By K. J. Gill, P. Chiotti

Thermal, metallographic, and vapor pressure data were obtained to establish the phase diagram for the thorium-zinc system. Four compounds corresponding to the stoichiometric formulas Th2Zn, ThZn2, ThZn4, and Th2Zn17 were observed. The melting points of these compounds under constrained vapor conditions were found to be 1055°, 1105°, 1095°, and 1015°C respectively. Four eutectics exist in this system with the following eutectic temperatures and thorium contents in wt pct: 1040°C, 89 Th; 945°C, 79 Th; 1045°C, 55 Th; and 995°C, 35 Th. The standard free energy, enthalpy, and entropy of formation for the compounds were determined from zinc vapor pressure data. ALTHOUGH the thorium-zinc system has been of technical importance in the commercial production of thorium and more recently of interest to some proposed pyrometallurgical separations processes for reactor fuels or blanket materials no detailed investigation of this system has been made in the past. Some previous work has been reviewed by Hanssen.1 The existence of four compounds, Th2Zn17, ThZn4, ThZn2, and Th2Zn has been established and their crystal structures have been studied by X-ray diffraction techniques.2-4 Smirnov et al.,5 determined the solubility of thorium in zinc and investigated the two-phase region between Th2Zn17 and zinc. They calculated some of the thermodynamic properties for these alloys from emf measurements on the cells Th/ThCl4(fused)/Cl2, C and Th2Zn17(s)+ Zn (l)/ThCl4(fused)/Cl2, C. The possibility of reaction between the anode materials and fused thorium tetrachloride to produce a lower valent thorium salt would have to be resolved in order to evaluate the results obtained. The purpose of the present investigation is to establish the phase diagram for the thorium-zinc system and to determine the standard free energy, enthalpy, and entropy of formation for the compounds formed. MATERIALS AND EXPERIMENTAL PROCEDURES The metals employed in the preparation of alloys were Bunker Hill slab zinc, 99.99 pct pure and Ames Lalboratory thorium. The major impurities in the thorium in parts per million were oxygen—1250, carbon—350, iron—100, nitrogen-75, and silicon—70. The metals in the form of several small massive pieces, total weight about 30 g, were cleaned with acid, washed with water and acetone, and dried just prior to their use for alloy preparation. Tantalum containers were found to be suitable for all the alloys studied and were used throughout this investigation. The metals were sealed inside of small 1-in.-diam tantalum crucibles by welding on preformed tantalum covers. A small thermocouple well made from 1/8-in.-diam tantalum tubing was welded in the bottom of each crucible. These crucibles were enclosed in

Jan 1, 1962

By J. Gordon Parr, D. H. Polonis

The formation and subsequent decomposition of metastable phases in Ti-Ni alloys containing up to 11 pet (atomic) Ni have been studied. The decomposition of a completely retained ß phase and of a completely transformed 8 phase in a 6 pet alloy has been followed by X-ray diffraction and metallographic methods and by hardness determinations made during the process. The possible mechanisms of the reactions are discussed. PREVIOUS investigations of the Ti-Ni system have usually been limited to phase diagram studies; but little attention has been given to metastable phases and tempering processes. These are important, however, since equilibrium conditions are rarely achieved—nor, perhaps, are they desired—in practice. Up to the present time the available transformation data for titanium alloys appear to be restricted to isothermal transformation curves for selected binary and ternary systems. No quantitative studies have been made of the mechanism by which equilibrium is approached. Several independent investigations have been carried out to determine the Ti-Ni phase diagram. Early work by Wallbaum' and later by Long et al.' produced tentative phase diagrams which were not representative of true binary conditions, since the alloys were contaminated with oxygen and nitrogen. The most recent diagram (Fig. 1) is due to Margolin et al.," and a slight modification of the a + ß/ß boundary (shown dotted) has been proposed by McQuillan.' The structure of the phase Ti,Ni was shown by Duwez and Taylor" to be face-centered-cubic, with 96 atoms per structure cell. The formation of a martensitic ß phase (close-packed-hexagonal) in Ti-Ni alloys has generally been observed when specimens of low nickel content are rapidly cooled from the 0 (body-centered-cubic) range. Margolin et al. reported an increasing tendency for P to be retained in lump specimens as the nickel content increases. McQuillan' has studied the effect on the microstructure of delay time in quenching, and has reported the formation of pro- eutectoid a precipitate in a quenched hypoeutectoid alloy. In a previous study of Ti-Fe alloys," experiments were made on powder specimens produced by filing alloy ingots. Techniques were devised for the preparation and heat treatment of alloys, and X-ray diffraction methods were used both for structure determinations and phase ratio estimations. A similar approach has been made in this study of Ti-Ni alloys. Experimental Methods Ten alloys ranging from 0.25 pet to 18 pet Ni* * All compositions are in atomic percentages unless otherwise stated. were prepared from iodide titanium bar stock (hardness Rf 72) and Johnson-Matthey spectrographic standard nickel by levitation melting.' As a check

Jan 1, 1957

By R. J. Reynik, F. R. Meeks

IN the classical paper1 of Mehl and Rhines entitled "The Rates of Diffusion in the Alpha Solid Solutions of Copper", the authors state: "It has been mathematically demonstrated that the treatment of the data as though the diffusion were taking place between two flat plates instead of radially in a cylinder has no appreciable effect upon the results. Were the bars of a much smaller diameter, a modification of the analytical treatment would have been required." Unfortunately, the errors in the reported concentrations are much too large to neglect, as shown in the results below. A planar treatment of diffusion data assumes that the reference planes separated by a nominal distance (AX) have identical areas. An adjustment must be made on the concentration data should the successive diffusion planes differ in area. The Mehl-Rhines' diffusion samples were cylindrical with copper electroplated onto copper-based alloys. Successive surface areas through which diffusion occurs are in the ratio ri/r1, where ri is the radial distance between the center of the sample and the center of the i th shell to which the host (alloy) atoms diffuse, and r1 is the radial distance between the center of the sample and the center of the innermost (i = 1) experimentally reported shell from which the alloy atoms diffuse. Hence, ri/r1 (i = 1, ..., n layers) is a dimensionless correction factor to be multiplied by the reported concentration data before planar-data analysis is attempted. In the forty-seven samples reported, the original interface between the copper alloys and the electroplated copper was located at a mean distance of 8.255 mm from the center of the samples. The successive layers, machined off the samples, were approximately 0.0762 mm thick. The distance (xi) at which concentration (ci) was reported was always a distance measured with respect to the original interface, that is, with respect to the fixed distance of 8.255 mm. Hence, the as yet undiscovered Kirkendall Effect was precompensated. The values of ri and r1 are therefore given by ri = 8.255 + xi and Y, = 8.255 + x,. The illustrative table below lists the position xi (mm), ri (mm), the value of ri/r1, the reported concentration (ci) in weight percent (only valid for radial analysis of data), and the corrected concentration [c'i = (ri/r1)ci] in weight percent (only valid for planar analysis of data). Similar tables can be constructed for the remaining forty-six samples. The corrected data can be used to re-evaluate the diffusion coefficients for the reported systems.

Jan 1, 1965

By John J. Gilman

BECAUSE of their layerlike structure, zinc crystals exhibit strong anisotropies for almost all physical and chemical properties. This should, and indeed does, greatly influence the plasticity of zinc for various crystal orientations. At low temperatures, the investigator of this plastic anisotropy is plagued by the great variety of deformation modes that operate. However, at high temperatures (250° to 419°C) only two deformation modes predominate: basal (0001) and prismatic (1010) glide. Furthermore, since strain hardening is virtually absent at high temperatures, the plasticity for these two modes of deformation can be very simply described by means of two equations of state. It is the purpose of this paper to describe the experimental behavior of basal and prismatic glide in zinc crystals, and to interpret this behavior in terms of other physical properties (in particular, the thermal expansion coefficients and the elastic constants) using the theory of dislocations. Fig. 1 defines the two planes of the zinc structure that will be discussed. Glide occurs very readily on the basal planes at all temperatures, and there is a very large literature on this subject. Much of the literature has been reviewed by Schmid and Boas;' it will not be reviewed here. Kolesnikovl was the first to show that if basal glide is circumvented by stressing a zinc crystal parallel to the basal planes (giving zero shear-stress on the basal planes) then, at temperatures above about 320°C, glide on the first-order prism planes occurs. His results have recently been confirmed by Cahn, Bear, and Bell." These previous workers have established the existence and crystallographic elements of prismatic glide; the present paper is concerned with the stress, strain rate, and temperature relations of prismatic glide as contrasted with basal glide. Experimental Methods The crystals were square ones, 6x6 mm, that had been grown in precision Pyrex tubes by a method that is described in detail elsewhere.' Most of the crystals were 99.999+ pct Zn (New Jersey Zinc Co. CP grade). Some were alloyed with 0.1 -+-0.005 atomic pct Cd, and chemical analysis showed that almost all of the added cadmium persisted through the crystal-growing process. For measurements of nonbasal glide, crystals were oriented with their basal planes parallel to both the rod axis and one of the flat faces of the square cross section. However, the orientation of the close-packed directions [1210] with respect to the rod-axis was variable. For basal glide measurements, the angle between the basal plane and the specimen axis was 35". The orientations were measured by the Gren-inger back-reflection X-ray method. The problem of finding a suitable method of gripping the crystals was the most serious experimental obstacle that arose. Because of the large plastic anisotropy of zinc, the usual gripping methods were unsatisfactory. Some methods that were tried were: high melting-point solder, making heads on the ends by locally melting a crystal, and electroplating nickel on the ends to form enlarged portions. For all these methods, the regions of the grips were weaker than the crystals themselves. Finally, two methods were decided upon: bend tests and direct machining of tensile specimens. In the bend tests, specimens were loaded as simple beams so that gripping was not a problem. The beams were 1 in. long and the axis of bending was parallel to the hexagonal axis of the crystals. For the crystals that were machined into tensile specimens, brass bars with slots in them were used to support the crystals, and thereby minimize the distortions due to machining. The crystals were glued into the brass bars with plastic cement which was later dissolved away with acetone. See Fig. 2, left. No clamps were used near the crystals and the machining was done using a milling machine with a fly-cutter. The tool bit was very sharply pointed to minimize burnishing. The feed was less than 1 mil per cut. The depth of cut was 2 mil for roughing cuts, and % mil for the finishing cuts. This machining method produced surface layers of tiny recrys-tallized grains only 2 to 3 mil deep, and the bodies of the crystals were not measurably disturbed. After the crystals had been machined and removed from the brass holders, they were chemically polished until about 5 mil had been removed from all their surfaces. The polishing reagent consisted of equal parts of concentrated HNO,, 30 pct H3O and ethyl alcohol; it is described in detail elsewhere." A typical crystal is shown in Fig. 2, right. The I-shaped faces are normal to the hexagonal axis of the crystal; otherwise the projections at the ends would simply shear off when the crystal was loaded. The cross section in the 2?-in. gage length is 0.215x0.115 in. It was found that the polished

Jan 1, 1957

By E. S. Greiner

Germanium and silicon have been plastically deformed in torsion at elevated temperatures. Slip took place on the four {Ill} planes. Dislocations, revealed by etch pits on a (111) face, occurred in rows that were traces of operative slip planes. THE plastic deformation of germanium and silicon by bending and tension at elevated temperatures has been reported by Gallagher.&apos; Transla-tional slip during plastic flow in these materials, according to Gallagher&apos; and Treuting,&apos; occurs on (111) planes. Recent work by Treuting&apos; indicates the direction of slip to be <1l0>. The present paper describes the plastic flow characteristics of germanium and silicon deformed by torsion. Torsional deformation was accomplished by twisting 1/4x1/4x2 in. specimens held in molybdenum grips and contained in an atmosphere of helium in a transparent quartz tube and heated by an external resistance furnace. The angular displacements were measured on a graduated circle with a pointer attached to the movable grip. Temperatures were measured with a chromel-alumel couple; the hot junction was within the quartz tube and in close proximity to the specimen. Photographs of samples of germanium and silicon twisted at 850" and 1180°C, respectively, are shown in Fig. 1. The germanium was twisted 230" per in. and the silicon 80" per in. These deformations are larger than those used in experiments to be described later and are presented only to emphasize the extensive plasticity of these materials. Germanium A single crystal specimen of germanium (n-type, 7 ohm-cm resistivity) with a (111) plane normal within 3" of the torsion axis, Fig. 2, was chemically polished with CP-4 solution" and then twisted 9" during the twisting of these specimens of germanium, the slip lines from the (lli) plane should have appeared in the four lateral faces instead of in only two. Perhaps the absence of rotational slip is brought about by the square cross-section. A cylindrical specimen would have a more uniform stress distribution in torsion than one with a square cross-section, and may deform by rotational slip. A specimen of germanium (n-type, 5 ohm-cm resistivity) twisted less than 8" per in. at 550°C, was cut to expose the (111) face 19" 28&apos; from the torsion axis, Fig. 4a. This face, after metallographic

Jan 1, 1956

By E. C. Burke, W. R. Hibbard

Plastic deformation in magnesium single crystals was studied by tensile tests at room temperature utilizing an improved preparation and testing technique. Consistent critical resolved shear stress values for basal slip were obtained. The advent of pyramidal slip at room temperature was rationalized upon the basis of grip constraints. A bend-twinning hypothesis was advanced as an explanation of mechanical twinning which occurs as a complex stress-relief mechanism. INVESTIGATIONS of the plastic deformation of magnesium have been limited to the determination of the fundamental kinetics which may be summarized as follows: 1—Twinning on the {102).l 2— Slip on the (001) plane in the [loo] direction at room temperature.&apos; 3—Slip on the {101) or {102) plane in the [loo] direction above 225°C." 4—Critical resolved shear stresses for basal slip in tension at room temperature of 83 g per sq mm with a variation from 57 to 127 g per sq mm." Bakarian&apos; studied the compression of thin wafers of magnesium single crystals and classified the components of the deformation mechanisms as follows: 1—The Basal field: (001) at an angle of less than 20" to the compression surface. Fracture along {101} or slip on (001) followed by {101} fracture. 2—The prism field: (001) at an angle greater than 60" to the compression surface. Twinning on the {102) generally occurring during the early stages of loading, basal slip in the areas of original orientation and (001) slip within twins. 3—The central field: (001) at angles greater than 20" but less than 60" to the compression surface. Slip on the (001). 4—The critical resolved shearing stress for {101} slip above 225°C was 400 g per sq mm. Observations of mechanical twins in hexagonal close-packed metals have been summarized by numerous investigatorsb-&apos; emphasizing a lateral or rotational atomic adjustment, in addition to the pure twinning shear, and the importance of reorienting the basal plane to a position more favorable for continued slip, rather than the resulting small dimensional changes. Criterion for the operative twinning planes has not been clearly established. Schmid and Boas hurmised that an energy condition related to the atom movements is the determining factor. MillerQ bserved that twinning stresses in zinc crystals decreased as the amount of prior deformation increased. Preparation of Specimens Magnesium single crystals % in. in diam x 8 in. long were grown from the melt under an argon atmosphere in a gradient furnace similar to that described by Jillson." Magnesium containing 0.018

Jan 1, 1953

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

Strain-induced porosity has been found to occur in titanium and other materials at tensile strains greater than the uniform elongation of the material. Porosity in titanium increases with increasing strain and temperature, being most severe at 300° to 800°F. Strain-induced porosity is believed to be a normal part of the mechanism of deformation in ductile materials. DURING the past few years there have been numerous references to the occurrence of voids in laboratory test specimens of metals subjected to strain.l-7 These voids have been referred to as intercrystalline cracking, strain-induced porosity, intergranular cav-itation, voids, and porosity. They appear to occur at grain boundaries or interfaces, and are generally associated with large amounts of strain and have been found mostly in creep specimens and to a lesser extent in tensile specimens. Because the phenomenon does not occur unless the material has been strained,

Jan 1, 1960

By A Guinier

RECIPITATION in alloys is undoubtedly one of the most essential phase transformations in metallurgy and, besides, it is a phenomenon of great interest to physicists. It seems then that it can be chosen as a topic for an Annual IMD Lecture. Of course, the subject is a very wide one and I shall discuss here only a very restricted part of it. I should like to show why it is now considered that there is, at the beginning of the process, a stage distinct from the real precipitation, which is the pre-precipitation. We shall be chiefly interested in the atomic structure of the metal in this preprecipi-tation stage. Numerous reviews on this subject have been published recently.&apos;, &apos; The latest was given by H. K. Hardyh t the last meeting of the Institute of Metals in London. One of the most complete articles has been written by the late Dr. Geisler." I should like, at the beginning of this lecture, to pay a tribute to the memory of our friend Arthur Geisler. Some of the ideas which will be developed here are different from those advocated by him. But everybody knows the considerable progress in experiment and in theory which we owe to him and, personally, I deeply feel how fruitful have been the long discussions which we have had during many years. Experimental Basis of the Precipitation Problems Let us recall the essential facts pertaining to the problem of the precipitation. The starting point and the final one are well known. The initial stage is the supersaturated solid solution before quenching. The dissolved atoms replace some of the atoms of the solvent at the points of a definite lattice. It is generally considered that the distribution of the atoms is completely random, and that the lattice distortions are relatively weak. These assumptions are only an approximation. It has now beenproven", that, in some cases, the dissolved atoms have a tendency to segregate to form very small nuclei. These fluctuations of composition are greater than the normal statistical fluctuations in a purely random alloy. We shall see the role played by these nuclei later. The final state is obtained by a very long annealing at such a temperature that an equilibrium is reached in a reasonable time. The alloy is then composed of a matrix which is a saturated solid solution, much poorer than the initial one. Imbedded

Jan 1, 1957

By S. E. Bronisz, R. E. Tate

s-plutonium samples possessing a strong growth texture have been produced by allowing them to transform under pressure from p to a. A fiber texture with [010] parallel to the pressure axis results. The textured samples are expected to be useful in determining the effects of crystallographic orientation on the physical properties of a plutonium, and initial results of measurements of resistivity and mechanical properties are described. THE crystal structure of a plutonium1 is mono-clinic, P21/m, and many of the metal&apos;s properties should reflect the crystallographic anisotropy. Unfortunately, it has not yet been possible to grow useful sizes of single crystals of a plutonium. Therefore, few of plutonium&apos;s orientation-sensitive properties have been determined as a function of crystallographic orientation. One way to gain information about at least some of the orientation-dependent properties is to study a highly textured sample. Such samples have been produced by cold rolling a plutonium,2 but they are necessarily very small in one dimension. We have now successfully used two other techniques to produce highly textured samples, not limited to small thicknesses. METHODS OF PRODUCING PREFERRED ORIENTATION The texture is produced by causing the plutonium to transform from ß to a while under pressure. It was observed by Gardner3 that applying a compres-sive load during the transformation resulted in the formation of columnar grains of a plutonium, and Cramer4 observed a similar structure in some diffusion couples rolled in the P phase. Neither of these workers, however, investigated the subject beyond these observations. The more flexible of the two methods developed is that of compressive loading. The technique is to enclose a sample of plutonium in a die assembly before applying the load. It is possible, of course, to dispense with the die and simply press the sample between two platens. In this case, however, the unrestrained sample deforms during the pressing, making it difficult to maintain the load and to control the final sample thickness. This compressive loading technique has been used on specimens ranging from 1/4 to 3 in. diameter, with height-to-diameter ratios ranging from 5 : l to 1:6. The procedure begins with loading the sample, a right cylinder of a plutonium, into the pressing die. Plastic deformation of the sample while it is being pressed is minimized by machining the sample so that its diameter is nearly the same as that of the die barrel. Then the loaded die assembly is placed in a vacuum pressing can that fits on a hydraulic press. After a vacuum is achieved the die assembly is heated to 180°C and equilibrated. The load is then applied and the specimen and die are allowed to cool to about 40° to 50°C before the pressure is removed. The resulting sample is composed of rod-shaped a -plutonium grains, the rod axes being parallel to the cylinder axis and the pressing direction. Photomicrographs of the oriented structure are shown in Fig. 1. Although most of the specimen is composed of grains whose rod axes are parallel to the cylinder axis, a thin, peripheral layer consists of rod-shaped grains whose rod axes are perpendicular to the cylinder axis. Presumably, the highly plastic nature of p plutonium leads to approximately hydrostatic conditions during the initial stages of the P — a transformation under pressure. At this time, the grains in the peripheral layer would have grown parallel to the local force direction. During the latter stages of the transformation, the accompanying volume contraction would have eliminated the radial forces, leaving only the axial force and resulting in the growth of the observed structure. The growth texture did not form without the application of pressure. Attempts were made to produce the texture by repeating the standard temperature cycle without

Jan 1, 1965

By C. G. Dunn, P. K. Koh

The primary recrystallization textures of 11 single crystals cold rolled 70 pct were determined. The effect of crystal orientation on recrystallization behavior was investigated also and found to be large. An exception was found to the relationship that strong components of the recrystolliza-tion texture are rotated from the cold rolled texture by 30° about <110> axes, but generally this relationship was found to hold quite well. Evidence supporting oriented nucleotion was found and discussed in terms of probable active slip systems and <110> edge dislocations. THE present paper is one of a series&apos;.&apos; on recrys-tallization phenomena in cold rolled 31/4 Si-Fe single crystals and is mainly concerned with the textures produced on recrystallizing from stable end orientations. Data for the cold rolled textures of the crystals used have been reported by Koh and Dunn." Their results showed that the sharpness of the cold rolled textures varied throughout the range of stable end orientations and that the tendency to re-crystallize was related to the sharpness of the cold rolled texture, wherein the rate of recrystallization increased and the size of recrystallization grains decreased with decreasing sharpness of the cold rolled texture. In the project under consideration the cold rolled crystals involved a range of initial orientations that, together with those studied earlier,&apos; provide information on several points. The first point is whether the recrystallization texture from a (111) [112] cold rolled texture, a stable end orientation that can be approached from different directions, correlates in any way with the initial orientation before cold rolling, or whether the recrystallization texture is entirely determined by the observable features of the cold rolled texture. The second point involves a preliminary study to see if the main components of the recrystallization textures correlate with the most probable active slip systems. The third point is to determine what effect departure from slip on one slip system has on the tendency to recrystallize. Experimental Procedure Nine specimens from a previous investigation and two additional ones from thicker stock (lot D) but of similar composition to the others were used in the present work. The latter two crystals, like the nine, were cold rolled to a reduction in thickness of 70 pct and the amount of widening was determined. Depending on their primary recrystallization behavior, the cold rolled crystals were given short or long anneals at temperatures of 980°C or higher. Table I summarizes the data on initial orientations, the textures obtained by cold rolling, and the anneals given to provide samples for the present work. Fine grained specimens were thinned to 0.002 in. thickness and placed in an integrating specimen holder. Chart recordings using a transmission X-ray method and MoKa radiation were obtained for diffraction from (110) planes. This method,&apos;,3 which gives data for all of the pole figure except a central region of 30" radius, proved sufficient to give generally five, and sometimes six, of the six possible pole concentration areas of any one component of the texture. These data, therefore, were generally adequate for a positive identification of each component present. The first texture obtained for specimen B-2 was poorly defined because of too coarse a grain structure and therefore too few crystals in each component for satisfactory X-ray reflections. The same

Jan 1, 1957

By B. D. Cullity, A. Freda

It is well known that deformation by cold drawing or swaging produces a kind of preferred orientation called fiber texture in metal wires. Such textures have been extensively studied by means of X-ray diffraction, chiefly by techniques in which the diffracted X-rays are recorded photographically. This paper describes some results obtained with a new method, involving the use of a diffractometer. X-RAY METHOD Since the pole figure of a material having a fiber texture is symmetrical about the fiber axis, there is no need to present the entire pole figure. Instead, texture data can be summarized by means of a curve showing the variation of pole density along any meridian of the pole figure, if the north-south axis of the latter is made parallel to the fiber axis. The position of a pole on the meridian is specified by the angle 9 between the pole and the fiber axis (wire axis). The X-ray method1 used here to measure pole density as a function of 9 actually consists of two methods, referred to as A and B. In method a, X-rays are reflected from the wire surface. Pole densities can be measured by this method from O = 90 deg down to a limiting value which is dependent on the Bragg angle 8 and is typically of the order of 30 to 40 deg. Method B involves diffraction from the wire cross section and covers a range of 0 values from 0 up to an angle sufficient to overlap the measurements made by method A. By a combination of the two methods, a complete pole-density curve can be obtained. However, method A alone, which requires no specimen preparation other than etching, can often reveal enough of the pole-density curve to provide complete information about texture components. Both methods require that the measured diffracted intensities be corrected for changes in absorption and diffracting volume with changes in 9. A11 intensities I reported in this paper are corrected diffracted intensities; they are propor-

Jan 1, 1960

By H. S. Cannon, F. N. Rhines

IT. H. Hausner( Sylvunia Electric Products Inc., Bay-side, N. Y.)—The results reported by the authors are interesting because they contribute some information on the principles of sintering and also because of a certain practical value for the manufacture of powder . metallurgical parts in production. Pressed powder compacts are frequently sintered in a boat in several layers so that the lower layers are actually sintered under the weight of the upper layers and, therefore, are frequently deformed. The authors gave information on this deformation process by determining the effect of the load on the density. The experimental setup of the authors, however, has a disadvantage—that the sintering occurred in a cylindrical container so that the deformation was stopped in the direction of the diameter. The authors should have rather called this a study of hot-pressing than of sintering. I want to call the attention of the authors and others interested in sintering under load to the experimental work described by Dawihl and Rix.&apos; These authors sintered cylindrical compacts under a lengthwise ten-sional load of 0 to 25 g and found that the shrinkage in length and diameter changes considerably with the load, but that the volume shrinkage is affected very little by the load. H. S. Cannon (authors&apos; reply)—We wish to thank Dr. Hausner for calling attention to the experimental work of Dawihl and Rix. The fact that they found volume shrinkage little affected by varying tensional loads during sintering seems to support the contention that the forces due to loading are equivalent to and additive to the forces which cause densification. This contention is the basis of our comparison of sintering and creep.

Jan 1, 1952

By E. C. W. Perryman

The recovery of X-ray line broadening, hardness, and electrical resistivity from cold worked AI-Mg alloys has been investigated. The results, together with those from density measurements, suggest that magnesium atoms freeze in the excess vacancies formed by cold working, and that this affects the climb of dislocations during the recovery process. PREVIOUS work1, " has shown that while 1 pct Mg increases the activation energy for recrystalliza-tion, it decreases the activation energy for the recovery of mechanical properties and decreases the subgrain size both after cold working and annealing. A similar result has been reported by Varley2 for an A1-2 pct Mg alloy. With plastic deformation at high temperatures, McLean and Farmer&apos; and Rachinger have found that magnesium appears to retard the motion of dislocations and, furthermore, they find little or no effect of magnesium on the size of subgrains formed during high temperature deformation. In view of the apparent contradictions as to the effect of magnesium on subgrain size, the recovery process in Al-Mg alloys has been investigated more thoroughly by studying the annealing out of X-ray line broadening, hardness, and electrical resistivity from alloys cold worked at room temperature. Material Used—The chemical analyses of the alloys are given in Table I. Fabrication—The material used was cold rolled 20 pct at room temperature, the grain size prior to the last cold rolling operation being similar to that used in previous work; i.e., 230. The experimental procedure for annealing, determination of X-rav half-veak breadth. hardness measurement, electEica1 resistivity, and density and metallographic examination was exactly the same as previously described." Variation of X-Ray Half-Peak Breadth with Annealing Time—Isothermal annealing curves at 100°, 200°, and 250°C were obtained for material cold worked 20 pct. The half-peak breadth of the (333) Ka, line directly after cold working is shown as a function of magnesium content in Fig. 1. Only with the 2.87 pct Mg alloy was overlapping of the a, and n.. reflections observed to any appreciable extent. To separate these, Rachinger&apos;s method&apos; was used. Typical isothermal annealing curves are shown in Figs. 2 and 3 for 100" and 200°C, respectively. These curves are similar to those obtained previously for super-purity aluminum except that the

Jan 1, 1957

By M. S. Burton, G. V. Smith, A. Rosen

The kinetics of re crystallization and the effect of recovery on recrystallization of pure iron were investigated within the temperature range of 517" to 632 OC. Grain growth and activation energies were also studied. Two stages can be distinguished during recrystallization; the first is gvowth-controlled and the second is nucleation-controlled. The extent to which the first stage succeeds before the second stage begins depends on both temperature of recrystallization and temperature of recovery. The softening of cold-worked metals and alloys due to transformation of the deformed crystals to strain-free equiaxed grains during annealing is well-known, and early inestiators established that recrystallization kinetics is strongly influenced by minute quantities of impurities. Generally, it is believed that impurities decrease the rate of recrystallization and the rate of grain growth. To understand the basic phenomena of recrystallization, investigations should be on pure materials. Most of the research on high-purity materials has been on metals having the fee Bcc materials, and especially high-purity iron, have been studied only in recent years. It is known that recovery may influence recrystalliation;" however, no general description of the influence, applicable to all materials, has been presented. This paper presents results of a study of the recrystallization kinetics of high-purity iron, after 60 pct cold deformation by drawing, with particular reference to the influence of recovery on the rates of recrystallization and grain growth. From observations of these rates, conclusions are drawn concerning nucleation. MATERIAL AND EXPERIMENTAL PROCEDURE Preparation of Material. High-purity iron, prepared by zone refining of vacuum-melted electroiytic iron at Battelle Memorial Institute under sponsorship of the American Iron and Steel Institute, was used in this study. Table I gives the reported chemical analysis of the material, taken at a point near the last molten zone and thereby rep- resenting the maximum impurity level for the entire bar. Prismatic specimens, approximately 10 x 10 X 50 mm, were sawed from the 50-mm-diam bar, perpendicular to the zone-refining direction, and turned to cylindrical shape. These specimens were sealed in quartz capsules under vacuum, approximately 10"e mm Hg, austenitized at 930° C for 15 min, slowly cooled, removed from the capsules, and cold-worked in air by swaging to approximately 20-pct reduction of area. The encapsulating, austenitizing, and swaging operations were repeated two additional times, after which the samples were encapsulated, austenitized, and cold-drawn to 60-pct reduction of area. A further vacuum anneal at 630°C for 120 min and cold drawing to 60-pct reduction of area produced wire 2.8 mm in diameter. The drawn wire was electropolished to remove deformed material on the surface, after which it was sawed into 4-mm-long specimens for the recrystallization study. Microscopical examination before the final cold reduction revealed equiaxed grain structure with very fine grains in a thin layer near the surfaces of the specimen and nearly uniform ASTM 3-4 grain size in the center. Recrystallization Heat Treatment. a) Direct Recrystallization of Cold-Worked The 60 pct cold drawn iron specimens were recrystallized at five temperatures, 517, 556, 590°, 612, and 632C, in a lead bath covered with graphite (the temperature was controlled to 1°C). Specimens were treated for twelve different times at each temperature, and all were water-quenched after heat &eatment. b) Recrystallization Following Preliminary Recovery Heat Treatment. After cold working, specimens were sealed into quartz capsules under vacuum, 105 mm Hg, and recovery-annealed at 362", 400", and 440°C for 20 hr prior to recrystallization. No evidence of recrystallization was found

Jan 1, 1964

By B. N. Das, P. A. Beck

THE o phases have a complex tetragonal structure with Lo/ao = 0.52 and 30 atoms per unit cell.1 A large number of such phases are now known to occur in various binary systems of the transition elements and they exhibit the following typical features: 2,3 The composition of binary o phases is variable, ranging from approximately A4B to ABI. With only a few exceptions, in the o phases the A-ele-ment comes from the V- or Cr- group of the periodic table, while the B-elements are from the Mn-, Fe-, Co-, or Ni- group. In the first long period the corresponding o phases of the V- and Cr-series have approximately the same compositions. However, as the B-element changes from Mn to Fe to Co to Ni, the mean composition shifts monotonously toward higher A-contents.2-4 For example, if the mean compositions of the various o phases with vanadium are compared with each other, the composition shift mentioned above becomes plainly visible: V 30Mn0 80 Vo.45Feo..,, Vo .,Coo. 45 and Vo.5Nio.3. Similiar composition shifts, although not the same composition values, were observed in u phases formed by second and by third long-period transition elements.3&apos;4 This behavior, very characteristic of o phases, is in rather sharp contrast to the usually quite well-behaved stoichi-ometry of the Laves phases. In the latter, the AB2 stoichiometry predominates, with A the large atom and B the small atom.= The p phase occurs in the four binary systems of Mo or W with Fe or Co. On the basis of their crystal structure determination, Arnfelt and westgren6 ascribed to the p phase in the Co-W system the ideal composition W,Co7. Since all four binary pphases have nearly the same composition, it would seem quite plausible that some definite stoichiometry such as A6B7, might be characteristic of this phase, as AB2 is of the Laves phases. On the other hand, it has been noted,7 that the phases occur at average electron concentrations near to those at which the various cr phases are found. Also, it has been pointed out by Shoemaker and associates8 that structurally the a phases and the p phases are somewhat related to each other; both of these structures may be described in terms of suitable stackings of quasi-hexagonal layers&apos;of atoms. By studying a suitably chosen ter- nary phase diagram, one might expect to be able to find out which one of the two conditions, the analogy with the o phase or the constant ratio between the number of large atoms and the number of small atoms in effect governs the behavior of the p phase. Several isothermal sections of ternary systems containing o phases have been investigated. In all cases where two binary o phases occur, these were found to be connected b a more or less straight ternary o phase field.7&apos; &apos;10 Such elongated o phase fields were also found in ternary systems in which only one of the limiting binaries is known to contain o phase. In this manner a latent o forming tendency could be detected and the virtual composition of a "binary o phase", which does not actually occur as such was approximately determined by extrapolation. The behavior of the phases, including their composition shift, is analogous to that of the classical electron compounds, as described by Hume-Rothery.11 In order to decide whether the p phase is essentially a "size compound" like the Laves phases, where a fixed stoichiometric ratio is quite generally maintained between the "large atoms" and the "small atoms", or whether the p phase is typically an "electron compound" in the same sense as ois, it was decided to investigate an isothermal section of the Mo-Mn-Co system. The Mo-Co system12 and the Mo-Mn system13 each are known to have a binary o phase. It could be therefore expected that a ternary o phase field will connect these two binary cr-phase fields. The p phase is known to occur in the Mo-Co system. If the p phase should turn out to form an elongated phase field extending deep into the ternary system, the following considerations mighto apply. The atomic radius of manganese (1.314for C.N.12) is between the va,lues for Mo (1.40Afor C.N.12) and for Co (1.26Afor C.N.12). If it is assumed that p is a "size compound", and that Mn is substituting for the smaller Co atoms in the p-structure in the ternary system, the y-phase field might be expected to extend parallel to the Mn-Co binary line. If Mn is substituting for the large Mo atoms in the p-structure, the p-phase field may be expected to extend parallel to the Mn-Mo binary line. On the other hand, if the p-phase turns out to be an "electron compound" like o, the ternary p-phase field should extend parallel to the ternary o -phase field connecting (Mo,Mn)owith (Mo, Co) a

Jan 1, 1961

By B. D. Cullity

A distribution of residual stress after plastic elongation is proposed, in which the bulk of the material is strained in compression and a very small portion in tension, This distribution is shown to account both for the X-ray observations and for the effect of plastic straining on magnetic losses in silicon steel. The regions left in compression are tentatively identified with the interiors of the sub-grains revealed by the electron microscope. THIS paper is concerned with the general problem of the nature of the residual stress which is produced in metals by plastic elongation. A particular stress distribution will be suggested which accounts for the main X-ray diffraction observations which have been made. It will also be shown that certain magnetic measurements made on silicon steel can be understood in terms of this stress distribution. X-RAY OBSERVATIONS Uniform straining of a crystal lattice (macro-strain) causes a diffracted X-ray beam to shift its position, and nonuniform straining (microstrain) causes line broadening. If a bar of metal is plastically elongated in the longitudinal x direction and then unloaded, diffracted X-ray lines are observed to be both shifted and broadened.&apos;-= Although the observed line shift indicates the presence of macro-strain, experiments have shown that no macrostrain, in the usual engineering sense of the term, exists.5"7 For example, removal of a layer from one surface of a stretched and unloaded bar does not produce curvature in the remainder of the bar 5&apos;7 Fig. 1 shows the variation of lattice strain in the x direction, as determined from X-ray line shifts, with the applied stress in the same direction. The curve ABC is the normal stress-strain curve of the material, AB being the elastic portion and BC the plastic. In the elastic region AB, the strain measured by X-rays, called the lattice strain, and the strain measured mechanically are both proportional to the applied stress, and both return to zero when the applied stress is removed. Above the elastic limit the lattice strain would be expected to continue to increase along the line BD. Actually, it increases less rapidly with respect to stress, or even decreases, as shown by BE. If the applied stress is then decreased, the lattice strain decreases along EF, which is parallel to AB. As a result, there is a compressive residual lattice strain FA after unloading. STRESS DISTRIBUTION. Since a stretched and unloaded bar does not contain macrostress, it follows that the observed line shift must be due to a special distribution of mi-crostress. Such a distribution is shown in Fig. 2, which shows the variation of the stress u, across a stretched and unloaded bar. The material is assumed to consist of two kinds of regions: regions C, stressed more or less uniformly in compression, comprising the bulk of the volume of the material and responsible for the observed diffrac-

Jan 1, 1963

By E. P. Abrahamson II

The effect of transition elements which form binary solid solution upon the recrystallization temperature of zirconium has been investigated. All additions raised the recrystallization temperature. A correlation is obtained between the logarithm of the rate of change of recrystallization temperature with atomic percent solute and the free atom ground state electron configuration of the solute element. ThE work of Abrahamson, et al., on dilute binary solid-solution alloys indicated a correlation between the free-atom ground state electron configuration of the solute and either the brittle-ductile transition or recrystallization temperature. These studies were carried out on bcc base materials. The implication is that the outer s and d electrons of the solute are the prime determinant of the absolute rate of change of recrystallization or transition temperature. Furthermore, the limit of linearity has been shown to be a function of solute electron configuration for recrystallization in iron and vanadium. To date no Complete systematic recrystallization study of dilute binary zirconium base alloys has been made. It is the purpose of this study to note whether the change in solvent structure from bcc to hcp will influence the correlation. It was also desired to learn more of the role of the electron configuration of the solvent on recrystallization temperature. PROCEDURE All alloys were made using 99.87 pct Zr with 0.01 Cr, 0.04 Fe, 0.006 Hf, 0.003 Mg, 0.003 Mn, 0.003 N, and 0.080 0 (132 BHN). The solute elements were 99.9 pct pure. According to the published binary phase diagrams6 and metallographic examinations at X750, all alloys used were solid solutions. The alloys were arc melted and remelted six times in the form of cubic 200-g buttons under an argon atmosphere. They were then hot pressed at 950°C to 0.450 in., upset pressed to 0.350 in., and annealed at 800°C for 1 hr. The specimens were then Blanchard ground to 0.250 in., removing 0.050 in. from each side. The grain size of the material at this stage was found to be 8000 100 grains per sq mm. The specimens were then cold rolled to 0.130 in. and cold pressed to 0.125 in., yielding 50 1 pct cold work. All alloys were then chemically analyzed for the principal addition. The interstitial contents remained at the values of the starting material when checked on random alloy specimens. The rolled sheet was cut into 6.75 by 0.25-in. lengths and heat treated in a gradient furnace for 1 hr. The gradient was 250o to 900°C over the 6-in. length, recorded continuously by six thermocouples resting on each specimen. Control was 3oC, accomplished at the hot end. The recrystallization temperature was determined metallographically using polarized light. The criterion chosen was the point on the specimen showing the first recrystallized grain at a constant magnification, X200. Specimens were repeated, and the agreement was found to be 3°C. RESULTS Three different pure zirconium specimens were tested, and the recrystallization temperature was

Jan 1, 1962

By Hsun Hu, R. S. Cline

A detailed studj) of texture formation in 2 pet Al-Fe single crystals with initial orientations of approximately (111) [112], (112) [111], and (112) [111] was made by examining the textures developed on the surface and at various interior sections of the crystal after rolling to various amounts. Depending&apos; upon the initial orientation of the crystal, the surface and interior textures may differ only in sharpness, or may differ essentially in orientation. The orientation of the (111) [112] crystal does not change upon rolling up to 70 pet, but after rolling more than 90 pet a distinct component of (001) (110] orientation is developed. The texture formed in the two (112) (1111 type crystals consists of (111) (1121 and (001) (1101 components. The latter, however, is largely confined to the surface layers. The textures formed on both sides of the crystal are identical, and the texture composition profile is approximately symmetrical with respect to the central section of the strip thickness. The formation of these texture components is analyzed. DURING the past seven or eight years, deformation and recrystallization textures in rolled Si-Fe single crystals have been extensively studied by various investigators.1-7 From these studies, much knowledge on texture formation in bee crystals of various initial orientations was obtained. However, these results also raised many questions, regarding particularly the correlation between deformation and recrystallization textures, as well as the deformation texture itself of some particular crystals. To take a (111) [112] type crystal as an example, it was shown by Dunn and Koh2, 3 that this orientation does not change during deformation by rolling. This finding is consistent with the conclusion reached by Barrett and Leven-son8 with respect to iron crystals that (111) [112] is one of the stable end orientations. However, different recrystallization textures were observed by Dunn and Koh3 in (111) [112] type crystals of different initial thickness, which widened differently during rolling even though their deformation textures were identical. Another interesting example, also from the results of Dunn and Koh2&apos;3 is that of texture formation in a (112) [111] crystal. This crystal developed a two-component deformation texture of (111) [112] plus (001) [110]. Its recrystallization texture, however, was found to be predominantly (110) [001], which is related to the (111) [112] component by a simple [110] rotation. This crystal, therefore, behaved as if the other deformation texture component, (001) [110], were not present. There are also discrepancies among the results of different investigators, as well as numerous unexplained fine features of the deformation texture of crystals of various initial orientations. In order to have a better understanding of all of these points, a detailed study of deformation textures is greatly needed. One of the obvious things that has been completely overlooked in previous texture studies is the possible effect of surface texture. All past work on the texture of Si-Fe single crystals was conducted in a rather simple manner, i.e., the rolled crystals were etched to a very thin sheet; then their textures were examined by transmission X-ray techniques. For recrystallization texture studies, unless precautions are taken by etching off a sufficient amount of the surface layer before annealing, the texture developed in the interior may be affected by the surface layer, which may well have a different initial texture and which may have undergone recrystallization earlier than the interior of the specimen. Because of this effect, it is now planned to reexamine the texture of various rolled and annealed single crystals at the surface, and at various sections below the surface by using reflection techniques. In some cases, both surfaces of the rolled crystal will be examined. In one of Dunn&apos;s early papers,9 he noted that at an early stage of rolling the crystal seems to divide roughly through the middle to become a sample which in effect consists of two layers having some what different orientations. This effect has never been further explored. The investigation described in the present paper constitutes the beginning of a series of thorough investigations of texture formation in deformed bee single crystals designed to clear up some of the uncertainties which have been discussed. We have chosen a high-purity 2 pet Al-Fe alloy for this investigation. It is known that the allotropic transformation of iron is eliminated by alloying with approximately 1petAl. Such an alloy, being very similar to silicon ferrite, can be heated to the solidus temperature without phase transformation. One reason for choosing A1-Fe instead of Si-Fe for the present investigation is that we have been able to make single crystals of a vacuum-melted high-purity A1-Fe alloy by the strain-anneal method without much difficulty, but were not successful in doing so with a vacuum-melted high-purity Si-Fe alloy. For many research purposes,

Jan 1, 1962

By H. I. Aaronson, H. A. Domian

The self-diffusivity of Ag10 has been measured as a function of temperature and composition in AgMg. a CsCl-type intermetallic compound with a substitutional defect structure on both sides of the stoichiometric (50 at. pct Mg) composition. These measurements show that In D increases linearly, and both In Do and Q decrease linearly with deviation from stoichiometry. The slopes of these lines are significantly steeper in magnesium-rich alloys. Equations for the variation of Q with composition have been derived by application of the theory of random walk processes on the assumption that diffusion in compounds of this type takes place by the six-jump cycle mechanism of Huntington, Elcock, and McCombie. The favorable agreement obtained with experiment furnishes fresh support for the correctness of this assumption. A principal result of this treatment is that. although the concentration of vacancies is considerably higher in the silver sublattice than in the magnesium sublattice, the acfivation energies for movement of the magnesium sublattice vacancies are so much lower that these vacancies are responsible for effectively all diffusion of silver in this compound. A tendency for vacancies of both types to be kinetically bound to wrong atoms is also noted. THIS study was undertaken to examine the influence of substitutional defects upon self-diffusion in an intermetallic compound, AgMg, with a CsCl-type crystal structure. The CsCl structure is exception- ally simple. At the equiatomic or stoichiometric composition in a binary alloy, it consists of two interpenetrating simple cubic sublattices, each of which is exclusively populated by the atoms of one species. When atomic size and other factors are favorable, deviations from stoichiometry can be entirely accommodated by the substitution of atoms of the species present in excess of 50 at. pct on the sublattice of the other species on a one-for-one basis. Under this condition, the only vacancies present are those formed by thermal activation. The excess atoms thus incorporated into the sublattice of the minority species may be considered as substitutional defects in this sublattice. Several X-ray studies have shown that the defect structure of AgMg is entirely of the substitutional type on both sides of the stoichiometric composition.1"3 The thermodynamic investigation of Kachi indicates that, aside from a low level of thermal disorder and these constitutional defects, order is maintained to the solidus temperature. This compound is therefore a particularly useful vehicle for a study of the influence of substitutional defects upon diffusion kinetics. Other advantages of AgMg for this purpose include: the broad composition region, as much as approximately 10 at. pct on either side of the stoichiometric (50 at. pct Mg), in which the compound is stable; the comparatively low temperature range of the solidus (820°C and below),5 making diffusion anneals near this range experimentally convenient; the reasonably good machinability of the compound, permitting utilization of the standard sectioning method of radiotracer analysis; and the availability of a good tracer, A for one of the constituent species. While this investigation was in progress, Hagel and westbrooks reported data on the self-diffusion

Jan 1, 1964

By Joseph B. Darby, Paul A. Beck

IN isothermal sections of several ternary systems, the a-phase was found1 to extend in the form of a relatively narrow elongated field, connecting the U-phases that are present in the adjoining binary systems. This was interpreted in accordance with the conception that the U-phase is an electron compound and the ternary U-phase fields were shown in several systems&apos; to extend approximately in the direction of constant average d-shell electron vacancy number per atom. &apos; However, in the various isothermal sections of the Fe-Cr-Mo system" the ternary a-phase field was

Jan 1, 1958