both alloys exhibit the same Tc after prolonged aging. The superconducting transition both in the quenched and in the aged alloys is relatively sharp (occurring ovev a temperature range of <0.5°K), and is interpreted in terms of the microstructure that characterizes the ß-w) mixture and proximity effects postulated for thin-film superconductors. At elevated temperatures alloys of the transition elements from groups 4 to 6 in the periodic table exhibit wide ranges of mutual solubility in the bcc structure. Except for compositions that are high in a group 4 element? the bcc structure can be retained at room temperature by quenching and several systematic studies of the influence of composition on superconductivity in bcc alloys have been reported.&apos;&apos;2 The high-temperature bcc form (ß) of the group 4 elements—titanium, zirconium, hafnium—is not retained upon quenching but instead transforms marten-sitically to the hcp structure (a). The Ms temperature can be lowered by alloying the group 4 metals with a solute from a higher group and with a critical amount of solute the martensitic transformation can be suppressed. The 3 phase, however, is not retained without modification. Rather, a metastable phase, w (in particular in titanium- and zirconium-base alloys), occurs over a fairly wide range of compositions above that required for suppression of the martensitic transformation.3,4 As in the formation of a, the transformation of ß to w occurs in a diffusionless manner during quenching and the temperature for its initiation (ws) is lowered by increasing solute content. The ws temperature can be well below room temperature and reversibility of the transformation allows w that forms on cooling to low temperatures to disappear again when the sample is returned to room temperature.5 In Zr-Nb alloys the w phase can also be formed during aging at temperatures below 550°c.5 In this treatment, a metastable equilibrium is established between a niobium-rich ß phase and a zirconium-rich w phase. The present study of Zr-Nb alloys was undertaken to examine the influence of microstructure: as controlled by composition and heat treatment, on the superconducting transition temperature, Tc. MATERIALS AND PROCEDURE The alloys were prepared from zirconium crystal bar that was spectrochemically pure except for 30 ppm of Al, 40 ppm of Cu, 100 ppm of Fe, and 1 ppm of each B and Pb. The niobium used was 99.5+ pct pure containing according to the suppliers&apos; (Stauffer Chemical Co.) analysis a maximum of 50 ppmO, 60 ppm of N, 30 ppm of C, 5 ppm of H, 200 ppm of Ta, 50 ppm of Mo, and 15 ppm each of Fe, Co, and Ni. The alloys were prepared in the form of buttons weighing approximately 4 g by arc melting on a water-cooled copper hearth in an inert-gas atmosphere. All alloys were heat-treated in the ß-phase region for 3 days at 1000°C and water-quenched. For heat treatment, the specimens, 0.5 cm in diam by 1.0 cm long, were wrapped in zirconium foil and sealed in an inert-gas atmosphere inside quartz capsules. Quenching was done by breaking the capsules under water. Subsequent aging treatments of Zr-10 pct Nb and Zr-15 pct Nb alloys were done by placing the specimens in a lead bath at 375°C and quenching in chilled brine. The phases present in the quenched and aged alloys were identified by optical and X-ray metallography. X-ray powder patterns were taken at room temperature with a 114.6-mm-diam Debye-Scherrer camera and CuK-a radiation. Superconducting transition temperatures were determined from magnetic-permeability measurements6 in a 10 oe field. The superconducting transition temperature was determined from a plot of galvanometric deflection as a function of temperature by extrapolation of the linear portion of the curve to zero deflection. In Figs. 1 and 3 the arrows indicate the temperature range of the transitions. RESULTS AND DISCUSSION Superconductivity in Quenched Alloys. In Fig. 1 Tc for alloys quenched from 1000°C is plotted against nominal composition. Indicated also in Fig. 1 are results of metallographic studies. Alloys containing less than 5 pct Nb transform martensitically to a during quenching from 1000°C and Fig. 1 demonstrates that Tc increases significantly as the niobium concentration in a is increased. On the basis of the Bardeen-Cooper-Schreiffer theory of superconductivity7 it seems most likely that this increase in Tc results from an increase in the density of electronic states as zirconium is alloyed with niobium. This increased density of states has been revealed clearly in low-temperature specific-heat measurements.8 The martensitic transformation to a is suppressed when the alloy content exceeds 5 pct Nb. In the range from approximately 6 to 30 pct Nb, quenched alloys consist of a mixture of B and w phases and the amount

Jan 1, 1967

By Paul M. Tyler

HISTORICAL concepts of the economics of the glass-sand industry are changing rapidly. The greatly expanded demand for glass containers combined with higher freight rates on raw materials and manufactured products have induced a migration of glass factories toward densely populated centers and the creation of new standards of place value for sub- standard sand deposits. This migration has been facilitated by the construction of pipelines to bring cheaper natural gas and liquid fuel to large cities and may be further speeded by the adoption of modern mineral dressing methods to permit economical utilization of local raw materials. Our national resources of naturally high-grade 1 silica sand are abundant, but most of the best de- posits are situated so far from large centers of population that it now costs $3.00 to $5.00 a ton to carry the sand from the mine to the optimum site for a 1 factory making beverage bottles, scientific and electrical glassware, and miscellaneous blown and pressed ware for local markets. It follows that on the basis of freight savings alone it may be economical to use material from inferior deposits closer to the factory even though the f.o.b. cost of mining and treatment may be much high

Jan 1, 1950

By AIME AIME

FOR the use of workmen and employees, the company should establish a dispensary and a -hospital where workmen who suffer accidents or professional diseases may be taken care of; and at suitable places in the mine or metallurgical plant it should install first-aid stations. Workmen have a right to receive 75 per cent of their wages while they are unable to perform their work as result of a professional disease; but some companies pay full wages and in the case of natural disease, with the exception of venereal, alcoholism, injuries from fights, and chronic illnesses, 50 per cent of their wages up to a period of two months. The number of diseases the Law considers as professional is large and increases almost daily. Among the professional diseases, the one which has caused greatest harm to the miners and expense to the companies is silicosis. To avoid its propagation, companies should take every possible precaution that the working atmosphere is free from dust, abating this by frequent sprinkling of the workings using, wet drills and furnishing the workmen adequate protective apparatus such as respirators.

Jan 1, 1937

By Olin M. Hart

Uranium ores occur in the Lower Cretaceous Inyan Kara group of heterogeneously stratified fluvial and fluvial-marine sandstones in the Black Hills of western South Dakota and northeastern Wyoming. There are three principal mining districts, each in the ancestral and present drainage area of a major river partially responsible for stripping the region to its present topographic form. Primary minerals in the deposits are coffinite and uraninite with minor amounts of paramontroseite and haggite. The ore minerals coat sand grains and fill interstices of complexly cross-stratified sandstone along solution fronts similar to "roll" type deposits of the other districts. Minerals of oxidized deposits are typically carnotite and tyuyamunite with different proportions of secondary vanadium accessory minerals. Ground water was the transporting medium and deposition of primary uranium and vanadium minerals occurred in reducing environments produced and controlled by physio-chemical characteristics of the sedimentary rocks.

Jan 1, 1968

By Charles C. Goddard

Since discovery of silver-gold lode deposits in 1864, the Butte district has produced more than $2.25 billion worth of copper, zinc, manganese, silver, and gold, an unprecedented value in the mining world. Exhaustion of the gold placer deposits along Silver Bow Creek, southwest of Butte, forced the early-day placer miners to turn their attention to the bold out- crops of the many veins exposed on the hillsides above the placer diggings. These outcrops bore silver and gold, and enough so that many lode claims were located. Such famous silver mines as the Alice, Moulton, Magna Carta, Nettie, and Blue Bird were developed. These and many smaller operations contributed to making Montana the leading silver-producing state in the 1880&apos;s. As depth was gained in the silver mines in certain parts of the district, occurrence of zinc minerals became troublesome. Zinc was not recoverable at the time, and in the chloridizing, roasting, and amalgamation of the ores, silver and gold recovery was greatly reduced. A period of active silver mining continued until 1892, when a decline in the price of silver brought the silver mining period to a close. Elsewhere in the district it was discovered that while some of the veins contained silver ores in the oxidized portions, the predominant minerals that were deeper were copper-bearing. Marcus Daly exposed rich copper ore on the 300 level of the Anaconda mine in 1891, and mining in the district disclosed that copper was destined to be developed in abundance. Early copper ore shipments were made to Swansea, Wales.

Jan 3, 1959

Jan 1, 1943

Jan 1, 1900

Jan 1, 1928

Jan 1, 1916

Jan 1, 1894

By Carl F. Floe, Michael B. Bever

ACCELERATED by the demands of war, research and development work in nonferrous physical metallurgy has continued at a rapid pace during the past year. In particular, advances have been made in processing and fabrication, especially of the light alloys, and in the surface treatment of metals. Theoretical physical metallurgy, although less active, has not been neglected and the year has brought forth some -notable contributions to our understanding of the fundamental structure of metals and their behavior in service. Of course, much work that has been done cannot be publicly discussed because of wartime restrictions.

Jan 1, 1945

Jan 1, 1949