By Kazutoshi Haga, Atsushi Shibayama, Altansukh Batnasan

"The aim of this study was to develop a hydromellurgical processing for removal of arsenic from high-arsenic copper sulfide ores and concentrates, providing increase in copper recovery. In this study, three different enargite ore samples containing 28.2–46.7% copper, 1.9–15.0% arsenic and 10.6–27.5% iron were used to determine optimum conditions for the extraction of copper and removal of arsenic. High pressure oxidative leaching process was preformed using various leaching reagents such as sulfuric acid (H2SO4), ferric sulfate (Fe2(SO4)3), hydrochloric acid (HCl), ferric chloride (FeCl3), sodium sulfate (Na2SO4), sodium chloride (NaCl) solutions and distilled water (DW), respectively, under the fixed conditions which were selected to be as follows: NaCl concentration, 0.34 M; concentrations of other leaching reagents, 0.1 M; particle size, -45 ?m; pulp density, 100 g/L; agitation speed, 750 rpm; leaching temperature, 160 ?C; leaching time, 60 min and total pressure (oxygen gas and vapor pressure) into an autoclave, 1 MPa. Results show that under the leaching conditions, more than 90% of copper leaching was achieved with lower than 2% arsenic content as a consequence of the formation of arsenic precipitates in a solution of Fe2(SO4)3–NaCl. It was determined that copper, arsenic and iron concentrations in the pregnant leach solution were 42 g/L, 0.3 g/L and 0.3 g/L, respectively. As a result, it can be concluded that the Fe2(SO4)3 solution in the presence of NaCl or FeCl3 are more efficient leaching media compared to other leaching agents under the high pressure oxidation conditions, because of their high copper recovery and lower arsenic level in the pregnant leach solution.INTRODUCTION Generally, copper is usually produced from copper sulfide ores by a combination of several processes which are flotation and smelting followed by refining [1-3]. Arsenic content in copper sulfide ores tends to increase due to the depletion of high grade copper deposits, hence conventional mineral processing and metallurgical processes cannot effectively treat these ores containing high levels of arsenic to obtain consistently high purity copper concentrates. Because high levels of arsenic in copper ores/flotation concentrates reduces the value of concentrates due to the restriction of smelting process and causes it to be a source of environmental pollution [4-6]. From this point of view, the known way of prevention against high-arsenic copper sulfide concentrates in further metallurgical treatments is to develop economically and environmentally competitive technologies for removal of arsenic impurity from copper sulfide ores before treating the ores/flotation concentrates by the pyrometallurgical routes."

Jan 1, 2018

By Markus A. Reuter, Yongxiang Yang, James R. Post

The packed coke bed in the lower part of an iron making blast furnace, the dead man, dissolves slowly in a pool of hot metal, which is tapped regularly. The coke particles of the dead man not only exhibit a size distribution, but also their size distribution is non-uniform throughout the dead man and as a result, the porosity of the dead man is non-uniform. This causes the flow of hot metal through the dead man to be irregular and non-uniform, bringing about channelling in the coke bed. Channelling is detrimental to the refractory lining life of the hearth of a blast furnace. Using population balance modelling and a porosity model it is possible to keep track of the local changes in size distribution and bed porosity during dissolution of coke particles. Numerical simulations show that carbon dissolution from a packed coke bed (with particles which exhibit a size distribution) increases the average porosity, decreases the mean particle size and changes the size distribution to a distribution with a smaller size range. Influence of the type of initial size distribution (mean, variance) is investigated. The calculated changes in porosity are used to dynamically adapt the flow and the mass transfer (kinetics) during calculations. This approach provides the possibility to implement dynamic porosity calculations for CFD applications, and thus simulate the results of various coke types and particle size distributions on dissolution and flow behaviour.

Jan 1, 2003

By Markus A. Reuter, Joep Verwoerd, Marc J. A. Pijnenborg, Yongxiang Yang

"Incineration is a proven disposal technology for all waste materials with heat release potentials, and provides high degree of toxic destruction and control for a broad range of hazardous materials. In the Netherlands, all the hazardous wastes are processed at AVR-Chemie located at the Rotterdam harbour, through rotary kiln incinerators. The newly enforced regulations from the European Union with stricter emission levels require a better understanding of the incineration process and improved process control. However, the transport phenomena and combustion processes within the kiln system are very complex and not well understood. In order to get better understanding of the incineration process, research has been carried out to study the fluid flow and combustion behaviour of the incineration system. Computational Fluid-dynamics (CFD) was used to simulate the gas flow and waste combustion process, and temperature measurements of the operating rotary kiln incinerator were conducted to validate the CFD model. This paper will present the latest results from the current research project for simulating gas flow and combustion heat transfer for a wide range of hazardous waste streams.The simulation of the waste incineration process was carried out using a general-purpose CFD code Phoenics. The rotary kiln and the secondary combustion chamber (SCC), with a waste processing capacity of 50,000 ton/y and an energy input of 30 – 40 MW, is translated into a CFD model. The model includes a k-e turbulence model and a global gas-phase combustion model (3-gas or 7-gas combustion model). The 3- gas model (Simple Chemically-Reacting System, SCRS) predicts only the thermal effect of the fuel combustion, and only one global fuel is used, therefore, real chemical species are not taken into account. In the 7-gas combustion model, (an Extended SCRS, ESCRS), different forms of waste fed into the incinerator have been modelled into a mixture of a general hydrocarbon fuel C3H4 and other components such as CO, CO2 and H2O. Thus, all the incoming fuel streams with different compositions and calorific values can be properly converted into separate inlets. The combustion of the waste is assumed to take place only in gas phase in two steps: (1) primary combustion of the main fuel component C3H4 to form CO and H2, (2) secondary combustion of CO and H2O to form CO2 and H2O. The rate of each combustion reaction is assumed to be controlled by turbulent mixing of fuel and oxidant (air or oxygen), i.e. the Eddy-Break-up (EBU) model. The resulted temperature field was validated with temperature measurement data, and the simulated temperature distribution from both 3-gas and 7-gas model have reasonable agreement with the measured data."

Jan 1, 2003

By I. Blayda

The purpose of this work is to study and make comparative analysis of germanium extraction and related valuable components of the sublimates from the burning of domestic power coals (product 1) and germanium sulfide materials, which are a waste of lead-zinc production (product 2), by traditional chemical methods (distillation of germanium in the form of tetrachloride from raw and preliminary burning source) and by microbial bioleaching of sulfur-oxidizing bacteria. The dependence of the germanium extraction by chemical methods from phase composition of the initial raw materials was installed. The germanium tetrachloride extraction from products 1 and 2 were 78.50 and 19.52%, respectively. Such difference in indexes on extraction, is caused by germanium confinement as concomitant trace component to the basic phases to carriers. The share of acid-non-soluble compounds (tetragonal modification GeO2 and silikogermanaties) in the product 1 account for 21.5 % of germanium. Ratio between acid-soluble and acid-not -soluble germanium forms are 19.52 and 80.48 %, respectively, in the product 2. Our experiments have shown, that implementation of restorative firing (with addition of 30-40 % carbon at 1150 0?) of sulfide product 2 considerably impacted on the extraction of germanium tetrachloride (91.76 %) in comparison with its low enough extraction at straight distillation of hydrochloric acid (19.52 %). The results are confirmed by a set of physical methods. The results of processing the same so-called hard phase?s material (product 2) with the help of microorganisms are presented. It Has been established, that selected strains of bacteria are capable of extracting from initial raw materials not only macro components (iron, zinc, lead, manganese, aluminum, nickel), but also micro impurity of rare metals (gallium, germanium, zirconium). It is important that these metals were not extracted by traditional chemical methods (with application of aggressive conditions and heats) independently of the phase composition of the source. Almost complete extractions of germanium in solution using sulfur-oxidizing bacteria take place in the first day of the process independently of the phase composition of the source and the type strain. The results have practical significance and can be the basis for developing a unified biotechnological method of technogenic waste processing with a purpose of their sterilization and detoxification with simultaneous obtaining concentrates of valuable metals. Keywords: germanium, extraction, sublimates, bioleaching, sulfur-oxidizing bacteria.

Sep 1, 2012

By M. Alvarez-Silva

The control of the amount of chromite reporting to the concentrate during the flotation of UG2 ore is of critical importance since its presence affects the downstream smelting process. It is generally reported that the main mechanism responsible for chromite recovery is through entrainment. This is reflected in analyzing the solids and water recoveries. These in turn are strongly dependent on the froth phase. In the present investigation a laboratory scale column flotation cell was used to investigate the role of the froth phase in the flotation of UG2 ore. Such a device is superior to a standard batch cell since it operates at steady state in open circuit and also allows for a greater degree of flexibility in terms of froth heights. The mass of solids and water recovered in the concentrate as well as chromite (Cr2O3) recovery by size class was determined as a function of froth height, superficial gas velocity and depressant dosage. The results showed that depressants had little effect on chromite recovery but increased the grade due to the depression of gangue minerals. A 60cm froth height always resulted in slightly lower solids, water and chromite recovery than for 30cm. Typically only 20-25 % of solids reaching the pulp-froth interface reached the launder. The relationship between solids and water recovery for a wide range of conditions indicated that chromite is mostly recovered by entrainment. Keywords: UG2 ore, column flotation cell

Sep 1, 2012

By Y. E. Brylyakov, M. A. Kostrova

"The apatite staffelite ores (ASO) of Kovdor deposit are dominated by fine-grained aggregates containing both phosphate minerals and silicates — vermiculite, smectites, zeolites. These minerals exhibit ion-exchange properties. In this connection, the magnitude of cation exchange, along with the content of P2O5 and CO2, is an important property of apatite staffelite ore, which largely determines the performance of concentration processes. In the examined ASO samples, the magnitude of cation exchange measured in terms of Ca2+ is 2546-4790 g/ton. The conducted laboratory studies of apatite staffelite ores with various mineral composition showed that adding calcined soda improves the recovery of P2O5 into the flotation concentrate. Full-scale tests were conducted at the apatite staffelite ore processing plant at Kovdor Mining and Concentration Operation and demonstrated the high performance of the proposed agent treatment. The test results showed that in the flotation of apatite staffelite ores, the optimum calcined soda feed rates range from 3,500 to 5,000 g/ton of the flotation feed. With close flotation feed and concentrate grade parameters, the P2O5 recovery gain is 17%. The effect of adding soda is associated with the desorption of the hardness cations from the minerals, precipitation in the pulp and, accordingly, improvement in the ionic composition of the liquid phase of the flotation feed due to a reduced content of calcium ions. Based on the test results, the proposed agent treatment with an elevated feed rate of calcined soda was implemented at Kovdor Mining and Concentration Operation in the flotation of apatite staffelite ore. The apatite staffelite ores (ASO) of Kovdor deposit are dominated by fine-grained aggregates containing both phosphate minerals and silicates — vermiculite, smectites, zeolites. These minerals exhibit ion-exchange properties. These minerals have certain properties requiring a more detailed examination for a better understanding of the flotation properties of apatite staffelite ores."

Jan 1, 2018

By Felix M. Zhuravlev, Vitalij P. Lyalyuk

"While there is a large industry based on recovering platinum group metals (PGM) from complex sulphide ores containing Cu and Ni, there is little information on the thermodynamics of the matte phase formed on smelting the ore and in particular the behaviour of Pt in the matte.The equilibrium between metallic platinum and industrial mattes was studied in a series of experiments where a small quantity of matte (5g) and platinum foil of 150 µm thickness (0.5 g) were equilibrated in magnesia crucibles at 1400°C under conditions where the oxygen and sulphur partial pressures were controlled.The chemistries of the phases were determined from EDS analysis using a scanning electron microscope. Line scans were initially used to confirm that the foils had attained a uniform composition across their thickness. The composition of the matte was determined from analysis of an area of matte including the small metallic droplets and dendrites.The distribution of Pt in Cu-Fe-Ni mattes (Pt: 1.5 – 3%) and solid Pt alloys (Pt: 54 – 72%) was studied. For a matte of base composition 45%Fe, 11%Ni, 8% Cu, at a base temperature 1400°C, the following behaviour was observed for the Pt distribution ratio:Under the range of sulphur and oxygen pressure of this study (log pO2 from -15 to –12.2, log pS2 from – 4.6 to –2.2), the distribution ratio of Pt between matte and alloy was independent of the sulphur and oxygen pressure, having a value of 0.04.The Pt distribution ratio increased from 0.02 to 0.08 with temperature from 1340 to 1450 oC.For mattes where the proportions of Cu and Ni were kept constant, a slight decreasing trend was shown for the distribution ratio of Pt versus the iron content (37 to 53%) in the matte but was not confirmed because of experimental uncertainty."

Jan 1, 2003

By Steven Wright, Sharif Jahanshahi, Shouyi Sun

"While there is a large industry based on recovering platinum group metals (PGM) from complex sulphide ores containing Cu and Ni, there is little information on the thermodynamics of the matte phase formed on smelting the ore and in particular the behaviour of Pt in the matte.The equilibrium between metallic platinum and industrial mattes was studied in a series of experiments where a small quantity of matte (5g) and platinum foil of 150 µm thickness (0.5 g) were equilibrated in magnesia crucibles at 1400°C under conditions where the oxygen and sulphur partial pressures were controlled.The chemistries of the phases were determined from EDS analysis using a scanning electron microscope. Line scans were initially used to confirm that the foils had attained a uniform composition across their thickness. The composition of the matte was determined from analysis of an area of matte including the small metallic droplets and dendrites.The distribution of Pt in Cu-Fe-Ni mattes (Pt: 1.5 – 3%) and solid Pt alloys (Pt: 54 – 72%) was studied. For a matte of base composition 45%Fe, 11%Ni, 8% Cu, at a base temperature 1400°C, the following behaviour was observed for the Pt distribution ratio:Under the range of sulphur and oxygen pressure of this study (log pO2 from -15 to –12.2, log pS2 from – 4.6 to –2.2), the distribution ratio of Pt between matte and alloy was independent of the sulphur and oxygen pressure, having a value of 0.04.The Pt distribution ratio increased from 0.02 to 0.08 with temperature from 1340 to 1450 oC.For mattes where the proportions of Cu and Ni were kept constant, a slight decreasing trend was shown for the distribution ratio of Pt versus the iron content (37 to 53%) in the matte but was not confirmed because of experimental uncertainty."

Jan 1, 2003

By Y. Y. Zhou

This paper introduces the application of CRIMM high-gradient magnetic separator in refinement of feldspar powders as well as the supporting technical outfits needed by the refining process with the high-gradient magnetic separator as main equipment. It could reduce the content of Fe2O3 to 0.03% with a deferrization rate of 85.88% from the feldspar raw ore containing 0.17% Fe2O3by using the above refining technology, producing an ultrapure feldspar product.

Jan 1, 2014

By Haghi. Hamed, Javad Vazifeh Mehrabani, Mehdi Sedigh

In this investigation, the possibility of physical separation methods such as attrition scrubbing, hydro-cycloning and also reverse flotation were investigated for silica and calcite removal from relatively low grade kaolin. The head sample was provided by the Iran China Clay Company and the major oxides contained in the head sample were Al2O3, SiO2, CaO and Fe2O3 with grades of 15.07%, 71.05%, 4.35% and 0.52% respectively. The liberation degree of calcite and iron impurities from kaolin particles were over 80% for particles finer than 210µm and 53µm respectively. Attrition scrubbing tests were carried out with scrubber cell of the conventional Denver flotation cell model D-12. Laboratory scale hydro cyclone was applied for the beneficiation of kaolin. Attrition scrubbing tests with control screen of 106µm did not achieve the desirable yield for purification of this kaolin sample, but hydro cyclone experiments resulted in better results. Hydro cyclone with 2.54 cm diameter used and the only variable was the cyclone inlet pressure ranging from 68.65kPa to 98.07kPa. The best inlet pressure was found to be 68.65kPa. Based on the optimized condition, Al2O3 and CaO amount in the hydro-cyclone overflow was 23% and 1.47% respectively. However weight recovery of the overflow in each cyclone experiment was less than 30% and multi stages of hydro-cyclones would have to be applied for higher weight recovery and better yield. All of the flotation tests were carried out in the conventional Denver flotation cell model D-12. Reverse floatation tests for calcite removal were carried out under alkali pH based on full factorial design of variables in 2 levels including one center point. The three parameters tested were collector dosage (gr/ton), pH and depressant dosage (gr/ton). The collected data from flotation tests were analyzed and optimized collector and depressant dosage were 1000 gr/ton and optimized pH was 8.5. Under the above mentioned conditions, calcite removal was about 75% and CaO content in the final product was reduced from 4.35% to 1.33%. However calcite removal will increase to more than 83% if the feed particle size in flotation tests is reduced from 210µm to finer than 53µm. Finally after optimization, the best working condition and possible flow sheet were developed.

Jan 1, 2014

By Hiroshi Sasaki, Herman D. Mendoza

"The surface-chemical property of nickel slag fiber was modified in aqueous media in order to act as an active and efficient collector of colloidal amorphous silica from geothermal effluent. Colloidal amorphous silica (0.05 µm) from geothermal wastewater causes operational and ecological problems. It clogs geothermal pipes and waterways, and when disposed to the environment poses hazardous effects on both the flora and fauna ecology. Because colloidal amorphous silica is extremely fine and remains in suspension in aqueous media, conventional solid/liquid processes to remove colloidal silica from its bulk liquid are rendered ineffective.A rapid separation technique is then developed to remove effectively amorphous colloidal silica from its bulk liquid by attaching the extremely fine particles of silica onto a nickel slag fiber coated with magnesium hydroxide, Mg(OH)2. The nickel slag fiber has the following characteristics: a high surface area and predominantly possesses negative charge in aqueous media with an iso-electric point at pH ~2.5. When soaked and saturated with Mg(OH)2 solution, the surface of the nickel slag fiber becomes coated with fine and compacted Mg(OH)2 precipitates. This modifies the surface- chemical property of nickel slag fiber transforming the negatively charged surface into a positively charged surface in aqueous media with an iso-electric point of around pH 11.8, which corresponds to the iso-electric point of Mg(OH)2. When geothermal effluent containing negatively charged colloidal amorphous silica particles (i.e.p. of silica is pH 2) is passed through a column-bed packed with surface-chemically modified nickel slag fibers under natural pH conditions, the colloidal amorphous silica particles are recovered by attachment onto the surface of the surface- modified nickel slag fiber. The recovery of colloidal amorphous silica by attachment is 97-99%, resulting in the production of a relatively clean and silica free output. Aluminum hydroxide, Al(OH)3, was also used to modify the surface –chemical property of the nickel slag fiber. In the same way, it also exhibited a positive response with the collection of colloidal amorphous silica from its bulk liquid, but yielding a lower recovery of 90%. This may be attributed to the lower surface potential and iso-electric point of pH 9.3 for Al(OH)3. The separation process was evaluated and analysed using existing potential energy theories. Figure 1 shows a micrograph of the surface of an unmodified and the Al(OH)3 –modified surface of nickel slag fiber."

Jan 1, 2003

By T. Ueda, T. Oki, S. Koyanaka

"Accurate assessment of the liberation state of crushed ore particles is important for efficient mineral processing. In general, the liberation state is assessed by two-dimensional (2D) measurement of polished ore sample sections. However, this 2D measurement inevitably suffers from overestimation of the degree of liberation, known as stereological bias. This arises from the fact that biphase particle sections of which only one phase happens to have been cut are indistinguishable from liberated particles. To date, several stereological correction methods have been proposed, but their applicability for various types of particles has not yet been sufficiently examined, and this tends to undermine their practicality. We have addressed this problem using a numerical-analytical approach in which various types of biphase particles are modeled, and the 2D sectional information is compared with actual three-dimensional (3D) information. Through simulations, we revealed a general relationship between the internal mineral structure of particles and the stereological bias. Finally, we have developed a unique stereological correction method in which the texture (a 2D pattern characteristic) of particle sections is used to estimate the internal structure of particles, and thereby the stereological bias. KEYWORDS Mineral liberation, stereological bias, texture analysis INTRODUCTION Mineral liberation assessment of 2D particle sections inevitably suffers from stereological bias; that is, overestimation of the degree of liberation. Stereological bias is caused by the fact that a composite particle can be misidentified as a liberated particle when only one phase happens to have been cut in sectional measurement. Stereological bias has attracted attention since Gaudin pointed out its importance in 1939 (Gaudin, 1939). Several attempts have been made to measure the 3D liberation state directly, avoiding the bias, using X-ray computed tomography (Gay and Morrison, 2006; Lin and Miller, 1996; Miller et al., 2003; Miller et al., 2009; Reyes et al., 2017; Videla et al., 2007). These have provided useful information through laboratory testing, but further technical refinement is necessary for practical usage, to overcome the technique’s limitations in terms of resolution, assessment of minerals of similar density, and speed. Therefore, for practical purposes, detailed information regarding mineral phase geometry is obtained by sectional analysis, using automated scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDX)-based analysis (e.g., with a mineral liberation analyzer (MLA) (Fandrich et al., 2007; Sandmann, 2015)); and the development of an effective method of stereological correction, which predicts the relevant bias and transforms the measurable 2D degree of liberation into its 3D counterpart, is an important research aim."

Jan 1, 2018

By T. Suzuki

Acid leach liquors from spent lithium-ion batteries employing lithium cobalt dioxide (LiCoO2) as a cathode active material contain valuable metals such as cobalt and lithium, as well as common metals such as aluminum and copper. The objective of this study was to develop a hydrometallurgical process providing a high selectively between aluminum, cobalt, copper, and lithium from hydrochloric acid solutions. Batch experiment results showed that selective hydroxide precipitation approach was not suitable because a significant amount of cobalt and lithium was co-precipitated with aluminum and copper hydroxides. In contrast, batch experiments and the subsequent data analysis indicated that the sequence of solvent extraction circuits using PC-88A, Acorga M5640, and tri-n-octylamine (TOA) extractants effectively separates four metals of interest. In the first circuit of the proposed process, copper was selectively extracted by Acorga M5640 at the pH 1.0-2.0. Aluminum, cobalt, and lithium remain in the aqueous phase. In the second circuit, aluminium is selectively extracted by PC-88A at pH 2.0-2.5. For the separation of remaining cobalt and lithium, Acorga M5640 provided higher separation efficiency compared to PC-88A single extractant and PC-88A/TOA mixed extractant. However, the stripping efficiency of cobalt from the Acorga M5640 organic phase was found to be low (less than 10 %). Therefore, PC-88A/TOA mixed extractant rather than Acorga M5640 is an advisable choice for the separation of cobalt and lithium. Keywords: spent lithium-ion secondary batteries, solvent extraction, lithium, cobalt

Sep 1, 2012

By N. T. Beukes, W. Banda

Recovery of Co from slag is a recent advancement in the extractive metallurgy of nonferrous metals. In this study a DC arc technology at laboratory scale has been applied to investigate the selective recovery of Co from slag, under three different flux types with an emphasis on influencing the activity of FeOx, SiO2 and CoO in the slag. It is known that reduction of slag by carbon is only up to a certain level after which, the recovery will depend on the chemistry of the slag, hence the need to modify the slag chemistry. Two power settings were employed to induce higher temperatures and aggressive agitation. The results were interpreted by comparing how much Co and Fe was in the slag and alloy. TiO2 reduced the amount of Fe in the product alloy compared to when CaO and CaF2 were used. The change in power did not seem to have had a major effect on the recovery although the amount of material lost to flue dust was more at a higher power rate.

Jan 1, 2003

By Robert Dunne

A review of the current ?state of the art? of refractory gold treatment will be provided. This will include a global perspective of the refractory processes that are being practiced, where they are and some discussion on why the processes were selected. Some discussion on the challenges that face the refractory gold industry will also be provided.

Sep 1, 2012

As a leading global company in the mining sector, we are committed to sustainable development. To this end, we invest in the responsible, integrated management of economic, environmental and social issues. Vale?s objective is for our businesses to produce local, regional and global prosperity, enabling the construction of a positive legacy throughout the lifecycle of our activities. This covers everything from talking with stakeholders and preventing failures to complying with legislation, paying constant attention to environmental issues and respecting ethics in business. Keywords: sustainable development

Sep 1, 2012

By M. M. Fan

In Florida?s phosphate industrial practice, the most favorable upper size limit of froth flotation is 1.18 mm which corresponds to particle weight of about 2.8 mg. Conventional froth flotation is not efficient in upgrading coarse particles (+0.425-1.18 mm). A limited number of studies have been devoted to understanding and improving coarse particle flotation. We have shown that the coarse particle flotation performance can be significantly improved by the presence of picobubbles generated by hydrodynamic cavitation. In this study, the size of picobubbles produced under certain hydrodynamic conditions was measured by a laser particle size analyzer. A size-by-size flotation performance analysis of coarse phosphate froth flotation in the presence of picobubbles is conducted in terms of flotation kinetics, selectivity and recovery. It was found that picobubbles doubled the flota-tion rate, increased the P2O5 recovery more significantly for +0.85-1.18 mm particles than +0.425- 0.6 mm and +0.60-0.85 mm particles. At a given acid insolubles (A.I.) rejection, the presence of picobubbles increased the P2O5 recovery by up to about 25%.

Jan 1, 2014

By V. K. Gupta

Selection of mill size for reducing a feed material of a given size to the desired product size is generally based on the specific energy estimate obtained from Bond test. Over the last thirty years or so, an attempt has been made to develop a more accurate and powerful alternative approach based on the characterization of the particle breakage kinetics and material transport through the mill over a range of operating conditions of interest and correlating the degree of size reduction achieved with the net specific energy input to the mill. Particle breakage kinetics are described in terms of the specific grinding rate and breakage distribution parameters for the individual size fractions. Precise estimates of these parameters and the net energy input to the test ball mill (a laboratory or pilot scale mill) are important for development of desired energy-size correlations. In this context, three tasks are important: (a) preparation of the feed charge, (b) design of batch grinding experiments and (c) computational technique used for estimation of the breakage rate and breakage distribution parameters. This paper highlights several aspects of these three tasks that have been overlooked by researchers working in this field, and describes a more appropriate approach for estimation of model parameters and specific energy input. Several examples are included based on the data available in the literature and those generated in our laboratories to illustrate important points.

Sep 1, 2012

By Alain Broussaud

The lecture is about the growing role and the evolution of advanced process control (APC) in the mining and mineral processing industry, taking into account major trends in Information Technology. It reflects the standpoint of a team, which has already successfully developed APC technology for more than 20 years. Advanced process control systems tend to rely on combinations of artificial intelligence techniques or algorithms that complement each other and cooperate. Each technique or algorithm makes it possible to use certain type of knowledge about the process, so that the advanced control systems benefit at any time from the combined knowledge of process and control engineers and plant operators, from knowledge derived from past research work and process modeling, from a considerable amount of data provided by advanced instrumentation in real time, and from knowledge that can be extracted automatically and at any time from past data and images. The lecture will first review and compare the role, merits and limitations of algorithms that are used for online decision making in mineral processing plants: expert systems, fuzzy logic, neural networks, soft sensors, optimizers, and MPC controllers. The lecture will also review the role of online image analysis and sound analysis in process control. Recent developments in this area open new dimensions, in particular the ability for advanced process control algorithms to automatically explore the past, move back and forth in time in order to make better informed decisions, and the ability to cooperate with the operators for better performance. Applications will be presented. Recent progress in process simulation makes it possible to design, configure, check, and pre-tune APC systems before plant startup, opening new options for implementing APC. In conclusion, the author will share his experience about the key ingredients for sustainable success in APC Keywords: mineral processing plants, APC, MOC controllers

Sep 1, 2012

By Hemant Nerurkar

The destination of human development journey is envisioned as human well being. Human well-being is the extent to which individual share the ability and the opportunity to live the kinds of lives they value it includes environmental security, good health and living conditions, all of which are closely related to each other. The breakthroughs, which transformed the human race, have close interdependency with the environment. With the increase in world population, the requirement of natural resources is increasing every day. The nature is still stronger than man is but we must use natural resources more responsibly. The key to our well being is sustainable development Development effort for human well being may have adverse impact on the environment also. To keep the net impact positive is critical for sustainable development. For mineral processing industry, the value of a mineral is in the actual value as perceived by the end user. The process designs, investments in technology development all have direct relationship with the value of use and making a net positive impact on our ecosystem The value proposition has shifted towards raw materials and is a big differentiator. The availability of good quality raw material is difficult or is available at a premium. The challenge today is to develop green technologies that make effective and efficient usage of low grade raw materials The low grade raw materials as available pose a significant opportunity for human race for delivering value. They offer an easier reach to a value as perceived in end use but the journey is full of challenges. The first challenge is development of technology for maximizing grade recovery as required by the downstream process. The second challenge is to make the technology viable so that it contributes value to end use and the third challenge is to keep the net impact of the process positive The mining and mineral processing fraternity, being at the beginning of this value chain is set to take the first step in this journey for a tryst with ultimate human well being. Keywords: sustainable development, challenges in mineral processing

Sep 1, 2012