By G. R. Leverant, M. Gell

The high- and low-cycle fatigue poperties of MAR-M200 directionally -solidified into columnar-grained and single crystal forms were determined at 1400" and 1700°F. These results were compared with the corresponding properties of conventionally -cast MAR-M200. The low-cycle fatigue lives of the columnar-grained and single crystal materials were similar at both temperatures and were one to two orders of magnitude greater than those of conventionally-cast material. The variations in the fatigue lives among the three forms of MAR-M200 were related to the more rapid rate of intergranular muck propagation compared to that of transgranular propagation. In conventionally-cast MAR-M200, cracks were initiated in grain boundaries and crack popagation occurred rapidly along an almost continuous grain boundary path. In the columnar-grained material, crack initiation occurred on short transverse segments of grain boundaries, but crack propagation was transgranular. The fatigue lives of columnar-grained and single crystal materials were approximately the same because most of the life in both materials was spent in trans-granular propagation. For the directionally -solidified materials, the number of cycles to failure, Nf, can be related to the total strain range, , by: heT = K where n and K are 0.16 and 0.044 at 1400'F and 0.29and 0.098 at 1700, respectively. In addition to intergranular crack initiation in the columnar-grained material, initiation also occurred at we-cracked MC carbides and micropores in both directionally-solidified materials. At 1400°F, fatigue life was reduced with increasing MC carbide size, but at 1700 there was no effect of carbide size. THE creep and stress-rupture properties of conventionally-cast nickel-base superalloys can be greatly improved by directional solidification into either single crystal or columnar-grained forms. The improvement in properties results from a reduction in intergranular cavitation and crack growth in the columnar-grained materials and the complete absence of this fracture mode in the single crystals. This paper describes the effect of grain boundaries on the elevated temperature fatigue properties of the nickel-base superalloy MAR-M200. The effect of cycling frequency on cracking arid fatigue life and the role of MC carbides and micropores on crack initiation are also emphasized. The fatigue properties of columnar-grained and single crystal MAR-M200 at room tem- perature,4,5 and the change in the mode of fatigue crack propagation with temperature6 have recently been described. I) EXPERIMENTAL PROCEDURE The material used in this study was the nickel-base superalloy MAR-M200, directionally-solidified into columnar-grained and single crystal forms. The columnar grains were approximately 0.5 mm in diam. The nominal composition of these materials in wt pct was 0.15C, 9Cr, 12.5W, loco, 5A1. 2Ti, lCb, 0.05Zr. 0.015B, bal Ni. They were solutionized for 1 to 4 hr at 2250°F followed by aging at 1600°F for 32 hr. which resulted in 0.2 pct offset yield stresses of 150,000? 144,000, and 95,000 psi at room temperature? 1400°, and 1700°F, respectively. The corresponding elastic moduli parallel to the testing direction were 19.2. 15.0, and 12.5 x 106 psi, respectively. Specimen design, testing procedures and alloy mi-crostructure have been described previously and will only be summarized here. Following the 1600°F aging treatment. MAR-M200 contains an ordered, cuboidal, y' precipitate 0.3 1 on edge, which is coherent with the 1 matrix. The y' precipitate is quite stable; even after testing at 1700°F. the precipitate is only slightly enlarged and its corners somewhat rounded. The alloy also contains a small volume fraction of micropores, and MC carbides. some of which contain preexisting cracks5 formed during casting. These cracks are always parallel to the long dimension of the carbide. Measurement of MC carbide size has been described previously.5 Axial fatigue tests were conducted in air over a wide range of strain amplitudes in both the high - and low-cycle fatigue regions, with specimen lives varying from about 10' to 10' cycles. Low-cycle fatigue (LCF) tests were strain-controlled with strain varied between zero and a maximum tensile value at a frequency of about 2 cpm. High-cycle fatigue (HCF) tests were stress-controlled with the stress varied between 5000 psi and a maximum tensile value less than the yield stress at a frequency of either 10 cps or 0.033 cps (2 cpm). The temperature in the gage section was controlled to 52°F. Specimen axes were within 5 deg of the [001] growth axis of the single crystals and the common [001 ] growth axis of the columnar-grained material. Specimen gage sections were electro polished prior to testing. After the standard heat treatment, three specimens were coated with a typical aluminide coating applied as a slurry. An additional specimen was given the coating heat treatment without actually being coated. In all cases: specimens were reaged at 1600°F for 32 hr after receiving the coating heat treatment at 1975'F for 4 hr.

Jan 1, 1970

By K. R. Evans

The yield and fracture characteristics of a Ti-8 pct A1 alloy have been examined at room temperature as a function of exposure temperatures to 1700°F. Em-brittlenzent of the alloy is observed to occur following exposures below 1280°F, the critical temperature for formation of ordered Ti3Al particles. Presence of Ti3Al particles results in an increase in the yield and flout stresses which, for a given exposure time, are a maximum at the critical temperature. Embrittlement is attributed to the occurrence of plastically induced fracture controlled by the increase inflow stress. This interpretation is compatible with the decreasing ductility and increasing crack popagation rates observed with increasing exposure time below the critical temperature. Slip line observations and measurements of the gain size dependence of the yield stress indicate that the slip character of the alloy is not influenced by exposure treatments below the critical temperature. ThE potential usefulness of Ti-A1 alloys in structural applications has prompted considerable interest in studies of their microstructure and mechanical characteristics. The relatively recent surge of interest in the system and at the same time its complexities are indicated by the fact that despite numerous recent efforts14 there has not even been general agreement upon a phase diagram for the system. However, most of the Ti-A1 alloys of commercial interest range in aluminum content from 5.0 to 8.5 wt pct where most investigators achowledge the existence of the ordered Ti41 phase. Goldak and parrs confirmed the existence of Ti41 from X-ray diffraction analysis of the stoichiometric composition while Blackburn6 has determined its presence in commercial Ti-8 pct A1 alloys by electron diffraction analysis and dark field transmission microscopy. The embrittlement of Ti-8 pct A1 alloys was initially reported by Crossley and carew7 who showed that aging in the temperature range of 750" to 1110°F resulted in extreme brittleness. This behavior was later confirmed and correlated by Soltiss to the presence of long-range order in the commercial Ti-8 pct Al-1 pct Mo-1 pct V alloy (Ti-8-1-1) which exhibited anomalous creep and yield strength behavior at 950°F. This investigation was designed to study the mechanical characteristics of a binary Ti-8 pct A1 alloy in order to further examine the nature of the embrittlement behavior reported for the alloy system. EXPERIMENTAL PROCEDURE A Ti-8 pct A1 binary alloy was obtained from the Wah Chang Co. in the form of 0.050 in. sheet. The chemical composition of the alloy is given in Table I. Heat-treatment of the alloy was conducted in evacuated vycor capsules for the tensile sDecimens (1.25 bv 0.25 in. gage section) and in evacuated stainless steel jackets for the crack growth-rate panels. All specimens were annealed at 1700°F for 24 hr and water quenched before an exposure at elevated temperatures. Tensile testing was conducted at room temperature in an Instron testing machine equipped with a pushbutton control for instantaneous control of the cross-head motion. In this manner the change in stress, Aa, accompanying an increase in strain-rate by a factor of 10 was measured immediately after yielding. The crack growth-rate panels used were 3 by 18 in. with a precrack 0.33 in. long cut into the center of the panel. The panels were cycled at a maximum gross stress of 40,000 psi at a maximum to minimum tension stress ratio of 20. Cycling of the specimens was continued until the crack propagated the width of the panels. The crack length was intermittently measured during slow crack growth. EXPERIMENTAL RESULTS Correlation of Embrittlement to the Critical Temperature for Ordering. Blackburn6 has found that the critical temperature, T,, for the formation of Ti41 in a Ti-8 pct A1 alloy with an interstitial content on the order of that given in Table I is approximately 1245°F. The relationship between the ductility of the binary alloy used in this investigation and T, was estimated from tensile tests on specimens which were exposed for 24 hr at various temperatures followed

Jan 1, 1970

By Nicholas J. Grant, John S. Benjamin

A series of composite alloys containing a high volume of NiAl, Ni3Ah or CoAl, bonded with 0 to 40 vol pct of a ductile metal phase, were prepared by powder blending and hot extrusion. The binder metals were of four types: pure nickel or cobalt, near saturated solid solutions of aluminum in nickel and cobalt, type 316 stainless steel, and niobium. Sound extrusions were obtained in almost all instances. Studied or measured were the following: interaction between the alunzinides and the binders, room-temperature modulus of rupture values, 1500° and 1800°F stress rupture properties, hardness, structure, and oxidation resistance. Stable structures can be produced for 1800°F exposure, with interesting high-temperature strength and good high-temperature ductility. Oxidation resistance was excellent. A large number of experimental investigations have been made of the role of structure on the properties of cermets and composite materials. Gurland,1 Kreimer et al.,2 and Gurland and Bardzil3 have indicated the preferred particle size in carbide base cermets to be about 1 µ, with a hard phase content of 60 to 80 vol pct. The optimum ductile binder thickness was noted to be 0.3 to 0.6 µ.1 Complete separation of the hard phase particles by the binder is important in reducing the severity of brittle fracture.' The purpose of the present study was to produce structures comparable to the conventional cermets, using a series of relatively close-packed intermetal-lic compounds rather than carbides as the refractory hard phase, and to study the effects of binder content and composition on both high- and low-temperature properties. The selected intermetallic compounds were particularly of interest because of the potential they offered in yielding room-temperature ductility. The highly symmetrical structures are known to possess high-temperature ductility and room-temperature toughness. Based on a ductile binder, the alloys were prepared by the powder-metallurgy route to avoid melting and subsequent alloying of the matrix, and were extruded at relatively low temperatures. It was expected that the composite alloy would retain useful ductility. In contrast, infiltration and high-temperature sintering led to alloying of the matrix and to decreased ductility. The systems Ni-A1 and Co-A1 were selected for this study. In the Ni-A1 system the compounds NiA1, having an ordered bcc B2 structure, and Ni3Al(?1), having an ordered fcc L12 structure, were chosen. In the system Co-A1 the intermetallic compound CoAl with an ordered bcc B2 structure was used. ALLOY PREPARATION The intermetallic compounds, see Table I, were prepared by using master alloys of Ni-A1 and CO-A1, with additions of either cobalt or nickel to achieve the desired compositions. The master alloy in crushed, homogenized form, was melted with pure nickel or cobalt in an inert atmosphere, cold copper crucible, nonconsumable tungsten arc furnace. The resultant intermetallic compounds were homogenized at 2192°C in argon, crushed, and dry ball-milled in a stainless mill to -100 and -325 mesh for the Ni-A1 compounds and to -325 mesh for the CoAl compound. Finer fractions were separated for some of the composite alloys. Several ductile binders were utilized. These included Inco B nickel, 5µ ; pure cobalt, 5 µ, from Sher-ritt Gordon Mines, Ltd.; fine (-325 mesh) niobium hydride powder; fine (15 µ) type 316 stainless-steel powder; and near-saturated Ni-A1 and Co-A1 solid-solution alloys, also in fine powder form. The niobium hydride was decomposed above about 700°C in processing of the compacts in vacuum to produce niobium powder. The Ni-7.1 pct A1 and the Co-5.3 pct A1 solid-solution alloys were prepared from pure nickel or cobalt and pure aluminum by nonconsumable tungsten arc melting under an inert atmosphere. The ingots were homogenized, lathe-turned to fine chips, and dry ball-milled in air to -325 mesh powder. These solid-solution alloys are designated NiSS and CoSS; see Table I. Subsequently the hard and ductile phases were dry ball-milled as a blend. Experiments clearly established the need to coat the hard particles with the ductile binder to optimize subsequent hot compaction by extrusion. Ordinary dry mixing usually resulted in nonhomogeneous alloys which were quite brittle. Conventional cermets are consolidated by liquid phase sinteiing or infiltration, which resulis in undesirable and uncontrolled alloying of the binder phase. For this study, a loose (unsintered) powder-extrusion process was emploved, minimizing reactions between binder and hard particle, thereby permitting much greater control of composition and structure. The constituent powders were first mixed in the desired

Jan 1, 1967

By W. A. Backofen, D. Lee

Titanium of commercial purity (RC-70) and two all-a (hcp) alloys (4Al-1/4O2 and 5Al-2.5Sn) were tested in sheet form under conditions of combined-stress loading. Plane-strain compression and plane -strain tension together with uniaxial compression and tension provided information for constructing the tension-tension and compression-compression quadvants of the plane-stress yield locus. Coordinate values were obtained from yield-strength measurements; the slope at each point was based on a plastic-strain ratio. The materials represented a wide range of plastic anisotropy, which was reflected in correspondingly varied departures of the yield locus from that for iso-tropy. The tension-tension and compression-compression quadrants were not identical. If the uniaxial yield strength is insensitive to direction and the sign of the applied stress, the Mises or perhaps the Tresca criterion is adequate for predicting the onset of yielding under combined-stress loading. The prediction is not so straightforward in plastically anisotropic material. Depending upon details of texture, combined-stress yielding resistance may be substantially different from that indicated by the usual criteria.' However. a continuum theory of yielding under such conditions is available for reasonably direct application.2,3 Whether or not it can be used successfully must, of course, depend upon how closely the conditions of the theory are satisfied in the material in question. In its present form the theory contains no provision for Bauschinger-type effects, nor does it allow for the consequences that might grow out of deformation by more than one mechanism, e.g., by slip and twinning.4 With those limitations, more importance must be attached to experimental information about the yield surface for anisotropic materials. Studies of the yield surface have generally been confined to states of plane stress (tension-tension and tension-compression) established in thin-wall tubes by externally applied forces and internal pressure. That approach would be entirely suitable for anisotropic materials if they were available in tube form or in sufficient bulk to be machined into test specimens. 6-9 It would not serve for the textured and anisotropic sheets of much current engineering interest, unless sheet could be formed into high-pressure tubing without structural change. Since there would seem to be little chance of the latter, practical alternatives are needed. One such alternative is the subject of this paper. It involves the use of a few selected but relatively simple uniaxial loading tests on sheet specimens. The underlying idea is presented here with some details relating to application and a few results bearing on how well it has worked. THE BASIS OF TESTING Conventional Measurements. Yielding for a general case of anisotropy is described by the plane-stress locus in Fig. 1. Reference directions in the sheet specimen are related to the stress coordinates as shown with the insert: x is the rolling direction, y the transverse direction, and z the through-thickness direction. The four reference-direction yield strengths (t, tension; c, compression), Xt, Xc, Yt, and Yc, are all different. Nine paths that can be followed in uniaxial loading experiments are identified. Paths 1, 2, 3, and 4 represent conventional tension and compression testing to establish Xt, Yt,.Xc, and Yc. Useful information also comes from the ratio of the transverse plastic-strain components associated with yielding and flow in conventional tension or compression. A condition to be satisfied in locus construction is that the plastic-strain vector be everywhere normal to the locus.10 The projection of the vector which would

Jan 1, 1967

By W. F. Flanagan, D. H. Polonis, S. D. Dahlgren

Rotation diffraction patterns of Cu-4.84 wt pct Si polymystalline samples were taken during the course of isothel-ma1 affing of the suPersaturated a phase, a diffraction spots were obserzled to streak during the initial stages of aging, and this streaking was similar to the streaking of a spots observed earlier by Barvett with deformed super saturated samples of the same composition. Although it was suggested that stacking faults were the sole cause of styeaking in the deformed samples, the present study has shown that plates with one small crystallite dimension can also contribute to the streaking when there is lattice coherency across close-packed planes. THE decomposition of the supersaturated a phase in Cu-Si alloys has been reported to occur by means of both thermal and stress activation.1-4 According to the Cu-Si phase diagram,3 Fig. 1, the supersaturated a phase (fcc) is expected to transform during aging by the precipitation of the y phase. The results of earlier studies2,4 have indicated that metastable k phase (hcp with nearly ideal close packing) forms initially at temperatures below the eutectoid temperature, after which the k transforms to the a and y phases. Hof-mann et al.4 have proposed a metastable version of the phase diagram, showing the approximate boundaries for k formation below the eutectoid temperature. In view of the close-packed nature of both the a and k phases, it is essential to consider the role assumed by stacking faults in the transformation. Streaking effects have been reported by Barrett 1 in the rotating crystal X-ray patterns of strained Cu-Si alloys and were attributed to stacking faults rather than particle size effects. This deduction was based on the observation that streaks in the diffraction patterns did not occur tangent to the 220fee Debye ring. It is known that the atom movements involved in faulting leave some X-ray reflections unaffected while others are broadened,' and, in particular, it has been shown that faulting will not cause streaking of 220fee reflections tangent to the 220fee Debye ring as would be expected if all the reflections were broadened.' The formation

Jan 1, 1967

By S. Leber, R. F. Hehemann

Diffusion coefficients for the Cb-W system were measured using couples prepared from poly crystalline, commercially pure metals. The diffusion coefficients, measured in the temperature range between 1700° and 2300°C, decreased exponentially as the tungsten concentration was increased from 0 to 50 at. pct, then decreased abruptly at higher concentrations. A decrease of two orders of magnitude was observed over the entin? compositional range. The diffusion coefficients were in the range defined by the self-difiusion coefficients of the individual elements, indicating their general validity. An activation energy of 60,500 cal per mole was measured for the 20 pct W composition. Such low values, when compared with energies over 100,000 cal per mole for the pure constituent elements, indicated that transport mechanisnzs more rapid than volume diffusion were contributing substantially to inter dijfusion. Difference should, therefore, be expected between these data and the intrinsic diffusion coefficients. These differences should be significant in the kinetics of 'transport phenomena in practical systems. CONSIDERABLE attention has been devoted in recent years to the mechanical behavior and other properties of the refractory metals and their alloys. The Cb-W system has been of special interest as a base for the development of more complex compositions of commercial interest. In spite of the importance of mass transport to all aspects of elevated-temperature behavior, and especially to the production of alloys by powder-metallurgy techniques, little attention has been paid to diffusion in the Cb-W system. Results from a previous study of this system1 appeared to be anomalously high. The present investigation is, therefore, an attempt to obtain more accurate diffusion coefficients in this system. Intrinsic diffusion coefficients, of primary importance from the theoretical viewpoint, can only be obtained accurately from studies utilizing compositional gradients approaching zero. However, many practical problems involve diffusion under significant concentration gradients. The diffusion coefficients determined in this investigation were, therefore, obtained from couples prepared from elemental metals. The data obtained should be of value in the analysis of problems such as homogenization during powder-metallurgy alloying or reactions between base and clad in coated structures. In this vein, the investigation was conducted on poly crystalline materials of commercial purity. PROCEDURE Diffusion couples were prepared by sandwiching a columbium sheet between two sheets of tungsten. The composite was welded around all edges, the tungsten forming a protective can for the columbium. The composite was soaked for 4 min at 1600°C in a hydrogen-atmosphere furnace, quickly forged to 40 pct reduction in thickness, and then rapidly cooled to room tempera-

Jan 1, 1967

By G. Y. Chin, M. T. Dolan, W. L. Mammel

In the case of plastic deformation by slip, von Mises&apos; showed that an arbitrary shape change of a crystal generally requires the activation of five independent slip systems. The selection of the five active systems was worked out by Taylor ,&apos; who hypothesized that, among all combinations of equivalent slip systems which are capable of accommodating a given imposed strain, the active combination is that one for which the sum of the absolute values of the glide shears is a minimum. Taylor analyzed the case of {lll}( 110) slip for fcc metals and applied the analysis to crystals undergoing axisymmetric flow, which approximates the shape change of an embedded grain in a polycrystalline aggregate deformed in tension (or compression). For the twelve equivalent (111) (110) slip systems, there are 384 independent combinations of five slip systems that satisfy the imposed strain.&apos; Taylor laboriously calculated the value of M = ZjIyj /E for each combination (although some were missed) and obtained the minimum M, hence the active combination, for a number of axial orientations distributed throughout the stereographic triangle. (yj is shear from slip on the th system and e is the tensile strain). Detailed contours of constant minimum M were recently obtained by Hosford and Backofen using a simplified but equivalent Bishop and ill&apos; analysis. Due to the numerous combinations of slip systems involved in the calculations, however, the full potential of the powerful Taylor analysis has not been exploited. For this reason, we have recently utilized techniques of linear programming to obtain solutions of the Taylor analysis for axisymmetric flow, for slip on {110)(< 111), {112)(111), and {123)(111) systems as well as mixed slip composed of these three systems. These slip modes are of obvious importance in the deformation of bcc crystals. Some of the salient results are summarized below. 1) Stress-Strain Data for Polycrystal. The value of M averaged over all axial orientations is the ratio of the tensile flow strength of a randomly oriented aggregate to the critical resolved shear stress for slip. This value enters importantly in theoretical deductions of the polycrystalline stress-strain curve from single-crystal data.2&apos;3&apos;5 Table I lists the values of Ma,, for the several cases of slip, as obtained by the present computer work. 2) Texture Hardening. Since the value of M depends on the axial orientation, the (tensile) flow strength of a specimen may be increased through texture control.&apos; An example of the computer results is shown in Fig. 1, where contours of minimum M have been computer-plotted for the case of mixed slip on {110}(111), {112)(111),and {123}(11 1) systems. It may be seen that, under axisymmetric flow, wires of (111) and (110) axial orientations are 50 pct stronger than those oriented at (100) .

Jan 1, 1968

By D. G. Westlake

Levine has concluded that prismatic slip in titanium is controlled by two distinct thermally activated processes in the temperature ranges O° to 220°K and 220" to 300°K. We feel that his evidence is not convincing. He has drawn a curve through the plot of activation volume u* vs temperature T with a break at 22WK, Fig. 2. We believe that considering the possible experimental error apd the fact that there are only four points between 4° and 196°K, one could be justified to represent these points by the smooth curve we show as a solid line in Fig. 12. Levine believes that (8rf/aT)+ is discontinuous at 220°K, but he hints that he recognizes the possible doubt. We doubt seriously that the results shown in Fig. 1 indicate a discontinuity at 220°K. Certainly if he were justified in drawing a straight line through only four points on Fig. 2, we are even more justified in drawing straight lines through the seven points between 77" and 297°K on Figs. 1 and 3, because a straight line touches all seven of his circles. If his measurements of t were so precise that his decision to draw two curves in Fig. 3 is valid, then the experimental technique is deserving of further mention. We have drawn a smooth curve through the results in Fig. 3 and used this and the curve in Fig. 12 to obtain the values of shown in Fig. 13. Finding continuous is a contradiction of Fig. 4, which deserves comment itself. Levine obtained the solid circles in Fig. 4 using Fig. 2 and a smooth curve through the points shown in Fig. 3. We have replotted these solid circles in Fig. 14. We submit that there is no basis for his two straight lines (dashed in Fig. 14), and therefore have superimposed the curve that we believe is indicated. Certainly, there is reasonable doubt that a discontinuity in dH/dT exists at 220°K, even when one accepts Fig, 2. Furthermore, if one draws the straight lines indicated by least-squares treatments of the results presented as open circles in Fig. 4, their intersection is at about 196°K, not at 220°K as shown. Thus the alleged agreement between Figs. 3 and 4 with respect to "break" temperatures is not apparent. In Fig. 9, Levine has drawn a straight line very much different from the one indicated by a least-squares treatment. Obviously, he has done this because he recognized that H = 0 when T = 0. He is consistent in drawing the low-temperature curves in

Jan 1, 1968

By D. G. Westlake, U. F. Kocks

WHILE single crystals of most materials with cph lattice structure show essentially unlimited ductility, polycrystalline specimens of the same materials exhibit the entire range of ductilities. A difference between the ductility of single crystals and polycrystals may be associated with the special stress concentrations to be expected, for example, at the intersections of slip bands or twin lamellae with grain boundaries. Whether such stress concentrations prove catastrophic depends on the cleavage strength of the material, the size of the stress concentrations, and the speed with which they are formed. Thus, the ductility may vary in degree from material to material. Another possible reason for differences in ductility between single crystals and polycrystals is that a sufficient number of independent deformation modes must be available to insure compatibility between the macroscopic strains in neighboring grains.&apos;&apos;2 This criterion is often taken to be a necessary condition for any polycrystal ductility whatsoever, not as one that determines different degrees of ductility; thus, a material with an insufficient number of independent deformation modes would have to be brittle as a polycrystal. The "sufficient number" is five if every grain is to accommodate arbitrary shape changes ("von Mises criterion "). We should like to argue that fewer than five independent modes may be sufficient to satisfy compatibility conditions; and that the internal stresses set up when the plastic strains are not compatible reach the theoretical fracture stress only after a significant amount of macroscopic strain has taken place which may vary in magnitude from case to case, allowing an influence on the degree of ductility. Experimental evidence for these statements is taken from the following review of the number of independent deformation modes observed in the various cph

Jan 1, 1968

By Yoichi Ishida, Ching-Yao Cheng, John E. Dorn

Tile creep behavior of a iron was investigated over the range of temperatures from 375° to 1150°K. Apparent activation energies for creep, obtained by the effect of sudden changes in temperature on the creep rate, revealed the presence of- four distinguishable regions. The creep behavior of a iron in Regions II (480° to 774°K) and 111 (775° to 1045°K) was found to correlate well with a model where the creep rate is controlled by the nonconsevualive motion. of jogged screw dislocations. An anomalous increase in the apparent activation energy fur creep in Region III was found to be in harmony with the known decrease in the free activation energy for self-diffusion over the Curie transformation range. Furthermore, the creep rates in Regions II and III were found to increase with stress due not only to the effect of stress on the activation energy but also to an increase in density of mobile dislocations. The evidence suggests that pipe diffusion along moving dislocations could be a significant factor over the lower temperatures of Region II. ALTHOUGH the creep properties of iron and steel have been of interest to metallurgists for some time and an extensive literature is now available, most of the published information has not produced much toward understanding the fundamental dislocation processes controlling the creep behavior of these materials. Whereas the activation energy for high-temperature creep of metals usually agrees well with that for self-diffusion, Sherby, Orr, and Dorn1 deduced from the data of Tapsell -and c1enshaw2 that the activation energy for creep of Armco iron is about 78,000 cal per mole and more recently Lytton and sherby3 reviewed the data of Jenkins and Mellor4 and found an activation energy for creep of a iron of 80,000 cal per mole. Both values are substantially greater than the activation energy for self-diffusion in a iron. Because of the limited data suitable for purposes of identifying the controlling dislocation mechanisms of creep and the unusually high activation energies for creep quoted above, it was considered desirable to reinvestigate in detail the creep of a iron by more reliable techniques which would provide sufficient data for determination of the creep mechanisms. EXPERIMENTAL TECHNIQUE Creep specimens were prepared from 3/8 by 4 in. iron bar stock of the following composition by weight percent: 0.001 C, 0.0120 0, 0.001 N, 0.004 S, and 0.003 P. The as-received bars were cold-rolled to a thickness of 0.100 in., annealed under argon for 30 min at 1113°K, cold-rolled to a final thickness of 0.063 in., and machined into tensile specimens having gage section 0.250 in. wide and 1.70 in. long. Finally they were recrystallized under argon at 1113°K. Specimens to be crept above 1060°K were recrystallized at 1173°K. Both recrystallization treatments gave the same reproducible equiaxed ASTM No. 4 grain size. Creep testing was conducted in machines fitted with Andrade-Chalmers arms that maintained a constant stress to within ±0.2 pct of the reported values. Deformation over the specimen gage section was sensed with a linear differential transformer and recorded auto-graphically as a function of time. The strains deduced from these measurements were sensitive to ±5 x 10-5. During creep the specimens were contained in an argon-filled chamber which was immersed in a temperature-controlled molten tin bath. Creep temperatures, as measured by thermocouples attached to the specimen, were maintained to within ±10.25°K of the reported values. For activation-energy determinations rapid changes in temperature of about 12°K were obtained within 30 sec by direct resistance heating of the creep specimen, and maintained to ±1°K of the reported values. Observations of structural details of specimens before and after creep tests were made by electrolytic polishing and etching in acqueous ammonium persulfate. EXPERIMENTAL RESULTS A typical example of the determination of apparent activation energies, Q, by the effect of small changes in temperature is illustrated in Fig. 1. Q is defined by

Jan 1, 1967

By N. L. Svensson

The model developed by Tuylor for the calculation of Polycrystalline yield strength has been applied to the case of an aggregate hawing a preferred orientation. In general this procedure requires the specification of texture by means of weighting factors applied to specific orientations. The problem to which the model has been applied is that of the yield-strength aniso-tropy of cold-rolled aluminum whose rolling texture was described as a combination of (110)[112] and (311) [112] In this case yield-strength anisotropy is defined by the rutio of yield strength measured at an angle 8 to the rolling direction to that measured along the rolling direction. The method of calculation of yield-strength ratio as a function of ? is described and the results show good agreement with experimental values. The orthotropic yield criterion suggested by Hill has been applied to the results and the strain ratio R also calculated as a function of ?. This has been compared with calculations using the method suggested by Elias, Heyer, and Smith which does not exhibit suck good agreement with observation. one deficietlcy of the method presented is that the strain ratios used by are those applying to iso-Irobic materials. The method should therefore be reg-clrded only as a first abbroximation to the prediction of anisotropy. THE problem of calculating the stress-strain characteristics of polycrystalline aggregates from the properties of single crystals has attracted attention for a number of years. The most important contributions to this study have been those due to: Sachs,&apos; Cox and sopwith,2 Taylor,3 Kochendorfer,4 Batdorf and Budiansky,5 Calnan and Clews,6 Bishop and Hill,7,8 Kocks,9 Budiansky, Hashin, and sanders, 10 Kroner,11 Cyzak, Bow, and payne, 12 Budiansky and Wu,13 and Lin.14 While the earlier work has been largely superseded, recent developments tend to support Taylor&apos;s solution" within the restriction imposed by his assumptions. The essential features of Taylor&apos;s approach were: 1) the material is rigid-plastic; 2) each grain experiences the same strain components as the aggregate as a whole (the problem was that of uniaxial deformation with principal strain components in the ratio 3) all regions of each grain deform uniformly; 4) work hardening occurs equally on all slip systems. While Bishop and Hill7 have generally validated this approach, there has been some criticism offered. Kocks? as pointed out that since multiple slip must occur the single-crystal data must be determined from orientations arranged such that polyslip takes place. Boas and Hargreaves,15 and others, have shown experimentally that the strain distribution within grains is not uniform, the strains in the vicinity of grain boundaries being less than those in the center of the grains. Both of these criticisms can be largely offset by the suitable choice of single-crystal critical shear stress. However, for the problem analyzed below, the critical shear stress is not directly used and, consequently, these criticisms lose their importance. The more recent contributions have attempted to obtain a more complete analysis by considering an elas-toplastic material and considering interactions between grains of differing orientations. Lin14 has considered the early stages of yielding for a polycrystalline aggregate having specific regions of defined slip plane orientations. On the other hand, Budiansky and Wu13 have allowed for these interactions for randomly disposed grain orientations and have calculated the polycrystalline stress-strain curves for crystals exhibiting either elastic-ideally plastic or kinematic hardening characteristics. This work has shown that yielding commences when the macroscopic stress is 2.2 times the critical shear stress for slip in a single crystal (7,). The yield stress-strain curve then rises becoming asymptotic to a value of 3.072 7,. This is close to the value obtained by Bishop and Hill (3.06) in their confirmation of Taylor&apos;s method. This, of course, is to be expected since, at large strain values, the elastic strains are negligible and the rigid-plastic model is satisfactory. The results of Budiansky and Wu indicate that the result obtained by Taylor is 7.7 pct high at a plastic strain which is two times the elastic strain at the initiation of yield. By defining the anisotropy in terms of relative values, the ratio of yield strength at orientation ?, to that measured in the rolling direction, the effect of the discrepancy in Taylor&apos;s solution is considered to be of lesser consequence. Therefore, it is anticipated that an analysis based on Taylor&apos;s solution, which can be quite straightforward, should provide a reasonable estimation of the anisotropy of materials having a preferred orientation texture. OUTLINE OF TAYLOR&apos;S METHOD In fee metals there are four possible slip planes (the octahedral planes) and in each there are three possible slip directions (the edges of the octahedron), that is a total of twelve possible slip systems. von Mises16 has shown that at least five independent slip systems must become operative in each grain of the polycrystalline aggregate in order to preserve continuity of strain. With this geometrical requirement as basis and the assumptions previously listed, Taylor determined the operative slip systems for a number of orientations of the tensile stress axis specified in the unit stereographic triangle. For the ith slip system, the critical shear stress

Jan 1, 1967

By S. H. Gelles

Samples of poly crystalline zinc of 99.999+ pct purity were observed metallographically after having been exposed to hydrostatic pressures of up to 27 kbars. The deforrnation produced by this treatment was analyzed using X-ray and metallogaphic techniques. Basal-plane slip occurred universally in all grains exumined at the lowest pressure used (8 kbars). At pressures of >23 kbars, {1012} twin nucleation and growth were noted as well as slip. Formation of bend planes, complex kink bands, and recrystallization at the gain boundaries were also observed in this pressure range. These observations are discussed in reference to the expected deformation behavior of zinc under high hydrostatic pressure. It has been shown over the past few years1&apos;3 that anisotropic, poly crystalline metals can be made to deform plastically by the application of a hydrostatic pressure. The effect is greater 1) the larger the anisotropy of linear compressibility and 2) the smaller the stress level needed to produce plastic deformation. Zinc having both very anisotropic linear compressibilities and a very low critical resolved shear stress (CRSS) for basal-plane slip has been shown to exhibit large amounts of plastic deformation when subjected to a hydrostatic pressure.2,3 At pressures up to 15 kbars, grain boundary migration and slip on one set of glide planes have been reported.&apos; After exposing samples to 20 kbars pressure, grain boundary migration, single slip, multiple slip, and twinning have been noted.&apos; The identification of the deformation modes operative under these conditions has not been reported. It was the purpose of this research to identify the deformation modes induced in poly crystal line zinc by the action of a hydrostatic stress and to study the strain accommodation at grain boundaries. Hydrostatic pressure could affect the operational modes of deformation by altering the Peierls-Nabarro stress. This may be roughly approximated by the relationship4

Jan 1, 1967

By P. Marier, T. R. Ingraham

When cylindrical powder compacts of nickelous oxide (NiO) are heated in an equilibrated stream of SO3, SO,, and 02, in the temperature range 500°to 800°c, tlickelous suljate (NiSO4) is formed as an adherent layer on the oxide. The reaction is diffusion-controlled, with an activation energy of 13 ± 3 kcal per mole. When cylindrical powder compacts of NiSO4 are heated in a stream of dry nitrogen in the temperature range 1000 0to 11500C, NiO is formed at a well-defined interface between the sulfate and oxide. The interjhce migrates into the sulfate at a constant rate at a constant temperature and gas flow. The reaction rate increases with increasing gas flow and decreases with increasing partial pressure of SO3 in the gas stream. Resolution of the partial-pressure data with a Lang-itzliir Adsorption Isothern suggests that about 80 pct of the NiO interface is covered with SO3. The heat of adsovption is about 68 kcal per mole. The activation energy of the decomposition process is 61 ± 3 kcal per mole. MOST of the work reported on the formation and decomposition of nickel sulfate is related to thermodynamics.1-3 No quantitative work has been reported on the decomposition process. The only kinetic work reported on the formation is that by Fletcher and shelef.4-6 whose main purpose was to study the effects of alkali metal sulfate additions on increasing the rate of nickel sulfate formation. They found that, in the absence of an additive, only small amounts of sulfate were formed and the kinetic data were difficult to interpret. However, they suggested that the sulfa-tion of nickel oxide is a diffusion-controlled process for which the activation energy is approximately 17 kcal per mole.6 In this paper, both the formation and decomposition reactions will be examined; and based on the effects of temperature, flow rate, interfacial area, and partial-pressure of sulfur trioxide, mechanisms and activation energies will be suggested for both processes. EXPERIMENTAL Material. The nickel source material used in all experiments was Baker and Adamson Reagent Grade NiSO4. 6H2O, for which the following analysis was supplied by the manufacturer: C1, 0.001 pct; NO3, 0.005 pct; Co, 0.02 pct; Cu, 0.005 pct; Pb, 0.002 pct; Fe, 0.001 pct: insol, 0.005 pct. The anhydrous sulfate was prepared by heating the hydrate at 420°C in a muffle furnace for 5 hr. Nickel oxide was prepared by decomposing the sulfate at 950°C over a period of 10 hr. Method. The technique used for measuring the rates of formation and decomposition was developed earlier in these laboratories.7-8 The method is based on the observation that the kinetic parameters of a reaction can be established in a flow system, with specimens prepared by compacting powder to a uniform pellet shape. The results are identical with those established with solid polycrystalline specimens or single

Jan 1, 1967

By B. W. Roberts, V. A. Phillips

A copper alloy containing- 25.5 at, pct Zn and 19.0 at. pct Ni, which was previously found to show an anoma1old.s hardening effect on quenching- from 600 "C and aging- at 400oc, has now been examined by neutron diffraction. No evidence of long-range order was found. The aged sample showed diffuse scattering- consistent with clustering. The anomalous hardening effect is now attributed to lattice strains caused by clustering rather than (long-range) order hardening. SOLID-solution Cu-Ni-Zn alloys (the commercial &apos;nickel silvers") have been reported to show anomalies in: change of resistivity on cold working,1-6 temperature coefficient of resistance,2-12 resistivity at low temperatures,13,14 parameter (vs temperature),2"4 calorimetric data,2,4 specific heat,15,16 dilation,2-4 and elastic modulus.17 The structure responsible for the anomalies is produced by annealing typically near 400°C and is rather loosely referred to as the (&apos;K-Zustands" (K state), a term coined by Thomas1&apos; who apparently meant simply that the arrangement of atoms on the sites deviated from that expected statistically. Thomas proposed that the K state occurred in a variety of (solid-solution) alloys such as Cu-Ni-Zn, Ni-Cr, Ni-A1, Ni-Cu, Fe-A1, and Fe-Si and is recognized because its formation is strongly temperature-dependent and results in an increase in electrical resistance which can then be decreased by cold working. Later workers on (&apos;nickel silver" have interpreted the K state variously as short-range order, long-range order. or a combination. The present work was prompted by the discovery by Phillips and Jones19 of a substantial hardening effect when an 18 pct "nickel silver" alloy which is fairly close to the Cu2NiZn composition, was reheated in the range 150" to 450 C after previously quenching from 600°C or, alternatively. was slow-cooled from 600°C or above. The phenomenon was attributed to (long-range) order hardening. Due to the similarity in the atomic scattering factors of copper. nickel, and zinc atoms, the &apos;&apos;nickel silvers" are unfavorable for X-ray diffraction studies aimed at detecting ordering. Nevertheless Bialas et a1.,20 using a powder sample containing 47.96 wt pct Cu, 24.03 wt pct Ni, and 27.98 wt pct Zn, slow-cooled from 400" to 200°C taking 500 hr, observed weak super lattice lines. Further unpublished work" using an anomalous dispersion X-ray technique indicates that zinc atoms are regularly ordered at the corner points of the lattice cell, while the nickel and copper atoms are statistically distributed on the remaining sites. Köster 17 also observed X-ray superlattice lines, for example, in an alloy containing 43.5 wt pct Cu, 28.6 wt pct Ni, and 27.9 wt pct Zn superimposed on the basic fcc cell with a = 3.62 kX. He proposed a Cu3Au-type superlattice with the Ll2 structure in which the A sites were statistically occupied by copper and nickel atoms and the B sites by zinc. He adds that substitution must be possible so that zinc atoms partly occupy A sites. Below about 35 pct Cu, Koster had some evidence for a CuAu-type superlattice with the Llo tetragonal fcc structure with a = 3.82 kX, c/a = 0.88 which could be preserved by quenching. This is suggested17722 to correspond to CuNiZn. While the present work was in progress Hirabaya-shi et a1.23 made an independent comprehensive neutron-diffraction study of a single crystal containing 50.05 at. pct Cu, 26.57 at. pct Ni, 0.25 at. pct Mn, 0.13 at. pct Fe, balance zinc. The presence of manganese and iron is surprising since the crystal was supposedly grown from high-purity metals. The homogenized crystal showed evidence of long-range ordering after an anneal of 5 months at about 300°C. Three possible crystal models were proposed. A curious feature of their results23 is that they could not find any neutron-diffraction evidence of ordering in a powdered polycrystalline near-stoichiometric Cu2NiZn alloy. There appears to be some essential difference between a near-stoichiometric Cu2NiZn alloy and one somewhat further off stoichiometry as used by the present authors. Thus Sato14 was able to reproduce the low-temperature resistivity anomaly reported by one of the authors13 on the present alloy if he used a similar composition, but found the normal behavior of the residual resistivity in a near-stoichiometric alloy. satol2 found that the resistivity of a cold-drawn slightly off-stoichiometric alloy increased to a maximum on isothermally annealing at 300°C and then decreased ("over-aged"). Since he could not explain this on the basis of ordering phenomenon, he proposed that zinc atoms were segregating to stacking faults (Suzuki effect) and found etching bands on the surface by replication which were attributed to the widening of faults. Sato suggested14 that the hardening effect observed by Phillips and Jones19 is partly due to the Suzuki effect. EXPERIMENTAL The starting material was 1/4-in.-diam hard-drawn rod of a commercial 18 pct "nickel silver" alloy identical with that used in a previous study by Phillips

Jan 1, 1967

By B. H. Kear, S. M. Copley

A dynamic theory of precipitation hardening in alloys containing cohevenl, stvess-.free, ordered particles is developed. The yield stvess is predicted from the stress dependence of the plastic strain vale, which is related to a derived dislocation velocity-stress function. The theory is shown to predict the magnilude and temperature dependence of the yield stress of a commercial nickel-base superalloy as well as many details of its slip structure. GLEITER and Hornbogen have developed a theory of the yield stress in alloys hardened by coherent, stress-free ordered ptrticles based on the observation that dislocations (b = a/2 (110)) glide in pairs.&apos; When a dislocation pair shears through an ordered particle, the glide motion of the leading dislocation is impeded since it must create antiphase boundary (APB), whereas the motion of the trailing dislocation is assisted because it annihilates APB produced by the first one. Taking into account the APB energy, the size, and spacing of the particles, G-H predict the observed yielding behavior in Ni/18.8 Cr/6.2 A1 alloys composed of a matrix phase y &apos;(nickel-solid solution) and particles of y&apos; (basically Ni3A1). The G-H theory, as well as all previous theories of hardening by coherent ordered particles, do not include the details of dislocation motion; the present dynamic theory is an attempt to overcome this limitation. In the dynamic theory, the yield stress is predicted from the stress dependence of the plastic strain rate, which is related to a derived dislocation velocity-stress function. This function can be evaluated if the structure of the alloy, the APB energy of the ordered phase, and the characteristic drag or frictional stresses of the matrix and precipitate phases are known. The theory is shown to account for the observed temperature dependence of the yield stress in a commercial nickel-base superalloy. 1) NICKEL-BASE SUPERALLOYS Although their compositions are complex, the nickel-base superalloys have remarkably simple structures. A detailed examination of the commercial superalloy

Jan 1, 1968

By Henry M. Otte, Ralph P. I. Adler

The changes of line position and integral line breadth in the X-ray diffraction pattern of a polycvys-talline Cu-30Zn tensile test piece, incrementally loaded (and unloaded) up to fracture, have been an-alyzed in detail. The stacking-fault probahility, cv, increased linearly with increasing strain, E, wheveas the effective domain size, De(hkl), decreased with decreasing E-1 Over the greater part of the stress-strain curve the rate of work hardening was essentially constant (about 86 kg per sq mwz), and could be correlated with the slope of stage II of the single-crystal stress-strain curve. Consequently the theories of work hal-dening (particularly those parts relating to stage 11) as developed by Mott and Hivsch and others could be applied to the observations made on the polycrystalline brass. A relationship of the form Aa = Aao - MhklEhkl between the change, Aa, in the extrapolated lattice pararneter and the rvns strain, Ehkl, was derived and found to fit the results acceptably well. From this and other relationships developed in the papev it was estimated that the equilibrium stacking-fault energy of Cu-30Zn was between 8.4 and 12.5 ergs per sq cm, in fuirly close agreement with the (corvected) value obtained by Howie and Swann (1961)43 using transmission electron microscopy. The theory of work hardening in the jorm developed and recently presented by Hirsch (1964)3 successfully described all the pvesent observations. In order to test certain aspects of the theories of work hardening, as developed by Mott,1 Hirsch,2,3 Seeger et el,4-7 and others (for review see Nabarro, Basinski, and Holt8), several recent investigations have been concerned with relating the dislocation density, p, with the shear stress, 7 (and strain, y), applied to the specimen. The results of these investigations have shown that the square root of the dislocation density appears to be linearly related to the applied shear (or flow) stress for fcc as well as bcc metals and alloys. Furthermore, the relationship appeared to apply not only to the deformation of poly-crystalline specimens, but also to stages I and I1 of the deformation of single crystals. An expression of the form has thus come into wide use. Here b is the Burgers vector for a total dislocation, G is the shear modulus, and 70 and q are constants. A review9 of available values of q shows it to have values (at room temperature) in general between 0.3 and 0.6. Forms of Eq. [1] can be deduced from, or predicted by, the current theories, and the various constants adjusted so that they are compatible with the experimentally found value of q . No unique relationship has yet been found between the dislocation density and the applied shear strain. There are several serious objections to the use of Eq. 11]. In the first place, it relates the shear stress to the density of the dislocations without regard to their arrangement, type, or distribution; the significance of the relation may therefore be justly questioned.5 In the second place, the values of the experimental quantities usually substituted into Eq. [11 are those of the applied shear stress and the total dislocation density measured after unloaditzg. The dislocation density value that should in fact be used is that for the mobile dislocations present in the specimen when under the applied load.* Finally, in cases where the values used for p, the dislocation density, are those obtained by electron microscopy, p is subject to considerable error,&apos; both systematic and random. The corrections to be applied are still controversial. Dislocation densities can also be measured by etch-pit and other techniques,&apos;&apos; each having their specific limitations. An objective of the present investigation has been to obtain information about the dislocation configyration and distribution by analyzing the changes in the position and shape of X-ray diffraction profiles as a function of deformation. The X-ray techniques employed, also open to criticism, have certain advantages, however. Thus, although the X-rays diffract only from the surface layers to an effective depth of about 20 p, the measurements can be made while the specimen is under load. The value of the dislocation density obtained by the X-ray method is also subject to errors, which are different from those of the electron microscope. Though a considerably larger volume of material is sampled by the X-rays, thereby reducing some of the statistical errors inherent in the electron microscope data, the information obtained is less detailed and is dependent on the method of analysis used to obtain a value for the dislocation density. Nevertheless, important observations can be made because the aforementioned advantages outweigh some of the limitations. In the present paper the X-ray method is briefly described and applied to a brass specimens deformed in tension. The results are then discussed in terms of some of the current concepts of work hardening. 1) EXPERIMENTAL PROCEDURE Details have already been extensively published elsewhere11-14 and therefore will only be dealt with briefly here. 1.1) Materials and Specimen Preparation. Commer-

Jan 1, 1968

By Y. H. Liu, G. W. Powell

Thin foils made from the gold-rich region of- short (0.15 mm)Au-Ag diffusion couples annealed at 880°C for 1 hr were examined in ax electron microscope and the structures were compared with that of pure gold subjected to identical heat treatments. The couples underwent Plastic deformation (bending) during the diffusional anneal. The foils prepared from the diffusion zone have a higher dislocation density and incidence of subboundaries than pure gold. The plastic bending of the couple can be interpreted in terms of the climb of edge dislocations, which are pavallel to the bend axis, along the direction of diffusion. THE interaction of lattice defects during interdiffu-sion between two metals has been considered by several investigators. In particular, da Silva and Mehl,1 Barnes,&apos; and Bardeen and Herring3 have proposed models based on interactions between point and line defects to account for the Kirkendall effect (marker movement). Each of these models is based on dislocation climb, which can either add or remove lattice planes, induced by an under- or supersaturation of vacancies. A theoretical treatment of the nucleation and growth of voids by the condensation of vacancies has been presented by Seitz.4 Stresses can arise in a binary diffusion couple as a result of the vacancy flux and the gradient in the lattice parameter. rinkmman&apos; has investigated the effects of diffusion-induced stresses on void formation; the results of his analysis suggest that voids can form and grow under the influence of these stresses in the absence of an excess vacancy concentration. The relationships between vacancy supersaturation and diffusion-induced stresses and void formation have been elucidated also by Balluffi and seigle6 who concluded that the stress generated by a vacancy supersaturation aids the growth of voids. Experimental evidence which indirectly shows that stresses are produced by chemical diffusion has been obtained by several researchers.2,7-9 This evidence consists in part of the observation by light microscopy of the formation of subgrains, a process characteristic of the high-temperature deformation of some metals during creep.&apos;0 More striking, however, is the plastic bending of short (0.2 mm) Cu-Ni couples observed by Barnes2 and of boron-doped silicon crystals reported by Queisser.9 Diffusion-induced dislocations in iron and silicon have been investigated by Ainslie et a1.11and Schwutte and Queisser,12 respectively, the former using transmission electron microscopy and the latter an X-ray transmission technique. Matthews and Crawford13 observed the formation of boundaries by the climb of interfacial misfit dislocations in thin, vapor-deposited Au-Pd couples diffused in situ in an electron microscope. In order to obtain additional information on the phenomena associated with defect interaction and diffusion-induced stresses in binary couples, an electron transmission study of foils prepared from the diffusion zone of short Au-Ag couples was undertaken. The initial objective was to investigate the processes occurring at various points of the diffusion zone. Subsequent research demonstrated that foils could be prepared only from the gold-rich region of the diffusion zone using the technique described herein. EXPERIMENTAL PROCEDURE Preparation and Annealing of the Diffusion Couples. The couples were made from annealed, high-purity (99.999 pct). polycrvstalline gold and silver sheets (0.075 mm thick). Shall (0.075 by 5 by 17 mm) elec-tropolished coupons of gold and silver were pressure-bonded by heating the two metals in a graphite device to 770°C and holding at this temperature for approximately 30 min. The quality of the bond was ascertained by metallographic examination at 150 times. Each couple subsequently was annealed at 880°C for 1hr; under these conditions, the extreme portions of the

Jan 1, 1968

By W. L. Phillips

Stress-train curves were obtained for single crystals of silver, Ag-5 pct Zn, Ag-10 pct Zn, and Ag-20 pct Zn tested in tension and shear at 78°, 195°, and 297°K. At room temperature the critical resolced shear stress gC increased, the length of&apos; the easy-glide region increased, and the rate of&apos; work hardening dwving easy glide decreased with increasixg zinc concentration. The change in the ratio of uc at room temperature to that at lower temperatures was significantly greater for the alloys than for pure silver. It was found that an increment in stress was necessary to continue slip when the slip direction was rotated 60 deg. The magnitude of this increment increased with strain for all alloys, increased with zinc concentration for a given strain, and for a given strain increased with decreasing -temperature. DESPITE its practical importance in improving the mechanical properties, alloying is not fully understood. Except for copper alloys few sets of systematic data are available. Von Goler and Sachs&apos; studied the deformation of Cu-Zn alloys of increasing zinc content and found that, for dilute alloys, the critical resolved shear stress increases linearly with concentration. The range of easy glide was found to increase with increasing zinc content. Schmid and seliger,2 Sachs and Weerts,3 and Osswald4 have shown that with Mg-A1, Au-Ag, and Cu-Ni crystals, respectively, the critical resolved shear stress also varies linearly with concentration. More recently, Linde and his coworkers have investigated the variation of the critical shear stress of copper alloyed with tin , antimony, indium, germanium, silicon, nickel, and gold. They found that the slope of the critical resolved shear stress is related to the change of lattice parameter with composition, and also to the difference in Goldschmidt&apos;s atomic diameter between solvent and solute atoms. Garstone, Honey-combe, and creetham6 have shown that similar relationships can be found for small additions of silver, gold, and germanium to pure copper. They found that, with increasing silver or gold concentration, the critical shear stress for glide is increased by alloying, and so is the range of easy glide, which reaches as much as 60 pct for 0.50 pct Ag alloy and 0.62 pct Au alloy, as compared to 6 pct for pure copper of similar initial orientation. They also found that the alloying additions had little effect on the rate of hardening during easy glide, the slope scarcely changing with increasing alloy content. General secondary slip was detected only when the crystals began to harden rapidly. Although the slip appeared to be very fine in the early stages of deformation, coarser slip bands were formed towards the end of the extensive easy-glide range. The present investigation describes the deformation characteristics of single crystals of Ag-Zn containing different concentrations of zinc. Tension and shear testing were used for this study. EXPERIMENTAL PROCEDURE The method of growing the single crystals, sample preparation, and method of testing have been described in detail previously.&apos; EXPERIMENTAL RESULTS A) Tension-Room Temperature. The initial orientations and stress-strain curves of single crystals of silver, Ag-10.0 pct Zn, and Ag-20.0 pct Zn are shown in Fig. 1. It is evident that there is considerable change in the stress-strain characteristics as a function of zinc concentration. The effects of zinc concentration on the critical resolved shear stress for both CU-zn8 and Ag-Zn alloys are summarized in Fig. 2. At all concentrations the resolved shear stress of the Cu-Zn alloys is higher than that of the Ag-Zn alloys. The resolved shear stress increases parabolically as a function of composition for both alloy systems. The length of easy-glide region increased with increasing zinc concentration, Fig. 3b). As the length increased the slope (do/de) decreased slightly, Fig. 3(b). Metallographic investigations demonstrated two significant effects of increasing zinc concentration. First, the amount of clustering increased, compare Figs. 4(a) and (b). The slip lines changed from uniform in pure silver to clustered in the Ag-20 pct Zn and Ag-30 pct Zn alloys. Second, the amount of cross slip decreased as the amount of clustering decreased.

Jan 1, 1968

By Raymond C. Boettner

The present work had for its purpose: 1) the identification of crack nucleation sites in AISI 4340, quenched to martensite and tempered over a range of &apos;temperatures; and 2) the comparison of fatigue processes in AISI 4340 with processes observed previously in pure metals From constant def1ection-bending fatigue tests, martensite boundaries were identified as the favored crack nucleation sites in quenched and tempered AISI 4340. It, also, was concluded that the fatigue processes operating- in this lous-alloy steel were similar to Processes observed in pure tnetals. ALTHOUGH much engineering data has been accumulated on the fatigue properties of quenched and tempered martensitic steels,&apos; fatigue as a process is not as well understood in martensite as it is in pure metals.&apos; Important features of the fatigue process, such as the identity of the nucleation sites, have not been determined in the commercially important high-strength low-alloy structural steels. The present work had for its purpose: 1) the identification of crack nucleation sites in a low-alloy steel, i.e., AISI 4340, which had been quenched to martensite and tempered over a range of temperatures; and 2) the comparison of fatigue processes in the AISI 4340 with processes observed previously in pure metals. This comparison of the fatigue processes in the different tempers was restricted to the high-strain low-cycle part of the S-N curve. Under these test conditions, previous work on a number of metals has shown that a large number of cracks are nucleated in less than 30 pct of the fatigue life.3 Furthermore, crack nucleation sites are not restricted to inclusions but are also associated with intrinsic structural characteristics of the metal. MATERIAL A 20-lb ingot of vacuum-melted AISI 4340 (for composition see Table I) was hot-rolled to 1-in.-diam rod and then cold-rolled to a 1-in.-wide strip, 0.08 in. thick. Fatigue specimens, see insert of Fig. 1, were machined from the strip with the long dimension parallel to the rolling direction. m this orientation, the stringers of 1 to 2 p inclusions present in the sheet lay parallel to the stress axis in the specimens. The specimens were austenitited at 2050°F in order to obtain a large prior austenite grain size, i.e., 2 mm, which facilitated the subsequent identification of the prior austenite boundaries. A helium atmosphere was used to minimize decarburization. After austenitiza-tion at 2050°F, the specimens were transferred to a 1450°F furnace so that specimen distortion was held to a minimum in the subsequent oil quench. Previous work4 indicated that refrigeration in liquid nitrogen prior to tempering reduced the percentage of retained austenite in the quenched specimens to less than 5 pct. Tempering was carried out in air over the temperature interval of 200°to 800°F to produce a range of mechanical properties, Table I. The preparation of the fatigue specimen was completed by grinding about 0.005 in. from each surface and electropolishing in a chrome trioxide-acetic acid solution for 30 min. Examination of etched cross sections of specimens prepared in this fashion showed the foregoing specimen preparation to be adequate for the removal of the decarburized layer present after the heat treatment. Transmission electron microscopy showed that the as-quenched microstructure of this alloy consisted of a mixture of martensite plates containing either a high density of dislocations or microtwins. Previous work5&apos;6 indicated that in the course of oil quenching autotem-pering resulted in the formation of E carbide on the martensite and microtwin boundaries. Tempering for 2 hr at temperatures up to about 400°F resulted in further precipitation of the E carbide. Finally, at about 400°F, cementite began to replace the E carbide on the martensite and microtwin boundaries in addition to forming a Widmanstatten structure within the plate matrix. EXPERIMENTAL S-N curves were obtained using electropolished specimens cycled at 1800 cpm as cantilever beams in fully reversed bending at selected constant deflections. The deflections were translated into surface strains by means of a calibration curve obtained through the use of strain gages. An argon atmosphere was used to minimize environmental effects. To investigate the development of fatigue slip bands, the specimens of the different tempers were unidirec-tionally bent to a surface strain of 0.005 to 0.007, photographed to record the location and appearance of slip bands so introduced, and then cycled to failure

Jan 1, 1968

By John E. Hockett

The need for basic information about the relationship between resistance to dejormatim (flow stress), temperature, strain, and strain rate, for the solution of metal-fovming problems, is pointed out. Some early attempts to satisfy the need are mentioned. A brief description of a machine called a Cam Plastome-ter is given, including the processing of results of testing in the machine. Next, a program of testing aluminum in compression over a wide range of constant true-strain rates (0.1 to > 200 sec-1) and a modevately broad range of temperatures (223° to 673°K) is described. The results of this program are presented in the form of true-stress us true-strain cuvves. The data in these curves are presented in the form of relationships between true stress and true-strain rate in sermilogarithmic and log-log form, as functions of temperatures—for several true strains. Finally, true stress, for a given true strain, is displayed as a function of log true-strain rate and absolute temperature, i.e., a surface. SINCE the publication of Hill&apos;s book1 on plasticity theory, increasingly rapid advances have been made in analytical solutions to forming problems. Methods in common use are the slab method, the uniform deformation energy method, the limit analysis method, the slipline field method, and the semiexperimental method called "visioplasticity". These approaches, and examples of their use, are covered in detail by Johnson and Melloor2 and by Thornsen, Yang, and Kobayashi.3 unfortunately, practically all of the above work has had to rely upon a number of basic assumptions, e.g., homogeneous deformation and Coulomb (sliding) friction; and virtually no dependence of the mechanical behavior of the deforming metal, upon temperature, strain, and strain rate, has been included. It is with this dependency that this paper is concerned. Loizou and sims4 looked at the above relationship for lead using both a constant compression-speed Cam Plastometer and a constant true-strain-rate Cam Plastometer designed by Orowan.5 Alder and Phillips8 investigated the relationships for aluminum, copper, and steel in the same constant true-strain-rate Plastometer. cook7 tested twelve steels at temperatures ranging from 1170° to 1473°K in the same Plastometer over a range of true-strain rates of 1.5 to 100 sec-&apos;. The writer tested commercially pure aluminum at room temperature and depleted uranium at temperatures from 573" to 873°K at strain rates from 10-3 to 1.0 sec-1 in a Cam Plastometer designed and built at Los Alamos Scientific Laboratory.8 During the past few years the Cam Plastometer at Los Alamos has been used for a number of relatively minor experiments on brass, mild steel, duralumin, Armco iron, and depleted uranium. In this time the machine has been continually modified and improved. It was decided to utilize fully the wide range of strain rates now available with the machine by testing a material about which some information was already in the literature. Prior work on commercially pure aluminum6 appeared to deserve confirmation and expansion. So it was decided to explore the resistance to compression of this material over the currently available range of constant true-strain rates and a convenient range of temperatures. This paper is a report of that exploration. I) EQUIPMENT AND PROCEDURE The principal item of equipment is, of course, the Cam Plastometer, the working part of which is shown in Fig. 1. In this figure, an aluminum specimen may be seen between two tungsten carbide platens, in position for a room-temperature test. Above the upper carbide platen is a load cell. Output from the load cell is amplified and applied to a galvanometer in a recording oscillograph. Auxiliary equipment includes the oscillograph, the control console, a counter, and a time-mark generator. The counter is first used in adjusting the time base. Then it registers the count, of sixty pips per revolution generated by the rotating cam, in each second. These pips and the time base are also applied to galvanometers in the oscillograph. Thus, load, time, and cam position are recorded simultaneously. Heating of a specimen prior to compression is done

Jan 1, 1968