By L. Russell, van Wert

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By K. J. Gill, P. Chiotti, J. T. Mason

Thermal, metallographic, and vapor pressure data were obtained to establish the pkase boundaries and the standard free energy, enthalpy, and entropy of formation for the compounds in the Y-Zn system. Three coinpounds with stoichiometric formulas of YZn, YZn2, and Y2Zn17 melt congruently at 1105", 1080°, and 890°C, respectively. Four compounds with stoiclziometric formulas of YZn3, YZn4, YZn5, and YZn,, undergo perztectic reactions at 905", 895", 870º, and 685ºC, respectively. Three eutec-tics exisl in this system with the .following eutectic temperatures and zinc contents in wtpct: 875ºC, 23.2 Zn; 1015ºC, 51 Zn; 865ºC, 82 Zn. The YZn, pkase undergoes an allotropic transformation. In the two phase YZn2 -YZn alloys the trans.formation gives a weak thermal arrest at 750°C, whereas in the two phase YZn2-YZn3 alloys no thermal arrest is observed and the transformation occurs over a temperature range below 750°C. At 500°C the free mzergies of formation per lnole vavy from —18,090 for YZn to —53,430 fov YZr11 and corresponding enthalpies vary from -24,050 to -92,080. The free energies and enthalpies per g atom as a function of composition show a maximum for the YZn2 phase; the 500°C values are -9580 and -13,180, vespectively. 1 HE only information found in the literature on Y-Zn alloys was the observation reported by Carlson, Schmidt. and speddingl that Y-20 wt pct Zn forms a low melting alloy. The alloy was produced by the bomb-reduction of YF3 and ZnF2 with calcium in an investigation of methods for producing yttrium metal. The solubility of yttrium in zinc has been determined by P. F. woerner2 and reported by Chiotti, Woerner, and Parry.3 In the temperature range 495" to 685°C the solubility may be represented by the relation In these equations N represents atom fraction of yttrium and T is the temperature in degrees Kelvin. The purpose of the present investigation was to establish the phase diagram for the Y-Zn system and to determine the standard free energy, enthalpy, and entropy of formation for the compounds formed. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in the preparation of alloys were Bunker Hill slab zinc, 99.99 pct pure, and Ames Laboratory yttrium sponge. Arc-melted yttrium buttons contained the following impurities in parts per million: C-129, N-12, 0-307, Fe-209, Ni-126, Mg-13, Ca < 10, F-105, and Ti < 50. Some of the alloys containing 70 wt pct or more of Zn were prepared from yttrium containing 5000 ppm Ti as a major impurity. Tantalum containers were found to be suitable for all alloys studied and were used throughout the investigation. The pure metals, total weight about 30 g, were sealed in 1 in. diam tantalum crucibles by welding on preformed tantalum covers. A 1/8 in. diam tantalum tube was welded in the base of each crucible for use as a thermocouple well. Welding was done with a heli-arc in a glove box which was initially evacuated and filled with argon. The sealed crucibles were enclosed in stainless steel jackets and heated in an oscillating furnace at temperatures up to 1150°C. Homogeneous liquid alloys were obtained within a half hr at these temperatures except for alloys containing less than 20 pct zinc. The latter alloys were held at 1000º to 1100°C for 2 to 3 days in order to obtain equilibrium. After the initial equilibrations the tantalum crucibles containing the alloys were removed from the steel containers and used directly for differential thermal analyses. Further annealing heat treatments for alloys in which peritectic reactions were involved were carried out in the thermal analyses furnace. After thermal analyses the tantalum crucibles were opened and the alloys sectioned and polished for metallographic examination. In the following discussion alloys referred to as "quenched" were obtained by quenching the sealed stainless steel jacket containing the tantalum crucible and alloy in water. The differential thermal analyses apparatus used was a modified version of the one described in an earlier paper., The graphite crucible was replaced by an inconel crucible, the nickel standard and sampie container were separated by a 1/8 in. MgO plate, no getter was used, and provisions were made to

Jan 1, 1963

By Arthur F. Taggart

The major portion of the work described in this paper was performed by R. W. Young, † a graduate student in the department of Mining and Metallurgy, Sheffield Scientific School, Yale University, working under a cooperative agreement between the Hardinge Conical Mill Co., the Sheffield Scientific School, and himself. Since this cooperative scheme is at present in effect in the case of a considerable number of other students in the department and since it is the hope of the school that the privilege thus extended may be utilized even more freely in the future by mining and manufacturing companies, it may not be amiss at this point to give a summary of the general plan. Briefly it is as follows: A graduate student, whose undergraduate work in this or other universities shows promise of ability to handle research work, is chosen by conference between the company and instructor involved. The aim of the company in the agreement then entered into is to obtain the solution of one or more of the technical problems with which it may be confronted, or, at the end of 1 or 2 years, to obtain as an employee a man especially trained in its work. As a means to accomplish one or both of these ends, the company furnishes the machine, apparatus, or material to be tested and pays the student during his graduate work a small salary, usually just sufficient to cover his living expenses, tuition and fees. The aim of the student is special training along a line in which he is particularly interested, the attainment of his advanced degree, and the chance to show to his future employer ability to handle such problems as may be presented to him. In return for the financial aid which he receives he agrees to devote at least half of his working time to the special problem submitted by his company. The other half is devoted to study of the collateral subjects required by the department for the granting of the degree which the student seeks. The student further agrees to enter the employ of the company in question at a wage not greater than that paid in like positions to recent graduates not specially trained and to remain with his employer at such wage for at east 1 year. If the student is to obtain a degree, the special work forming the basis of his investigation must be such as will involve real research and not mere routine manipulation. The subject is chosen by conference between the three parties to the agreement. The work is carried on under the direct supervision of the instructor involved. The school furnishes the general laboratory and library equipment essential to the pursuit of any extended investigation. In

Jan 1, 1918

By Arthur F. Wendt

Introduction.—In the year 1885, the writer signed a contract to take charge of the reopening and developing of the celebrated old mines of " El Cerro Rico de Potosi." Two years earlier, an Eng- . lish firm of engineers had made a very glowing report on the property. In the summer of 1885, telegrams arrived from the parties in charge of operations at the mountain, claiming the finding of one of the old veins, with an average richness of over 200 ounces to the ton. In the fall of 1886, the author first personally visited Potosi, but found neither the English report nor the telegram borne out by the facts. After an expenditure of over half a million of dollars and more than three years of continuons hard work, the writer succeeded in unwatering and developing one of the principal old veins of the mountain. This vein, called "Cotamitos," now yields ores of about 75 ounces to the ton, and the old historic mountains of Potosi may be said to have again fairly entered the list of silver-producers. The experience of the author, during his residence in Bolivia, and data obtained from Sr. Don F. Avelino Aramayo, form the basis of this description. POTOSI. Etymology of the Name.—The Quichuá (pronounced Keechna) Indians, known to North American students as the " Incas," although the word "inca" merely signifies &apos;&apos;king," or "chief," of the Quichuás, called the mountain "Sumac-orcko," or the beautiful mountain." Eighty-three years before the discovery of the mountain by the Spaniards, the inca, or king, Huaina Ccapac, travelling from Cantumarca to Calque-Porco, saw the mountain of Potosf and, admiring its grandeur and beauty, said that within its bowels there was, no doubt, much silver. He ordered his vassal* to work the mines. They, having carried their mining implements to the mountain, ascended it and were on the point of commencing work, when they heard a voice of thunder, which said: " Do not take

Jan 1, 1891

By van Wert, L. Russell

During an investigation in which the solubility relations of the phases in Muntz metal (60 per cent. copper, 40 per cent. zinc) were under study, certain phenomena that had no immediate connection with the main problem were observed, which were thought sufficiently interesting to study further. Because of lack of time, only a preliminary survey was made of two of these; namely, the cleavage structure developed under certain conditions in a 60:40 brass and abnormal grain growth in this alloy. Cleavage Structure in Heat-treated Muntz Metal Carpenter noted many years ago that cold-working a brass of the Muntz metal type, which had been quenched previously from within the beta field, results in a partial breakdown of the supersaturated beta solution and the precipitation of the solute (the alpha solution) in the cleavage planes of the beta grains. This manner of rejection of a solute from a metastable solid solution is not peculiar to this particular alloy, for among others, it occurs in the cold-working of certain austenitic steels; for example, the austenitic nickel steels. In these ferrous alloys, cold deformation produces a partial decornposition of the austenite, with the formation of martensitic "needles" and zigzags in the austenitic poly-hedra. It is interesting to note that while the two solid solutions— austenite and quenched Muntz metal— are metastable and in their mode of decomposition behave quite alike when deformed in the cold, the metastability of each results from a different cause; viz., that of the austenite from the fact that it is a supercooled solution (its solvent. gamma iron, at ordinary temperatures is below its normal stable range whereas the metastability of the quenched Muntz metal is the result of supersaturation. When a 60:40 brass is quenched from above 800" C.—that is, from within the field where the beta phase alone is stable—this solution is retained practically intact and the alloy so cooled is found to consist almost entirely of polyhedra of this solution with only a little alpha present ordinarily at the boundaries of the beta grains—the result of a slight

Jan 1, 1929

By Welton Crook

UNLESS present in considerable proportion, metals of the precious-metal group-other than gold and silver-are not readily detected by the methods of fire assaying usually applied to ores and metallurgical products. Platinum, when present in small quantity, will ordinarily be reported as silver unless special methods of parting are used. Other elements occurring in the gold itself are all fluxed and slagged in the assay operation and if analyses are made on bullions the melting and slagging operations to which the bullion has been subjected may eliminate most of the associated elements. On the other hand, the analysis of precipi-tate from the cyanide treatment of gold ores may reveal the presence of many unexpected elements, such as tungsten and molybdenum. It is uncertain, however, whether many of the elements present in the pre-cipitate are derived from the ore gangue or from the gold itself. No very general survey of the distribution of metallic elements in gold seems to have been made. Rose and Newman,1 in connection with the composition of native gold, say in part as follows: Gold is occasionally found alloyed with copper and sometimes also with iron, bis-muth, lead, mercury, tin, antimony, palladium or rhodium. Rhodium gold from Mexico was found to be of the specific gravity 15.5 to 16.8 and contained 34 to 43 per cent of rhodium. The native alloy of palladium, gold, and silver from Porpez con-tains 85.98 per cent of gold, 9.85 per cent palladium and 4.17 per cent silver. Mal-donite, from Victoria, contains gold 64.5 per cent, bismuth 35.5 per cent (Louis). Dana&apos; says that native gold is usually alloyed with silver in varying amounts, and that sometimes it also contains traces of copper and iron. Rare varieties contain palladium, rhodium and bismuth. Other authors, for instance Zeigler3 and Clark,4 give similar information. Most refer-ences on the subject agree that ordinary native golds contain, in common, the elements silver, copper and iron. After completion of the work of which this paper is a record, the conclusion is reached that all ordinary native gold probably does contain these elements and, although in certain cases other elements may be found to be present, that it is difficult to

Jan 1, 1939

By A. Hultgren, B. Herrlander

The original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between A1 and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880&apos; was free from veining. Bannister and Jones&apos; considered veining in ferrite to be a manifestation of microscopical and sub-microscopica~ inclusions. NorthCOtt,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berg1und. TrittOn (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling. Slight distortion would not allow projecting parts of a growing crystal to join up with atomic symmetry. Hanemann and co-workers showed that veining in ferrite consisted of ridges

Jan 1, 1948

By H. A. Stacy

THE ability of galvanized sheet steel to withstand severe bending is of very great importance as relates to all such sheet material which, in service, is not used in the flat condition in which it is purchased. A "bend-test" clause is found in, all specifications for material of this kind. In the attempt to draw up a specification for galvanized sheet steel the subcommittee of the Federal Specifications Board having this work in charge, soon found that there was a surprising lack of published data and apparently very little available from manufacturing sources upon which to sustain or reject the various requirements embodied in the tentative specification which, in turn, had been based largely upon other specifications submitted to the subcommittee for this class of material. Specifications from 25 sources were received; 10 Government specifications, 10 from private users of such material, and five from manufacturers. The main points raised were: (1) The minimum mandrel thickness, expressed in terms of the thickness of the sheet tested, over which sheets with different weights of coating can be bent 180°, without serious damage to the coating; (2) the minimum radius of curvature on the inside of the angle in 90°-bends in such material; (3) effect of double seaming on the coating; (4) uniformity in the thickness of coating over a sheet, particularly as relates to the results of bend tests. In view of the uncertainty existing, it was considered very desirable for the subcommittee to conduct a series of tests in order to secure reliable information.

Jan 10, 1926

By Herbert Haas

1. INTRODUCTION COPPER matte is now converted into blister copper at a cost of only $5 per ton of copper, or, based on a 40 per cent. matte, $2 per ton of matte, which is the record of at least one large smelting Works; and it seems hardly likely that a further reduction, large enough to warrant, a change in existing practice, could be made in bessemerizing costs. But the new type of converter here described and the new practice proposed are intended, not so much for the treatment of mattes, as for the extension of, the process to the direct reduction in the copper-converter of pyrite ores

Jan 6, 1914

By J. B. Austin

Jan 1, 1945

By J. S. Pascover, J. K. Abraham

The influence of the early stages of precipitation on the kinetics and structure of martensite formation in Fe-27Ni and Fe-29.5Ni alloys containing from 0 to 10 pct Ti was examined with X-ray and electron microscopy techniques. The formation of a coherent, ordered preprecipitate had a profound stabilizing effect on the austenite. The Ms was decreased by increased titanium content and aging time up to a critical time. When the critical aging time was exceeded, the Ms was observed to increase markedly. The formation of the clusters was insuppressible and the volume fraction of clusters formed during the quench was a function of the titanium content. Martensite resulting from transformation of the clustered austenite is tetragonal with the c/a ratio increasing with titanium content. A model for the tetragonality is suggested. The morphology and substructure of the m artensite is inter-preted in terms of the above information and the cur-rent models of twinned martensite. ThE ramifications of precipitation in austenite to the properties of austenite have been the subject of numerous investigations. The current research is concerned with the influence of precipitation in austenite on the kinetics and structure of subsequent marten-site formation. In a previous investigation, Abraham et al.1 followed the aging reaction in an Fe-29.5Ni-4.2Ti* (at. pct) alloy using an X-ray diffraction technique. This technique, employing a Guinier camera, provided kinetic measurements through observation of the side band position as a function of aging time. The salient results of this work were: 1) The initiation of precipitation was not suppressed by quenching, i.e., there was a finite cluster zone size at zero aging time; and 2) The hardness of the aged austenite correlated extremely well with the zone size. During the previous work it was noted that the mar-tensite formed after aging was tetragonal, substanti-ating an earlier observation.2 Systematic investiga-tion revealed that the martensite was tetragonal in both the solution-treated then quenched, and the solu-tion-treated, aged, and quenched condition, and, furthermore, that a marked stabilization of the austenite occurred as a function of aging time. The present work is concerned with documenting the tetragonality and the stabilization phenomena as well as the ob- served microstruction with a suggested rationale for the behavior noted. EXPERIMENTAL PROCEDURE The compositions of the alloys are listed in Table I. The analyses were performed after the solution treatment of the strip material. Nickel was determined using the standard dimethy1-glyoxime procedure whereas titanium was determined colorimetrically with hydrogen peroxide and volumetrically by titrating with ferric iron. The materials were melted in a 5-lb vacuum induction furnace, cast into 2-in.-diam ingots, and forged in a temperature range of 950. to 1200°C to 1/2-in. slabs. The three higher titanium containing materials cracked during forging; therefore, to get the alloys into strip form, slices 1/8 in. thick were cut from the slab, homogenized 4 hr at 1150°C, then cold-rolled to a 0.04-in. thickness. The remaining slabs were hot-rolled, homogenized 4 hr at 1065"C, then cold-rolled to a final thickness of 0.03 in. All of the heat treatments were performed under a protective atmosphere of argon. The Ms temperature for most of the alloys is below room temperature; therefore, it was possible to solution treat, quench to room temperature, polish, and then observe the transformation optically on a cold-stage microscope. To determine the effect of aus-tenitizing temperature on Ms, eight of the alloys were treated at two temperatures, 1025" and 1120°C. No measurable variations in Ms were noticed. The remaining alloys were treated at 1025°C. The specimens, : by 5/16 by 0.03 in., were austeni-tized in a vertical tube furnace under a dynamic argon atmosphere. The bottom of the tube was submerged in water for quenching purposes. The question of stabilization that may be operating at room temperature was investigated and found to be negligible. Many of the specimens were held at room

Jan 1, 1970

By Howard Eavenson

EARLY in 1917, the United States Coal & Coke Co. secured options on several tracts in Harlan County, Ky., aggregating about 1.9,000 acres in area, and after careful prospecting by outcrop openings and diamond drilling, completed the purchase late in July of that year. This property is situated in the eastern end of Harlan County, south of the Poor Fork f Cumberland River, and extending across Big Black Mountain to the Clover Fork of Cumberland River, a distance of about 7 mi. (11.3 kg.). It extends from the Kentucky-Virginia line westward for about 6 mi. Looney Creek, which empties into Poor Fork, crosses the property for about 4 mi. (6.4 kg.), and as several of the seams within the property outcrop along this stream, it afforded an easy, and the logical, place for development. The property is on the northern side of the geological trough formed by the uplifting of Stone Mountain, on the southern, and Pine Mountain, on the northern side; the northern boundary along Poor Fork is practically at the base of Pine Mountain. This, area has been described in various geological reports.1 The main seam on this property is the one known variously as the "C," Benham, Keokee, Taggart, and Roda; it is, also called, by the Kentucky Geological Survey, the Kellioka seam of the western portion of Harlan County. This seam averages, in this property, about 5 ft. (1.5 m.) in thickness, although local rolls reduce this thickness considerably over small areas; and at the extreme western end of the property the seam splits. It is usually clean, although occasionally a small parting occurs within a few inches f the bottom f the seam; it is one f the best

Jan 9, 1921

By Laurence Delisle, Aaron Finger

THE alloys formed by the addition of nickel to iron by convelltional metallurgical procedures show physical properties that differ widely from those of the individual metals. The effect of alloying on the mechanical properties is most pronounced in alloys containing between 15 and 25 per cent nickel. The tensile strength of an alloy containing, for example, 20 per cent nickel and 80 per cent iron (with 0.06 per cent carbon), in an annealed condition, is above 150,000 lb. per sq. in.? owing to a martensitic type of transformation, as compared with about 50,000 lb. per sq. in. for pure iron in the same condition. The object of this work was to determine whether the same beneficial alloying effect could be obtained in alloys of iron and nickel prepared by powder metallurgy technique. PROCEDURE Bars and pellets for tension and compression tests, respectively, were made. Two groups of specimens were prepared: (I) by cold-pressing the powders and sintering; (2) by cold-pressing the powders, sintering, repressing and resintering. Raw Materials Nickel powder supplied by Metals Disintegrating co., marked MD-151, was used. A typical analysis of this powder was as follows: sulphur, 0.040 per cent; copper, 0.18; iron, 0.23; manganese, 0.002; magnesium, 0.001 5 ; lead, 0.035; tin, 0.025 ; silicon, 0.08; chromium, 0.008. Electrolytic iron powder supplied by Plastic Metals Inc. was used. A representative chemical analysis for impurities other than gases, supplied by the vendor, gave the following results: carbon, 0.005 per cent; manganese, 0.002; silicon, 0.003; phosphorus, 0.001; sulphur, 0.004; nickel, 0.008. The fractions from these powders passing a 3 2 5-mesh sieve were reduced in hydrogen at 600°C. for one hour, to clean the surfaces of the particles. The reduced powders, slightly caked, were ground in a mortar and screened again through a 325- mesh sieve. Mixing The proper proportions of the powders were mixed overnight on rolls, in glass jars fitted with iron-wire baffles to break aggregates of particles that might form. Pressing All specimens were compacted on hydraulic presses. The pellets were compacted in a cylindrical die, ½ in. diameter. The ratio of thickness to the diameter of the pellets was maintained as nearly as possible at 0.9, as specifed for standard short compression pieces. The tensile bars were made by compacting 30 grams of powder. Their shape is shown in Fig. I. The compacting pressures for the pellets and the tensile bars were:

Jan 1, 1946

By H. R. Aldrich

THIS paper is not a treatise on the theory and practice of magnetic surveying. It merely presents a diagram upon which have been plotted observations taken with the simplest form of magnetic instrument, the lowly dip needle, over a large area astride the Lake Superior syncline of northern Wisconsin. The exposures of the underlying formations are not sufficiently great in number nor fortunate in distribution to have provided the fuller understanding of the geology which has been secured by the use of the magnetic observations as an auxiliary tool or accessory in the hands of the geologist. The diagram (Fig. 2) in large part speaks for itself if studied in connection with the geological map (Fig. 1) for which it is the main control. It is presented to demonstrate the extent to which the use of such methods may aid in the solution of geological problems in a covered country. The diagram is probably unique in assembling the expression of such a wide range of formations, affected by so wide a range of secondary processes, and deformed by so many different structures in terms of magnetic variation. Few geologists outside of the Lake Superior country have had any first-hand experience in the taking of magnetic observations and the interpretations of the results in terms of geological conditions; nor have the Lake Superior men gone with the methods far afield from the mere tracing of iron formations. In more recent years the oil companies have gone heavily into investments in magnetometers, balances, and dip needles in the quest of concealed structural anomalies which are the favorable loci of petroleum accumulation. But these geophysicists come back from the fields with their collections of observations facing the question of interpreting the geological meaning of their magnetic anomalies.

Jan 1, 1928

The first record of coal anywhere in the Appalachian regions of which we now know is along the north fork of the Potomac River, above the mouth of Savage River, on a map entitled, A Plan of the upper Part of Potomack River call Cohongorooto Survey&apos;d in the Year 1736. Benj. Winslow1 two "Cole-mines" are shown, one just above Green Island and the other just below Hopwood Run. Winslow was in charge of a surveying party to "Lay out the Bounds of the Northern Neck of Virginia," or Lord Fairfax&apos;s Grant, his party locating the liver above the mouth of the Shenandoah, while another party located it below that point, and then around Chesapeake Bay and up the Rappahannock River. The results of the two surveys were combined in a map called, The Courses of the Rivers Rappahannock and Potowmack, in Virginia, as surveyed according to Order in the Years 1736 & 1737, made by Wm. Mayo, which does not show the "cole-mines;" this map was used with the report of the boundary commission which was sent to London in the case before the Privy Council. The boundary line decided upon was surveyed on the ground in 1746, just ten years after the original one. The results of this work were shown on A Map of the Northern Neck in Virginia, According to an Actual Survey begun in the Year MDCCXXXVI, and ended in the Year MDCCXLVI, Drawn by Peter Jefferson And Robert Brooke, Surveyors, which is now in the Colonial Office in London. This map shows the "cole-mines" in the same location as on Winslow&apos;s map, and taken from his record, of course, as that part of the survey was not retraced. Faulkner, who examined all of these records in his review of the case in 1832, refers to the notes of the original survey as "No. 10. The original field notes of the survey of the Potomac River, and the mouth of the Shenandoah to the head spring of said Poto¬mac River, by Mr. Benjamin Winslow." While the notes of the 1746 survey are in the London records and photographic copies of them are in several libraries in this county, the notes of the 1736 survey cannot be found anywhere. (For Chas. J. Faulkner&apos;s report, dated Nov. 6, 1832, see Kercheval&apos;s History of the Valley of Virginia, pp. 160-173. Jas. W. Foster&apos;s Maps of the First Survey of the Potomac River, 1736-37, in Wm. and Mary College Quarterly History Mag., April, 1938, gives a complete history

Jan 1, 1942

By R. J. Wysor

SINCE the outbreak of the European war, few problems of raw-material supply have commanded more nation-wide attention than potash. It is well known that before the war the domestic production of potash was an insignificant percentage of the imports. The average annual importation of raw potash salts for several years prior to 1914 was slightly over 300,000 net tons, and f other potash manure salts about 700,0000 tons. The sudden and almost total cessation f these imports created a unique and stringent situation. Methods of recovering potash from feldspar and other native mineral sources, and reclamation from hitherto waste products, have received a marked impetus. Soaring prices have been a keen-incentive to research and industrial development. Although several brief articles concerning the possibilities of potash recovery have appeared in recent trade journals, it still may be a matter of some surprise to the average technical mind that potash might be reclaimed as a profitable byproduct in the manufacture of pig iron. At the present time it may be of special interest to present some data, largely of a technical nature, on this subject. A fairly thorough search of the literature reveals a number of articles concerning salts of the alkali metals in the blast furnace. Many of them deal with the-theoretical role f alkali cyanides in the furnace. Several discuss the, probable effect of the alkalies on the furnace brickwork. Two or three ambitious patents have been granted for reclaiming potash or other products from blast-furnace gas. However, we have heard nothing further as to the practical application of these patents. Little literature of importance has appeared during the last 10 years concerning alkalies in blast-furnace practice, and I have discovered no record whatsoever as to the actual sale or commercial disposal f flue dust for its , potash content until this was inaugurated in our plant at Bethlehem. A bibliography of the most important articles discovered is appended.

Jan 1, 1917

By Fred D. DeVaney

DURING the past few years a radically new process for the magnetic roasting of iron ores has been investigated and developed by Pickands Mather & Co. and the Erie Mining Co. in the Erie laboratory at Hibbing, Minn. This process, originally devised by Dr. P. H. Royster of Washington, D. C., involves the use of a roasting technique quite different from older methods. It has now been demonstrated that iron-bearing materials can be roasted as effectively as by any previously known method, and at a much lower cost. The increasing shortage of highgrade iron ores in this country has accelerated the search for new methods that would permit low grade materials to be utilized. The concept of magnetically roasting low grade nonmagnetic ores such as the oxidized taconites and then separating such material magnetically has always had considerable appeal. The magnetic concentration idea is attractive because of the sharpness of the separations and cheapness of the method. Heretofore, however, the equipment and the processes available for the magnetizing-roasting -step have left much to be desired. The customary equipment available for reduction roasting has been: 1-multiple hearth furnaces, 2-rotary kilns, and 3-shaft type kilns. In addition, it is understood that some work has been done in magnetically roasting fine ores by a process using the FluoSolids principle, but little information on this process is available. The multiple hearth kiln has been used the most but first costs and operating costs have been high because of low capacity, high maintenance, and poor gas utilization. Magnetic roasting can be done in a rotary kiln, but the radiation losses are high and the conversion to magnetite is usually unsatisfactory because of poor contact between the gases and the solids. Of the shaft-type furnaces, probably the most efficient yet developed is that designed by E. W. Davis of the Minnesota Mines Experiment Station. This furnace was operated at Cooley, Minn., during 1934-1937 but was abandoned in 1937 because the operation was uneconomic. Heretofore the basic concept behind most magnetic roasting processes has been the idea of heating iron ore to a temperature of 800° to 1100 °F in a strong reducing atmosphere, preferably either carbon monoxide or hydrogen. Temperatures under 800°F were undesirable since excessive roasting time was required. Temperatures over 1100°F were avoided because of the danger of converting part of the iron to ferrous oxide which is nonmagnetic. In the new roasting process, the operation is carried on in a shaft furnace using a controlled atmosphere containing a low percentage of reducing gas. The temperature in the roasting zone is considerably higher than with the usual reducing gas and this speeds up the reduction time. Portions of the spent furnace gases are cooled and recirculated and this together with the good contact between ore and gas makes for high reducing gas utilization. High heat economy is secured by recuperating heat from the roasted ore by passing the cold reducing gases countercurrent to flow of ore. The heat transfer principle is similar to that employed in a pebble stove and to that used in the Erie Mining Co. furnace at Aurora, Minn., for pelletizing fine magnetite concentrates derived from taconite. The theory of controlled atmosphere during the roasting operation can best be appreciated by inspecting the equilibrium diagram of the Fe-C-O system shown in Fig. 1. An inspection of this diagram shows that in certain areas magnetite, Fe3O4, is the only stable form of iron. A further inspection of this table shows that if the proper ratio is maintained between carbon dioxide to carbon monoxide, such a gas will be reducing with respect to hematite, Fe2O3, and will be oxidizing with respect to both ferrous oxide, FeO, and iron, Fe. It should be kept in mind that the formation of ferrous oxide in a roasting operation is harmful, since this oxide is nonmagnetic; if it forms in any quantity, it will cause substantial loss of iron in the ensuing magnetic separation step. If a ratio of approximately three parts carbon dioxide to one of carbon monoxide is maintained, the resulting operation can be carried on at a relatively high temperature without fear of over-reduction. Specifically, most of the tests in the Erie furnace have been made at a temperature of 1500° to 1600°F, with an entrant gas containing approximately 5 pct carbon monoxide and 15 pct carbon dioxide, with the remainder largely nitrogen. It should be remembered that the ratios of carbon monoxide to carbon dioxide shown in Fig. 1 hold even though the bulk of the gas is an inert gas such as nitrogen. It may surprise many to learn that a gas containing as low as 3 pct carbon monoxide, and 12 pct carbon dioxide with the remainder nitrogen is an extremely effective reducing gas in the 1000° to 1600°F temperature range. The reducing gas is not limited to carbon monoxide, and mixtures of hydrogen and carbon monoxide may be used effectively, provided that a similar ratio is maintained between the reducing gases and carbon dioxide and water vapor. For a more detailed explanation of the theory involved, the reader is referred to U. S. patents 2,528,552 and 2,528,553. From a safety standpoint, the weak reducing gas used in the furnace offers an advantage. Its composition is such that it is well below the limits of explosion should air enter a hot furnace. This condition is not true with the usual reducing furnace, in which a gas rich in carbon monoxide or hydrogen is used. The general furnace design and method of operation may best be understood by an inspection of

Jan 1, 1952

By E. A. Gulbransen, K. F. Andrew

The vacuum-microbalance method was used to study the oxidation behavior of Zircaloy-2 and -3A over the temperature range of 300 to 850°C and at 0.1 atm pressure. The results fit in well with the authors&apos; earlier studies on zirconium. Tin was found to increase the rate of oxidation and also the temperature at which the metal burns. Both the cubic-rate law and the parabolic-rate law gave imperfect fits to the rate data. Since the parabolic-rate law has been derived from accepted physical principles, this rate law was used to interpret the rate data. A heat of activation of 28,600 cal per mole was calculated. The transition phenomenon previously observed in hot-water and steam-corrosion processes was studied systematically for oxygen atmospheres. Observations on the rate of oxidation, color and properties of the oxide films show that the transition phenomenon was associated with a failure in the adherence of the oxide to the alloy. ZIRCALOY-2 and -3A have found important uses in the field of reactor metals due to their low neutron adsorption, good strength and good resistance to corrosion. One feature of the corrosion reaction in steam or hot water is the sharp transition in the rate of corrosion to a higher value after a certain amount of reaction has occurred. This paper presents a study of the reaction of Zircaloy-2 and -3A with oxygen including a study of the transition phenomenon which has been found to occur also in oxygen atmospheres. A comparison will be made between the oxidation behavior of these alloys and the pure metal. It was hoped that a study of the details of the oxygen reaction would lead to a better understanding of the reactions occurring in hot-water and steam atmospheres. Literature Kinetics-—The reaction of Zircaloy-2 and -3A with hot-water and steam atmospheres has been studied by Thomas.&apos; Goldman and Thomas,&apos; Thomas and Forscher," and Thomas and Kass.&apos; Empirical equations for the kinetics of the reaction have been given by Thomas and Forscher." The change from the initial slow rate of reaction to the final rapid rate of reaction has been termed transition with the post-transition corrosion kinetics following a simple linear equation in time. The corrosion behavior in high-temperature steam was similar in many features to the corrosion in high-temperature water. Goldman and Thomas&apos; and Pray and Peoples&apos; have shown that the addition of tin, while increasing the rate of corrosion, counteracts the deleterious effect of nitrogen. The beneficial effect of iron, nickel and chromium was to improve the adhesion of the oxide to the metal as well as to counteract the deleterious effect of nitrogen. Mallet and Albrecht" have studied the oxidation of two zirconium-tin alloys. The cubic-rate law was found to fit the oxidation data for the 1.5 pct tin alloy while the parabolic-rate law was found to fit the data for the 2.5 pct alloy. Kendall&apos; in a recent paper has studied the oxidation of Zircaloy-2 containing 1.5 pct tin in air atmospheres. Transition Phenomenon—In steam atmospheres Thomas&apos; has observed fora 1.8 pct tin alloy containing small amounts of iron, nickel and chromium that transition to a more rapid rate of corrosion at 400°C

Jan 1, 1959

By B. Herrlander, A. Hultgren

The original aim of the present investigation was to study the mechanism of cracking on hot-deforming red-short steels. During the microscopical examination of hot-deformed soft steels attention was directed to various patterns of so-called veining in the ferrite, as related to variations in the deformation procedure and the heat-treatment of the steels. Later, a hot-short steel of higher carbon content was also studied. Historical Storey1 suggested in 1914 that veining developed during the gamma-alpha transformation from the growing together of several alpha nuclei within the same gamma grain. Rawdon and Berglund2 found that in soft steel, forged somewhat below A3, the ferrite showed profuse veining, while usually there was very little veining after forging at very high temperatures. They emphasized the similarity between the pattern of veining formed by deformation about 600°C and that of slip lines formed by deformation at room temperature. They also suggested a relation between the gamma-alpha transformation and veining. They became convinced from etching and from the slip-line pattern in cold-deformed material, that the orientation within any ferrite grain showing veining was uniform. In recrystallized alpha grains veining was absent. Veining did not appear materially to affect the properties of ferrite. Independent of veining, continuous networks, attributed to preexisting delta and gamma grain boundaries were sometimes found, the former only in cast steel. Those networks were usually connected with small inclusions. Ammermann and Kornfeld3 confirmed that recrystallized ferrite grains showed no veining. In soft steel annealed between A1 and A3 there was veining only in the ferrite grains formed during cooling. Electrolytic iron deformed at 880&apos; was free from veining. Bannister and Jones&apos; considered veining in ferrite to be a manifestation of microscopical and sub-microscopica~ inclusions. NorthCOtt,5,6 in studies on veining in steel and other metals and alloys, attributed veining to oxide inclusions. It could generally be removed by annealing in hydrogen, a suggestion earlier made by Rawdon and Berg1und. TrittOn (discussion in ref. 5) emphasized the importance of perfect polishing for bringing out veining by etching, and thought the veins or subboundaries were produced during the gamma-alpha transformation, when it was rapid, as a result of the volume change and contraction during cooling. Slight distortion would not allow projecting parts of a growing crystal to join up with atomic symmetry. Hanemann and co-workers showed that veining in ferrite consisted of ridges

Jan 1, 1948

By R. C. Earlougher, F. G. Miller, T. D. Mueller, H. J. Ramey

There are many studies of flow in radial systems that can be used to interpret unsteady rerervoir flow problems. Although solutions for systems of infinite extent can be used to generate solutions fur finite ow systems by superposition, application is tedious. In this paper a step is made toward simplifying calcu1ations of such solutions for finite flow systems. Superposition is used to produce a tabulu-lion of the dimension1e.s.s pressure drop function at several locations within a bounded square that has a well at its center. The square system provides a useful building block that may be used to generate flow behavior for any rectangular shape whose sides are in integral ratios. Values of the tabulated dimensionless pressure drop function are simply added to obtain the dimensionless pressure drop function for the desired rectangulm system. The rectangular system may contain any number of wells producing at any rates. Furthermore, the outer boundaries of the rectangular system may be closed (no-flow) or they may he at constant pressure. Mixed conditions also may be conyidered. Tables of the dimensionless pressure drop function for the square system are presented and various applications of the technique are illustrated. Introduction In 1945, van Everdingen and Hurst&apos; published solutions for the problem of water influx into a cylindrical reservoir. Since this problem is mathematically identical with the depletion of a cylindrical reservoir with a well at the origin, the van Everdingen-Hurst solution may be used to study the depletion problem. In their analysis, they assumed that the fluid had a small, constant compressibility such that flow was governed by the diffusivity equation For a constant production rate q starting at time zero, van Everdingen and Hurst showed that the unsteady pressurc distribution for both finite and infinite systems could be expressed in terms of a dimensionless pressure &apos;Sabulations of the dimensionless pressure drop for a unit value of r, were provided by van Everdingen and Hurst,&apos; and later by Chatas.&apos; Others also presented values in graphical or tabular form." If the radius of the well becomes vanishingly small, r,+ O, the line source solution may be used for Eq. 2 when infinite systems are considered. Eqs. 5 and 6 are excellent approximations for Eq. 2 under certain conditions: In 1954, Matthews, Brons and HazebroekV emonstrated that solutions such as Eq. 5 can be superposed to generate the behavior of bounded geometric shapes; i.e., the behavior of a bounded single-well system can be calculated by adding together the pressure disturbances caused by the appropriate array of an infinite number of wells producing from an infinite system. These wells are referred to as image wells. Matthews, Brons and Hazebroek considered systems containing a single well producing at a constant rate. This superposition can be represented analytically as

Jan 1, 1969