Search Documents

By Nicholas J. Grant, Bill C. Giessen

The phase diagram Ta-Ni has been treated repeatedly; investigations up to 1958 are summed up in Ref. 1. Since then, an equilibrium diagram has been presented by Kornilov and Pylaeva.2 They found the following intermediate phases: Ta2N; (CuA12 type),3 "TaNi" (p phase, Mo8Co7 type), TaNiz, and TaNi3 (Ticus type).5 Of these, the crystal structure of TaNin remained unknown, and no further literature reference was found. According to Kornilov and pylaeva,&apos; TaNil melts peri-tectically at 1420°C. A 5-g alloy of Ta + 66.7 at. pct Ni was prepared by inert-gas arc melting using 99.95 pct Ta rod (NRC-MG) and 99.9 pct Ni shot (Fisher). The weight loss after three melts was <2 mg; a microscopically homogeneous ingot resulted. As shown in Ref. 6, no oxygen or impurity pickup needed to be considered under these conditions. Specimens were annealed for 15 hr at 1350°C, 15 hr at 1205oC, and 15 hr at 875°C with subsequent powdering and stress relief for 10 min at 1350°C, 15 min at 1205oC, and 1 hr at 875oC, respectively. Micrographs and X-ray analysis (114.6 mm Norelco camera, filtered CuK, radiation) showed homogeneous one-phase alloys in the as-cast state and at all three temperatures, all having the same powder pattern except for broad lines in the as-cast state. From this it is concluded that either TaNi, melts congruently or its melting behavior is a transition between the eutectic and peritectic cases. Since it was found that very slight surface contamination on stress relieving can considerably alter the structure of similar phases (e.g.,TaPt3),7 patterns before and after stress relief were also compared; they were identical except for line broadening in the non-stressrelieved condition, and two faint impurity lines in the stress-relieved samples. The powder pattern is presented in Table I. All lines were accounted for by indexing with a tetragonal lattice, 0Yh- I4/mmm , with a, = 3.154 ± 0.001A, co = 7.905 * 0.002i and c/a = 2.506. The atomic positions are: 1000; 1/2, 1/2, 1/2] + 2Ta(a): 000; + 4Ni(e): *(002); z = 0.333 * 0.002 This proves TaNi2 to be a representative of the MoSiz (Cllb) type. The variable parameter was determined by grouping the visually estimated intensi- ties according to their 2 indices, plotting their F values, and varying z for best fit, which was obtained at z = 0.333= 1/3. Since absorption was not considered, only the relative intensities with similar 28 can be expected to agree. The interatomic distances are presented in Table 11; the standard error is *o.o2A, resulting chiefly from the uncertainty in z. These distances indicate a coordination number 10 for both kinds of atoms and show that the pseudohexagonal layers along (110) are rather un-distorted. The mean atomic volume of 13.1A3 is close to the Vegard&apos;s law value of 13.3A3, showing

Jan 1, 1964

By P. W. Bridgman

FLOW and fracture are admittedly complicated phenomena of which we are yet only partially masters. There is not even universal agreement as to the details of the language best adapted merely to describe the phenomena, to say nothing of any theory. Certain points of view, however, are widely held, and there are certain general expectations as to what sort of procedures will prove permissible. A complete description of any situation involving fracture would demand a complete history of all the variables in the control of the experimenter. The experimenter endeavors so to choose his independent variables that they are adequate to determine completely the situation in the sense that when an experiment is repeated on the same initial material and with the independent variables running through the same sequence, all the other measurable properties of the system will also run through the same course. It is, I think, the universal conviction that when we are dealing with phenomena of flow and fracture, the most important of the necessary variables are the external forces acting on the various parts of the body; when the force history repeats, with certain obvious restrictions such as that temperature must be constant and non- mechanical forces, such as magnetic field, must be small enough to be ineffective, then the history of all measurable properties will repeat; in particular the alteration of geometrical shape due to flow will run through the same course, and when fracture comes, the character of the fracture will be reproduced. Complete mastery of merely the descriptive aspects of flow and fracture would demand the ability to predict the entire course of flow and complete characterization of the final fracture for every possible combination of forces, varying in time in all possible ways, when applied to bodies of all possible shapes. This full situation is obviously of prohibitive complexity. The first stage in reduction to manage- able simplicity is to resolve the total situation into the sum of contributions made by small elements. Our thesis is that if each of the elements is adequately characterized, the behavior of the whole system is fixed. The element is usually taken of a simple geometrical shape, suggested by the mathematics best adapted to the particular situation. The forces acting across the faces of the elements are ultimately determined by the forces acting across the free faces of the whole system. The detailed process of finding the precise forces on the faces of all the elements in terms of the external forces involves the use of a special mathematical invention, the stress, a constructional quantity consisting of six components. The stress at any point in the body is determined by both the external force system and by the physical properties of the body at all points; quite different stresses prevail at the interior of bodies of the same shape under the same external forces in the elastic and plastic ranges. The forces on the faces of any element are, however, uniquely determined by the stress system at the element. Our fundamental thesis

Jan 1, 1944

By F. W. Lake, H. A. Brett

With each year bringing the exploration of deeper and deeper producing horizons in the effort to maintain production, the problem of lifting the oil to the surface is continually becoming more difficult. Flowing and gas-lift wells eventually decline to such a point that pumping is necessary. The increasing loads on sucker rods resulting from deeper pumping operations are approaching the ultimate strength of the rods with consequent reduction in the factor of safety. With this diminishing factor of safety, the vibratory stresses causing fatigue, crystallization, and ultimate fracture become more important. These vibratory stresses are the result of varied pumping conditions which, if properly understood and investigated, may be eliminated to a great extent. To accomplish this purpose, a recording dynameter has been developed which gives an indicator card showing the actual load on the polished rod at each point of the pumping cycle. Recording Dynamometer The instrument consists of a dynamometer head of the piston and cylinder type filled with castor oil, and a recording device, the movable card holder being connected with the dynamometer through a system of levers and the hollow spring gage connected with the fluid chamber of the dynamometer by a high-pressure flexible tube. The dynamometer head is hung from the beam with an ordinary hanger and lugs on the cylinder, while the piston is attached to the polished rod. The movable card holder actuated through levers moves in a vertical direction pro-portionate to the movement of the polished rod. The recording arm of the hollow spring gage inscribes on the card the pressure at all times. Thus by proper scales, the indicator card gives the load on the polished rod at all points in the pumping cycle. Fig. 1 shows the hookup of the recording dynamometer at a pumping well.

Jan 1, 1928

By E. S. Bumps

A series of macrographs are presented for the purpose of graphically recording the strain phenomenon that accompanies the energy transition in the Charpy impact testing of a mild steel that is susceptible to strain aging. STRAIN patterns in mild steel Charpy impact specimens were obtained in order to determine whether, on the first appearance of plastic strain during deformation, the initial fracture cracks appear in the region of plastic strain or in the elasti-cally deformed regions between. Although this attempt to locate the initiation of cleavage was not successful, the observed strain patterns illustrating various stress conditions in partially deformed Charpy specimens are presented along with a discussion of the possible dependence of transition energy on the yield phenomenon. Earlier work on the development of strain patterns in mild steel have been reported by Fry1 and later by Jevon.2 Harris, Rinebolt, and Raring3 observed characteristic strain markings on the surface of Charpy V-notch impact specimens fractured above and below the transition temperature which they presented schematically. It is intended that the strain figures presented here will add to the literature a graphic correlation of strain with transition energy in impact specimens. Samples of % in. round hot rolled, 0.20 pct C steel were machined to standard 0.394 in. sq, V-notch Charpy impact specimens. Preliminary testing involved determination of transition temperature, Fig. 1, using a Sontagg impact tester. These data were subsequently used to select temperatures above, within, and below the transition range at which specimens were partially deformed. Partial deformation was obtained by either varying the energy or the testing temperature, see Table I. Macroscopic strain figures shown in Figs. 2 to 19 were produced by several metallographic repolish-ing and etching steps. The macroetchant used was as follows:4 120 g HCl, concentrated; 100 ml water; and 90 g cupric chloride. Strain figures were obtained on the outer surface and on sections through the central portion of the impact specimens in order to determine an approximation of the volumetric strain pattern. In the tensile strain figures reported by Jevon, it was found that strain etching would not work immediately following strain unless the material was heated to 200°C. The impact strain patterns presented here were obtained without this heating, but the specimens were not etched until ten months after straining. This confirms a discussion of Jevon&apos;s paper, in which it was pointed out that strain figures can also be developed after aging for long periods of time at room temperature. Hardness of the strained and unstrained portions, revealed by the etched pattern, was explored using R, impressions converted to R, hardness values. Discussion of Results In the impact test, as in the tensile test, some parts of the specimen yield and deform plastically, while other regions are deformed only elastically. The plastic deformation bears a relation to the imposed stress pattern. In the strain figures presented here, the plastically deformed regions are the dark etching ones. The strain figures are always symmetrical because the stress state in the Charpy-type specimen under impact loading is symmetrical. The difficulties encountered to produce initial cracks are intimated in Figs. 2 and 4. At a temperature of —75ºF, the stress was not sufficient to pro-

Jan 1, 1953

By W. R. Finlay, W. R. Jr. Hibbard

The key feature of the lattice coherency theory of precipitation hardening1 is the forced coherence between matrix and precipitate which elastically strains both lattices and is believed to be the major source of strengthening in precipitation hardening. In systems exhibiting age hardening, the atom movements leading to precipitation are not at all extensive and are such as to require the minimum amount of energy to produce the interface; that is, the new lattice forms in such a way as to be as nearly as possible a continuation of the old with a matched, coherent plane at the interface at least during the initiation of the precipitation. The crystallographic sequence whereby regions of the matrix change to the precipitate lattice usually can be resolved into a set of shearing operations.6&apos;6 Conversely, the perhaps novel speculation is made that solution of a second phase is accompanied by shearing movements which are possibly the reverse of the precipitation shearing movements. A basic premise of the investigation reported in this paper is that precipitation and solution shearing movements constitute structural weaknesses which might cooperate with applied stresses to facilitate plastic deformation. Another basic premise of the investigation is that the application of hydrostatic pressure to a precipitation hardening system will significantly alter the degree of disregistry across the matrix-precipitate interface and thereby significantly affect the course of age hardening. Two binary precipitation hardening systems were investigated: rz pct zinc in aluminum which undergoes transformations, both precipitation and solution, by a simple crystallographic mechanism; and 4 pet copper in aluminum which undergoes a complex transformation in precipitating and dissolving a second phase. The effects of the application of uniaxial tensile creep stress during elevated temperature aging of both systems and of hydrostatic pressure during the elevated temperature aging of 12 pct aluminum-zinc were then investigated. Previous Investigations Van Wert in 1935,~ studied the effect of hydrostatic pressure on the room temperature age hardening of a few precipitation hardening systems. The latter were rather unfortunately selected since none is known to exhibit any marked volume change on aging and the majority were complex commercial alloys the precipitation mechanisms of which are not known. Jenkins, Bucknall and Jenkins~n,~ in 1944, applied tensile creep stresses to a complex copper. nickel-silicon alloy at various temperatures. The complexity of the alloy and the industrial objective of the work did not permit an appreciable addition to the theoretical understanding of either deformation or precipitation hardening.

Jan 1, 1949

By R. P. Carreker, R. W. Guard

True stress-true strain data are given for nominally pure molybdenum (99.95 pct) over the temperature range -196° to 1540°C (0.027 to 0.63 T/T). Strain rate sensitivity was determined by rate change tests and stress relaxation tests. Inhomogeneous yielding and strain aging effects were observed. The yield stress and tensile strength depend markedly on temperature below 400°C and are insensitive to temperature in the range 400&apos; to 800°C. The ductile to brittle transition range is +25O to -25OC. Strain rate sensitivity and stress relaxation effects are very large near room temperature. THIS report presents data which were obtained as a part of a continuing program designed to document the deformation behavior of nominally pure metals over a wide temperature range.&apos;" This research program is rooted in the conviction that sufficient tensile and creep data of appropriate quality and detail does not exist to provide precise phe-nomenological descriptions of the deformation behavior of pure metals as a function of temperature, strain rate, and grain size. Such knowledge is needed to provide a firm base for alloy design and an experimental framework to which theories of deformation must conform. These data also complement a parallel exploratory program investigating the properties of refractory metals, including molybdenum, and their alloys. Several important reviews and research reports dealing with the tensile properties of molybdenum as a function of temperature have appeared."-lo To a great extent the work to be reported in the present paper parallels that of Bechtold and of Pugh. The authors&apos; results are in general agreement with those of Bechtold and Pugh. The principle differences be- tween the present experiments and those published previously are as follows: 1—Wire specimens prepared from arc cast molybdenum were used in the present experiments, bar specimens were used by others. Pugh used arc cast material while Bechtold&apos;s most extensive results" were obtained on powder metallurgy specimens. 2—Several different grain sizes were tested in the present experiments. 3—The testing range was extended to cover from -196°C to 1570°C (0.027 to 0.63 T/Tm). 4—The combination of wire specimens, high speed autographic recording, and a stiff testing machine permitted more detailed study of initial yielding. The principle contribution of the present paper is the demonstration of the relatively consistent mechanical properties of nominally pure arc cast molybdenum specimens of differing metallurgical history. Bechtold and Scotts have shown that arc cast and powder metallurgy molybdenum samples have comparable tensile properties in the range —75" to 200°C when processed to have the same re-crystallized grain size. Material The molybdenum used in this investigation was supplied by the Climax Molybdenum CO. Its metallurgical history is outlined in Table I; the final products were 0,030 in, diam wire specimens annealed at 1100&apos; and 1375°C and 0.060 in. diam wire

Jan 1, 1957

By L. A. Panek

Research on roof bolting has developed significant information with respect to the functions that can be performed by properly installed bolts and the methods that can be used to ensure that effective installation has been achieved. The present paper brings together results that are pertinent to the design of a bolting system for reinforcing horizontally stratified mine roof with vertical bolts. The design approach is based on the use of bolts to decrease the maximum bending stress within an arbitrary sequence of roof strata (see Fig. 2) in which the only loads are the weights of the individual beds. The use of rock bolts to achieve other objectives, such as to stabilize a fractured rock mass on the periphery of a mine opening,3 is excluded from consideration herein. Reinforcing effect of bolts consists of a friction effect and a suspension effect in combination. "Friction effect" refers to reduction of bending in a stratified roof due to clamping action of tensioned bolts, which compress the strata, thereby creating frictional resistance to displacement along planes of stratification. (The flexure of a sequence of strata is necessarily accompanied by horizontal displacement of each bed with respect to its neighbor, along mutual surfaces of contact.) Although the sliding of the beds tends to exert a shearing effect on the bolts, tests show that this has negligible influence on the bending stresses, probably because the bolts are so far apart. "Suspension effect" refers to the transfer of part of the weight of the weaker or thinner strata to one or more thick strata, which occurs when strata with differing tendencies to deflect are constrained to have equal deflection. The term "suspension" is used irrespective of whether the thin strata are above or below the thick strata, because tests show that the supporting effect of the flexurally more rigid roof strata is for practical purposes independent of their position in a bolted sequence of strata. An earlier paper4 dealt with a bolted unit in which all strata had equal flexural rigidity; bolting could develop a friction effect but no suspension effect. The present paper deals primarily with a bolted unit in which all strata do not have equal flexural rigidity, so that bolting can develop both a friction effect and a suspension effect. The reinforcing effect of the bolts was determined by a combination of experimental and theoretical stress analysis.4&apos;6&apos;7 The experimental method consisted of loading a model by rotating it in a centrifuge to simulate the gravity forces exerted about an underground excavation. Models were made from two different limestones, although the results are independent of the material because the elastic constants were taken into account in the data analysis. Electric resistance strain gages were bonded to the highest and lowest members of the bolted unit to determine the outer-fiber bending strains at the center and at the supports. The quantitative results presented herein are based on tests of 56 different models, which included a range of values for the structural parameters. Each model was tested several times, with different combinations of spacing and tension of the bolts. DESIGN EQUATIONS The effects of friction and suspension on the flexure of a bolted stratified roof can be expressed by the following equations, which give the maximum bending stress, the deflection, the friction effect, the suspension effect and the transferred load for any (the i-th) member of the bolted unit in terms of the structural parameters:

Jan 1, 1964

By H. D. Williams, R. A. Scriven

The distribution of elevation angle of finite plane facets distributed symmetrically about a given axis is derived in terms of the angular distribution of lines which these facets produce in a plane section parallel to the axis. It is assumed that the facets are not markedly elongated in preferential directions. The theory is intended for application to the angular distribution in polycrystalline metals of slip planes and of particular grain boundaries on which certain phenomena such as cavitation can occuv. Illustrative examples are given in closed form and simple numerical techniques are de-ueloped for practical application. The results are applied to the distribution of cavitated boundaries in a copper specimen after fatigue at 400°C and it is found that voids form on the boundaries that exper~enced maximum shear stress. When investigating the distribution of elevation angle between a given axis and planes symmetrically distributed about this axis the angular distribution observed in a plane section parallel to the axis is not necessarily the same as the required distribution. Consequently a technique for processing the results obtained by sectioning methods is required. An example where such a technique would find application is in the problem of intercrystalline void formation during uniaxial tensile creep. Two theories have been proposed to explain this cavitation in terms of the normal and the shear components of stress, respectively. Hull and Rimmer (1959) postulate that the growth of intercrystalline voids is controlled by the rate of supply of vacancies from the grain boundary, the local vacancy concentration being proportional to the normal stress on the boundary. Gifkins (1956) considers that slip arising within a grain causes a ledge to be formed at the grain boundary which is subsequently opened up into a cavity by grain boundary sliding. It might be possible to differentiate between these mechanisms by determining the angular distribution of grain boundaries containing cavities since the former theory predicts a predominance of cavitated facets normal to the stress direction whereas the latter should favor an angle of 45 deg to this direction. In a similar manner an indication may be obtained of the type of mechanism responsible for intercrystalline cavitation during high-temperature fatigue. Davies and Wilshire (1962) have analyzed the slip-plane distribution in a nickel specimen but the problem was not treated in any detail nor was any account taken of the finite extent of the planes being sectioned. Hilliard (1962) has given a very general account of how anisotropy in the microstruciure can be related to measurements taken in one or more plane sections by expressing both the measured and the true angular distributions as expansions in spherical harmonics.* The present analysis is con-

Jan 1, 1965

R. Culver, Colorado School of Mines I appreciated Professor Starfield&apos;s presentation, because his approach to blasting research reflects my feelings that a lot of practical work can be done toward making short-term advances that can be used by the blasting industry. We should not forget this in our attempt to obtain solutions to such idealized problems as a mathematical theory of cratering. The blasting industry would like very much to have the efficiency of the basic blasting processes improved from the range of 20 percent up into the range of 50 percent. And many of these problems should be approached and attacked in the laboratories. Blasting research at the Colorado School of Mines for the past two or three years has been aimed at improving the pre-splitting process, because we feel it will become increasingly important to the construction industry. We have attempted to develop a unified theory of how pre-splitting works; and the more we investigate, the more variables we find. We may never obtain an entirely satisfactory theory of pre-splitting, but we have developed a tentative explanation. One of our first conclusions was that we are making very poor use of the explosive in current pre-splitting practice. But to appreciate this we must first consider how pre-splitting works. A series of parallel boreholes are loaded with low density charges which are detonated simultaneously. (Delayed detonation has been tried, but most people agree that simultaneous detonation is best, and this is what we found.) Stress waves traveling out from each borehole interact with the stress waves from the two adjacent boreholes influencing the direction of the fractures that occur and propagate from each borehole. It has been suggested in private communication with Mr. Wilbur Duvall of the U. S. Bureau of Mines, that the fracture between the adjacent boreholes is a result of the net particle velocities above and below the pre-split plane which tend to set up a net tension along the pre-split plane. Regardless of what the exact mechanism is that causes the fracture to propagate from one borehole to the next, we know that it, in general, relies upon an interaction of the stress waves. However, if there is a large compressive stress normal to the pre-split place, it can practically eliminate any possibility of obtaining the desired pre-split by preventing the desired fractures from getting started. Aside from obtaining a fracture along the pre-split plane, the other major aim of pre-splitting is to minimize the fracturing that occurs around the borehole. We do this by drilling a large hole and putting a small charge in the middle of it. This results in a badly decoupled charge which is very inefficient; most of the energy is used in compressing the air in the borehole. Out of discussions about how pre-splitting works, we decided that perhaps there was some other explosive geometry which would make more efficient use of the explosive, and result in optimizing the pre-splitting process. Starting in the laboratory with small plexiglas blocks, we found that a fully-coupled explosive charge of 5 grains/in. of PETN gave random fractures extending about I in. from the borehole. A 1/4 in. plexiglas plug fit into a 1/4 in. hole in a similar block with the same fully coupled charge gave random fractures extending out only about 1/2 in. due to the energy absorbed in fracturing the plug. If the plug was split longitudinally but otherwise using the same geometry, it was possible to drive a fracture about 2 in. in either direction from the borehole, with an even smaller amount of fracturing around the borehole.

Jan 1, 1967

By E. S. Machlin, C. W. Chen

RECENTLY Chen and Machlin&apos; proposed a mechanism for intercrystalline cracking in metals during high-temperature stressing. According to this mechanism the formation of voids at grain boundaries is primarily responsible for intercrystalline cracking. A model has been provided to demonstrate the initiation of submicroscopic cracks and voids at jogs of grain boundaries where grain boundary sliding is inhibited. Submicroscopic cracks can grow as a result of either further grain boundary sliding or localized tensile stress. In the former case, it is believed that grain boundary sliding produces more voids which link together to produce macroscopic cracks and which may lead to the eventual failure of the metal. Concurrently, Nield and Quarrell2 reported their interesting results obtained in a systematic investigation of intercrystalline cracking in two aluminum alloys under various creep conditions. Their observations are generally in agreement with the above mechanism, especially the conclusion that voids are formed as a direct consequence of grain boundary sliding. On the basis of the volume fraction occupied by voids, they could find no confirmation of vacancy condensation as the mechanism for void growth. Furthermore, an important feature of intercrystalline cracking has been likewise pointed out by them that the majority of cracks are not formed at grain corners. Nield and Quarrel1 meanwhile emphasized the importance of grain boundary migration by designating it as one of two main processes operative in the mechanism of crack formation during creep. The designation seems unnecessary because overemphasis of grain boundary migration only complicates the mechanism of void formation. There are two reasons which militate against the inclusion of grain boundary migration in the mechanism of void formation. In the first place, the formation of intercrystalline voids per se does not require grain boundary migration. Secondly, in addition to grain boundary migration, void formation may be minimized by any other process such as plastic deformation which is capable of relieving localized stresses around jogs. Chang and Grant3 have shown that intercrystalline cracking is prevented in aluminum by lattice bending in high stress regions. The influential role played by grain boundary migration in creep has also been realized in our studies. In several cases, voids did not appear at all in grain boundaries whenever grain boundary migration took place prominently during creep. The purpose of this paper is to discuss the effect of grain boundary migration on the formation of intercrystalline voids and other related rupture properties. Experimental evidence indicates that in an unstable grain structure void formation may be markedly modified by structural changes. The abnormally high ductility and the transcrystalline mode of fracture observed in copper at elevated temperatures reveals that effective grain boundary migration minimizes void formation. Grain boundary migration has long been known as a common high-temperature phenomenon in metals with the grain configuration in a nonequilibrium state. Its effect on ductility and mode of fracture has not been recognized until recently.4 Since the introduction of the term "Equicohesive Temperature," the conventional belief has been that below the equicohesive temperature the ductility of metals increases moderately with decreasing temperature until the ductile-to-brittle transition temperature of fracture is reached. In this temperature range, metals fracture in a ductile mode with a "cup-and-cone" fracture surface. Above the equicohesive temperature, ductility remains invariably low and decreases slightly with increasing temperature. The mode of fracture is strictly brittle and intercrystalline. Typical examples have been shown for a brass and copper in Fig. 1 and 9, respectively, in the paper by Greenwood, Miller, and Suiter.5 The observation in the upper temperature range that ductility of metals is low and insensitive to temperature may be explained in terms of void formation at grain boundaries. It is also in accordance with the findings of McLean6 and Fazen, Sherby, and Dorn7

Jan 1, 1961

By R. Maddin, C. H. Mathewson, W. R. Hibbard

According to conventional crystal mechanics, a face-centered cubic single crystal slips on the system {111} <110> which receives the highest shear stress in terms of the stated orientation of the stress axis of the crystal.l However, in brass, the slip process is never as simple as this conventional analysis indicates. There is always a second cooperating plane which contains the same slip direction as the primary plane.2&apos;3 There is still another cooperating slip system commonly called the conjugate system3 previously observed to function with considerable lag only after the rotation due to the action of the first plane had produced a symmetrical condition of equal shear stress on the two systems. In the 1943 Campbell Lecture,4 a slip mechanism was outlined in which the {111) planes moved step-wise in two adjacent <112> directions integrating into the <110> slip direction. "... the slipping process would be visualized as a succession of steps 30" to the right and left of the resultant, microscopically observed, slip direction; a first step setting up the twinned configuration in the single spacing involved and an ensuing slip returning the atoms to the untwinned configuration while completing a fully integrated <110> movement."4 This process is shown diagrammatically in Fig 1 which shows two close packed layers of atoms at a slip site. A movement of the full circles through the "valleys" into the adjacent sites would produce a twin configuration with respect to the open circles. The term, "twin fault," seems most appropriate to define this faulted condition of the lattice. Annealing twins in face-centered cubic metals may arise from preformed nucleii which could be described as twin faults produced by the first movement of this two stage slip process. However, it is clear that this kind of slip does not take place so as to embrace a measurable number of adjacent planes because careful X ray examination has not conclusively shown the existence of ponderable twin lamellae (as in the case of Neumann bands in the body-centered ferrite). In view of the imponderable character of these hypothetical twin faults, the search for evidence of their existence seems restricted to indirect methods. The most obvious experimental technique serving this purpose is the determination by micrographic and X ray methods of the alignment of the composition planes of annealing twins with the former slip planes in axially strained and recrystallized single crystals. In previous attempts of this sort not all of the annealing twins could be traced to slip planes known to be operative in the conventional sense and hence evidence appeared negative or inconclusive. With the discovery of additional slip systems2&apos;3 operating in conjunction with&apos; the major system of highest resolved shear stress in axially strained brass it became apparent that the simple technique outlined above might be re-employed with more gratifying results. If, on annealing single crystals of alpha brass previously strained in tension, twins are found with their composition planes parallel to all three operative slip planes and with no participation of the fourth plane there is good evidence in favor of the existence of twin faults and of the two stage slip process. Experimental Procedure and Resuits Single crystals of alpha brass of the 70-30 composition were grown by solidification from the molten state.

Jan 1, 1950

By M. J. Marcinkowski, K. S. Sree Harsha

A detailed numerical analysis has been made of the equilibrium configuration of partial dislocations in a blocked deformation twin under an externally applied stress. Twins made up of both pure screw and pure edge partials have been considered. The components of stress in the vicinity of the twin tip associated with each of these configurations have been plotted. It has been found that at some critical degree of oblateness the shear stress fields of the blocked screw or edge twin can both sPontaneously nucleate slip, whereas only the component of stress oxx about the edge twin can nucleate and propagate cracks. TWINNING becomes a predominant mode of plastic deformation at low temperatures and/or high strain rates. Fig. l(a) shows what must be the first step in the formation of a deformation twin, namely the formation of a loop of imperfect dislocation bounding a stacking fault. In an fcc crystal the partial dislocations have Burgers vectors of the type 1/6 a,(112) and the fault is of the intrinsic type while in the bcc crystal the partials have Burgers vectors of the type ao(lll). The stacking sequence of (111) planes in a perfect fcc crystal is given by ABC ABC, and so forth, and in one which contains a twin by ABCABACBA, and so forth. It is apparent that the stacking fault and twin give rise to no mistakes associated with adjacent close-packed planes; however, with respect to second-neighbor close-packed planes the faulted crystal has twice as many mistakes as the twin. The energy of the twin boundary may thus be taken to be one-half that of the intrinsic fault boundary. In the case of the bcc crystal the stacking sequence of (112) planes is given by ABCDEFABCD, and so forth, in a perfect crystal, by ABCDCDEFA, and so forth, in a crystal which contains a fault, and by ABCDCBAF, and so forth, in one which contains a twin. An analysis similar to that applied in the fcc crystal shows that both the fault as well as the twin involve no neighbor violations across adjacent planes. However, there are twice as many violations across second-neighbor (112) planes associated with the fault as compared to that of the twin. Thus once again the energy of the twin boundary may be taken as one-half that of the fault. It is important to note that, unlike the fcc, the faults in the bcc crystal involve first nearest-neighbor violations and are thus expected to be of much higher energy than those in fcc crystals. A more detailed analysis of the material discussed above can be found in Ref. 1. To a good approximation then, the lenticular twin shown in Fig. l(b) can be generated by adding partial dislocation loops on successive (111) planes for fcc crystals or (112) planes for bcc crystals in the manner shown, with no additional expenditure of chemical energy other than that required for the fault shown in Fig. l(a). In practice, deformation twins are much more extended than that shown in Fig. l(b) and more closely resemble one shown schematically in Fig. l(c). It is readily apparent that the free energy of the twin and matrix are identical. In those cases where the partials lead to a structural change, the free energy of the material contained within the dislocation array is lower than that of the matrix and we have the so-called martensite transformation. The present investigation is the first in a series of five major theoretical-experimental efforts which will deal with the static and dynamic behavior of twin nucleation and growth. There has been a recent surge in activity pertaining to the equilibrium shapes of twin lamellae2&apos;3 and

Jan 1, 1969

By R. J. Sherman, M. R. Achter

Creep rates have been measured for nickel at 1200°F in air and in vacuum, and related to the depth of surface cracks in the specimens tested in the two environments. The surface cracks were observed to grow faster in air than in vacuum in both short-time and long-time tests. Crack depths, however, could be correlated with creep rates only in the short-time tests. Although no cracks were observed in a relatively brittle Ni-Cr-A1 alloy creep tested at 1300°F, the appearance of alloy specimens fractured after interruption in creep indicated that there was a decrease of intergranular cohesion resulting from the diffusion of atmospheric gases into grain boundaries. PREVIOUS investigations1-3 have demonstrated that the effect of atmosphere on the high-temperature strength of nickel and nickel-base alloys may be reversed by changes in the stress or temperature of the test. At high stress and low temperature the creep-rupture life is longer in vacuum than in air, while at high temperature and low stress the relative strengths are reversed. A mechanism to explain this behavior was proposed based on two competing processes. Oxidation hardens and strengthens a metal, but adsorption of gas, by lowering surface energy, reduces the work required to propagate an intergranular crack. The controlling process is determined by temperature and stress. Basic to this mechanism is the concept that environment determines the ease of propagation of intergranular cracks and thus affects creep rate and rupture life. To explore the mechanism in greater detail, this investigation was undertaken to determine the effect of atmosphere on crack initiation and propagation rates in nickel1 and a relatively brittle Ni-Cr-A1 alloy.3 EXPERIMENTAL PROCEDURE The materials were the same as used previously. Nickel of 99.8 pct purity had the following impurity content: 0.02 pct Co, 0.03 pct Fe, 0.02 pct Mg, 0.03 pct Si, and 0.008 pct C. Rods were cold swaged from 1/2 in. to 3/8 in. in diam and machined into speci- mens with gage sections 1/4 in. in diam by 1-1/4 in. long. They were annealed in vacuum at 1600" F for 1 hr to achieve a grain size of 0.07 mm. The alloy was composed of 19.1 pct Cr, 3.6 pct Al, 1.7 pct Si, 0.57 pct Fe, 0.10 pct Mg, 0.027 pct C, 0.004 pct S, and the balance Ni. Sheet specimens of 0.500-in. width and 1.25-in. gage length were machined from 0.033-in.-thick strip and annealed in vacuum at 2000° F for 2 hr, resulting in a grain size of 0.036 mm. Large amounts of an intergranular phase were introduced as a result of the anneal. Creep tests on both materials, using equipment previously described by Shahinian; were conducted in air and in a vacuum of 1 x 10-5 mm Hg. They were continued to rupture and interrupted at various stages of the test. Although extensions were measured from dial gage readings of movement of the lever arm, it is considered that valid comparisons of creep rate may be made in this manner.l Two parameters were measured metallograph-ically* on longitudinal sections of nickel specimens interrupted during creep—the mean depth of surface cracks 2, and the density n as the number of cracks per unit length of surface. They were combined into one parameter by the relation p = n-d [1] As used here, p is equal to the total of crack depths per unit length of surface. RESULTS Nickel. It is well known that the incidence of intergranular cracking is increased with increasing rupture life. Indeed, it is evident in Tables I and I1

Jan 1, 1962

By H. R. Ogden

The notch sensitivity of titanium alloys is affected by impurity content, microstructure, and heat treatment. Using notch tensile properties to evaluate notch sensitivity, three commercial titanium-base alloys were investigated over the temperature range of -320o to 390°F. The alloys studied were Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo. Six interstitial levels were studied for each alloy in four mi-crostmctural conditions. The ff- 0 alloys were studied in both the annealed and heat-treated condition. All tests were conducted using 1/4-in. diam round tensile samples. The notched samples had a 50 pct notch with a notch sharpness (a/r) of 53, corresponding to Kt 6.3. Notch sensitivity was increased by increased interstitial content, low temperature, and acicular-type microstructures. The heat-treated, high-interstitial content - 13 alloys were more notch sensitive than the same alloys in the annealed condition. In addition, minima in the notch tensile-temperature curves were observed at temperatures near 32°F. These minima became more pronounced with increasing interstitial content. 1 HE increaseduse of titanium alloys in high strength applications at subzero temperatures requires that a better under standing of the low-temperature behavior of the alloys be obtained. At low temperatures, metals generally exhibit increased strength with lowered ductility and tohness. Notch sensitivity and the factors which influence it become more important as the strength level is increased and the temperature is decreased. Some of the factor s which affect notch sensitivity in ti- tanium alloys are composition, interstitial content, microstructure, and heat-treatment condition. In this paper, the results of a study of these variables on the notch sensitivity of three titanium alloys at temperatures from —320o to 390o are reported. The notch geometry selected for this program was chosen to provide a severe test of notch sensitivity. The ability of the metal to flow without initiating fracture under these severe conditions is reflected in the notch-strength values. Since notch strength is, in part, determined by the constraint exerted by the combined tensile stresses, the behavior of notch specimens reflects the properties of the material under combined stresses. For example, a material with a high notch-unnotch strength ratio may be expected to withstand the biaxial stresses encountered in a pressure vessel better than a material with a low ratio of notch-unnotch strengths. This implies that maximum strength alone is not a sufficient criterion for applications of this type. It further may be concluded that the various conditions that promote poor notch behavior also will affect adversely the performance of materials under combined stresses. In the alloys studied, these included low temperatures, high interstitial levels, and hasformed microstructures. EXPERIMENTAL PROCEDURES Three alloys, Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo, were purchased from commercial producers as 2-in.-dam rod stock. Oxygen and nitrogen were added to these alloys by remelting to obtain a variety of interstitial contents as shown in Table I. In order to Compensate for the much more potent strengthening effect of nitrogen compared with oxygen, an oxygen equivalent content is used to describe the total oxygen plus nitrogen contents studied. It has been suggested previously1 thatnitro-gen is approximately twice as effective in strengthening as oxygen, and carbon, to the extent it is in so-

Jan 1, 1962

By H. Sigurdson, T. V. Cherian, C. H. Moore

The phenomenon of recovery of cold-worked metals is interesting not only because of its practical importance but also because of its fundamental significance in solid state reactions. Although extensive investigations1,2 have already been made in an attempt to discover the mechanics of the recovery process, many of the observations have not yet been satisfactorily correlated to provide a completely consistent model for the process. The wide differences in the recovery rates of various properties can be cited as a typical example of one of the difficulties that are encountered. Frequently, for example, the electrical resistance will have almost completely recovered before any recovery in tensile strength can be detected. Of course, such differences in the recovery rates of different properties might be explained by assuming that each property is a unique function of the work-hardened state, and consequently each property exhibits its own unique recovery rate. The assumption that different properties are uniquely related to the work-hardened state cannot be denied. On the other hand, the properties that recover at different rates often exhibit more or less parallel changes upon work-hardening. This suggests that the microstructural changes attending recovery are not exactly the reverse of the changes attending work-hardening. Several types of imperfections must be postulated in order to account for this apparent anomaly. The different recovery rates for various properties, then, are due to the different recovery rales of the type of imperfection to which each property is most sensitive as well as the unique dependence of each property on the cold- worked state. This concept assumes that a simple model of the work-hardened state consisting only of one type of imperfection, such as Taylor&apos;s type of dislocation patterns, is inadequate to cope with the diversified phenomena attending work-hardening and recovery. Although current models for the work-hardened state are not useful for describing all aspects of the recovery process, the general trends of the recovery of each postulated type of imperfection as a function of time and temperature should be at least qualitatively deducible from the rather well developed laws of kinetics of reactions in the solid state. Consequently, recovery data might prove useful for elucidating some aspects of the complexities of the work-hardened state of metals. A preliminary attempt to study work-hardening by investigating recovery rates of cold-worked metals is outlined in the following pages of this report. Experimental Procedure Many properties recover when cold-worked metals are annealed below their recrystallization temperature. Therefore, electrical resistivity, thermal electromotive force, X ray diffraction line widths, X ray diffraction line intensities, elastic spring back, density and other physical and chemical properties have been used to study the recovery process. Major interest, however, has generally been directed toward the recovery of the mechanical properties such as hardness, yield strength, and tensile strength. But a search of the literature suggests that the effect of recovery on the true stress-true strain curve has been neglected, in spite of the current recognition of the fundamental importance of such an investigation. An investigation on the effect of recovery treatment on the true stress-true strain curves in tension, therefore, was undertaken in the present study. Commercially pure aluminum (99. + pet Al) in the form of 0.100 in. thick rolled sheet of 2S-O aluminum alloy was selected as the material for this investigation because rather extensive correlatable data are already available on the recovery of some of its properties. Tensile specimens having a 6 in. long gauge section and a uniform reduced section width of 0.500 in. were machined from the sheet in accordance with a design that has previously been reported.3 All specimens were selected with their axes aligned in the rolling direction. In order to eliminate the effects of previous work-hardening and the effects of machining, the specimens were annealed for 15 min. at 750°F before testing. During tensile testing the loads were measured by means of a proving ring (sensitive to 1/2 lb) in series with the specimen.4 Strains were determined from the extension of a rack and pinion strain gauge sensitive to a strain of + 0.0001. The stress was recorded as the true stress, namely

Jan 1, 1950

By Walter A. Backofen, Donald H. Avery

Intense primary and cross-slip traces were observed in easy glide on Cu: 6 pct-A1 single crystals deformed in tension. A mechanism of cooperative source operation is developed which recognizes that both the applied stress and that resolved from dislocation arrays contribute to the stress on a source. By considering the stress from arrays, the activation of secondary systems in easy glide and the difference in appearance of slip markings on pure and solid-solution crystals are explained. Furthermore the cross-slip system is predicted to be second favored during easy glide for a large range of orientations. FROM many studies of easy glide in fcc metal crystals, a pattern of observations has developed which still requires full explanation. In pure copper, aluminum, and silver, the easy-glide, slip traces are fine and uniform with steps 50 to 100A on the primary* system.1-4 Yet it has not been at all clear why slip in the pure materials should occur in this way. On the contrary, one might expect, with simple slip and a low hardening rate, that the weakest sources on the primary system would operate extensively to produce strong slip traces. In a brass, however, intense slip steps up to 0.5 are found on both primary and cross-slip system4,6-9 seeger10 has pointed out that in a material of low stacking-fault energy such as a brass, extensive easy-glide cross-slip could not be thermally activated, but rather must originate on the cross-slip plane. In further explanation, the wilsdorfs4 and seeger10 noted that only the cross-slip system would not harden differently than the primary, whatever the latent hardening tendencies of other systems; therefore, in brass, which exhibits high latent hardening, the cross-slip is the only secondary system which could be expected to operate extensively, once it became active. The explanation of how the cross-slip system, on which the applied stress is low, becomes activated has been related, in a nonspecific way, to pileups by Hirsch11 and Honeycombe.l2 In the work to be described, deformation traces on solid-solution Cu: 6 pct A1 single crvstals were studied with conventional light microscopy and a mechanism proposed to explain both the observed activation of secondary systems in easy glide and the difference in appearance of slip markings on pure and solid-solution crystals. EXPERIMENTAL In preparing the Cu-A1 single crystals, rectangular bars approximately 0.4 in. by 0.4 in. by 6 in. were first machined from ingots made by vacuum melting copper of 99.999 pct and aluminum of 99.99 pct purity. They were then packed in powdered graphite and the crystals grown in a modified Bridgman apparatus at a rate of 5 mm per hr under an atmosphere of purified nitrogen. Crystal perfection as indicated by Laue back-reflection spots was good except for the last inch to freeze, which was discarded. Orientations so determined are shown in Fig. 1. Tensile specimens with a reduced gage section were obtained by masking the ends with electrical tape and chemically polishing in a solution of 20 pct HNO3, 24 pct HAc, 52 pct H3PO4, 2 pct Hcl, and 2 pct H20 at room temperature.13 Finally, the specimens were electropolished in a 30 pct ortho-phosphoric acid bath at 12 v. Tensile deformation was performed in an Instron testing machine at a strain rate of approximately 1 pct per min. During easy glide, extensive cross-slip was observed with all crystals, in spite of the low Schmid factor on this system, and in no case was any other secondary trace encountered. A certain sequence of slip-line development was associated with the extension. At yielding, intense primary traces passing completely through the crystal developed at some point on the gage section, generally near the grips; weak cross-slip traces also appeared, extending from the primary traces into the adjacent undeformed crystal, Fig. 2. Further extension led to primary traces adjacent to the first-formed and connecting with those of the cross-

Jan 1, 1963

By T. H. Alden

BaCKOFEN, Avery, and Turner have shown"2 that the large tensile elongation in superplastic metals is correlated with a high strain-rate sensitivity of the flow stress. At present, the reported superplastic materials are complex eutectic or eutectoid systems with a large solubility range in at least one of the terminal phases. This note describes the behavior of a solid-solution alloy (at 22°C)5,= Sn-1 wt pct Bi, which has been processed in order to produce a fine grain size.2,3,6 The chill-cast, 1/2-in.-diam ingot was homogenized for 1 week at 130°C, extruded at O°C to 0.083 in. diam, quenched within 15 sec, and stored at -196°C. Samples were warmed to room temperature 16 hr prior to mechanical testing or metallography. During tension testing at room temperature, it was found that the flow stress reached a steady-state value which depended on the imposed elongation rate and was independent of strain to an error of about ±5 pct. In Fig. 1 is plotted log a vs log e where a is the measured steady-state flow stress and i the imposed strain rate. These quantities were calculated using "instantaneous" area and length to an accuracy in the sample diameter of ±5 x 10-4 in. The log a-log 1 curve is sigmoidal. The strain-rate sensitivity, which may be given by d log old log 6,&apos; has a maximum value of about 0.48 between i = 5 x 10-4 and 5 x 10-3 per min. The value is well above frequently measured values for metals at creep temperatures (0.1 to 0.3) and comparable to the rate sensitivity for Pb-Sn solder: which has been shown to be superplastic.2,3 Note, however, that below or above the strain rate of 10-3 per min the rate sensitivity of Sn-1 pct Bi decreases and at high rates is more nearly like that of conventional metals. The grain size of this material is relatively uniform, Fig. 2, and may be specified by an average linear intercept i.&apos; Grain growth occurs at room temperature but after 16 hr, L = 5. Tensile elongation was measured on finer-grain-size specimens, which had been at room temperature 15 min prior to testing. After 15 min, the samples are fully recrystallized. Three strain rates, 5 x 10-3, 10-2, and 2.5 x 10-2 per min, were employed for which the measured elongations varied from 425 to 500 pct. These results would seem to justify the term superplastic, applied to this alloy, although the ductility is inferior to that of the Sn-Bi eutectic.3 The Sn-1 pct Bi alloy, which is a single-phase material with equiaxed, fine grains, is an excellent one on which to make an estimate of the Nabarro-Herring9 creep rate. According to the model of Avery and Backofen2 a substantial part of the deformation must be accomplished by N-H creep in the strain rate-temperature regime in which d log a/d log 1 = 0.5. The maximum N-H creep rate is given by9 L2kT where v is the atomic volume and D the self-diffusion coefficient. For this test v = 3.O x 10-23 cu cm, D = 1.4 e-23,300/RT = 2.5 x 10-l7 sq cm per sec,7 L = 5x 10+4 cm, T = 295°K, and a = 2000 lb per sq in. = 1.38 x 10&apos; dyne per sq cm. The calculated creep rate is E= 4 x 10-11 per sec which may be compared with the measured creep rate at this stress, Fig. 1, of 6.7 x 10-5 per sec. The N-H creep rate is seen to be negligible. Earlier consideration2 of this question was in error because incorrect diffusion coefficients were used. The assistance of R. R. Russell in metallography is acknowledged gratefully.

Jan 1, 1967

By D. P. Kedzie, R. A. Dodd

The fatigue strength, fatigue hardening, and effect of fatigue deformation on subsequent age hardening of supersaturated Al(Cu) solid solutions have been determined as functions of alloy composition and temperature. The fatigue strength/tensile strength ratios, determined at 150°, 25°, and -195°C, decreased with increase in alloy content for all temperatures, but the F.S./U.T.S. ratios at -195°C decreased much more rapidly than did the ratios for 150" and 25°C. This suggested that strain aging and/or age hardening occurred during tests at higher temperatures. Additionally, the F.S./U.T.S. ratios at 150°C exceeded those at 25°C for all compositions, indicating greater strengthening during fatigue at 150°C. The effect of fatigue or tensile deformation at 150°, 25°, and -195°C on subsequent age hardening showed that the deformatzon increased the rate of precipitation and indicated that mechanically produced vacancies were probably formed during deformation. Fatigue hardening was studied at 150°, 25°, and -195°C, and the effect of room-temperature rests after 10 and 100 cycles was examined. The results confirmed that strain aging occurred at the higher temperatures . DURING the last 15 years various mechanisms of fatigue crack nucleation and growth based on dislocation and vacancy interactions, operating singly or collectively, have been proposed. The probable consensus of present opinion is that the fatigue process in pure metals essentially involves dislocation interactions, and that vacancies formed by such interactions play a minor or inconsequential role. However, there is some evidence that age-hardened alloys tend to overage during fatigue, probably by local vacancy-enhanced diffusion, and strain aging also might be important in selected cases. Furthermore, it has been established that the behavior of quenched-in vacancies in Al(Cu) and other solid solutions is composition-sensitive. Therefore, it seemed worthwhile to investigate various aspects of the fatigue behavior of supersaturated Al(Cu) alloys and to examine the results in terms of vacancy-enhanced effects. EXPERIMENTAL The alloys used in this investigation were prepared from 99.994 wt pet A1 and OFHC copper, the latter containing 0.04 pet 0 as the principal impurity. Six alloys were made, containing, by actual analysis, 0.58, 0.96, 1.96, 2.85, 4.45, and 5.51 wt pet Cu. They were induction-melted in air in graphite crucibles, cast as 7-in. by 7/8-in.-diam rods in graphite molds, and hot-rolled to 5/8 in. diam. The experimental work was a three-part program involving the determination of a) 10&apos; cycle fatigue stresses as a function of alloy composition and temperature; b) the effect of fatigue deformation on subsequent aging of the supersaturated alloys; and c) fatigue hardening as a function of alloy composition and temperature. For determining the 105 cycle fatigue stresses, a portion of the 5/8-in. stock was machined into Krouse rotating cantilever beam fatigue specimens, 2 in. in length by 1/4 in. minimum diameter. These were tested at +150°, 25°, and -195°C (liquid nitrogen) on a Krouse high-speed machine, with special weights to provide lower -than-normal loading ranges, this being necessitated by the small load requirements of those alloys of lower copper content. For the high-temperature tests a small resistance heater was designed to clear the collets and fit in between the chucks, while for the low-temperature tests a hollow nylon cylinder was used, having closed ends drilled to pass a fatigue specimen, and positioned similarly to the heater. A plexiglass container completely enclosed the fatigue machine; rubber gloves fixed to ports in the walls enabled the machine to be operated from outside the box. A tray of magnesium perchlorate dried the air in the container and prevented both atmospheric corrosion fatigue at room and elevated temperatures and troublesome ice build-up at low temperatures. A total of ten to fifteen specimens was used for each combination of alloy composition and temperature. The result of each test was plotted on a standard S-N diagram, and the next stress was selected on the basis of the trends indicated by previous specimens. In this manner a small portion of the S-N diagram was constructed, and the 105 cycle fatigue stress obtained. Small Krouse fatigue specimens were also used to study the effect of cyclic prestrain on subsequent

Jan 1, 1964

By N. Jaffee, J. E. Dorn

An activation energy of 27,400 5 1000 cal per mole was obtained for the creep of poly crystaLline aluminum over the temperature range of 273° to 350°K, at strains varying from 0.003 to 0.230. Stresses varied fronz 2250 to 6000 psi, strain rates from 0.1145 x 10-5 to 29.5 x 10~s min.-1. A strain temperature-compensated time correlatzon was oblained indicating that the structure was depedent solely upon the strain at a given stress; X-ray diffraction analyses and tensile tests on precrept specimens verified this. PREVIOUS investigations1 have revealed that the apparent activation energies for creep of high-purity polycrystalline aluminum are insensitive to the applied stress, strain, and strain rate. On the other hand, the apparent activation energy is dependent on the temperature1,2 as shown by the data reproduced in Fig. 1. Each plateau of this curve is associated with a unique rate-controlling dislocation mechanism for thermally activated creep. It is now very well-established that over the high-temperature range, where the activation energy is about 35,500 cal per mole, the creep rate is controlled by the dislocation climb mechanism. 3 Over the intermediate range of temperatures, from about 260° to 370°K, another unique activation energy, namely 28,000 cal per mole, is obtained. Current evidence strongly supports the contention that cross slip is the rate controlling mechanism for creep in this case: 1) Crystal recovery can occur by a number of mechanisms prominent among which are climb and cross slip. Astrom,4 using the Borelius micro-calorimeter, reported rapid crystal recovery of cold-worked polycrystalline A1 at 340° to 370°K giving an activation energy of 28,000 cal per mole and additional recovery at 455° to 478°K giving an activation energy of 3 6,000 cal per mole. Whereas the latter recovery process was clearly associated with the dislocation climb mechanism, the former, 28,000 cal per mole process could have arisen as a result of the cross-slip mechanism. 2) Single crystals of high-purity A1 favorably oriented for octahedral glide exhibit an activation energy for creep of about 3400 cal per mole over the range from 0° to 400°K and that of about 28,O:O cal per mole over the range from 600° to 775°K . Whereas the lower activation energy process is accompanied by the development of sharp slip-band traces, the 28,000 cal per mole process was uniquely characterized by extensive cross slip. 3) Theoretical calculations by Seeger and schoeck6 suggest an apparent activation energy for cross slip in A1 of about 24,000 cal per mole and another theoretical estimate by Friedel 7 gives the observed 28,000 cal per mole as the theoretical activation energy. It is therefore consistent with this evidence to, at least tentatively, ascribe the 28,000 cal per mole creep process in A1 to the operation of cross slip as the rate controlling mechanism. Although creep has been rather well-explored in the dislocation climb range, very little, excepting perhaps the activation energy, is known about creep in the cross slip range. This investigation was undertaken, therefore, to reconfirm the activation energy for creep in polycrystalline A1 in the intermediate temperature range and to study the strain-time relationship for creep at a constant stress in the cross slip region. EXPERIMENTAL PROCEDURE AND TECHNIQUE The three types of high-purity A1 alloy specimens described in Table I were used in this investigation. Specimens were milled from 0.100 in. thick cold-rolled sheets with their tensile axes in the rolling direction following which they were given a recrys-tallization and grain growth heat treatment at temperatures well above those which were subsequently employed in the creep tests.

Jan 1, 1962

By H. C. Chang, N. J. Grant, A. R. Chaudhuri

During the creep of coarse-grained polycrystalline magnesium at elevated temperatures, a nonbasal type of slip was found to play an important role in the deformation processes. The nonbasal slip traces were examined metallographically in eight specimens (13 grains) and the observed glide plane located stereographically for each grain. The tests were run at 500&apos; and 700°F at stresses of 148 to 786 psi. Based on these measurements and theoretical calculations, the crystallographic elements for nonbasal slip were determined. WHEN a metal deforms by slip, the conventional appearance of the slip bands on the surface of a specimen is that of straight lines. Such is the behavior of the face-centered-cubic metals, as for example, aluminum. The particular slip system on which slip occurs in these metals is governed by the criterion of resolved shear stress. Work on the body-centered-cubic metals a-iron,&apos;. &apos; molybdenum, and columbium4 has shown that the process of slip is somewhat more complicated than the simple gliding of one close-packed plane of atoms over another in a close-packed direction and that it results in the formation of wavy and irregular slip traces on the surface. The recent reviews and experiments of Vogel and Brick and Chen and Mad-din3 show that, for the body-centered-cubic metals, the resolved shear stresses along the planes and the degree of close-packing do not necessarily determine the slip system. Theirs and other investigations indicate that a complete understanding of the slip process in the body-centered-cubic metals is not yet possible. However, one behavior displayed by all these metals is that the slip direction is invariably one of the close-packed directions <11l>. The wavy nature of the slip-band traces has been explained on the basis of cooperative slip by planes sharing this same slip direction.1&apos;3l&apos; It is generally acknowledged that, when the hexagonal-close-packed metal magnesium (axial ratio c/a = 1.624) deforms by slip at room temperature, it does so by basal slip in the close-packed direction <1I%>. This type of slip has the conventional appearance of straight lines and is governed by the critical shear-stress law. Schmid and coworkers" showed that basal slip was operative in the temperature range of —185" to 300°C (—300" to 572°F). Work by Servi, Norton, and Grant6 has shown that, during the creep of coarse-grained aluminum at high temperatures, new slip systems come into operation. The existence of a new high temperature slip system at temperatures greater than 225 °C (437°F) for magnesium was suggested also by Schmid. This was later indicated by Bakarian and Mathewson&apos; to be slip along the pyramidal planes (10i1) in the close-packed direction <11%>.* They * Mention will be made in the text of pyramidal planes and prismatic planes. The pyramidal planes referred to are the type I. order 1 of the form {10il); and the prismatic planes of the type 1 of the form (10i0). For the sake of brevity, they are termed in the teat as pyramidal (10il: and prismatic (10i0) planes, respectively. Where reference is made to the pyramidal plane type 1, order 2 of the form {10i2), they are referred to as the pyramidal planes of the type (10i2:. observed that this kind of slip resulted in irregular markings on the specimen surface. According to them, a possible cause for the appearance of the markings was due to "limited accessory slip on the pyramidal {10i2) planes." Burke and Hibbard," on deforming a single crystal of magnesium at room temperature, found evidence of slip on a pyramidal plane {1011). They explained it as being due to the effect of grip restraints. It is pertinent to note at this point that, although basal slip has received a fair amount of attention, only two specimens have been investigated, that of Bakarian and Mathewson and of Burke and Hibbard, to establish the elements of nonbasal slip in magnesium. During the study of the deformation mechanisms

Jan 1, 1956