By Florian Kongoli

Non-ferrous smelting slags .can contain magnesia, which substantially increases the liquidus temperature. One option to counter this increase is to flux with calcia. In this work, experimental liquidus measurements including new measurements on industrial slags have been compared with a FACT-based thermodynamic model, which predicts the liquidus surface of multi-component iron silicate smelting slags containing both magnesia and calcia. The predictions, which agree well with experimental results, are summarized in both isothermal and non-isothermal diagrams to give a quantitative description of the liquidus surface.

Jan 1, 1998

By Neng-Wen Yu, Shau-Jun Zhu, Ji-He Wei

The desulfurization process by powder injection and blowing in the RH refining of molten steel and its mechanism have been considered and analyzed. Based on the two-resistance mass transfer theory and the mass balance of sulfur in the system, a kinetic model for the process has been developed. The related parameters of the model, including the mass transfer coefficients and the effective amount of powder in the molten steel being treated for desulfurization, have been more reasonably determined. Modeling and predictions of the process of injecting and blowing the lime-based powder flux under assumed operating modes with the different initial contents of sulfur and amounts of powder injected and blown in a RH degasser of 300 t capacity have been carried out using the model. The relevant circulation rate of the liquid steel and the powder injection and blowing rate were taken to be 100 t/min and 150 kg/min, respectively. The initial contents of sulfur in the liquid steel to be treated and the amounts of powder injection and blowing were respectively assumed to be 0.007, 0.006, 0.005, 0.004, 0.003, 0.002 mass-% and 10, 8, 6, 5, 4, 3 kg/t-steel. The total treatment time for desulfurization under each mode was set up at 24 min, equivalent to eight circulation cycles of the liquid steel to be treated. The results indicated that the predictions made with this model are in good agreement with some data of the industrial experiments and practice. Injecting and blowing the lime-based powder flux with the composition of 85 mass-% lime (CaO) + 15 mass-% fluorspar (CaF2) of 3-5 kg/t-steel, it is possible to decrease the sulfur content in the molten steel to ultralow level below (5-10)x10·4 mass-% from (60-80)x 10·4 mass-%. The total treatment time needed will appropriately be 12-20 min. Intensifying the powder injection and blowing operation and increasing the circulation rate of the liquid steel may effectively' raise the rate of the process in RH refining. The model may be expected to offer some useful information and a reliable basis for determining the reasonable process parameters and help in optimizing the technology of desulfurization by powder injection and blowing in the RH refining of molten steel.

Jan 1, 2000

By F. Elgersma

A high purity electrolysis solution is essential for hydrometallurgical zinc winning processes. For this reason ferric iron containing compounds such as jarosite are precipitated as iron and impurity collector during the calcine leaching. Jarosite thus forms a chemical waste and creates environmental problems. This research contributes to the development of a wet jarosite treatment process, where less contaminated jarosite is produced which can act as an iron source. The present work studies jarosite precipitation kinetics and the uptake of zinc cations in batch and continuous experiments. The distribution coefficient for zinc in continuous experiments is constant for a wide ratio of zinc over ferric ions in the solution. Addition of NH, + ions in batch experiments accelerates the conversion rate equivalent to the driving force increment. Addition of 50,2-ions above the stoichiometric ratio increases the conversion rate less then could be expected from the increase in the estimated driving force. Zinc ions tend to retard the conversion rate. An increasing reaction temperature increases the conversion rate. Below 75 ?C the conversion rate approximates zero.

Jan 1, 1990

By Kuniaki Murase

Cadmium telluride (CdTe) semiconductor has been well investigated as a CdS/CdTe heterojunction solar cell material since its band gap is suitable for energy conversion from sunlight into electricity. In this paper a new electrochemical processing of thin-layered CdTe using basic aqueous electrolytes is reviewed from the standpoint of thermodynamics using a potential-pH diagram. The cathodic electrodeposition of the stoichiometric CdTe with a flat surface morphology took place at more positive potentials than that of the Nernst potential for the bulk-Cd deposition and at more negative potentials than that for the hulk-To. In this potential region deviation from the stoichiometric composition of eleetrodeposited CdTe was controllable by the Cd(II)/Te(IV) concentration ratio, pH, or concentration of complexing agent for Cd2+ ions of the electrolytes, The deposition behaviors for ammoniacal media were well accounted for by the potential-pH diagram of the Cd-Te-NH3-H2O system devised by a combination of those of the Cd-NH3-H20 and the Te-H2O systems, Diagrams for other complexing agents, ethylenediamine and diethylenetriamine, were also constructed to investigate and discuss the electrodeposition conditions regarding the corresponding media.

Jan 1, 2003

By F. H. (Sam) Froes, C. Suryanarayana, K. C. Russell, C. M. Ward-Close

"Far from equilibrium synthesis allows development of novel crystal structures and microstructures, leading to achievement of enhanced physical and mechanical properties. A number of ""far from equilibrium"" techniques are reviewed with emphasis on the amount of departure from equilibrium. The ability of two such techniques, mechanical alloying (MAl, and physical vapor deposition (PVD) to develop novel structures are discussed in detail. For the MA process emphasis is placed on intermetallic compound compositions. Solubility extension, beyond rapid solidification (RS) levels, is found in terminal compositions but not for the intermetallics. Nanostructure-sized grains (< 100nm) form which can be retained after ""low temperature"" compaction. On continued milling in many cases the nanometer-sized grains transform to an amorphous structure. Ordering is destroyed by MA, except in those intermetallics with large negative enthalpies of formation. For the PVD process, a review of application to terminal light alloy compositions is presented. This includes a new high-temperature aluminum alloy, layered materials with nanometer spacing, corrosion-resistant magnesium alloys and low-density titanium compositions. IntroductionTo enhance the mechanical property combinations of advanced structural materials innovations in process/synthesis are required [1-6]. In this paper the capability of various ""far from equilibrium"" synthesis techniques [7,8] to produce novel constitutional and microstructural effects, and hence potentially enhanced physical and mechanical properties, in advanced materials is presented. The application of two such methods, mechanical alloying (MA) and physical vapor deposition (PVD) is discussed in detail. For the MA process emphasis is on intermetallic compositions with consideration given to solid solubility extension, microstructural refinement, amorphization, and formation of intermetallic compounds. For the PVD process application to terminal light alloy compositions is discussed."

Jan 1, 1994

By D. C. Azubike

Wolframite (FeWO4) usually having cassiterite (SnO2) as a major impurity is a primary source of tungsten. Its direct reduction/carburisation with carbon in the temperature range 1000-1400°C, and with hydrogen at 600-900°C followed by carburisation with CO at 900°C are described. Depending on the conditions and reactants employed, Fe, Fe2W, B-Sn,WC, W2C, Fe3W3C and Fe6W6C are the products. Tin was found to inhibit the overall reduction and carburisation reactions significantly. The potential for either efficient separation of iron and tungsten or a one-stage production of an iron-based metal carbide composite is discussed.

Jan 1, 1992

By Li. Jiarong, Zuojian Liang, Qingyan Xu, Baicheng Liu, Shizhong Liu, Hailong Yuan

Single crystal solidification of turbine blades is a key technology for the production of reliable and high efficiency gas turbines. The solidification process of single crystal investment castings causes a number of problems that have to be solved such as the increase of casting defects and complexity of production process. Computer modeling and simulation is helpful to predict the defects and improve the process design. In the paper, a mathematical model for three dimensional simulation of solidification and single crystal growth of investment castings was developed based on CA, mechanism of crystal growth and basic transfer equations such as heat, mass transfer equations. Many factors including constitutional undercooling, curvature undercooling and anisotropy, which had vital influences on microstructure evolution, were considered in the model. Temperature, crystal growth interface and structure defects of investment castings of single crystal superalloy were investigated at withdrawal rates of 4.5mm/min and 7mm/min. Simulated results showed that microstructure evolution and structure defects were predicted reasonably and calculated results were coincident with experimental ones. The study indicated that three dimensional solidification simulation technique is a powerful tool for understanding the fundamental of solidification and the formation of structure defects in single crystal investment castings and finally for optimizing process design.

Jan 1, 2004

By Jenq-Gong Duh, Jyh-Wei Lee

"Hard chromizing process is a method for developing a surface modified coating providing wear, corrosion resistance and high temperature surface protection. Two carbon steels with 0.45 wt% and 0.95 wt% carbon contents, respectively, were chromized with pack cementation process at 950'C for 4 and 9 hours, respectively. The phase transformation and microstructure phenomena of chromized coating layer and matrix of two steels were studied with X-ray diffractometer and electron probe microanalyzer. (Cr,Fe)23C6 and (Cr,Fe)7C3 carbides and (Cr,Fe)2N1-x nitride phases were observed on the chromized surfaces. The thickness of chromized layers obeyed the parabolic rate law. The mechanism and diffusional kinetics of the chromizing process were proposed. The diffusivity of chromium in the (Cr,Fe)7C3 carbide phase was calculated using the moving boundary method.IntroductionChromizing process is one of the surface treatment technologies that can produce a chromium contained surface layer with sufficient corrosion and wear resistance on the steel matrix [1-7]. The relatively low cost and no ""line-of-sight"" restrictions are main advantages of chromizing. Adequate bonding strength of these coatings to the substrate was reported [7]. Chromizing process can be classified into soft chromizing and hard chromizing [2]. Soft chromizing is applied to steels containing less than 0.1wt% carbon through which chromium will be diffused. High temperature oxidation resistance improvement is the main purpose of soft chromizing process. On the contrary, the hard chromizing can be applied to steel containing more than 0.3wt% carbon, and very hard chromium nitride and carbide layers will be formed on the surface, which are very resistant to wear, corrosion and temperature [5-7]. In the previous studies on the Fe-Mn-Al-Cr alloy [5,7] and carbon steels [6], the thickness (X) of chromizing layers was analyzed and found the parabolic rate Jaw prevailed:"

Jan 1, 2004

By K. Kalgraf

The motion and stability of the metal/electrolyte interface is determined by Navier-Stokes equation. The equation may be decomposed into two independent equations by taking the divergence and curl of Navier-Stokes equation. The divergence determines the motion and stability of magneto-gravitational waves. The curl of Navier-Stokes equation gives an equation containing only velocity and magnetic field, and states that the magnetic field is driving a circulation pattern in the cell, and this magneto-flow has its own stability conditions. The waves are called Alfven waves, and their stability properties are related only to magnetic field and geometry.

Jan 1, 2001

"Hematite pellets were electro-deoxidized to iron in molten sodium hydroxide to produce iron containing about 10-wt % oxygen. The anodic reaction was the evolution of oxygen on an inert nickel anode. Before the electrochemical reaction, there is a reaction between sodium hydroxide and ferric oxide to form sodium ferrite and, in order to compensate for the reduction in sodium oxide content, 1 wt % sodium oxide is added to the melt. In a laboratory cell, the cell voltage was 1.7 V with a current density of 5000 A m-2, a current efficiency of 90% and an energy consumption of 2.8 kWh kg-1.Introduction The iron and steel industry contributes about 2.3 bn tonnes/annum of the carbon dioxide to the atmosphere, which is about 10% of the total, and some believe that, in order to prevent a catastrophic rise in the earth’s temperature, carbon dioxide emissions must be reduced by 50% come 2050. However, by 2050, it is likely that the iron and steel industry would have grown significantly so that the production may have risen to 2 or 3 bn tonnes/year so in order to meet the 50 % reduction on today’s figure, the carbon dioxide may have to be reduced to 25% or less, which is a very demanding requirement. There are probably three ways of reducing the carbon dioxide output:1. By capture and sequestration, but this may be technically very demanding.2. Reduction using hydrogen in place of carbon."

Jan 1, 2009

By Richard D. Hagni

Microscopic examination of selected, representative, unweathered samples of Birmingham, Alabama, Silurian, sedimentary iron ores has fully revealed the nature of the phosphorous-bearing mineral grains. The grains are composed of carbonate-fluorapatite (collophane), range in size from 1 um to 2.25 mm, and exhibit varied types of intergrowth with hematite. Modal analyses conducted under cathodolumi-nescence have provided quantitative data on the a3undance of each of 15 types of phosphorous-bearing mineral grains and made it possible to assess the potential phosphorous liberation from four types of iron ore. The results indicate that 27% of the total phosphorous contained in the iron ores in the western part of the Birmingham district can be expected to be liberated by fine grinding; 60% for ores in the eastern part of the district.

Jan 1, 1982

By Gus Van Weert

Solvent extraction of iron from zinc refinery liquors has been investigated before, mainly on the MEHPA / HC1 stripping combination. Leakage of chloride into the zinc electrolyte and the costs of handling the ferric chloride eluate have prevented this option from being adopted. This work explores the stripping of the ferric loaded organic phase with nitric acid to take advantage of the possibility of regenerating up to 6N nitric acid, and clean spheroidal hematite production by autoclave treatment of ferric nitrate solution. The work was carried out with DEHPA (di 2-ethyl-hexyl phosphoric acid) in kerosine. Degradation testing proved the DEHPA to be very stable, when exposed to nitric acid solutions up to 6N and temperatures up to 70" C over a period of five days. Ferric iron was removed completely froma synthetic hot acid leach liquor, irrespective of the DEHPA concentration. Stripping the ferric turned out to be the problematic step. Although the stripping efficiency was considerable better at 50 than at 20° C, it decreased with increasing DEHPA/Fe ration in the organic phase. Eluates of no more than 5-10 g/l ferric nitrate were produced. surprisingly, nitric acid was found to be a less efficient stripping agent than sulphuric at equivalent normality and its efficacy levelled off above 4N. It was concluded that DEHPA does not appear to be the S.X. reagent to take advantage of the low cost autoclave decomposition of ferric nitrate opportunity in zinc hydrometallurgy and that another S.X. reagent, also resistant to nitric acid, but based on weaker compound formation is needed.

Jan 1, 1998

By A. S. Rao

In the original roast-leach-electrowin (RLE) circuit at the Chambishi Cobalt Plant, commissioned in 1978, the separation of nickel and zinc from cobalt in aqueous streams was achieved by successive stages of precipitation using lime. However, this technique was not able to meet the increasingly stringent metal quality requirements of customers whilst maintaining acceptable process recoveries. Intensive process development work was carried out and, in July 1988, an ion exchange circuit for nickel removal was commissioned using DOW XFS 4195 resin and for the first time Z.C.C.M. produced high purity cobalt metal containing less than 0.10% nickel. Following further work, a solvent extraction circuit for zinc removal, using DZEHPA, was commissioned in February 1991 in order to enhance cobalt recovery by reducing co-precipitated cobalt losses. This paper outlines the process development, design, commissioning and subsequent operation of these nickel ion exchange and zinc solvent extraction circuits.

Jan 1, 1993

By Muammer Kaya, Sait Kursunoglu

"The aim of this study was to investigate the effectiveness of ascorbic (C6H8O6) / oxalic (C2H2O4) acid as a reductant for the simultaneous recovery of zinc and manganese from a spent and mixed zinc-carbon and alkaline battery powder in sulphuric acid leaching. The effects of sulfuric acid concentration, ascorbic/oxalic acid dosages, reaction temperature and leaching time on the zinc and manganese dissolutions were investigated according to 2k full factorial experimental design; then, a simple optimization study was carried out for the best reductant. The optimum reductive acid leaching conditions were determined at 3 hours leaching time, 70°C leaching temperature, 0.5M sulfuric acid concentration, 13 g/L ascorbic acid dosage, 1/20 g/mL solid/liquid ratio and 200 rpm stirring speed. Under these conditions, the dissolution efficiencies were 99.9% for Zn and 99.3% for Mn. When our results were compared with the previous results, our findings were better than previous studies.In addition, the manganese dissolution kinetics was undertaken, and the activation energy was found to be 7.04 kJ/mol. Selective precipitations of Zn and Mn from acid solutions were carried out using NaOH and KOH. Using 3M NaOH as precipitating agent at room temperature and at pH 8; 95.4% of Zn and at pH 10; 93.7% of Mn were precipitated from the leaching solution. Under the same conditions, using 3 M KOH at pH 8; 91.6% of Zn and at pH 10, 96.4% of Mn were precipitated. Based on the experimental results obtained, an appropriate flow sheet was proposed to recover zinc and manganese."

Jan 1, 2012

By Nagahiro Saito, Takashi Nishimura, Takamichi Ichikawa, Akio Fuwa

"Yttria-stabilized zircohia (YSZ) has high potential to be used as solid-oxide fuel cell (SOFC) electrolyte. However, the high efficiency of SOFC has not been yet achieved due to the high internal resistance of bulk electrolyte. The resistance becomes lower with the decrease in the electrolyte thickness. Thus, the decrease in electrolyte thickness leads to lower internal resistance. . The aim of this study is as follows: (a) to prepare the thin films of YSZ by inductively-coupled RF plasma-enhanced metal organic chemical vapor deposition (PEMOCVD) process using Zr(t-OC4H9)4,Y(DPMh and oxygeil, and (b) to reveal the relationship between the structural characterizations and the process parameters.1. IntroductionYttia-stabilized zirconia (YSZ) has, been widely used as not only heat-resistant materials but also the components in automotive oxygen sensors, electrolytes of solid-oxide fuel cell (SOFC)(1)(2) and the buffer layers for the high-temperature superconductor because of its low thermal conductivity, good mechanical properties and high ionic conductivity. However, it is said that the internal resistance of the bulk electrolyte is too high to be appropriate as a solid electrolyte for high-efficient SOFC. The authors believe that the thin YSZ electrolyte can give a high performance to characteristics SOFC, since the internal resistance becomes lower with the decrease of electrolyte thickness. Thus the process technology to prepare YSZ thin films is desirable and must be established.In recent years, the YSZ thin films have been reported by chemical vapor deposition (CVD), thermal CVD using metal chlorides (MC) of ZrCl4 and YC(3)(4), thermal CVD using metal organic compounds (MO)(5)(10) Zr(t-OC4H9)4 and Y(C11H19O2)(11) and plasma-enhanced (PE) CVD using MO. Here, these methods are called MCCVD, MOCVD and PEMOCVD. MCCVD has two disadvantages; a large quantity of chlorinated impurities in deposited films and high processing temperature (> 1273K). This high processing temperature leads to damage of substrates in particular, so the application of this technology is limited. On the other hands, the processing temperature by MOCVD becomes and is lower. Unfortunately, the accurate vapor pressures of these metal organic compounds have not been, known so: that it is difficult to control the composition and the film thickness by MOCVD method well. Moreover, the large amount of carbonic compounds in the films prepared by MOCVD method is produced. However, plasma-effect has been reported to decrease large amount of the carbonic impurities by PEMOCVD. However, PEMOCVD has many reaction parameters in plasma processing; the geometry of experimental apparatus, radio frequency, electronic power input and so on. Thus, the general understanding about the relationship among reaction parameters, the composition and crystal structure of thin deposit film by this method has not yet been established."

Jan 1, 2000

By M. Suzuki, M. Dobashi, M. Kahata, T. Yoshida

Almost 30% of steel in Japan is produced by electric arc furnace (EAF) treatment of iron scrap. EAF dust includes approximately 20 wt % of Zn and 3- 5 wt % of CI and is treated by the pyrometallurgical processes to recover Zn as Zn oxide. Direct hydrometallurgical processing is one of the most effective methods to recover high purity Zn. In this case, CI in the EAF dust is dissolved in the liquid phase by leaching, and the CI anion in electrolyte attacks anodes which are commonly made of a lead base alloy. Several processes have been proposed to remove CI anions from acidic sulfate solution. In this study, an electrolytic process was examined to eliminate CI anions from Zn sulfate electrolyte. From our study it can be said that the elimination rate of CI anion depends on the anode material ( i.e., the elimination rate is Pb-Ag alloy == Pb > DSE== Pt). In industrial Zn electrowinning process, the electrolyte contains Mn, which means the influence of Mn should be considered in the elimination of Cl. Mn dioxide deposition on an anode plate reduces the efficiency of CI removal. A periodical reverse current electrolytic system was examined to prevent this efficiency decrease, and deposited Mn dioxide could be removed very rapidly when the current is reversed. More than 95% of CI anion could be removed by this method in a shorter period than direct current method.

Jan 1, 1997

By Nieves Iglesias

The removal of the refractoriness of a gold bearing pyrite- arsenopyrite ore is studied. Flotation concentrates were prepared and leached with a dilute acidic ferric sulfate solution. The elemental sulfur film which forms on arsenopyrite in the oxidation process is not responsible for the low rate of the arsenic dissolution observed. A positive effect on the leaching rate is observed when Ag&apos; is added. This pretreatment eliminates the refractory nature of concentrates.

Jan 1, 1993

By Kimio Itagaki

The distribution behaviours of the VA elements between the gas, slag and matte phases in copper smelting were evaluated on the basis of the thermodynamic data, most of which were determined by the authors. The distribution is basically dependent on the process factors such as temperature, the content of the element in charge, the amount of the waste gas and degree of vapour saturation with the elements. The thermodynamic quantities such as the activity coefficients of the VA elements in matte, the activities of iron and copper, SO2 or 02 potential and the distribution ratio of the elements between the slag and matte phases seriously affect the distribution, and the behaviours in various smelters could be explained systematically and reasonably by considering the changes in these quantities, In oxidation smelting at PSO2= 0.1 to 1 atm, the proportion of arsenic and bismuth in gas is predomi22t for the arsenic and bismuth distributions in both smelting and converting stages. The degree of vapour saturation has serious effect on the distribution, and sufficient contact between gas and matte phases is desirable for transferring arsenic and bismuth into gas phase.The elimination of antimony by means of vaporization is not significant. In reduction smelting at po2 = 10-11 atm, the proportions of arsenic and antimony in the gas phase are quite small, but the proportion of bismuth does not change significantly.

Jan 1, 1983

By S. M. I Kytö, J .. K. Mäkinen, K. Saarhelo

"At the Outokumpu Oy Harjavalta Copper Smelter the control philosophy of the flash smelting process has been changed from the slow feed-back control to feed-forward control. This is important as the fluctuations in the flash smelting furnace matte grade and slag temperature are desired to be minimized.The system is based on a specially designed automatic sampling device and the Outokumpu Courier 20 on-stream X-ray fluorescence analyzer. A microcomputer-based Analyzer Operator Station (AOP) controls the system and calculates the process parameters for the furnace from the analyzed chemical composition and other existing data.A considerable reduction in the deviation of the matte grade and slag temperature has been gained. This has resulted in conservation of energy and refractories, lower copper losses and higher through-put in the flash smelting furnace and converters.1.0 IntroductionThe flash smelting technology for copper concentrates was developed at the Outokumpu Oy Harjavalta Smelter soon after the World War II. The incentive for this development was shortness and high price of any form of energy. The fact that smelting can be carried out autogenously, without external energy by utilizing the latent heat of sulfide combustion was known decades before, but Outokumpu Oy was the first company to take the advantage of this knowledge in practical operation. A further advantage of this technology was that the SO2 containing gases suited well for sulfuric acid production, thus minimizing the detrimental effects on the environment (1).The very heart of the flash smelting process is the reaction shaft of the flash smelting furnace (see Appendix I). Heating up of the dried feed mixture, dissociation of several compounds, ignition and oxidation of the feed take place very intensively in the reaction shaft during 2 - 3 seconds, which the fine grained particles reside in the reaction shaft. A very accurate control of the amounts of the feed materials as well as of oxidizing gases, fuel, etc. is of primary importance."

Jan 1, 1989

By M. Moinpour, E. Liao, C. Y. Aw, D. J. Brown, P. W. Cheung

"Currently, silicon-based insulated-gate field-effect devices are being widely developed as the basic structural elements in a new generation of chemical microsensors. In this paper, we discuss some of the process considerations related to the fabrication of the Chemically Sensitive Field-Effect Transistor (CHEMFET). This ion-sensitive CHEMFET (or ISFET as it is often called) can be used for pH measurements (i.e., as a pH sensor) when the gate insulator of the electrolyte/insulator interface is made of Si3N4 obtained by the LPCVD method. Effects of processing parameters such as the Si3N4 deposition rate, gas composition, total flow rate, annealing treatment, etc. on Si/Si02, Si/Si3N4 and Si/Si02/Si3N4 structures are discussed in relation to the CHEMFET fabrication. Their effects on the electrical characteristics and chemical response of the sensor are also examined. Capacitance-Voltage (C-V) measurements and ESCA analysis have been used to interpret the results. The Si3N4/Si02 double dialectric layer provides improved ion blocking for the gate insulator in electrolyte solutions with enhanced pH sensitivity over time. The stability and performance of the fabricated CHEMFET sensors were tested by measuring the pH sensitivity in various storage conditions. The SEM analysis was used to evaluate the hydration effect at the ISFET's gate insulator with respect to different storage conditions.IntroductionThere has been a continuous interest in the development and fabrication of various chemical microsensors for chemical and biomedical applications over the last fifteen years. The application of semiconductor (particularly silicon) technology to the area of sensor fabrication has led to an emergence of a new generation of miniaturized, microelectronic, solid-state chemical sensors. There are numerous clinical situations where continuous monitoring of body electrolytes concentrations such as Na+, K+, Ca+2 , etc. and blood gases (pH, Po2 , and PC02) would be essential for the effective diagnosis and management of patients under critical conditions. Solid- state microsensors can be used for direct and continuous in vivo measurement of the above parameters in most instances."

Jan 1, 1988