By Walter A. Backofen, Donald H. Avery

Intense primary and cross-slip traces were observed in easy glide on Cu: 6 pct-A1 single crystals deformed in tension. A mechanism of cooperative source operation is developed which recognizes that both the applied stress and that resolved from dislocation arrays contribute to the stress on a source. By considering the stress from arrays, the activation of secondary systems in easy glide and the difference in appearance of slip markings on pure and solid-solution crystals are explained. Furthermore the cross-slip system is predicted to be second favored during easy glide for a large range of orientations. FROM many studies of easy glide in fcc metal crystals, a pattern of observations has developed which still requires full explanation. In pure copper, aluminum, and silver, the easy-glide, slip traces are fine and uniform with steps 50 to 100A on the primary* system.1-4 Yet it has not been at all clear why slip in the pure materials should occur in this way. On the contrary, one might expect, with simple slip and a low hardening rate, that the weakest sources on the primary system would operate extensively to produce strong slip traces. In a brass, however, intense slip steps up to 0.5 are found on both primary and cross-slip system4,6-9 seeger10 has pointed out that in a material of low stacking-fault energy such as a brass, extensive easy-glide cross-slip could not be thermally activated, but rather must originate on the cross-slip plane. In further explanation, the wilsdorfs4 and seeger10 noted that only the cross-slip system would not harden differently than the primary, whatever the latent hardening tendencies of other systems; therefore, in brass, which exhibits high latent hardening, the cross-slip is the only secondary system which could be expected to operate extensively, once it became active. The explanation of how the cross-slip system, on which the applied stress is low, becomes activated has been related, in a nonspecific way, to pileups by Hirsch11 and Honeycombe.l2 In the work to be described, deformation traces on solid-solution Cu: 6 pct A1 single crvstals were studied with conventional light microscopy and a mechanism proposed to explain both the observed activation of secondary systems in easy glide and the difference in appearance of slip markings on pure and solid-solution crystals. EXPERIMENTAL In preparing the Cu-A1 single crystals, rectangular bars approximately 0.4 in. by 0.4 in. by 6 in. were first machined from ingots made by vacuum melting copper of 99.999 pct and aluminum of 99.99 pct purity. They were then packed in powdered graphite and the crystals grown in a modified Bridgman apparatus at a rate of 5 mm per hr under an atmosphere of purified nitrogen. Crystal perfection as indicated by Laue back-reflection spots was good except for the last inch to freeze, which was discarded. Orientations so determined are shown in Fig. 1. Tensile specimens with a reduced gage section were obtained by masking the ends with electrical tape and chemically polishing in a solution of 20 pct HNO3, 24 pct HAc, 52 pct H3PO4, 2 pct Hcl, and 2 pct H20 at room temperature.13 Finally, the specimens were electropolished in a 30 pct ortho-phosphoric acid bath at 12 v. Tensile deformation was performed in an Instron testing machine at a strain rate of approximately 1 pct per min. During easy glide, extensive cross-slip was observed with all crystals, in spite of the low Schmid factor on this system, and in no case was any other secondary trace encountered. A certain sequence of slip-line development was associated with the extension. At yielding, intense primary traces passing completely through the crystal developed at some point on the gage section, generally near the grips; weak cross-slip traces also appeared, extending from the primary traces into the adjacent undeformed crystal, Fig. 2. Further extension led to primary traces adjacent to the first-formed and connecting with those of the cross-

Jan 1, 1963

By J. E. Drury, W. M. Byers, E. J. Lynch

Measurements made with starch ~~~~s indicate that the Presence of starch serves to depress the streaming potential of a clay mud system. Measurements with pure starch slurries show that the addition of NaCl or CaO reduces the streaming potential significantly. The addition of NaOH, however, causes only a minor reduction in potential even when there are large changes in mud resistivity. INTRODUCTION In their excellent study of the streaming potential, Hill and Anderson' proposed that the presence of conductive solids within the filter medium will reduce the generated potential. This theory was demonstrated with measurements on shaly sandstone cores having various "b" factors; the cores with the higher negative b factors showed markedly lower potentials. (The factor b was originally defined by Hill and Milburn2 in an expression relating the resistivity of a shaly sandstone to the resistivity of the interstitial water: log F, = log F,, + b (log 100R,)'. 'he factor b, therefore, is a measure of the contribution of the conductive solids to the total conductivity of the sample. It has been found experimentally to be directly related to the amount of chemically exchangeable ion per unit pore volume.) In the logical extension of this hypothesis to the streaming potential created by filtration through mud cakes, they suggested that the presence of nonconductive starch in a drilling mud would have the opposite effect; i.e., it would cause the streaming POtential to be increased. The high streaming potentials that they observed with lime muds were attributed to this cause. A cross-plot of some of their results which are relevant to this discussion is given in Fig. 1. The lime-mud curves and untreated-mud curve are taken from curves given in their paper. The gyp-mud line was estimated from their statement that the measured streaming potential for gyp muds in the range of 1.5 to 2.0 ohm-m was approximately 18 mv/1,000 psi. These gyp-mud potentials were the lowest that they reported for any of the bentonitic-clay muds, and were the only ones which were less than the untreated-mud potentials. This very low streaming potential of gyp muds has also been observed in field studies.' By way of comparison, a U. of Texas publication4 gives the approxi-ate compositions for lime and gyp muds shown in Table 1. These materials are added to a bentonitic-clay mud base. It can be seen that both of these muds contain significant amounts of calcium salts and that the gyp mud has the higher concentration of starch. It would appear from this and from the data shown in Fig. 1 that starch may well be the cause of a streaming-potential reduction, rather than a potential increase. EXPERIMENTAL A series of streaming-potential experiments has been performed using a cell of a design similar to that reported by Wyllie.5 Calomel electrodes were used in both the mud slurry and the filtrate. Pressure in the cell was generated with high-pressure nitrogen. The primary objective of the investigation was to determine the effect of starch on the potential. Five different slurries were made which ranged in composition from untreated ben-tonitic mud (Baroid Aquagel) to a pure starch suspension (Baroid Im-permex). The intermediate slurries were prepared by mixing together a 9-lb/bbl clay mud with a 12-lb/bbl starch suspension in the ratios 1:3, 1:1 and 3:1. When starch was used alone, it was necessary to use an 18-Ib/bbl mixture, since leaner mixtures would not form a suitable filter cake. The clay mud used in the experiments was aged for three months before use. In addition to this series of measurements on the starch-clay mud mixtures, other experiments were performed to determine the effect on the potential of the absolute starch and Aquagel concentration, and the effect of adding various chemicals. RESULTS The effect of starch on the streaming potential is shown clcarly in Fig 2. Increasing percentages of starch resulted in n continually decreasing

By Richard J. Fruehan

ThE thermodynamic activities of nickel and chromium in liquid Ni-Cr alloys have not been previously reported. There have been several investigations on the solid alloys.1-3 In the present investigation the activity of chromium in liquid Ni-Cr alloys at 1600° C was determined by the use of the following galvanic cell, The use of galvanic cells employing solid oxide electrolytes for determining the activity of metals in solid alloys was first demonstrated by Rapp and Maak4 on Cu-Ni alloys between 700° and 1000°C. Recently Schwerdtfeger5 tested the performance of the ZrO2(CaO) electrolyte at 1600°C and found it satisfactory for oxygen pressures as low as 10"12 atm. He also demonstrated the use of solid oxide electrolytes for determining the activities in liquid metal systems in measuring the activity of manganese in Fe-Mn alloys at 1500°C. Extensive investigations have been carried out in this laboratory, exploring the oxygen partial pressure lower limit at which ZrO2(CaO) electrolyte can be used satisfactorily in oxygen galvanic cells at 1600°C. In a paper to be published at a later date,9 it is demonstrated conclusively that ZrO2(CaO) exhibits insignificant electronic conductivity at oxygen pressures down to about 3 x 10"13 atm which is lower than the oxygen partial pressure in equilibrium with Cr-Cr2O3 at 1600°C. Therefore, the activity of chromium can be related to the measured reversible electromotive force of the cell in the present investigation since no electronic short circulating will occur. Fig. 1 is a schematic diagram of the cell used. The Cr-Cr2O3 electrode was made of equal weights of chromium and Cr2O3 powders which were mixed and packed into a recrystallized alumina crucible. A Pt-wire lead was embedded into the Cr-Cr2O3 compact to insure good contact. A ZrO2(CaO) crucible, supplied by the Zirconium Corp. of America, contained the Ni-Cr melt equilibrated with solid Cr2O3. The ZrO2(CaO) crucible was placed on the Cr-Cr2O3 electrode and additional Cr-Cr2O3 mixture was packed around it. Contact with the Ni-Cr alloy was made with a Cr2O3 tube, which is a weak electronic conductor. A platinum wire lead was attached to the Cr2O3 tube. The galvanic cell was lowered slowly into the hot zone of the furnace tube in order to avoid too large a thermal shock which could break the ZrO2 (CaO) crucible. The furnace was con- tinuously flushed with purified argon during the experiment. The temperature was measured with a Pt-Pt/10 pet Rh thermocouple and maintained at 1600° ± 5°C. The electromotive force was measured with a recording potentiometer. The furnace was turned off when measurements were being made in order to avoid induction effects and the reversibility of the cell was demonstrated in the usual manner. The electromotive force was measured several times over a period of approximately 1 hr. During that period the electromotive force remained constant within ± 3 pet and did not continuously drift in any one direction. After the experiment the alloys were analyzed for chromium in the usual manner. The measured electromotive forces of the cell at 1600°C, (2912°F), are listed in Table I. The activity of chromium, with solid pure chromium as the reference state, (a), was calculated using Eq. [l], , n F E I, n lna RT- U] where E is the measured electromotive force, F is the Faraday constant, and n is equal to 3, the number of equivalents per mole, (nF/RT = 18.59 volts'1 at 1600°C). The resulting activities are listed in Table I. The activity of chromium relative to pure liquid chromium was also calculated. The free energy of fusion of chromium at 1600° C was calculated using

Jan 1, 1969

By R. H. Oliver

The purposes, types, preparation, and testing of flocculants are discussed. A flocculation compendium is included, indicating choice of flocculant for a given set of conditions. An economic evaluation of the process is presented. Solid-liquid separation is a major expense in most mineral processing flowsheets today. Proper use of flocculation can often lower the overall cost of a solid-liquid separation by reducing the size of sedimentation or filtration equipment. PURPOSE OF FLOCCULATION When is use of a flocculant justified in terms of overall process economy? 1) when it results in process improvement, such as producing a clear liquor for electrolysis, precipitation, ion exchange, or solvent extraction; 2) when it results in satisfying requirements of pollution abatement ordinances; 3) when it results in increased recovery of values that would otherwise be lost; or 4) when it results in considerable savings in capital expenditure due to use of smaller equipment. When can the use of a flocculant adversely effect overall process economy? 1) when it results in increased filter cake moisture, 2) when it results in decreased filtration rates, 3) when it results in considerable bulking of sedimentation underflow, 4) when it contaminates either the supernatant or sludge, or 5) when the cost of using the flocculant is greater than the savings due to its use. First step in consideration of flocculants for a given application is establishment of desired goals in terms of increased clarity of effluent, increased recovery of solids, or decreased size of equipment. The most economical solution to a solid-liquid separation problem is that combination of equipment and flocculant costs which meets the established goals at the lowest total annual expenditure. This economic decision can be made only after technical data has been obtained as outlined in next four sections. TYPES OF FLOCCULATION Flocculation is a process wherein individual particles are united into more or less tightly bound agglomerates or flocs, thereby increasing effective particle size of solids suspended in a liquid. Degree of flocculation of a suspension of finely divided solids in a liquid is controlled by a combination of probability of collision between particles and probability of adhesion after the collision has occurred.' Probability of collision can be increased commercially through use of a paddle-type flocculator, combination flocculator, and clarifier or flocculating-type feedwell. Probability of adhesion usually can be increased by addition of a reagent known as a flocculant. Reagents act as flocculants through one or a combination of three possible mechanisms. The first is electrolytic neutralization of inter molecular repulsive force due to Zeta potential. This neutralization enables Van der Waal's cohesive force to hold the particles together after they collide.' The second is the precipitation, within a definite pH range, of voluminous metallic hydroxide flocs which entrap fine particles. This process is known as coagulation.14 Third is the bridging of two or more particles by either natural or synthetic long-chain, high-molecular-weight organic polymers. This bridging is accomplished by adsorption of two particles at different sites on the same molecule or by bonding of two molecules, each adsorbed to a different particle. Considerable effort has been expended in explaining the action of these polyelec-trolytes and detailed accounts are available in the literature. CHOICE OF FLOCCULANTS It is impossible, at the present time, to specify the optimum type or amount of flocculant for a given application from a knowledge of the material to be treated. The standard procedure is to choose reagents or combination of reagents most likely to be effective on the slurry; then test them.' The accompanying Flocculation Compendium (Table I) contains details of all currently available reagents sold as flocculants and it should be used when selecting the group of reagents for tests. This selection can be based on information listed in columns 4 and 5. Column 4 presents industries in which each floc-

Jan 1, 1961

By R. L. Schmidt, J. D. Verhoeven

The diffusion coefficients and electrotralzsport mobilities of aluminum, gallium, and arsenic have been determined in molten germanium with the capillary reservoir technique. The diffusion coefficients are slightly higher than those determined by the solidification technique of Brirton et a1.1 It was found that aluminium and gallium migrate to the cathode in molten germanium) whereas arsenic migrates to the anode under an electric field. A possible technique for producing p-n junctions by means of electric field freezing is discussed in view of the experimental data. In the past decade or so the literature has abounded with articles concerning the solid-state properties of the semiconducting elements germanium and silicon. It is surprising by comparison how little has been published concerning the liquid-state properties of these materials. In the production of doped germanium or silicon the diffusion coefficient of the dopant in liquid germanium or silicon is an important quantity. Yet, to the best of our knowledge, no one has ever made a direct measurement of the diffusion coefficient of solutes in either molten germanium or silicon. A number of authors'-4 have determined some diffusion coefficients by the indirect technique developed by Burton et al.1 This technique appears to give numbers of the correct order of magnitude but it does depend upon a number of assumptions in the analysis and also requires prior knowledge of the viscosity of the melt. In the present work a more direct measure of the diffusion coefficients of arsenic, gallium: and aluminum in molten germanium has been made. It has been shown independently by two groups of authors5, 6 that, when an electric current is passed through the interface of a solidifying metal containing an impurity, the resulting electrotransport in the liquid boundary layer at the interface offers a mechanism for control over the redistribution of the impurity accompanying the solidification. These authors show that the degree of control is proportional to the mobility, U of the impurity atoms in the liquid boundary layer, where the mobility is defined as the drift velocity relative to the solvent per unit electric field. In principle the results apply to the solidification of a doped semiconductor and offer an interesting technique for control of the doping of a semiconductor. In the present work the mobilities of aluminum, gallium, and arsenic were determined in molten germanium in order to evaluate the potential usefulness of electro-transport as a technique for solute control when applied to the solidification of doped germanium. EXPERIMENTAL PROCEDURE Both the diffusion coefficients and the mobilities were measured using high-purity alumina capillaries and a resistivity technique for analysis. A schematic diagram of the electrotransport apparatus is shown in Fig. 1 and the details of the cell design are shown in Fig. 2. For the mobility experiments electrical contact with the bottom of the capillary was made with graphite, as shown in Fig. 2. In order to prevent electrical contact with the melt the graphite was coated with a thin layer of alumina using a plasma spray torch. The cell assembly, a graphite electrode, and another assembly containing two blank capillaries were fastened to the lavite disk shown in Fig. 1. To make a run the system was evacuated and the doped germanium was outgassed at the operating temperature of 1030°C. The cell and blank capillaries were then submerged beneath the melt and a slightly positive pressure of helium was introduced to fill them. After passing current through the cell for a given time the cell and blank capillaries were raised from the melt and the furnace was shut off. The temperature of the cells dropped below the freezing point of germanium within 1 to 2 min after the furnace was shut off.

Jan 1, 1968

By T. E. Seidel, A. U. MacRae

The dependence of the electrical and crystalline properties of silicon containing ion implanted boron atoms have been studied as a function of the incident dose, substrate temperature, and annealing tempera-ture. Hall effect studies show that the compensation due to defects is negligible after annealing at and above 500°C for a dose of 1013 ions per sq cm. Steps occur in the isochronal annealing curve for the sheet resistance at 300°C and 800°C and the mechanisms responsible for these steps are discussed. The range of the ions at 150 kev is 3500 * 5001. Electron diffraction studies on samples implanted with 150 ker ions show the existence of damaged (polycrystalline) silicon closer to the surface than the range of the ions. Etching and subsequent annealing of etched and unetched specimens suggest that the poly crystalline silicon is closer to the surface than the bulk of the distribution of ions. THE purpose of this study is to investigate some electrical and crystalline properties of ion implanted boron in silicon. Sheet resistance, Hall measurement, depth distribution by chemical staining, thermal probe and electron diffraction have been used to study the properties of samples implanted in a random direction with ions having energy up to 150 kev. The boron-silicon system has been the subject of considerable study'-7 due to its possible application in the fabrication of electronic devices. The implanted ions produce considerable crystalline damage to the substrate crystal before they lose most of their primary energy and come to rest. Fortunately, most, if not all, of this damage can be removed by subsequent annealing or by holding the substrate at an elevated temperature during the implantation process. Sheet resistivity measurements of the p-type layers produced by boron implantation into room-temperature silicon, reveal that the annealing occurs in a two-step process: the first occurring at -300°C and the second at -800°C.' Electron-microscope and low-angle electron diffraction studies of this damaged material indicate that the bombarding ions produce an amorphous silicon region about the trajectory of each ion.' At high doses, these damaged regions overlap and an amorphous surface layer results. Furthermore, the 800°C annealing step, appears to be associated with the elimination of this gross damage. The depth distribution of the as-implanted and also the annealed samples have been studied by an angle lap and staining technique as well as by Hall measurements.3-7 We find the experimentally determined ranges of the boron are less than those calculated by the Lindhard-Scharff-Schiott theorys (hereafter referred to as the LSS theory). Our results are in essential agreement with pre- vious results. In addition, we have made Hall measurements on samples bombarded with a low dose (2 x 1013 ions per sq cm) to minimize impurity banding effects, and find that deep ionized levels influence the carrier concentration and room-temperature hole mobility until the sample is annealed at temperatures above 500°C. Above this temperature, the data corresponds to that obtained when silicon is doped with boron by conventional techniques. We have also made a depth distribution determination of the crystalline damage due to the implanted boron by using glancing angle electron diffraction techniques. It was found that the gross damage depth distribution of heavily implanted samples is closer to the surface than the depth distribution of the electrically active boron. By removing this gross damage, without affecting the distribution of the implanted boron, we have determined that the 800°C annealing stage is not exclusively due to the improvement in the crystalline perfection of the amorphous material but also appears to be associated with the annealing of some point defects. These results and their relation to previous results are discussed in the following sections. IMPLANTATIONS Boron ions were implanted into silicon samples using an accelerator capable of operating from 10 to 150

Jan 1, 1970

By J. B. Cheatham, C. E. Murphey

Presently, computer control of Borobolic direction cannot be obtained during drilling, and most straight-holc drilling methods attempt to resist hole deviation rather than control direction. Many of the theories advanced as possible explanations of the cause of hole deviation are Summarized berein. A new correlation of physical partables is introduced to indicate bow factors such iis drill collar stiffness clearance and hit weight influence borehole deviation, .A methord is proposed for predicting the rate of change of hole angle when drilling conditions are changed. INTRODUCTION Control of borehole direction during drilling can be difficult and costly. Unintentional crooked holes are often lrilleti in dipping formations and many times directional drilling is required when the surface location is not directly above the target area —- for example, at offshore and mountainous locations. Prilllng progress can be greatly hindered in either air or liquid drilling when it be comes necessary to use low bit weight to prevent excessive hole angle build-up. If hole inclination becomes too great, drill pipe drag becomes excessive and fishing risks are increased, logging is more difficult and problems of differential sticking, key seating and fatigue failures may be encountered. Dog-legs and key seats are more serious problems than steep inclination angles: therefore, reducing rate of direction change is preferred to attempting to maintain absolutely vertical holes. Consequently, a straight inclineti hole is preferable to a nearly vertical crooked hole containing numerous dog-legs. In this paper, theories of the cause of hole deviation and analyses of drill string behavior under down-hole conclitions are summarized. Methods for computing hole deviation are presented und systems for resisting deviation as well as neans for provic!ing control of holt- direction are iliscusseI. A new correlation of physical variables is introduced tu indicate how factors such as drill collar stiffness, clearance and bit weight influence borehole deviation. A method is oroposeti for predicting the rate of change of hole anFrle when drilling conditions are clianged. IIEVIEU' OF PREVIOUS WORK ON HOIaE DEVIATION Significant progress in the theoretical analysis of hole deviation problems has been made in the past 1 5 years. The pioneering work has been primarily a result of the efforts of Lubinski and Woods.l-5 In 1950, Lubinski 1 considered the buckling of a drill string in a straig:rt vertical hole, a problem also considered by Willers6 in 1941. It wns concluded that very low bit weights must be used to prevent hole deviation resulting from drill collar buckling. The use of conventional stabilizers was proposed2 in 1951 by Mac Donald and Lubinski as a method for permitting greater Sit weights to he carried without drill collar buckling. These authors pointed out that a 2° nearly vertical spiral hole can cause severe key seatinp, and drill pine near, wilereas n 3 straight inclined hole with deviation all in one direction, while not vertical, will not result in serious drillirig or producing problems. Studies were continued with an investigation of straight inclined holes by Lubinski and Woods3 in 1953. In this paper they concluded that perfectlv vertical holes cannot be drilled even in isotropic forriations unless extremely low bit P-eights are used. .l'l~ey postulated that constant drilling conditions produce holes of constant inclination angle and varying conditions cause the hole to drill at a neiv equilibrium angle. This analysis was not concerned with drill string buckling since it was based on an equilibrium solution in which the ~irill string Was presumed to lie along the lower side of the hole abcrve the point of tangency. Weight of the drill collars below the point of tangency tends to force the hole toyard the vertical, whereas the weight on hit tends to force the hole aurav from the vertica l. The concept of an anisotropic formation Lvas introduced as an empirical method for explaining actual drilling data and as a means for extrapolating known deviation data to otiier conditions of hit

Jan 1, 1967

By O. D. Gonzalez, R. A. Oriani

The migration of hydrogen and of deuterium dissolved in a iron and in nickel induced by an applied electrical potential has been measured over a range of temperature. In all cases the intevstitial solute migrates to the cathode. The deduced charges of transport are positive, independent of or slightly dependent on temperature, and markedly larger for the beavier mass. These results are interpreted as showing predominating momenlum transfer between electron holes and the acticated complex of the elementary diffusion act. THE migration of components of a metallic system under the action of an applied electrical potential is called electromigration or electratransport. This phenomenon has been known since 1861 and is becoming of increasing interest to metal scientists because of the opportunity it offers to explore the connections between mass transport and electron transport. Until recently, reliable data have been very scarce because of the difficulties inherent in the measurements. In addition, theoretical understanding has been either nonexistent or rudimentary and at present this situation is only moderately improved. Whereas the prevalent notion had been (and is still widely held) that electromigration directly reflects the state of ionization of a component in its equilibrium state in the metal, it is now becoming clear that the major, if not the sole, factor is the momentum transfer between the charge carriers, themselves in motion because of the applied field, and the metallic components in their activated state. It becomes important therefore to obtain reliable data over a range of temperature on electrornigration in systems where only one component moves, that is, either in pure metals (vacancy motion) or in interstitial solid solutions. Our choice of systems was dictated by our measurements' of the Soret effect in solid solutions of hydrogen and deuterium in iron and nickel. Indeed, the main reason for making measurements on electromigration at all is that we suspected a mechanistic connection between thermal diffusion and electromigration. In our former paper' we proposed that what is common to both phenomena is the momentum transfer between the charge carriers in the metal and the atom as it jumps from one equilibrium position to another. In Soret diffusion, however, there is in addition the dissipation of the energy of the jumping atom via pho-nons. We have since found that similar ideas for this interconnection have been developed by Fiks.2 In the present paper we will discuss in more detail our understanding of the mechanism of electromigration itself, but we turn first to a presentation of the experiments and results. EXPERIMENTS AND RESULTS Let us consider a metallic system in which only one component, m , can diffuse at the temperature in question, and to which are applied simultaneously an electrical potential gradient, grad cp, and a chemical potential gradient, grad p,. One may write3 for the material flux Jm and the electronic charge flux Je by applying the condition, grad = 0, to Eq. [I] and evaluating grad(um/T) for the isothermal case and for activity coefficient independent of composition over the relevant composition range. ere, c is the concentration and D the diffusivity of the mobile component. The experimental technique that we have used to measure Z* for the isotopes of hydrogen individually dissolved in each of two transition metals has been developed from a method used by Wagner and Heller.4 (A somewhat similar method was also used by Herold.5) A wire or thin rod of the metal under study connects two volumes of gaseous hydrogen at identical pressures; hence grad um = 0. A direct current is made to pass through the specimen, serving to maintain the specimen at the desired temperature and also to produce the electromigration of the hydrogen dissolved in the metal in equilibrium with the gaseous hydrogen. Under these conditions, the flux of hydrogen from one volume to the other is given, from Eq. [I] for grad( um/T) =0by

Jan 1, 1968

By R. E. Collins

The existence of fluid migration across fixed boundaries in oil and gas reservoirs has been known for many years. Several techniques have been developed in the past for estimating The rate of migration across fixed boundaries as an aid in planninng field development and in the valuation of oilfied properties. The principal de/errc7nt to the use of these techniques lies in the rather extensive reservoir and field data required for ca1cula1ion.s of fluid migration. For this reason, a new, simplified procedure has been developed which makes possible the calculation of fluid migration with a minimum of field and resrvoir data. This new technique is based on certain. solutions of the differential equations describing flour in the reservoir which assume, for the portion of the reservoir of interest, that the formation can be approximated by a homogeneous rock of uniforrn thickness, that only a Single mobile fluid phase exists, and {hut fluid production at the well is solely a result of expun.rioti of rile resersoir fluds. The results of the, present work are compiled in a set of curves. These curves can he used to calculate both rule and cummulative fluid migration when the abovc assumptions ore ju.r/ifiril. The only data required for such calcu1ations are the production hisrories of all wells in the field, the permeability and porosity of the reservoir., the, compressibility and viscosity of the fluid. and the shape of the reservoir, INTRODUCTION The migration of fluids across fixed boundaries in oil and gas reservoirs has long been recognized as an engineering and economic problem, but no methods for estimating the extent of migration during the development stage of a reservoir have been published. The investigation reported here has been directed toward providing a simple technique for estimating the extent of such migration and has therefore been restricted to the simple case of a homogeneous reservoir of uniform thickncss containing compressible liquids. It is assumed that only a single mobile fluid phase exists and that fluid production at the wells is solely by expansion of the reservoir fluids. Obviously, few, if any. reservoirs conform to these assumptions during their entire productive life. On the other hand, most reservoirs approximate fluid expansion reservoirs during their initial stages of primary production. Consequently, the present work should be applicable during the field development of most reservoirs, regardless of whether or not they ultimately are gas cap, dissolved-gas, or water-drive reservoirs. The mathematical analysis of this problem has been outlined in the Appendix, while the results of the investigation are presented in the following discussion. DISCUSSION OF CALCULATION PROCEDURE SLNGLE Well, Ini-iimite Reservoir The procedure for calculating fluid migrations is based on solutions of the partial differentia1 equations describing the flow of a homogeneous compressible liquid in a homogeneous reservoir of uniform thickness. This differential equation has the form of the well-known diffusion equation. The equation, as applicable to our problem, is where p is fluid density, is porosity, EL is viscosity, c is compressibility,* and k is permeability; .r, y and t are the space coordinates and time. Derivation of this equation is given in the Appendix. The analytical solution of this equation for a single well of negligible radius producing at a constant rate. q, from a reservoir of infinite areal extent for a time, 1. can he readily obtained. From this solution the rate of flow and also the cumulative flow across a straight line segment of length, 1, at a perpendicular distance. 6. from the well can be computed. One end of the line must be on the perpendicular joining the well to the

By A. R. Elsea, E. E. Fletcher

Cast X-40 alloy with the lowest nitrogen content studied had a 100-hr rupture stress at 1500°F about equal to the reported value for the commercial alloy. Increases in nitrogen content progressively decreased the rupture strength, and with about 0.1 to 0.2 pct N a minimum strength was reached, but there was no accompanying change in microstructure. Further increases in nitrogen resulted in the fomzation of progressively increasing amounts of a lamellar, pearlitic-type structure at the grain boundaries, with accompanying increases in rupture strength, and above about 0.25 to 0.33 pct N, the rupture strength exceeded the normally reported values. Two series of melts representing different melting stocks exhibited minimum rupture strengths at different nitrogen contents. This suggests that some unidentwed trace element not removed by vacuum melting has a strong influence on the response of this alloy to variations in nitrogen content. In a series of melts with manganese contents ranging from 0.6 to 3.2 pct, the material with the lowest manganese content had the highest 100-hr rupture strength at 1500°F. The manganese variations had no appreciable effect on the microstructure. CAST cobalt-base alloys such as X-40* exhibit high strengths at elevated temperatures (1500°F and above), but they also show considerable scatter in high-temperature properties. Since the design of parts for critical applications must be based on the minimum expected properties, this broad scatter appreciably lowers the design strength of the alloy. If the relatively poor properties exhibited by a few test parts from any given group could be improved, the spread in properties would be narrowed, and the design stress could more closely approach the average expected properties. The purpose of this research investigation was to learn what were the causes of these erratic properties and, if possible, to find methods for eliminating them. Earlier unpublished work showed that vacuum melting markedly influenced the high-temperature strength of cast X-40 alloy. There were indications that this behavior may have been the result of changes in the nitrogen or manganese content of the castings. Consequently, in the current investigation, the influence of variations in nitrogen and manganese content on the structure and high-temperature properties of cast X-40 alloy was studied. In this program, X-40 melting stock was vacuum melted to produce a base material that was very low in nitrogen content and in volatile trace elements. Additions were then made to this base material to produce alloys of the desired composition. The metal was cast into investment molds producing coupons which were machined into stress-rupture bars. These bars were subjected to stress-rupture tests and me-tallographic study to determine the influence of changes in analyses (nitrogen and manganese content) on the structure and properties. Material—The melting stock used for these experi-ments was in the form of shot from two master heats of commercial X-40 alloy. Only one master heat was used in a given series of melts. Thus, any differences in structure or properties that showed up in the specimens from a given series would be the result only of the intended variations in composition. The certified analyses of the master heats were as follows: C Mn Si Cr Ni Lot No. 2 0.50 0.71 0.66 25.44 10.53 Lot No. 3 0.54 0.73 0.70 25.95 10.00 W Fe Co P S Lot No. 2 7.45 1.34 Bal. 0.011 0.013 Lot No. 3 7.58 1.53 Bal. 0.005 0.016

Jan 1, 1960

By S. W. Kennedy, M. Cohen, L. D. Calvert

A high-temperature X-ray diffraction method has been used to study the composition and the kinetics of formation of oxide scales at 800 °C on iron and pure iron-nickel alloys containing 25.6, 75, and 84 pct Ni. This technique has been combined with chemical analysis, and metallographic examination, and determination of weight-gain time curves. The 75 and 84 pct Ni alloys form a three-layer scale consisting of porous NiO next to the metal, a spinel layer, and a -Fe203 on the outside. The 25 pct Ni alloy produces a scale of spinel and Fe,O,, in which, however, traces of FeO and NiO are observed near to the metal. On all the nickel alloys the Fe20, is orieqted with the (107) plane parallel to the surfaces. The exposed surface of the Fe20, is in the form of needles whose axis is perpendicular to the specimen surface. Although the alloys show nonuniform oxidation rates as determined from weight-gain measurements, the X-ray data indicate that the total scale and individml scale layers grow uniformly and parabolically. Deep subscale formation is observed in the 25 pct Ni alloy only. This appeared to be associated with cracking of the scale and penetration of the oxygen along the grain boundaries. ALTHOUGH film formation has been investigated by high-temperature electron-diffraction techniques, for example by Gulbransenl and Hickman,' there have apparently been no investigations of scaling by methods permitting study of the scale during formation at the reaction temperature. Methods involving quenching of scales are based on the working assumption that no significant changes take place on cooling. In general, however, compounds may disproportionate, and the different thermal expansions of constituents may cause disruption of the scale on cooling. In particular, some scales cannot be quenched without spalling. These difficulties are avoided by X-ray diffraction examination at the temperature of formation. High-temperature diffraction procedures also provide a method of determining the kinetics of formation of each phase separately in a multicom-ponent scale. The scaling of binary iron-nickel alloys Containing up to 30 pct Ni at a temperature of 800°C has been studied by Benard and Moreau using cooled specimen~,~ whilst Foley, Druck, and Fryxel14 made an electron-diffraction study of cooled oxide films formed on an iron 42 pci Ni alloy. In the present work the scaling of three iron-nickel alloys containing 25.6, 75, and 84 pct by weight of nickel, at 800°C in oxygen at atmospheric pressure was investigated by X-ray diffraction techniques using a Norelco Geiger-counter diffrac-tometer. The oxidation of iron was investigated for comparison. In addition normal metallographic examinations and chemical and X-ray analyses were made, and weight-gain time curves obtained. EXPERIMENTAL Materials Used—The analyses of the alloys were as follows: Percent by Weight Nickel 25.6 pct 75.4 pct 83.2 pct Aluminum 0.004 None found 0.002 Cobalt — 0.05 0.05 Chromium — — — Silicon — 0.01 None found Carbon All less than 0.05 pct The chemical analysis of the iron was: Al— 0.002 i 0.001 pct, C—0.007 pct, Cr less than 0.001 pct, Cu—0.002 ± 0.001 pct, Mn—0.003 ± 0.001 pct, N—0.0002 pct, 0-0.013 pct, P—less than 0.0002 pct, Pb—not detected, S—0.0017 pct, Si—0.0095 pct, Sn—none detected. This iron was the same as that used to make the alloys and was obtained from the same source-Vacuum Metals Corp. One specimen of pure iron from The British Iron and Steel Research Association was used for preliminary investigation. Specimens were machined to shape from cast rod, polished (the final polish being with 600 Sic paper), degreased in trichlorethylene, washed, and etched. The etching and neutralizing procedure adopted by

Jan 1, 1960

By E. M. Elkin, J. H. Schloen

All known methods of treating and recovering the various components of copper refinery slimes are discussed. The slimes treatment processes presently used by five copper refineries are described and flowsheets are given. A bibliography is appended. THE recent increase in anode copper production at the Noranda smelter placed an additional load on the Montreal East plant of Canadian Copper Refiners Limited. The consequent increase in the amount of anode slimes led to a careful consideration of the various methods of slimes treatment. A critical review of these methods is presented here in the belief that it would be of interest to copper refiners. No such review has yet been published, although a number of individual flowsheets have been described. To make the information of greater value, a questionnaire was sent to all copper refineries. While the overall response to the questionnaire was not entirely satisfactory, the foreign refiners gave much detail in their answers and expressed willingness to cooperate further if needed. Although the data below do not cover all refineries, it is thought that examples of all flowsheets currently in use are included. A comparison of these flowsheets should prove of interest. The paper is divided into two parts. One part deals with a discussion of all known methods of treating and recovering the various components of the slimes. The second describes the processes now in use at various copper refineries for the treatment of raw slimes up to the production of Doré bullion. A brief description of the two main electrolytic methods of parting Doré bullion is appended. Since the first commercial application of electrolytic refining of copper by J. B. Elkington in 1865, the treatment of anode mud or slimes has undergone many changes. The object of treating slimes has always been the recovery and separation of precious metals. With the passage of time, increasing attention has been paid to improvement in recovery and quality of byproducts, mainly selenium and tellurium. The original methods of treatment were crude, although relatively direct. For example," the slimes were fused on a dolomitic clay bed in a reverbera-tory furnace; the slag was removed and the resulting metal cupelled to silver and gold. In another process, the dried slimes were oxidized and scorified on the lead bath of a cupelling furnace. Later, these pyrometallurgical methods were modified by sulphuric acid leaching, followed by fusion with niter in a reverb eratory furnace. A preliminary oxidizing roast improved the leaching step. Straight hydro-metallurgy has not found practical application. No matter what method is employed, the result is Dorb metal—a silver-gold alloy, with or without the metals of the platinum group. Characteristics of the Slimes Anode slimes are made up of those components of the anodes which are not soluble in the electrolyte. They contain varying quantities of copper, silver, gold, sulphur, selenium, tellurium, lead, arsenic, antimony, nickel, iron, silica, etc. The color of raw slimes is grayish black and the particle size is —200 mesh. However, Baraboshkin and Gaev (Ref. 1, p. 37), describe light gray colored slimes from the electrolysis of secondary copper which are composed predominantly of sulphates and of basic salts. In anode furnace practice primary and secondary metals are not usually segregated and such slimes do not commonly occur. Copper in the slimes originates to a large extent in the cuprous oxide of the anodes and is therefore dependent on the oxygen content of the latter: Cu2O + H2SO4 + CuSO4 + H2O + Cu [I] Opinions have been expressed that some of the copper is formed by decomposition of cuprous to cupric sulphate Cu2SO4 ? CuSO4 + Cu PI The product of either reaction is very finely divided. Depending on the slimes composition, much of the copper is combined with sulphur, selenium, tellurium, etc. The balance of the copper is in the free metallic state.

Jan 1, 1951

By I. M. Bernstein

The steady-state creep behaviov of zirconium and zivcaloy-2 was examined in the temperature vatlge 520° to 620°C A1 low stresses the creep rates were cimracterized by a linear stress dependence; at highev stresses the stress dependence was much more pronounced. Temnperature-cycling tests yielded values for the aclivation enevgy for creep. Various tlzeories were examined in the ligltt of- the experimental re-sults and it mas concluded that the low-stress creep behavior is the result of the stress-direcled diffusion of vacancies along gain boundaries. It has been observed,"&apos; usually under conditions of high temperature and low stress, that creep deformation can occur for which the steady-state creep rate is linearly dependent on the applied stress. For magnesium and certain magnesium alloys, Harris and ones&apos; and ones&apos; have argued that this type of creep occurs by mass transfer as a result of the stress-induced generation and migration of vacancies, along a gradient defined by the stress direction. Jones&apos; demonstrated that the rate-controlling diffusion path is sensitive to grain size and temperature, and that by suitable control of these variables creep could occur by vacancy diffusion either predominately along grain boundaries or through the lattice. Recently, Jones3 suggested from an examination of limited high-stress data for zircaloy-2, composition in Table I, that significant diffusion creep could occur at low stresses, at least between 375" and 500°C, controlled by grain boundary vacancy diffusion. This process could have an important implication in assessing the role of zirconium alloys as a structural or cladding material in certain classes of nuclear reactors, since it predicts creep deformation far in excess of any estimates based on extrapolating slip creep data from higher stress levels. If the diffusion creep process occurs it should be possible to describe the total steady-state creep rate of zirconium and its alloys as the sum of two terms, Eq. [I]; the first term relates to a slip creep process important at high stresses and which is manifested by a much more pronounced dependence of creep rate on stress4 than diffusion creep and the second to a process controlled by mass transfer,5&apos;6 dominant at low stresses: where A and BI are parameters which can depend on structure, Ql and Q2 are the activation energies for the particular creep process occurring, and n describes the sensitivity of the creep rate on stress. It is the purpose of this paper to present some direct experimental evidence in support of this view. It is recognized that other analytical approaches have been proposed to explain data of this kind and these will also be discussed. 1) EXPERIMENTAL PROCEDURE Flat creep specimens (gage length 1 by 0.25 by 0.02 in. approx) were prepared from cold-rolled, argon-remelted, crystal bar zirconium and cold-rolled commercial-grade zircaloy-2, the analyses of which are given in Table I. The specimens were annealed at a pressure of < 10-5 Torr at temperatures from 625" to 675°C for 2 hr and slow-cooled. This treatment produced stable grains of average size (defined here by the average linear intercept) of for zirconium and -4xin. (-10 p) for zircaloy-2. The specimens were tested in a dead load tensile creep rig. The stress was maintained constant by adjusting the applied load after approximately each 1 pct of strain. The specimen temperature was controlled to better than +1°C. This system had a small thermal lag, so that rapid temperature changes were possible. To minimize corrosion, the specimens were tested in high-purity (99.95 pct) argon, further dried,

Jan 1, 1968

By S. H. McFarlane, K. H. Zaininger, G. W. Cullen, C. C. Wang, G. E. Gottlieb

Heteroepitaxy of silicon on stoichiometric spinel has been studied. Both boron-doped (p-type) and arsenic-doped (n-type) single-crystal silicon films have been grown by the pyrolysis of silane on sioichiometric spinel (MgAl2O4) substrates prepared by a flux technique. The spinel crystals are free from strain and subgrains, and exhibit no thermal instability at temperatures employed for silicon deposition. The growth parameters of epitaxial silicon have been studied. Effects of substrate orientation, surface preparation, and growth conditions on the silicon Properties have been determined. The silicon-spinel composite was characterized by X-ray diffraction, electron diffraction, electron microscopy, and optical techniques. Information on epitaxial orientation relationship, defect structures and film-substrate interface has been obtained. A parallel orientation relationship was found between silicon and spinel. The silicon films exhibit no subgrain structures. However, growth pyramids, microtwins, stacking faults, and dislocations are the prevalent defects. The deformation of epitaxial silicon was measured by an X-ray technique. It was found that the epitaxial silicon is strained under compres-sive stress due to the thermal expansion difference between the film and substrate. The stress was estimated using the classical plate theory and beam equation. Electrical properties of the epitaxial silicon have been measured, including resistivity, carrier concentration, and Hall mobility. MIS and vertical through diffused junction structures have been fabricated wing silicon-spinel composite. Information on MIS characteristics, minority carrier life time, and junction properties has been obtained. THE achievement of single-crystal growth of large area silicon semiconductor films on oxide insulating substrates is of technical importance to many solid state electronic devices. The semiconductor-insulator composite structure is also of scientific interest because the heteroepitaxy is determined by the spatial relationship between the atomic arrangement in the substrate and that of the atoms in the appropriate crystallographic plane of silicon. The degree of crystalline perfection of the silicon deposits depends also on the physical condition of substrate surface. Epitaxial growth of silicon on commercial flame fusion Al-rich spinel (MgO:3.3A12O3) has been reported by several investigators.&apos;-4 The lattice of spinel of this composition is distorted. The material cracks and exsolves the excess alumina in the lattice at temperatures (-1200°C) used in fabricating silicon devices. Stoichiometric MgA12O4 spinel exhibits neither lattice distortion nor thermal instability. Results are given on the epitaxial growth and characterization of silicon on stoichiometric spinel. EXPERIMENTAL Fabrication of Silicon-Spinel Composite Structures. The MgA12O4 spinel substrate wafers were prepared from bulk single crystals grown at about 1200°C by a flux technique5 using a PbF2 flux. The crystals are free from strain and subgrains, and exhibit a typical dislocation density of less than 50 lines per sq cm. The crystals are thermally stable without cracking and exsolution of alumina to at least 1500°C. The spinel crystals were oriented for cutting by the Laue X-ray back-reflection method.6 Substrate wafers (about 25 mil thick) of (Ill), (loo), and (110) orientations have been obtained bu cutting the X-ray oriented crystals using a standard type diamond wheel. An accuracy of better than 1/2 deg is maintained throughout the operation. The spinel substrate wafers were mechanically lapped and polished to produce the flat and smooth surface which is required for silicon epitaxy. Lapping was carried out with about 30-µ boron carbide abrasives to obtain a flat coplanar surface. The lapped surface was further polished using successively finer grades of alumina, ending with the 0.3-µ grade. After polishing the wafers generally have a flatness of ±0.4 µ per cm, as revealed by interferometry. Fig. 1 shows (111) oriented MgA12O4 spinel wafers of various shapes.

Jan 1, 1970

By H. E. Lee, P. C. Feddersen

Greenockite is the only known cadmium mineral of importance. It occurs rather universally, in minor concentrations, as a secondary mineral in sphalerite deposits. The world&apos;s cadmium output is obtained through the processing of metallurgical by-products, largely from the treatment of residues from electrolytic zinc, retort zinc and lithopone plants. These sources are supplemented by the processing of fumes from lead and copper smelting operations. The development of modern selective flotation practice in the decade 1920-1930, which permitted the economical mining of complex lead-zinc ores, resulted in significant increases in the quantities of cadmium entering lead smelting systems. Being closely related to zinc as to occurrence, properties and production, most detailed description of cadmium recovery methods are to be found recorded in connection with zinc metallurgy. Other than occasional articles pertaining to particular operational procedures, literature offers but little in the nature of a balanced survey of lead smelter cadmium recovery practices. While many of the basic operations described for the recovery of cadmium from zinc by-products are applicable to the treatment of lead plant products, the inherent problems involved differ widely. In general the cadmium content of related by-products from routine lead smelting operations is present in lower concentrations, exists in a less soluble state and is associated with both a greater quantity and a greater variety of detrimental impurities. To cope with these problems, lead smelter practices are found to follow the general outline: Preparatory Processing 1. Concentration operations 2. Sulphation operations Cadmium Plant Processing 1. Leaching operations 2. Purification operations 3. Sponge precipitation operations 4. Metal recovery operations 5. Refining and casting operations As in the case of related zinc plant operations, cadmium recovery practices at lead smelters are not standardized. They not only vary as to type, but also extent. Depending upon prevailing conditions, lead smelter cadmium operations range from simple concentration campaigns, for the purpose of sufficiently "up-grading" products for shipment elsewhere, to complete processing steps for the production of refined metal. Preparatory Processing The cadmium content of lead smelter receipts is low and, as a rule, proportionate to the zinc content; the usual range of cadmium contained being of the order of 0.01-0.05 pct. Were it not for the low boiling point of cadmium, such small concentrations would, no doubt, be lost in the large tonnages of slag, metal and other smelter end products. However, the ready volatility of cadmium and its compounds at prevailing lead smelting temperatures results in its concentration in fractional portions of fume collected. This collected fume comprises a circulating load within the smelter system. Thus, the cadmium content of blast furnace fume* increases with each successive circulation until an equilibrium value is reached when the sum of the cadmium losses, due to handling and in slag, waste gases and other end products, becomes equal to the intake as ore. With ore receipts averaging, say 0.03 pct cadmium, the concentration value obtainable, through fume circulation in a routine manner, approaches 10-12 pct. In such operations, cadmium concentrations in blast furnace fume of from 3-5 pct are readily .attainable. However, the concentration gain beyond this range, with each additional circulation, is progressively decreased as a result of mounting losses occurring through handling and in end products. Therefore, to avoid excessive cadmium loss and to enhance the ultimate concentration anttainable, it is customary practice to isolate blast furnace fume at some intermediate cadmium content for special concentration procedure. The most common type cadmium concentration "campaign" involves special smelting operations wherein a relatively high portion of blast furnace fume at 3—6 pct cadmium is incorporated into the sinter charge. This type practice is roughly illustrated by the diagram on p. 111. Cadmium fume collected from lead blast furnace operations is not amen-

Jan 1, 1950

By H. Wilton Clark

VARYING in thickness and in number from place to place, coal seams in the Canadian Rockies also range in pitch from nearly horizontal to vertical, sometimes with overturns. Over the entire coal-bearing area there are considerable differences of rank in coals of the same geological age, and there are marked differences in ash content and wash-ability characteristics. Correlation of seams at mining operations within a few miles of each other has often proved impossible. These factors influence mining methods, and, of course, production results. The oldest coal formations of western Canada are of Lower Cretaceous age, as the carboniferous sediments are marine and contain no coal. Coal is also present in formations of Upper Cretaceous and Tertiary ages. The rank of coal varies from semi-anthracite in some operations in the Kootenay and Luscar formations of the Lower Cretaceous in the Rockies to lignite in the Tertiary fields of the Saskatchewan prairies. Fig. 1 shows the general extent of the formations. The pitching seams, chiefly Lower Cretaceous, occur in the western belt of the Rocky Mountain foothills and the eastern slopes of the Rockies themselves. (The road to Tent Mt. strip pit, elevation 7000 ft, is shown on p. 832.) Formations extend from the U. S.-Canadian boundary for several bundred miles in Alberta and continue for a similar distance in British Columbia. Present geological estimates show a probable reserve of the order of 25,000 million tons of coal ranging from high volatile bituminous to semi-anthracite, with a large percentage of coking coal, constituting one of the major world reserves of that type. It should be noted that although the quoted estimate probably errs on the conservative side, the question of access to the seams in a mountainous terrain will always be a problem; a wide divergence may exist between actual reserves and the quantities of coal economically recoverable. An excerpt from the Canadian government Report of the Royal Commission on Coal 1946 states that conditions favorable to coal formation were intermittent and these intervals relatively brief in comparison with periods in which no coal was formed. Conditions were favorable to the growth or accumulation of vegetation in one area, while fresh water sediments and marine shales were being deposited in other areas. During periods of emergence the coal deposits were subjected to erosion or were covered by coarse sands and gravels from the mountains, whereas during submergence they were covered by fine clays deposited in embayments of the sea. During some of the periods of coal formation, volcanic activity deposited beds of fine volcanic ash and dust with the coal-forming vegetation. Coal deposits reach their greatest development in the mountains and thin rapidly to the east into the plains area, where they are deeply buried beneath younger sediments. For example, in the Fernie area of southeastern British Columbia there are in places 22 seams having an aggregate thickness of 150 ft in a stratigraphic interval of 3500 ft, whereas at Cole-man in the Alberta Crowsnest area the measures are only 800 ft in thickness and contain a maximum of five seams aggregating about 47 ft of coal. At Belle-vue, 10 miles further east, the measures are reduced to 430 ft with only three seams aggregating about 37 ft of coal. Subsequently the tremendous forces involved in the upthrust of the Rocky Mountains produced great displacement of the coal-bearing formations and at the same time a change in geologically young coals from low to high rank. The floor or footwall of most seams consists of carbonaceous shales, which are almost as adaptable to bending as the coal seams themselves. The seams show very few cleats or cleavage planes and have been so weakened structurally that as mined 50 pct or more will pass through a ¼-in. screen, seldom

Jan 1, 1955

By L. S. Darken, H. A. Wriedt

An investigation has been made of nitrogen absorption by the lattice defects in a low-carbon steel afte~ Plastic deformation. Specimens in which defects were distributed by various combinations of cold rolling and vacuum heat treatment were equilibrated with controlled ammonia + hydrogen mixtures at 300° to 450°C to study the relation between the solubility and the thermodynamic activity of nitrogen. The results are interpreted in terms of nitrogen being absorbed upon two different types of defect sites, called A sites and B sites. The concentrations of these sites are calculated for specimens with various histories of straining and annealing; and the thermodynamic relations descrihing the equilibrium distribution of nitrogen among the A, B, and ordinary interstitial sites in ferrite are evaluated as follows: THE generalization that the solute atoms in a solid solution interact with imperfections in the solvent lattice is now universally recognized and the subject of an extensive literature. All types of imperfections—point, line, or surface—exhibit these interactions, but the relative importance of each type depends upon its concentration, the strength of its interaction with the particular solute atom, and whether the interaction is attractive or repulsive. The strength and sign of the interaction vary with the vectorial displacement of the solute atom from the imperfection in the crystal. The concentration of lattice defects increases during plastic deformation and the effect of the imperfections upon the solute atoms is usually perceived only after cold work or irradiation. Two experimental methods have previously been used to observe the effects of interaction between nitrogen atoms and lattice imperfections in a iron. Internal friction, which was first used for this purpose by Dijkstra,1 has been applied more often than the electrical-resistivity method of Cottrell and Churchman.2 The method of the present investigation has not been used before.* Uniform specimens of steel with a metastable defect structure are produced by cold rolling and subsequent heat treatment below the recrystallization temperature. Variations in the defect structure are obtained by varying the amount of strain and the heat-treatment conditions. The specimens are then saturated with nitrogen at moderately elevated temperatures in ammonia + hydrogen mixtures having various thermodynamic activities of nitrogen below saturation with Fe4N. From the nitrogen contents of analyzed samples, the metastable equilibria of interactions between the defects and nitrogen can be established and the concentration of sites for nitrogen atoms in the lattice defects calculated. A steel was used in the present experiments instead of purified iron or iron alloys because the amount of nitrogen absorbed at defects is larger in the steel over a much wider range of experimental conditions and could therefore be measured more accurately. The effect of alloy composition is discussed in Part II of this paper; it is sufficient to say here that impurities and phase heterogeneity in ferritic alloys favor the generation and/or retention of larger defect concentrations during plastic deformation and annealing at 300° to 500°C. MATERIALS AND EXPERIMENTAL PROCEDURE The experimental specimens were prepared from stock of a low-carbon steel, which will be called "X steel" here, with the composition: C, 0.12 pct; Mn, 0.43 pct; P, 0.010 pct; S, 0.034 pct; Si, 0.007 pct; As, 0.086 pct; Cu, 0.022 pct; Ni, 0.009 pct; Cr, 0.003 pct. The stock was all from a single ingot made by the basic open-hearth process, which was hot-rolled to strip 0.080 in. thick.. This hot-rolled strip, given the code designation "XH", was the starting material for preparing a series of cold-rolled sheets. The latter are designated "XC27",

Jan 1, 1965

By J. A. Musselman, P. F. Gnirk

A study was made of indexed penetrations by a single dull bit tooth under statically applied loads into rock subjected to confining pressures from atmospheric to 5,000 p.si and atmospheric pore pressure. Experimental results obtained with a 45" wedge tooth over the above range of pressures are presented for two limestones and a sandstone, a variely of indexing distances and two degrees of tooth dullness. The optimum distance between successive bit-tooth penetrations required for maximum rock damage and chip formation decreases substantially with increa.sing confining pressure above the brittle-to-ductile transition pressure of a particular rock. However, the distance remains approximately constant for a variation in confining pressure below the transition pressure. At a given confining pressure, the bit-tooth force required lor chip formation is constant for indexing distances greater than optimum, but generally decreases linearly with decreasing indexing distance for distances less than optimum. The chip-formation force data obtained at confining pressures for which the chip-generation mechanism is macroscopic-ally of a pseudoplastic nature compare favorably with previous theoretical results for indexed dull hit-tooth penetrntion into an idealized, rigid, perfectly plastic rock. INTRODUCTION To study the cutting action of a roller-cone bit, the interaction of a penetrating bit tooth with craters formed in a rock surfacc by the passage of previous bit teeth must be considered. Current knowledge of the basic mechanics of bit tooth-rock intcract:on under simulated borehole environmental conditions has been extensively reviewed.&apos;,&apos; Particularly of current interest are the effects of bit-tooth shape, distance between successive penetrations and differential pressure at the rock surface on the extent of the interaction. Pertinent to this paper are results of an experimental investigationb f the interaction between successive penetrations by sharp, wedge-shaped bit teeth. It was demonstrated that both bit-tooth angle and differential pressure influence the extent of rock damage between successive bit-tooth penetrations. Specifically, the optimum or minimum distance between successive penetrations required for maximum interact&apos;on or chip generation tends to decrease with decreasing bit-tooth angle and increasing differential pressure. In addition, at differential pressures on the order of 2,000 psi for four va- rieties of limestones and sandstones, the macroscopic mechanism of chip formation exhibits a transition from brittle to ductile. In this paper, experimental consideration is given to successive or indexed penetrat ons by wedge-shaped bit teeth. Since pore pressure in a rock sample is maintained at atmospheric pressure, the differential pressure at the fluid-rock interface is equal to the confining pressure. The degrees of bit-tooth dullness include teeth with flat and round apexes (Fig. 1). Of primary concern in this paper are the bit-tooth forces required for chip formation, the macroscopic mechanism of chip formation and the minimum distance between successive penetrations, i.e., optimum indexing distance required for maximum rock damage, as functions of differential pressure. Of further interest is a comparison of actual bit-tooth chip formation forces at elevated differential pressures with calculated forces from previous theoretical results4 for indexed dull bit tooth penetration into a rigid-plastic rock. EXPERIMENTAL APPARATUS AND PROCEDURE The experimental apparatus consists of a pressure vessel equipped with a piston through the side of the vessel (Fig. 2). A single bit tooth inserted in the lower end of the piston is forced at a desired rate into the rock when the ram pressure chamber is pressurized. Electrical instrumentation incorporated into the apparatus yields a graphical plot of force on the piston as a function of bit-tooth penetration or displacement into the rock. Since the piston and ram assembly are in force equilibrium for a constant confining pressure in the main vessel, the fluid volume in the vessel remains constant during bit-tooth penetration. Hence, the force resisting penetration of the tooth is independent of the force exerted on either end of the as-

By J. J. Gilman

Zinc monocrystals, when compressed nearly parallel to their basal planes (within 20), deform in a new way; and certain deformation markings, called "-bands," are typical of this new mode. Characteristics of these bands are described. Mechanical behavior of low angle zinc monocrystals was investigated in some detail. Recrystallization did not occur upon annealing of banded specimens that were free of deformation twins. -Bands do not seem to be the result of nonbasal slip, but rather, a result of a microbuckling mechanism. u-Bands differ qualitatively and quantitatively from ortho kink bands. A dislocation model, consistent with some of the features of u-bands, is described. THE plastic deformation of zinc monocrystals with slip planes (0001) nearly parallel to the stress axis was studied in this investigation. In a previous investigation, it was shown that some low angle zinc crystals (those with slip planes making angles of more than about 2.5+1° with the compression axis), deform by ortho kinking while others (those with slip planes making angles of less than 2.5+1° with the compression axis) deform in a new way.&apos; This new mode of deformation will be described in some detail here. Some of its striking features are: 1—it operates only for compressive stresses, 2—its temperature dependence is anomalous, and 3—it exhibits a new type of "yield-point" behavior. The mode of deformation to be discussed is not new in the sense that no previous evidence of its existence had been reported. The markings that it creates on the cleavage surfaces of zinc crystals have been described by several investigators.&apos;" However, this is the first time that it has been made to operate under controlled conditions so that its response to mechanical variables, temperature, and aging treatments could be investigated and its geometry completely described. Apparently. Jillson&apos; as well as Holden3 and Pratt" believed that the small bands they observed were simply small versions of ortho kink bands. In fact, two of these authors3,6 "alled the markings "micro kink bands." In spite of the precedence, it is felt that this term is not entirely suitable because these bands do not have the same genesis as kink bands, and they are qualitatively different in structure. As will be indicated by later discussion, the bands seem to be related to the tensile deformation bands observed in aluminum. The present author has chosen to call the bands "micro deformation bands," or simply ",ubands," and the deformation process, &apos;&apos;p-banding." Experimental Methods Crystals were grown from 99.999+ pct Zn obtained from the New Jersey Zinc Co. The details of the technique are given elsewhere." It should suffice to say that the crystals were seeded for orientation control, and precision pyrex tubes were used for molding them. About 40 crystals were used, yielding some 130 specimens. Fig. 1 illustrates the typical form of the specimens and shows how the orientation angles are defined. The crystal specimens were usually 1 3/4 in. long and about 150 mil in diameter. The angle between the slip or cleavage plane (0001) and the specimen axis is designated by xo, while a is the angle between the maximum slope of the (0001) plane and the nearest close-packed direction [1210], vary ing from 0°to 30°. The crystals were cut into specimens with a jeweler&apos;s saw and the ends were squared by filing (specimens held in V-block). Crystals of this orientation are stiff toward bending, so this procedure introduced only deformation localized at the ends. Then the specimens were polished either chemically in 50 pct HNO³ or electrolytically in 20 pct chromic acid. The mechanical tests were made with an Instron testing machine. This machine weighs by means of electric strain gages on elastic bars and is quite stiff, since the full-load deflection of its load cells is at most 0.002 in. Most of the testing was done at a

Jan 1, 1956

By J. Weertman

It is shown that conditions suitable for the conversion of straight dislocations into helices are common in crystals hardened either through long-range dislocation interaction or by jog formation on dislocation lines. For dislocations other than screw dislocations or dislocations nearly screw in orientation, helices can be formed with the aid of core difhsion at temperatures low relative to the melting point of the material. It is assumed that, once formed, helices will degenerate into dislocation tangles. THE dislocation tangle is one major dislocation arrangement observed by the transmission electron microscope which had not been predicted previously from dislocation theory. Since first being observed, the tangle itself has become important in applied dislocation theory. The Cambridge school (P. Hirsch) bases part of its theory of work hardening upon this phenomenon.&apos; In spite of the fact that the tangle obviously is a structure of prime importance to a cold-worked crystal, until recently relatively little attention has been paid to the question of exactly why or how tangles arise. It was generally assumed at first that cross slip and perhaps jog formation will lead to tangles. However Wilsdorf and schmitz2 concluded that cross slip cannot markedly contribute to the tangles. The Wilsdorfs and Maddin3&apos;* have proposed that tangles arise by means of prismatic dislocation loops and superjogs which are produced by a precipitation of point defects. Dislocations with superjogs or which have joined with prismatic loops are themselves dislocation sources and they can produce new dislocations, a process they call "mushrooming", which then tangle with each other. There is no question that the Wilsdorfs et al. mechanism as well as the cross slip one can pro- duce tangles. However these may not be the only paths leading to tangle formation. In this paper we wish to consider another way tangles can form. Our work will be based on the theory of dislocation screw We wish to show that whenever a crystal is cold-worked there always is present a "driving force" leading to helix formation and thus to tangle formation. We do not expect to observe well-developed, regular helices in cold-worked metals. Rather we would expect that after a helix is formed random interactions with nearby dislocations will cause a well-developed helical dislocation to go over into an irregular form. A dislocation tangle is, of course, a grouping of dislocations with irregular forms. Therefore we feel that, in accounting for the formation of dislocation tangles, it is sufficient to show that many dislocations in a cold-worked crystal will take on helical form. The crucial step is helix formation. In order to have a straight dislocation assume a helical form, diffusion of vacancies, or interstitials, must occur. Our discussion of tangle formation therefore will be limited to crystals which have been deformed at temperatures ranging from about one fifth to half their absolute melting point. In this tem per a ture range appreciable core diffusion is possible. (There is no problem in explaining tangle formation at temperatures greater than half the melting point. At such temperatures dislocation climb through a bulk diffusion of point defects gives an extra degree of freedom to dislocation motion. This extra freedom of motion makes tangle formation easy.) At temperatures much below one fifth the absolute melting temperature diffusion processes are sufficiently slow that helix formation does not occur. Of course helix or tangle formation could occur in material deformed at very low tempera-tures which was subsequently warmed in order to make the thin specimen necessary for electron-microscope examination. Since within the temperature range of approximately one fifth to half the melting temperature the diffusion of point defects in the core of the dislocation is rapid, we can reasonably assume that within

Jan 1, 1963