By C. S. Samis, D. P. Seraphim

In the presence of oxygen, galena is oxidized in an aqueous medium containing ammonium acetate in accordance with the following reaction: PbS + 1/2 0, + 2 NH~Ac -» PbAc, + So + 2 NH: + H2O. This reaction was studied in an autoclave under oxygen pressure by polarographic measurement of the concentration of lead ion in solution. Oxidation rate is parabolic. The reaction products are lead acetote and elemental sulfur, the latter forming a film on the galena crystal. Reaction kinetics appear to be determined by the diffusion of lead from the galena phase to the solution interface through the film of sulfur. RECENT applications of pressure leaching on a commercial scale have emphasized the metallurgical importance of the oxidation of sulfide minerals in aqueous media by oxygen under pressure. Research experience has shown that sulfates, thio-nates, and metal oxides are the products of humid oxidation of sulfide minerals in basic solutions. The metal oxides may be solubilized in the presence of a complexing ion.' Certain oxide minerals are also amenable to treatment by this type of oxidation.' Several kinetic studies have been made of reactions of this type. Stenhouse' found that pyrite (FeS?) oxidized in a sodium hydroxide solution to produce a soluble sulfate and an insoluble layer of iron oxide and that the kinetics of the reaction were controlled by oxygen diffusion through the oxide layer. Andersen' studied the oxidation of galena (PbS) in a sodium hydroxide solution under oxygen pressure. He found the lead and sulfur to be simultaneously oxidized to produce plum bite ions and sulfate ions, and that the reaction rate was proportional to the surface area of the galena. The kinetics appeared to be determined by the reaction of oxygen and water with the galena surface. In each of the above reactions the metal and sulfur components of the mineral were oxidized simultaneously and at equal rates. In the present study the alkaline medium has been replaced by an approximately neutral solution of ammonium acetate in which lead sulfate is soluble. Under the conditions no sulfate was produced and no sulfur could be detected in the solution. The metal component of the mineral was solubilized and the liberated sulfur remained as a film of elemental sulfur on the surface of the galena crystal. A kinetic study of this reaction was undertaken to establish the kinetic mechanism and to determine the rate controlling step. Specific reaction rates were determined by oxidizing crystals of galena of measured surface areas in an autoclave maintained at the desired temperature and oxygen pressure. The rate of reaction was followed by measuring the concentration of lead in the ammonium acetate solution with a cathode ray polarograph, employing stationary platinum electrodes incorporated in the autoclave. Experimental Materials and Equipment Crystals of galena obtained from Violamac Mines, Retallack, B. C., were selected for oxidation because

Jan 1, 1957

By Milton E. Wadsworth, R. Ted Wimber

Cobalt sulfate solutions containing ammonium acetate and chloroplatinic acid were reduced by hydrogen in a pyrex-glass lined autoclave in the temperature range of 170o to 232°C and hydrogen partial pressure range of 115 to 830 psia. The reduction rate was directly proportional to the hydrogen partial pressure and surface area of the pyrex glass and was independent of the quantity of chloroplatinic acid added initially. Experiments involving the variation of the relative concentration of ammonium acetate indicated that the reducible cobalt complex was probably the diacetate complex of cobalt, Co(AC)4H20, or a new mononcetate complex Co Ac, which was in solubility equilibrium with a pink precipitate of CO(AC)-4HzO. THE reaction in which a metal is dissolved by an acid to produce gaseous hydrogen and a salt solution was discovered early in the history of chemistry. In 1859 Beketoff found experimentally that this reaction could be reversed; i.e., a salt solution could be reduced by gaseous hydrogen to produce a metal and an acid. A review of work done on this phenomenon since that time may be found elsewhere., The hydrogen reduction of a cobalt salt solution is facilitated by complexing the cobalt ion. An ammonia complex of cobalt has been reduced commercially in the recovery of cobalt metal. A new reducible complex of cobalt was discovered5 when it was found that a co-baltous sulfate solution containing ammonium acetate could be reduced by hydrogen at temperatures in the region of 200°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature below its normal boiling point, a violet color became apparent, indicating complex formation. The nature of this complex was investigated5 by the addition of NH4Ac to a CoSO4 solution maintained at 85o. During the first additions of NH, Ac, the pH of the solution remained fairly constant at about 5.85. However, as the ratio of NH,Ac to CoSO, approached two, the pH rose and then leveled off at about 6.05. The absorption spectra of a Co(Ac), solution and a CoSO,, NH Ac solution were obtained at 85°C and were compared and found to be the same. These findings suggested that the diacetate complex of cobalt, Co(Ac),.4H20, was formed at 85°C. When a cobalt sulfate-ammonium acetate solution was heated to a temperature above about 165o, a finely divided pink precipitate appeared. The X-ray diffraction pattern of this precipitate indicated that it was Co(Ac), - 4H,O. In addition, it was discovered that when chloroplatinic acid, H,PtCl;, was added initially to the cobalt sulfate-ammonium acetate solution, a faster reduction was obtained. The roles of the solution complex, pink precipitate and chloroplatinic acid in the reduction process were then investigated. APPARATUS The experimental work was carried out in a two-liter stainless-steel autoclave. Adetailed description of the autoclave and the auxiliary equipment used in maintaining constant temperature and pressure may be found elsewhere.= Because the stainless steel was corroded, and also because it acted as a hydrogena-tion catalyst, an all-glass liner was fabricated such that the solution came only into contact with flame-polished pyrex glass. EXPERIMENTAL PROCEDURE The solutions used in the experimental work were prepared by dissolving reagent grade chemicals in distilled water. Although variation of the brand of ammonium acetate appeared to have no effect on the experimental results, CoSO, 7H O from the J. T. Baker Chemical Co. of Phillipsburg, N. J.,was found to give faster reductions than that prepared by Allied Chemical and Dye Corp., N. Y. The former was used throughout the course of the experimental work and was weighed up at the outset of each experiment. The ammonium acetate was dissolved to form a 6M stock solution, which was stored under refrigeration. A 10 pct solution of chloroplatinic acid (J. T. Baker Chemical Co.) was diluted to a 1.15 x 1Q2 M stock solution, which was standardized by precipitation of K,PtCl, as outlined by Scott. The appropriate volume of the chloroplatinic acid, H,PtCl,, solution was pipetted into the clean, dry glass liner. The cobalt sulfate-ammonium acetate solution, which had previously been saturated with

Jan 1, 1962

By W. A. Tiller, J. D. Harrison

HOT pressing of powder particles has gained importance recently, since it affords a method in which high densities are rapidly attained. In a recent study on hot pressing of alumina powders, Mangsen, Lam-bertson, and Best1 have shown within the limits of their experiment, the validity the rate equation for densification in hot pressing, originally proposed by Murray, Livey, and Williams.2 i.e., where D = fraction of theoretical density, t = time, P = pressure and 77 is the viscosity, all in appropriate units. This equation was derived from earlier work of Shuttleworth and Mackenzie3 which is based on the closing of spherical pores under the action of surface tension. The integrated form of this equation yields a straight-line relation between log (1 - D) and t. Such conditions were found by Felten4 to be true only after extended periods of pressing. In an endeavor to quantitatively evaluate the exactitude of this equation in the initial sintering stage, i.e., prior to sealing of the pores, spherical anti-

Jan 1, 1962

By F. A. Schaufelberger

Early work on chemical precipitation of metals from metal salt solutions is reviewed. The chemistry and thermodynamics of precipitating copper, nickel, cobalt, and cadmium metals by reaction with hydrogen are discussed. Mechanisms of metal precipitation, nu-cleation, growth, and agglomeration are reviewed, as well as some solubility phenomena of cleation,gases and solids at elevated temperatures. Experimental data presented deal mainly with the reaction of copper sulfate solution with Hz. METAL can be recovered from a leach solution either indirectly by precipitation as a compound that is later reduced or directly by electrolysis, cementation, or chemical reduction, for example, with hydrogen. The widely used electrowinning processes suffer from the inefficiency of converting fuel to low voltage dc and from low current efficiency when complete recovery is attempted. With the batch hydrogen reduction methods outlined here, a unit of fuel converted to hydrogen in modern gas reform plants will make two to three times as much metal as can be obtained with electrolysis. With continuous hydrogen reduction, four to six times as much metal is obtained. Precipitation by reducing a metal salt solution with H, has been known for almost 100 years.' Commercial use of the process, however, awaited the research and development program initiated by Chemical Construction Corp. Within the last few years this program has brought about construction of commercial plants, listed on p. 701. Ideal hydrogen reduction will precipitate a pure metal from a solution obtained by commercial leaching methods at a rapid rate without excessive temperatures and pressures. The metal precipitate will be of desired size and density, less than a percent left in the vessel being deposited on the wetted parts. The present discussion will outline Chemical Construction Corp.'s early development program and will discuss the chemistry and mechanics of reducing copper, nickel, cobalt, and cadmium from solution by H2. Work on selective reduction of nickel from cobalt has been described earlier.2 The article is not concerned with precipitation of copper by disproportionation of cuprous solutions where yield is limited" to 50 pet.* It does not discuss use of gaseous reducing agents other than hydrogen, such as SCV which may lead to contamination with sulfur, or CO," which is considerably more expensive than hydrogen and produces a gaseous reaction product, CO2.† The article does not include use of other nongaseous reducing agents: which are far more expensive than CO. Also, notes on the history, engineering design, and performance of commercial plants have been given elsewhere." It will be shown that a pure metal can be precipitated by reduction with hydrogen from solutions obtained by commercial leaching methods when the solution cohposition is controlled and proper acidity, proper metal ion concentration through controlled complex formation and hydrolysis, and adequate agitation for suspension of metal and for transfer of reducing gas are maintained. Reasonable temperatures and pressures are used which are less excessive than those used by previous workers, although they are maintained at above equilibrium values because of process kinetics.' It has also been found necessary to induce nuclea-tion and to control growth and agglomeration in order to get a powder product of suitable physical properties. Review of the Literature Muller, Schlecht, and Schubardt of I. G. Farbenm claimed a successive reduction of silver, copper, nickel, cobalt, and zinc from ammoniacal solution by applying progressively higher temperatures and hydrogen pressures. Metals produced by this technique were not pure, since no attempt was made to adjust the solution composition between the different reductions. It is doubtful that the zinc product contained any metallic zinc. The major contribution to the literature" was made by the Ipatiews,12 who prepared platinum, iridium, copper, nickel, cobalt, lead, tin, arsenic. antimony, and bismuth at often extreme conditions, up to the critical temperature of water (373"C), at 1500 to 7500 psi, for as long as several days. Even cadmium and zinc were claimed to have been observed in trace quantities precipitated together with basic salts. In the early experiments solutions were not stirred. Extensive formation of oxides and basic salts occurred. probably long before sufficient hydrogen could be supplied in the unstirred liquid to decrease the metal concentration in solution by reduction. The importance of hydrogen pressure was

Jan 1, 1957

By W. W. Stephens, W. J. Kroll, H. P. Holmes

THE only two methods for producing commercial quantities of malleable zirconium, up to now, have been using magnesium reduction of the anhydrous chloride under a neutral gas, and using purification of raw zirconium by the iodide dissociation method on a hot filament. The purity of the metal obtained by the latter process is about the same as that resulting from the chloride reduction, with the exception of the oxygen content, which may be about 0.05 pct lower in the iodide metal. Even traces of oxygen have a strong hardening effect on zirconium. Since, in the iodide process, the impurities, Si, Al, Fe, Ni, and Mg in the raw zirconium used, are carried over, it would appear uneconomical to use this method of refining solely to eliminate the traces of oxygen, unless very soft metal is desired. One important step to improve the iodide method, namely, dissociating pure iodide made from carbide and recycling the iodine, which would change this refining process into a method for extracting zirconium from the ore, has not yet been made. The Bureau of Mines, by using the chloride reduction, wanted to produce quantities of a reasonably pure and malleable metal at low cost for large-scale industrial use. This aim has been achieved, and a pilot plant permitting production of 600 lb of malleable zirconium per week will be described (fig. 1). Briefly, the Bureau of Mines process consists of reducing purified gaseous anhydrous zirconium chloride with fused magnesium under a noble-gas atmosphere. The reaction product, magnesium chloride, and any excess magnesium metal present are removed from the sponge zirconium in the next step by fusion and evaporation in a good vacuum at about 925°C. In this process, care is taken to keep air out of contact with the hot metal, which otherwise would contaminate the product with oxygen and nitrogen. Both these impurities embrittle zirconium even when present in an amount as low as 0.1 pct. A number of previous reports1-3 describe the method and the various improvements that finally led to a workable process. The major steps made were the production of large quantities of carbide, which is the raw material for producing the chloride, its chlorination with reasonable efficiencies, and the elimination of iron trichloride contained in the raw chloride, as well as that of the zirconium oxide which is always present in this product. The physical nature of the anhydrous chloride, which sublimes at 331°C at atmospheric pressure and melts at 420°C under a pressure of 25 atm, made it necessary to provide a special safety device on the purification and reduction vessels in the form of a lead-alloy seal, permitting escape of excess gases if pressure tended to build up. The main difficulties encountered in the reduction and in the following step, salt separation in a vacuum at elevated temperature, were caused by the material from which the reaction pot was constructed—iron. This metal reacts with zirconium at about 940°C with formation of a eutectic. The last step, salt separation by evaporation of the magnesium and magnesium chloride in a vacuum, is quite unconventional and has not been used before on such a scale. It is only due to the improved construction of high-vacuum pumps, especially oil-diffusion pumps, that such a method could be used. The various steps of the Bureau of Mines process, as described in the general outline above, may be summarized as follows: (1) production of the carbide, (2) chlorination of the carbide, (3) purification of the raw chloride, (4) reduction of the pure chloride with fused magnesium, (5) separation of excess magnesium and magnesium chloride in vacuum at elevated temperature, and (6) melting of the sponge obtained. Production of Carbide The arc furnace, described in a previous report,' was improved both to reduce the graphite consumption caused by the burning of the bottom plates and to concentrate the heat in order to obtain better power efficiency. This was achieved by providing the bottom with graphite plates entirely embedded in refractory bricks, the contact with the current being made with three water-cooled copper plugs. Figs. 2 and 3 show the arrangement. The crucible, made

Jan 1, 1951

By W. M. Albrecht, W. D. Klopp, R. I. Jaffee, B. G. Koehl

Kinetic studies were made of the reactions of tantalum with oxygen, nitrogen, and air at 400o to 1500°C. The tantalum-oxygen reaction is linear from 500° to 1250°C. The tantalum-nitrogen reaction follows a cubic rate law at 400° to 700°C and a parabolic rate law at 800" to 1475°C. The reaction behavior in air is initially parabolic followed by a transition to linear behavior. In the search for high-temperature materials, considerable interest is being shown in the refractory metal, tantalum. It is the third highest melting metal with a melting point of 2996°C. Also, tantalum has excellent ductility, making it one of the most workable refractory metals. In considering high-temperature applications of tantalum, the oxidation kinetics of the metal must be known. Such information also serves as a basis for the development of corrosion resistant tantalum-base alloys. Therefore, this study was made to investigate the reaction of tantalum with air, nitrogen, and oxygen. LITERATURE Several oxides of tantalum have been reported. The pentoxide, Taz05, is the only oxide of tantalum whose identity has been established. A high-temperature modification, aTa2Os, has been reported by several investigators.1-4 A low-temperature phase, ßTa2O5, undergoes an allotropic transformation at 1320o to 1350oC. 5-8 Four other oxides of tantalum have been reported. The oxides TaO2, TaO, and Ta4O have been reported by schonberg.9 A suboxide Ta2O, was observed by Wasilewski 6. However, the presence of oxides lower than Ta2O5 is questioned by Lagergren and Magneli.7 In oxidation studies, vermilyeal0 and Peterson, et al.,12 reported one possible phase intermediate between Ta and Ta2O5. Only Ta2O5 was formed in the tantalum air reaction, as reported by Michae1.l3 Several studies have been made on the kinetics of the tantalum-oxygen reaction. vermilyeal4 investigated the range 50° to 300°C and found that the rate of growth of a thin adherent oxide film could be described by the Cabrera-Mott theory. Gulbransen and Andrew15,18 studied the reaction kinetics of tantalum in oxygen pressure of 1/10 atm at 250° to 450°C. At all temperatures the reaction followed the parabolic rate law for periods up to two hours. The oxidation behavior in the range 500" to 1000°C was found to be linear at oxygen pressures of 0.2 to 600 psi according to Peterson. et al.l1 At very low pressures (1 x 10-3 to 2 X lo-' mm of Hg) Gebhardt and seghezzi17 reported linear oxidation at 800° to 1500°C. The reaction of tantalum with air is similar to the reaction with oxygen. Studies have been made by Waber, et a1.,12 and Michae1.l3 Two nitrides of tantalum, TaN and Ta2N are known. Their structures have been determined by Brauer and Zapp 18,19 The tantalum-nitrogen reaction kinetics have been investigated by Gulbransen and Andrews. 15, 16 The reaction follows the parabolic rate law at 500° to 850°C at a nitrogen pressure of 1/10 ,atm. At the same temperature, the tantalum-nitrogen reaction is much slower than the tantalum-oxygen reaction. EXPERIMENTAL TECHNIQUES Material— The material used in this study was high-purity, electron-beam-melted tantalum obtained from the Temescal Metallurgical Corp. The hardness of the as received ingot was 76 Vhn. The analysis of the material is given in Table I. Methods—Cylindrical specimens of tantalum approximately 0.9 cm in diam and 0.5 cm in length

Jan 1, 1962

By J. H. Bain, D. C. Haigh, L. C. Parsons

Jan 1, 1964

By Stuart S. Forbes

Changes and additions made to the Canadian Copper Refiners Ltd. electrolytic refinery between 1949 and 1955 are reviewed. The effect of high current density on current efficiency and section work is discussed. OPERATING and physical changes which have been made to the electrolytic tank house of Canadian Copper Refiners Ltd. suggest a review of present conditions. Previous papers1 a have described the general arrangement. Since then, expansion, closer anode spacing, and higher current densities have increased annual cathode capacity from 112,000 to 182,000 tons. A recent extension to the tank house, begun in the spring of 1954 and completed in August 1955, was undertaken to handle the monthly production of about 3,000 tons of anodes from Gasp6 Copper Mines. The anticipation of these additional receipts and large stocks of unrefined copper caused by the increase in custom smelting at Noranda made it necessary to increase production without immediately available additional cell capacity. Accordingly, from December 1954 through March 1955, the tank house was operated successfully at a current density of 24.0 amp per sq ft. Again, as of September 1955, one of the two tank house circuits is being operated at this high density. Although other refineries may operate at current densities higher than 24 amp per sq ft, none is doing so with anodes which contain silver and gold content as high as those being refined at Canadian Copper Refiners Ltd. General Arrangement The original building consisted of two parallel bays, each 660 ft long and 60 ft wide, with a 24 ft pump bay extending along the west side of the building. A previous expansion, completed in 1939, was to the west of the original building and consisted of two 60 ft parallel bays 240 ft long. The length of these two bays was extended in 1954 to 540 ft, adding one stripper and 12 commercial sections to No. 2 electrical circuit. Space is still available for an additional six commercial sections and one stripper section. Construction on these seven sections started in September 1955, and will be completed early in 1956. The tank house capacity will then be 206,000 tons of cathodes per year. In the two tank houses there is a total of 900 cells distributed as follows—commercial, 468; stripper, 36; total, 504 in the No. 1 tank house (No. 1 circuit): commercial, 360; stripper, 36; total, 396 in the No. 2 tank house (No. 2 circuit). Section arrangement consists of nine cells to a tier and two tiers or 18 cells to a section. Anodes, weighing 620 lb each, are cast with a Baltimore groove and are refined by the multiple system. Solution enters each cell through a bottom inlet at one end and overflows at the top of the opposite end. Rate of solution flow through the cells is controlled by valves at each section to 4.5 gpm. Electrical power to the tank house is now provided by nine 675 kw motor generator sets. Each set consists of a 135-12 v 5000 amp dc generator, driven by a 980 hp 2300 v synchronous motor. When No. 1 circuit is operated at 22,000 amp, five sets, at 4400 amp each, are connected in parallel. As the maximum allowable current on No. 2 electrical circuit has recently been set at 18,000 amp, only four sets are connected in parallel on No. 2 circuit. A tenth set, now being installed, will be reserved as a spare, for use in either circuit as required. Recent Changes In 1949, the annual capacity of the tank house was increased from 112,000 to 132,000 tons by closing the

Jan 1, 1957

By Ling Yang, John Henderson

Self-diffusion coefficients of copper in molten copper have been measured by the capillary reservoir method in the temperature range 1140o to 1260°C. The results can be represented by the equation D = [(1.46 * 0.01) x 10-3) exp [(-9710 * 710)/RT] cm2/sec. The energy of activation agrees within the limit of experimental uncertainty with that for viscous flow. The relationship between the diffusivity and coefficient of viscosity is best described by the equation D = kT/4pnr cm2/sec. MEASUREMENT was made of the self-diffusion coefficient of copper in molten copper in the temperature range 1413º to 1533ºK, using the capillary reservoir technique and CU64 as the radioactive tracer.The procedures for filling the capillaries, making the diffusion run and evaluating Dcu from the counting results were the same as described previously.1,2 All experimental operations involving the melt were carried out in a purified argon atmosphere. A graphite crucible, enclosed in a McDanel tube, was used as a container for the melt because of its satisfactory nature as a refractory material and the low solubility of carbon in copper. Graphite was also used for the capillary material. A McDanel thermocouple sheath, to which graphite radiation shields were affixed, was used to hold the capillaries. By moving this sheath through a rubber seal at the top of the McDanel tube, the capillaries could be lowered into or raised out of the melt. A Globar furnace with a constant temperature zone (± 2°C) of 2 in. was used to heat the assembly. The temperature of the furnace was the equilibrium value corresponding to a given setting of the transformer. Temperature was measured with a Pt-10 pct Rh/Pt thermocouple and varied during a run

Jan 1, 1962

By A. G. Starliper, H. Kenworthy, A. Ollar

Vapor pressure determinations were made on synthesized germanium sulfides. Germanium and cadmium were removed from sphalerite concentrates by fuming. The fume was retreated to separate some of the cadmium from the germanium and, at the same time, upgrade the germanium to more than 5 pet content. MANY sphalerite concentrates contain certain impurities which have economic value as byproducts. These may include the volatile sulfides of germanium, cadmium, and lead. The objectives of the research reported in this paper were to study the fundamental volatility characteristics of germanium sulfides, to increase the recoveries of ger-

Jan 1, 1957

By G. T. Engel, W. G. Gruzensky

Jan 1, 1960

By I. Cadoff, E. Miller, K. Komarek

Jan 1, 1960

By B. C. Allen, W. D. Kingery

Surface tension and its temperature dependence have been determined for pure liquid Fe, Cu, Co, Ni, and Sn and for Fe-C, Co-C, and Ni-C alloys. The temperature coefficient of surface tension is negative for all these liquids. The surface tension and wetting behavior of tin and tin-titanium alloys on A120,, Si,N,, MoSi,, and Sic, as well as the behavior of titanium-containing nickel alloys on A1 20, have been determined over a wide temperature range. For all the solids investigated titanium additims markedly lower the contact angle. Some limits for the solid-surface energies have been calculated from liquid surface tension and wetting behavior. SURFACE tension and interface energy are important variables in a number of metallurgical and ceramic phenomena, and have been discussed at some length in connection with determining micro-structure of polyphase systems,' solid-state sintering,' thermal etching of grain boundaries, heats of solution and fine powders,'1 grain-growth phenomena,' the mechanical behavior of fine foils and fibers, nucleation, soldering and brazing,' and other phenomenz of academic or practical interest However, until recently few quantitative data have been available for high-temperature systems. Among available data are some indicating positive temperature coefficients for the surface tension of liquid copper,*,11,'2 cast iron,l3 and iron-carbon14 alloys. Although carbon was found to be not surface active in iron at 1570" some preliminary studies had indicated the possibility of a positive temperature coefficient for the eutectic composition at lower temperatures.16 One part of the present study has been largely concerned with determining the temperature coefficient of surface tension for several metals at elevated temperatures, In addition to surface-tension studies, the wetting behavior of alloys containing titanium has been investigated over a wide temperature range. Previous measurements indicated that titanium was selectively adsorbed from nickel at a liquid nickel-solid alumina interface,17 and the use of titanium hydride or titanium-alloy techniques for metal-ceramic soldering is well known. In the present study, previous data have been extended to new alloy systems, and measurements have been carried out with other oxidation-resistant ceramics. EXPERIMENTAL The sessile-drop method was employed to measure liquid surface tension and contact angle between liquid and solid, utilizing apparatus and techniques which have been described previously.'g The shape of a sessile drop depends on equilibrium between forces of surface tension tending to form a spherical surface of minimum area and forces of gravity tending to flatten the drop. Typical sessile drops are shown in Fig. 1. From precise measurements of maximum drop diameter and drop height the surface tension and drop volume were calculated. Four solid materials were employed as supporting plaques for the liquid-metal drops. Aluminum oxide (99.9 pct, J, T. Baker, reagent grade) was pressed and sintered at 1800°C. Molybdenum-disilicide powder (99.0 pct, Electro Metallurgical Co.) was pressed and sintered at 1650°C. Plaques were cut from silicon carbide (99.4 pct, hot-pressed at Alfred University) and silicon nitride (95.1 pct, with Al, Fe, 0 as major impurities, Norton Co.) rods. All plaques were polished, cleaned, and dried prior to use. A number of metals and alloys were employed. Chemical analyses of vacuum-melted ingots of iron, nickel, cobalt (National Research Corp.), commercial nickel-base alloys, electrolytic copper (International Smelting and Refining Co.), and tin (Mal-linckrodt Chemical Works) are given in Table I. Alloys were prepared in the laboratory by vacuum melting the base metal with either titanium hydride (Metal Hydrides, Xnc.) or spectroscopic-grade carbon (National Carbon Corp.). Nickel-titanium alloys contained between 0.001 and 0.005 pct oxygen and the ferromagnetic metal-carbon alloys contained 0.001 pct. Cylindrical metal specimens (1 to 2.5 g) were machined and bevelled at the bottom to insure a uniform advancing contact angle on melting. Before use the samples were acid-etched, cleaned with acetone, and rinsed in petrol ether.

Jan 1, 1960

By R. E. Boni, G. Derge

SURFACE tensions of molten silicates are of metallurgical importance for many reasons. From a knowledge of their values, an insight into the problem of liquid slag structure can be gained. Also, such problems as separation of slag from metal, slag penetration of refractories, spreading of enamel coats on metals, bonding of cutting wheels, adsorption of gases, frothing of slags, and homogen-ization of slags are related to the surface tensions of the silicates. Because of the absence of a correlated review of the work that has been conducted in this field, the following survey is presented. It is not a complete summary of all the surface tension studies of silicates but only a review of the literature which is pertinent to metallurgical applications and research. Liquid Surface Tension The surface of a liquid differs from the interior in that its particles (ions, atoms, or molecules) are not

Jan 1, 1957

By Ove Sandberg, Olav Bowitz

The operational characteristics of the Soderberg vertical spike anode are briefly discussed stressing the importance of the flow properties of paste in the fluid zone, the thermal shrinkage in the carbonizing zone, and the surface disintegration in the consumption zone. The requirements for paste recipe and binder quality are combined with design and operation of cell. A low temperature susceptibility of viscosity and low thermal shrinkage of paste together with a low microporosity of the binder coke are important properties. PRACTICAL application of Soderberg's idea of a selfbaking carbon electrode proved successful just before 1920. Shortly after, experimental work was started with the aim of developing a continuous electrode that could be adopted as anode in aluminium reduction cells. The intermittent operation of a large number of small prebaked anodes made the idea of developing a continuous anode for electrolytic production of aluminium especially tempting. Moreover, the electrode consumption in this process, even on a theoretical basis, is very high. Many installations were carried out in the 1930's and during the Second World War. During the tremendous post-war expansion of the aluminium industry, the Soderberg electrode has been steadily more widely adopted. Thus, today more than 60 pct of the Western World's output of aluminium is produced in cells with selfbaking anodes, see Big. 1. The quality of the anode paste of Sfiderberg elec- trodes is considered a major factor influencing the specific carbon consumption. The purpose of this paper is to survey the fundamental requirements which must be met in order to obtain good anode operation. We have limited this paper to a discussion of Elektrokemisk's research on the vertical spike type anode. I) FUNDAMEKI'TALS OF ANODE CARBON PERFORMANCE A) Brief Introduction. The only practical method for producing a conductive carbon anode of the size required is to form and carbonize a mixture of a carbonaceous binder and a precalcined dry aggregate coke. In the Soderberg electrode, the forming and carbonization take place in the electrolytic cell

Jan 1, 1962

By Charles L. Mantell, Kurt Straler

The hydrogen reduction of Cr2O3 to chromium metal was found to be feasible at very low water-vapor concentrations, corresponding to dew points of -38° to -24°C, over a temperature range of 1130" to 1490°C. Hydrogen reduction under these conditions was predicted by the calculated equilibrium curves which also indicated that CrzOs is reduced directly to chromium without forming the intermediate oxide, CrO. This reduction path was confirmed by X-ray diffraction analysis. The percent reduction of Cr2O3 at each reaction temperature was constant with time, suggesting an inhibiting effect of water vapor. A small increase in the residual water-vapor concentration of a single temperature, 1490°C, strongly retarded the rate of reduction This effect was expressed by an empim'cal equation which indicated a direct relationship between "distance from equilibrium" and the rate of reduction. me effect of temperature over the range of 1130" to 1490°C was expressed in an Arvhenius plot of log rate vs reciprocal absolute temperature. From this curve the apparent enthalpy of activation was found to be 29,600 cal. Based on the hypothesis that the rate of reductiun is contvolled at the oxide-metal interface, an over-all rate equation consistent with the experimental data and the thery of absolute reaction rates was formulated. A simplification of this expression to an Arrhenius equation was justified by the overriding effect of temperature on the rate of reaction for the minimum water-vapor concentration range. MOST of the metals in Subgroup V1 of the periodic table can be prepared commercially by direct reduction of their oxides by hydrogen or carbon monoxide, at temperatures considerably below the melting points of both the metals and their oxides. Chromium is an exception, being generally reduced from its ore, Cr2O3 . FeO, by silicon in an electric arc furnace which operates above the melting point of the Fe-Cr alloy or above the melting point of chro- mium if a chromium oxide be the starting material. In reduction of chromium oxide by hydrogen, either reduction does not occur at all or the rate of reduction is extremely slow. Theoretical considerations based on the high, exothermic, free energy of formation of Cr2O3 compared to the oxides of the other Subgroup VI metals, molybdenum, tungsten, and uranium, would also suggest a slow rate of reaction and a high activation energy. Interest in the direct gaseous reduction of fine-powdered ores in fluidized beds was considered justification for examination of this reaction. In order to develop a basis for a continuing study of the commercial feasibility of the direct gaseous reduction of chromite, a study of the kinetics of the reduction of Cr2O3 with hydrogen was undertaken. To the authors' knowledge no accurate kinetic data for this reaction have been obtained. Neither has an activation energy been determined nor has an attempt been made to establish a mechanism of reaction. LITERATURE Maier10 compared the data of I. Y. Granaat,6 H. von Wartenburg and S. Aoyama, and G. Grube and M. Flad7 with that derived from calorimetric and ther-modynamic properties for the equilibria for the reduction of Cr2O3 with hydrogen. These results, plotted as the log of the equilibrium constant vs absolute temperature for the reduction of Cr2O3 and the intermediate oxide, CrO, to chromium, show agreement between the differently derived data. In both cases the equilibrium constants were extremely low. Maier showed that, over a temperature range of 1000° to 2000°K, Cr2O3 is more readily reducible than CrO. Granat assumed that CrO was preferentially formed from Cr2o3 above 1100°C. Grube and Flad's analysis of their reaction products in the 895" to 1000°C range indicated the coexistence of only Cr2O3 and chromium. The hydrogen reduction of the other Subgroup VI metals, molybdenum, tungsten, and uranium, shows that reduction of the higher oxide proceeds through all of the intermediate oxides before being reduced to the metal. Since evidence pointed to an anomaly in the reduction behavior of Cr2O3, the authors investigated the reduction path of Cr2Os.to chromium. This was done theoretically with more recently available free-energy data and experimentally by X-ray diffraction analysis. This work reinforces Maier's conclusion.

Jan 1, 1964

By R. W. Kewish

The preparation of massive uranium metal containing very low concentrations of a number of light elements by bomb reduction of UF4, with calcium is described. Details of procedures are given for preparing high-purity ingredients for the bomb reduction. The as-reduced uranium metal contained, on the average, less than the following amounts of light element impurities, in ppm: Li, 0.1; Be, 0.1; B, 0.1; C, 25; 0, 70; Na, 1; Mg, 3; Al, 2; and Si, 7. Other impurities for which the metal was examined averaged, in ppm: Ca, < 10; V, < 10; Cr, 2; Mn, 6; Fe, 50; Co, < 5; Ni, 8; and Cu, 1. THE preparation of very high-purity uranium metal in massive form for research purposes is of great importance. Recently the kilogram-scale preparation of uranium metal containing less than 70 ppm of detected impurities was accomplished by Blumen-thal and coworkers by vacuum remelting of high-purity crystals of uranium obtained by fused salt electrolysis.1"3 Albert and coworkers4 have reported successful experiments in lowering the concentrations of certain impurity elements in uranium, notably iron, to a few ppm by the zone-melting method. The present paper describes the preparation of high-purity massive uranium metal by the bomb reduction of UF4, with calcium. Early in 1951 a program was undertaken at the Los Alamos Scientific Laboratory to prepare uranium metal of very high purity with respect to a number of the light elements. The methods considered for this purpose were 1) bomb reduction of a uranium halide with calcium, 2) electrolysis of fused salts, and 3) hot wire decomposition of UI4, The first of these processes had been used extensively at Los Alamos since 1943 (and still is used) for the production of uranium metal.5 In considering the three processes it was evident that either of the last two would require an extensive development program with no certainty of success. On the other hand, a study of available data showed that uranium metal of very high purity with respect to some light elements had occasionally been made in routine processing by the first method. It was therefore decided that an intensive study of the bomb-reduction process would be made to see if it could be improved to yield uranium metal with very low concentrations of light elements. DEVELOPMENT OF PROCEDURES The bomb-reduction process used at Los Alamos consists of reducing UF4 with calcium, using iodine as a booster. The reaction is carried out in a magnesium-oxide crucible enclosed in a steel bomb. Argon is used in the bomb to avoid objectionable side reactions which would occur in the presence of air. All ingredients for this bomb-reduction process were examined as possible sources of light elements. It was known that high-purity UF4 was required. The calcium used in the reductions was a source of carbon and magnesium. The magnesium-oxide crucibles were sources of boron, silicon, and magnesium. The iodine did not appear to be a source of any impurities. Pure UF4- The UF4 for bomb reduction is prepared from U3O3 , by successive reduction to UO2, with hydrogen and hydrofluorination of the UO2, with anhydrous HF. Since it was known that no impurities were normally introduced during the gas-solid reactions, effort was directed toward the preparation of high-purity U3O3. Of the many possible procedures for the purification of uranium solutions the following were investigated: 1) Precipitation of uranium peroxide. (Two procedures were tried. The first consisted of simultaneously adding hydrogen-peroxide and ammonium-hydroxide solutions to a uranyl-nitrate solution, containing citric and malonic acids, at such relative rates that precipitation was carried out at a constant pH of 1.5 The second consisted of simultaneously adding uranyl-nitrate, ammonium-hydroxide, and hydrogen-peroxide solutions to an aqueous solution

Jan 1, 1960

By W. J. Kroll

Jan 1, 1960

By Frank E. Woolley, Robert D. Pehlke

Jan 1, 1965

By Thomas C. Wilder

Jan 1, 1965