By Yury Kapelyushin

Formation of cementite in the reduction of hematite by CO–CO2 gas was studied in situ using high temperature XRD (HT XRD) analysis. Reduction of hematite was examined in the temperature range 873–1173 K by CO–CO2 gas mixture with high carbon activity. When carbon activity in the system was 1.5, cementite was formed only at 1023 K; it was not observed in experiments at 973, 1073 and 1123 K. Formation of cementite was observed at 923–1073 K when carbon activity increased to 3–5; and at 873 K when carbon activity was 10. Formation of cementite at 973–1073 K proceeded through metallic iron; however, in the reduction of hematite at 873 and 923 K, iron was not observed; cementite apparently was formed directly from wüstite. XRD spectra were used to estimate concentration of carbon in austenite in the process of cementite fromation.

By G. C. Yao

Branch and needle-shaped intermctallic compounds of iron, silicon and aluminum normally exist in the molten aluminum. If a suitable amount of manganese metal is added into molten aluminum, the shape of the intermallie compound particlcs may become lumpish and spherical. According to the difference in electric and magnetic properties of these impurity particles and molten aluminum, these impurity intermctallie compound particles can be separated by applying an alternating magnetic field. In this experiment the alternating magnetic field was formed by a "C" type loop with AC (50Hz) current. The inner vacuum of the fireclay refractory separator is 25>< 15" 130mm3 with a lateral baffle inside. The separator was put into the interspace of the "C" type loop. It was found that the longer the separation time, the larger the amount transferred of impurities. The amount of transferred impurities increases with the increase of separation time and intensity of magnetic field. The addition of manganese metal enhanees signifieantly the efficiency of impurity separation.

Jan 1, 2003

By Feng Liu

A thermal upgrading process by which nickel value can be concentrated in a ferronickel alloy is a possible alternative to treat Sudbury pyrrhotite (Po) tailings with nickel content of 0.5–1.5 wt%. The basis of this process is precipitation of Ni from Po at high temperature once Fe/S ratio in the iron-deficient Po is shifted towards stoichiometric or near stoichiometric FeS (troilite) either by the addition of iron and/or the removal of sulfur. For the iron addition route, the reaction between elemental iron and nickeliferous pyrrhotite to produce ferronickel alloy and Ni-depleted iron sulfide phase plays a critical rule. In this paper, the formation mechanism of ferronickel alloy was investigated using the diffusion couple technique to better understand the nickel diffusion behavior in the iron and sulfide phases.

By Yuanbo Zhang, Bin Xu, Guanghui Li, Xiao Kang, Chen Liu, Tao Jiang

Iron-bearing dusts, containing valuable constituents such as Fe, CaO, MgO, C, etc., are generally utilized as raw material in iron ore sintering. However, the dusts characterized by low granulating and refractory performances always lead to negative effects on sintering indexes. As we know, the innovative process named composite agglomeration process (CAP) has a series of advantages compared to traditional sintering process (TSP). In CAP, part or all of the iron-bearing dusts is made into green pellets with 5-15mm in diameter, while the rest of iron-bearing dusts and all of the other fine ores is granulated after mixing with fuels, fluxes and return fines. Compared with TSP, CAP could increase the ratio of iron-bearing dusts from 5% to over 20%. Meanwhile, the yield, ISO tumbler index and productivity reached 75.82%, 65.13% and 1.531t·m-2·h -1, respectively.

Jan 1, 2015

By L. M. Luckevich

Gypsum is a product from the neutralization of sulfuric acid by lime or limestone. This paper will discuss specifications for gypsum used in wallboard, cement and agriculture and the factors affecting its utilization potential. Process conditions during the neutralization which enhance or inhibit utilization potential will be included. In addition, this paper provides a technical and economic perspective of the gypsum industry in North America with a view to the factors affecting the utilization of synthetic gypsum in traditional applications. Current production and consumption of natural and synthetic gypsum in Nonh America are described and the impact of their differences on utilization options are discussed.

Jan 1, 1996

By James W. Reeves

DuPont was the titanium metal pioneer who put the greatest effort into both R&D and commercial sponge and powder metallurgy production. This was concentrated in the period 1945 through 1963. The commercial results were development of the chloride process for TiCl4 using ilmenite, development and improvement of the Kroll process, development of a modified Hunter process to make titanium powder and commercial development of a direct powder process. The powder metallurgical process failed because of the inability to meet powder chloride specifications. All this work remained a trade secret until published in NMAB -392 by Mahla in 1983. There were other processes explored by DuPont, both improved sponge and powder processes. Much of this work has been continued by others but none, as of yet, resulting in new improved titanium metal capacity.

Jan 1, 2001

By Jr. Langhans, J. S. McPartland

"The presence of zinc in cyanide solutions is generally thought to not have an adverse effect on precious metal recovery or recovery rate by heap leach processing. However, analytical interferences of zinc in solution can cause problems in accurately determining and controlling cyanide concentration in the leach solution, leading to increased cyanide consumption. Analytical methods and the chemistry of cyanide in the presence of zinc are reviewed. The effects of solution pH and zinc concentration on the free cyanide determination were evaluated in detail. Use of the standard silver nitrate titration and a modified titration method for controlling cyanide concentration during heap leaching were investigated experimentally. The practical implications of cyanide heap leaching in the presence of cyanide soluble zinc minerals are discussed.IntroductionThe presence of zinc in precious metal cyanidation circuits is not uncommon. Zinc can be introduced into cyanide leach solutions through dissolution of various zinc minerals1>, or through the use of a Merrill Crowe (zinc precipitation) circuit. Zinc minerals typically occur infrequently and in low concentration in gold ores, but are more abundant in silver ores. Merrill Crowe systems are most commonly employed for recovery of precious metals from solution for relatively high silver ores. It is desirable to control the amount of dissolved zinc in a cyanidation circuit for several reasons. Excessive zinc build-up in cyanide leach solution can, under certain circumstances, inhibit precious metal dissolution and adversely affect solution recovery systems. Additionally, high zinc concentrations can lead to excessive in-process cyanide inventories and potentially, to higher cyanide consumption"

Jan 1, 1999

By Yan Beygelzimer, Alexander Spuskanyuk, Victor Varyukhin

"A cellular model of the plastic deformation of polycrystalline aggregate is proposed and comprehensively described. Representative volume element (RVE) of a solid body, that is being deformed, is described as a population of interconnected units that, in turn, can consist of lower scale level units. Sliding along the various allowed sliding systems deforms simple units, which do not have an internal structure. For consideration of stress distribution within the limits of components, the approach of self-consistent field is used. Rotation of units and moment stresses connected with it are taken into account. Results of computer experiments are analyzed.1. IntroductionMicromechanical models of polycrystals are a link between the research of plastic deformation on micro and macro levels. Computer simulation of inelastic strain of polycrystals has found a great deal of interest as well. Despite the fact that this approach does not allow to obtain macroscopic constitutive relationships that are used in deformed solid body mechanics, it clarifies essential features of the phenomena in many aspects. First of all, it concerns effects stipulated by interdependence of micro-level and macro level of plastic deformation processes. Also, with the computing mechanics, instead of constitutive relationships, the adequate computer models can be used. Broad possibilities for computer simulation of various processes are opened by cellular automata approach. By means of numerical experiments, the cellular automata allows to study the macro behavior of the whole ensemble of cells depending on the local microscopic laws that define evolution of each cell and its interaction with the closest environment.We propose a mathematical model of a polycrystalline aggregate (the cellular model) based on a self-consistent scheme and on the interaction law similar to the one by Berveiller and Zaoui [1]. Our original solution is the self-similar structure of cellular automata that allows modeling of the fractal nature of real materials (Figure 1). The goals of this work are to present the major structures and relations of cellular model of polycrystal and to test this model for its adequacy as for describing known effects and dependencies. Identification of the model and its application for studying of concrete polycrystals are put aside for the future research."

Jan 1, 2001

By Wenya Du, Qingbo Yu, Peng Li, Qin Qin

"A new heat recovery system is proposed. This system uses the endothermic heat of gasification reaction instead of sensible heat to recover the energy of molten blast furnace slag. The gasification technological parameter in molten blast furnace was calculated and the exergy of the system was analyzed. The gasification reactions were studied kinetically by the isothermal thermogravimetry using STA409PC thermal analyzer. The results showed that, according to different gasification agent, this system can produce syngas with different C-H ratio. The exergy efficiency of this system is high and its internal exergy loss rate is about 11%. This method can bring huge economic and environmental benefits which are important to the survival and sustainable development of iron-steel enterprises. The molten BF slag acts as not only thermal media but also good catalyst. The kinetic parameters on gasification reaction with different types of coal used differ from each other.IntroductionEnergy consumption in the iron-making process is about 50%~60% of the total energy input. The blast furnace is very important in the iron & steel process. So energy conservation and emission reduction about blast furnace is very important. In recent years, in order to recovery energy, many new technologies such as TRT (Top gas pressure Recovery Turbine) and CCPP (Combined Cycle Power Plant) were used in iron-making. But the energy of molten blast furnace (BF) slag has only been used limitedly so far.Molten BF (Blast Furnace) slag is the byproduct of iron-making at the high temperatures range from 1723 to 1923K, and has a large amount of sensible heat remaining. The yield of molten BF slag is about 300 kg per ton of pig iron. In conventional processes, molten BF slag is quenched rapidly using a large amount of water to produce a glassy-granulated slag. The quenching slag must be dried before it can be used in cement manufacture. During the process, a large amount of water was consumed and the energy of molten slag can not be recovered. At the same time, it causes environmental pollution problems. So the critical problems of the process are not only energy recovery of molten slag and reducing emission of H2S and SO2, but also guaranteeing the subsequent use value of slag. For this propose, many new technologies were investigated to recover the thermal energy of molten slag. The promising methods are dry granulation [1-4] and reforming of methane [5-9]. The method, utilization of reaction heat instead of latent heat and sensible heat, is quite attractive from viewpoints of energy storage without heat loss, and makes a connection to other industry. But both of them are in laboratory. In this paper, coal gasification in molten BF slag was used to recover the energy of molten BF slag. The gasification technological parameter in molten BF was calculated and the exergy of the system was analyzed. The gasification reactions were studied kinetically by the isothermal thermogravimetry using STA409PC thermal analyzer."

Jan 1, 2011

By Xuan Cheng

The electrochemistry of sulfide mineral flotation is reviewed with particular emphasis on galvanic interaction among minerals and grinding media, and its relevance to flotation of complex sulfide ores is discussed. Surface alteration due to galvanic interactions among chalcopyrite, pyrrhotite and mild steel is analyzed in terms of voltammetric and chronoamperometric studies on individual minerals and through galvanic current measurements in 2- and 3- electrode combinations. The results are related to laboratory flotation behaviors of chalcopyrite-pyrrhotite mixtures simulating copper-nickel bearing Duluth gabbro.

Jan 1, 1993

By Jamil M. Khalifeh, Shadia J. Ikhmayies, Bothina A. Hamad

"We computed the optical properties of the cubic niobium nitride (o-NbN) compound using the full potential linearized augmented plane wave (FL-LAPW) method within density functional theory (DFT). The complex dielectric function and optical constants, such as optical absorption coefficient, refractive index, extinction coefficient, energy-loss spectrum, and reflectivity, are all calculated and compared with experimental results. The behavior of the computed quantities is similar to that obtained experimentally, but the optical positions are shifted to lower energies. This shift was related to the strong interband transitions, which are located at energies higher than 5 eV for NbN- as they are for IV B transition-metal mononitrides- and they appear in the computed spectra and not in the experimental spectra. These interband transitions simply shift the position of the reflectivity edge or the screened plasma frequency to the longer wavelength side.IntroductionIn recent years, NbN, as a transition metal nitride, has become a very popular material due to its high hardness, melting point, wear resistance, chemical inertness and temperature stability, which makes it suitable for use as emission cathodes in microelectronics and sensors, optical films and micro-mechanics etc [l]. Niobium nitride has long been known as highly polymorphic material, for which several crystalline structures have been reported in the literature [2]. These structures include the well known super-conducting rock-salt (Fm-3m, or Bl) structure (o-NbN), the hexagonal structure with space group p63/mmc and prototype Fe2N (18fuN), the hexagonalstructure with space group p63/mmc and prototype NiAs ~-NbN) and others.There has been a lot of computational studies for the structural and electronic properties ofNbN [3, 4-7], but according to our knowledge there is not any computational work that has been devoted to study the optical properties of this transition metal compound. At the same time a number of authors had performed experimental work in this direction. For example, Xin-kang et. al [l] studied the microstructure and optical properties of magnetron sputtered NbN thin films. Torche et. al [8] studied the composition, structure, electrical and optical properties of nonstoichiometric niobium nitrides. Newport et. al [9] investigated the reflection and transmission spectra of cubic niobium nitride films, and Tanabe et. al [10] had investigated the optical parameters and reflectivity of reactively sputtered NbN thin films by using in situ ellipsometry."

Jan 1, 2013

By D. F. Suarez

Spontaneous nodulation leading to growth of well developed glossy spheroids (generally hemispheres) of up to 0.06 cm width in 120 min has been observed during copper electrodeposition with certain levels of glue, thiourea and C1-. Thiourea alone can produce spontaneous nodulation but addition of glue and/or Cl- is required for rapid and sustained growth. In most cases once the glossy nodules develop they consume the majority of the copper deposited; thus, the specific current densities (and hence copper electrodeposition rates) on the glossy nodules are about an order of magnitude or, more greater than on the adjacent planar surfaces. The texture of the adjaoent planar surfaces is not glossy in appearance but is well faceted showing the usual deposition grain structure for such additives. Cathode potentials when spontaneous nodulation occurs are about TOO my more negative than with usual copper electroplating. This fact associated with evidence of extremely high levels of cathode surface passivation based on cyclic voltammograms indicates that the conditions which lead to spontaneous nodulation result from a very tightly adsorbed additive surface film. This film breaks down in specific points initiating the glossy nodules which then grow at extremely rapid rates. Current density is also important in spontaneous nodulation. At equal deposition times a current density of 21.5 mA/cm produced much larger glossy nodules than at 48 mA/cm2. The surface concentration of the glossy nodules was much greater in the latter case, however. The role of current density is still not well understood. The role of it as well as the relative roles of the three additives, thiourea, glue and Cl- in spontaneous nodulation is presented. Preliminary results and some possible correlations of these to help explain spontaneous nodulation are presented. It is believed that tankhouse upsets where cathode nodulation occurs may be related to this phenomenon.

Jan 1, 1987

By Shu Yamaguchi

The behavior of halide impurities in pyrometallurgical processes such as Wealtz kiln and MF process has been discussed based on the thermochemical data and the reported data of PbO activity in PbCl2-PbO melts. The role of PbCl(g) has been estimated to be significant in the chloridization evaporation reaction. From reported data on the PbO activity in PbC12-PbO melts, activity of PbCl2 has been calculated by the numerical integration of Gibbs-Duhem equation, and the stability domains and the composition of the liquid phase as well as the vapor pressure of PbCl2 have been estimated as functions of log P2HCI/PH2O and temperature. From the discussion of the path during cooling process on the log P2 HCI . PH2O vs. temperature diagram, the authors proposed a possible dechioridization process that utilize water vapor as a dechloridizer for the direct precipitation of PbO from gas phase.

Jan 1, 2003

By Reza Kamali, Mohsen Bashiri, Hadi Fanisalek

"Half of the input energy to aluminum reduction cell will be lost as waste heat which could be studied for possible recovery. Since price of energy is increasing and the main production cost in primary aluminum industry is energy, so waste heat recovery consideration will be interesting. One of the possible choices for recovering is from aluminum exhaust gases that needs minimum modifications for reduction cell and has no influence on cell heat balance which is vital for the operation. By using heat exchangers with in-line and staggered tube arrangements which placed before fume treatment plant (FTP) we will be able to recover enough amount of heat. The main challenging problem which is necessary to overcome will be the heat exchanger material and its design because of corrosive and dusty exhaust gases from potroom. In this paper, a desalination system with six effects of evaporator is proposed for producing distilled water by using recovered heat from hot exhaust gases. The calculated amount of produced distilled water is around 27,000 / in this specific suggested desalination plant. The suggested desalination plant is based on Hormozgan Aluminum Company data (Hormozal) in Bandar Abbas, Iran which is constructed by the Persian Gulf.IntroductionWaste heat losses arise both from equipment inefficiencies and from thermodynamic limitations on processes. The exact quantity of industrial waste heat is poorly quantified, but various studies have estimated that as much as 20 to 50% of industrial energy consumption is ultimately discharged as waste heat [1]. In order to achieve a final decision for establishing the waste heat recovery plant in any type of industry, a strong feasibility study is mandatory. Also, we need to remember that the possible amounts of energy and suggested process plant for recovery have to be investigated before starting any feasibility study. This kind of study which is important to be finished before moving to feasibility step is mainly a theoretical study, and was done for the Hormozgan Aluminum Company (Hormozal). In addition to the exhaust gases from the potroom, the exhaust gases from anode baking plant appear to have a better potential for waste heat recovery compared to potroom exhaust gases. The average temperature of exhaust gases from anode baking kiln is 120°C higher than the exhaust gases temperature in the potroom. This needs further investigation in a different study, because this study is just focusing on potroom exhaust gases."

Jan 1, 2011

By G. Van Weert, A. van Sandwijk, O. W. J. S. Rutten

"Cathodic and anodic reactions in an acidic nitrate medium were studied in reference to the production of electrolytic manganese dioxide from pyrolusite' (Mn02) ores by reductive leaching. Two USA ores were investigated. The reductant for the pyrolusite ore is produced cathodically in an electrolytic cell and can either be nitrous acid (HN02) or nitric oxide gas (NO). In this work emphasis was placed on the nitrous acid leach. In a high-temperature leach in a nitrous/nitric acid medium, manganese and silver are solubilized and iron is not. Anodic electrowinning of manganese dioxide from the acidic manganese nitrate electrolyte yields flaky y-Mn02, similar to that produced from sulfate and chloride electrolytes. Cathodic regeneration of nitrorts acid was studied in a membrane cell in 1.0 M nitric acid and 0.0 to 0.1 M nitrous acid on a' platinized titanium cathode. At cathode potentials ranging from +950 to +700 mV (SHE), cathodic reduction to nitrous acid takes place, at cathode potentials < +700 mV, cathodic reduction of nitrous acid to nitric oxide takes place. A conceptual process is presented and discussed.IntroductionManganiferous-silver oresLarge reserves of manganiferous-silver ores are present in the Southwestern United States and Latin America. These ores are generally refractory to hydrometallurgical methods of treatment, due to the insolubility of the higher oxides of manganese (Mn 4+) in all common lixiviants such as cyanide solutions, dilute sulfuric acid, nitric acid, ammonia, salt solution, thiosulfates, etc. The silver is either bound by the insoluble manganese, or is rendered inaccessible to cyanide leach solution by the surrounding manganese mineralization.Higher oxides of manganese will dissolve if they are first reduced pyrometallurgically to manganous oxide (Mn2+). This is a widely used pretreatment for manganese dioxide ores and subsequent dissolution in sulfuric acid is common. In order to avoid the pyrometallurgical pretreatment with its large energy requirements and gaseous emissions, fully hydrometallurgical processes have been proposed. These processes are based on the presence of a reductant in solution, in order to reduce the insoluble higher oxides of manganese to soluble lower oxides. Aqueous S02 has been proposed and tested on industrial scale by the U.S. Bureau of Mines. After washing, silver could be extracted by cyanidation. The neutralization of the pulp prior to cyanidation however causes problems in filtration and the reagent consumptions are high [1]. More recently, acidified thiourea and bacteria were proposed for the solubilization of both manganese and silver in a single leach step. High extractions were obtained, but drawbacks of these methods are high reagent consumption or slow kinetics [2,3]. For the options of manganese recovery from the leach filtrate, precipitation with persulfate or ammonium carbonate and ion exchange have been proposed. The proposed options for silver reclaim are precipitation with either zinc or Na2S and adsorption onto activated carbon."

Jan 1, 1997

By Heikki K. Jalkanen

Thermodynamic properties of copper-iron mattes and slag-matte distribution of copper and some minor matte constituents (Ni, Co, Mo, As, Sb and Bi) are discussed on? the basis of equilibrium measurements: a change from. oxidic to sulfidic solubility as the predominant form of dissolution of copper takes place as matte grade decreases. Distribution coefficients of minor matte constituents are complex functions of sulfur and/or oxygen potentials?. The distribution behaviour of different? metals can be qualitatively derived from their affinities to copper and stabilities. of their sulfides and oxides. The equilibrium results are compared with commercially observed values. from Outokumpu.Oy flash smelting furnace.

Jan 1, 1983

By E. W. Lithgow

Commercial volumes of nickeliferous laterite ores overlie part of a 90 km long belt of peridotites in central Dominican Republic. Protores are serpentinized harzburgites and dunites, with lesser serpentinite. The ore mineralogy consists mostly of goethite, serpentine-group minerals, quartz and poorly crystallized, x- ray amorphous materials. Minor constituents are hematite, gibbsite, olivine and enstatite. In the Ore Dressing plant the mine feed is subjected initially to proper sizing and blending to produce a homogenized mix. Subsequent drying and upgrading, by selective crushing and screening of rock fragments through a Barmac circuit, complete preparation of the ore for pyrometallurgical processing.

Jan 1, 1993

By Z. R. Llanos

This paper presents a review of industrial and experimental processes for the recovery of molybdenum, vanadium, nickel, cobalt and aluminum from spent hydrotreating or hydrodesulfurization catalysts. Numerous processes have been developed in a laboratory and pilot scale. However, worldwide, there are only four well established commercial facilities currently in operation. The installed capacity of these facilities exceeds the availability of spent catalysts and may be sufficient to assimilate future increases of spent catalysts. Despite liability risks; significant quantities of spent catalysts are still being landfilled. Changing regulations that may affect the future handling and disposal of spent catalysts are also reviewed.

Jan 1, 1995

By G. C. Yao

Iron and silicon impurities can form needle and branch shape intermetallie compounds in molten aluminum when there is no manganese. It is difficult to separate them from molten aluminum by electromagnetic separation. The Fe-Si-AI and Fe-AI intcrmetallic compounds were transformed into Mn-Fe-Si-AI and Mn-Fe-AI compounds by the addition of manganesc into molten aluminum, In molten aluminum the morphology of these intermetallic compound particles is lumpish and spherical. Migration resistance of these impurity particles is small, which is beneficial to separation. FeSiMnAl4 and FeMnAl6 arc paramagnetic. These impurity particles can be moved by magnetic force and can be separated from the molten aluminum.

Jan 1, 2003

By Satu Strömberg

Four different nickel concentrates were oxidized in a laboratory scale laminar flow furnace in simulated flash smelting conditions. The major nickel- and iron-bearing minerals in the con- centrates were pentlandite, violarite, gersdorffite, and pyrite and pyrrhotite, respectively. Thermal decomposition, ignition and oxidation behavior of nickel and iron sulfides were examined by using optical and scanning electron microscopy. General reactivity of the concentrates was monitored with sulfur removal which was most effective in violarite-based concentrate. Pentlandite-concentrates needed higher experimental temperatures for complete desulfurization and gersdorffite-based concentrate contained 5 - 10 % of the original sulfur even in the most oxidizing conditions studied (1 100°C, 50 vol-% 02). The reactivity of the iron minerals was found to depend on the other minerals present in the concentrate. In this paper, the observed re- action products and mineralogical changes are presented and preliminary conclusions of possible reaction mechanisms of nickel-bearing minerals are discussed.

Jan 1, 1997