By W. G. Davenport, M. Paneni

Experiments in sheets of mercury and water have confirmed that the dynamics of bubble rise are simi-lur in Liquid metal and aqueous systems. RECOGNITION that bubble/metal interactions are important in pyrometallurgical refining processes (e.g., steelmaking, vacuum degassing, deoxidation of copper) has led to a number of investigations into the dynamic behavior of bubbles rising in liquid metals. Terminal velocities of bubbles rising in mercury (20°C)' and silver (1000" to 1050"c)1,2 have been measured. Good agreement between aqueous and liquid metal systems has been obtained. Shapes of air bubbles rising in mercury have been determined experimentally by Davenport, Bradshaw, and Richardsonl who used a system of electric probes to measure maximum horizontal and vertical dimensions, Fig. 5. In the present work the motion and shape of nitrogen bubbles rising in a thin sheet of mercury (i.e., a "two-dimensional" environment) have been studied with the view of confirming dynamic similarity between aqueous and metallic systems. The use of thin sheets of liquid permitted direct visual and photographic comparisons of bubble behavior in clear liquids and in mercury. EXPERIMENTAL METHOD The thin sheets of mercury or water were held in a clear acrylic plastic container, Fig. 1. The sheets of liquid were 80 cm high by 30 cm wide and 0.47 cm thick. Single bubbles were formed by injecting the desired volume of nitrogen into an inverted semicircular cup (stainless steel). The cup was then rotated into the upright position using an external handle thus releasing a single bubble of measured volume. Nitrogen was injected into the cup from a nitrogen cylinder through the external handle and a hollow rotating axle. The volume of a bubble (volume range 0.01 to 10 cu cm) at any instant was obtained by connecting a soap film meter to a small gas space above the liquid. By this technique any change in the volume of a gas bubble in the liquid (i.e., during cup filling or during rise) produces an equivalent displacement from gas space A into the buret B. This displacement is determined by measuring the movement of a horizontal soap film in the buret. Bubble shapes were determined using single-frame photography. Rising velocities were determined by cinephotography with a 1/100-sec stopwatch in the field of view. In both cases dimensions were referenced to a rule attached to the container surface, also in the field of view. Linear dimensions were measured on projections of the single-frame negatives. Rising velocities were calculated from measured heights of rise (10 to 20 cm) and times of rise. The effects of disturbances caused by cup rotation and by bubble release were minimized by photographing bubbles at a point not less than 25 cm above the cup. MATERIALS Mercury: Technical-grade purified: minimum 99 pct Hg; Johnson Matthey and Mallory Limited, Toronto. Nitrogen: Technical-grade purified nitrogen: 99.99 pct Nz, 0.01 pct 02, trace argon; Air Liquide Canada Limitee, Montreal.

Jan 1, 1970

By R. M. Goldhoff, J. W. Spretnak, R. Speiser

IT has been observed by Grange and Garvey' that the homogenization of boron-treated steels could lead to complete elimination of the hardenability effect caused by boron. The experimental conditions leading to this conclusion involved the heating of steel specimens with and without boron at 2350°F for 24 hr. To prevent oxidation and decarburization, the specimens were encapsulated under vacuum in silica tubes. This observation of permanent deterioration of boron effect was noted in both a 0.63 pct plain carbon steel and a 0.25 pct C low alloy steel, both of which had been treated with ferroboron and homogenized at 2350°F for 24 hr. In another series of boron-treated steels which had been homogenized for shorter times, the effect was to reduce, but not completely eliminate, the boron effect. Under these circumstances, it was presumed that longer heating times would cause permanent deterioration of the boron effect in this series of steels also. Since the characteristic grain boundary constituent could not be formed in any of these steels after homogenization, it was concluded that possibly boron was being converted into an ineffective form through chemical combination resulting from prolonged heating at high temperatures. Assuming the validity of this observation, a series of experiments to establish the relationship between temperature of homogenization and kinetics of deterioration was contemplated. Initially an attempt was made to reproduce the results just described. For this purpose commercial lots of AISI 8640 and AISI 86B40 steels were used. The analyses of these steels appear in Table I. Hardenability evaluation was on the basis of the hardness of normalized sections. Grange and Garvey' pointed out that these steels are air hardening to some extent and such a technique can be used. For these tests the specimens were held for 20 min in a salt bath at 1600°F and then cooled in still air. Several evacuated silica capsules containing pairs of the test steels were made up and heated for 24 hr at 2350°F. A number of failures occurred among these capsules, but evaluation of the specimens successfully treated indicated a complete deterioration of the boron effect. However, examination of the surface of the treated specimens showed that some reaction, probably with the silica tube, had taken place, since none of the specimens was bright. One further test was made at 2350°F for 12 hr, using a pair of specimens wrapped in tantalum foil prior to encapsulation. These specimens appeared bright after treatment, and their hardenability evaluation showed that no deterioration had taken place. Since these steels are extremely sensitive to de-boronization at high temperatures and particularly at long times of holding, the experimental observations raised some doubt as to the real occurrence of the permanent deterioration effect. To resolve this question an experiment was undertaken in which the high temperature portion of the treatment was completed in vacuum. For this purpose a molybdenum wound resistance furnace capable of maintaining good vacuum was used. All the pertinent accessories to this furnace were machined from molybdenum stock in order to withstand the high temperature involved in the experiment. With this equipment a temperature of 2400 °F was obtained and held under a pressure of 5x10-" mm Hg for 24 hr. A specimen of each of the two test steels was suspended in the furnace and both were heated simultaneously. Temperature was measured with a standardized Pt—Pt-13 pct Rh thermocouple, whose millivoltage at 2400°F was extrapolated from the standardization equation, good up to 2200°F. The complete evaluation of these specimens is shown in Table 11. The hardness values attained by each steel after normalizing, both before and after the prolonged high temperature treatment, remain the same. A microscopic study of the decomposition products present in the microstructures of specimens at various points in the heat treatment correlated with the hardness values observed. It seems that no permanent loss of boron hardenability effect occurs, at least in these Grainal-treated steels, when deboronization is circumvented. Acknowledgments This work was conducted under the sponsorship of the Aeronautical Research Laboratory, Wright Air Development Center, under Contract No. AF 18(600)-94, and their support and permission to publish is gratefully acknowledged. A note of thanks is also extended to the Republic Steel Corp. for supplying the materials used in the work. References ' R. A. Grange and T. M. Garvey: Factors Affecting the Harden-ability of Boron Treated Steels. Tro.ns. ASM, 1946, vol. 37, p. 136.

Jan 1, 1957

By Thomas T. Read

IN reviewing the field of mineral industry education last year reference was made to recent assertions, mostly emanating from sources not in a position to know the facts, that mining engineers as a class are disappearing. Attention might also then have been called to a statement that appeared in Engineering News, August 11, 1892 (p. 130), ". . . the great absolute decline in number of mining graduates, which last amounts almost to a complete abandonment of mining engineering as a distinct branch of study." Evidently we outrank opera stars in the number of farewell appearances we are able to make; 43

Jan 1, 1936

By Roshan B. Bhappu, Zeki M. Dogan

Two magnesite ores containing 3.15% and 8.73% SiO2 and a calcined magnesite product assaying 2.6% Si02 were first reduced in size to -20 mesh by roll crushing. 'They were then treated dry on a high intensity magnetic separator to reduce their silica content by rejecting iron-stained silicate minerals in the magnetic fraction and obtaining marketable magnesite or calcined magnesite as a nonmagnetic product.

Jan 1, 1975

By Bedrand L. Johnson

THE phosphate-rock industry is built upon natural deposits of rocks and minerals in which the element phosphorus is present as a phoshate. The term ?phosphate rock? is a general one, applied to certain rocks of different degrees of consolidation and of diverese origin, charater and occurrence, composed of intimate mixtures of several phosphate minerals, largely submicrocrystalline, usually calcium phosphates, in commerical quantities, with various impurities. This term includes phosphatized limestones, sandstone, shales, and igneous rocks; nodular phosphates ; residual weathered phosphatic limestones ; vein phosphates ; and phosphatic sediments, both consolidated and unconsolidated.

Jan 1, 1944

This discussion was prepared by members of the Phelps Dodge Corpn. staff who were designated to review the minutes. It is confidential but permission has been granted to distribute copies among those who attended the Conference. The minutes of the above conference contain numerous references to the plants and practices of Phelps Dodge Corporation. As many of these references are inaccurate, the following notes are made covering such points: Construction Magnesite Brick in Reverb. Arch (1) An.18" arch, 20 feet long, was built on one furnace with 5 feet on each side of magnesite brick, the center portion .being of silica brick. The furnace was put in operation February 13, 1930 and on April 23rd after 68.8 days' operation it was replaced due to failure of the silica brick forming the center of the arch. At this time, while the silica brick had completely gone, there was 14" of magnesite left. Bridgewall Tapping (2) Tapping matte through the burner wall was first tried at the Copper Queen Smelter in April, 1925. At that time, a copper casting with 1 ½ extra heavy pipes for water cooling cast in it, and having one taphole block was used. Later, on the other (old) furnaces, similar castings, but equipped with two tapholes, were used. We found with these furnaces that we could tap through the burner wall at the beginning of a campaign, but would subsequently have to go back to side wall tapping. This was the case until sometime in 1926. The new furnaces, that went in operation at the beginning of 1927, each had water. cooled castings with two tapholes. These have been used entirely and have been quite successful. Sometime after the furnaces were put into operation sidewall tapholes were put in, simply for the removal of any accumulation of matte that might be temporarily retained at the front end by bridges or dams in the furnace formed by overcharging locally.

Jan 1, 1930

By Herbert H. Kellogg

The chemistry of sulfide roasting is analyzed to show those aspects of performance which Thecan be predicted from considerations of thermodynamic equilibrium. It is concluded that equilibrium calculations can serve as a yardstick for prediction of roaster-gas composition and sulfate formation in the calcine for fluid-bed roasting practice. A method of calculation which combines the equilibrium and stoichiometric factors is outlined, and illustrated by an example from the roasting of Cu-Fe sulfides. ON first examination the roasting of sulfides would not seem to be a process to which equilibrium calculations could be applied to yield results of practical value. The burning of sulfides is an ex-tremely spontaneous reaction, excess air is always used to obtain rapid reaction, and in most traditional roaster designs (hearth roasting) the temperature and gas composition vary widely from point to point in the roaster. These are all conditions which promote a non-equilibrium state in the roasting process. However, the introduction of the fluid-bed roaster1 has brought to roasting practice new conditions of operation, so that equilibrium calculations can be used to predict certain limited aspects of practical operation. The fluid bed is characterized by uniformity of temperature, gas composition, and calcine composition from point to point throughout the bed. These relatively uniform properties of the bed make the meaningful calculation of the equilibrium state of certain reactions in roasting possible. It is the purpose of this paper to analyze roasting from an equilibrium viewpoint, to show where the method may be expected to yield valuable information, where it fails, and to outline methods of calculation. Main Roasting Reaction The reaction MS (s) + 3/2 0, = MO (s) + SO, [I] might well be called the main roasting reaction. It adequately accounts for the well known facts that metal sulfide and air are the main reactants, and metal oxide and SO, the main products. Deviations from this simple stoichiometry will be discussed under side reactions. For all metal sulfides, Reaction 1 is strongly exothermic and the equilibrium position is far to the right. Since the reaction is exothermic, the equilibrium shifts in the right-to-left direction as the temperature is raised. However, at all practical roaster temperatures (between 500" and 1200°C), the amount of this shift is small, and the equilibrium position remains far to the right. The main roasting reaction is essentially irreversible, and the application of equilibrium considerations to this reaction will not be! a fruitful field of investigation. A knowledge of the rate of this reaction. although not the proper subject of this paper, is of great importance to the roasting process. Analysis of the factors which influence this rate shows that: 1) The rate will increase rapidly with increased temperature. 2) The rate will be proportional to the partial pressure of oxygen at the surface of the reacting particle. Because of diffusion effects, the partial pressure of oxygen at the particle surface may be considerably less than in the bulk of the roaster gas. For this reason, intimate contact between gas and solid and high relative velocity between gas and solid, such as can be obtained in a fluid bed or flash roaster, will markedly increase the rate of reaction. 3) The rate will be proportional to the surface area of metal sulfide. Therefore, smaller particle size will permit a more rapid rate per unit of weight. To achieve practical rates of roasting the partial pressure of oxygen in the roaster gases must be maintained at a finite level at all times. Even where the gas-solid contact is very good, as in the fluid-bed roaster, the oxygen content of the gas must not be allowed to drop below some limiting value (perhaps 1 pct), or the rate of the main roasting reaction will become too small for practical operation. Side Reactions in the Gas Phase The gas phase during roasting of metallic sulfides contains the elements oxygen, sulfur, nitrogen, by-

Jan 1, 1957

By William L. Saunders

Many members of the Institute, who participated in the visit made, during the Bethlehem meeting of February, 1906, to the shops of the Ingersoll-Rand Company, at Phillipsburg, N. J., inspected with interest the new Electric-Air drill, which the company had set up for the purpose of showing it in actual operation to American mining engineers. At the request of the Secretary of the Institute, I promised at that time to prepare a paper for our Transactions, describing the construction and advantages of the machine. But such a paper would then necessarily have contained much that was only expected or claimed by the designers and manufacturers of the drill, and not yet incontrovertibly proved by varied and long-continued practice. However moderate such statements might have been, they would have given inevitably to the paper, to some extent at least, the air of a prospectus, rather than of a technical contribution. I therefore decided, with the Secretary's approval, to postpone the writing of the promised paper until it could set forth the results of adequate actual practice, as well as the latest details of construction, etc., based upon practical experience. That period has now arrived. The Electric-Air drill has been exhaustively tested in the field, under varied and arduous conditions and upon the hardest rocks. It is now fairly in the field; its merits and performances are matters of unimpeachable record, and its place among established competitors can be definitely determined. As a representative of the Ingersoll-Rand Co., as well as a member of the Institute, I may be permitted to add that my company, being largely interested in the manufacture of air-coxpressors and machinery driven by compressed air, has no desire to injure its own business by claiming for this new machine that it should immediately supersede all existing applications of pneumatic transmission of power for drilling. On the

Jan 1, 1908

By David B. Burrows, Francis R. Conley

INTRODUCTION A prerequisite to the evaluation and management of oil properties is accurate information derived from the analysis of core samples; but reliable data, such as porosity and permeability, can result only if all oil and water have been removed from the core samples analyzed. The most common method of core cleaning used to date has been Soxhlet extraction—a somewhat static technique, which depends upon the slow diffusion of hot solvent through the core sample. Soxhlet extraction performs satisfactorily only with highly permeable samples and at best requires long cleaning periods. The centrifuge method was developed in 1951 by Continental Oil Co. to overcome the inefficiencies inherent in the Soxhlet method. The new method is basically an operation in which hot solvents are caused to flow through the samples under the influence of centrifugal force. The centrifuge unit has proved so successful that samples which formerly required days for partial extraction can now be completely cleaned in approximately one hour. The original idea was conceived in 1950 by Elmer S. Messer, whose early experiments consisted of flowing solvent over sandstone samples suspended in a revolving basket and driven by a vertically mounted vacuum cleaner motor. Results were so outstanding that more permanent units were constructed. A modified model using this basic design was recently built by Core Laboratories, Inc., and is now used regularly in their operations. DESIGN Fig. 1 shows a photograph of the two extractors routinely used to clean small core plugs in the Production Research Div. of Continental Oil Co.'s Ponca City laboratories. For illustrative purposes, the basket from one of the units has been removed, and because both extrac- tors are of identical design only one is described in the following discussion. Each extractor unit consists of a centrifuge and a solvent still. The core basket of the centrifuge is made of mild cold rolled steel 7 1/2 in. in diameter and 1 1/8 in. deep. The basket holds 18 1-in. samples (cubical or cylindrical) and is attached directly to a cone fitted to the shaft of the motor. Both the outer rim and the hollow hub of the basket contain perforations for the passage of solvent and extract. The solvent is delivered to the perforations by means of a copper tube inserted into the hollow hub. The motor is a vertical tool post grinder motor; (115 v, 5.6 amp, 0-60 cycles, AC-DC, rated at 1/3 hp). It has a rated speed of 10,000 rpm under full load and 15,000 rpm with no load. Variation of speed is obtained by the use of a variable transformer. The solvent still was constructed from one end of a stainless steel oxygen bottle by inserting a heating element, sight glass, and piping as shown on the schematic diagram, Fig. 2. The heater used was a three-position, 1,000 w, 115-v, immersion type. Intermittent flow of solvent to the centrifuge is obtained by means of a siphon bottle inserted between the condenser and the centrifuge.

Jan 1, 1957

By Jerome F. Kuzmick

Condusions. From the work on aluminum powder, the following general con clusions can bc drawn: I. The physical properties of aluminum compacts, such as density. strength and ductility, increase with increasing pressure, up to the practicable pressure limits. 2. Good properties ill aluminum con pacts can be secured only by the use of high pressures, because it is neccssary to rupture the refractory oxide film on aluminum powder. 3. Considerable softening of the specimens occurs upon sintering. regardlers of the pressure used. General Conclusions 1. For relatively short-time sintering. molding pressure is a very important factor in the final physical properties of the sintered specimens. 2. The effect of pressure. is difierent for each metal, so that few general rules can be drawn that would apply to all metals. 3. In many cases, fur a particular metal powder and sintering temperature there is a critical pressure at which the best physical properties can be obtained. 4. The principles of cold work and in nealing and their effect on grain structure applied to massive metal also holds true for sintered metals. 5. Particle size, at least for electrolytic iron powder, does not have a. great effect on ultimate grain six. DISCUSSION [E. E, Schumacher presiding V.. V. Crane. *—I was particularly impressed with Dr. Kuzmick's work on tin IF not the illustration, particularly the Second one. a very good illustraition of hot preessing. in that

Jan 1, 1945

By A. W. Schlechten, R. P. Abendroth

Jan 1, 1960

By J. B. Clark

In 1933, R. paris1 published a phase diagram for the entire Mg-Ca-Zn system. He reported the existence of a ternary intermetallic phase, Mg5Zn5Ca2, which formed a quasi-binary with the magnesium solid solution. Since then, no extensive work has been reported on the system. Recently however, indications of the existence of a second ternary in-termetallic phase in equilibrium with the magnesium solid solution led to a reinvestigation of the solid phase equilibria involving the magnesium solid solution. The 335°C (635°F) isothermal section was chosen for study. Metallography and powder X-ray diffraction were selected as the best mutually corroborating methods for determining the solid phase constitution. Seventy-six alloys were prepared from singly sublimed (99.95 pct) magnesium, electrolytic (99.95 pct) zinc and USP calcium. The analyses of some of the alloys are shown in Fig. 1. The alloys were melted in a graphite crucible under a chloride flu and chill cast in a split graphite mold. Dif-fusion couples (see Fig. 2) were prepared by casting molten Mg-20 wt pct Zn alloy around a cylinder of Mg-30 wt pct Ca alloy. The alloy samples and the diffusion couples were sealed under argon in Pyrex vials and annealed in a furnace capable of controlling within 1/2°C of 335°C. At the conclusion of the anneal, the alloy samples were quenched in ice water and the diffusion couples were air cooled. Procedures standard for magnesium alloys were used for metallographic examination. Powder X-ray diffraction patterns were taken on a G. E. camera with a 14.32 cm dim using nickel-filtered copper radiation. The redetermined 335°C (635°) section of the Mg-Ca-Zn phase diagram is shown in Fig. 1. TWO ternary intermetallic phases, designated w and

Jan 1, 1962

By C. F. Lucks, W. D. Wood, H. W. Deem

Electrical ad thermal-conductivity measurements have been made on titanium and 6 titanium alloys. The following expression was derived for calculating thermal conductivity from electrical conductivity: K = 0.626 s T x 10-8 + 0.00497 where K = thermal conductivity, cal sec-1 cm-2 cm0C-1 s = electrical conductivity, ohm-]cm-1 T = temperature, deg Kelvin This expression gives calculated thermal conductivities that are not in error by more than 10 pct from the experimental values for A-55 titanium and the 6 alloys measured; namely, A-110AT, C-110M, C-130AM, Ti-6A1-4V, Ti-140A, and Ti-155A, which are representative of the presently available commercial a and a-ß titanium alloys. THERMAL conduction in a gas, liquid, or amorphous solid is accomplished by energy diffusion from molecule to molecule, a relatively slow process. For this reason, such materials have a low thermal conductivity. When a material is crystalline, there is in addition a heat transfer by a vibratory motion of the crystal lattice. It is the contribution of this lattice conduction that makes a crystal a much better conductor than a gas, liquid, or amorphous solid. Lattice conduction, however, does not account for the relatively enormous thermal conductivity of a metal. This is explained by the freedom of movement of valence electrons. These valence electrons drift in a metal in a direction toward a drop in electrical potential and, to a lesser degree, in the direction of a temperature drop in the metal. Since both the electrical and thermal conductivities of a metal depend upon the presence of free electrons, there should be some relatively simple relation between the two. Wiedemann and Franz in 1653 first discovered an approximate empirical relation between the electrical and thermal conductivities of metals at the same temperature. This ratio varies appreciably with temperature, and Lorenz later showed that by adding a temperature factor to the Wiedemann-Franz ratio the value of K/(s T) is constant, where K is the thermal conductivity, a the electrical conductivity, and T the absolute temperature. This Lorenz constant shows a greater variation for alloys than it does for pure metals, the ratio increasing slightly as the proportion of alloying elements increases. It has been found that a closer correlation between electrical conductivity and thermal conductivity can be obtained by means of an equation of the form K - A s T + B [1] where A and B are constants. In this equation the term AsT is the contribution of electronic conduction and B is the contribution of lattice conduction to the total thermal conductivity. EXPERIMENTAL MEASUREMENTS Electrical-resistivity and thermal-conductivity measurements on titanium and 6 titanium alloys serve as the basis for determining an equation of the K = AsT + B type for titanium alloys. Specimens—Table I shows nominal compositions of the 7 metals on which electrical and thermal conductivities were measured. The electrical and thermal-conductivity specimens for each alloy were taken from stock of the same heat and usually from adjacent sections of the same bar. All of the metals measured were in a mill-annealed condition. Methods—Electrical-resistivity measurements

Jan 1, 1959

By D. H. Gurinsky, D. G. Schweitzer

The empirical equilibrium constantsd the heat of reaction for the reduction have been determined from 300° to 500°C. The mechanisms of the oxidation of uranium and magnesium from dilute bismuth solutions have been investigated. The kinetics of some of the reactions were affected by air adsorbed on the uranium oxides. THE Liquid Metal Fuel Reactor studied at Brook-haven National Laboratory uses a solution of uranium in bismuth as the fuel. Corrosion and stability problems require that the fuel solution contain corrosion inhibitors and deoxidants. Of the additives tested, magnesium has been found to be the best deoxidant and zirconium the best corrosion inhibitor in bismuth. Some experiments1 indicate that magnesium may play a secondary role in increasing the effectiveness of zirconium in inhibiting corrosion. The work reported here was intended to determine the relative concentrations of Mg and U required to prevent oxidation of the uranium fuel in the event of an air leak. In addition, an attempt was made to identify some of the mechanisms of the oxidation and reduction reactions occurring in the liquid bismuth solutions. EXPERIMENTAL Apparatus and Procedure—The equipment shown in Fig. 1 was designed so that the reaction kinetics could be studied as functions of temperature, melt composition, pressure, and flow rate. At the start of a run, the 10-liter bell jar (F) is removed by opening the bottom Dresser fitting (L), and the bismuth and additives are placed in a pyrex crystallizing dish (I). The bell jar is replaced, the system is evacuated to 10-5 to 10-6 mm Hg and then the heater (J) is turned on. When the selected temperature is reached, the oxidizing gas is admitted to the system to the desired pressure as read on the manometer (D). Gas is introduced through the slide tube (Q) which has a pyrex frit (R) sealed to its bottom. Stirring is accomplished by immersing the end of the tube in the melt. To maintain a constant pressure under flow the input and evacuation rates must be equalized. To obtain this condition stopcock (C) is closed and flowmeters (B) are matched. The reaction is "stopped" by closing the inlet flowmeter and quickly evacuating the system. To obtain a liquid metal sample, the system is evacuated with the sampler positioned near the surface of the liquid. The sampler, Fig. 2, is then immersed until its thermocouple reading matches thermocouple (G) Fig. 1. The system is then pressurized with helium which forces the solution through the frit. Twenty to 30 min elapsed between the time the system was evacuated and sampled. During evacuation and pressurization of the system, the temperature variations did not exceed ± 5°C. While bubbling occurred the temperature remained constant to within 1/2 oC. The volume of the equipment was determined by adding a known volume of air at atmospheric pressure to the evacuated system and noting the resulting pressure.

Jan 1, 1962

By AIME AIME

DOUBT in anyone's mind that this is the age of metals, industrially speaking, could easily have been dispelled by attending the National Metal Congress in Chicago, Sept. 22 to 26. Iron, copper and aluminum; zinc, lead and nickel, often alloyed with each other or with some of a dozen minor metals, make the materials without which the modern world could not run. Science, pure and applied, is doing marvels in finding new mixtures, new alloys to meet new needs; in developing new means of rolling, fabricating, casting and welding metals cheaply-and effectively. These and related matters were the subject of 100 papers presented at 33 seperate sessions of the organizations that participated in the congress.

Jan 1, 1930

Strain-Hardening Exponent of Cross-Rolled Beryllium Sheet by S. R. Maloff, Vol. 215, No. 5, page 872, was omitted from Table of Contents for the October issue. Stabilization Phenomena in Beta Phase Au-Cd Alloys by Howard Birnbaum, Vol. 215, No. 5, page 786. The figure denoted Fig. 1 should be Fig. 3, Fig. 3 should be Fig. 4 and Fig. 4 should be Fig. 1. The captions are in the proper sequence. Activity of Carbon in Liquid Iron Alloys by Tasuku Fuwa and John Chipman, Vol. 215, No. 4, page 708. First equation, right hand column, page 710 should read

Jan 1, 1960

By Samuel Hoyt

SOME of the more important properties of finished materials are strength, ductility, toughness, resistance to alternating and repeated stresses, etc: Of these, the property that appears to have received the least consideration, at least in this country, is toughness, which is clue, possibly, to our regarding toughness as a qualitative property or, at any rate, as one that, parallels ductility. This arises out of our greater experience with the simple carbon steels in the rolled or forged (non-heat-treated) condition which, qualitatively, are tough if ductile and are not tough if brittle. In this way we have erroneously become, accustomed to judging the toughness of a material from its behavior in the tensile or similar test. The point of view presented in the present paper is that toughness, like hardness or tensile strength, should be regarded as an independent property and of sufficient importance to require, in so far as that may be possible, quantitative determinations. If such be true, it becomes at once necessary to devise experimental means for measuring, or valuating toughness, and the notched-bar impact test (the Charpy test) is advanced as the most logical test that has so far been developed for this purpose. It is further advanced, with particular emphasis, that we have two kinds of toughness to deal with and, accordingly, they will be dealt with independently. CLASSIFICATION OF MATERIALS ACCORDING TO TOUGHNESS Toughness has been defined somewhat as follows: Tough materials are those that offer considerable resistance to permanent deformation but which, once such resistance has been overcome, may' be deformed plastically, but only by the expenditure of considerable energy. In other words; tough materials may be deformed plastically but they absorb a considerable amount of work in the process. This kind of toughness may be called "static" toughness when the rate of loading is reasonably slow or "dynamic" toughness when the rate of loading is

Jan 2, 1919

By R. M. Waterstrat

X-ray diffraction and metallographic examination of binary Mn-rich alloys with Ti revealed the presence of intermediate phases in this system. A binary R phase has been identified and also a phase having an a-Mn type structure. The X-ray pattern of the phase TiMn3 is presented and a tentative phase diagram for the Mn-rich portion of this binary system has been constndcted. MANGANESE-rich alloys with titanium have been subjected to thermal analysis at temperatures down to 1100°C by Hellawell and Hume-Rothery.1 Their results indicate the existence of an intermediate phase TiMn3 in this binary system. This phase appears to coexist with the Laves phase TiMn2, and with terminal solid solutions based on the allotropes of manganese, at least down to 1100°C. The above investigators did not attempt to determine the crystal structure of this phase, however. Since, by analogy to the binary systems Mn-V and Mn-Cr3 one might expect to find a phase in this region of the diagram, it seemed desirable to obtain X-ray diffraction patterns of alloys in the concentration range in question, in order to ascertain whether the sigma phase or related structures occur. EXPERIMENTAL PROCEDURES Alloys were prepared by arc-melting electrolytic manganese and iodide titanium in a water-cooled copper crucible under a helium atmosphere. Excess manganese was added to each melt in order to allow for losses incurred during melting. The alloys were then wrapped in molybdenum foil and sealed in evacuated quartz tubes for annealing at various temperatures, as shown in Table I, followed by quenching in cold water. Although the inside of the tubes showed evidence for some loss of manganese from the specimen during annealing, there was no evidence of any reaction between the specimen and either the molybdenum foil or the quartz tube at these temperatures. It was later found that the manganese loss was considerably reduced by annealing these alloys in sealed quartz tubes containing one atmosphere of purified argon. As an added precaution the surface of each specimen was ground off before crushing the alloys to -270 mesh powder, using a hardened steel mortar and pestle. X-ray powder patterns were obtained using either FeKa or CrKa radiation in an asymmetrical focusing camera, which gave excellent dispersion of the closely spaced lines. Pictures were also obtained using a Debye camera of 5-cm radius which provided data in the angular region not covered by the focusing camera. The alloy specimens were polished and examined metallographically, using an etchant consisting of 60 pct glycerine, 20 pct nitric acid, and 20 pct hydrofluoric acid. The 10-g buttons were in each case broken in half and found to be well-melted and free of any gross segregation. One half of certain alloy buttons was submitted to chemical analysis in the "as-cast" condition. No appreciable change in composition seemed to occur during annealing . RESULTS The X-ray pattern of alloy Ti1.17Mn0.83 was found to agree well with that of the ternary R phase which was first found in the Mo-Cr-Co system,' and re-

Jan 1, 1962

By Eugene R. Rice

There are many methods for determining the meridian, but all of those in common use involve at least two separate observations, one for latitude and one for azimuth. Such observations made upon a south star at any hour are open to the objection of possible inaccuracy due to ignorance of the absolute refraction, and also to slow change in the altitude of the star when near the meridian. The method of observing a circum-polar star at elongation. besides requiring a separate observation for latitude, is open to the serious objection that clouds may obscure the star at the critical moment. Moreover, a tedious wait for the star to come to elongation is sometimes necessary. Many of us can recall 'long, cold, weary vigils, waiting for Polaris to reach elongation. For observing a circumpolar star at any hour, not only the latitude, but also the true time, must be known. This it is practically impossible to obtain, except in regions reached by the telegraph, and usually then one has to know the longitude also, in order to reduce " standard time" to " local time." The results obtained by this method, when the star is at culmination, are not very good, unless the true local time is absolutely known. The methods of obtaining the nleridian from the sun, by means of a solar attachment, or by direct observation, while good, are not absolute, by reason of refraction, change in declination of the sun, and small change in vertical angle, when the sun is near the meridian. For these two methods, latitude, time, and approximate longitude have to be known. In the method here described, only one observation is needed, and from it are computed azimuth, latitude, aud sidereal time. In other words, one call observe a circumpolar star—Polaris

Jan 1, 1911

By K. C. Mills, E. T. Turkdogan

A number of investigators1 6 have noted the presence of a liquid miscibility gap in the Fe-Sn binary system. However, the first attempt to measure the

Jan 1, 1964