By Edwin Adoyi Ali, Zainab Shehu Aliyu, Adele Dzikwi Garkida, Muhammad Dauda

Feldspar from Matari, Nigeria was analyzed using SEM, XRD and XRF techniques for microstructural analysis, mineral phase analysis and chemical composition analysis respectively. Qualitative and quantitative XRD analyses revealed the presence of microcline 59.6%, albite 34.7% and quartz 5.71%. The XRF results showed that the feldspar contains 67.32% SiO2, 17.54% Al2O3, 11.33% K2O, 2.75% Na2O, 0.12% CaO, 0.01% MgO, 0.02% MnO2, 0.10% Fe2O3, 0.00% Ti2O, etc and 0.14% LOI. SEM/EDX analysis shows the presence of microcline feldspar as the dominant phase, exhibiting lamellar twinning. The XRD has also revealed that potash has the highest peak, indicating its high concentration. The 0.10% Fe2O3 present is within the permissible level (0.1-0.3%) for glass making and also within the potash feldspar specifications (0.17%). The Matari feldspar is a microcline type, rich in potash, alumina and silica, enabling it meet the standard specifications for alumino-silicate glass.

Jan 1, 2015

By W. Petruk, M. J. Matos

An aplite ore from Guarda in northern Portugal, containing albite, microcline and quartz and muscovite gangue was studied to identify conditions for extracting the feldspar minerals. The large amounts of quantitative mineralogical data needed to evaluate grinding behaviour were provided by automated image analysis. The images were acquired on polished surfaces by measuring back-scattered electron signals produced with a microprobe. Minerals were identified from X-ray spectra and discriminated by grey level and element-characteristic X-rays. The quantities and size distributions of the minerals were determined by measuring thin sections of unbroken ore to predict the grind required to liberate the feldspars. The ore was then ground to -1.7 mm, polished sections were prepared from sieved fractions and the quantities of mineral species and apparent total liberation were determined by analysis. The predicted and measured liberations were compared and the grinding behaviour of the ore interpreted. In an appended correction, the correct version of Equation 1 is represented and Tables 3 and 6 are revised to consider all size fractions, including those coarser than 300 micrometres, in calculating the total liberation from King's fractional liberation

Jun 18, 1905

By Tammy G. R. Portela

A comparative characterization of the dimensional and mechanical properties as well as structural aspects of two different types of fibers extracted from the leaves and petioles of the buriti palm tree was performed. A statistical analysis revealed that both types of fibers present a significant dispersion in length and equivalent diameter. However, the corresponding intervals of dimensional variation are sensibly different. The tensile properties showed that both types of fibers display a tendency of higher strength for smaller diameters. Moreover, the fibers extracted from the leaves depict a comparatively lower strength. By contrast, the fibers from the petiole present an average strength sufficiently high for the use as reinforcement of polymeric composites. The structural aspects of tensile-rupture fibers, characterized by scanning electron microscopy, showed marked distinction in the microstructure and fiber behavior of both types of investigated fibers. This could explain the differences in mechanical behavior

Jan 1, 2010

By Luiza Esteves

Corrosion testing was performed in white liquor from a Brazilian Kraft mill. Specimens of duplex stainless steel (DSS) and lean duplex (LDSS) were exposed at 170 °C for 30 days to simulate conditions of the digester. Corrosion rates were determined from weight loss measurements. After this exposure, the corrosion products formed on the steel surface was characterized by using scanning electron microscope (SEM) equipped with EDS, X-Ray Diffraction (XRD), and X-ray photoelectron spectrometer (XPS). EBSD can be used to quantify of basis balance phases in DSS and LDSS. General corrosion rates for UNS S32304 LDSS were higher than the UNS 31803 DSS in industrial white liquor at 170 °C for 30 days. XPS and XRD analyses indicated that the film formed after the immersion test may be consisted by Fe and Cr oxides and sulphides.

Oct 30, 2017

By A. Djebara

Today, indoor air quality, especially in manufacturing industries, is of great interest due to the use of new processes and advanced materials such as those containing nanoparticles. Manufacturing processes generate aerosols (dry or wet) which can be detrimental to occupational health and safety and to the environment. Controlling metallic particle emissions during machining processes should limit their formation at the source, and thus minimize the risk of exposure; this at-source reduction requires the characterization of the particle emitted (size, nature, concentration, etc). The metrics normally used in characterizing fine and ultrafine particles include the mass concentration, the specific surface and the number concentration. Most of these metrics are affected by the size, the geometry and the density of the measured particles. Information about the form and the real size of the particles is thus very important. A procedure for collecting and characterizing fine and ultrafine metallic particles was developed and applied to the study of particles emission during the machining of aluminum alloys. It was found that metallic particles emitted during the machining of aluminum alloys are of various shapes and sizes, and this information must be taken into account when characterizing these particles.

Jan 1, 2011

By J. Guerrero, O. Pavez, N. Toro, A. Nazer

In the 19th century, mining in northern Chile was of great economic importance. Today, the ruinsof the copper smelters and abundant fragments of refractory bricks from their furnaces remain. Therefractory materials have not been previously studied. the origin, physical and chemical properties, and compressive strength of 10 different samples of historical refractory bricks collected on-site were investigated. The characterization results showed that the bricks are silico-aluminous, unlike the magnesium-chromium bricks used by current foundries. It was determined that 90% of them were produced in the UK and 10% were manufactured in Chile. The phases present are mullite, quartz, cristobalite, and tridymite, and the chemical composition corresponds mainly to SiO2. The compressive strength of the historical bricks is similart to those currently used,. These results may contribute to the knowledge of the 19th century mining and metallurgical historical heritage of Chile and the UK.

Jul 5, 2023

By B. Jena, M. Rigaud, S. C. Panigrahy

"The influence of flux addition on the structure and properties of pellets produced from low silica specularite with peat moss and bentonite as binders was investigated. Specific pellets basicities in the range of 0.4 to 3.2 were obtained by the addition of limestone or a combination of dolomite and limestone as flux. A t basicities < 1.6, the bonding in the pellets was provided by a glassy silicate phase. At basicities =1.6, calcium ferrites were the predominant bonding phase. When dolomite was added as a flux, presence of magnesia-ferrite was noted. The reduction behaviour of pellets at different basicities was found to be influenced by the type of flux and binder. The pellet compression strength and swelling characteristics were improved with increased basicity.IntroductionThe properties of iron ore pellets are influenced by the type and nature of the ore or concentrate, additives and their subsequent treatment to produce pellets. The interaction between various constituents of the concentrate and additives, i.e. iron oxides, gangue and fluxes etc. result in the formation of various mineralogical phases which affect the degree and nature of bonding achieved in the pellet and the structure and distribution of pores. The pellet properties such as pellet strength and reducibility are influenced by the extent and type of bonding achieved between the ore particles. In view of the present emphasis on the production of high quality pellets to meet progressively stringent quality control requirements, it is essential to investigate the effect of additives on the bonding mechanism and properties of the pellets.In the past, the effects of additives on the bonding mechanism of pellets have been investigated. It is important to note that the conditions and parameters to be controlled are typical of a given concentrate/ore. In this paper, the results of the investigation on characterization of fluxed pellets produced from a low silica specularite concentrate are reported.This investigation was also aimed at assessing the suitability of peat moss for use as a binder for the production of low silica fluxed pellets. Peat moss is abundantly available in the vicinity of iron ore mines in Quebec and encouraging results have been obtained du ring the production of high silica acid and fluxed pellets."

Jan 1, 1992

By John W. Graydon

Incineration is an attractive alternative to the disposal of MSW in landfill sites. However, the process of incineration generates fly ash which contains significant levels of leachable heavy metals - particularly cadmium, lead, and zinc - and it is essential to manage this fly ash in an environmentally sound manner. The compositions, phases, textures, morphologies and size of fly ash particles have been studied by light microscopy, scanning electron microscopy, X-ray microanalysis, and X-ray diffraction. The detailed spatial relationships and speciation of the environmentally significant constituents have received particular emphasis. The information obtained is useful in understanding how fly ash is formed during incineration, in understanding the leaching behavior of untreated fly ash if it is disposed of in a landfill and, most importantly, in guiding the development of the best treatment strategies for fly asti to mitigate its environmental impact.

Jan 1, 1992

By Carlos Mauricio Fontes Vieira, Sergio Neves Monteiro, Thiago Samarão Motta

This work has as its objective to characterize ceramic bodies formulated with ornamental rock waste and two different clays to produce ceramic paver. Specimens were made by uniaxial press-molding at 20 MPa and then fired at 950 and 1050oC respectively. The determined technological properties were: plasticity, dry bulk density, linear shrinkage, water absorption and flexural rupture strength. The results showed that the type of the clay has strong influence on the properties of interest for heavy clay ceramics. The investigated waste must be incorporated in small amounts to avoid increasing in the porosity of the ceramics.

Jan 1, 2015

After several years of laboratory and field evaluations, it has been established that each frother has its own unique relationship among bubble size reduction, gas hold-up increase, froth stabilization and frother concentration. It has been shown that a frother?s hydrodynamic properties can be characterized using the relationship between the froth zone property froth height and the pulp zone property gas hold-up. The relationship is established in a bubble column run at a given air rate over a range of frother concentration. The use of relationships in frother selection and plant diagnostics is illustrated in a series of plant case studies.

Jan 1, 2009

By S. J. Schatzel, P. W. Jeran, W. P. Diamond, F. E. McCall, F. Garcia, J. C. LaScola, T. P. Mucho

The National Institute for Occupational Safety and Health, Office for Mine Safety and Health Research, is investigating the geologic and mining factors influencing the migration of longwall gob gas. One goal of these studies is to optimize methane drainage strategies to reduce the volume of gob gas that reaches the underground workplace. As part of this research effort, longwall gob gas flow paths in a mine operating in the Pittsburgh Coalbed, PA, were investigated using SF6 tracer gas. Tracer gas released into the ventilation airflow underground generally stayed in the bleeder system and was vented at the associated bleeder fan shafts. Tracer gas injected into an inactive (intaking) gob gas venthole migrated to the two inby producing ventholes on the study panel, indicating that all three ventholes were in communication. The tracer gas that was injected into the gob generally stayed in the gob and only migrated to the ventilation system in response to the venthole on the study panel closest to the injection hole going off production. Tracer gas flow velocities in the longwall gob reservoir and factors influencing the production performance of gob gas ventholes in the study area are also discussed.

By P. Sergi

A method of characterizing gold ores with respect to processing is proposed. The method includes microscopical examinations to obtain qualitative and quantitative data that relate to processing. The main thrust, however, involves laboratory heavy liquid separation tests, laboratory amalgamation tests, and laboratory cyanidation tests to determine the proportions of gold that can be recovered in a conventional processing operation. Two different Brazilian gold ores: a quartz vein gold ore, and gold in metasediments were tested.

Jan 1, 1989

By J. F. Stenebråten, W. P. Johnson

Carbonaceous material (CM) from the Barrick Goldstrike Mines, NV, was characterized with respect to its gold sorption (preg-robbing) and gold recovery behavior. The breadth of graphite peaks measured by X-ray diffraction were used to calculate crystallite dimensions (002) of the CM. The (002) dimension was found to vary inversely with preg-robbing activity and directly with gold-recovery behavior, indicating that the degree of graphitization (maturation) experienced by the carbonaceous material is correlated with gold-loss during ore processing. The inverse correlation of preg-robbing activity was improved when percent preg-robbing was regressed against (002) crystallite size and carbon content. The (101) crystallite dimensions of all samples were calculated from laser Raman analysis, and were not found to correlate with preg-robbing behavior of the CM. BET surface area and micropore size distribution results were affected by grinding history, negating comparison of these characteristics between samples.

Jan 1, 2000

By J. F. Stenebråten, W. P. Johnson, D. R. Brosnahan

Carbonaceous material (CM) from ores of varying preg-robbing activity from Barrick Goldstrike Mines Inc. (BGMI), Nevada, was characterized in terms of its functional group content, hydrocarbon content, elemental composition, and humic acid content. FT-IR analyses showed neither the presence of hydrocarbons nor of carboxylic, phenolic, or sulfhydrol functionalities. FT-IR bands present included C=C stretching in aromatic rings and C-O-C stretching, indicating presence of oxygen as ether linkages in the carbon matrix. Calculated atomic oxygen to carbon (O/C) ratios did not reveal a trend between maturity of CM and preg-robbing behavior, possibly due to low resolution of electron microprobe analysis. However, the atomic O/C ratios agree with other chemical analysis, indicating that the organic carbon is very mature, similar to or higher in grade than anthracite coal.

Jan 1, 1999

By F. G. Caballero, J. L. Gonzalez-Carrasco, S. Barrius, H. Carreon, M. Lieblich

"The grit blasting is a low-cost technique successfully used to enhance mechanical fixation of the implants through increasing their roughness. As a result of the severe plastic surface deformation, it produces subsurface effects such as grain refinement, hardening and compressive residual stresses which are generally evaluated with destructive techniques. In this research work, non-contacting and contacting thermoelectric power measurements are performed in blasted 316L VM and Ti-6AI-4V specimens using Ah03 and Zr02 particles which yield a coarse and a fine rough surface, respectively. This study correlates the microstructural changes induced by the grit blasting treatment and the limitations and advantages of each of the nondestructive thermoelectric techniques based on the Seebeck effect used to evaluate these biomaterials.IntroductionIt is well known that surface properties play an important role in metallic materials used in bio-medical applications. Since the biological response is correlated directly with surface properties it is comprehensible the intense activity in superficial modification by physics or chemistry methods in this field. Grit blasting, one of the most popular surface modification of metallic biomaterials, enhances the mechanical fixation of the implant through the increase in roughness [1-3]. Roughening is developed by bombarding the surface with a high-velocity jet of ceramic particles, being the final roughness a function of the processing parameters (pressure, distance, time, ... ) and blasting particles (nature, shape, size). As the plastically deformed surface layer tries to expand relatively to the intact interior of the specimen, residual compressive stress gradients develops perpendicular to the surface at shallow depths with a maximum value at a depth in the range of 5 to 60 µm. This surface treatment also may cause subtle variations in the subsurface material properties, such as increased hardness and grain size refinement, which are consequences of the significant plastic deformation through cold work. Blasted affected zones may extend to a depth of up to about 200 µm. The subsurface hardening and the near-surface compressive stress gradient playa beneficial role by retarding fatigue crack nucleation and further growth, ultimately extending the fatigue life of the metallic part [4]. In this work, two non-destructive thermoelectric techniques (NDTT), the non-contacting and contacting thermoelectric power measurements were used to analyze the subsurface induced changes on blasted Ti-6AI-4V and 316L VM specimens using Al2O3 and Zr02 particles. Detailed information on the microstructural induced effects and subsurface mechanical properties were published elsewhere [5-8]. Here the nondestructive evaluation of the involved microstructural changes is used to assess the global subsurface damage. Advantages of using nondestructive techniques during manufacturing are envisaged."

Jan 1, 2012

By S. Mohammadnejad, M. Olizadeh, B. Mehrabi

A new method using a combination of comprehensive mineralogical and analytical approach which includes optical and electrical microscopy and several analytical techniques with diagnostic leaching has been used to characterize the associations and distribution of gold in a variety of minerals from the Zarshuran refractory gold ore, NW Iran. Zarshuran ore with an average of 7.9 g/t Au-grade and about 8% arsenic with gold recovery less than 20% in direct cyanidation is considered as high arsenic, high au-grade refractory gold ore. In most of the refractory ores, gold is associated with arsenopyrite and co-para genetic ore minerals, while in Zarshuran ore; gold is associated with orpiment, realgar and arsenian-pyrite. Considering its mineralogy and As content, it can be considered as the most difficult refractory ore for characterization and processing. Results from the mineralogical examination and diagnostic leaches indicate that there is only a small amount of free gold (17-19%) that is present in cyanide-soluble sulfo-arsenides compounds, predominantly orpiment and realgar. Diagnostic leaches also indicate that little gold is occluded within the silicate structure (14%). Overall, the gold is mostly included in sulfides, arsenic sulfides and sulfo-arsenides (50%). The results also have shown how the technique can be used to gain a good initial understanding of potential metallurgical problems for a refractory gold ore.

Jan 1, 2005

By Zhou Wenbin

In this paper the mechanical properties of high carbon equivalent cast iron for automobile brake discs were analyzed through thermal analysis curves. Experiment results show that the mechanical properties have a strong correlation with thermal analysis curves and an effective way to predict the mechanical properties of high carbon equivalent cast iron was proposed based on the features of thermal analysis curves.

Jan 1, 2010

By G-L. Wu, S-W. Wu

"The hot deformation behaviour of Nb-Ti microalloyed high-strength steel was investigated. Hot compression tests were conducted in the temperature range 900 to 1100°C under strain rates of 0.1, 1, and 5 s-1. Dynamic recrystallization (DRX) occurs as the main flow softening mechanism at high temperature and low strain rate. The hot deformation activation energy was calculated to be about 404 699 J/mol. The constitutive equation was developed to describe the relationship between peak stress, strain rate, and deformation temperature. The characteristics of DRX at different deformation conditions were extracted from the stressstrain curves using the work hardening parameter. The Cingara-McQueen equation was developed to predict the flow curves up to the peak strain. The processing maps were obtained on the basis of a dynamic materials model. The results predict an instability region in the temperature range 1010 to 1100°C when the strain rate exceeds 0.78 s-1. IntroductionThe 700 MPa grade HSLA steel is widely used in engineering machinery, automotive beams, carriages, and axle tubes, etc. (Pan et al., 2017 ). Generally, such grades contain a moderately high amount of Mn (approx. 1.4% and above), and microalloying elements like Nb, Ti, V, and Mo to impart the desired strength and toughness through solid-solution strengthening, precipitation hardening, and grain refinement dislocation strengthening (Chen and Yu, 2012; Opiela, 2014). However, the production costs can be greatly reduced by replacing part of the Nb, V, or Mo with inexpensive Ti and adopting the compact strip production CSP process (Opiela, 2014; Chen et al., 2015). Furthermore, the microalloying technology coupled with new-generation thermomechanical control processing (NG-TMCP) has proved efficient for achieving the proper balance between strength, toughness, ductility, and formability by means of a suitable combination of chemical composition and thermomechanical treatment parameters (Shukla et al., 2012; Wu, Zhou, and Liu, 2017).In hot forming processes, the complex microstructural evolutions are often induced by multiplicative hot deformation mechanisms, such as work hardening (WH), dynamic recovery (DRV), and dynamic recrystallization (DRX) (Zhang et al., 2014; Liang et al., 2015). Dynamic softening behaviour during hot processing has generated considerable interest because component properties are influenced significantly by its corresponding microstructural evolution (Wu et al., 2010). During deformation in the DRX process, deformed grains are replaced with substructures and newly formed fine and uniformly distributed grains. This occurs only when a critical strain for the onset of DRX is reached, and at the same time, the minimum rate of energy dissipating is reached (Ferdowsi et al., 2014). DRV occurs at a high strain rate and low temperature, reducing the stored energy greatly and making DRX difficult (Liang et al., 2015). The microstructural changes during DRX are sensitive to the processing parameters, such as strain rate, deformation temperature, and strain (Zhang et al., 2014; Ferdowsi et al., 2014). Therefore, in order to optimize the hot processing parameters, it is important to understand the behaviour of hot deformation visà- vis control of microstructural evolution."

May 1, 2019

By D. E. Walsh

Over a period of seven years (1989-1996) the Mineral Industry Research Laboratory (MIRL) University of Alaska Fairbanks, has investigated the effects of temperature, residence time, and particle size on the degree of low-rank coal (LRC) upgrading for a non-evaporative, hydrothermal drying process, also known as hot water drying (HWD). Three Alaskan LRCs were used in this study: Usibelli coal (Seam No.4) from the Nenana Coal Field, Little Tonzona coal from near McGrath, and Beluga coal from the Beluga-Yentna field on the west side of Cook Inlet. Replicated, factorial tests were conducted. Experimental results indicate that most of the low-rank coal upgrading via HWD occurs rapidly within the first 10-20 minutes of residence time. Thereafter, the upgrading process slows down and over 100 minutes of additional residence time are required to produce similar percentage increases in coal properties to those achieved in the first 10-20 minutes. The properties of the hot water dried products were very sensitive to process temperature. Calorific value, carbon and oxygen contents, equilibrium moisture levels and Hardgrove grindabilities all appear to change linearly with temperature within the 275" C to 325" C range.

Jan 1, 1997

By O. Noirot, H. C. Owens, P. D. Rao, D. E. Walsh, J. R. Mokka

Over a period of seven years (1989-1996) the Mineral Industry Research Laboratory (MIRL) University of Alaska Fairbanks, has investigated the effects of temperature, residence time, and particle size on the degree of low-rank coal (LRC) upgrading for a non-evaporative, hydrothermal drying process, also known as hot water drying (HWD). Three Alaskan LRCs were used in this study: Usibelli coal (Seam No. 4) from the Nenana Coal Field, Little Tonzona coal from near McGrath, and Beluga coal from the Beluga-Yentna field on the west side of Cook Inlet. Replicated, factorial tests were conducted. Experimental results indicate that most of the low-rank coal upgrading via HWD occurs rapidly within the first 10-20 minutes of residence time. Thereafter, the upgrading process slows down and over 100 minutes of additional residence time are required to produce similar percentage increases in coal properties to those achieved in the first 10- 20 minutes. The properties of the hot water dried products were very sensitive to process temperature. Calorific value, carbon and oxygen contents, equilibrium moisture levels and Hardgrove gindabilities all appear to change linearly with temperature within the 275°C to 325°C range.

Feb 24, 1997