Search Documents

By W. L. Finlay

Size effects in quenching steel are particularly prominent and well recognized because of the existence of a critical cooling rate separating nuclea-tion and growth transformations, as exemplified by the formation of pearl-ite, from the shear type of transformation characterizing the martensite reaction. The absence of a similar, sharply demarcating cooling rate is characteristic of precipitation hardening systems and size effects in these are correspondingly less prominent. This paper is concerned with a size effect in high-purity, precipitation-hardenable alloys which appears not to have been recognized previously. This effect is believed to result from the thermal fluctuations which inevitably occur in quenching a specimen of finite size into a cooling liquid rather than from the existence of a critical cooling rate. QUENCHING "ANOMALIES" The precipitation hardening literature contains many references to so-called anomalous quenching and aging results. By "anomalous", investigators usually meant that their alloys did not consistently harden on aging after quenching according to some anticipated pnttern: not infrequently virtually no age hardening occurred with compositions known to be precipitation-hardenable. Perhaps the most prominent series of anomalies was reported over a 15-year period by Gayler and coworkers on aluminum-copper.l,2,3,4 Working with silver-rich copper alloy, Cohen5 secured some very interesting Rockwell F hardness changes of from 1-5 Rockwell points between the first peak and valley. Fink and Smith borrowed one of Cohen's specimens and, following his heat treatment and quenching practice to the letter, secured6 very different results in which only one peak was obtained and in which the hardness level at the aging lime of Cohen's first peak was 20 Rockwell F points higher. Fink and Van Horn7 encountered serious deviations in age-hardening high purity aluminum-zinc alloys. They stated that "the discrepancies were larger than might be expected from possible experimental errors in the Brinell readings." Geisler, Barrett and Mehl8 likewise encountered anomalous hardening results in aluminum-silver alloys, securing quite different age-hardening curves from two identical specimens. They stated that "the treatments of these samples had been the same, so that the different behaviors could be attributed only to accidental variations in the quenching practice."

Jan 1, 1950

By R. R. Joseph, K. A. Gschneidner

The solid solubility of magnesium in the close-packed modifications of lanthanum, cerium, praseodymium, neodymium, gadolinium, dysprosium, and lutetium was determined from approximately 250°C to the eutectoid temperature by the X-ray parametric technique. The maximum solubility at the eutectoid temperature was found to be 9.4 at. pet in La, 8.2 in Ce, 9.2 in Pr, 8.2 in Nd, 14.1 in Gd, 13.5 in Dy, and 11.5 in Lu. The solubility when compared at a homologous temperature was found to increase in a smooth manner with decreasing size factor from lanthanum to lutetium. It was found that the apparent atomic radius of magnesium when dissolved in the lanthanide solvent was constant and could be accounted for by consideration of several models dealing with departures from Vegard's law. The eutectoid temperatures for the lanthanide-rich La-Mg, Ce-Mg, and Nd-Mg systems were found to be 544", 505°, and 551°c, respectively. A study of the solid solubility of magnesium in the lanthanide metals was initiated because the valency and electron egativity difference are essentially constant and favorable for solid-solution formation, and thus one could examine the effect of size on terminal solid solutions. The size factors based on metal radii range from 14.6 pet for lanthanum to 7.5 pet for lutetium. Since the electronegativity difference is small, 0.06 unit or less, application of the Hume-~othery' and Darken and Gurry2 criteria for solid-solution formation indicates that the solubility of magnesium would be expected to be small for lanthanum (between 5 and 10 at. pet) and to increase as we proceed along the lanthanide series. A search of the literature revealed no data on the solubility of magnesium in the lanthanide metals except for the solubility of magnesium in cerium at 450oCA typical phase diagram for the lanthanide-rich end of the lanthanide-magnesium phase diagram is shown in Fig. 1. EXPERIMENTAL PROCEDURES Preparation of Alloys. The lanthanide metals used in the preparation of alloys for this investigation were prepared from the corresponding fluoride by metallothermic reduction techniques previously described by Daane.4 The chemical analyses of the metals used are listed in Table I.

Jan 1, 1965

By L. F. Pease, J. H. Brophy

A phase diagram for the Ta-Zr system is presented. The system is of the minimum-melting point type with the 0-zirconium phase decomposing monotectoidally at 785°C and 95.5 at. pct Zr. The minimum solidus temperature is 1875°C and the temperature of the top of the monotectoid loop is 1775°C. Techniques employed included X-ray diffraction and fluorescmce, electron microprobe analyses, diffusion couples, metallography, and melting-point measurements. Errors due to interstitial solutes and in melting observations are particularly common in this system, and their occurrence is discussed. SEVERAL versions of the Ta-Zr phase diagram have been reported in the literature.lm7 Williams et al.' report a diagram of the minimum-melting point type with a monotectoid reaction at 800°C and 12 wt pct Ta. The minimum in the solidus occurs at 1820°C and 25 wt pct Ta, while the top of the monotectoid gap is located at 1780°C and 80 wt pct Ta. The experimental techniques employed were metallography, electrical resistance variation with temperature, dilatometry, X-ray diffraction, and direct observation of melting by the technique of Pirani and ~lterthum.' Experience in the Nb-Zr phase diagram has shown that small changes in the interstitial content can cause large shifts in the positions of the phase boundaries. Small amounts of inter -stitials can cause similar changes in the Ta-Zr system and may be responsible for the wide variations in the phase diagrams previously reported.'-' The authors15 have found that alloys containing 0.75 wt pct 0 and 1.0 wt pct Ni with tantalum contents from 19 to 85 at. pct often contain a lamellar or cellular precipitate after annealing above 1400°C. This precipitate is very similar to that reported by pollack,12 Ralls," and Donlevy17 for the Ni-Zr system. In the present investigation, a wider variety of experimental techniques and improved alloy purity were applied to the resolution of errors in diagrams for this system as they now appear in the literature. New results have been obtained in the areas of alloy homogeneity and purity. Errors in the common techniques of direct melting observation in binary alloys have been demonstrated. In the commercially important high-tantalum region, the more accurate metallographic method of solidus determination has been employed. EXPERIMENTAL PROCEDURE Nominal analyses of the materials employed are given in Table I. The zirconium was low hafnium reactor grade iodide crystal bar, and the tantalum was in the form of high-purity sheet. Powders were impossible to use because of gas content. Alloys were melted on a water-cooled copper hearth, with a thoriated tungsten-tipped nonconsumable electrode in 2/3 atm of Zr "gettered" argon. Alloys were

Jan 1, 1963

By J. T. Norton, N. J. Grant, I. S., Servi

Coarse grained high purity aluminum was tested in creep at temperatures of 400° to 1200°F to develop subgrain structures. Measurements of subgrain size, distribution, and rotation were made from X-ray diffraction patterns. Subgrain size and distribution were checked metallographically and the size was compared with average slip band spacing. The slip family was determined for several specimens. THE interest and research recently evident abroad in the role of subgrain formation and polygon-ization as a contribution to the creep of metals at elevated temperatures is deserving of greater attention in this country. Such metallic subgrains can be defined as macroblocks existing within the grains. The general observation has been that the macro-blocks which belong to the same grain have a maximum difference in orientation of a few degrees. In spite of the considerable amount of work that has been done since Jenkins and Mellorl observed the "division of existing crystals into smaller units when deformation occurs at an annealing temperature," the subject of subgrain formation is only now receiving truly active discussion and investigation. The existence of subgrains has been revealed by metallographic methods, as in the work of Jenkins and Mellor,1 and by X-ray methods, first applied to this problem by Homes.' Hirst3 and Calnan and Burns4 applied the back-reflection Laue technique to the study of coarse grained specimens. Wood et al.5 and Greenough and Smith' examined the ring obtained with a back-reflection camera for the study of fine grained specimens. In addition to the above, the transmission technique was used by Wood.6 A special technique was developed by Guinier and Tennevin8 in order to improve the resolution. Metallographically, the subgrains have been observed directly on the surface of deformed specimens by Wood et al.,3 or have been made evident on repolished surfaces by applying a suitable etching reagent. The latter technique, first suggested by Lacombe and Beaujard,9 was then improved by Wyon and Crussard.10 Subgrains can be formed in single crystals after small amounts of bending followed by heating after this cold work, or during deformation at elevated temperatures. The first phenomenon was analyzed by Cahn11 for the simple case of pure bending followed by annealing. Cahn suggested a mechanism of subgrain formation based on the dislocation theory and called this phenomenon "polygonization." He extended this mechanism to the more complex case of local bending, such as the bending which may occur when a polycrystalline specimen is deformed in tension. Cahn's suggestion was later found quite consistent with the results obtained by Dunn and Daniels." An explanation has been presented recently regarding the formation of subgrains during deformation at elevated temperatures by Chang and Grant.'" In general, there are two schools of thought on the subject. One, according to Wood et al.,5 is that subgrain formation is a mechanism of deformation which is operative under certain conditions in the same way that the slip process is the mechanism of deformation which is operative under other conditions. The boundaries between the subgrains undergo a viscous flow which contributes substantially to the deformation of the material. The second, according to Cahn,13 Wyon and Crussard,10 and Chang and Grant,18 is that subgrain formation is the effect of simultaneous deformation and annealing and is,

Jan 1, 1953

By Laurence Pellier

Electron microscopical studies were made of the effect of sensitization at 1200oF on a Type-.104 stainless steel with high carbon and low nitrogen and oxygen contents, after solution annealing and after cold working. The loci of the carbide precipitates in the early stages of sensitization were followed in dry stripped plastic replicas. Some observations were made by direct electron transmission on thinned films. Intragranular dislocations showed a high degree of stability through the annealing necessary to produce sensitization. I HE present work was undertaken to determine the effect of sensitization, at 1200°F, for 1/2 hr, on the electron microstructure of a Type-304 stainless steel with high carbon, and low nitrogen and oxygen contents, after solution annealing and after cold working. Many electron microscopical studies of sensitization of 18-8 stainless steels have already been made. Most of them utilized extraction replicas, from which the morphology and composition of the precipitated carbides could be established.'-" ry stripped replicas were seldom used for such studies, although it was demonstrated that they are applicable, in general, to EurveYs of the general microstructure of many alloys' and, in particular, to the observation of precipitated carbides in austenitic stainless steels.3

Jan 1, 1963

By H. H. Podgurski, Hsun Hu

Large cryslals of high-purily iron (99.996+ pcl) cannot be obtained by the usual strain-ameal technique. Repealed phase transformation by thermal cycling prior to crilical deformation improves the capabilily of cryslal growith but fails to yield satisfactory crystals. Imperfect columnar crystals can be produced by the phase-transition method. The addition of a small amounl (0.005 wl pet) of nilrogen IT was reported'-4 that for metals of very high purity the usual procedures of the strain-anneal technique fail to produce large crystals. This was eliminates practically all the difficulties in crystal growth by the normal strain-anneal procedures. An actual example is presented, showing that most parts of a strip have been converted into a large crystal by this method. The addition of nitrogen, which can be removed from iron with less difficulty, is believed to be more desirable than carbon additions for the same purpose. thought to be due to the strong tendency for recovery in the high-purity metals: hence the critically strained matrix undergoes polygonization instead of recrystallization upon annealing for crystal growth. Talbot1,2 succeeded in overcoming this difficulty by adding 0.03 to 0.04 pct C to high-purity iron before critical deformation. followed by annealing in hydro-

Jan 1, 1965

By Nicholas J. Grant, H. C. Chang

TRANSCRYSTALLINE fracture surfaces of the cleavage type have been examined by microscopy and X-rays for several metals.' These investigations revealed that the fractured surfaces were not flat and invariably had cleavage and other deformation markings on them. On the other hand, the study of inter crystalline fracture surfaces has been limited. Perryman, in a recently published paper on the inter crystalline fracture of ß-brasses,' found that a thin layer of heavily deformed metal was invariably associated with these surfaces. Furthermore, the thickness of this layer was found to depend on the orientation of the grain boundary surface with respect to the applied stress. The mechanisms of grain boundary sliding and intercrystalline fracture have been presented in two previous papers,which described certain aspects of the deformation of a 20 pct Zn-A1 alloy. It is the purpose of this paper to present some observations on the structure of intercrystalline fracture surfaces and to correlate the structure of such surfaces with the mechanism of intercrystalline fracture. Experimental Techniques—The high purity 20 pct Zn-Al alloy was generously supplied by the Research Laboratories of the Aluminum Co. of America. Two sizes of specimen were used; the first had two parallel flat surfaces of dimensions 1x0.17x0.09 in. and the second was round with a 0.25 in. diam. A grain diameter of 1 to 3 mm was obtained by annealing the specimens at 1000°F for 24 hr. The specimens were then air cooled. The specimens were subjected to creep at 500°F and 2300 psi. The rupture times ranged from % to 3 hr, with one room temperature tensile test. It has been mentioned previous1y" that the intercrystalline fracture surfaces of this alloy, when tested under the conditions given above, are sharply defined. In the optical examination of the fracture surfaces, whenever possible, magnifications of at least X250 were used. The locations of the regions examined, both optically and by X-rays, were selected to give several fracture surface orientations with respect to the stress axis and to the specimen surfaces. This was possible for the X-ray studies since the grain diameters were large compared to the X-ray beam. A film to specimen distance of 3 cm, a 1 mm pinhole and Cr radiation were used for the Laue back reflection pictures.

Jan 1, 1957

By R. G. Aspden

The cold rolling and annealing textures were studied for 3 pct Si-Fe grains initially (001) [hkl]. A concentration of (001) [loo] primaries were observed only in the annealing textures of crystals initially having [loo] within 8 deg of the rolling direction. Eke annealing textures of the (001) [I101 cold rolling textures were sensitive to the initial orientation of the grains. Single crystal data were used to explain the formation of (001) [loo] in poly-crystalline malerial. CUBE texture formation in 3 pet Si-Fe sheet occurs during the final high temperature anneal. Its formation is dependent on the proper distribution of (001) plane primaries with reference to the rolling direction&apos; and on the growth of these primaries by secondary recrystallization. The selective driving force for these primaries with (001) within 7 deg of rolling plane is derived from the difference in surface energy between the annealing atmosphere and the crystallographic planes exposed at the surface of the sheet.&apos;-= The alignment of [loo] directions of (001) secondaries with the rolling direction is required for optimum magnetic characteristics7 and is dependent on processing.&apos; A high degree of alignment has been observed when the final cold rolled texture has a strong (111) [ll2] type component3 and the normal grain growth texture prior to secondary recrystallization has components with a [loo] parallel to the rolling direction and planes from (001) to (110) parallel to the rolling plane.1,3,8,9 Generally, this (001) component is much weaker than the (110) component. The growth rate of (001) plane primaries to secondaries has been found to be independent of the orientation of the primaries with reference to the rolling direction, i.e., the secondaries have the same degree of alignment of [loo] directions with the rolling direction as the (001) primaries.&apos; Hence, the rolling and annealing textures of individual grains or single crystals are of interest in understanding the development of the (001) [loo] secondary recrystallization texture. (001) components have been observed in the annealing textures of cold rolled grains initially having a [loo] parallel to the rolling direction and an (001) rotated up to 30 deg from the rolling plane. Crystals initially near the (001) [loo] orientation when rolled under the influence of constraints imposed by neighboring grains form deformation bands and ro- tate in both directions toward (001) <110>.10,11 Deformation bands have been reported also for crystals initially with an (001) within 1 deg of the rolling plane and a [loo] within 1 deg of the rolling direction when rolled as a free single crystal.12 These crystals have weak recrystallization textures and contain near an (001) [loo] component.10-12 When near (001) [loo] crystals are rolled as free single crystals no deformation bands form and the crystals rotate by a single rotation toward (001) [110]. Recrystallization after a 70 pct cold reduction yielded near an (001) [loo] component13 and after a 90 pct cold reduction an (001) [I201 component." Crystals initially near (210) [001] had a texture after a reduction of 70 and 84 pct which was similar to the (111) [li2] but rotated 10 to 15 deg in the transverse direction. These crystals recrystallize to (210) [OOl] or (410) [001] and contain an (001) [loo] component.10,13 An (001) component has not been detected in the normal grain growth textures of other single crystals. Crystals initially having orientations between (110) [001] and (111) [ll2] have a cold rolled texture of principally (111) [ll2] .10>16 Other crystals with a [I101 parallel to the cross direction rotate to (111) [112] and/or (001) [110] stable end orientations. Crystals initially having from (001) [110] to (111) [lie] retain this orientation after cold rolling.15 The cold rolled textures having [I101 directions parallel to the rolling direction had components in the annealing textures related to the deformation textures by 25 to 30 deg rotations about common (1 10) poles. Cold rolled textures of the (111) (112) type recrys-tallized to (120) [001] or (110) [00l]. The purpose of the present work was to further the understanding of the alignment of [loo] directions of (001) secondaries with the rolling direction. The cold rolling and annealing textures of grains initially (001) [hkl] were studied. These data were applied to the formation of (001) [loo] by secondary recrystallization. PROCEDURES AND EXPERIMENTAL TECHNIQUES The (001) poles near the sheet normal and rolling direction are given in Fig. 1 for the 10 grains studied. Each of these grains was located in the center of a polycrystalline specimen approximately 25 mm wide and 50 mm long. The lower case lettered grains, a through dl were about 1.2 mm in diam and near the (001) [loo] orientation. Specimens containing these grains were from a commercial 3 pct Si-Fe alloy with the principle orientation of (110) [001] as obtained by impurity inhibition of growth with manganese sulfide inclusions.17,18 Upper case lettered grains, A through F, were about 6 mm in diam and had (001) planes near the rolling plane and [hkl] di-

Jan 1, 1963

By C. G. Wilson

DURING the course of some experiments on the plastic deformation of gallium a standard stereo-graphic projection was prepared with (001) at the center and it was felt that this might be useful to others working with single crystals of gallium. The stereogram, given in Fig. 1, was made using the following crystallographic data (Bradley, 1935):

Jan 1, 1962

By G. W. Brock

Experiments in the form of aging of overstrained tension specimens and elevated temperature tension testing, have been carried out on recrystallized arc-cast molybdenum. The aging behavior of molybdenum was found to be strongly dependent on the degree of plastic strain present in the lattice: the reason for this being the low solid solubility for the common interstitial elements in molybdenum. GEORGE W. BROCK, formerly Research Associate, Department of Theoretical and Applied Mechanics, University of Illinois, Urbana, III., is Research Associate, Department of Engineering Sciences, IBM Research Center, Yorktown Heights, N. Y. Manuscript submitted January 19, 1961. IMD THE term strain aging is familiar in connection with the recovery of the yield point in mild steel after tensile overstraining, and there are other instances where it is known to exert an appreciable effect on mechanical properties. For example, steel exhibits a greater tensile strength at mildly elevated temperatures than at room temperature and serrated stress-strain flow curves occur under certain conditions. It has been known for a number of years that the phenomenon of strain aging is directly connected with the presence of carbon and nitrogen in the lattice; and extremely small amounts of either element are sufficient to produce the effect. In this study, the aging behavior of overstrained tensile specimens of recrystallized molybdenum has

Jan 1, 1962

By T. Price, H. A. Holl, A. P. Greenough, A

UdIN, Shaler, and ulff&apos; first used wires for the determination of the surface energy of a solid metal. A gage length was marked by tying knots in the wires, which were then suspended in a cylinder of the same metal, heated in an inert atmosphere for the appropriate time, cooled to room temperature, and finally removed from the furnace so that the lengths of the wires could be measured. With iron wires, difficulties associated with deformation during the phase changeszp3 made it necessary to measure the gage lengths at the tem-

Jan 1, 1964

By G. K. Manning, E. R. Stein, E. E. Underwood

Columbium, carbon. and nickel additions were made to iron-base alloys with 20 pct CY. The effects on microstructure, precipitation-hardening characteristics, and High-temperature properties were investigated by means of metallographic, hot-hardness, and magnetic measurements. An austenitic alloy consistilzg of Fe-20Cr-14Ni-0.8C-2.5Cb had higher hot-lzaciness at 1700°F than the other alloys investigated. Its favorable standing is attributed to an enhanced interaction of Cb and Cr4C particles dispersed within a stable austenitic matrix. FOR the past 20 years, cobalt- and nickel-base alloys have been used for the more stringent high-temperature applications because of their excellent creep resistance. Although their performance is quite satisfactory, other base materials must be considered for large tonnage, low-cost applications such as for the automotive gas turbine. Iron-base alloys are also used extensively, but at somewhat lower temperatures, primarily because of the instability of particles or because precipitation occurs at relatively low temperatures. Since unusual stability has been reported for Fe-Cb and Cb-C compounds.1-3 it was hoped that effective amounts of these compounds could be taken into solution at temperatures just below the melting range, then precipitated upon reheating. Actually, strengthening was found to occur by both precipitation hardening in some alloys and by phase transformations in others. Among the alloys investigated, that with the best high-temperature properties owes its strengthening to a combination of carbide particle interaction and a relatively stable austenitic matrix. EXPERIMENTAL PROCEDURES Small preliminary melts of about 100 g were made in a vertical Glotube furnace, using alundum crucibles and an argon atmosphere. Alloys weighing 35 lb were melted in a basic-lined induction furnace, also under argon. The compositions of the alloys are given in Table I. The nickel-free alloys were usually ferritic, while those containing nickel were generally austenitic. Depending upon the particular heat treatments, or the combination of alloying elements, two-phase alloys of ferrite and austenite could be obtained. In the following text, however, the nickel-free or nickel-bearing alloys are referred to simply as either ferritic or austenitic alloys respectively. The small ingots were swaged at 2000°F, in steps, to rods of approximately 3/16-in. diam. The large ingots were forged at 2100°F to 1-in. sq bars. No difficulties were encountered in swaging or forging any of the alloys to as much as 90 pct reduction in area. For heat treating at temperatures above 2000°F, specimens were sealed in quartz tubes under a partial pressure of helium. No special precautions were found to be necessary at lower temperatures. Intermetallic compounds in the preliminary alloys were identified by means of X-ray diffraction measurements. Correlation of these results with micro-structural characteristics (such as color, shape, size, and location) of the compounds aided in their identification. Magnetic susceptibilities were also obtained at room temperature with a Magne Gage instrument after the various heat treatments. To

Jan 1, 1962

By Robert Bakish, William D. Robertson

AFTER more than fifty years of investigation and continuing failure in service, a satisfactory mechanism to explain stress corrosion cracking in homogeneous alloys is still lacking. The relative chemical activity of grain boundaries and adjacent grains, inferred from the boundary structure, has been used to explain intergranular cracking in a brass.&apos; This concept is probably correct as a general hypothesis, but it requires much more extensive development in order to explain satisfactorily the observed phenomena. For example, the specific function of the solute in an alloy must be considered, because intergranular failure does not occur in pure metals,&apos; which are structurally similar to homogeneous alloys. Also, in this connection, an inter crystalline fracture path in binary copper alloys can be changed to a transcrystalline path by relatively small ternary additions.&apos; The fracture path in ß brass is predominantly transcrystalline,&apos; in contrast with an inter crystalline path in a brass. Whether the two different fracture paths are the result of a difference in composition, crystal structure, or the state of long range order is unknown and cannot be determined with ß brass, because only the ordered state can be obtained at room temperature. The study of chemical activity at structural sites in the Cu-Zn system is restricted by the formation of opaque films in an ammonia environment in which stress corrosion cracking is generally observed. Furthermore, both components of the alloy are chemically active and the interpretation of observations is therefore relatively complicated. The Cu-Au system is a better choice for the purpose of studying structural factors. In particular, CuAu is very susceptible to cracking in ferric chloride and opaque films are not formed in this solution; it may be obtained in different states of long and short range order; and, finally, only copper is oxidized in dilute ferric chloride, which considerably simplifies the chemical problem. To provide information necessary for a more general explanation of stress corrosion cracking in homogeneous solid solutions, the following structural factors have been investigated in a Cu-Au alloy having a composition corresponding to Cu,Au: 1) the effect of long and short range order; 2) the structural sites from which copper is removed from the annealed and cold worked polycrystalline alloy; and 3) the effect of annealing time and temperature on structural reactions in the cold worked alloy. Experimental Procedure A Cu-Au alloy of nominal Cu3Au composition was cast from cathode copper and high purity gold and fabricated into sheet and wire. Chemical analysis for copper and gold indicated 48.92 wt pct Cu and 51.01 pct Au. Quantitative spectrographic analysis indicated 0.01 pct Ag, 0.002 pct Pd, 0.001 pct Pb, and 0.002 pct Fe, with traces of magnesium, silicon, and zinc. Presumably most of the remaining 0.055 pct corresponds to the limits of analytical precision. Heat treatments of wire and sheet were conducted in argon or vacuum. Wire specimens, 0.064 in. diam, were heated for 1 hr at 850 °C to establish a definite

Jan 1, 1957

By Kichizo Niwa, Toshio Yokokawa, Mitsuo Shimoji, Yoshihiko Watanabe, Satoshi Kado

A LTHOUGH a systematic research on diffusion in liquid metals has not been carried out, partial studies have been developed by various workers in several systems. A few recent papers among them have shown that this line of approach is quite useful for understanding the structure of the liquid state. Furthermore, it has been found in kinetic

Jan 1, 1958

By David A. Thomas, John F. Peck

Fibrous microstructures and their development have been studied by metallography and by hardness and quantitative metallographic measurements. Thin, curved grains were observed in transverse sections of commercial tungsten wire and were developed in laboratory-drawn iron wire at reductions greater than about 70 pct. The unusual grain shapes are attributed to the nonuniform mode of deformation of the grains associated with the characteristic [I101 preferred orientation that develops in bcc metals during drawing. Transverse sections of heavily swaged iron wire showed a ospiral nebulao structure that appears to result from the elliptical shape of the cross section of the swaging dies and their rotary motion. Hardness and quantitative metallographic results show unusual trends that parallel the changes in microstructure. Other phenomena are considwed in light of the results, including the strength of fine wires of bcc metals, ocylindricalo textures, and the ductility of fibrous tungsten. 1 HE microstructure of tungsten wire in a longitudinal section shows grains highly elongated in the working direction, giving the appearance of a bundle of parallel fibers, Fig. l(a). Wires of tungsten and other bcc metals show a pronounced preferred orientation in which a [I101 direction is parallel to the wire axis.l The microstructure and texture of tungsten develop during warm working (working above room temperature but below the recrystallization temperature) into wire by swaging and drawing. Fibrous tungsten so produced has limited but useful room-temperature ductility, whereas annealed tungsten is brittle at room temperature. During an investigation of the effect of recovery annealing on the substructure of commerical 0.030 in. diam tungsten wire, it was found that transverse sections of the as-received material showed thin, curved grains, Fig. 1(b), instead of the expected equiaxed grains. The fact that Figs. l(a) and (b) show different sections of the same material at the same magnification is at first disconcerting, because the long dimension of the curved grains in the transverse section is several times the average fiber width in the longitudinal section. However, a longitudinal section cuts most of the curved grains across their narrow dimension, giving the appearance of a multitude of narrow fibers. On the other hand, the plane of a longitudinal section occasionally includes a long dimension of a curved grain, resulting in a broad ofibero, such as A in Fig. l(a). EXPERIMENTS AND RESULTS To investigate the origin of fibrous microstructures and particularly the unusual transverse-section structure of tungsten, rods of iron (also bcc) were drawn and swaged in the laboratory. One rod of annealed Ferrovac E was drawn in six steps to a total reduction in area of 87 pct (0.10 to 0.036 in. diam), and a second rod was swaged to the same reduction, using approximately the same reduction steps. Longitudinal and transverse sections of the swaged and drawn iron wires are shown in Fig. 2, for reductions in area of 39, 73, and 87 pct. A fibrous microstructure in longitudinal section is first evident at 73 pct reduction, and it is further developed at 87 pct reduction. The grains in transverse section remain equiaxed until about 73 pct reduction, when they become somewhat elongated and curved. At 87 pct reduction, the drawn wire shows thin, curved grains in the transverse section, similar to those observed in tungsten. The transverse sections of the iron wires swaged 83 and 87 pct reduction in area show the striking ospiral nebulao structure in Fig. 2(d). This struc-

Jan 1, 1962

By M. von Heimendahl, G. Thomas

The microstructure of TD-Ni has been examined by transmission electron microscopy in the extruded, annealed. and deformed states. The tensile properties hove been correlated with the observed microstructures and the results ore com-pared with those obtained from pure nickel. The important conclusions are that the thorin particles in TD-Ni act as strong burriers to dislocntion motion during both deformation (slip) and annealing (climb). During deformation. the dislocations tangle around the particles and a cell structure is devleloped after 10 pct or more strain. The cell size appears to be determined by the spacing of the largest particles and is about five times smaller than that in pure nickel for the same strain. The higher work-hardening rate in TD-Ni compared to nickel is probably due to the more rapid rate of dislocation multiplication in the alloy as a result of dislocation-particle interactions. The Th0,particles inhibit recrystallization and twin growh so that some strengthening may arise from the high density of small annealing twins. THE strengthening of materials due to the presence of a dispersed second phase has been the subject of considerable experimental and theoretical investigation in recent years. One of the newest dispersion-strengthened alloys to be developed is TD-Ni,1 a system of approximately 2 vol pct thoria (ThO2) dispersed in a matrix of commercially pure nickel. This material is fabricated by powder-metallurgical techniques and offers high-temperature stability and useful mechanical properties virtually to the melting point of the base metal. While the mechanical properties of this system have been investigated,2,3 there have been no reports in the literature concerning the microstruc-ture of TD-Ni and its correlation to mechanical properties. This paper describes a transmission electron microscopy investigation of the micro-structure of TD-Ni together with its mechanical properties. The results are compared with the structure and properties of pure nickel.

Jan 1, 1964

By J. J. Pye, J. B. Drew

The surface-diffusion coefficients of Ni63 diffusing on low-index planes of nickel single crystals have been measured over the temperature range from 400° to 1000°C using a precision autoradio-gvaphic technique. The activation energy for sur -face diffusion appears to he the same on the {111}, {110), and (100) planes and amounts to -0.60 ev. This is in good agreement with the value (-0.62 ev) reported for (111) planes obtained by mass-transport techniques. In an earlier paper, the authors have reported self surface-diffusion coefficients on silver.&apos; In that work, a deviation of the diffusion coefficients from linearity in the Arrhenius plot was observed at high temperatures. This effect was attributed to a loss of tracer atoms into the bulk by volume diffusion. The purpose of the present work was to extend the technique developed to the nickel surface-diffusion system up to the point where volume diffusion would come into play. The nickel system especially lends itself to this technique due to the high efficiency of the isotope in darkening the film and the large absorption of the weak radiation (0.063 mev /3- particle of the trapped tracer atoms. The diffusion coefficients and ictivation energy for different orientations on nickel can also be compared with a report published by Blakely and Mykura 2 where a mass-transfer technique was used. This paper reports the self surface diffusion of nickel on the low-index planes over a wide temperature range using a precision autoradiographic technique. EXPERIMENTAL PROCEDURE The experiment is similar to that described in the earlier publication consisting of a radioactive needle as a source resting on a flat, smooth, chemically polished surface annealed in a dynamic dry-hydrogen atmosphere. The needle is held snugly on the surface by a holder fabricated from commercially pure nickel. The point source is made by grinding down a small-diameter nickel rod until a tip of approximately 0.1 mm radius is formed. It is then etched and the needle tip plated with the radioactive isotope Ni63. Nickel single crystals were used whose main impurities were spectrographically determined as Co 0.05, Fe 0.007, C 0.005, and S 0.003 pct. The surfaces, oriented to within 1/2 deg of the low-index planes, were carefully mechanically polished and etched in a 50-30-10-10 hot solution of acetic, nitric, sulfuric, and phosphoric acids giving a smooth polished surface. The crystals were then washed in distilled water and alcohol. Annealing temperatures ranged from 400° to 1000°C with a furnace arrangement in which the crystals could be brought up to temperature in times short compared to diffusing times. The temperature was maintained constant to ±10°C. In the temperature range investigated, the ratio of the surface-diffusion coefficient to the volume-diffusion coefficient (Ds/Du) was 105 or more and the mean bulk-penetration values, calculated from literature values of volume-diffusion coefficients,3 were on the order of 10-5 cm. After the diffusion anneal, the sintered needle is removed, and both the radius of the needle point and spot left on the crystal face are measured. The crystal is then placed on photographic film. Diffusion profiles are obtained by scanning the film with a recording microdensitometer which has a slit width of 10µ. DISCUSSION AND RESULTS The experimental conditions are such that the source strength and needle radius are essentially constant and the time is adjusted such that the mean bulk penetration is small. An exactly analogous heat-flow problem has been considered by Carslaw and Jaeger4 and the solution can be written in integral form as:

Jan 1, 1964

By R. W. Kraft

A back- reflection precession-type X-yay camera for determining the crystallographic orientation of the crystallites of both phases in small areas of thick specimens of polyphase alloys is described ad the geometry, advantages, and limitations of the apparatus are discussed. Metallographic obseg-vations of interfacial angles (or habit planes or growth direction are made on the same specimen so that the crystallographic and metallographzc orientation data call be directly correlated. An example of the application of tile technique to a unidi-~~ectionally solidified CuA12-A1 eutectic specimen is presented. The interfacial planes ad growth directions of each phase were established, and the orientation relationship between the phases was observed and found to be approximately intermediate between two previously reported relationships. The crystallographic interfacial relationship between two solid phases is an important parameter in a variety of metallurgical phenomena because of the energy associated with the interface and because this energy is at least partly associated with the way in which the two space lattices are in contact along the interface. In order to describe the interfacial planes in the crystallites of both phases it is necessary to determine the crystallographic orientation of each phase in a specimen relative to each other, and to directly correlate these data with met-allographic measurements from which the interfacial planes can be determined on the same specimen. The back-reflection Laue technique is the easiest way to determine the orientation of thick single crystals or large grains and the method can be combined with metallographic techniques to provide the necessary data, provided the reflections from each phase can be distinguished from one another. However, if the crystallites are small or of varying orientation or if one or both phases has a unit cell with less than the maximum symmetry, many overlapping and complex Laue patterns are recorded simultaneously and it becomes impractical if not impossible to interpret the photographs. All of these complexities were present in a unidirectionally so- lidified A1-CuA12 eutectic alloy1 for which a crystallographic analysis was desired. Consequently the method described here was developed since no known X-ray or electron diffraction technique had all of the following attributes which were required. 1) Method should yield data from which the crys-tallographic orientation of every crystallite or diffracting unit in the irradiated area can be determined. 2) Method should be adaptable to the study of small areas. Depending upon the degree of preferred orientation in the specimens, it should be possible to obtain reliable data in a reasonable length of time on irradiated areas as small as 1.0 or even 0.1 mm in diam. 3) Method should permit direct correlation of crystallographic data with microscopic orientation data pertaining to crystallite axes, habit, morphology, and growth directions as determined by optical microscopy. 4) method should be such that selected areas of large specimens can be easily studied. Trepanning of a small specimen (such as an electron microscope specimen) from larger specimens was undesirable since it would greatly increase the problem of correlating the crystallographic and microscopic directional data. Requirements 3 and 4 dictated that an X-ray back-reflection pinhole technique should be used on large samples, such as metallographic specimens which had previously been examined and analyzed for their microscopic characteristics. Similarly, requirement 2 could be satisfied by choosing a collimator of appropriately small diameter. Exposure times would not be excessive provided the detector were close enough to the specimen. Because of space limitations film was chosen in preference to a Geiger counter. Requirement 1 was fulfilled by using monochromatic radiation and providing enough additional degrees of freedom in specimen rotation to compensate for Bragg law restrictions on diffracted beams. DESCRIPTION OF APPARATUS The apparatus shown in Fig. 1 consists of a pin-hole collimator, (a), projecting through a rotatable circular film in a holder, (b), which records X-ray reflections in the back-reflection region. The specimen, (c), is mounted on the end of a shaft, (d), which is provided with an adjustment, (e), so that the specimen surface can be placed accurately on

Jan 1, 1962

By J. W. Rutter, K. T. Aust

The temperature dependence of the rate of grain boundary migration was measured in bicrystals of zone-refined lead containing from 20 to less than 1 ppm by wezght of tin. The apparent activation energy in the temperature range from 320" to 200oC is markedly dependent upon the solute tin concentration and upon the orientation relationship of the grains adjacent to the grain boundavy. The quantitative experimental observat~ons are compared with the predictions of various theories of grain boundary migration. In previous work.&apos;?&apos; the mobility of individual grain boundaries was studied as a function of impurity concentration and type of boundary. Grain boundary migration occurred at the expense of dislocation arrays which were introduced into the specimen during solidification. Boundary mobility in zone-refined lead at 300°C was markedly decreased by small additions of tin. 0.004 wt pct being sufficient to decrease the rate of grain boundary migration by a factor of 1000. The mobility of grain boundaries having polar orientation relationships near 38 and 22 deg about <Ill>, and 28 deg about <100>, was much less sensitive to tin concentration in the range studied. As a result, these boundaries have relatively high mobilities. The present paper is a continuation of the above study. Data are now presented on the temperature dependence of the motion of individual grain boundaries in zone-refined lead as a function of solute tin concentration and orientation relationship of adjacent grains at the grain boundary. The experimental observations are compared with the predictions of a number of theories of grain boundary migration3-8 which, prior to the present experimental investigation, could not be critically evaluated. EXPERIMENTAL PROCEDURE The striation or lineage structure of melt-grown single crystals of zone-refined lead, containing various additions of tin, was utilized to provide a driving force for grain boundary migration, as previously described.1,2 Each grain boundary under study separated the striated single crystal from another grain which was introduced by localized plastic deformation and recrystallization of a small region of the sample. The speed of migration of grain boundaries in dilute alloys of tin in zone-refined lead was investigated as a function of 1) tin concentration from < 0.0001 to 0.002 wt pct, 2) temperature in the range of 200" to 320°C, and 3) orientation relationship of the adjacent grains at the grain boundary. The substructure driving energy available for grain boundary migration was estimated to be about 4000 ergs per cu cm, within a factor of two, from specimen to specimen.&apos; The specimen dimensions, and growth and alloying procedures for the preparation of striated single crystals of lead of known tin composition, were as described previously.&apos; Each bicrystal was carefully wrapped in aluminum foil, and annealed in a well-stirred salt bath consisting of 50 pct NaNO2 and 50 pct KNO3, for known periods of time at a series of constant temperatures (*2°C). The grain boundary positions, before and after each anneal, were determined by etching lightly in a solution of 5 pct nitric acid in methyl alcohol, in order to follow the motion of the boundary and determine its rate of migration. Thus, the rate of motion of the grain boundary in a single specimen was measured at various temperatures. The above procedure was carried out for each grain boundary in seventeen different bicrystal specimens.

Jan 1, 1960

By J. H. Westbrook

UNTIL very recently the development of high temperature alloys has been strictly empirical. It is, in fact, a great tribute to the intuition, perseverance, and industry of the practicing metallurgists of this country and abroad that the amazing increases in gas turbine service temperature over the past 15 years have been achieved with so little fundamental knowledge. The result of this development has been the realization of successful but highly complex alloys possessing five, six, or more alloying elements and correspondingly complex microstructures. Within the last few years, considerable effort has been devoted to the identification of the secondary phases in these alloys and to the correlation of the presence or absence of such phases with alloy properties. Little attention, however, has been given the problem of identification of the mechanism (s) by which such phases enhance the properties of the alloy and especially to the assessment of the particular properties of the secondary phase (either in- trinsic or relative to the matrix phase) which are basically responsible for the improvement. Conceivable mechanisms which might apply include dispersion hardening and precipitation hardening. In both cases geometrical factors—particle size, dispersion, volume fraction, etc.—and agglomeration re-

Jan 1, 1958