By A. U. Seybolt

In part 111' of this series it was shown that during the selective oxidation of a 3 1/4 pct Si-Fe alloy in damp hydrogen, only silica, (observed at room temperature) as low cristobalite or low tridy-mite or both, was formed as an oxidation product. In some in- „ stances where the film was fairly thin (probably well under 100A) there was some suggestion of an amorphous form of SiO2. The present investigation of oxidation rate showed that the selective oxidation of silicon-iron can be rather complicated, and apparently impossible to rationalize in an unequivocal manner. In some temperature regions, notably near 800" and 1000°C, the data seem to obey the familiar parabolic rate law. However, at intermediate temperatures complications were noted, some of which are possibly due to the order-disorder reaction in the silicon-iron solid solution. IN an earlier report' it was shown that during the oxidation of 3 1/4 pct Si-Fe alloys in H2O-H2 atmospheres only silica films were formed in the temperature range from 400° to 1000°C in hydrogen nearly saturated with water at room temperatures, or at dew points as low as -45°C. In the work to be reported here, some observations are made on the rate of oxide film formation. As in the earlier investigation, electron diffraction patterns generally showed either low tridymite or low cristobalite or both, except for some very thin films. These sometimes showed diffuse rings, presumably due to a very small crystallite size, or in a few cases, diffuse bands probably caused by an amorphous film. EXPERIMENTAL PROCEDURE Vacuum-melted silicon iron made of high-purity materials was rolled into strips 0.014 in. thick, and cut into samples 1/2 in. wide by 1 in. long. Chemical analysis showed 3.2 pct Si and 0.002 pct C. All samples were surface abraded with 600-grit paper, were solvent cleaned, and then placed in an paper,apparatus containing a "Gulbransen type"2 micro-balance. Here the gain in weight of the samples of about 5 sq cm area could be followed as a function of time during the oxidation caused by the water in atmospheres of various controlled water-hydrogen ratios. The water-hydrogen ratios can most easily be described as varying from a dew point of 0°C (PH2O-p^2 = 6.2 x 10-3 , to K (P j -40°C (PH2O/PH^= 1.3 X 10-* Most of the experiments were conducted at the 0°C dew-point atmosphere because drier atmospheres caused so little gain in weight that the accuracy of measurement was poor. Because of this, only the data obtained at PH2O,/P,,,= 6.2 x X3 will be reported. The temperature range extended from 800" to 1000°C; and most of the oxidation runs lasted for about 24 hr. The reproducibility of any reading was about ± 1 ?, but the sensitivity of the balance was about 0.2 ?. The atmosphere, flowing at 200 cm per-min, was preheated to the furnace temperature before contacting the specimen. While the gas flow caused a measurable lift on the sample, it was ordinarily sufficiently constant so that it was not an appreciable source of error. X-ray and electron diffraction checks of the samples before and after oxidation showed no evidence of preferred orientation, either on the metal samples or on the silica films formed. EXPERIMENTAL RESULTS The data obtained are summarized in Table I, and some are given in detail in Figs. 1 to 4. In the fourth column of Table I, kp refers to the parabolic rate constant in the expression (?/cm2)2 = kpt + c [1] where ? = micrograms gain in weight kp = parabolic rate constant in units r2 /cm4 t = time in minutes c = constant It will be noted that in many cases no value for kp is given; this is because in these instances the data did not obey the parabolic rate law. The silica film thicknesses given in the last columns are values calculated from the weight gain, an average tridy-mite-crystobalite density, and by assuming a perfectly plane surface. Fig. 1 shows the data plotted in the form of Eq. [I], hence a linear plot indicates parabolic behavior. It has been frequently observed in the literature that

Jan 1, 1960

By H. R. Spedden

As part of its broad program of educational assistance-including grants, fellowships, and scholarships -Kennecott Copper Corp. offers summer employment opportunities for college students at each of its operations. Originally, summer job programs were intended primarily to help students defray their educational expenses. But as the nation's economy expanded with increased production and a growing demand for well-trained engineers, summer employment became an important means to help qualify future professionals and fill industry's need for them. Both the employer and the student thus derive benefits from such training.

Jan 6, 1967

By F. E. Bash

Previous to the war, this country depended on Europe for its supply of a number of alloys of great importance in the manufacture of electrical apparatus and equipment. When this source was cut off shortly after the beginning of hostilities and the small stocks in the United States were exhausted, either inferior substitutes had to be used or the manufacture of the apparatus suspended. Since electrical equipment was of primary importance in the prosecution of the war, the substitutes had to be used until the composition and processes of manufacture of the alloys could be determined. Included among these alloys was one generally known as manganin, which is composed chiefly of copper and manganese and which, beside having a low-temperature coefficient of resistance, has a low thermal electromotive force against copper. These qualities make it valuable for the manufacture of electrical instruments and machines in which it is used in the shape of wire, rod, and strip. As a result of these circumstances, an investigation was started to determine how manganin could be made on a commercial basis so that a product of uniform quality and the necessary electrical characteristics could be produced. The object was to procure an alloy with temperature coefficient of resistance not greater than 1 X 1X per " C. and a thermal e.m.f. against copper no greater than that of the imported material. It is characteristic of manganin that the temperature-resistance curve is not a straight line but has a peak, which varies in position with different samples; it is most desirable, however, to have it at a temperature of 25' C. if possible. The coefficients of manganin from all records available ranged from a large negative to a large positive value. The composition as reported by different authorities is given in Table I. Prof. Matthew A. Hunter, of Rensselaer Polytechnic Institute, made up a number of small melts of manganin in a graphite crucible and the one that he reported as having the best cocfficient gave the following analysis: Copper, 83.6 per cent.; nickel 2.5 per cent.; manganese, 13.6 per cent.; iron, 0.3 per cent. An analysis of a sample of German manganin gave the following: Copper, 82.6 per cent.; nickel, 3.8 pcr cent.; manganese, 12.8 per cent.; iron 0.7 per cent.

Jan 1, 1921

By Robert G. Woolery, S. Ramachandran, James A. Weber, Donald J. Hansen

Union Carbide began looking seriously at heap leaching in 1971. At that time some 1.6 million tons of mineral averaging 0.40 kg U3O8 /t) (0.80 lb U3O8) were stockpiled at various sites around the Gas Hills, Wyoming, uranium facility. Several alternatives for economically exploiting these reserves were considered and heap leaching seemed the most attractive. At the time, Western Nuclear Inc. was operating a heap leaching project nearby in which the low-grade ore was leached with sulfuric acid, the product liquor treated in an on site solvent extraction circuit, and the stripped product liquor re-acidified and recycled. The operators were most generous in allowing us to visit their site and in answering our questions. They were also helpful in discussing the problems associated with heap leaching. Their experience confirmed our belief that it was possible to operate a heap leach profitably on material too low grade for conventional milling. Based largely on what we had learned from Western Nuclear's experience, we undertook a program involving a laboratory study to determine the characteristics of the mineral stockpiles, as related to heap leaching, and to conduct a pilot heap leach adjoining our Gas Hill mill. Basically the pilot heap construction and leach procedure were similar to those described in the literature l, 2 with certain modifications to permit detailed monitoring of the operation. In May 1972, the decision was made to construct a test heap. The UCC plant at Gas Hills, Wyoming was selected as the most appropriate site for the following reasons: (1) The necessary equipment for heap construction was readily available. (2) Stockpiles of mineral from the various mining sites were on hand: (3) Construction of the heap could be made on an abandoned tailings pile minimizing problems associated with environmental approval. (4) Proximity of the mill would allow product streams to be absorbed into existing circuits. (5) Necessary utilities were available. (6) Tailings water from the existing circuit could be used for leaching. A program for the pilot heap leach was developed with the following primary objectives. (1) To confirm the data obtained in bench-scale tests particularly on uranium recovery, acid usage, and ore permeability. (2) To evaluate plastic liners used for base preparation. (3) To investigate heap configuration variables. (4) To determine heap leach amenability of the different mineral sources. (5) To establish the economics of heap leaching low-grade ores.

Jan 1, 1979

By Thomas H. Clagett

ThE Pocahontas coal field comprises the area in Tazewell County, Va. and Mcrcer and McDowell counties, W. Va., in which Nos. 3 and 4, Pocahontas seams of bituminous coal are mined. It is a mountainous region with ridges rising 300 to 1000 ft. (91 to 305 111.) above the very narrow valleys and, except for some poorly kept farms along the tops of the ridges and the area occupied by the mining and coking plants and villages, is wooded throughout. First shipments were made from Pocahontas in 1883. There are now about 100 mines, 95 per cent. of which are drift mines. At the end of 1920, approximately 298,000,000 gross tons of coal had been produced and 35,000 acres of coal mined. No. 3 seam is from 4 to 10 ft. (1.2 to 3 m.) thick, but the change is gradual and the thickness fairly uniform in any particular locality. It has a streak of bone, about 2 in. (5 cm.) thick, to which the coal adheres on both sides. In parts of the field this bone is replaced by hard slate, usually from 2 to 4 in. thick. The seam has a slate or fireclay bottom and a draw-slate top. No. 4 seam is from 65 to 80 ft. (19.8 to 24 m.) above No. 3 seam, and of minable section only in the western part of the field. It is from 3 to 8 ft. thick and has two streaks of bone, cach from 1 to 2 in. thick. It has a fireclay or slate bottom and is overlaid by from 4 to 24 in. of a laminated coal and slate, locally termed "black rash," which is separated from the coal seam by about 3 in. of slate. This "black rash" averages about 2.5 per cent. ash, but contains some clean coal. The coal in both seams is quite soft. Cleavage sufficieiltly well defined to exert an influence on the mining is rare. Overlying strata arc slates, shales, and sandstones, the sandstones predominating, extending from 30 to 1000 ft. above No. 3 seam. The strata directly above the draw slate of No. 3 seam, or "black rash" of No. 4 seam, and up to the first sandstone are usually slates or shales, about 10 ft. thick over the.

Jan 1, 1923

By Thomas H. Clagett

ThE Pocahontas coal field comprises the area in Tazewell County, Va. and Mcrcer and McDowell counties, W. Va., in which Nos. 3 and 4, Pocahontas seams of bituminous coal are mined. It is a mountainous region with ridges rising 300 to 1000 ft. (91 to 305 111.) above the very narrow valleys and, except for some poorly kept farms along the tops of the ridges and the area occupied by the mining and coking plants and villages, is wooded throughout. First shipments were made from Pocahontas in 1883. There are now about 100 mines, 95 per cent. of which are drift mines. At the end of 1920, approximately 298,000,000 gross tons of coal had been produced and 35,000 acres of coal mined. No. 3 seam is from 4 to 10 ft. (1.2 to 3 m.) thick, but the change is gradual and the thickness fairly uniform in any particular locality. It has a streak of bone, about 2 in. (5 cm.) thick, to which the coal adheres on both sides. In parts of the field this bone is replaced by hard slate, usually from 2 to 4 in. thick. The seam has a slate or fireclay bottom and a draw-slate top. No. 4 seam is from 65 to 80 ft. (19.8 to 24 m.) above No. 3 seam, and of minable section only in the western part of the field. It is from 3 to 8 ft. thick and has two streaks of bone, cach from 1 to 2 in. thick. It has a fireclay or slate bottom and is overlaid by from 4 to 24 in. of a laminated coal and slate, locally termed "black rash," which is separated from the coal seam by about 3 in. of slate. This "black rash" averages about 2.5 per cent. ash, but contains some clean coal. The coal in both seams is quite soft. Cleavage sufficieiltly well defined to exert an influence on the mining is rare. Overlying strata arc slates, shales, and sandstones, the sandstones predominating, extending from 30 to 1000 ft. above No. 3 seam. The strata directly above the draw slate of No. 3 seam, or "black rash" of No. 4 seam, and up to the first sandstone are usually slates or shales, about 10 ft. thick over the.

Jan 1, 1923

By G. Sachs, L. J. Ebert, W. F. Brown

IT is a generally recognized fact that a steel quenched from the austenitic range and tempered to yield a structure composed of tempered martensite becomes increasingly more ductile with increasing tempering temperature. However, the conventional tensile test fails to yield any value that is sensitive to differences in behavior on tempering among the various low-alloy steels or among different heats of a particular steel. The notched impact bending test, on the other hand, has been recognized for a considerable length of time as capable of revealing differences in impact properties among various steels tempered to the same strength level (i.e., the same tensile strength in a conventional tensile test), However, this test is very complex and its significance has not been clarified up to the present time. Of its three characteristic features-the high speed, the notch, and the bending-the notch has been found by Davidenkov2 to be the most potent embrittling factor. Recent investigations on low-alloy steels3,4,7,8 have shown static notch-bar tensile tests to be more lucid and to evaluate the metal properties in much the same manner as impact tests, In an attempt to analyze the fundamental nature of this test,8 it was found possible to separate the effects of the two basic characteristics of the stress pattern introduced by the presence of a circumferential notch, the stress state and the high initial stress concentration at the notch bottom, The major conclusions drawn from these previous investigations were as follows: I. The magnitude of the triaxiality at fracture depends primarily on the initial notch depth. Its effect is a great reduction in the average ductility (contraction in area at fracture in the notched section) as compared with that observed in uniaxial tension, This triaxial stress state occurs at a point in the interior of the notch specimen, It determines the notch ductility if the notch is mild and/or the metal possesses a considerable ductility. On the contrary, brittle specimens probably fracture on the metal surface (at the notch bottom) at which point biaxial stress state is present, This biaxiality also considerably reduces the ductility of the metal. For small notch ductilities the notch strength and the notch ductility become very sensitive to embrittling factors, This is contrary to the behavior of the ductility values derived from a conventional tensile test, which are comparatively insensitive.

Jan 1, 1946

By N. S. Stoloff, K. R. Jordan

The temperatwe and grain size dependence of the mechanical avoperties of ordered and disordered Fe-49 pct Co-2 Pct V were investigated. The yield and flow stresses obeyed the Hall-Petch relationship u = ai + kd-&apos;I2. Ohdering reduced the intercept stress cjj and raised the Petch slope, k, at all temperatures. Ordering also increased the temperatwe dependence of k. The ductile to brittle transition temperature increased with order and grair~ size. Cleavage fracture was nucleation limited and the fracture stress did not zlary linearly with d-&apos;". A quantitative test of the Cottrell-Petch fracture theory (and recent modifications which consider the influence of slip mode), demonstvated that this theory is not applicable to FeCo-V. COTTRELL&apos; and etch&apos; independently suggested that a criterion for cleavage failure at the yield point, a,, based on dislocation pileups at a grain boundary or other obstacle to dislocat.ion motion, is: aYYkd&apos;I2 1 opy [ll or, equivalently, aikz,d112 +k:)bpy [2] where a, and ky are the Hall-Petch intercept and slope, respectively, 2d is the grain diameter, P is a geometric factor dependent on the macroscopic ratio between shear and tensile stress, p is the shear modulus, and y is the true elastic surface energy. When the product of quantities on the left side of the equation is equal to or exceeds that on the right, cracks should be able to nucleate and propagate at the yield stress, as shown schematically in Fig. 1. Therefore a high intercept stress, high Petch slope, or coarse grain size favors brittleness. petch3 associated the existence of a ductile to brittle transition in ferrous alloys with the temperature dependence of ai. One of the earliest modifications of the Cottrell-Petch theory was presented by ~rmstrong,~ who derived an expression for transition temperature in terms of several measurable flow and fracture parameters. The latter paper was able to rationalize situations in which the transition temperature increases with decl-easing grain size, as in the case of molybdenum,&apos; and also suggested that Ppy should be a function of grain size as well as temperature. More recently Johnston et a1.6 and Smith and worthington7 have suggested that the temperature or composition dependence ol&apos; ky must also be taken into account if there is any cha.nge in deformation mode, as from wavy to planar slip, or wavy slip to twinning, with change in temperature or solute content. Armstrong %as suggested that for hcp metals changes in o;k,dw> o;k,d1/2< / is / ^^^^ / / y_______________________________________ d-"2 Fig. l—Schematic representation of grain size dependence of yield stress, cry, and fracture stress, CTF. Intersection defined by Cottrell-Petch equation. slip mode should be incorporated in the theory through changes in the critical resolved shear stress for the slip system which controls ky. The purpose of the present investigation was to critically test the modified677 Cottrell-Petch theory of fracture in the superlattice alloy Fe-49 pct Co-2 pct V, by studying the grain size dependence of the yield and fracture stresses over a range of temperatures, in conjunction with an investigation of slip mode and fracture behavior. Previous work has shown that long range order results in a sharp decrease in flow stress, a small increase in work hardening rate and a drastic upward shift in the ductile-brittle transition temperature of F~CO-V.~&apos;~ The only comprehensive study of slip character in this alloy has been reported in a preliminary account of the present investigation.10 EXPERIMENTAL PROCEDURE The experimental work was carried out on material produced from a 10 lb vacuum melted ingot, of composition 49.32 wt pct Co, 2.09 wt pct V, balance Fe. 30-mil thick sheet samples with a 1; in. gage section were machined from cold rolled stock. The degree of cold work ranged from 85 pct for the finest grained samples to 5 pct for the coarsest grain size. Details of ingot fabrication are reported elsewhere." Equi-axed grain sizes in the range 12.7 to 75.4 p were obtained by annealing for varying times at 850°C. (Re-crystallization annealing time, rather than temperature , was varied to control grain size to insure that samples of all grain sizes contained equivalent quenched-in vacancy and interstitial concentrations.) Grain sizes were measured by the line intercept method on several specimens of each grain size. Following recrystallization, all samples were disordered by quenching into iced brine.

Jan 1, 1970

By Y. C. Liu, W. R. Hibbard

An aluminum single crystal cold-rolled from (110) [1121 essentially retains its initial orientation after 99.6 pct reduction in thickness. The orientation of the recrys-tallized grains of this material can be described in terms of crystallographic rotations about principal poles of deformation texture. DURING the study of the recrystallization of a copper single crystal cold-rolled from a (110) [112] initial orientation, the orientation of the re-crystallized grains could be derived by a 30" rotation of the orientation of the cold-rolled matrix about its <111> poles.&apos; The present investigation was undertaken to extend the work done on copper&apos; to an aluminum crystal also cold-rolled from a (110) [112] initial orientation. Experimental Procedure The procedure of this experiment was similar to that reported for copper.&apos; An aluminum (99.998 pct) single crystal rod* 1 % in. in diameter was grown in back-reflection technique.&apos; The specimen (1.20x 1.004x0.6787 in. thick) was then rolled along the [112] direction. The final thickness was 0.0028 in., giving a reduction in thickness of about 99.6 pet. Specimens were cut from the rolled strip with scissors, and approximately in. of disturbed metal was removed with Tucker&apos;s reagent. The rolling edge remained intact. The specimens were sandwiched between two graphite plates and annealed in a lead or lead alloy bath which was electrically heated. Pole figures were constructed using the techniques previously described.&apos; Specimens were electrolytically polished4 and etched with 47 pct HNO8, 50 pct HC1, and 3 pct of 48 pct HF. The electrolytic polishing method and etching reagent employed for aluminum specimens were not entirely satisfactory and the microstruc-tures could not be studied in any detail. Results and Discussion The octahedral pole figure of cold-rolled aluminum strip is plotted in Fig. 1. The <111> poles spread in the transverse direction approximately 8" for the highest intensity areas. The spread in the transverse direction can be related to a rotation about two <110> directions lying in a plane containing the rolling direction and rolling plane normal. The two <110> directions and a scale of rotation for the <111> poles are shown in Fig. 2. The amount of rotation is consistent for three of the four <111> poles, about 35" to 40". The discrepancy for the fourth pole is believed to be due to limitations of the film technique. Alternate inter-

Jan 1, 1956

By A. S. Grove, C. T. Sah, E. H. Snow, B. E. Deal

A summary of- several recent investigations in to the properties of the metal-oxide-silicon system is presented. A major portion of these studies makes use of the MOS capacitance-z)oltage method of&apos; analysis. The particular areas of investigation which are reported include: 1) a general survey of the electvical properties of thermally oxidized silicon surjbccs; 2) a study of ion migration through silicon dioxide films ; 3) measurements of electron and hole mobilities in surface inversion layers; 4) a study of impurity redistribution due to thermal o.ridatiotz; and 5) measurements of the rates of oxidation oj-heavily doper7. silicon. THE importance of the metal-oxide-semiconductor (MOS) system in the semiconductor industry is well-known. In addition to its importance in the "planar" device technology,&apos; the MOS structure is now also used in the fabrication of active solid-state devices. Consequently, extensive efforts have been made recently to obtain a better understanding of the characteristics of this system. A summary of some studies of the MOS system conducted in our laboratories during the past year is presented. For the most part these studies used silicon as the semiconductor, along with silicon dioxide and aluminum as the other two components of the system. Since the MOS capacitance-voltage method of analysis was used extensively in these studies, we will first briefly describe its nature and consider some of the possible causes of deviation of experimental observations from the simple theory. We will then outline the various related areas of investigation carried out in our laboratories and will briefly indicate some of the results. It should be noted that the purpose of this paper is merely to provide a brief summary of MOS studies. More detailed discussions of the various areas of investigation are given in the references cited. PRINCIPLES OF THE MOS C-V METHOD OF ANALYSIS&apos; A sketch of the MOS structure is shown in the upper portion of Fig. 1. In this case the insulating film is Si02 and the semiconductor p-type silicon. If a large negative bias is applied to the metal field plate, holes are attracted to the silicon surface. The silicon then behaves much like a metal and the capacitance measured is that of the oxide layer alone, Co. If a small positive bias is applied to the aluminum, holes are repelled and a region depleted of majority carriers is formed at the silicon surface. This depletion I-egion adds to the width of the dielectric and the measured capacitance begins to drop. With increasing positive bias, the width of the electrical depletion region increases. At some large positive bias an inzevsion regiotr is formed at the surface and additional charges induced in the silicon appear in the form of electrons in this narrow inversion region. Thus the depletion-region width approaches a maximum value and, consequently, the capacitance reaches a minimum value and then either levels off or rises again depending on the measurement frequency and the rate of equilibration of the minority carriers in the inversion layer.3 Band diagrams, along with the corresponding charge distributions, are shown in Fig. 1 for the above bias conditions. If minority carriers cannot accumulate at the surface to form an inversion region, the depletion-region width continues to increase with increased positive bias and the capacitance drops toward zero as in a reverse biased p-n junction. The effect of a work-function difference $hs between the metal and the silicon, and of surface charges per unit area Qss located at the oxide-silicon interface, is simply to attract charges in the silicon much like the applied bias. It can be shown that this results in a parallel shift of the capacitance-voltage characteristic along the voltage axis by an amount corresponding to AV = -$bIs + Qss/Co. Theoretical curves have been calculated4 giving the capacitance of the MOS structure C normalized to the oxide capacitance Co vs the quantity VG here VG is the voltage applied to the metal field plate. In Fig. 2 such calculations are shown as points for a particular oxide thickness and bulk impurity concentration for a p-type semiconductor. (For an n-type semiconductor the curves would be mirror images of these.) All three cases, i.e., low frequency. high frequency, and depletion, are indicated. Also shown in the figure are recorder tracings of the characteristics of actual devices. These characteristics have been shifted along the voltage axis to compensate the effect of surface charges and work-function difference. It is evident that agreement between experiment and theory is good. The nature of this shift along the voltage axis is

Jan 1, 1965

By C. A. Stetefeldt

The iron-ore deposits worked by this Company occur in lenses 200 to 1000 feet long and 5 to 80 feet wide, and stand at an angle of from 65&apos; to 75, with a vertical height of 250 to 500 feet, other lenses occurring below. A number of the deposits were first worked as open pits, which in some cases were carried to the depth of 150 feet, when, owing to the weakness of the walls, underground mining was adopted. While the ore was being removed from the open pit, shafts mere in several instances sunk into the foot-wall, the intention being to mine the ore with breast-stopes of an approximate height of 20 feet, followed by underhand-stopes of the same height, leaving floors between of the necessary thickness to support the walls, or to effect the removal of the ore by means of what is known as the stall system. As the work progressed, however, it was found that the walls (which are of chlorite) were too weak to permit the working of breast-stopes 20 feet high, there being frequent heavy falls of ground from the hanging and, in some instances, from the foot. The plan of following breast-stopes with underhand-stopes was, therefore, abandoned. By working breast-stopes only, but little more than one-half of the ore could be removed, and that only at an excessive cost, the ore being so hard that power-drills with 3 1/8-inch pistons . and 6-inch stroke, working under 60 pounds of compressed air, are able to drill but 8 feet in ten hours as a yearly average, while from 6 inches to 2 feet is a common result of ten hours&apos; drilling. It was plain that some other system of mining must be adopted, and it was proposed to sink by levels of 75 feet, carrying in the cross-cuts from the shafts and working out the ore each way from the shaft from foot to hanging, and from 15 to 20 feet in height. When this has been done, drift-sets consisting of caps and legs are set up the whole length of the opening and connected with the cross-cut; the necessary openings for ladder-ways and chutes or mills are timbered from

Jan 1, 1893

By F. E. Bash

PREVIOUS to the war, this country depended on Europe for its supply of a number of alloys of great importance in the manufacture of electrical apparatus and equipment. When this source was cut off shortly after the beginning of hostilities and the small stocks in the United States were exhausted, either inferior substitutes had to be used or the manufacture of the apparatus suspended. Since electrical equipment was of primary importance in the prosecution of the war, the substitutes had to be used until the composition and processes of manufacture of the alloys could be determined. Included among these alloys was one generally known as manganin, which is composed chiefly of copper and manganese and which, beside having a low-temperature coefficient of resistance, has a low thermal electromotive force against copper. These qualities make it valuable for the manufacture of electrical instruments and machines in which it is used in the shape of wire, rod, and strip. As a result of these circumstances, an investigation was started to deter mine how manganin could be made on a commercial basis so that a product of uniform quality and the necessary electrical characteristics could be produced. The object was to procure an alloy with temperature coefficient of resistance not greater than T 1 X 10-5 per ° C. and a thermal e.m.f. against copper no greater than that of the imported material. It is characteristic of manganin that the temperature-resistance curve is not a straight line but has a peak, which varies in position with different samples; it is most desirable, however, to have it at a temperature of 25° C. if possible. The coefficients of manganin from all records available ranged from a large negative to a large positive value. The composition as reported by different authorities is given in Table 1. Prof. Matthew A. Hunter, of Rensselaer Polytechnic Institute, made up a number of small melts of manganin in a graphite crucible and the one that he reported as having the best coefficient gave the following analysis: Copper, 83.6 per cent.; nickel 2.5 per cent.; manganese,-13.6 per cent.; iron, 0.3 per cent. An analysis of a sample of German manganin gave the following: Copper, 82.6 per cent.; nickel, 3.8 per cent.; manganese, 12.8 per cent.; iron 0.7 per cent.

Jan 9, 1919

By J. S. Bowles

THE martensite transformation in lithium, dis- covered by Barrett,&apos; has been studied extensively by X-ray techniques by Barrett and Trautz,² and Barrett and Clifton.V he present paper reports the results of an investigation into the metallographic characteristics of lithium martensite. Such an investigation has not been carried out before. The spontaneous transformation in lithium consists of a change from a body-centered cubic to a close-packed hexagonal structure with the hexagonal layers in imperfect stacking sequence." As far as is known at present, this transformation can be regarded as being crystallographically equivalent to the body-centered cubic to close-packed hexagonal transformation that occurs in zirconium,5 although stacking errors have not been reported in zirconium. From a study of the orientation relationships in zirconium, Burgers5 as proposed that the martensite transformation, b.c.c. to c.p.h., occurs by a heterogeneous shear on the system (112) [111]. The crystal-lographic principle underlying this proposal is that the configuration of atoms in the (112) plane of a b.c.c. structure is exactly the same as that in the (1010) plane of a close-packed hexagonal structure based on the same atomic radius. The pattern in 2v2 both these planes is a rectangle d X 2v2d where v3 d is the atomic diameter. Thus a close-packed hexagonal structure can be built up from a body-centered cubic structure by displacing the (112) planes relative to each other.* This mechanism leads to orientations that can be described by the relations: (110)b.c.e. // (0001)c,p.h.; [111]b.c.c. // [1120]c.p.h Observations confirm these relations. In zirconium, Burgers&apos; measurements indicated an angle of 0" to 2" between the close-packed directions, while Barrett&apos;s measurements on lithium indicated an angle of 3". According to the Burgers&apos; mechanism, the martensite habit plane for this transformation would be expected to be the (112)b.c.c. plane, for this plane would not be distorted by the transformation. One of the purposes of this investigation was to find out whether the observed lithium habit plane agrees with this prediction of the Burgers&apos; mechanism. Experimental Procedure Materials: The lithium was from the same purified ingot used by Barrett and Trautz.² The Bridgman technique was used to produce single crystals. To maintain a temperature gradient in the melt, during the production of these crystals, it was necessary to use a steel mould with a wall thickness of only 0.015 in. Metallographic Techniques: Lithium specimens could be given an excellent metallographic polish by swabbing them gently with cold methyl or ethyl alcohol.? The best results were obtained with methyl alcohol saturated with the reaction product, lithium alcoholate. With higher alcohols the reaction became progressively slower and the attack became an etch pit attack rather than a polish attack. Butyl and amyl alcohols were used for macroetching. After polishing, it was necessary to remove all traces of alcohol from the specimens; otherwise, on subsequent quenching in liquid nitrogen, the alcohol froze to a glassy film. The alcohol was removed with dry benzene. The benzene in turn had to be removed before quenching, but since it does not react with lithium it could be allowed to evaporate. The specimens could then be quickly quenched before they began to tarnish. This operation could be carried out in air on all but excessively humid days when it was advisable to use an atmosphere of dry nitrogen or argon. For examinations at room temperature, the specimens could be transferred directly from the benzene bath into a bath of mineral oil. In mineral oil the specimens oxidized slowly by the diffusion of oxygen through the oil but the structure remained visible for about an hour. Lithium Martensite: Specimens prepared in the manner described above transformed spontaneously to martensite with an audible click when quenched into liquid nitrogen; i.e., M, was above the boiling point of nitrogen (77°K). The disparity between this result and the M, temperature of 71°K, found by Barrett and Trautz, is probably to be attributed to the large grain size and freedom from mechanical deformation of the specimens used in the present work. The relief effects produced by the transformation did not disappear when specimens were quenched from liquid nitrogen into mineral oil at room temperature. This permitted the microstructures to be studied at room temperature where, of course, the martensitic phase was no longer present. Typical micrographs of lithium "martensite" made at room temperature are reproduced in figs. 1, 2, and 3. As anticipated by Barrett and Trautz, the microstruc-

Jan 1, 1952

By Lester Blackner

THE PROPERTY AND LOCATION THE Ray Consolidated Copper Co.&apos;s mining property is located on Mineral Creek 6 miles north of Kelvin, at Ray, Pinal County, Ariz. (Fig.. 1) . The mining claims now owned by the company consist of 126 lode claims, comprising 2,144.9 acres, containing at the beginning of operations 82,904,368 tons of 2.19 per cent. copper ore. GENERAL CHARACTERISTICS OF THE OREBODY The main orebody is a disseminated deposit in schist and porphyry formed by secondary enrichment. Its existence was proved by churn drilling, and it is at present one of the largest proved copper deposits in the world. The orebody itself covers .205 acres with an average thickness of 121 ft., and occupies a definite belt which has a northwest direction. Its length is approximately 5,000 ft. The width varies, being about 2,000 ft. at the west end and 2,500 ft. at the east, narrowing down irregularly front both ends to a few feet in the center. The thickness of the body varies greatly along the line of lode, ranging from a few feet up to 470 ft. thick. The ore horizon is not constant, but varies, following in a broad sense the topography The body in general dips slightly to the northeast, and is broken up by numerous small faults and fractures. The ore-bearing formations, consisting of mineralized schist and mineralized granite porphyry, stand fairly well and offer no difficulty in mining operations.

Jan 6, 1915

By Sheldon Rideout, E. L. Kamen, B. S. Lement, Paul A. Beck, W. D. Manly

The 1200°C isothermal sections of the following ternary phase diagrams were investigated: Cr-Co-Nil Cr-Co-Fe, Cr-Co-Mot and Cr-Ni-Mo. In all these systems the u phase was found to form extended solid solutions. Two new ternary phases of unknown structure were identified. The existence range of intermediate phases of transition elements was correlated with 3d electron vacancy concentrations. THE occurrence of extensive ternary d solid solutions in the Cr-Co-Ni and in the Cr-Co-Fe systems was described in a brief note.&apos; More recently d- solid solutions were also found in the Cr-Fe-Mo system by two independent groups of investigators.2,3 The existence of binary d phases in the V-Co and V-Ni systems, predicted in ref. 1, was experimentally discovered recently by Duwez and Baen and independently by W. B. Pearson, J. W. Christian, and W. Hume-Rothery.5 Duwez and Baen stated two general conditions for the occurrence of the d phase in alloys of the transition elements: "(1) The atomic diameters of the two metals do not differ by more than 8 per cent. (2) One of the two metals has a body-centered cubic structure while the other is face-centered cubic, at least in one of its allotropic forms." In the course of an extensive research program conducted at this Laboratory under the sponsorship of the NACA, several ternary systems, containing d solid solutions and also certain new ternary phases, were investigated. The present report describes the investigated portions of the 1200°C isothermal sections of the following ternary phase diagrams: Cr- Co-Ni, Cr-Co-Fe, Cr-Co-Mo, and Cr-Ni-Mo. It was found that the range of existence of the d phase in these four ternary systems, as well as in one of two ternary systems which were investigated by others, can be fairly consistently described in terms of electron vacancy concentrations. This supports the suggestion of Sully and Heal" that the d phase is an electron compound. Experimental Procedure The ternary alloys were prepared by vacuum induction melting in zirconia and alumina crucibles. Lot analyses of the metals used are given in Table I. Specimens of all alloys were annealed at 1200°C in an atmosphere of purified 92 pct helium and 8 pct hydrogen mixture. Alloys consisting mainly of

Jan 1, 1952

By G. Baralis, P. Gondi, I. Tangerini, G. Scandola

The precipitation behavior of Zn-0.5 pct A1 alloy single crystals was studied by means of electrical resistivity measurements and by optical and electron microscopy. The single crystals for the resistivity measurements were prepared by an original method in - 100-p -thick sheets. The order of the precipitation kinetics ranged between 1 and 1.5. The dislocations play a relevant role in the first-order kinetics. Precipitation always occurs both on dispersed particles and on dislocations. Statistical examinations have shown that the first-order kinetics can have two different activation energies; i.e., the precipitation can have dz;fferent mechanisnrs which could not be identified, however, in the course of the research. During the tnetallographic exanzination of the precipitation structures a specific process of dislocation decoration was obsereed. The main purpose of this work was to study the contribution of dislocations to the precipitation. A number of authors have observed precipitation on dislocations and reference might be made to several monographs on the ubject.&apos;&apos; The possibility that dislocations also accelerate precipitation has been considered by Turn-bull3 and Fischer et al.4 The studies described in the present paper were carried out on zinc, chosen as a base metal owing to the ease with which dislocations can be introduced into it and because of the absence of excess vacancies after quenching in conditions where phenomena of accelerated precipitation still occur. Aluminum was preferred as alloying element because of the accelerated precipitation phenomena that resulted in a preliminary reearch. EXPERIMENTAL METHODS The observations refer to a Zn-0.5 pct A1 alloy. The zinc was 99.995 pct pure; a typical spectroscopical analysis is given in Table I. As a rule the alloy was subjected to homogenization, quenching, or slow cooling and annealing. Homogenization was carried out by heating at 390" to 410°C for 24 hr. From the homogenization temperature, some specimens were quenched and some slowly cooled at a rate of 2°C per sec. At this rate no precipitate was detectable under the optical microscope just after cooling. Quenching was carried out simply by dropping the specimens into water, aqueous ethylene glycol solution at -30" c, or liquid-nitrogen baths placed close to the homogenization oven. Vaseline oil baths were used with a thermal stabilization of 10-20 for both the aging treatments and the measurements; aging was generally carried out at 90" or 130°C. To avoid oxidation phenomena during heating, the vaseline oil baths had to be frequently renewed. The precipitation kinetics were studied by means of electrical resistivity measurements, using ans potentiometric method (reproducibility ± 5 x 10 5 v, that is 0.5 pct of the total voltage decreases on the specimens during precipitation). First, various types of specimens were tested, i.e., polycrystals, single crystals grown in capillary quartz tubes, and thin single-crystal sheets prepared by means of an original method requiring no container except for the natural oxide. Even if fully annealed, the polycrystals and the capillary grown single crystals showed resistivity in -creases, most probably due to dislocations introduced in the course of the measurements. Similar resistivity increases in pure zinc were noticed by another author. Only the single-crystal sheets showed no resistivity change; thus they were chosen for the subsequent tests. As already mentioned, these single crystals were obtained by using, as a container, the natural oxide on the zinc surface; the oxide strength is sufficient to maintain the original shape during melting with sheets up to 500 p thick. An initial zone melting and subsequent zone leveling, which led also to formation of the single crystals, were thus carried out on rolled sheets of the required thicknesses (- 100 p) and shape, lying on a flat silica surface. The resistivities were first evaluated by measurements at the liquid-nitrogen temperature. This method gave poor reproducibility, however, and this was attributed to the thermal cycles which had to be operated. To avoid cycles and handling, it was therefore decided to make measurements directly in the annealing oil baths; this required thermal stabilization at ilo-&apos; "C. In this way only the resistance changes were measured. Specimens of pure zinc and of completely annealed alloy were always examined as controls together with those under consideration; only those measurement runs were taken into account where the reference samples showed no resistance increases. Again, the main inconvenience was due to oxidation and this was avoided by renewing the oil baths; even so data reproducibility was poor and the observations were therefore carried out on a large number (many hundreds) of specimens so as to provide indications of statistical value. For the transmission observations under the elec-

Jan 1, 1969

By R. N. Orava

TO the author&apos;s knowledge, only one satisfactory high-resolution technique for etch-pitting dislocations in Cu-Zn alloys has been published.&apos; In that account, pits in 70/30 brass single crystals were produced by etching electrolytic ally in a 30 pct orthophosphoric acid bath. Thereafter, observations were made from surface replicas by electron microscopy. The method of pitting and observation permitted the high resolution necessary for the distinction of individual dislocations in arrays of pile-ups. However, no comment was offered concerning the possibility of obtaining pits which are amenable to optical resolution. Moreover, for adequate results, the electrolytic pitting process is invariably preceded by a polishing stage which could obscure the surface features of interest. Consequently, it would be desirable to be able to delineate, by solely chemical means, dislocations which could be detected by both optical and electron metallo-graphic techniques. This was achieved by the simple expedient of modifying two etchants reported by young2 to reveal dislocations on the (100) planes of pure copper. Single crystals of 70/30 a brass, described previously,3 were sectioned to provide a surface parallel to a set of {100) planes, mechanically polished, and subsequently electropolished at 2.4 v in a solution comprised of 2 parts H3PO4, 4 parts ethanol, and 3 parts water. The inclusion of ethanol tended to inhibit nonuniform surface attack. Etch-pitting was effected by a 2 to 3 sec immersion in a 70 pct aqueous solution of HNO3. The samples were then washed in a fast-flowing stream of water, and rinsed further in distilled water, and ethanol, before drying. It is important to note that this reagent should be either used immediately after mixing, or, if allowed to cool, reheated to about 35°C prior to use. No pitting was obtained at room temperature. Typical results are shown in Fig. 1 where (a) is an optical view of the pitted surface and (b) is an electron micrograph of a silicon monoxide replica shadowed with tungsten oxide. The former is characteristic of a somewhat longer etching time (-6 to 8 sec) which varied with bath temperature. Similar pits accrued from a 1/10 aqueous dilution of another of Young&apos;s solutions2—2 M FeC1,6H20 and 7.8 M HBr.

Jan 1, 1968

By J. W. Gwinn

THE underground haulage system in the lead-silver mine of the-Bunker Hill & Sullivan Co., situated at Kellogg, Idaho, is the most extensive in the Coeur d&apos;Alène district, comprising about 35,000 ft. of tunnels, drifts, and cross-cuts where locomotive haulage is in use. The main working adit, known as the Kellogg tunnel, or No. 9 level, is approximately 10,000 ft. in length from the portal to the main working shaft and extends beyond that about 4,500 ft. in each of two directions. On this level all the ore from the Bunker Hill & Sullivan, the Sierra Nevada Consolidated, and the Caledonia Mining Co. an average of 44,600 tons per month-is hauled to the mills, located a short distance from the portal. Electric haulage by the trolley-type locomotive is used on this level throughout. Below this level, at intervals of 200 ft. vertically, are five other working levels (Nos. 10, 11, 12, 13, and 14); and the total haulage distance on these, where electric locomotives are used, is approximately 16,000 ft. No. 13 level has but recently been opened up and is not working-to capacity; while the main cross-cut on No. 14 has just been started, and has no need of power haulage. Of the four levels equipped with electric haulage, Nos. 11, 12, and 13 have storage-battery locomotives, and No. 10 still retains the trolley type by reason of the small and decreasing tonnage produced.

Jan 2, 1915

By J. K. Abraham

In recent years there has been interest displayed in the precipitation phenomena occurring in austenitic alloys based on the binary Fe-Ni system.1&apos;2 Previous communications have been extended covering the kinetics of clustering in the Fe-Ni-Ti system and the effect of cluster size on subsequent mechanical properties.3&apos;4 To a great extent the question of coherency, which has a dominant role in determining the mechanical properties, is dictated by the degree of misfit between the precipitate and matrix. Thus, the change in lattice parameter of the matrix with composition is an important variable that should be examined. The lattice parameter, ao, of austenite was determined for Fe-29.75 Ni-1 to 6 Ti and Fe-27 Ni-1 to 10 Ti alloys in this study. The alloys used in this investigation were melted in a vacuum induction furnace from a starting stock of plast iron (99.95), electrolytic nickel (99.9), and ti- tanium sheet (99.5) in a MgO crucible. The alloy compositions in atomic percent are given in Table I and their relative position in the Fe-Ni-Ti ternary is indicated in Fig. 1. The chemical analyses were taken from the homogenized bulk materials treated in a manner related earlier.3 A diamond file was used to obtain powder from the bulk. To remove the stresses induced by filing, the powders were austenitized at 1875°F for

Jan 1, 1969

By D. K. Crampton

NEARLY everyone who has not had the benefit of study in the field of metallurgy subscribes to a persistent and enthusiastic belief in the legendary lost art of hardening copper. This of course supplies a perfect introduction to a chapter of information on copper and its alloys, since the dissipation of fallacies and superstitions affecting an art probably constitutes the best method of getting at its real substance. Metals are hardened, but also embrittled, by a plurality of impurities. In the modern technology of copper-base metal products, we are familiar with a great host of materials, passing from one extreme of dead soft copper better than 99.9 pct pure, which in the form of wire about as thick as a match will stand hundreds of full twists in a 12-in. length, to an alloy containing less than 3 pct of alloyed substance possessing the strength of pretty good steel and capable of manufacture into razor blades, should we suddenly be deprived of steel; certainly a much better material for this purpose. Every copper alloy known to primitive man lies in some inter- mediate position and the ancient bronzes that have been found all over the world wherever an early civilization existed are usually contaminated by such impurities as sulfur, oxygen, antimony, arsenic, iron, or other materials, so that they could not possibly conform to any modern intelligent specification insuring the best combination of useful properties in alloys of their type and would go

Jan 1, 1953