By R. D. Carnahan, J. E. White

A study of dispersion strengthening in TD-Nickel (nickel plus 2 vol pct Tho2) was conducted employing microstrain techniques at ambient room temperature. It was found that optimum strength was due primarily to the incorporation of stored energy developed by a variety of thermal-mechanical treatments. The relatively low strength of the recrys-tallized condition implies that the dispersed particles themselves offer only token resistance to deformation. The development of resistance to large-scale recovery or recrystallization at temperatures near the melting point requires a more extensive sequence of strain-anneal cycles than does the development of optimum strength. A micro-Bauschinger effect was observed which appears to be related to the lattice resistance to the movement of free dislocations. The effect was nearly identical to that in pure nickel indicating that the presence of the dispersed phase and considerably increased dislocation density (stored energy) only alters the number or effectiveness of barriers. THE early stages of deformation of engineering materials can be conveniently studied by utilizing strain-gage techniques which permit resolution of strains less than 5 X 10-7 in. per in. for testing in four-point bending (Carnahan and white1). The present investigation, part of a continuing study on the very early stages of deformation, was designed to reveal the true role of a dispersed phase in promoting high strength in a commercially available dispersion-strengthened alloy. Although this technique has been used for some time to study microdeformation in pure metals and alloys, it has just recently received attention as a means of investigating dispersion strengthening. Studying the very early stages of deformation in alloys which depend upon a finely dispersed inert phase for strength may prove to be a very important method for a better understanding of these materials. It is essential to obtain considerable clarification of actual dislocation movement and the kinds of deformation barriers which exist before optimum properties can be designed into this type of material with any degree of confidence. Considerable research on a variety of dispersion-strengthened materials has resulted in two different schools of thought regarding the strengthening mechanism. One faction2-4 favors the idea that the particles themselves resist the motion of dislocations. The criterion for yielding is the fracture of the dispersed second-phase particles due to an array of piled-up dislocations. Other invesfigators5-a have shown that particles are effective primarily by allowing a greater buildup of stored energy or dislocation density through thermal-mechanical treatments in the composite than the pure matrix material. The particles themselves, then, are not exclusive obstacles, but the complex network of particles, dislocation tangles, subboundaries, and grain boundaries are strength determining. The development of such a complex dislocation network in SAP has been studied recently in some detail by Goodrich and Ansell. The ability of dispersion-strengthened alloys to resist softening or recrystallization is also of considerable importance; however, the criteria for maximum stability may not necessarily be those for maximum strength. In this study, in addition to the evaluation of the microstrain properties of TD-Nickel, it is felt that considerable clarification of the true dependence of strength and stability on the dispersed phase is shown. I) MATERIAL AND PROCEDURE TD-Nickel is a dispersion-strengthened alloy developed by the E. I. DuPont de Nemours Co., which contains 2 vol pct thoria (Tho2) in a pure-nickel matrix. The average ThO2 particle size is approximately 0.1 p and the interparticle spacing is less than 1 u. The material was supplied by DuPont in two conditions: hot-extruded bar stock, and stress-relieved cold-rolled sheet 0.025 in. in thickness. The bar was extruded at 2200°F from a cold-pressed and sintered billet. The sheet stock was prepared from the extruded material by a process involving ten or more 50-pct cold reductions by rolling with intermediate anneals at 1800° to 2000°F. Test specimens used in this study were prepared in the form of rectangular parallelepipeds measuring 0.375 by 1.375 in. in thicknesses ranging from 0.025 to 0.040 in. Samples prepared from sheet and extruded stock were mechanically polished before heat treatment and were handled with extreme

Jan 1, 1964

By John F. Lundeberg

CLAUSS1 observed that if isothermal creep data could be approximated as straight lines on a log stress-log time plot, a relationship existed that could be expressed as log t = m log s + b [ l] where t = time,

Jan 1, 1965

By N. A. Tiner, Saara Asunmaa

The early stages of nucleation of vacuunz-deposited gold coatings on electropolished surfaces of pure nickel and binary alloys of Ni-A1 and Ni-Ti have been studied, employing carefully controlled temperature and vacuum conditions. The preferential nucleation of gold on slip-plane edges on the crystal surfaces gave rise to a very pronounced decoration effect which was used in studying the morphology of the pain boundaries, etch pits, and slip planes on crystal faces. Characteristic surface patterns were observed with local dimensional variations. Most pronounced geometric patterns were ohserved in the pain boundaries of nickel and on the crystal faces of Ni-A1 alloy. The nucleation behauior of gold indicates contamination on the Ni-T1 alloy and the getter properties of titanium are presented as a tentative interpretation for the detected contamination. The markings and imperfections on cleavage surfaces of crystals have long been observed by optical microscopy.1,2 Surface-replica techniques are also used to detect the smallest steps and structural details on crystal surfaces by electron microscopy. Recently, Bassett3-5 and Sella, Conjeaud, and Trillat 6 have shown that, when gold is deposited onto a rocksalt cleavage surface, there is preferential nucleation at steps and slip-plane edges on the crystal surface. This gives rise to a very pronounced decoration effect which is invaluable for revealing the lattice steps on a cleavage surface. According to Bassett,3 gold atoms arriving during vacuum evaporation at the crystal surface have a certain mobility on the surface after arrival, particularly at elevated temperature. If a significant

Jan 1, 1964

By D. Kuhlmann-Wilsdorf

A new theory of work hardening is developed which rests on only a few simple principles and is applicable to a wide variety of materials and dislocation structures. It explains, qualitatively, the general characteristics of the three-stage shear stress-shear strain curve of fcc metals, as well as the most important features connected with easy glide. The value of, the work-hardening coefficient in stage 11, is derived quantitatively, from first principles, and is shown to be insensitive to many changes in detailed dislocation behavior. The low rate at which energy is stored during mechanical working in stage 11, the dependence of slip line length on stress, and the so-called Cottrell-Stokes law are explained. Although the theory is primarily developed for fcc metals and alloys, it is largely applicable also to some other materiuls, and in particular apparently to poly crystalline simple steels in theh linear range of hardening. FOR pure fcc metals and alloys, after many different pretreatments and under a great variety of testing conditions, the well-known three-stage work-hardening curve is commonly observed. Moreover, the work-hardening coefficient in stage 11, 011, bears an almost constant relationship to G, the modulus of rigidity, such that K = G/Brr" = 300, within a factor of about 2 either way. The very fact that the three-stage curve and the value of K are so very persistent, can hardly be understood except on the assumption that some quite simple phenomena are responsible. In this light all available theories of work hardening must be judged unsatisfactory: Each of them is based on some quite specific dislocation model, while it is known that metals with similar values of K may have widely different dislocation structures, for example, dislocation tangles in the case of pure fcc metals, and piled-up groups of dislocations in a-brasstype alloys. Thus, while a particular theory might conceivably represent a special case with a reasonable degree of accuracy, it cannot possibly have illuminated the underlying principle. Another severe criticism applying to the presently most widely discussed theories is that they employ empirical or even quite unexplained parameters in order to arrive at a numerical value of K. This indicates that some vital aspect of the work-hardening process has remained unexplained. In the present paper, a new theory of work-hardening is developed which does not suffer from the above shortcomings. It is derived from first principles, and is founded on the realization that the underlying causes for the three-stage work-harden- ing curve and for the persistence of the numerical value of O,, must be few and simple. As a first step it is shown herein that the experimental oklservations on "easy glide" can be explained on the assumption that in this stage dislocations multiply, beginning in a number of restricted area:;, and from there penetrate into crystal regions still substantially free of glide dislocations until a quasi-uniform dislocation distribution has been established. During "easy glide", the resistance to the movement of the foremost dislocations, advancing into still largely a dislocation-free regions, is believed to control the flow stress. This resistance is determined by various factors, among them the reaction of the dislocations against bowing-out into loops, which is due to their line tension. Without such bowing-out no dislocation multiplication would occur, but the corresponding contribution to the flow stress stays practically constant all through stage I. According to the present theory, stage TI begins as soon as there are no more areas left into which newly formed dislocations have not yet penetrated, i.e., as soon :is a quasi-uniform dislocation density has been attaned. Regardless of how, in detail, the dislocations should happen to be arranged at the end of "easy glide", whether in pileups or tangles, on one glide system or on several, the stress necessary to overcome the line tension of the segments must now increase, because the dislocation density increiises while the average free dislocation length decreases. It is argued that all other contributions to the flow stress stay at about the same level as in stage I, and that the said increase in the stress necessary to bow out dislocation segments into loops is responsible for the major part of work hardening in stage 11. Stage TII of the stress-strain curve is explained by largely follouing the ideas of Seeger and his co-workers; however, it is pointed out that the start of stage m may on occasion indicate the onset of "conservative climb" instead of cross slip. Indirect evidence indicates that linear work hardening persists even under the profuse action of cross slip, but at a lower rate. Only when, in addition to cross slip, climb operates extensively, does the work-hardening rat,. drop sharply, ultimately down to zero. BRIEF SURVEY OF EXPERIMENTAL EVIDENCE The stress-strain curve of crystals of many different substances are qualitatively similar. No significant permanent plastic deformation takes place below the so-called "critical resolved shear stress". As the applied stress is raised beyond this level. yielding occurs with little or no work hardening and

Jan 1, 1962

By H. H. Hausner, H. S. Kalish

IN recent years zirconium and beryllium have become of great interest because of their special properties. Zirconium is known for its remarkable ability to absorb the gases oxygen, nitrogen and hydrogen, has extensive use as a getter in electron tubes and has indeed become the primary metal in the manufacture of photoflash bulbs. Beryllium is of interest because it is light metal and as such could supplement aluminum and magnesium in light metal applications. The late development of zirconium ductile at room temperature produced by both the iodide and calcium reduction methods has stimulated frequent articles on this metal in the recent literature. Beryllium is so closely akin to zirconium crystall-ographically that some investigators are of the opinion that beryllium should be ductile at room temperature if it were pure enough. The crystallographic relationship of beryllium and zirconium, the interest created in Be-Zr alloys where the zirconium is believed to function as a remover of solid solution gas in beryllium and thus increase the ductility of the beryllium rich alloy, and the amenability of these metals to powder metallurgy methods stimulated this approach to an investigation of the system Be-Zr. Preliminary work showed that a zirconium compact melted when pressed in contact with a beryllium compact and sintered at 1250°C, without any apparent final bond between the two. A search of the literature revealed nothing pertinent about the Zr-Be system or about any zirconium - beryllium alloys. In 1936 Misch³ vaguely identified the compound ZrBe2 and reported that it has a deformed cubic structure. Two patents," , were issued to Mach-lett Laboratories in 1943 and in 1946 regarding the addition of small amounts of zirconium to beryllium in order to improve the ductility of beryllium so that it may better be used for X ray windows. In considering the alloy formation of beryllium with other metals Raynor thought it unlikely that zirconium would have any solid solubility in beryllium. From this indefinite information nothing could be ascertained about the possible use of Zr-Be alloys or the use of these metals intimately. A brief preliminary study of the system Zr-Be by powder metallurgy methods was undertaken to provide regions for more intense studies of Zr-Be alloys and as a guide to a formal phase diagram determination. The investigation described in the following pages was completed in less than three weeks. The usefulness of this rapid method to facilitate phase diagram studies and new alloy investigations will be shown. Materials and Procedure Zirconium powder was produced from crystal bar stock of high purity supplied by Foote Mineral Co. The crystal bar was converted to hydride at 730°C, crushed, and the hydride decomposed in purified argon at 850°C. 60 pct of the powder passed through a 325 mesh screen, 40 pct of the powder was —140 mesh, +325 mesh and the average particle size of the total was 8 to 12 microns. The beryllium powder was used as re-

Jan 1, 1951

By N. Brown

From the theories of flow and fracture it is shown that the difference in reciprocals of the transition temperatures (OK) is a quantitative measure of temper ernbrittlement. Experimental data are given which support this conclusion. STUDIES of temper embrittlement have been made with various viewpoints; some involved a study of the kinetics of the reaction,',2'" others were concerned with changes in the mechanical properties," . and still others investigated the structural differences between the embrittled and unembrittled states by means of the microscope," -ray ,' measurements of electrode potential," and electrical resistivity." In all these studies, the difference in impact properties was the criterion for distinguishing between the embrittled and unembrittled states. By common agreement the difference in transition temperatures is now taken as a measure of the degree of embrittlement, and this measure is used as the quantitative measure upon which studies of the phenomenon are based. Vidal and Jolivet"' suggested that the degree of embrittlement was the same whether measured by impact or by a slow bend test. Their conclusion was based on tests at constant temperature. Jaffe and Buffum" using the impact and slow bend test showed that, for a given degree of embrittlement, the difference in transition temperatures varied with the method of testing. Hultgren and Chang" showed that the difference in transition temperature produced by the V-notched Charpy impact test was not the same as the value produced by the keyhole-notched impact test. This is a very fundamental point because there can be no true measure of temper embrittlement unless it is invariant with respect to the test method. Theory The purpose of this analysis is to show how the transition temperature depends on the stress distribution and the state of the material. The criterion for fracture may be stated as follws: where iF is some function of the principle stresses and F is a critical condition depending on the state of the metal. Similarly yielding occurs when Where is another function of the prin-ciple stresses and Y is a critical value depending on the state of the material. There is some controversy as to the exact form of the function f,.(u,, u,, us) but most experimental data give the following criterion:= where 8, and 6, = 21 or 0. Combinations of 6, and 8, give the various criteria such as the normal stress, the hydrostatic tension, and the maximum shear stress laws. Agreement is general that the octahedral shear stress law adequately describes the yield condition. where the bracketed factor will be called the design factor and depends on the stress distribution. Whether the metal decides to yield or fracture is given by the condition that The effect of temperature and strain rate upon Y has been studied by various investigators, It has been shown by MacGregor and Fisher" that

Jan 1, 1955

By R. E. Ogilvie, J. I. Goldstein

The a and y solubility limits in the Fe-Ni phase diagram have been redetermined at temperatures above 500°C. Both a diffusion-couple and a quench and anneal technique were used. The solubility limits were measured with an electron-probe micro-analyzer. The nickel concentration at the phase boundary is increased below 700°C and the a solid-solubility range is much larger than had been previously measured. The solubility limits are also extrapolated to 300°C. It is suggested that the solubility of nickel in a FeNi reaches a maximum in the temperature interval 400o to 500°C. THE equilibrium diagram has been of great use in the field of meteoritics, where the phase relations between kamacite (a) and taenite (?) in metallic meteorites can be described by means of the Fe-Ni diagram. The study of metallic meteorites by electron-probe microanalysis has cast some doubt on the accuracy of the presently available Fe-Ni diagrams.1, 2 Recent thermodynamic studies of the Fe-Ni system also suggest that the diagram may be in error.3 For these reasons the high-temperature (800o to 500°C) part of the diagram was redetermined. INTRODUCTION The currently accepted Fe-Ni diagram is that of Owen and Liu.4 Above 910°C, there is a region of complete solid solubility, ? (fee). Below 910°C, the a (bee) phase is stable in pure iron. The effect of increasing amounts of nickel is to stabilize the y phase. The phases that form when Fe-Ni alloys are heated or cooled bear little relation to the equilibrium diagram. If an alloy is cooled from the y state and held at a temperature within the a + y field, no evidence has been found for the occurrence of the y - a transformation.5 If the alloy is cooled to low enough temperatures the y phase breaks down into a supersaturated bee phase called a2. In fact, in alloys over 27 pet Ni the y phase is retained at room temperature.6 The a, phase has the same composition as the original y. The temperature at which a2 forms, the M, temperature, has been determined experimentally.' A state of equilibrium can be approached by cooling below M, to form a2 and then reheating the alloy into the two-phase region of the diagram. The y phase will then begin to precipitate out of the a2 phase and grow. The growth of the phase, however, is quite slow. Using the interdiffusion coefficients -Da of Goldstein et al.,8 it is estimated that it takes about 1 year to grow a 10-µ-wide region of ? at 700°C in a 5 pet Ni alloy. Owen and Liu4 used the technique just described to form the equilibrium phases. The phases present were determined by means of X-ray analysis. The accuracy of their diagram depends on the number of alloys available near the phase boundary at a given temperature. In this study two different techniques were used to determine the a/a + ? and ?/a + ? solubility limits. The inherent accuracy of both techniques was greatly improved over that used by previous investigators because the phase-boundary compositions were measured with an electron-probe microanalyzer. PROCEDURE The two methods used to determine the Fe-Ni diagram are the diffusion couple (D.C.) and the quench-and-anneal (Q.+A.) techniques. In the first method, diffusion couples whose diffusion path goes through a two-phase region of the phase diagram were used. A description of the technique used for making the diffusion couples has been described in a previous paper.' After the diffusion treatment a discontinuity in the resultant concentration vs distance profile was measured. The nickel concentrations in the a and ? phases at the interface of the discontinuity are the solubility limits of the a and ? phases in the phase diagram at the diffusion temperature. If the interface com-

Jan 1, 1965

By J. H. Brophy, A. L. Prill, H. W. Hayden

An error lzas been found in the conventional way of determining the time exponent of linear shrinkage for the solution-precipitation stage of liquid-phase sintering. Large amounts of shrinkage due to initial rearrangenzent result in erroneously low exponents and tni si dentification of the rate-controlling process. Two alternative, mathematically correct, methods of calculation are applied to existing data on Fe-Cu, WC-Co, and Tic-Ni-Mo. This results in reidentifi-cation of the rate-controlling process and somewhat better agreement with related data. In each case the solution-precipitation process is solution-controlled and not diffusion-controlled. THE liquid-phase sintering process has been the object of a considerable amount of research for many years. Linear shrinkage vs time data at various sintering temperatures have been used recently in an attempt to identify the prevailing mass-transport processes in a number of metallic and nonmetallic systems. There is an analytical error inherent in the methods previously used for handling data during the "solution-precipitation" stage of shrinkage which must be recognized before the correct rate-controlling processes can be determined. It is the purpose of this paper to show how the error has affected previous conclusions and to suggest corrections. A number of mechanisms have been proposed to explain experimental observations during sintering in the presence of a liquid phase. The earliest of these is due to Price, Smithells, and williamsl who attributed the observed growth of the solid phase to the simultaneous solution of smaller particles and growth of larger particles. From the work of Lenel et al.2,3 and Gurland and Norton4 has come the suggestion that the liquid-phase sintering process may be divided for analysis into three steps: 1) rearrangement upon formation of the liquid phase; 2) solution and reprecipitation of the solid phase in the liquid; and 3) "coalescence" or a final stage of sintering, characteristically slower than the solution-precipitation process. The sequence of steps is shown schematically in Fig. 1. Kingery5 presented a thermodynamic and kinetic analysis of the first two "stages" of the liquid-phase sintering process in which the functional dependence of lineal shrink- age on time at temperature was used to identify the rate-controlling mass-transport process. Table I summarizes the time dependences and processes considered by Kingery.5 This method of data presentation has been employed by Kingery and coworkers for Fe-CU,6 WC-Co, and a number of nonmetallic systems," and bv Whalen and Humenik for Tic-Ni-Mo and Fe-cu.8 In each of these studies, the rate-controlling step during the "solution-precipitation" stage was identified from the slope of the curve in that stage on a logarithmic plot such as Fig. 1. However, in all of the previous studies, at a certain composition, relatively large amounts of shrinkage due to rearrangement preceded the solution-precipitation stage. Under these conditions, the larger the amount of rearrangement shrinkage the

Jan 1, 1965

By E. C. van Reuth

FIFTY-three alloys have been examined in the Fe-W and Co-W alloy systems in an attempt to verify the finding of o phases in these systems as reported by Goldschmidt.' The alloys were examined metallographically and by X-ray diffraction. The 10-g specimens were made by powder metallurgy techniques. Very fine, high-purity powders were compressed in a double-acting die at 120,000 psi after hydrogen reduction. All compacts were then sintered for 200 hr at 950°C in a helium atmosphere. Metallographic investigation and X-ray diffraction proved this time to be sufficient to allow complete homogenization before the subsequent high-temperature anneal. Each specimen was then sealed into an evacuated silica capsule and annealed at 1400"or 1500 C (except two) for 25 hr. (The 60 pct Fe and 55 pct Co alloys taken to 1610"and 1680°C respectively were held at these temperatures for 1hr. However, since these structures were at equilibrium before the anneal, and in view of their resultant structures, it is assumed that they reached equilib-

Jan 1, 1960

By Wilhelm in der Schmitten

A necessary condition for a uniaxial stress distribution in compression testing is that the specimen end surfaces make full contact with the apparatus compression plates. In addition all compression surfaces must be machined perpendicularly to the loading axis. In general this condition is not sufficiently fulfilled in a simple apparatus. Therefore on application of the load the compression plate may first touch the specimen at one point only. This may cause crumbling of the specimen if the material under investigation is brittle (e.g., ionic crystals). It also precludes a precise study of the beginning of deformation as the effective cross sectional area is unknown. In addition a complex stress state is set up which renders quantitative work impossible, e.g., on dislocation density and arrangement as a function of stress. To overcome these difficulties a "self-adjusting" upper compression plate is required. A simple and reliable method of achieving this is shown in Fig. 1: A steel hemisphere is placed on the specimen. As soon as the compression plate (which no longer needs precise machining) makes contact with this hemisphere the load is uniformly distributed over the whole specimen surface, and a homogeneous uniaxial state of stress results. An advantage of the method is that the loading is always central, even when the specimen surface is not parallel to the compression plate (Fig. 1, dashed line). Therefore to a first approximation a uniaxial state of stress is maintained if the misorientation of the specimen end surface is small. Two typical stress strain curves of identically prepared sodium chloride crystals are shown in Fig. 2; curve 1 was taken without and curve II with the hemisphere under otherwise identical conditions. The improvement in the accuracy of defining the beginning of elastic and plastic deformation is clearly indicated. The writer wishes to thank the Deutsche Forschungsgemeinschaft for financial support, and Professor P. Haasen for providing facilities for this work.

Jan 1, 1962

By J. E. Hilliard, H. E. Cook

It is shown that for systems having a miscibility gap the spinodal composition (c,) in the vicinity of the critical temperature (Tc) is related to the equilibrium composition (c,) by where cc is the critical composition. This expression is exart for the limit T — Tc and is a good approximation down to (T/Tc) - 0.9. If the miscibility gap meets the composition of the pure components THE recent theoretical treatment by cahn1,2 on spinodal decomposition of solid solutions has revived interest in methods of estimating the chemical spinodal, * i.e., the locus on a binary phase By use of the appropriate expression, the spinodal can be drawn on the Phase diagram almost by inspection with an accuracy comparable to that of lengthy calculations in which a free-energy function is fitted to the phase diagram. Satisfactory agveemenf is also obtained with spinodals comPuted from experimental free-energy curves. where G is the Gibbs free energy of the homogeneous solution and c the atomic fraction of component 2, the derivative being evaluated at constant temperature (T) and pressure (P). (These subscripts will hereafter be omitted from the partial derivatives.) If experimental measurements of G as a function of c and T are available in a single-phase region above the spinodal, then these can be extrapolated to obtain a series of metastable free-energy isotherms in the two-phase region, and from these isotherms a series of spinodal compositions can be calculated. Because the value of is very sensitive to experimental errors, an elaborate analytic procedure is required for

Jan 1, 1965

By L. F. Mondolfo

An investigation of the relationship between properties of the elements and type of binary diagram formed was conducted. It was found that, for each type of equilibrium diagram, the factors for the size, valence, electronegativity, period, melting point, entropies of fusion, and sublimation calculated for each pair of elements cover a range of values. However, these factors show sufficient relationship to the equilibrium diagram so that the correlation of several of them can be used to predict the type of diagram formed, or at least limit the choice to only a few types. ThE goal of the metallurgist concerned with alloy development has always been to find a method that predicts the properties that can be obtained when a certain metal is added to another one. In most cases a qualitative predictiton of properties can be made if the equilibrium diagram is known. However, this means that for new metals the alloy development has to start with the experimental determination of the equilibrium diagrams. Because this determination is at least as complicated and time-consuming as the determination of the properties themselves, most alloy development has taken place by trial and error, and the study of the equilibrium diagrams has followed rather than preceded the creation of new alloys. Alloy structures and properties depend on the interaction between electrons and a complete knowledge of these interactions would permit prediction of structure and properties of alloys. Unfortunately direct measurement of these interactions is extremely difficult and somewhat doubtful and only properties that depend on them can be measured easily and with certainty. Study of the relationship between properties of the elements and equilibrium diagrams is not new. Besides the well known Hume-Rothery rule of the necessity of an atomic diameter fit within 15 pct for extensive miscibility in the solid, and the wide knowledge of the effect of such factors as size, electronegativity, electron-atom ratio on solid state features,"' work relating to liquid state and liquid-solid reactions can be found in the literature. Of particular interest is the work by Axon,3 who investigated the effect of size and melting point on a selected number of eutectic and monotectic dia-

Jan 1, 1962

By James F. Watson, Jack L. Christian

The austenite to martensite solid state phase transformation in the 300 series austenitic stainless steels was studied over the temperature range of 788° to -423°F. The primary variables controlling this transformation are temperature, plastic strain, and chernical composition. Consequently, temperature effects were studied by measurements at 78", -100°, -320°, ad -423°F; plastic strain was controlled by cold-rolling the alloys varying amounts between 40 and 80 pet; and chemical compositions were varied by using 301, 302, 304 ELC, and 310 stainless steel alloys which exhibit varying degrees of austenite stability. The martensite contents of various alloys were correlated with several mechanical properties including yield and ultimate tensile strength, elongation, and notched tensile strength (Kt = 6.3). The yield and tensite strengths generally increased with increasing martensite content, but ) no correlation was observed between elongation and martensite content. The notched/un-notched ratio (Kt = 6.3) at -423°F exhibited a maximun at about 65 pct martensite. Attempts to correlate austenite stability (as measured by the Ms temperature) with both martensite content, and incremental increases in martensite content resulting from tensile testing were generally unsuccessful because the variable of cold Work could not be separated. As a result, only a general correlation of these variables was obtained. A (111) pole figure of austenite in a cold-rolled 301 stainless steel mas prepared an attempt to further investigate directionality as exhibited by mechan- ical properties. Yield strength was correlated with this pole figure, but ultimate and notched tensile strengths were not. 1 HE literature contains a wide variety of references pertaining to the austenite to martensite solid state phase transformation in austenitic stainless steel, see references 1 through 18. Discussions of the crystallography and kinetics of this transformation are given in references 2, 7, 8, 'and 11, while further discussions of austenite stability and hardening mechanisms are given in references 1, 3, and 10. Two important processing variables involved in this reaction are the degree of cold work and the temperature at which cold work is performed, and the nature of these effects are outlined in references 4 and 12, and 15 and 16 respectively. The latter two references deal primarily with cold rolling conducted at subzero temperatures. The effect of chemical composition on the austenite to martensite reaction was treated in detail by Eichelman and Hull, and they determined an equation for the M, temperature of this type of steel which included the effects of nickel, chromium, carbon, nitrogen, silicon, and manganese.5 Previous studies have shown that austenitic stainless steels of AISI types 301, 302, 304ELC, 310, and 301-N exhibit mechanical properties between 78" and -423"~ that are microstructure dependent, and the dependence of this microstructure on chemistry, temperature, tensile stress, and prior deformation is in general accord with previous investigations which have measured the effects of each of these variables on structure, or more specifically, the austenite-to-martensite transformation.lg The behavior of fully stable alloys, such as ATST type 310, at cryogenic temperatures is

Jan 1, 1962

By R. E. Reed-Hill, J. L. Martin

Kinking is an important deformation phenomenon in poly crystalline a zirconium. The crjlstallo-gvaphic features of the most important form of kinking have been determined with the aid of twins formed at 77°K in grains previously kinked at high temperatures. It has been .found that the kink-band boundaries correspond to walls of edge dislocations with (1150) Burgers vectors and dislocation lines parallel to (1070). The present observations imply that basal slip is an important secondary-slip mode in polycrystalline zirconium. Previous single-crystal studies13 did not veveal this mode Other evidelzc.e for (0002)(1120) slip is also presented. ThE first studies of kinking in hexagonal metals were made by orowan,1 using single-crystal cadmium wires. He suggested that this was a new de- formation mode in metals, different from ordinary glide or twinning. Next, Hess and Barrett2 studied zinc-crystal rods in compression, and were able to offer an explanation of the phenomenon described by Orowan. They concluded that kinks required no new deformation mechanism and were a special form of deformation band that developed gradually and solely from basal glide. Similar kink bands were then observed by Washburn and parker3 on zinc crystals deformed in tension at low stresses and high temperatures. In titaniun,4 kink bands associated with {1010}<1120> prism slip have been observed in coarse-grained specimens. Magnesium5 and rhenium6 have also been observed to kink in conjunction with their basal- and {1010} prism-slip systems, respectively. Yttrium has (1010) as a predominant slip plane, but no observations of kink bands were reported.7 Since no previous investigations of kink bands in zirconium have apparently been made, this study was proposed. Its aim was to determine the crys-tallographic features of a type of kink band frequently observed in polycrystalline zirconium. EXPERIMENTAL APPARATUS All tests were performed on a type TTC Instron machine. The cross-head speed usually chosen in tension or compression was 0.02 in. per min. Ten-

Jan 1, 1964

By N. A. Tiner

A study was made of the effects of temperature, type of loading, and electric polarization on the fracturing behavior of copper and zinc coated with mercury. Copper showed an em-brittlement only in cyclic loading, whereas zinc showed an em-brittlenzent in both static and cyclic loading. The embrittle-ment of zinc in static loading was prevented by sub-zero cooling to a temperatzcre of about -70°F. The emhrittlement of both metals was sliglztly reduced by cathodic polarization of mercury. The basic processes involved in fracturing were discussed in the light of these observations. When a solid metal is in contact with certain liquid metals possessing high wetting characteristics, a weakening effect is produced, and the solid metal fractures in brittle manner at a relatively low stress. This lowering of the fracture stress generally is considered different from the stress cracking caused by a corrosive liquid environment and is attributed to the lowering of the solid-liquid interface tension at the grain boundaries.1-4 The purpose of this paper is to describe a number of observations on the special features of fracturing of copper and zinc coated with a liquid mercury film, and to analyze the basic processes involved in fracturing in the light of these observations. EXPERIMENTAL OBSERVATIONS I) Effect of Type of Loading—The evidence appears to indicate that in static loading, metals usually fracture by the initiation of microcracks in the interior preferentially at the grain boundaries or at the intersection of slip bands.&apos; In cyclic loading, cracks develop on the surface within the active slip zones, and gradually propagate with increasing num- ber of cycles.6&apos;7 Because of this difference in the manner of initiation of cracks, a series of bare and mercury coated copper and zinc specimens was subjected to static and cyclic loading, and their fracturing behavior was examined. The specimens were machined to 0.25 in. in diam and 1 in. in length from a high-purity commercial bar stock, and annealed at an appropriate temperature. Mercury was applied to the surface of the specimens by rubbing with cotton wool soaked in a saturated solution of HgCl2 or by etching with a dilute solution of HC1 and rubbing with purified mercury and by washing in water. The static tension load-extension curves were obtained by means of a Riele Screw Power Universal Testing Machine. The room-temperature load-extension curves for copper and zinc are shown in Fig. 1. The deformation behavior of copper, as judged from the general configuration of the load-extension curve, was not affected by mercury coating. The maximum load to fracture and the elongation at the maximum load were practically the same for both specimens. The mercury coated copper, however, showed somewhat less localized necking and had smaller reduction of area than the uncoated metal. The behavior of mercury coated zinc was radically different from the behavior of uncoated metal. The load-extension curves were the same at the

Jan 1, 1962

By D. S. Tomalin, D. F. Stein

The effect of reducing oxygen to low concentrations on the fracture of high-purity iron single crystals has been examined at 78° and 20°K. It is found that iron single crystals grown by the strain-anneal method usually contain a few occluded grain boundaries which may become embittled in the presence of oxygen, thereby nucleating cleavage fractures. High purity with respect to interstitial elements was found to inhibit twinning and evidence is presented for an orientation dependence of the resolved yield stress. Deformation occurred by slip rather than twinning at both temperatures of testing with elongations of as much as 9 pct at 20°K. THE fracture properties of iron single crystals have been observedl-3 to be a function of temperature, orientation, and purity. Allen, Hopkins, and McLennan1 demonstrated that at 78°K iron single crystals became increasingly brittle as the tensile axis approached the (001) pole of the stereographic unit triangle. Iron crystals with the tension axis near a (001) pole were completely brittle and orientations near the (011)-(111) boundary were very ductile, achieving a 100 pct reduction in area prior to fracture. Later work of Biggs and pratt2 and of Edmondson3 demonstrated that by reducing the carbon content of the single crystals the transition between brittle and ductile failure at 78°K could be shifted to orientations nearer the (001) pole. Ed-mondson went further and pointed out that any mechanism which tended to increase the yield strength of the iron (i.e., carbon addition, pre-strain) also increased the tendency for brittle behavior at 78°K. Thus by a reduction of carbon content Biggs and Pratt were able to obtain ductile behavior to within 20 deg of the (001) pole, and Ed-mondson was able to obtain ductile behavior to within 26 deg of the (001) pole. Edmondson&apos;s material had a total interstitial content (carbon, oxygen, and nitrogen) of approximately 60 ppm and, although Biggs and Pratt reported no analysis, indications were that their iron contained comparable impurities. Stein, Low, and seybolt4 purified iron single crystals to a total carbon, oxygen, and nitrogen content of approximately 20 ppm. They observed a lowering of the yield stress with this increased purity, and thus one might have expected an observation of increased ductility. Although they tested specimens of orientations which the previous workers had indicated should be ductile, the crystals failed at a 78°K in a brittle manner with little elongation. Stein noted,&apos; however, that about 90 pet of the failures could be traced in origin to occluded grains. Allen et al.1 and Edmondson3 do not report examination of their cleavage surfaces, but Biggs and pratt2 reported that microscopic examination of the cleavage surfaces of many of their specimens revealed the presence of small occluded grains. Honda and cohen6 and Keh7 have also observed the initiation of fracture at occluded grains in iron single crystals. Therefore, the additional complication of occluded grains must be considered in studying the properties of iron single crystals and the origin of fractures determined if the ductility exhibited by the crystals is to be considered meaningful. Various investigators8-12 have studied the effects of impurities on grain boundaries in high-purity polycrystalline iron. Rees and Hopkins10 showed that the addition of oxygen to low-carbon (0.002 pet) iron weakened the grain boundaries, causing a shift from transcrystalline to intercrystalline fracture and a progressive decrease on the brittle-fracture stress with increasing oxygen content. In addition, it has been shown by Low and Feustel11 that the addition of carbon to polycrystalline iron containing oxygen eliminated grain boundary brittleness. Thus, oxygen can embrittle grain boundaries in high-purity polycrystalline iron, but the addition of an appropriate amount of carbon can eliminate the oxygen-induced brittleness. The oxygen content (19 ppm) of the iron "single crystals" employed by Stein el al. was large enough to suspect impurity effects at the occluded grain boundaries. Allen et al.1 Biggs and pratt,2 and Edmondson3 may have masked any occluded grain problem in their specimens considering the relatively high carbon levels they employed. stein13 demonstrated that the addition of as little as 0.9 ppm C to previously purified (less than 5 x 10-3 ppm C) "single crystals" would increase the elongation from a few percent to more than 20 pet at 78°K and the fracture was not associated with grade boundary initiation.

Jan 1, 1965

By T&apos Ke, ing-sui

THE subject of recrystallization and grain growth has been much studied and the literature on this subject is numerous. Such studies have been mostly carried out by metallographic examination of X ray methods. Since recrystallization and grain growth involve elementary atomic processes, their mechanism can best be elucidated by a study of some properties which can be readily traced back in terms of such atomic processes. Prior to a detailed quantitative study, however, it is necessary to explore first the possibility and practicability of utilizing any particular property for obtaining the desired information. We have pointed out in a preceding article&apos; that the internal friction of cold-worked metals is extremely high during recrystallization and it drops abru~tlv once the recrystallization is complete. ~reviois work has also shown that the viscosity of grain boundaries in a recrystallized specimen at a given temperature is raised by grain growth.&apos; It seems thus that the measurements of internal friction may furnish a useful tool for the study of the mechanism of recrystallization and grain growth in terms of elementary atomic processes. The purpose of this paper is to report results of a study along this line. We will demonstrate that the internal friction method does give results in agreement with those furnished by conventional metallographic examinations. Once such a correlation has been established, we will be in a position to take further steps to achieve new information which cannot be achieved by conventional methods. The measurements of internal friction were made using apparatus and procedures similar to those used in the preceding article. All the measurements were made under such a small stress level that the internal friction is independent of stress level. The frequency of vibration is, unless mentioned otherwise, about one cycle per second in all cases. Internal Friction and Recrystallization Complete Recrystallization Temperature: Fig. 1 shows the internal friction curve during annealing of a few metals: aluminum, alpha brass and iron. These curves were determined in the following manner. In the curve for aluminum, internal friction measurements were performed upon. 99.991 aluminum subjected to 95 pct reduction area. The internal friction was first measured at room temperature. The specimen was then annealed at 50°C

Jan 1, 1951

By B. R. Banerjee

MATERIAL used throughout this investigation was high-purity aluminum (99.998 pct). The 1/2-in. cubes were cut out of a cold-rolled slab and annealed at 550°C for 1 hr before deformation. The single crystal specimen was 1 in. in diam x 0.33 in. thick, cut from a cylindrical crystal produced by cooling at about 55°C per hr in a furnace which had a convenient gradient of about 10°C in every 4.5 in. vertical crucible length. Specific data on the ten specimens studied are summarized in table I. Three types of deformation were employed: (I) compression in a hand-operated hydraulic press; (2) impact with a 7-lb sledge hammer; and (3) rolling, using a wedge-shaped specimen&apos; to obtain a gradient of deformations varying from 0 to 50 pct along the length of the wedge. Specimens were either deformed at room temperature, or first cooled in a freezing mixture of dry ice and ether at a temperature of —72°C and then deformed between steel blocks cooled with dry ice. The specimens deformed at the low temperature were ground and polished through 000 emery paper and wheels impregnated with alundum and alumina No. 1. During this entire procedure the specimens were dipped frequently in the freezing mixture of dry ice and ether in order to maintain constantly a frosty surface as insurance against overheating. All specimens were given a final electrolytic polish, using two different electrolytes* to insure that the surface effects observed were not char- acteristic of the polishing technique. With both electrolytes, the annealed specimens gave even surfaces with good polish. Several standard etchants were tried without success. The best results were obtained with an immersion etchant, developed in this connection, containing: hydrofluoric acid, 4 parts; nitric acid, 1 part; glycerine, 3 parts. Discussion of Results Typical strain markings have been observed within deformation bands, as shown in figs. 1, 2, and 4. By stereographic plotting of metallographic measurements, the strain markings within a deformation band in a single crystal of aluminum deformed by compression were found to be traces of (111) planes within a maximum scatter of 6". The edges of the deformation band were found to be traces of the (100) planes also within the maximum scatter of 6" (in agreement with previous workers). At 30 pct deformation, this scatter was considered quite normal because of the fragmentation and rotation of the crystal. This solution, based on the traces on one plane of observation is not unique, but as the planes were observed to be those normally and logically to be expected, further work in this regard was not felt to be necessary. The study of strain markings in a wedge-shaped specimen, rolled to obtain a gradient of deformation from 0 to 50 pct, revealed prominent strain markings at 25 pct reduction in thickness (fig.5). Faint and weak strain markings were visually observable up to a minimum reduction in thickness of about 12 pct. Since strain markings have been observed in other face-centered cubic metals after much smaller deformations;1, 2 and since the rate of recovery in aluminum is high, it is believed that, at lower deformations, self-recovery removes the localized strains at the slip interfaces, thus removing the source of the etching effects that give rise to strain markings. At high magnifications, strain markings sometimes seem to appear as very thin, light-banded re-gions bounded by a pair of dark edges. This so-

Jan 1, 1951

By W. D. Robertson, Raymond C. Boettner

A study was made of the change in density during the first (transient) and second (linear) stages of the creep curve of polycrystalline copper as a function of 1) stress, 2) temperature, 3) plastic strain, 4) impurity and atmosphere effects, and 5) structure, including single crystals. Voids were not observed in single crystals strained 15 pct at 500°C, or in a polycrystal-line aggregate produced by recrystallizing a single crystal, within the limit of sensitivity, Ae/e = 1 x 10-4. It appears that voids are heterogeneously nucleated at grain boundaries by an insoluble phase, or phases, which can be removed by directional solidification. The principal controlling mechanism of void growth appears to be condensation of vacancies at grain boundaries. Vacancies are transported to a boundary and condense as a consequence of the tensile stress component across the boundary, which depends on the orientation and configuration of the boundary plane and on boundary shear across ledges and other irregularities. The ultimate source of vacancies is the free surface and diffusional transport is by way of the boundary plane. PREVIOUS investigations have dealt with the nucle-ation of voids at grain boundaries under creep condition~&apos;-~ and with the connection between grain boundary voids and subsequent brittle fracture.5-7 Growth of voids during the creep process, particularly in the transient and linear stages of creep, has not been studied with the same intensity. Therefore, it seems pertinent to investigate the process of void growth with respect to the related creep curve, and the morphology of growing voids with respect to the structure.

Jan 1, 1962

By J. W. Pugh, J. D. Nisbet

THIS study of the ternary has been made as one phase of a metallurgical investigation which began nearly four years ago in the General Electric Company&apos;s Research Laboratory in Schenectady, N. Y. The objective of this program is the discovery of new metallurgical information which will lead to the development of better high-temperature materials. Combinations of the four pure base elements—iron, chromium, nickel, and cobalt—are being studied at the present time. It is essential in an investigation such as this to know as much as possible about the constitutional diagrams involved. The study of the iron-chromium-nickel system has been made to this end. Preliminary Explanation of Experimental Procedure: In all, fifty-five alloys at steps of 10 at. pct were made for the investigation of this ternary. Several ternary alloys in the chromium rich corner had to be omitted because their extreme brittleness made testing impractical. All alloys were vacuum melted with hydrogen reduction and centrifugally cast. The apparatus and technique of this process has been described in detail by Nisbet.1,2 The purity of the alloys prepared in this way is considered to be quite good. Impurities are listed as follows: Pct Carbon.............................0.02 Oxygen................................0.02 Nitrogen.........................0.005 Magnesium..................0.03-0.05 Sulphur...........................trace Hydrogen....................trace Phosphorous..................trace Silicon........................ trace After casting, all samples were given a homo-genization treatment which consisted of holding them for 15 hr at 1150°C (2100°F) and water quenching. Testing was begun with the samples in this condition. The tests employed in the study of this system were (1) dilatometer, (2) hardness versus aging temperature, (3) tensile strength and elongation versus temperature, (4) microstructure analysis, and (5) electrical resistance versus temperature. Dilatometer tests were made at the rather rapid heating rate of 1093°C (2000°F) in one hour on a Bristol-Rockwell type instrument. Hardness data were taken on specimens cooled from 204", 427", 649°, 760°, 871°, 982°, and 1093°C under conditions which are thought sufficient to bring the specimens to equilibrium in all but the cases of the very sluggish transformations. Electrical resistance data for several specimens were taken for both heating and cooling conditions in a vacuum furnace especially designed for this work by D. W. Bainbridge, formerly of this laboratory. Provisions were made for heating and cooling standard specimens at a constant rate, while autographic records of resistance and temperature were made simultaneously. Micrographs of all the alloys were made in the quenched condition. Some question may exist as to how such physical values as hardness, tensile strength, and elongation were interpreted to indicate a change in phase. Original data were recorded on physical property versus temperature graphs, each of which was made from the data of a single alloy (fig. la). From these, another series of graphs were plotted with the physical property as a function of composition for constant temperatures (fig. 1b). Sharp deviations in the slope of these composition versus hardness curves often indicate a change in phase. The example of fig. 1 will serve to describe this experimental technique. The plotting of a single point from graph "a" to graph "b," and finally to the phase diagram "c," is illustrated. The location of the point on graph "b" is indicated as point (1). If all the alloys of the A-B binary system were solid solutions at temperature X, the hardness in this curve would be expected to rise at a fairly even rate as A is diluted with B to a maximum at some intermediate value between A and B, as

Jan 1, 1951