By A. L. Pranatis, G. M. Pound

Changes in length of copper foils of varying thickness and grain size were measured under such conditions of low stress and high temperature that it is believed that creep was predominately the result of interboundary diffusion of the type recently discussed by Conyers Herring. The surface tension of copper was calculated and results confirmed previous work within the limits of experimental error. Under the assumption of viscous flow, viscosities were calculated as a function of temperature and grain size. Predictions of the Nabarro Herring theory of surface grain boundary flow were borne out fully and the Herring theory of diffusional viscosity is strongly supported. ONLY a relatively few techniques for obtaining the surface tension of solids are presently available. Of these, the simplest and most straight forward is the direct measurement of surface tension by the application of a balancing counterforce. Thin wires or foils are lightly loaded and strain rates (either positive due to the downward force of the applied load or negative if the contracting tendency of surface tension is sufficiently greater than the applied stress) are observed. By plotting strain rates against stress, the load which exactly balances the upward pull is found and a simple calculation yields a value for the surface tension. The technique is of comparative antiquity, and solid surface tension values were reported by Chapman and Porter,' Schottky; and Berggren" in the early part of the century. Later, the filament technique became fairly well established as a method for determining the surface tension of viscous liquids, and Tammann and coworkers,'. " Sawai and co-worker and Mackh howed good agreement between the values of surface tension for glasses and tars obtained by the filament technique and by more conventional methods. With the increased confidence in the technique gained in these experiments, the method was applied to solid metals and the first reliable values of surface tension of solid metals were reported by Sawai and coworkers10' " and by Tammann and Boehme." More recently, Udin and coworkersu-'" have reported the results of experiments with gold, silver, and copper wires. Similar experiments with gold wires were carried out by Alexander, Dawson, and Kling.'" The excellent review articles of Fisher and Dunn" and of Udinl@ should be referred to for detailed criticism of the foregoing work and for discussion of underlying theory. In all the foregoing calculations, it is assumed implicitly that the material contracts or extends uni- formly along the length of the specimen and also that it flows in a viscous fashion, i.e., that strain rates are proportional to stress. For an amorphous material, such as glass, tar, or pitch, the assumptions are quite valid and good agreement is obtained with values of surface tension measured by other techniques. The values reported for metals, however, are occasionally regarded with misgiving, since it can be argued that, because of their crystalline nature, true solids can not deform in a viscous fashion. If this is true, then the results reported for solid metals over a long period of years are of only doubtful value. Thus it is clearly necessary that a mechanism be established that would explain both the viscous flow and the uniform deformation that has been assumed. Such a mechanism has been proposed by Herring."' Briefly, he suggests that, under the conditions of the experiment, deformation takes place by means of a flow of vacancies between grain boundaries and surfaces. This is a direct but independent extension of the theory proposed by Nabarro" in an attempt to explain the microcreep observed by Chalmer~.In a condensed form the Herring viscosity equation is TRL there 7 is the viscosity, T the absolute temperature, R and L grain dimensions, and D the self-diffusion coefficient. In its complete form, all constants are calculable and it includes such factors as grain shape, specimen shape, and degree of grain boundary flow. When applied to existing data, good agreement was obtained between predicted and observed flow rates. The theory received provisional confirmation from the work of Buttner, Funk, and Udin" who observed viscosities in 5 mil Au wire much higher than those in the 1 mil wire used by Alexander, Dawson, and Kling.'" More significant were the completely negligible strain rates found by Greenough" in silver single crystals. Opposed to these observations were those of Udin, Shaler, and Wulff'" who found indications of viscosity decreasing as grain size increased. Thus, complete confirmation of the theory was lacking in that the data to which it could be applied contained only a limited number of grain sizes. Hence, it was proposed that a series of experiments be carried out with thin foils of varying grain size up to and including single crystals, where, according to the Herring theory, deformation would occur only at almost infinitely slow rates.

Jan 1, 1956

By B. Ramaswami

INTERNAL oxidation occurs readily in silver due to the rapid diffusion of oxygen in silver.' It has a marked effect on creep in polycrystalline silver2 and raises the critical resolved shear stress in single crystals of silver.3 However, the effect of oxygen on the work-hardening parameters of silver is not known. It is the aim of this paper to describe the effect of internal oxidation on the work-hardening characteristics of single crystals of silver and an Ag-0.1 at. pct A1 alloy. The materials used were: 99.99 pct Ag from Handy and Harman and 99.993+ pct A1 from Alcoa. Single crystals, 6 mm by 6 mm in cross section of silver and Ag-0.1 at. pct A1 of mo.5 orientation, i.e., the orientation with the Schmidt factor m = 0.5. were grown by the Chalmers technique.4 One set of specimens, referred to herein as oxidized specimens, was annealed at 940°C for 24 hr in a muffle furnace, in air, and furnace-cooled to room temperature. Another set of specimens, referred to as nonoxidized specimens, was annealed in oxygen-free helium at 940°C for 24 hr and furnace-cooled over a period of 7 hr to room temperature. The annealed single crystals were tested at room temperature in a floor-model Instron testing machine. The results are presented in Figs. 1 and 2. A

Jan 1, 1965

By Goldye Leeds, Marian Balicki

A SURVEY of literature reveals the scarcity of experimental evidence relating to work hardening and reannealing of silver.'-'" With the exception of the well-known X-ray investigation of silver and other metals by W. A. Wood? the effect of progressive cold working has not been studied. The determination of thermal stability of silver in the work-hardened state by means of isochronal or isothermal annealing has been confined apparently to very high reductions only. In the survey made, no study was encountered which endeavored to produce a complete picture of the changes in various properties due to cold working and subsequent reannealing. To fill these gaps and to assemble data that could be used for the determination of activation energies and of frequency coefficients of primary recrystallization, a systematic experimental approach, which was developed by one of the authors, has been applied to pure silver. Material and Processing The silver used was Handy and Harman fine silver, with a spectroscopic analysis at the testing stage of Cu, 0.0001 to 0.001 pct; Te, 0.0001; Pb, Si, Ca, Mg, and Mn, traces. The material was supplied in the form of a rod 0.406 in. diam and was converted into test samples according to the procedure condensed in Table I. It should be mentioned that air annealing was adopted to simulate industrial practice, though it was realized that annealing in a neutral gas or in a vacuum would be preferred. The usual precautions have been taken to eliminate any structural changes and property changes resulting from the storage of the samples prior to annealing or testing. Thus the wires were kept at the fully annealed stage, and the final wire drawing, which produced the desired degree of work hardening, was done just prior to the final annealing or testing. During the short waiting period, the samples were kept in a thermosflask filled with ice. Even with these precautions some strain-age-hardening or self-annealing could occur. To test such a possibility, wires of different reductions were prepared in the manner adopted and portions of them were immediately tested. The remaining portions were similiarly tested after different periods of storage, both at room and melting-ice temperature. Within experimental error, all samples obtained from a wire of a given percentage of reduction yielded identical values. This result qualified the material for further tests and interpretations, because it showed that either strain-age-hardening and self-annealing were absent, or that these effects fully balanced each other. The final annealing was carried out in an electric resistance furnace automatically controlled to within a 10°F. It was realized that the temperature fluctuations were greater than desired for this type of work. TO diminish the errors due to fluctuations of temperature, the hot junction of the thermocouple was placed as close to the samples as possible; the time of soaking was reduced to 15 min; and the number of samples annealed at different temperatures was increased. It will be seen from Table I that some tests were performed on the same material at rising temperature. These will be discussed elsewhere. Room temperature testing was limited to the determination of some of the mechanical properties that are known to be additive in a degree sufficient to be used for indirect study of the kinetics of the reannealing process, Tensile tests, carried out on a manually operated J. Camillon machine, accurate to within permitted the determination of the ultimate stress (U.S.1 and of the 2 in. elongation, (A,). The proof stress (d,e) has been determined from a series of bend tests carried out on a Tinius Olsen Stiffness Tester by using the offset method. This involved accurate determination for each sample of load-angular deflection curves, finding a

Jan 1, 1952

By E. J. Dulis, A. Kasak, R. C. Westgren

The potential of uirought tungsten- and tantaluw-rich alloys of the W-Ta-Mo-Cb system was investigated for high-strength structural applications above 2500° F. Appreciable strengthening of tung-sten and tantalum—essentially attributable to solid-solzction effects—was obtained with binary, ternary, and quaternary alloys. Tensile strengths as high as 67,000 psi were achieved at 3000 OF. ThE quest for wrought structural materials which possess good strength properties at temperatures above 2000°F has led to a considerable research effort during the past decade. In addition to exploring the potential of various high-melting-point refractory metals (such as molybdenum, columbium, tantalum, and tungsten) for very high-temperature structural applications, alloy-development programs have been undertaken to achieve greater strengths than could be achieved with unalloyed refractory metals. The methods of strengthening refractory metal alloys have included both solid-solution and dispersion strengthening. General relationships among the relevant properties (melting point, recrystallization temperature, and high-temperature strength) of refractory metals indicate that the highest strengths at temperatures of 2500°F or higher would be obtained with tungsten-or tantalum-base alloys. Therefore, the present investigation was undertaken to determine the high-temperature strength potential of solid-solution strengthened alloys based on the binary system W-Ta; to effect further strengthening, minor additions of molybdenum and columbium (at the 6 and 12 pct levels) were made. The portion of the W-Ta-Mo-Cb quaternary alloy system of interest is shown schematically in Fig. 1. The component metals—W, Ta, Mo, and Cb—have a bcc structure at all temperatures, and their binary systems are mutually completely soluble.' Complete solid solubility in the W-Ta-Mo and W-Ta-Cb alloy systems has been demonstrated,' and, therefore, it was expected that the quarternary alloys of the system would also exhibit complete solid solubility at all temperatures. In the virtual absence of contamination by interstitial elements, all the alloys would be truly solid-solution strengthened. Twenty specific compositions of this investigation included binary, ternary, and quaternary alloys of the W-Ta-Mo-Cb system as well as unalloyed tungsten and tantalum. The compositions are shown in Table I. EXPERIMENTAL PROCEDURE Consumable-electrode vacuum-arc melting with ac power was used to produce small laboratory-sized, cylindrically shaped ingots (1-1/4 in. in diameter and 2 to 3-1/2 in. long) of the twenty compositions. A furnace was specially constructed to melt as many as four electrode rods simultaneously into molds lined with tungsten or tantalum sheet. High-purity rods of tungsten, tantalum, molybdenum, and columbium were used for consumable electrodes; the diameter of each rod was determined by the desired weight percentage of the component metal in a given alloy. The details of the construction and operation of the melting furnace will be discussed in another p~blication.

Jan 1, 1964

By Robert E. Green, Kenneth Reifsnider

A microscopic X-ray diffraction technique was employed for the simultaneous study of the behavior of several families of lattice planes, whose local orientatiotz changes are manufestations of internal distortions resulting from specimen deformation. Photographs taken using aluminum were single crystals 1/64 in. In diam are presented which illustrate the appearance of various types of deformation- or growth- induced structural variations. Slip and lattice bending were detected in tensile tests for strains as small as 0.1 pct. Evidence of deformation bands, lineage structure, and void formation wns also shown. AmONG the most important methods of studying internal stresses in metals is the utilization of various X-ray techniques. The general subject of X-ray metallography has been treated in a most excellent manner by Taylor,1 and the use of X-rays for the direct observation of imperfections in crystals has recently been reviewed in an article by Newkirk2 and in the book edited by Newkirk and Wernick.3 Since the inception of metallographic X-ray analysis, there have been numerous technological developments and refinements, each with its particular advantages and disadvantages and, acrording to these, its particular applications. X-ray diffraction techniques can be divided into two general categories, that of X-ray diffraction microscopy and that of X-ray diffraction macroscopy. In the former are included such methods as those of Berg-Barrett, Lang, and Schultz2,3 which are concerned with microscopic imperfections such as dislocations. The second category includes all work concerned with the study of the condition of a crystal lattice structure as indicated by the marroscopic detail in its diffraction patterns. An example of this is the study of the diffraction manifestations of inhomogeneous plastic deformation as manifested by formation of deformation bands and inhomogeneous lattice rotations. The method used in the present investigation was an X-ray diffraction macroscopy technique. The geometry and analytical aspects of the method were similar to those of Julien and Cullity.4,5 The source was collimated with a single slit in a manner simi- lar to the "parallel beam'' method of Barth and Hosemann6 except that a continuous spectrum of radiation was employed. The apparatus produced large-beam transmission Laue patterns of thin cylindrical aluminum-wire crystals, which were deformed either in tension or torsion. Although the conventional X-ray target and interposed slit were not capable of the high resolution obtainable with a fine-focus X-ray source as employed in a microfocus apparatus, resolution was a secondary consideration in our technique, and was sacrificed to obtain sufficient intensity along a sizable length of the specimen. By using a grid indexing technique similar to that of Barth,7 we were able to study several diffraction lines from various planes simultaneously. The results of these tests give additional information with regard to the inhomogeneous deformation of single crystals, and the indexing procedure used provides a correlation between portions of the test specimen and portions of a diffracted beam. EXPERIMENTAL TECHNIQUE The experimental arrangement used is shown schematically in Fig. 1. A source of continuous X radiation from a vertically mounted Machlett X-ray tube possessing a copper target and operated at 20 kv and 10 ma was passed down a horizontal lead tube 80 cm long which terminated in an adjustable vertical brass slit. The slit opening was adjusted to correspond with the diameter of the test specimen. In front of the brass slit it was possible to place a screen wire mesh, one horizontal strand of which was a lead wire which served as a fiduciary mark, the screen itself serving as an indexing system as will be described later. Behind the screen was the test specimen which consisted of an aluminum single crystal wire 1/64 in. in diameter and 3 in. long. These 3-in.-long crystals were cut from

Jan 1, 1965

By J. P. Boisseau, C. N. J. Wagner, E. N. Aqua

An analysis ulas made of powder-paltern peaks from cold-rolled polycrystalline copper and from copper powders, compacted into briquets (1 in. diameter) with pressures up to about 106 psi. Powder-pattern peaks from both contact faces were measured with a diffractometer and CuKa radiation. Laltice-parameter measurements indicate the presence of residual stresses in the bulk specimen of the order of a - -10 kg per sq mm after 93 pct reduction in thickness, and give some evidence for the occurrence of deformation stacking faults (probability a - 0.003) in both bulk and powder samples. Fourier analyses of the line profiles were carried out on the (111) - (222) and (200) - (400) Pairs of reflections. The particle sizes decrease rapidly with increasing deformation and reach asymptotic values of De (111) = 550A and D, (200) = 350A at about 25 pct reduction in thickness or 80,000 psi pressure for compaction. The anisotropy of the particle sizes indicates the presence of microtwins and stacking faults on (111) planes. The rms strains increase also with deformation and reach limiting values of 2 x 10-3 in the [100] direction and 1 x 10-3 in the [Ill] direction at a distance L = 100A normal to the reflecting planes. THE diffraction of X-rays in cold-worked, polycrystalline, fcc metals and alloys yields Debye-Scherrer patterns in which the individual (hkl) lines may show a broadening, a shift, and an asymmetric shape.' These effects can be explained by the fragmentation of the small, coherently diffracting domains, the presence of residual elastic strains in the lattice, and the formation of stacking faults. X-ray studies of stacking faults in fcc metals and alloys have been methodically performed during the last few years, but so far most of the investigators dealt with cold-worked powder specimens obtained by filing.2-8,10-19 In such specimens, the crystals are randomly oriented and the average elastic strains are assumed to be zero, so that the observed peak shifts are due to stacking faults only. The agreement between X-ray diffraction theory1,20 and experiment is generally good. On the contrary, cold-worked, polycrystalline bulk specimens (after wire drawing, rolling, plastic deformation by tension or compression, etc.) contain residual elastic strains, which may not average to zero in the surface of the specimen and show very strong preferred orientation of certain lattice planes (texture) parallel to the specimen surface. Nonzero elastic strains also produce peak shifts, the magnitudes of which depend upon the crystallographic orientation of the reflecting lattice planes in elastically anisotropic materials as well as on the type of plastic deformation and which have to be taken into account when measuring stacking-fault probabilities in deformed bulk specimens.21-23 The purpose of the present investigations was to perform a detailed X-ray analysis on a bulk specimen of a fcc metal deformed by rolling at room temperature and on powder of the same material deformed by compaction, and to compare these results with those previously obtained on cold-worked filings.18 Pure copper was chosen for this study since it is known to produce only a small quantity of stacking faults by filing at room temperature.3,16,17,19 The residual elastic strain in the surface of the bulk copper should be the predominant factor determining

Jan 1, 1965

By W. P. Evans, R. W. Buenneke

Warren and Averbach's multiple order, Fourier method was applied to solid specimens of SAE 1045 steel. The material was hardened to three hardness levels and specimens of each hardness were shot peened to three intensities. Particle size, root-mem-square strain, mean strain, md macro residual stress were determined for each. Microstrains caused by either hardening or peening varied markedly over microregions. In general, increasing the hardness or peening intensity increased the rms strain and decreased the particle size. Similar effects were observed by varying hardness and peening intensity independently. At a Rockwell hardness of C 50, peening had little effect on line broadening, but both mean strain and macro residual stress increased. Mean strain was independent of column length. Induced macro residual stress by peening was affected most by initial hardness, but not by specific peening intensity. The purpose of this work is to establish the state of residual strain and particle size by X-ray diffraction in hardened and cold-worked plain carbon steel and attempt to relate these X-ray measured parameters to fatigue performance. X-ray line broadening (and its micro implications), along with X-ray residual stress (and its macro implications), may be basic indicators of the inherent fatigue resistance of the material. X-ray line broadening is caused by variable lattice strains and small particle size. Both are a result of plastic deformation which accompanies hardening or cold working processes. Therefore, X-ray line broadening is a good measure of both. warren1 has recently reviewed the Warren and Averbach2,3 Fourier analysis of line broadening. Strain and particle size effects can be separated because broadening due to particle size is independent of order of the diffraction peaks, while broadening due to strain is not. Microstrain is obtained as a root-mean-square strain averaged over discrete distances within the crystals causing diffraction. These distances are quite small, varying from 10 to 10081, and may be interpreted as the gage length over which the strains are averaged. Because of their variable nature, the X-ray line is broadened. The plot of rms strain vs distance (or column length) within the specimen gives a measure of their variability. Small particles also cause X-ray line broadening as already mentioned. A particle is interpreted as a region within a crystal or grain which diffracts X-rays coherently. This region is one of given orientation and may be bounded by a small angle grain boundary, dislocations, a twin boundary, or a stacking fault. The present work covers measurement of X-ray line broadening and macro residual stress on an SAE 1045 steel, quenched and tempered to various hardnesses. Various amounts of cold working were produced by shot peening the surfaces to various Almen intensities. Particle size, root-mean-square strain, and mean strain were calculated from the Fourier coefficients of the X-ray diffraction profiles in a direction normal to the peened surface. No effort was made to separate the various causes of particle size broadening. Macro residual stresses were reported in directions parallel to the peened surface. I) X-RAY METHOD The Fourier coefficients were determined for the 110 and 220 X-ray profiles. They were corrected for instrumental broadening by the method of Stokes,4 using an annealed reference specimen of similar geometry presumed to be free from broadening due to small particles and distortions. The nth Fourier cosine coefficient, A,, is related to a particle size coefficient, Ap, and a distortional coefficient, ADn, by the equation:

Jan 1, 1963

By J. A. Berger, R. J. Towner

The pjPocesses of polygonization and subgrain growth were followed in slightly stretched 99.99 pct A1 single crystals heated for cumulative times at 400°, 500°, and 600°C. Changes in sub-grain size and boundary angle were determined from measurements on X-ray micrographs. CAHN1, 2 studied polygonization in stretched and heated aluminum single crystals of 99.99 pct A1 using various techniques, including etch pits, Laue patterns, and a slight restretching of heated specimens to reveal small changes in lattice orientation by the direction of new slip lines. He found that kink bands, which had well-defined boundaries lying in a plane perpendicular to the slip direction (at least in the early stages of deformation), formed during stretching. Also, he noted that bending occurred about the <211> axis lying in the (111) slip plane perpendicular to the <110> slip direction. His studies of polygonization were largely confined to the kink bands rather than to the weakly bent matrix regions between bands. The minimum temperature required to bring about polygonization was established at about 450 "C. Guinier and Tenevin used a focusing Laue X-ray diffraction technique to study polygonization in aluminum single-crystal specimens of 99.99 pct purity. Stretching the crystals 5 pct in tension caused a widening of the focused Laue spots. After heating for 4 hr at 450°C, their method revealed no change in the specimen. Above 450°C polygonization was detected and further annealing near 600°C led to subgrain growth. They concluded that the orientation of the crystal relative to the axis of deformation had no marked effect on polygonization. Gay and Honey-combe4 using an X-ray microbeam technique found that polygonization did not occur in a stretched aluminum crystal heated at 250oC, although some decrease in the yield strength occurred. When the temperature was raised to 475oC, the asterism became broken up as a result of polygonization. Honeycombe5 noted that reflections on X-ray mi-

Jan 1, 1961

By Ganesh P. Mohanty, James J. Wert

THE brittleness of the intermetallics usually render their deformation studies at ordinary temperatures using conventional techniques inadequate. On the other hand, although X-ray line broadening measurements is not a complementary technique, it provides a means for gaining limited but useful information on the cold worked state of these materials. In the present instance, a study of the effects of cold work in the lead telluride intermetallic compound was carried out by analyzing the diffraction profiles of the deformed and the corresponding annealed samples. An ingot of PbTe was prepared by induction melting high-purity lead and tellurium in a quartz crucible under an atmosphere of argon. After homo-genization, the ingot was ground to -325 mesh at room temperature, and using a polished die the cold- worked powder was pressed into the form of flat faced briquets for diffraction measurements. A spectrometer with 0.125 deg per min scanning velocity, CuKa radiation, pulse height analyzer, and a proportional counter were employed in the X-ray measurements, and the powder peaks were collected from the sample in fully cold-worked state and after it had been annealed to relieve the effects of cold work completely. For reliable estimates of the peak extremities, small angular ranges where the tails merged into the background were point counted. Fourier inversions of the experimental peaks were carried out in an IBM 705 computer using the procedures introduced by stokes.&apos; Both the cosine and sine components of the Fourier series were used to take into account any peak assymetry arising

Jan 1, 1963

By D. Geiselman, A. G. Guy

Single cvystals were grown from high-purity magnesium containing known amounts of nitvogen in the range 0.0008 to 0.0048 wt pet. Crystals of known ovientation were tested in tension in an Instron ma chine to determine the yield strength and to obsevue wheather a yield point occurred. Slowly cooled crystals or those given a solution heat treatment did not show a yield point. However, crystals that were aged following a solution treatment showed a yield point for all of the nitrogen contents studied. It was concluded that nitrogen caused the yield point by the Cottrell mechanism. NITROGEN has been shown to produce sharp yield points in single crystals of cadmium, zinc,2&apos;3 ß-brass,4 and iron,5,6 as well as in polycrystalline iron7 and molybdenum.8,9 Since magnesium has a structure similar to zinc and cadmium, it seemed reasonable that magnesium should also exhibit a sharp yield point provided it contained sufficient nitrogen. Bobalek and Shrader10 reported a total nitrogen content of 0.002 to 0.0065 wt pct in com- mercial magnesium alloys, an amount well in excess of that required by theory. However. magnesium differs from cadmium and zinc in that it forms a stable nitride, Mg3N2, which has a standard free energy of formation of -95,480 cal per mole at 25" c." If rather than being in solid solution, the nitrogen were predominantly combined as the nitride, it could not act to produce a yield point. This type of behavior is the basis for the elimination of strain aging and a yield point in steel by the addition of strong nitride formers such as titanium,12 columbium,13 aluminum,14 vanadium,15 and boron.16,17 Thus, there appeared to be factors both favorable and unfavorable to the production by nitrogen of a sharp yield point in magnesium, and the purpose of this investigation was to determine the actual behavior of magnesium crystals containing known amounts of nitrogen.

Jan 1, 1960

By Joachim J. Hauser

Experiments on latent hardening were peyformed by compressing single crystals along a direction perpendicular to the tension axis. The slope and length of easy glide in the tension test were found to depend only on prior deformation in the same slip plane. Prior deformation on a different slip plane changes the stress level of the resulting stress-strain curve. The yield points appearing upon reloading after prior extension and unloading were related to the end of easy glide. SEVERAL researchers have studied the latent hardening due to deformation of a crystal by slip on a slip System after prior deformation. These experiments can be divided into those in which the prior deformation was on the same plane as the subsequent and those in which the two deformation processes were in different planes. In the former category are the experiments of Buckley and Entwistle,1 Parker and washburn,2 and Haasen and Kelly.3 The latter case has not been studied systematically; it was the main purpose of this investigation to produce this type of latent hardening and explain the results in terms of the existing theories of work hardening. In general, tension producing slip on a certain slip system can be preceded by tension, transverse compression or longitudinal compression, each with predictable dislocation movement and intersection. The intersection of dislocations can lead to glissile or sessile jogs, Cottrell-Lomer locks and other sessile dislocations. The effect on the stress-strain curve could depend on which combination of the former mechanisms is operating. Haasen and Kelly3 have studied the yield points which occur in aluminum and nickel single crystals upon reloading after prior unloading in a tension experiment. They attributed this effect to the anchoring of dislocations occurring during unloading. As Cottrell and stokes4 have shown that dislocations cutting through the "forest" could only lead to reversible changes, they attributed the anchoring to the formation of sessile dislocations during unloading. However, different kinds of sessile dislocations could be formed during unloading, and it was the purpose of this experiment to determine whether Cottrell-Lomer locks are responsible for the yield effect and for the end of easy glide. The case where a longitudinal compression is followed by tension along the same axis is commonly referred to as a Bauschinger test. This type of effect was studied by Buckley and Entwistle1 on aluminum single crystals and by Parker and washburn2 on zinc single crystals. In such a test, the tension and the compression activate the same slip plane with opposite slip directions. The use of sideways compression in the present experiments permits the activation of different types of slip systems and the study of their effect on the easy glide region and on the transition between the elastic and easy glide region. The theory of seeger5 for the flow stress in fee materials is applied to explain the latent hardening. EXPERTMENTAL PROCEDURE All the single crystals used in this investigation had an axial orientation close to <210>, called the "0.5" orientation. This is the orientation for which the tensile axis is 45 deg from both the slip plane and the slip direction. The single crystals were grown from the melt under a helium atmosphere using milled graphite boats,=at a rate of 8.6 mm per min. The silver used in the experiment was 99.98 pct pure. The single crystals had a square cross section about 0.9 by 0.9 cm and a length of 14 cm. The orientation of the specimen was determined within ±2 deg by the Laue back-reflection method. The specimens were annealed at 940&apos; ± 2°C in a helium atmosphere for 24 hr and then furnace cooled over a period of 7 hr. The specimens were electropolished in a solution of 9 pct KCN in water. The specimens were tested in a soft-type tensile machine (the load is prescribed) up to 3 pct strain. The stress was increased continuously at approximately 30 g per mm2 per min. The strain was measured over a 5 cm gage length with a mechanical extensometer employing an optical lever. The strain and stress were measured with accuracies of i 2 X 10-5 and ± 2 g per mm2, respectively. The remainder of the stress-strain curve up to 20 pct strain was obtained in a hard-type tensile machine (the strain rate is prescribed). The strain and the stress were measured in that machine with an accuracy of ±2 pct. The compression tests were performed in the hard-type machine using accurately machined steel blocks without lubrication. The blocks were used so as to apply a uniform compression over a length of 13 cm. The strains were measured on the hard-type machine and with a micrometer.

Jan 1, 1962

By T. J. Koppenaal, M. E. Fine

A yield point effect attributed to short-range ordevi?g (SRO) occurs in Cu base Al. At at 296°K varies with heat treatment, decreasing as the annealing ternperature is raised .from 433Oto 598°K. Davies aid Cahn&apos; observed a corresponding decrease in SRO. (523 °K anneal, measured at 77°K) is approximateZy proportional to the variations of A7 with strain rate and testing temperature are also Consistent with the idea that is associated with SRO. A preliminary investigation of the tensile properties of a Cu-Al single crystals showed the presence of a rather strong yield-point effect (drop in flow stress after initial yielding). The object of this research was to investigate its origin and behavior. a Cu-Al alloys are particularly interesting because diffuse X-ray scattering measurements by Davies and Cahn,&apos; Houska and Averbach,&apos; and Borie established the presence of short-range order. The degree of local order may be changed with heat treatment.&apos; cottrel14 suggested that the presence of local order might result in a yield-point effect, and thus the possibility exists here for experimentally ascertaining the importance of short-range order with respect to yield points in these alloys. Since a 12 pct difference exists between the atomic sizes, elastic or Cottrell locking5 must also be considered. Further, Howie and swanne have shown that the stacking fault energy of copper is reduced by aluminum additions. The width of extended dislocations should thereby increase. hus the conditions appear attractive for Suzuki locking.&apos; Finally, the possibility of stress-induced order at dislocations, schoeck locking,&apos; must also be examined, EXPERIMENTAL PROCEDURE Alloys up to 14 at. pct Al were prepared by induction melting high-purity (99.999 pct) Cu and (99.996 pct) Al in a graphite boat under a dynamic vacuum of 5 X 10o mm of Hg. After homogenizing the ingots at 900°C for at least 24 hr under vacuum, they were rolled with intermediate anneals to strips 1.55 mm thick. Single crystals 10 in. long were grown by lowering strips, contained in a split graphite mold sealed in fused quartz at 5 X lo-&apos; mm of Hg, through a single coil induction heater at a constant rate of 1/2 in. per hr. Tensile specimens 1.25 in. long were cut from the single crystal strips and reduced cross sections about 0.7 in. long and 3.0 to 3.5 mm2 in area were introduced by filing and abrading.8 To remove the worked portion about 10 pct of the cross-sectional area was removed by etching. Back-reflection Laue photographs of a filed and etched specimen were taken before and after annealing at 900°c for 24 hr. Small, well defined Laue spots were obtained with no visual difference in the two photographs. Further, specimens with and without the reduced sections began yielding at about the same stress. Hence, for our purposes, filing and abrading did not affect the structure of the specimens. Each single crystal specimen was annealed at 900° c in vacuum for at least 24 hr and furnace cooled; while cooling through the range of 250o to 200°c, the rate was about 55°C per hr. Orientations were determined by the usual back-reflection Laue

Jan 1, 1962

By R. Grierson, R. N. Parkins

The m.echanica1 properties, at high lzomologous temperatures, of the intermetallic compounds InzBi and Mg17A112 were measured as a .function of temperature, applied strain rate, previous thermal and mechanical history, and composition. Mgl,Al12 was investigated ilz compression, whereas Zn,Bi was investigated in tension. A decrease inflow stress with increasing strain was observed jor both alloys. The results obtained are discussed in terms of the dislocation-multiplication processes in these materials. MANY intermetallic compounds are reported to undergo a brittle-ductile transition at high homologous temperatures.&apos; There is evidence in the literature that some of these compounds exhibit a large yield drop when plastically deformed.&apos;j3 Both of these forms of behavior are shown by the covalent elements germanium and silicon4,5 and also by certain ionic compounds.8 The present work is a study of the deformation, at high homologous temperatures (>2/3 Tm), of two intermetallic compounds, In2Bi and Mg17Al12. InzBi has a disordered hexagonal structure7 (c/a = 0.598) and a solubility range of 32.3 — 33.2 at. pct Bi.8 It has a melting range from 72° to 89°C. Mg17Al12 has an ordered bcc (A12 type)7 structure and exists over the range 50 to 60 at. pct Mg8 with a melting range from 437° to 462°C. We have been unable to find any reference to previous investigations of the mechanical properties of BiIn,. Novikovg has reported that cast samples of Mg17A112 show ductility, when bend-tested, at temperatures above 380°C. EXPERIMENTAL Ingots of In2Bi and Mg17Al12 were melted under an argon atmosphere and cast, in situ, in a graphite crucible. The materials used were of 99.99 pct purity. The alloys prepared contained 66.9 at. pct In in the case of In2Bi and 58.4 at. pct Mg in the case of m17A112. The ingots were homogenized and then extruded. Two-in.-diam Mg17Al12 ingots were extruded at 375°C to give 3/8-in.-diam rod. The rate of formation of this rod was 0.25 in. per min. One-in.-diam InzBi ingots were extruded at 20°C, using a rate of 1 in. per min, to give 1/8-in.-diam rod. In both cases the extruded rod had a recrystal- lized, fine-grain, structure. (For Mg17Al12, d = 11.2 µ; for BiIn2, d = 22 µ.) Mechanical-property determinations were made in a hard-beam machine, in tension in the case of In2Bi and in compression with Mgl7Al12. The tensile tests were on specimens having a gage length of 1.1/2 in. and a diameter of 1/8 in. The compression tests on Ml7A112 were on specimens of 3/8 in. diam by 3/8 in. high and the ends were coated with poly-tetrafluorethylene to minimize friction. RESULTS In2Bi. Fig. 1 shows, particularly at the higher applied strain rates, that In2Bi exhibits a marked yield drop as the deformation increases to about 2 pct, after which the material shows neither hardening nor softening up to 15 pct strain. The magnitude of the yield drop, the stress in the region of flow under constant stress (the stress plateau), and the 0.5 pct proof stress were all dependent upon the applied strain rate according to an expression of the form

Jan 1, 1965

By R. M. Rose, D. P. Ferriss, J. Wulff

The effect of orientation on the stresses, nctivation energies, and activation volumes for yielding and plastic flow of tungsten single crystals was investigated. Tensile tests showed the proportional limit to be a function of orientation: crystals whose tensile axes were near the [I10} direction were roughly three times as strong as [loo] crystals. The [ 1101 crystals showed low strain hardening and displayed yield phenomena, whereas the other orientations yielded smoothly and showed considerable strain hardening. The fracture mode was cleavage, except for crystals near the [1101 , many of which gave "chisel" fractures at 300°and 373°K. The activation energy for yielding was approximately one- half an electron; volt at all orientations, and the volume of activation was (12 to 14)b3, except near the [1101, where it was 7b3. Activation volumes generally increased after yielding. The most common theoretical models for yielding and strain hardening of bcc metals were. found to be insufficient to the intepretation of the observations here in. An explanation is proposed, based on the dislocation reaction dislocation networks and jogs, md jogs formed during plus tic flow. PRECLSE knowledge of the Drocesses involved in the yielding and plastic flow of the refractory metals is essential to the formulation of models for their flow and fracture. Despite this need, the single -crystal investigations, especially of tungsten, have been sparse. Slip occurs at low temperature, according to schadler,i in <111> directions on {110) planes; as the temperature rises to room tempera-

Jan 1, 1962

By W. C. Elli, M. E. Fine

YOUNG&apos;S modulus of elasticity in metals ordinarily decreases with rising temperature. The range of the thermoelastic coefficient at room tem- 1/E dE/dT perature (temperature coefficient of modulus, is illustrated1 by the values for tungsten and hard-drawn aluminum, —95 and —1220x10-6 eg C-1. However, a nearly zero thermoelastic coefficient is observed in some ferromagnetic alloys over a limited temperature range. In these alloys, as the temperature is raised, an increase in modulus arising from loss of ferromagnetism compensates the normal decrease. Iron-nickel alloys containing 36 to 52 pct Ni behave in this manner. In the present investiga- tion, the dependence of the modulus and thermo-elastic coefficient on cold working and annealing were studied in iron-nickel alloys in this range of nickel. Although these alloys, when fully annealed, have a coefficient near zero over a very small temperature interval, the temperature range of low coefficient can be extended greatly by straining and then stress-relief annealing. The modulus of face-centered cubic iron-nickel alloys annealed at 1000°C does not vary linearly with composition at room temperature but, as shown by the solid line of fig. 1, from Koster,&apos; is minimum at 40 pct Ni and maximum at 87 pct Ni. The modulus increases with applied magnetic field but retains the minimum near 40 pct Ni. Schematic change of modulus with temperature for three compositions is shown in fig. 2.&apos;. &apos; With increasing temperature, the slope becomes less negative, goes through zero (temperature of minimum modulus for the alloy), becomes positive, and resumes its normal negative value above the Curie

Jan 1, 1951

By E. H. Rennhack

Phase equilibria of the zinc-rich portion of the Zn-Fe-A1 system containing up to 20.0 wt pct Fe and Al have been investigated at 600°C (1112°F), 450°C (842°F), and room temperature by metallographic and X-ray diffraction techniques. The phase relationships were found to involve only those phases present in the three binary systems. THE presence of small quantities of aluminum (approx. 0.2 wt pct*) in zinc galvanizing baths is known to suppress the formation of Zn-Fe alloy layers within the coating.&apos; As part of an extended investigation of this suppression effect and the alloy reactions involved, the zinc-rich corner of the Zn-Fe-A1 equilibrium system containing up to 20.0 pct Fe and Al was determined at 600°C (1112°F), 450° F (842° F), and room temperature. The present paper reports the findings of this study. The constitution of the Zn-Fe system has been reported by Raynor2 based mainly on the work of Schramm3-3 and Truesdale et a1.6 The solid solubility of iron in zinc is extremely small and lies between 0.0009 and 0.0028 pct in the range 150° to 400°C (302°to752°F). Within the temperature and composition range of interest, a eutectic reaction involving nearly pure zinc, liquid = Zn+FeZn13, is observed at about 419°C (786° F) and 0.018 pct Fe along with a peritectic reaction, FeZn7+ liquid e FeZn13, at 530°C (986° F) and 6.2 pct Fe. The latter reaction is sluggish due to the large proportipn of solid phase involved in the transformation. Halla et al.,7 identified the compound FeZn13 as monoclinic with a = 13.68, b = 7.63, c = 5.07, and B = 128°44&apos;. The structure of FeZn7 was reported by Bablik, et al.,8 to be of hexagonal symmetry, belonging to either the C6v = C6/m mc or D46h = C6/mc space group. Divensions of the unit cell are a = 12.81A and c = 57.6a. The Zn-A1 diagram as composed by Raynor9 and later Gebhardt10 is characterized by a eutectic decomposition, liquid 382°C (720°F) and 95.0 pct Zn and a eutectoid decomposition, at 275° (527°F) and 78.0 pct Zn. The eutectoid reaction cannot be suppressed permanently by quenching. Above 275° (527° F), a and a&apos; co-exist in a closed miscibility gap between 31.6 and 78.0 pct Zn. Both phases are fcc and have nearly the same lattice parameter. The maximum solubility of aluminum in zinc (B) is approximately 1.0 pct at the eutectic temperature. PROCEDURE Materials. The experimental alloys were prepared from both massive and powdered material. Cast alloys were composed from three zinc-base master alloys containing 8.0 pct Fe, 16.0 pct Fe, and 50.0 pct Al which were made from C.P. zinc, Armco iron, and

Jan 1, 1962

By D. R. Hay, E. Scala

Electrotransport has been superimposed on the rate-limiling- step in zone refining which is the impurity diffusion through the liquid at the solid/liquid interface. The efficiency of zone refining is increased and relative resistivity ratios (P300°k/P4 2°K) he increased by 50 pel in tungsten for a given number of posses using- the electrotransport field-aided method. The effiect of zotze refining in the presence of an electric field on the relative resistivity ratio is examined as a function of its intensity and polarity. THE effect of electrodiffusion on the effective distribution coefficient of zone refining has been discussed by Pfann and Wagner.&apos; Control of the distribution coefficient in zone refining is of twofold interest. A distribution coefficient of unity can be increased or decreased, making possible the transfer of some previously inseparable solutes. The general efficiency of zone refining can also be increased. In the conventional zone-refining process impurities are removed by their retention in the molten zone and subsequent deposition at the end of the rod after a complete passage of the zone. In higher-melting-point systems a second mechanism may also operate, the volatilization of impurities from the molten zone. It has been suggested by schadler2 that, in refractory metals, vacuum distillation plays the predominant role in purification. In Koo&apos;s results,3 the resistivity ratio decreased beyond a zone-refined length of 6 in. from the starting end, indicating that some purification does in fact occur by true zone-refining action. Hay and scala4 showed that the degree of purity as measured by the relative resistivity ratio method depends on the square root of time in the molten zone (number of passes) and thus appears to be limited by diffusion in the boundary layer at the solidifying interface assuming good mixing in the body of the molten zone where a linear rate would prevail. The final concentration of impurities in electron-beam floating-zone purification depends very much on the operating conditions and results obtained by various investigators2,3,5 are difficult to correlate. The diameter of the starting material, operating vacuum, and rate of traverse are among the factors to be considered. There are, nevertheless, some general observations to be obtained from the literature. Lawley5 reviewed the literature up to 1962 and concluded that the major contaminants generally remaining in tungsten after electron-beam zone refining are molybdenum and carbon. Molybdenum due to its high melting point and distribution coefficient of nearly unity would be expected to be difficult to remove by either volatilization or zone refining. Carbon is not only a common contaminant in vacuum systems, but is also very difficult to remove by conventional vacuum melting. even with vacuums of 10-7 mm Hg. For each of those impurities removed by zone refining the equation of Pfann and Wagner may be applied: It relates the effective distribution coefficient k to a superimposed driving force which accelerates the solute away from the interface with a terminal velocity L" and to the more conventional zone-refining parameters; v = rate of traverse, t = thickness of the diffusion layer at the solidifying interface, D = diffusivity of the solute in the molten zone, and ko = equilibrium distribution coefficient of the impurity.

Jan 1, 1965

Jan 1, 1942

By C. H. Mathewson

EXCEPTING the joint sessions on gases in metals held during the day on Tuesday, the Institute of .Metals opened its activities with a division dinner at the Commodore on Tuesday evening, with Sam Tour, retiring chairman, presiding. W. M. Corse, secretary-treasurer, outlined the financial status of the division and stated the investment fund is becoming large enough so that in the near future it will be possible to pay all expenses of a foreign lecturer once in two years and not rely on an extended speaking tour to cover expenses. W. B. Price reported on his attendance at the Zurich, Switzerland, meeting of the International Society of Testing Materials and gave a graphic account of his visit to the Grand Salon, his meeting with Mussolini, and his audience with the Pope. Buffalo was announced as the place of the fall meeting, to be held during the week of Oct. 3.

Jan 1, 1932

By Charles S. Barrett

There is a road into the microscopic realm that has remained untraveled through all these years of intense activity with high-power optical and electron microscopy. The road is worthy of careful scouting by metallurgists and other investigators, for it leads into relatively new country and it makes some areas accessible that heretofore could be reached only by very indirect paths or by the use of imagination. And when the road passes through familiar territory it frequently permits a new view of commonplace things that should prove of value from time to time. An accepted way to interest people in new sights such as this is to present an illustrated travelogue. This I propose to do, using many pictures taken in my recent exploration of this road. In the manner of travelogues, I shall touch briefly upon a large number of different subjects in physical metallurgy and shall attempt to give an exhaustive treatment of none, for the objective is to provide a means for further research, to interest others in it, and to indicate what appears at the moment to be profitable directions for it to take. The method I shall present involves X-rays, but does not make use of the usual accompaniments of X-ray research such as reciprocal lattices, Fourier series, or the stereographic projection. The method is so simple in its fundamentals that it could have been developed 2o years ago, or perhaps even 30 years ago. It is well to have a destination for our travels, so that when we are through we shall have explored some region of importance, despite our preoccupation with the novel means of transportation and our interest in the sights to be seen along the way. So let us name the Cold-worked State as our destination, and make side trips into the territories known as Recovery, Recrystallization, and Precipitation-hardening. A great many investigations have been made of the nature of cold-worked metal, and a great variety of methods used, many of which are indirect, such as X-ray line intensities, X-ray line widths, calori-metric measurements, and magnetic measurements. Since comprehensive reviews of these investigations have been published in recent years, they need not be discussed here. The investigations that were the direct forerunners of the present work should be first mentioned. In 1931 I became interested in the structure of individual spots in X-ray diffraction patterns.l When a crystal is placed in the narrow pencil of X-rays in a Laue camera, the spots recorded on the film are not always uniformly black, but may have an internal structure. The meaning of this may be understood from Fig. I, which represents a narrow beam containing X-rays of many wave lengths (&apos;&apos;general radiation") penetrating a crystal in the direction of the arrow and forming a pattern on the vertical film at the right.

Jan 1, 1945