By J. W. Pugh, J. D. Nisbet

F. B. Foley—The use of data published by Wever and Jellinghaus in 1931 to fix boundaries of the sigma phase in the Fe-Cr system, in the face of the author's own references to the suggestions of Bradley and Goldschmidt, Aborn and Bain, and Hougardy that the phase is much more extensive, and the very much more accurate work, which weighs heavily in favor of these suggestions, of Cook and Jones, published in 1943 and evidently disregarded by the authors, makes their derived ternary diagram, especially fig. 15 for 400°C, quite inaccurate on the Fe-Cr side and affects the extent of phase boundaries in the most controversial and important part of this ternary system. In commercial Fe-Ni-Cr alloys the occurrence of sigma has been observed time and time again at lower chromium contents than that of the 24 pct Cr, 16 pct Ni, 60 pct Fe alloy which is the lowest permitted by fig. 15 of practically carbonless metal. Newel1 reports sigma in 27 pct Cr-Fe even with some carbon present to be one of the greatest detriments to its extensive application, whereas Pugh and Nisbet set a low limit of 36 pct Cr for sigma in the binary Fe-Cr system. J. J. Heger—The diagrams presented by the authors do not agree with observations made on commercial Fe-Cr and Fe-Cr-Ni alloys, nor do they agree with two recent investigations made on the Fe-Cr and the Fe-Cr-Fe systems. I refer first to the investigation made by Cook and Jones1' on the sigma region of the Fe-Cr system. On the basis of their results which were published in 1943, Cook and Jones established new boundary limits for the sigma and the alpha plus sigma regions. These new limits have been accepted and are incorporated in the Fe-Cr diagram that appears in the 1948 edition of the Metals Handbook. This diagram is shown here as fig. 34. As will be noted, the boundary limits of the alpha plus sigma region in this diagram extend to much lower chromium contents than do those in the diagram presented by the authors in fig. 2. These new limits indicate that sigma phase should form in an Fe-Cr alloy containing 26 pct Cr, and experience with commercial alloys confirms this finding. Indeed, recent studies on a commercial Fe-Cr alloy containing 17 pct Cr have shown sigma phase to be stable in this alloy at 550°C. I recognize that the authors' work did not include studies on the sigma region; however, I believe this is a serious omission because sigma phase may profoundly affect the physical properties of these alloys and should be evaluated in any investigation which attempts to relate physical properties to the equilibrium diagram. The second investigation to which I refer is that made on the Fe-Cr-Ni system by Rees, Burns, and Cook,'' who used pure alloys and employed heating 17 W. P. Rees, B. D. Burns, and A. 3. Cook: Journal Iron and Steel Institute. (July 1949) 162, Part 3. p. 325. times that extend to 200 days. These investigators published their results in July 1949 and from these results constructed isothermal sections at 800" and 650°C. The isothermal section at 650°C is shown here as fig. 35. This diagram indicates sigma phase should form in a pure 18 pct Cr-8 pct Ni alloy. Although sigma phase has not been observed after 10,000 hr at 1200°F in commercial 18-8 alloys containing carbon and nitrogen, it has been observed under the same conditions in 18-8 alloys modified with titanium and columbium, both of which serve to reduce the effect of carbon and nitrogen. This section and the one at 800°C suggest that the constant iron sections which are presented by the authors, should be considerably altered, if they are to represent an accurate picture of the system. A few of the suggested alterations are as follows: In fig. 9, the section at 50 pct Fe, the gamma plus sigma region should be widened, not narrowed at 800" and 650°C. In fig. 10, the section at 60 pct Fe, the gamma plus sigma region should be widened at 800° and 650°C. In fig. 11, the section at 70 pct Fe, an alpha plus sigma, an alpha plus gamma plus sigma, and a gamma plus sigma region should be added. In fig. 12, the section at 80 pct Fe, the alpha plus gamma region should be widened at 800°C. In fig. 13, the section at 90 pct Fe, the alpha plus gamma region should be widened at 650° and 800°C. Undoubtedly, the chief reason for the discrepancies between the authors' data and those of Rees, Burns, and Cook is that the authors did not employ long enough heating times to allow for transformation. In this connection, I wish to warn that transformations in these alloys, particularly transformations at temperatures below 800°C, are extremely sluggish and may require a year or more to approach completion. Therefore, unless extremely long heating times are employed or steps are taken to accelerate these transformations by such means as mechanical working, the results will not yield an accurate picture of the alloy system. Certainly, an accurate picture is needed for the development of better high-temperature materials. E. J. Dulis-The purpose of this work is not clear. If an improvement of the ternary equilibrium diagram of the Fe-Cr-Ni system was wanted, it seems logical that testing techniques superior to those previously used would be a prime requirement. To approach equilibrium in this system, long holding times are needed; a fact established long ago but apparently ignored by the present authors, who used the continuous heating and cooling tests in equilibrium studies. A publication on the same system by Bradley and Goldschmidt6 was criticized by Monypenny in a

Jan 1, 1951

By D. J. Mack, R. E. Reiswig

Six examples of the peritectoid transformation were selected from the literature and studied by the method of isothermal transformation. The kinetics and mechanisms of five of the examples are presented as TTT diagrams and photomicrographs. The exist-enc- of a peritectoid in the sixth case is doubtful. ALTHOUGH the peritectoid transformation per se has been known for many years, no precise published data exist concerning the kinetics or mechanisms involved in transformations of this type, except for the brief treatment by Rhines, et al. 1,10 Bearing in mind the fact that investigations of recent years are uncovering more and more peritectoids and suspected peritectoids, a thorough study of the well-established peritectoids appeared to be in order. It was for this reason that a study of the kinetics and morphological mechanisms of six binary peritectoids was undertaken. The six peritectoids selected from the literature for study were those reported at 7.02 wt pct Al-Ag, 26.0 wt pct Sb-Cu, 30.5 wt pct Sb-Cu, 32.3 wt pct Sn-Cu, 8.35 wt pct Si-Cu, and 21.2 wt pct Al-Cu. These selections were based on availability and purity of components, ease of preparation and heat-treatment, and estimated reliability of the available equilibrium diagrams in the regions of interest. EXPERIMENTAL PROCEDURE The alloys used in this investigation were induction melted in electrode-grade graphite and chill-cast in cast-iron split molds. In all cases, the alloys were so brittle that they could easily be broken into samples weighing 1 or 2 g. Chemical analyses showed that the alloys used were close to the respective peritectoid compositions reported in the literature and that the impurity levels were low in all cases. Metallographic examination showed uniform distributions of phases in all samples, indicating uniformity of composition in the samples studied. Isothermal transformation studies were carried out in fused-salt media, using the familiar inter-rupted-quench method. Uniformity of temperature in the salt baths was maintained by continuous stirring with a stainless-steel agitator. On the basis of actual observations of the temperature fluctuations, the estimated temperature control was + 10C for the Ag-Al and Cu-Sb alloys and ±30C for the Cu-Sn, Cu-Si, and Cu-Al alloys. The accuracy of all temperature measurements was estimated to be ±1°C. It was found necessary to mount metallographic specimens of the Ag-Al alloy in cold-curing methyl methacrylate, since the temperatures encountered in mounting in bakelite or lucite caused an appreciable degree of transformation to the ß phase. For the other alloys, wood-flour-filled bakelite mounts were used to avoid extraneous X-ray diffraction lines during the later examination of the metallographic specimens on a Norelco Geiger-counter d if f r ac tomete r. In the X-ray diffraction procedure, agreement between the published diffraction patterns and those obtained in this study was good. This was particularly important for phase identification, since the literature contained little in the way of micrograph description in some cases. Etching of the silver-aluminum alloy for metallographic examination was done by swabbing with either of the following reagents: 1) 10 g CrO3, 1 g (NH4), SO2, 0.5 g NH4NO3, 100 ml H2O, or 2) 10 ml NH4OH, 1 ml 20 pct KOH, 4 ml 3 pct H2O2, 5 ml H2O. The other alloys were etched with the usual bichromate etchant: 2 g K2Cr2O7, 1.5 g NaC1, 8 ml conc. H2SO4, 100 ml H20 (swabbed vigorously). EXPERIMENTAL RESULTS A) The Ag-Al peritectoid at 7.02 wt pct Al— The phase equilibrium involved in this peritectoid is shown in Fig. I.2 The phase boundaries in the vicinity of the peritectoid were most comprehensively established by Hume-Rothery, et al,3 who placed the equilibrium temperature at 448 °C and the equilibrium compositions of the a ß' and y phases at 6.11, 7.02, and 7.24 wt pct Al, respective The alloy used in this study analyzed4 6.95 wt pct A making it slightly hypoperitectoid according to the accepted equilibrium diagram. The rate of the transformation a+ y — ß' varies rapidly with degree of undercooling below the equilibrium temperature, passing through a maximum in the vicinity of 350°C. Thus the TTT dia-

Jan 1, 1960

By F. D. Rosi, C. H. Mathews

THE plastic properties of face-centered cubic metals below room temperature present a field of investigation which has not been extensively ex-plored. The work by Schmid and Boas1 has demonstrated the importance of temperature upon such properties as strain hardening and critical resolved shear stress. The work by Yamaguchi2 upon the shear stress as related to the number of slip bands accentuates the necessity for further experiments of a similar nature. The approach to a mechanical equation of state from the standpoint of thermal fluctuations and activation energies by Becker3 and more recently by Kauzmann4 further emphasizes the need for a quantitative and more comprehensive analysis of the dependence of fundamental plastic properties on temperature. The purpose of the present work was to investigate specifically: (1) The gross shape of the stress-strain curves at several temperatures, (2) the change in the critical shear stress as a function of temperature, and (3) the number and appearance of slip bands as a function of strain and temperature. Preparation of Specimens Single-crystal specimens of 99.996+ pct alumi-num, 1/2 in. in diam and 5 to 6 in. in length, were made by the Bridgman method of gradual solidification from the liquid state. The crystallographic orientation of the single crystals was determined from back-reflection, Laue X-ray photograms ac-cording to the method described by Greninger.6 In most specimens the Laue photograms showed double diffraction spots indicative of the lineage structure type of imperfection, discussed in great detail by Buerger.7 The angular spread of these spots was never observed to exceed 2". Most of the crystals were radiographed to insure against microporosity. In preparing the metal surface for optical microscopy, the following sequence of operations gave good results: The as-cast crystals were turned down in a lathe, 0.001 in. per cut, to obtain a 2.5 in. gauge length. The cold-worked layer resulting from this operation was removed chemically by etching with Tucker's reagent. Then the specimen was polished mechanically through 2/0 metallographic emery paper, after which it was etched again to remove the cold-worked layer resulting from the mechanical treatment. A 48-hr anneal at 580°C ±10°C followed so as to insure an essentially stress-free single crystal. After the annealing treatment, the specimen was electrolytically polished in a 2:l solution of methyl alcohol and concentrated nitric acid. With a current density of 10 amp per sq dm (decimeter) the time required to obtain a satisfactory surface varied from 10 to 12 min. The polish-ing was carried out for short periods of 2 min to avoid rapid deterioration of the solution as well as to enable the rotation of the specimen 180" for uniformity of polish. It was necessary to place the solution in a bath of dry ice in view of its explosive nature at room temperature. Etching of the electrolytically polished surface was accomplished by using the fuming etch-pit method recommended by Lacombe and Beaujard8 for high-purity aluminum. Method for Tensile Testing A modification of the loading equipment devised by Miller9 was used. In this apparatus, the specimen was suspended from a chain and gimbal arrangement (for axial loading) in a heavy steel framework connected at the bottom to a balanced 6:1 lever and bucket system. Loading of the specimen was accomplished by allowing sand to flow from a reservoir into the bucket suspended from the longer end of the lever-arm at a rate of approximately 3 lb per min. Strain measurements were made using the Baldwin SR-4, bonded, resistance-wire, strain gauge and an SR-4 portable strain indicator (type K), which permits a reading accuracy of 2 microinches per inch. For low-temperature study, the gauge was calibrated by measuring the elastic modulus of an annealed stainless steel rod, which is known to be independent of temperature."

Jan 1, 1951

By A. Gatti, R. L. Fullman

A very fine dispersion of aluminum oxide is produced by internal oxidation of solid-solution alloy of 0.14 pet A1 in Ag. The particle size of the aluminum oxide is approximntely 50 to 100A in radius. The yield strength of the alloy is increased markedly by internal oxidation. A further increase in strength is produced by cold working the internally oxidized alloy. Recrystallization is retarded by the finely dispessed aluminum oxide particles, so that the strength increase resulting from cold work is retained on annealing at temperatures 14 to about 700°C. MANY workers'-3 in the past have studied various aspects of the internal oxidation of aluminum-silver alloys. This paper is an extension of these studies with emphasis placed on the effect of time and temperature of annealing on the strength of these alloys after oxidation and subsequent cold working. Two general conditions are necessary to internally oxidize an alloy. First, oxygen must diffuse through the base material more rapidly than does the addition; otherwise oxidation will take place as a surface layer. Secondly, the affinity of oxygen for the addition must be greater than for the base material. After internal oxidation of certain alloys takes place, a marked increase in hardness accompanied by higher yield stress and improved creep properties is noted, presumably as a result of the highly dispersed oxide within the base material. Meijering and Druyvesteyn1 also noted that the internally oxidized portion of a partly oxidized alloy failed to recrys-tallize under annealing conditions that led to coinplete recrystallization of the unoxidized part. EXPERIMENTAL-METHODS AND PROCEDURES Few alloys can be made to contain a second phase that is extremely stable at high temperatures. Silver plus aluminum in solid solution was chosen for these internal oxidation studies because of the high rate of oxygen diffusion through silver and the very stable nature of aluminum oxide. Two alloys were vacuum cast. The nominal compositions were: Alloy A—1 pct Al, balance Ag; Alloy B—0.1 pct Al, balance Ag. Chemical analysis, which does not distinguish between aluminum and aluminum oxide, showed the conlposition to be: Alloy A—1.6 pct Al, and Alloy B—0.14 pct Al. The ingots were machined for surface cleaning, swaged and drawn to 0.020-in. diam wire. A sample 20 ft long of the 0.020-in. dianl wire of each composition was annealed 24 hr at 800°C in pure dry hydrogen. Each wire was then cut into two equal pieces. Photomicrographs of the 0.14 pct A1 alloy are shown in Fig. 1, the annealed 0.020-in. wire at the left and the oxidized wire to the right. The oxidation treatment for the first set of data was 1000 hr at 800°C in air. After this treatment the 1 pct A1 proved to be brittle. It is assumed that high alunlinum oxide concentration at the grain boundaries was responsible. The 0.14 pct Al wire remained ductile and all further data were derived using this alloy. One-half of this wire, about 5 ft, plus 5 ft of as-homogenized wire, was then drawn cold to 0.005 in. diam. All tensile tests were conducted with an Instron Engineering Corp. tensile-testing machine, Model TT-B. Unless otherwise indicated, the tests were made at room temperature with a strain rate of 0.1 per min. All metallographic samples were etched with an aqueous solution of 2 pct each of CrO3 and H2SO4 . EXPERIMENTAL RESULTS AND DISCUSSION PARTICLE SIZE DETERMINATION A study was made of the particle size of the aluminum oxide produced in the samples of Ag + 0.14 pct Al, oxidized 1000 hr at 800°C. A cross section of the as-oxidized wire was mounted in bakelite, polished, and etched with an aqueous solution of 2 pct each of CrO3 and H2SO4. The specimen was then thoroughly cleaned by stripping successive coatings made by applying 10 pct nitrocellulose in amyl acetate. The final replica of the cross section was made by applying 2 pct nitrocellulose in amyl acetate. The replica was stripped, transferred to a copper screen, shadow cast with chromium at 10 deg and photographs taken using a Phillips Metallix electron microscope at an accelerating potential of 100 kv. A photograph of an etched sample of the as-oxidized material is shown in Fig. 2. We believe the pits in the photograph are places were A12O3 inclusions were sitting in the matrix. By inspection, it appears that the volume fraction ob-

Jan 1, 1960

By W. S. Hyler, W. L. Bruckart

The powder metallurgy and arc-cast types of wrought molybdenum stock were studied in rotating beam fatigue. Endurance ratios of unnotched specimens after 5x10 cycles were found to be 0.74 and 0.81, respectively. Fatigue notch factors (K,) of 1.36 and 2.05, respectively, were obtained on V-notched specimens having a theoretical stress-concentration factor Kt = 3.1. MOLYBDENUM and its alloys are rapidly gaining importance as engineering materials of construction for high temperature applications. AS a wrought material, molybdenum and its alloys are outstanding above 1800°F. It is necessary, however, with molybdenum to provide elevated temperature oxidation protection. This is currently being studied by a number of investigators. Thus far, there have been no published data on the fatigue behavior of molybdenum either at room temperature or at elevated temperature. The knowledge of fatigue behavior, particularly notched fatigue behavior, becomes increasingly important as the engineering importance of a material increases, especially from the design standpoint. The work described here was directed toward determination of the notched and unnotched rotating beam fatigue characteristics of molybdenum at room temperature. Also, it was desired to learn whether any difference exists between wrought molybdenum of the powder metallurgy and the are-cast types. Fabrication History of Bar Stock For this work, bar stock was procured from Climax Molybdenum Co. (are-cast type) and from Westing-house Electric Corp. (powder metallurgy type). The processing histories of these materials are listed in Table I. The first lot of are-cast molybdenum was deoxidized by aluminum additions. The second lot was deoxidized by carbon." Both lots of the powder Microstructure A microscopic examination of these materials, as received, revealed the powder metallurgy molybdenum to be free of inclusions and to be finely fibered. On the other hand, the are-cast C molybdenum possessed numerous carbide inclusions, and the arc-cast A appeared to have coarse grained fibers. These are shown in Fig. 1. Owing to the large apparent difference in fineness of fiber between the are-cast A and the powder product and are-cast C, a check was made of the recrystallized grain sizes to determine whether these differences persisted. A series of recrystallization anneals revealed mixed grain sizes in both the are-cast A and the powder product. Variations in grain diameter of as much as 50 times were found after full recrystallization at 1200°C for 30 min. There was no distinction between the two. Arc-cast C was not checked. Room Temperature Mechanical Properties Prior to subjecting the materials to fatigue tests, room temperature mechanical properties were determined. These data, together with the tensil: strength of the notched bars, data,togetherare listed in Table tensil: There were no significant differences in the tensile strengths of the two types of molybdenum. However, the powder metallurgy material was generally more ductile and yielded at a somewhat lower stress than the arc-cast material. Tensile strengths of the notched specimens indicated a slightly greater notch strengthening effect in the are-cast C than in the powder product, lot 2. Room Temperature Fatigue Properties Sample Preparation: Specimens were prepared for use in R. R. Moore rotating beam fatigue machines. These specimens had a continuous radius test section with a minimum diameter of 0.260 in. The specimens were prepared by grinding to shape and polishing to produce a smooth unworked surface. Polishing consisted of rotating a disk in the continuous radius section on which were attached, successively, emery belts of 240, 400, and 600 grit. The specimens were slowly rotated during the operation. The belt speed was high, and rotation was such that polishing scratches were longitudinal. Unnotched Fatigue Properties: Unnotched fatigue data were obtained from a number of specimens of each of the four lots of molybdenum. The results of the tests are presented in Fig. 2. From this figure,

Jan 1, 1956

By E. F. Adkins, R. W. Douglas

The variation of the spectral emissivity of osmium and ruthenium with temperature can be expressed by the following relations: DURING a study of the sintering characteristics of osmium and ruthenium, discrepancies in the previously accepted melting points of the metals were noted. The melting temperatures had not been measured at the time of the work, but were estimated in the literature as 2700°C for osmium and 2450°C for ruthenium.' A recent investigation by Baird2 has shown the melting temperatures of osmium and ruthenium are 3000" and 2250° C, respectively. In the present work, osmium bars sintered at temperatures as high as 2900° C showed no evidence of melting, whereas ruthenium showed definite evidence of melting at temperatures as low as 2250°C. In view of the apparent discrepancies, the melting temperatures of both metals were determined. The spectral emissivities of both metals were determined as an aid to studies of the sintering characteristics of these metals. MATERIALS AND PROCEDURES The materials used in these studies were metal powders supplied by Englehard Industries, Inc., through the courtesy of The International Nickel Co. Analytical data from three laboratories, although not in complete agreement as to the purity of the material or the major impurity elements, indicated that the maximum impurity levels were 0.5 and 1.0 wt pct in osmium and ruthenium, respectively. The metal powders were pressed to 1/4 by 1/4 by 6-in. bars at 20Tsi using carbon tetrachloride as a lubricant. The pressed bars were presintered 1 hr at 1200°C after heating 1 hr at 400°C. The presintered densities of the several bars of the metals ranged from 65 to 80 pct of ideal density. Specimens were self-resistance heated in a vacuum sintering bell. Temperatures were measured with an L&N, disappearing filament optical pyrometer. True temperatures were read at the base of an 0.30-in.-diam, 0.150-in. deep hole drilled into the center of a presintered bar. Apparent temperatures were read from the surface of the bar adjacent to the hole. MELTING POINT DETERMINATION The melting temperature of the metals was determined as the temperature at which a slight additional increase in current through the specimen resulted in a reduced temperature at the base of the hole. The apparent reduction in temperature is a result of the liquid metal filling the hole, thus altering the black-body conditions. The melting points of osmium and ruthenium, based on three deter-

Jan 1, 1962

By R. E. Reed-Hill

The lattice reorientations in (1011) and (1013) twins of pure magnesium have been investigated using polarized light. Both forms (Ire subject 20 almost complete second-order twinning on the (1012) plane of the first-order twin. The observed deviations of composition planes by 6 and 3 deg, respectively, from coherent twinning planes are caused by second-order twinning. The experimental data indicate that (1011) and (1013) are reciprocal twins with a twinning shear 0.136. In a previous paper1 it was shown that the primary fracture mechanism in single crystals of magnesium strained in tension parallel to the basal plane is parting or fracture inside twins. In the temperature interval 25oto286oC, the observed twinning form, dominant in fracture, was a very small twin which formed in bands. Because these twins were very small and appeared in extensively deformed regions they did not lend themselves to X-ray analysis. Lacking Cou-ling and Pearsall&apos;s2 recently reported polarized light technique for magnesium, the twinning plane indices (K1) were originally determined by two surface composition plane measurements. This plane fell in a major zone (axis < 1120>) at an angle of 55.75 deg to the parent crystal basal plane. Because its habit deviated by 6 deg from{l0ll), 61.9 deg, the experimental data per se were not consistent with simple (1011) twinning and, for expedience, the twin was designated with habit plane indices (30341, 54.5 deg, representing the lowest set of indices corresponding to measured angles. Couling, Pashak, and sturkey3 have also found bands of reoriented lattice with a similar habit in polycrystalline specimens of magnesium and certain dilute magnesium alloys. These bands are significant because their formation in large numbers during plastic flow permit specific magnesium alloys to undergo very extensive deformation by cold rolling. Using polarized light2 they showed that the basal plane in the reoriented material was nearly parallel to the band habit and, as a result, proposed a mechanism for band formation involving a double twinning process in which (1011) twins form and then retwin according to (1012). Because of the obvious similarity between the twin bands observed in single crystals and in polycrystalline specimens, it was decided to investigate if the two phenomena were not identical and, if possible, to verify the retwinning hypothesis. The present paper is a report of this investigation and shows that the twins with the (3034) habit correspond closely to retwinned (l011) twins. Evi- dence is also given for an analogous retwinning process in (1013) twins. EXPERIMENTAL PROCEDURE Rectangular single-crystal specimen deformed in tension (stress axis in the basal plane parallel to [1010], as previously described,4 were polished electrolytically by Jacquet&apos;s method5 and etched in acetic picral.2 All twins studied in this investigation belong to a major zone, whose axis, [1210], was perpendicular to both stress axis and two sides of each specimen [(1210) surfaces]. These latter contain the plane of shear of the twins and measurements of the basal plane trace of twins on these surfaces determines the lattice orientations of the twins. The position of the basal plane in each case was determined with a polarizing microscope using a modification of the technique of Couling and Pearsall.2 For each twin the four positions of maximum extinction were measured, the data averaged, and then the pair of extinctions corresponding to the basal plane was determined by rotating the microscope stage and observing the position at which the color changed from orange to blue with a gypsum red, first-order plate inserted between the crossed Nicol prisms. EXPERIMENTAL RESULTS (1013) Twins—In general, especially in speci-mens deformed at 150°C, (1073) twins appear in greater numbers and larger sizes than (1011) twins, and the lattice reorientation inside these twins is therefore easier to study and measure. Fig. 1 shows an area of an unetched and unpolished (1210) crystal surface containing a number of (1073) twins sloping upward to the right at about 29 deg with the basal plane of the original crystal (horizontal direction). Slip line segments may be seen in both the parent crystal (running horizontally) and in the twins (sloping downward to the right at approximately -22 deg with the horizontal). As may be seen in Fig. 2, the slip lines in the twin are not at the proper angle (64 deg from basal plane of the

Jan 1, 1961

By R. Taggart, G. R. Purdy

DURING a study of the tempering of ß-quenched alloys of cobalt in titanium, parallel lines were observed crossing certain faces of retained-ß crystals in the early stages of tempering, Fig. 1. The lines closely resemble stress-induced martensite&apos; or substructures attributed to clusters of faults in titanium-nickel2 and copper-silicon3 alloys. The markings were observed only in intensely etched quenched and tempered alloys having compositions ranging from 4.5 pct* Co (the composi- formed by the lines was reproduced upon repolishing and reetching. Close metallographic examination indicated that the markings were troughs, Fig. 2, and that the characteristic surface substructure persisted within the troughs. The occurrence of the troughs was associated with the age hardening reaction due to the metastable u) phase (previously reported in titanium-cobalt alloys by Raub and Beeskow4 and indicated in this work by the broadening of 0 diffraction peaks and by hardnesses approaching 600 Dph). The troughs

Jan 1, 1961

By W. Rall, A. J. Birkle

The effect of fast-neutron irradiation on the micvo strcture of a common reactor pressure-vessel steel, A212 Grade B, was studied using thin-foil transmission electron microscopy. The dislocation density of the irradiated material is considerably greater than that of the nonirradiated control material. Annealing studies indicated that dislocations and hardness ill the irradiated material annealed out—as docs the radiation-induced embrittlement according to other- investigators— at temperatures STEELS in nuclear reactors are affected by neutron irradiation. In the American Society for Testing Materials (ASTM) A302B and A212B steels commonly specified by designers for reactor vessels, between 650° and 800°F. However, the dislocations and hardness in control samples cold-worked to 9 and 70 pct did not anneal out readily, and a high dis -location density was observed, even after a 1-hr anneal at 850°F. Based on the hypothesis that cllrster defects, rather than the increased dislocation density, are primarily responsible for mdicltiotz-iudziced e)nbriftlen7ent, reconzmendations are made for reducing the susceptibility to such ernbrittlement. exposures at a temperature of 550°F or lower to neutron dosages encountered during a 20- to 30-year life (-3 X 10&apos;&apos; nvt, >1 mev) may increase the nil-ductility transition temperature (NDT) as much as 300" or 400".&apos;9 Therefore, to prevent brittle failures in reactor structures, extreme caution is required to reduce thermally induced stresses during all reactor shutdowns and startups when the temperature is below the NDT of the pressure vessel.

Jan 1, 1964

By R. W. Armstrong, D. H. Feisel

Self-diffusion in pure crystalline solids has been described through extension of the Cohen and Tum-hull volume -fluctuation model originally proposed for diffusion in simple liquids. It is shown, for a number of crystalline solids, that the self-diffusion coefficient, D, obeys the relationship where a is the lattice spacing, v the Debye frequency, Z&apos; the lattice-volume fluctuation per atom required for a diffusion jump, and (?V/Vo) the relative increase in the lattice volume resulting from thermal expansion between O°K and the temperature under consideration. The calculated value of Z&apos; is dependent upon the difiusion mechanism and the lattice geometry. ThE need for an increased understanding of mass-transport processes in crystalline solids has resulted in much research to determine rates of self-diffusion.&apos; For several metals (e.g., copper, silver, and iron), the experimental values of the self-diffusion coefficient, D, have been determined over a large interval of temperature and the accuracy of D has been investigated through repeated experiments. Also, a number of empirical and theoretical diffusion studies have established a rational basis for understanding the D values for the different elements.2"6 The empirical diffusion analysis by Sherby and simnad6 supplied the main stimulus for the present study. Sherby and Simnad, reviewing the self-diffusion data for a substantial number of pure crystalline solids, suggested that sufficient data were available to establish with some certainty the apparent intrinsic material properties which influence D. Without explicit regard for any mechanism of diffusion, these investigators obtained an empirical relationship for D which correlated the self- diffusion coefficient for each element with the melting temperature, crystal structure, and valence of the particular element. Their analysis is only unsatisfactory in that the effect on D of crystal structure is not very clear and the valence to be assigned to an element is not always straightforward. The present study is an attempt, from a very different viewpoint from that of Sherby and Simnad, to establish a basis for understanding the self-diffusion coefficients for crystalline solids. This analysis was undertaken for the purpose of developing a general expression for D which would explicitly depend on the mechanism of diffusion. The main result of the study is that diffusion in crystalline solids may be described in terms of a volume-fluctuation model which was originally proposed by Cohen and Turnbull7 to describe diffusion in simple liquids. The model appears to be useful for predicting self-diffusion coefficients in crystals. The following sections describe the volume-fluctuation model for diffusion, the application of this model to crystals, and the resultant agreement with experimental data. 1) THE VOLUME-FLUCTUATION MODEL FOR DIFFUSION Cohen and Turnbull7&apos;8 developed their model for liquid self-diffusivity for the purpose of describing certain properties of liquids, glasses, and the liquid-glass transition. A hard-sphere model for the liquid structure is used. In this model, the size of a spherical molecule or atom is fixed for all temperatures by the interatomic spacing at the absolute zero of temperature. At any temperature above O°K, the atom is viewed as being contained within a larger spherical cage defined by the interatomic spacing of the atoms at that temperature. A random distribution of varying cage sizes is assumed to exist in the liquid. An individual diffusion jump occurs when the free volume of an atom (the volume of the cage containing the atom minus the volume of the atom) is large enough for the atom to jump out of its cage. With this physical picture of diffusion in liquids, Cohen and Turnbull derive the following equation for self-diffusivity: D=Doe-yv*/vf [1] where Do is the product of three factors which are the diffusion-path geometry, the diffusion-jump distance, and the velocity of the diffusing atom, v*

Jan 1, 1964

By E. T. Wessel

UNEXPECTED brittle failures of metals in practical applications are a serious problem to many industries and to the nation as a whole. Considerable effort has been devoted to studies of the brittle behavior in metals. However, the major portion of this effort has been directed at developing techniques and apparatus for the purposes of determining the susceptibility of metals to brittle failure and of making various types of observations of the phenomena. Relatively minor effort has been made to understand the basic mechanisms involved in initiating brittle failures. A more complete understanding of the nature and mechanism of the brittle failure problem would be very helpful in efforts directed toward predicting and avoiding brittle failure and toward the development of suitable materials and designs that are not susceptible to a brittle behavior. The intent of the present investigation is to acquire this basic understanding. The pronounced transition from a ductile-to-brittle behavior is most prevalent in metals having the body-centered-cubic lattice structure, primarily be- cause metals of this structure exhibit a strong dependence of yield strength upon temperature and the rate of straining. The generally recognized qualitative concept of the ductile-to-brittle transition is that brittle (cleavage) failure occurs when the yield strength exceeds the cleavage fracture strength. This condition can apparently be achieved by decreasing temperature or increasing strain rate. Likewise, a normally ductile metal can be made to fracture in an apparently brittle manner by the introduction of triaxial stresses (notches) where the ratio of normal to shear stresses can be increased to such an extent that the normal stress exceeds the fracture strength before the critical shear stress for plastic flow is achieved. Neither of these concepts require any prior plastic deformation or explain why the observed fracture strengths are so much less than the theoretical cohesive strength. The results of several investigations of the ductile-to-brittle transition in body-centered-cubic metals illustrate rather conclusively that measurable amounts of nonelastic deformation do precede cleavage fracture, even at extremely low temperatures. These studies suggested that the early stages of plastic flow, particularly abrupt yielding, and their relationship to brittle fracture should be examined

Jan 1, 1958

By J. E. Pavlick, A. G. Guy

The total creep of tin alloys containing antimony in solid solution was observed to decrease with increase in antimony content. However, near the solubility limit an anomalous maximum in deformation was. found, in agreement with similiar observations by Bochvar. IT has long been recognized that alloys may deform more rapidly under stress if there is a tendency for a phase change or other structural change to occur simultaneously. However, the phenomena involved are complex and in some instances the opposite effect, strengthening, may result.&apos; This area of research has not attracted much interest in the western world, and although Russian investigators have studied it for the past 15 years their work has not received due attention here. Recently diametrically opposing views on one aspect of this problem have been espoused by two Russian investigators, Kornilov and Bochvar. The question is this: in certain binary alloys tested in creep at the temperature where the solute is at the limit of solid solubility, does the incipient formation of the second phase strengthen or weaken the alloy? Korni-lov&apos;s arguments in favor of strengthening were presented at the 1954 Symposium at the National Physical Laboratory, =Creep and Fracture of Metals at High Temperatures.The most recent statement of Boch-var&apos;s theory of weakening is in Oding&apos;s new book on creep and rupture.3 Although Bochvar agrees that strengthening occurs in some alloy systems, he argues that in certain alloys an anomalous weakening is observed. However, the extensive work of Korni-lov&apos;s group on creep properties of alloy systems has not revealed any anomaly of this type, but instead has tended to refute Bochvar&apos;s theory. This clear-cut controversy offered a good opportunity for a simple experiment to resolve the problem. The experiment and its results supporting Bochvar are the subject of this paper. However, it will be helpful first to sketch the present status of the larger question of the effect of a phase change or other structural change on plastic deformation. PREVIOUS WORK One of the first researches in this area was by Pfei1,37 who investigated the creep resistance of an 80 Ni-20 Cr alloy containing varying amounts of titanium. He found that the resistance to creep increased rapidly as the solid solubility limit in the alloy at 775&apos;c was approached and slightly exceeded. With further addition of titanium the creep resistance decreased, presumably because of precipitation effects. Bochvar&apos;s first work in this field was a study in 1945 of "superplasticity" in zinc alloys containing 15 to 25 pct Al.4 He found that alloys quenched from about 400 had anomalously low hardness when tested below this temperature. The following year, in a paper on the dependence of mechanical properties on the composition and structure of alloys,5 he extended some observations of Kurnakov to predict that at high temperatures of testing the hardness values for solid-solution alloys might be lower than those for the component metals. He also pointed out the influence of changes in solidus temperature in affecting curves of hardness vs composition, and he

Jan 1, 1962

By Y. A. Rocher, J. E. Dorn, L. A. Shepard

Creep activation energies for single aluminum crystals favorably oriented for shear by (010) [101] glide were detemined over the temperature range from 78" to 900°K. Observations of slip bands on the specimen surface were made in conjunction with the investigation. From 78" to 780°K, the activation energies obtained in this imestigation agreed closely with those previously found for creep by (111) [101] slip. Between 78" and 140°K, the activation energy was identified with the Peierls process, while between 260°and 780°K the activation energy was close to that for cross-slip. The coarse wavy slip bands nominally parallel to the (010) plane observed above 260°K were attributed to fine cross-slip. From 800" to 900°K, unusually high apparent activation energies ranging from 28,000 to 54,000 cal per mole were obtained. These apparent activation energies were attributed to re crystallization. AS illustrated in Fig. 1, a recent investigation1 has shown that creep of aluminum single crystals by the (111) [i01] mechanism is controlled by three unique processes, each of which is characterized by a single activation energy which is independent of the applied stress and the creep strain. A comparison of the observed activation energies with theoretically calculated values permits a fairly clear identification of the three operative creep processes. Below 450°K, where the activation energy for creep is 3,400 cal per mole, the deformation is controlled by the Peierls process, the activation energy for creep agreeing well with that calculated by seeger2 for the energy required to nucleate the motion of a dislocation loop against the atomic forces of the lattice. Between 590° and 750°K, the observed activation energy for creep of about 28,000 cal per mole agrees well with the energy necessary to induce cross-slip. Seeger and schoeck3 estimate that the activation energy is about 24,000 cal per mole whereas Friedel4 recently calculated this activation energy to be 28,000 cal per mole. Above 800°K the activation energy of 35,500 cal per mole that was observed for creep agrees well with that estimated for self-diffusion in aluminum.= In this range the operative rate-controlling slip process has been clearly identified as that arising from the climb of edge dislocations. The objective of this investigation is to ascertain whether a single crystal of aluminum favorably oriented for simple shear in the [loll direction on the (010) plane might exhibit uniquely different activation energies for creep from those obtained previously for (111) [101] slip. Whereas the exis- tence of such unique activation energies would constitute incontrover table evidence for new mechanisms of slip, the absence of any new activation energies might suggest that slip of aluminum is confined to the (111) [loll mechanism. Several factors prompted the selection of the (010) [101] orientation for study. First, there are more reported observations of (010) [loll slip than of any other nonoctahe-dral mechanism.8-10Secondly, Chalmers and Martius1l have concluded from considerations of the energies of dislocations that (010) slip is the second most favored mechanism in face-centered-cubic metals. Finally, favorable orientations for simple shear by the (010) [loll mechanism provide the least favored orientation for slip by the (111) [101] mechanism. EXPE-RIMENTAL PRO-CEDURE The high-purity aluminum stock, specimen preparation, shear fixture, extensometry, and experimental technique used in this investigation were the same as those previously reported.&apos; Single-crystal spheres grown from the melt of 99.995 pct pure Al* were _ *The high-purity aluminum used in this investigation was graciously given by the Aluminum Company of America. oriented, carefully machined into dumbbell-shaped shear specimens, annealed, and chemically polished. The finished specimen had a central reduced section 0.190 in. wide and 0.590 in. in diam and 1/4-in. grip sections at both sides, 0.690 in. in diameter. The specimen was oriented in the stainless steel grips of the shear fixture with the (010) plane perpendicular to the dumbbell axis and the [loll direction parallel to the stress axis within 2 deg. Creep activation energies were calculated in the previously described manner1 from determinations of the instantaneous change in shear strain rate produced by an abrupt 15 to 20 deg increase or decrease in test temperature. If is the instantaneous strain rate at strain y and temperature T1, and ?2 the instantaneous rate at y and T2,

Jan 1, 1960

By H. I-Lieh Huang, O. D. Sherby, J. E. Dorn

RECENT investigations1-4 have suggested that the total plastic strain, C, for high temperature creep under a given stress can be correlated by means of a temperature-compensated time, te- where t is the duration of test, e is the base of natural logarithms, aH is the activation energy for creep, R is the gas constant, and T is the absolute temperature. A typical set of data on which this deduction was based is given in Fig. la. Inasmuch as the e-in t curves for the various temperatures are identical except for their displacement along the In t axis where f and are appropriate functions. If the increase in creep rate with an increase in temperature is exclusively ascribable to a single process involv- ing thermal activation, (T) should equal RT and therefore it = constant [2] where ?= te Assuming the validity of this relationship, ? = ?2 at the same strain, or where the subscripts refer to two alternate test conditions.

Jan 1, 1957

By J. E. McDonald, J. G. Eberhart

A model is discussed from which the work of adhcslon .tor liquid transition metals on aluminum oxide surfaces can he calculated, A close-packed (00011 oxygen surface on A12O3 is assumed with two different types of surface sites: one type involving metal-oxygen bonds and the other man der Waals into actions. The work of adhesion is thus expressed as the sum of these two bonsding free energies. Calculated works of adhesion for nickel, titanium, chromium, and zirconium on sapphire agree well with the experimentally determined quantities. The model is extentled to the calculation of the work of adhesion and shear stress required to remove a thin metal film from a sapphire substrate and is in good agreement with experimental values. The obsewed dependence of the work of adhesion on the free energy of oxide formation of the metal is shown to also provide an interpretation of the tittle dependence of thin-film adhesion. THIS paper presents a model for the type of bonding which occurs across a metal-A12O3 interface. The model is used to explain the results of two types of experiments in which such an interface exists: 1) the adhesion of thin metal films on Al2O3 substrates and 2) the wetting of A12O3 by liquid metal drops. The adhesion of thin films to various substrates has been the subject of a variety of investigations.&apos;-&apos; Benjamin and weaver3 and Bowie,6 using the scratch test developed by Heavens,10 studied the adhesion of metallic films to glass substrates. Their observations for noble-metal film adhesion agree well with an adhesion model involving a van der Waals type of bonding between the film and the substrate. For films of metals whose free energy of oxide formation. ?F°f, has a negative value. Benjamin and weaver3 and Bowie6 found a time-dependent adhesion with an initial value that can be interpreted in terms of van der Waals interactions but a larger terminal value which was related to ?F°f, Karnow-sky and Estill7 deposited films on sapphire at elevated temperatures and noticed no time dependence of film adhesion but a similar correlation with ?F°f. Because of the kinetic problems associated with thin-film adhesion it is desirable to examine adhesion in an equilibrium system. The wetting behavior of liquid-metal drops on Al2O3 provides such a system. Systems of this metal-ceramic type have been studied extensively.11 Humenik and Kingeryl2 have measured the wetting of A12O3 (and other substrates) by several metals and have pointed out that the wetting ability of these metals increases with increasing values of -?F°f. It is thus seen that thin-film adhesion and metal wetting on A12O3 are both related to the tendency of the metal to react with the surface oxide ions of the Al2O3 substrate and, because of this, both phenomena should be explainable by an appropriate model for the metal-Al2O3 interfacial bonding. In the sections that follow, wetting and adhesion data on A2O3 are reviewed and a model is presented by which these phenomena can be interpreted. ANALYSIS OF WETTING EXPERIMENTS In an equilibrium system involving a liquid-metal drop on a solid Al2O3 substrate, the work of adhesion, WAD, is defined by the Dupre, equation as WAD = ?s + ?L -?sL [1] where ?s and ?L are the surface free energies of the solid substrate and the liquid drop, respectively, and ?sL is the interfacial free energy. The work of adhesion is the work required to separate a unit area of the solid-liquid interface into two surfaces. The work of adhesion is usually determined from a sessile-drop experiment in which yL and the contact angle, ?, are measured. The Young-Dupr6 equation is then used to calculate WAD Wad = ?L (1+ cos ?) [2] The literature of this subject has been examined and Table I shows work of adhesion data for various liquid metals as measured on A12O3 substrates. The standard free energy of oxide formation of the metal at the temperature of the wetting experiment, ?F°f . is also tabulated in kcal per g-atom of oxygen. The data is grouped according to the gaseous atmos-

Jan 1, 1965

By C. S. Barrett

The torsional after-effect in polycrystalline cadmium is interrupted by an abnormal twisting when the film is removed by etching. This is accounted for by the pile-up of dislocations beneath anodic or other oxide films during the original twisting, and the relief of the residual stresses from these by elastic and plastic processes during etching. WHEN an iron or zinc wire coated with oxide is plastically twisted and then released, it untwists according to a law of equal increments in equal intervals of log time, but if the oxide is suddenly removed by etching this normal after-effect is interrupted by a transient, and thereafter the untwisting is slower.&apos; Etching may even reverse the strain temporarily. Related effects caused by hydrated oxide films on cadmium in creep tests have been observed by Phillips and Thompson:&apos; definite transient strains caused by the removal of the film from single crystals of cadmium were observed; however, negligible effects were obtained with polycrystalline wires. Pronounced effects of both transient and steady nature were observed by Phillips and Thompson when anodic films 10-4 cm thick were etched off, and weak effects, transient only, occurred with hydrated oxide films 3x10 cm thick such as were formed by standing in water for 10 min. It was estimated that 10.&apos; cm films, formed in water in 1 or 2 min, could be detected in the apparatus of Phillips and Thompson. Since abnormal after-effects were observed by the torsion method equally well with polycrystalline and monocrystalline iron and zinc wires,&apos; it was anticipated that the torsion method would also disclose them in polycrystalline cadmium, in spite of the fact that analogous effects had not been observed in tensile creep tests on polycrystalline zinc by Pickus and Parker3 r on polycrystalline cadmium in tensile studies by Andrade and Randall." Because of its high sensitivity, particularly its sensitivity to surface conditions, the torsion method was thought to merit further study as a method of investigating thin films of various types and the action of various reagents on these films. Materials and Methods Cadmium wires were cold-drawn to a diameter of 0.039 in. from a stock that was determined spectro-scopically to contain 0.05 pct Bi, 0.005 pct Cu, 0.008 pct Pb, and 0.007 pct Si. The wires were cut to about 17/8 in. lengths and were annealed 1 hr in air at 290°C, after which the grain size was such that there were 5 to 7 grains across a diameter. The wires were then mounted as indicated in the insert in Fig. 1, one end being fastened with laboratory wax into a small diameter brass tube and the other end being waxed to a thin glass fiber which supported, on its upper end, a small galvanometer mirror. The wires were waxed with care to avoid straining or annealing, for it was found that the after-effect rate was sensitive to prior cold work in a wire. The assembly was then clamped above a beaker into which the reagent could be poured. The lower end of the wire was held in the hand while the wire was twisted 180"; it was then released immediately. Since precision timing of these manipulations was not attempted, the different wires cannot be compared as to exact rates of untwisting. The length subjected to plastic strain was 15/8 in. The surface coatings studied were those produced by the annealing in air, by anodic treatment of

Jan 1, 1954

By N. Brown, H. Green

The effect of quenching temperature and of aging temperature and time on compression stress-strain curves of ß brass was investigated. Age softening occurs at a rate which decreases with decrease of quenching temperature below the critical temperature for ordering. The activation energy for softening is 15,400 cal per mol. No matter how rapidly brass is quenched or what the temperature from which it is quenched, practically complete order is obtained at room temperature. It has been demonstrated that with respect to the specific heat,&apos;,&apos; electrical resistivity," X-ray diffraction, and microstructure, the slowly cooled and rapidly quenched specimens are the same and that complete long range order exists in both cases. However, Smith" showed that the hardness of ß brass depended upon the cooling rate and the temperature from which brass is quenched. Smith showed that the hardness was a maximum for specimens quenched from about 445 °C and that the as-quenched structure softened at room temperature at a rate depending upon the temperature prior to quenching. This softening after quenching is in this paper referred to as age softening. The results of this investigation are qualitatively the same as the findings of Smith. However, a more detailed analysis of these phenomena has been possible since the stress-strain curve offers a more sensitive index of the state of the metal than hardness. It is the purpose of this paper to show how the mechanical properties are related to the ordering of ß brass. A 200-lb ingot made from electrolytic copper and electrolytic zinc was extruded to 1/2in. rod. Chemical analyses at frequent intervals along the rod showed that the alloy contained 51.5 pct Cu with the greatest impurity being iron, at 0.01 to 0.001 pct. To obtain a constant test material, the 1/2in. extruded rod was warm-rolled to % in. diameter at 200°C and then recrystallized to a grain size of 2.0 mm. The specimens for the compression test were % in. high and % in. in diameter. The specimen ends were polished on 600 metallographic paper and coated with Molykote for a lubricant. The compression rig consisted of an anvil resting on the machined table of the Baldwin Southwark testing machine and a plunger fixed to the movable cross

Jan 1, 1954

By G. R. Speich

The age-hardening of Fe-18 to 21 pct Ni marten-sites containing small amounts of titanium, aluminum, copper, or molybdenum has been studied by hardness measurements, transmission electron microscopy, extraction replicas, and X-ray and electron diffraction. Electyon-probe microanaly-sis of the extracted precipitates was also performed. The effects of temperature and composition on the aging kinetics have been studied in detail for Fe-20 pctNi-Ti martensites. All the martensites hardened on aging at 400" to 500 "C with a single aging peak. In the Fe-20 pct Ni-Ti martensites hardening was associated with the formation of a fine dispersion of NisTi. No precipitation was observed in an Fe-21 pct Ni-2.6 pct A1 alloy, although the hardness increased from 327 to 545 Dph during aging at 500°C. Copper was precgitated from an Fe-20 pct Ni-10.7pct Cu alloy, at least during the later stages of age-hardening. Hardening in an Fe-18 pctNi-5pct Mo alloy was associated with the precipitation of an intemzetallic compound tentatively identified as NisMo. The formation of austenite and the recovery of the defect structure of the martensite occur simultaneously with the normal precipitation processes &ring aging of these alloys. THE age-hardening of substitutional iron-base martensites is an important subject for study since age-hardening is one of the principal means of strengthening the substitutional iron-base martensites in precipitation-hardening stainless steels1 and maraging steels.a~4 In contrast to Fe-C martensites, these martensites are relatively soft and ductile in the as-quenched condition, due to the low solid-solution hardening effect of the substitutional elements as compared to carbon. Also, these martensites are hardened by aging at low temperatures in contrast to Fe-C martensites which generally soften on tempering. Titanium and aluminum, singly or in combination, as well as copper and molybdenum, have been the principal alloying additions to stainless steels to obtain an age-hardening reaction.&apos; Ti-A1 or Co-Mo-Ti combinations have been used in the case of maraging steels.3"4 The present work has been confined to a study of the age-hardening characteristics of an Fe-18 to 21 pct Ni martensite to which small amounts of titanium, aluminum, copper, and molybdenum were added in order to study the effects of each alloying element separately. The age-hardening characteristics of these alloys were studied by hardness measurements, transmission electron microscopy, extraction replicas, and X-ray and electron diffraction. Electron-probe micro-analysis of the extracted precipitates was also performed. The types and dispersion of precipitates, the formation of austenite, and the recovery of the defect structure of the martensite all were studied. EXPERIMENTAL PROCEDURE Alloys. The compositions of the alloys studied are listed in Table I. The level of 18 to 21 pct Ni was chosen to assure complete transformation to martensite on quenching and is the same nickel level used in maraging steels. The concentrations of titanium, aluminum, copper, and molybdenum were chosen after a study of the and Fe-Ni-MO&apos; ternary diagrams indicated how much of each alloying element could be dissolved in austenite. Alloys with 2 and 4 pct Cu were also studied, but these did not show precipitation hardening at the nickel levels studied and will not be discussed further. The alloys were prepared from electrolytic iron and high-purity* nickel, titanium, aluminum, copper, and molybdenum by vacuum melting of 20-lb heats. These were vacuum-cast into two 8-lb ingots. The ingots were hot-rolled at 1100°C to 1/2-in. plate and subsequently cut into 3/8-in. cubes. The cubes were sealed in evacuated quartz capsules and solution-treated for 16 hr at 1100°C, except for the Fe-20 pct Ni-10.7 pct Cu alloy and Fe-21 pct Ni-2.6 pct A1 alloys which were solution-treated for 16 hr at 1300" and at 1250"C, respectively. Metallographic examina-

Jan 1, 1963

By P. W. Ramsey, G. L. Werley

THERE have been numerous examples in recent years of the similarity between aging behavior and diffusion behavior, where a plot of the logarithm of the aging rate versus the reciprocal of the absolute temperature yields an approximate straight line, analogous to a similar plot of the diffusion coefficient D (log D vs. 1/T). Austin and Rickettl have pointed out that this linear relationship holds empirically for the de- composition of austenite into pearlite and bainite in carbon steels, and Robertson&apos; has shown similar trends in the aging of 24S-type aluminum alloys. Jenkins and Bucknall³ have also demonstrated the association between aging and diffusion rates for nickel-silicon-copper alloys. Jetter and Mehl,4 however, have shown that the maximum rate of dilation of a series of aluminum-silicon alloys does not show this linear relation and Mehl5 has pointed out that careful study of available knowledge indicates that "aging rates increase with temperature approximately exponentially, whereas D increases precisely exponentially." He further notes that "the rate of aging at a given temperature is the greater the lower the melting point of the alloy, which is also true for D." This paper describes the aging changes occurring in a zinc-25 pct manganese-15 pct copper-0.1 pct aluminum die casting alloy. It was found that this alloy does show this linear relationship and use was made of this relationship to estimate aging rates at low temperatures from data acquired at elevated temperatures. It should be noted that the aging reaction is being studied only indirectly, using changes in certain properties as criteria of the progress of the phenomenon. This alloy is purely an experimental one and is not available commercially. Zinc-Manganese-Copper System: The zinc-rich portion of the zinc-manganese-copper diagram which is of significance in the present work is quite uncertain. X ray examination of the alloy as die cast shows a phase similar to the epsilon phase (hexagonal close packed) of the copper-zinc system. All of the data accumulated indicate that the epsilon phase of the zinc-manganese-copper alloy is stable at high temperatures; that is, 500°C or above. Below this temperature a new phase is precipitated on annealing, and a decrease in specific volume occurs. At elevated temperatures this phase change occurs quite rapidly, while at room temperature the alloy has shown no change after several years. According to X ray data, this precipitated phase resembles the gamma phase (cubic) of the copper-zinc system, a hard and brittle structure. From examination of the microstructure and from X ray examination of the alloys annealed at

Jan 1, 1951

By N. J. Grant, R. Nordheim

An extensive study was made of the aging characteristics of alloys based on the 80 pct Ni-20 pct Cr composition hardened with aluminum and/or titanium, each up to 4 pct. Aging was followed by means of hardness and hot electrical resistance measurements as well as by X-ray and microscopy. Stress rupture tests at 1500°F were utilized as a check on the predicted behavior. THE titanium and aluminum hardened Ni-Cr alloys, exemplified by Nimonic 80 and Inconel X, constitute one of the more important groups of alloys developed to meet the demand for materials retaining their strength at elevated temperatures. For service in the temperature range 1200" to 1500°F, these alloys offer high creep resistance. With increasing service temperature, however, the strength of the simpler Ni-Cr base alloys falls off rapidly so that above 1500°F there is a significant loss of strength. The present investigation was undertaken with the hope that a better understanding of the factors controlling the precipitation hardening of these alloys would make it possible to increase the useful service temperature range. Primarily this investigation involved the study of the effects of titanium and aluminum on the hardening and the subsequent softening at elevated temperatures. The titanium and aluminum contents were each varied between 0 and 4 pct by weight at a constant nickel to chromium weight ratio of about 4:1. (Except when otherwise stated, all compositions are expressed on a weight basis.) The major part of the investigation was confined to alloys with less than 0.06 pct C. Recently several papers dealing with the identity of the microconstituents in the titanium and aluminum hardened Ni-Cr alloys have been published. Using X-ray analysis of the residues from anodic dissolution, Rosenbauml was only able to identify carbides and nitrides in Nimonic 80 and Inconel X. However, since Rosenbaum worked with alloys in the hot rolled rather than in the aged condition, his results are inconclusive. Recently Hignett&apos; reported that the hardening of Nimonic 80 was due to the controlled precipitation of Ni,(TiAl) having the cubic Ni3A1 structure. Taylor and Floydv-" published the results of an investigation of the nickel-rich corner of the Ni-Cr-Ti, Ni-Cr-Al, and Ni-Ti-A1 systems. In the Ni-Ti and the Ni-A1 systems the hexagonal Ni,Ti phase, 7, and the cubic Ni3A1 phase, -y&apos;, respectively, exist in equilibrium with the nickel-rich solid solution. The interatomic distances in the basal plane of Ni,Ti and the octahedral planes of the matrix are almost equal, thus explaining the Wid-manstaetten type structure formed when Ni,Ti precipitates from solid solution. When Ni:,Al precipitates from solid solution, it appears usually in globular form, often dispersed along rows corresponding to definite crystallographic directions. The 7 and phases are also the only intermetallic compounds which occur in the nickel ternary alloys with up to 25 pct Cr and 10 pct Ti or Al. Taylor and Floyd found that Ni,Ti takes practically no nickel, chromium, or aluminum into solution. Nial, on the other hand, dissolves a considerable amount of chromium and titanium and some nickel. Up to three out of every five aluminum atoms could be replaced by titanium in Ni,Al. This substitution caused a slight increase (less than 1 pct) in the lattice parameter. With respect to the effect of variation in the titanium and aluminum contents on the high temperature strength of Nimonic 80 type alloys, Pfeil, Allen, and Conway" reported that an 80 pct Ni-20 pct Cr alloy containing 0.20 to 0.30 pct A1 had the highest creep resistance when the titanium content was kept between 1.65 and 2.75 pct. Experimental Procedure The materials used for this investigation were electrolytic nickel, electrolytic or low carbon chromium, sponge titanium and 2s aluminum. The alloys were melted in an indirect carbon arc furnace under

Jan 1, 1955