By G. L. Watt

Fine sized titanium diboride (TiB2) powders have been synthesized in a thermal plasma reactor. Precursor for the synthesis were rutile, boron oxide, and methane. The effect of plasma gas type, precursor ratio, and input power on the synthesis was studied. The produced powders were characterized by X-ray diffraction and chemical analysis. The purified powders were CIP'd, HIP'd, sintered and characterized for porosity, hardness, and microstructure and the results compared with a commercially available TiB2 powder sample.

Jan 1, 1995

By James T. Skoch

With the ongoing pressure on the secondary aluminum business to limit the amount of waste generated from processing aluminum dross, it becomes very advantageous to preprocess the dross to reduce waste. The advantage of preprocessing is that it significantly reduces the oxides and salt cake generated when melted. Various products can be produced from the oxides for the steel industry. The following paper will demonstrate that removal of oxide fines before melting will result in large volumes of material not being landfilled. We will show that the end result of this technology is to significantly reduce the amount of salt cake sent to a landfill while maximizing the recyclability of the aluminum dross.

Jan 1, 1995

By K. Nona C. Liddell

There is a significant amount of early work that has been largely forgotten that deals with the validity of the pseudo-steady approximation for liquid-solid reactions. Much of this was originally published in the chemical engineering literature but is highly relevant to hydrometallurgical processes. The purpose of this paper is to summarize some criteria that were been developed by various authors for determining the error associated with use of shrinking core models for liquid-solid systems.

Jan 1, 2002

By Petrus Christiaan Pistorius, Ming Tang

Magnetite concentrate is pelletized and then hardened by elevated-temperature oxidation to hematite, to produce pellets for ironmaking. Previous work showed that the rate of oxidation is under mixed control of gaseous mass transfer of molecular oxygen through the pellet pores, and solid-state diffusion into the oxidizing grains. Because of the partially limiting role of solid-state diffusion, concentrate size distribution strongly affects pellet oxidation. Previously, a simple mixed-control model was formulated to describe isothermal oxidation. In that model, the main effect of concentrate size distribution was on the plateau level of oxidation which is reached at a given temperature. However, the extent of plateau oxidation increases with increased temperature, requiring a more complex model for non-isothermal oxidation. In this paper, predictions of the non-isothermal model confirm the strong effects of concentrate size distribution and oxygen enrichment. In particular, a greater fraction of coarse magnetite particles would be beneficial, decreasing the size of the macroscopic unoxidized pellet core.

Jan 1, 2015

By Sedef Pinar Basag, Onuralp Yucel, Ahmet Turan

Niederschlag process is commonly used to produce metallic antimony. The process is a metallothermic process which is conducted in one step for metallic antimony production. Using this method Sb2S3 is mixed with coal and metallic iron and subjected to reduction. During heating, antimony sulfide is decomposed and sulphur combines with iron to form the matte phase. Metallic antimony is collected at the bottom of the crucible. In this study, evaluation of Sb2S3 concentrate, extracted and obtained from West Anatolian Region of Turkey was investigated by using Niederschlag process. The reductant stoichiometry, reduction temperature and duration were carried out in the experiments. Chemical analysis methods by using atomic absorption spectrometry (AAS) and X-ray diffraction spectrometry (XRD) techniques were used for the characterization of the concentrate, metallic nuggets and matte phases.

Jan 1, 2016

By E. A. Werner, W. Liebfahrt, J. Blaha

"The influence of the composition and the microstructure on the plane strain fracture toughness of five cold work tool steels all processed via the powder metallurgical route is investigated using 3-point bending specimens. The steels differ in composition and therefore possess different volume fractions of carbides. The amount, size and distribution of the carbides in the matrix are estimated by quantitative image analysis on a plane parallel to the fracture surface without discrimination of the carbide type, since the carbides are always much harder [1,2] than the matrix, irrespective of their composition. Due to the production of the steels via the powder metallurgical route almost all carbides are spherical in shape. The mechanical in-situ properties of the matrix are characterized by indentation tests performed with an ""UltraMicro"" -indenter in a scanning electron microscope.IntroductionCold work tool steels are used as tools in applications where excellent wear resistance and high hardness are required. Examples are cutting, woodworking, thread rolling, wire and deep drawing, cold extrusion and pressing of parts at process temperatures below 200°C. For such applications the steels must show an optimum combination of hardness, wear resistance and toughness while offering good machinability. Hardness and wear resistance are controlled by the amount of carbon and carbide forming elements such as molybdenum, tungsten, vanadium, chromium and niobium. These elements are present in the MC-, M6C and M7C3-carbides and are also responsible for the precepitation of secondary carbides during tempering. In this report attention is paid to the influence of the primary carbides only, while the very small ~~nm) secondary carbides will be treated as constituent of the homogeneous matrix. Increasing the amount of carbides (alloying elements) usually results in a decrease of the material's toughness which is caused by the presence of clusters and/or bands of carbides. To achieve an optimum combination of hardness, wear resistance and toughness many of the today's cold work tool steels are processed via the powder metallurgical (PM) route, which helps to prevent non-uniform element/carbide distribution because of the rapid solidification of the powders used. The resulting microstructure of the tool steel then consists of a tough matrix with uniformly distributed hard carbides· of globular shape. This shape of the carbides is also desirable instead of blocky carbides present in non-PM tool steels, since they improve the machinability of the steel. An additional advantage of PM-steels lies in the possibility to produce near net shaped tools thus lowering the costs of machining."

Jan 1, 2000

By Xiangru Chen, Honggang Zhong, Qijie Zhai, Qingqing Sun

"A horizontal directional solidification equipment, with an in-situ pouring system, was employed to physically simulate the solidification behavior of continuous casting. In this paper, the 2304 duplex stainless steel (DSS 2304) was investigated using this equipment due to its microstructure produced by continuous casting process was usually not satisfied. The grain size combined with the position of columnar to equiaxed transition (CET) of DSS 2304 were observed and the results showed these microstructure characteristics were very close to those of the continuous casting slabs. In addition, the influences of pouring temperatures and cooling conditions on the CET behavior were investigated. The results revealed that the length of the columnar grains decreased with decreasing the pouring temperatures and flow rates of the cooling water. Besides, the content of austenite decreases with increasing the distance from the chilled sidewall.IntroductionDuplex Stainless Steels (DSSs) have been widely used in industry for their excellent mechanical strength and superior corrosion resistance in Cl- environments when compared with other stainless steels [1,2]. Their good performances are mostly on account of the duplex phase structure-ferrite (d) and austenite (?) and the high proportion of alloying elements. Although, DSSs have good ductility, but worse formability compared to the austenitics, and this is the key to restrict DSSs application [3]. This is due to the differences properties between the two phases. The hot workability of ferrite (d) is better than austenite (?) and exhibits a lower flow stress during hot rolling processing [4]. The early workers had revealed that coalescent force of phase interface, microstructure, difference of mechanical property between two phases and the precipitations are the main factors affecting the formability of DSSs [5,6]. Another important reason that affects the alloy’s mechanical properties is columnar to equiaxed transition (CET) [7]. It often occurs during continuous casting solidification process and induces inhomogeneous mechanical properties and the microstructure varies with different processing parameters, such as pouring temperatures, cooling conditions (water flow rates in the cooling zones) and casting speed [8]."

Jan 1, 2012

By Marta Cabral, C. A. Nogueira, F. Margarido

"Physical processing of spent batteries which includes shredding and sieving operation is the first step for chemical treatment by hydrometallurgy. A laboratory study was carried out to evaluate physical processing efficiency, by analysing the resulting particle size, of alkaline and saline mignon-type Zn-MnO2 batteries. After shredding with a tip shredder, results obtained showed that alkaline batteries were more efficiently size reduced than saline batteries. Difference in particle size distribution was larger for granulometric fraction -20+11.2 mm and also higher for saline batteries. Average diameters (d50) for saline and alkaline batteries were respectively 9.1 and 6.2 mm. Chemical composition carried out on several granulometric fractions allowed to identify metals distribution through size categories. This analysis showed that zinc concentration with the grain size was almost constant, while manganese decreased when particle size increased. More than 95% of iron scarp from the battery cases had a particle size higher than 5.6 mm.IntroductionRecycling process of spent batteries includes physical unit operations which involves a fragmentation step in order to open the battery cases and to allow the access of chemical reactants to the electrode materials, on further chemical unit operations. Shredders are usually used for that purpose, using cutting mechanisms and allowing efficient fracture of residues in order to promote further processing of the contained materials. Batteries are complex products with a large variety of sizes and shapes which causes serious difficulties for predicting and carrying out its fragmentation.Domestic-type batteries are essentially of the Zn-Mn systems and with cylindrical shape, varying from the large size Mono (or D) type to the small size Micro (or AAA) type [1]. Recycling of batteries involves collection, sorting [2] and metallurgical processing [3, 4]. In some processes, the first step of metallurgical processing is dismantling and size reduction by shredding. Research work on spent batteries considering grinding/shredding and physical separation of fractions is scarce [5-7], but investigation in this domain is very necessary."

Jan 1, 2008

By Kiyoshi Takai

The Para-Eco Incinerator Ash Processing System for cleaning slag has been developed after a seven-year pilot plant study. The major part of the system is an electric furnace heated to 1773 K. The feed material consists of a municipal solid waste incinerator ash mixture containing a reducing agent of a coke and an inorganic flux of calcium and magnesium. With this furnace system, three kinds of products are produced. They are an inorganic molten salt that is slag, molten iron alloy absorbing non-ferrous metals, and fly ash. Due to the reducing atmosphere in the furnace, the slag does not contain any metal components as well as chlorine components just like natural rock and/or aggregate. A retreatment plant modifies this slag into a practically useful aggregate. The plant consists of a slow cooling step for crystallizing the slag as well as a water granulation step. The iron components in the ash are reduced to molten iron droplets, which concentrate at the furnace bottom. The non-ferrous metal components such as copper, chromium, and others are absorbed into the molten iron but not into the molten slag. Volatile metals such as lead, zinc, cadmium and others as well as sodium, potassium, and chlorine go back into the fly ash. A solvent extraction method and/or other appropriate procedures can be used to extract the metal components from this fly ash.

Jan 1, 2003

By KAGAN BENZESIK, Onuralp Yücel, Mehmet Bugdaycı, Ahmet Turan

ZrB2 and B4C are one of the most significant advanced ceramics. They are being used in various industrial areas from space technology to nuclear industry owing to their physical properties such as high melting point, high thermal/electrical conductivity and low density. Present study was conducted in two main stages: Self-propagating high-temperature synthesis (SHS) reactions and leaching. ZrO2, Carbon black, B2O3 were used as starting material to produce ZrB2-B4C powders by SHS. Also Mg powder was used as the reductant. The reaction mixtures (approximately 100 g) were mixed thoroughly 15 minutes in a turbula mixer and charged into Cu crucible and compacted. W (tungsten) wire was placed at the top of copper crucible and the reaction realized by passing current through the wire. After initiation, a highly exothermic reaction became in a self-sustaining mode and propagated throughout the SHS mixture. The samples were characterized by using AAS and X-Ray Diffraction.

Jan 1, 2016

By Luben Xie, Lin Hu, Qiang Wang, Min Gan, Tao Jiang, Wenqi Li, Xiaohui Fan, Zhiyuan Yu

"Crystal precipitation behavior of calcium ferrite (CF) during iron ore sintering process along with the effect of cooling rate, SiO2 and Al2O3 on crystalline condensation were studied. The results show that CF, has strong ability of precipitation. The precipitation is barely affected by extenal factors. It begins to precipitate when the liquid phase cools down to about 1200oC. CF could crystallize rapidly at the cooling speed of 150 °C /min. Furthermore, decreasing of the cooling rate favors the development of crystal. Binder phase transformed from CF system to silicate system when SiO2 content was increased to 5~6%, with a constant basicity (R) 2.0. Increasing Al2O3 content could promote the precipitation of CF and the development of crystal.IntroductionCrystalline condensation is the last stage of sinter mineralization. It includes the processes that crystalline substance and amorphous substance precipitate from high temperature solution phase and the consolidation of material when melt cools down. During the crystallization process, minerals precipitate following the order from high to low melting point coupled with the decreases of free energy. Most of binder phase minerals and part of iron oxides crystallize in this process, which have an important influence on mineral composition and microstructure of sinter. They finally determine the sinter strength and metallurgical properties."

Jan 1, 2011

By A. Martins, L. Goulart, E. Araujo, R. Batista, A. Costa e Silva

Steel cleanness is of great importance to the performance of almost all steel products. From very clean steel for bearings to long products used in civil construction, processing variables – in special those in steelmaking operations- must be properly balanced to achieve adequate cleanness for the desired performance. With the present complexity of steels as alloy systems, it is not efficient nor appropriate to develop these processes on empirical basis alone. Computational thermodynamics can greatly improve process development to achieve the desired cleanness level at reasonable costs. In this work, examples of these calculations and their applications to real steel processing are presented and discussed. The advantages, limitations and areas in which improvement in these calculations is desired are highlighted and discussed.

Jan 1, 2015

By T. Ahokainen, J. Pitkälä, J. L. Xia, A. Jokilaakso, J. Vaamo

"The aim of the present paper is to use the two CFD codes to model the two phase flow in a water model ladle with central gas injection. The codes examined are CFX and Phoenics. An Eulerian two phase model is used and predictions are compared against the experimental data available. The results show that the codes can reasonably well predict the gas-liquid plume in the ladle, and predictions are generally in a good agreement with experimental data. However, differences do exist in predicting the gas volume fraction and velocity profiles. The results should be interpreted most carefully and cautiously, because they are very sensitive to the boundary conditions and dependent on the models for the physical phenomena involved. IntroductionSubmerged gas injection has widely been used in the metallurgical industry for more than a century. At the present, the use of gas is most effective in steelmaking industry where the advantages of the gas injection have already been long well understood. Effective mixing, large contact area between reactants, easy modifications and flexibility of the processes are the most important advantages. Disadvantages include refractory wear, blocking in the tuyeres, and splashing. These disadvantages can be reduced and advantages further improved by studying the flow phenomenon in process vessels. However, it is difficult to study flow in a real vessel because of the high temperatures and physical and mathematical modelling is therefore increasingly used in the process development work."

Jan 1, 1999

By Fuqiang Zheng, Yufeng Guo, Pengfei Li, Guanzhou Qiu, Tao Jiang, Andrew Yakovlevich Travyanov

Low content of TiO2 and high impurities content of Ca and Mg are the shortcomings of domestic ilmenite. To meet the requirements of the material in the titania produced by chlorination process and titanium sponge industry, enrichment of ilmenite is necessary. In the process of enriching ilmenite, high temperature and reductive condition were beneficial to the formation of anosovite, but the high content of magnesium oxide which was solid soluble in anosovite baffled the following separation. So the effects of pre-oxidation and reductive conditions including reduction temperature, reduction time and hydrogen concentration on the phase composition and metallization rate were studied. The characteristics of reduction samples were analyzed by X-ray diffraction and optical microscope. Results have shown that the reduction product is mainly composed of Fe, Fe(Mg)TiO3 and TiO2 at 1123K, its metallization rate is about 65%,magnesium exists in Fe(Mg)TiO3.

Jan 1, 2015

By Byung-Su Kim

The recovery of elemental sulfur from sulfur dioxide has important implications for coal- burning power plants and nonferrous metal smelters. The thermodynamic analyses showed calcium sulfide to be suitable for recovering elemental sulfur from sulfur dioxide. At the temperatures of 1023 to 1153 K under the sulfur dioxide partial pressures of 5.0 - 60.1 kPa, elemental sulfur from sulfur dioxide was recovered by its reaction with calcium sulfide. The kinetics of this reaction were measured at the same conditions using a thermogravimetric analysis technique. This reaction scheme would be attractive if the coproduct calcium sulfate can be reduced to regenerate calcium sulfide. This is the topic of another paper. At 1073 K under the sulfur dioxide partial pressure of 25.8 kPa, 48 % of the original calcium sulfide was converted to calcium sulfate in an hour. Under the same conditions, 55 % of the regenerated calcium sulfide were converted to calcium sulfate in an hour even after third regeneration.

Jan 1, 1999

By Sevinc Yildirim, Cigdem Oruclus

"Metal-Porous Silicon (PS) based structures dipped in water show the direct hydrogen fuel cell behavior. The effect of the thickness of the cupper (Cu) film on the electrical properties of direct hydrogen fuel cell is studied by fabricating Cu/Porous Silicon/n-Silicon/Indium structures. PS samples were produced electrochemical etching of n-type single crystalline silicon with a resistivity of 1,25 Ocm and (111) orientation. The thin films of Cu with different thickness between 200 and 600 nm were deposited on PS surface by electron-beam technique. Investigation of the effect of Cu layer on the performance of the structure indicates that the performance parameters such as open circuit voltage (Voc) and short circuit current (Isc) strongly depend on the Cu layer thickness. It was observed that the divice with an 350 nm Cu layer exhibits the highest open circuit voltage (0,5 V), short circuit current (0,01 mA) and power density (10 W.m-2).IntroductionHydrogen is the most attractive and ultimate candidate for a future fuel and an energy carrier. Hydrogen is recognized as the environmentally desirable clean fuel of the future since it can be used directly in different types of hydrogen fuel cells [1]. In the past years, the rise in portable electronics requires the development of miniature fuel cells compatible with standard silicon micro fabrication technology. Most silicon micro-fuel cells have used the polyperfluo-rosulfonic acid membranes (Nafion R) as a proton exchange membranes (PEM) that is not really integrated with standard micro fabrication techniques [2-5]. The composite materials such as inorganicorganic hybrid materials (Nafion-silica, Nafion-borosiloxane etc) are next generation of proton conducting membrane [4-8]. But, fuel cells run on pure hydrogen gas, which can be produced with other energy resources. Hydrogen smallest atom and thus the H2 gas can leak easiliy. The application of hydrogen for power sources has been greatly restrained due to the lack of safe and convenient generation and storage methods.A kind of hydrogen fuel cells Metal-PS-Si structures used as an energy water directly. There is no need pure hydrogen. Cu-PS-Si Schottky-type fuel cells with as proton-conducting membrane and the thin-film cupper catalist and water as fuel, which are interesting for fabrication of lowcost miniature fuel cells. Generation of the open-circuit voltage and short-circuit current has been observed by Cu-PS-Si structure dipping in different hydrogen-containing solution."

Jan 1, 2014

By Laszlo Kadar, J. D. Lavers

"In the continuous casting of aluminum killed steel, the tundish nozzle often experiences clogging problems. Water model studies have shown that the clogging problem is dependent on the flow pattern in the nozzle entry region. In particular, the flow can separate at the entrance to the nozzle, leading to the development of a recirculation region. Although a nozzle can be designed such that no recirculation develops, even a small misalignment from the vertical positioning of the nozzle may render the design ineffective.To reduce the possibility of nozzle clogging, the recirculation zone must be reduced or eliminated. This may be achieved by moving the fluid downwards or raising the turbulence level in the separation region. In the case of a tundish nozzle, it is proposed that this can be achieved by using electromagnetic forces.To generate the required electromagnetic force, two systems are considered. The first is based on injecting a DC current; the second by using electromagnetic induction. Both methods are described in this paper. Order of magnitude calculations are provided to illustrate that both methods are essentially feasible. The performance of each method in terms of modifying the turbulent flow characteristics in the nozzle entry region is then examined using a numerical model. It is shown that both methods can greatly reduce the recirculation zone. A cylindrical nozzle was chosen for the model studies since it represents a worst case situation.On the basis of the model studies, it can be concluded that whereas both of the proposed methods have the potential to reduce the troublesome recirculation zone, the induction method appears to be simpler in terms of practical implementation."

Jan 1, 1999

By N. V. Gorelikova

A new type of zirconium mineralization has been recognized in the Devonian volcanic rocks from an orogenic depression in the Central Kazakhstan. The most characteristic features of this deposit are the fine-grained nature of the zirconium mineralization, an unusual texture of the zirconium ores, and a close association of zirconium with phosphorus in the ores. Zircon grains form fine globular aggregates with the features of hexagonal crystal habit. In addition to crystalline zircon, the ores contain metacolloidal zircon, similar to hydrozircon. The morphological and textural features of the zirconium ores suggest that the deposition of ore deposits took place at a low temperature from colloidal solutions. It is believed that this deposit should be considered to be a new type of zirconium mineralization that is related to low-temperature hydrothermal processes.

Jan 1, 1995

By Sutham Niyomwas

Biomorphic Cellular TiCIC ceramics were produced by vacuum-infiltrating carbon preforms with Ti02 sol and subsequent synthesis by the carbothermal reduction process. The carbon preforms used in the study were obtained by pyrolysis of parawood and neem wood. The effect of infiltration time on the composition and microstructure of the biomorphic TiCIC ceramic was analyzed by X-ray diffractometry and scanning electron microscopy. The biomorphic structure of the TiCIC ceramic is consistent with that of the biotemplate natural parawood and neem wood.

Jan 1, 2008

By Tracy Lucas, Ian Hamill

"Issues of importance in the area of continuous casting centre around product quality. This can be affected by particle inclusions transported into the mould from upstream processes and by draw-down of particles from the meniscus. Turbulence of the meniscus can increase the latter and is also detrimental to product surface quality.Suitably validated Computational Fluid Dynamics (CFD) modelling can provide the operator with an efficient tool with which to investigate the effects of changes to the design and operation of the caster and associated plant.In this paper, examples are presented of the use of the CFD software, CFX, to simulate:•,free-surface shape and turbulence in the mould using deforming meshes•,solidification in the mould using a fixed-grid, source-based method•,argon gas injection through a submerged entry nozzle using a full multiphase model•,inclusion motion and removal in tundishes using an algebraic slip model.The CFD simulations of the free surface shape are complemented by detailed Particle Image Velocimetry measurements performed on a full-size water model of a thin-slab mould and upper strand. Close agreement is demonstrated between the predictions and experiments."

Jan 1, 1999