By H. H. Podgurski, J. C. M. Li, Y. T. Chou, F. N. Davis, R. A. Oriani

When an Fe-2 pct A1 alloy is nitrogemted at 500ºC with a gus tnixture (NH3-H2) in which the nitrogen activity has been kept Lou] enough to avoid the formation of iron nitride, a two-phase alloy is generuled which consists of AlN particles and a ferrite phase cotaining a heavy network of dislocations. The amount of nitrogen contained in such an alloy, when equilibrated with the nitrogenating atmosphere, far exceeds both that needed to satisfy the normal solution requirements of a Fe and that needed to convert all of the aluninuwi to AlN. This excess nitrogen is accounted for as being trapped on dislocations, adsorbed at the ferrite -AlN interface, and as an en-Iuznced lattice solubility in strained ferrite. This excessive uptake of nitrogen had previously been attribuled by other investigators to the formation of a nonstoichiornetric aluminum nitride. Isotope exchange experiments revealed various amomts of exchargeable N14 present in the originally nitrided samples that could not be removed by reduction with HS at 500ºC. This exchangeable nitrogen has been identified us that bound to the AlN -ferrite interface. Estimates of inter facial areas in alloys containing -3 pct by weight of A1N are as high as 10 sq m per g of alloy. ThE first1 of this series of papers described the experiments forming the basis for the elucidation of the mechanism of the formation of aluminum nitride particles within an Fe-A1 alloy. It was found that not only are dislocations necessary for the nucleation of the AlN particles but also the nitriding reaction in turn produces a dense network of dislocations in the ferrite matrix. It was also observed that nitrogen in excess of that needed for the formation of stoichiometric AIN is taken up by the alloy without the formation of an iron nitride. The present paper is an analysis of the excess nitrogen sorbed by the nitrided Fe-A1 alloy which considers the structure generated by the formation of the aluminum nitride particles. Because of the high density of dislocations, this system has proved to be quite useful in studying nitrogen-dislocation interactions. Wriedt and Darken2 have already reported such studies in a cold-worked ferritic steel. EXPERIMENTAL Nitrogen Sorption. The specimens of this alloy were cold worked (50 pct reduction) to 0.011 in. thickness and chemically cleaned in a 2:1 concentrated phosphoric acid-50 pct hydrogen peroxide solution before nitrogenation. The flowing nitrogenating atmosphere (11 pct NH3-89 pct H2) was established before the ni- trogenating temperature was reached. The same gravimetric and gas-flow equipment described in an earlier paper1 was also used in this investigation. Changes in nitrogen concentration were followed gravimetrically when establishing the isotherms. In the isotope exchange experiments, concentration changes were followed volumetrically. In some instances chemical analyses (Kjeldahl method) were used to check for material balances in both the gravimetric and volumetric procedures. Our objective was to obtain reversible nitrogen sorption isotherms for alloys equilibrated with NH3-H2 gas mixtures over a large range of nitrogen activity* and temperature. The *Defined as equal to PN H /P3/2 ,where P corresponds to partial pressure in atmospheres. Actually the nitrogen activity, aN, in the alloy equals K PNH3 /p3/2H2, where K is the equilibrium constant for the reaction NH3 = N + 3/2H2. upper limit for nitrogen activity was below that which would produce iron nitride; for reasons which will become apparent later, most of the sorption studies were made in the temperature range between 400" and 500'C. The alloy sample studied most extensively in this investigation was given a series of successive reductions (100 pct H2) and nitrogenating treatments at 500°C to attain a stabilized structure. Presumably some dislocations were lost during these treatments. Throughout most of the sorption studies, temperature was held at ± 1°C and the gas-phase composition was held to k0.2 pet NH3. Based upon the results of numerous diffusion experiments with this alloy* the 'Results to be published in a third paper of this series. times chosen for equilibration were considered more than adequate, Nitrogen Isotope Exchange. The first exchange experiments were carried out by circulating a measured quantity of H2 and NH3* (with a predetermined isotopic *The NH3 was synthesized over a synthetic ammonia iron catalyst using H2, and N2, enriched with N15. AS the NH3 was formed it was removed continuously from the gas phase by circulating the mixture through a refrigerated (78ºK) trap. When most of the nitrogen had been converted to NH3, it was distilled from the trap into a glass storage vessel. composition, N15/N14) over a nitrided specimen at 450°C in a closed glass system. Attempts to reach the exchange limit isothermally, i.e., an isotopic ratio (N15/N14) in the gas phase identical with the extractable nitrogen in the nitrided alloy, were futile. The exchange rate between the gas phase and the alloy was too slow, involving many days. To circumvent the slow exchange with the gas phase, measured amounts of N15 and N14 were introduced into the alloy by nitrogenating with an NH3-H2, mixture at 500°C containing an N15/N14 ratio of 7.76; the charged specimens were then sealed by allowing an oxide film to form over them in air, and in this final condition the specimens were subjected to 500°C in vacuum for various times during which isotope exchange was allowed to proceed within the specimen. It was estab-

Jan 1, 1970

By M. J. Spendlove, H. W. St. Clair

An automatic surface-follower mechanism was used to measure the surface temperature and the rate of evaporation of molten zinc while undergoing distillation at low pressure. At pressures of 50 to 100 microns Hg, the rate of evaporation may be 60 to 80 pct of the theoretical maximum corresponding to the measured temperature. The rate decreases rapidly at pressures above 100 microns Hg, to only 7 pct of the theoretical maximum at 2000 microns Hg. Measured temperature gradients at the surface are in agreement with theoretical gradients calculated from the heat of vaporization, rate of evaporation, and thermal conductivity of molten zinc. THIS paper covers a series of careful measurements of the rate of evaporation of molten zinc at low pressures, undertaken as a part of a general investigation on the separation of metals by distillation.' Preliminary results on the rate of evaporation of zinc were described in a previous publication.' The results of the preliminary study are as follows: 1—The observed rates of evaporation of zinc were as high as 0.60 g per sq cm per min, corresponding to 75 pct of the maximum rate as determined by the temperature of the metal. 2—The evaporation rate was decreased from 0.30 g per sq cm per min at a pressure of 25 microns to only 0.09 g per sq cm per min when the pressure was increased to 5 mm. 3—The temperature of the surface during rapid evaporation may be 35" to 100°C less than the main mass of metal. Observed temperature gradients at the surface are consistent with those calculated from the heat of vaporization and the thermal conductivity of liquid zinc. In the preliminary experiments, the rate of evaporation was determined from the loss in weight of the metal in the crucible during the test. This was compared with the weight of the condensate. Obviously, this method was subject to error because of some uncertainty as to the period of evaporation that should correspond to the loss in weight. Furthermore, this method did not permit taking into account probable variations in the rate of evaporation during the test. A more serious shortcoming was that the temperature at the evaporating surface was not known, so the maximum theoretical rate of evaporation could not be calculated accurately. To improve the precision of rate measurements and to allow accurate measurements of the surface temperature, a refined experimental technique was developed whereby the temperature and position of the surface could be measured accurately. This was done by an automatic surface-follower mechanism that gave a continuous record of the surface temperature and the amount of zinc evaporated. These data permitted an instantaneous determination of the actual rate of evaporation and the surface temperature throughout the test. Pure zinc (99.99 pct Zn) was used in all experiments. Description of Distillation Furnace The details of construction of the distillation furnace are shown in Fig. l. The furnace is enclosed in a large quartz tube open at one end. The open end of the quartz tube is sealed by means of a water-cooled head. The entire enclosure is vacuum tight. The connection between the water-cooled head and the quartz tube is sealed by means of a rubber gasket which fits tightly against the smooth end of the tube. The metal is heated by induced current set up in the molten zinc and the walls of the graphite crucible by means of a water-cooled induction coil outside the quartz tube. High frequency current is passed through the induction coil from a 6 kw mer-

Jan 1, 1952

By Shozo Saito, P. A. Beck

Mettrllographic and X-ray diffraction study of Cb-Co alloys in the Composition range of 7 to 33 nt. pct Cb, after annealing at 1175 °', showed that near 25 al. pct Cb on MgNi,-lype hexagonal Laves Phaseexists in a narrow composition range, and that an MgCl- type cubic Laves Phase occurs between approximately 27 and 32.6 ut. pd Cb. Lattice parameter and density measures indicated that, in both phases. the deviations from proper Loves sloichimetry result from the substitution of cobalt atoms for some 0f the columbium atoms. Tlle same phases occurant 1000'C, together with an additional phase of unknown structure, which appears between the hexagonal Laves phase and the cobalt-bose terminal solid solutions KOSTER and Schmid' identified a phase corresponding to the composition VCo,, and more recently the crystal structure of this phase has been determined.' In the Ta-Co system Korchynsky and Fountain recently found two intermediate phases at the composition Taco,, one of them metastable. In contrast to the V-Co and the Ta-Co systems, in the Cb-Co system no intermediate phase has been found4 at the composition CbCo,. The present investigation was undertaken in order to reexamine the question of the existence of such a phase. EXPERIMENTAL PROCEDURE Twelve alloys were prepared by arc-melting in a water-cooled copper crucible under helium atmosphere. Electrolytic cobalt and 99.9 pct pure colum-bium powder have been used as starting materials. It was found that melting losses can be reduced by compressing the colunlbium powder in the form of thin pellets before melting. For the alloys used the melting losses were not higher than 1 pct. The intended compositions of all alloys and the chemical analyses of three of them are given in Table I. Specimens from all alloys were annealed in evac- uated fused silica tubes at 1175°C for 3 days and quenched in cold water. A second set of specimens of most alloys was annealed at 1000°C for 7 days and then quenched in cold water. The annealed and quenched specimens were examined metallographically, using the following etchant: 60 pct glycerine +20 pct H,NO, + 10 pct HF + 10 pct water. Powder specimens for X-ray diffraction were prepared by crushing annealed solid specimens in a mortar. Alloys containing 27.3, 28, 29.7, and 32.6 at. pct Cb annealed at either 1175" or 1000°C were very brittle and it was found unnecessary to reanneal the powders. However, alloys containing 24.8 at. pct Cb, or less, especially those annealed at 1000°C, were much less brittle and re-annealing was required to remove the strains present in the crushed powders. In each case reannealing was done at the same temperature at which the corresponding solid specimens were annealed and it, too, was followed by quenching in cold water. In many instances X-ray diffraction patterns were also taken of the polished and etched solid specimens and compared with the corresponding X-ray diffraction patterns obtained with powders. The X-ray diffraction patterns were taken with an asymmetrical focusing camera, using CrK radiation. For precision lattice parameter measurements some X-ray diffraction patterns were taken with a symmetrical focusing camera, again using CrK radiation. EXPERIMENTAL RESULTS A microscopic examination of the alloys annealed at 1175°C revealed that the alloy containing 25.5 at. pct Cb was composed of a single phase, but that the 24.8 at. pct Cb alloy did contain a small amount of a second phase, identified by means of X-ray diffraction as having a fcc structure, undoubtedly the terminal solid solution based on cobalt. Apart from the few very weak lines corresponding to this minor phase, the X-ray diffraction patterns of these alloys could be well interpreted in terms of a MgNi,-type hexagonal Laves phase structure. The indexing of the X-ray diffraction pattern, Table 11, yas based on the lattice parameter values a, = 4.740A and c,

Jan 1, 1961

By S. E. Clay

In the chemical reaction control regime employed in the laboratory dissolution experiments, calcined trona ore dissolves in aqueous solutions according to a first order, irreversible reaction rate. The study showed that the reaction is first order with respect to solution NagCO3 concentration. The activation energy was determined to be 20.233 kJ/g. mol with a rate constant equal to 1235 mm/s (2917 in. per min). The dissolving particle may be described by shrinking particle behavior.

Jan 1, 1986

[Alphabetic Section: The letter immediately following a member's name indicates grade: M-member, A-associate, J-junior. The numerals following member's grade indicate year of election. The letter following year of election indicates primary divisional affiliation: A. Mining & Exploration F. Coal B. Minerals Beneficiation G. Petroleum C. Iron and Steel H. Industrial Minerals D. Extractive Metallurgy J. Council of Education E. Institute of Metals K. Council of Economics Geographic Section: An asterisk (*) preceding a member's name indicates availability for consulting work:]

Jan 1, 1961

By Robert H. Hafner, Irvin R. Kramer, Stewart L. Toleman

IN his paper on the calculation of hardenability from chemical composition, Grossmann1 discussed the effect of most of the alloying elements used commercially. The purpose of the work reported in this paper was to determine the effect of several other elements on hardenability-arsenic, antimony, beryllium, cobalt, columbium, germanium, tellurium, tin, aluminum, and titanium-and to extend the range of composition of some of the elements studied by , Grossmann-chromium, copper, manganese, molybdenum, nickel and silicon. EXPERIMENTAL METHODS To determine the effect on hardenability, suitable amounts of the alloying elements were added to experimental heats and the hardenability determined by means of end-quenched hardenability specimens. The steels were melted in a high-frequency induction furnace with a basic crucible, using ingot iron as a base for some of the heats and S.A.E. 1015 for others. The alloying additions were made as ferroalloys or as metal, depending on the ' alloying element. Hundred-pound heats were split and poured into square, tapered, cast-iron ingot molds with hot tops. Aluminum was not used as a deoxidizer in most of the heats. The ingots were homogenized for 12 hr. at 1260°C. (2300°F.) , and forged into rounds of 1 ½ in. diameter. These bars were normalized twice from 840°C. (1550°F.) before machining into Jominy bars. The composition of the steels was deter- [ ] mined in most cases by samples taken from the end-quench hardenability specimen. As suggested by crafts,2acid-soluble

Jan 1, 1943

By W. F. Stowasser

A downdraft traveling grate process to agglomerate pelletized iron ore concentrates has been successfully demonstrated in a pilot plant at Carrollville, Wis. Work there followed several years of development in the Allis-Chalmers Mfg. Co. laboratories, and the pilot plant phase was carried out in co-operation with Arthur G. McKee & Co., consultants and engineers to the iron and steel industry. End result of the process is conversion of iron ore concentrates into a form which can easily be transported and smelted in the blast furnace.

Jan 5, 1955

By M. S. Burton, G. V. Smith, A. Rosen

The kinetics of re crystallization and the effect of recovery on recrystallization of pure iron were investigated within the temperature range of 517" to 632 OC. Grain growth and activation energies were also studied. Two stages can be distinguished during recrystallization; the first is gvowth-controlled and the second is nucleation-controlled. The extent to which the first stage succeeds before the second stage begins depends on both temperature of recrystallization and temperature of recovery. The softening of cold-worked metals and alloys due to transformation of the deformed crystals to strain-free equiaxed grains during annealing is well-known, and early inestiators established that recrystallization kinetics is strongly influenced by minute quantities of impurities. Generally, it is believed that impurities decrease the rate of recrystallization and the rate of grain growth. To understand the basic phenomena of recrystallization, investigations should be on pure materials. Most of the research on high-purity materials has been on metals having the fee Bcc materials, and especially high-purity iron, have been studied only in recent years. It is known that recovery may influence recrystalliation;" however, no general description of the influence, applicable to all materials, has been presented. This paper presents results of a study of the recrystallization kinetics of high-purity iron, after 60 pct cold deformation by drawing, with particular reference to the influence of recovery on the rates of recrystallization and grain growth. From observations of these rates, conclusions are drawn concerning nucleation. MATERIAL AND EXPERIMENTAL PROCEDURE Preparation of Material. High-purity iron, prepared by zone refining of vacuum-melted electroiytic iron at Battelle Memorial Institute under sponsorship of the American Iron and Steel Institute, was used in this study. Table I gives the reported chemical analysis of the material, taken at a point near the last molten zone and thereby rep- resenting the maximum impurity level for the entire bar. Prismatic specimens, approximately 10 x 10 X 50 mm, were sawed from the 50-mm-diam bar, perpendicular to the zone-refining direction, and turned to cylindrical shape. These specimens were sealed in quartz capsules under vacuum, approximately 10"e mm Hg, austenitized at 930° C for 15 min, slowly cooled, removed from the capsules, and cold-worked in air by swaging to approximately 20-pct reduction of area. The encapsulating, austenitizing, and swaging operations were repeated two additional times, after which the samples were encapsulated, austenitized, and cold-drawn to 60-pct reduction of area. A further vacuum anneal at 630°C for 120 min and cold drawing to 60-pct reduction of area produced wire 2.8 mm in diameter. The drawn wire was electropolished to remove deformed material on the surface, after which it was sawed into 4-mm-long specimens for the recrystallization study. Microscopical examination before the final cold reduction revealed equiaxed grain structure with very fine grains in a thin layer near the surfaces of the specimen and nearly uniform ASTM 3-4 grain size in the center. Recrystallization Heat Treatment. a) Direct Recrystallization of Cold-Worked The 60 pct cold drawn iron specimens were recrystallized at five temperatures, 517, 556, 590°, 612, and 632C, in a lead bath covered with graphite (the temperature was controlled to 1°C). Specimens were treated for twelve different times at each temperature, and all were water-quenched after heat &eatment. b) Recrystallization Following Preliminary Recovery Heat Treatment. After cold working, specimens were sealed into quartz capsules under vacuum, 105 mm Hg, and recovery-annealed at 362", 400", and 440°C for 20 hr prior to recrystallization. No evidence of recrystallization was found

Jan 1, 1964

By T. S. Maio, J. G. Mansanti

In 1978, Ozark Lead Co. made the decision to expand the capacity of its mine/mill complex by 33%. The objectives of the expansion were to increase mine production capacity by 1.8 kt/d (2000 stpd), increase lead metal production by 21.8 kt/a (24,000 stpy), and to construct new facilities and modify existing equipment to accommodate increased production. This paper gives a brief explanation of the equipment installed and the overall production and metallurgical benefits realized from this expansion. The expansion was completed in the second half of 1980 with all equipment debugging and fine tuning completed by the first quarter of 1981. Concentrator modifications and improvements were basically restricted to four areas: materials handling, automation of the mill grinding circuit, increased flotation capacity, and concentrate dewatering.

Jan 1, 1985

By Richard W. Brummett, Robert L. Dubms

Located some 180 miles east of Los Angeles in Riverside County, California, the Eagle Mountain mine supplies iron ore concentrates for the Kaiser Steel Corporation steel plant in Fontana, California, and for export to Japan. Although the deposits were first discovered in the early 1890's, no production was realized from the area until 1948 when Kaiser Steel Corporation commenced operations. A part of the large Basin and Range province, the Eagle Mountain area's geologic column comprises a thick series of metasediments resting on Precambrian gneisses and schists that have been intruded by sill-like masses of porphyritic quartz monzonite. The metasediments are composed of three quartzite units that are separated by a schistose meta-arkose and by two ore zones. They have been folded into a large east-west trending anticlinal structure that extends completely across the Eagle Mountains. The iron ore deposits occur in two well-defined horizons in the metasedimentary series, and they are found only along the north limb of the major anticline. Host rocks for the ore zones were a series of limestones and dolomites with associated quartzites. Magnetite plus pyrite comprised the primary mineralization that formed many replacement lenses and stringers of ore within the ore zones. The primary ore has been oxidized to hematite and goethite in a broad zone at higher elevations in the deposits. Hydrothermal alteration formed actinolite- tremolite granofels, local phlogopite, and minor tourmaline in the ore zones. This alteration and the ore deposition seem related to the same magmatic event that formed the porphyritic quartz monzonite intrusion

Jan 1, 1968

By Folke H. Kihlstedt

Geophysical prospecting for ore has been more or less at a standstill during the present crisis owing to the lack of interest in base-metal exploration. A notable exception is the increased use of electrical and magnetic methods in prospecting for gold, the former in Canada, United States, Sumatra, Africa and Western Australia, and the latter on the Rand. This application to gold prospecting marks a forward step in ore prospecting because it is based upon mapping the geology instead of a direct location of the ore in question, as the amount of gold in an average gold ore is far too small to have any influence upon the physical properties of the rock in which it occurs. The development has thus gone in the same direction as geophysical prospecting for oil; that is, to find geological conditions that are genetically connected with the gold ore as exemplified by known occurrences. Naturally the success of this indirect prospecting depends upon two things: (1) the soundness of the geological conclusions upon which is based the hope of discovering new deposits, because a great many geological "set-ups" are barren, and (2) the ability of geophysical methods to help the geologist to collect the pertinent geological data within reasonable cost, after which favorable structures may be drilled or trenched. The first point is one to be considered by the mining geologist. In the vicinity of producing mines or promising prospects, the chances of finding ore in quartz veins and shear zones are great, and a survey giving the location of these features will materially guide both surface and underground exploration. Even in outside exploration the chances are sometimes favorable. As an example may be taken the Northeastern Ontario-Western Quebec gold zone. Large areas are here covered with glacial and post-glacial deposits and a simple study of available maps reveals the fact that less than 30 per cent of the area can ever be even preliminarily prospected by cominonly used prospecting methods, of which the pick and shovel are the main tools. Considering the number of deposits found, it is evident that many deposits remain hidden below the overburden. The knowledge of gold geology gives a starting point

Jan 1, 1934

By R. A. Swalin, A. H. Geisler

THIS study represents an investigation of the effect of annealing temperature on the texture of drawn molybdenum, iron, and an iron alloy containing 14 pct Al. The effect of temperature on annealing textures has not been widely investigated in the past. One of the obstacles in making such a study using usual X-ray diffraction techniques results from the

Jan 1, 1957

By A. G. Weber, R. L. Ledbetter, A. L. Hicks

A procedure which makes use of both analog and digital computers has been developed for predicting the pressure-production behavior. of water-drive reservoirs. The electric analyzer is used for matching the past pressure and production history of the reservoir and inferring the physical characteristies of the aquifer. When the history has been matched, a .set of base curves called influence functionce" are derived and the future behavior of the reservoir is calculated from these curves. INTRODUCTION Electric analog methods are particularly well-suited for complex water-drive problems. Like all other methods of analyzing water-drive reservoirs, however, analog methods are subject to certain limitations. One of the more obvious and serious of these results from inaccurate or insufficient knowledge about physical characteristics of the reservoir and aquifer. However, it is not insurmountable because the unknown characteristics can usually be inferred from the reservoir's previous behavior. Simons and Spain have shown that even with scant reservoir data and limited production history, electric analyzer studies can provide useful and reliable results. Aside from this limitation on analyzer predictions, the main disadvantage has been lack of a technique for keeping predictions abreast of latest production forecasts. Pressure behavior of a reservoir depends on the rate at which fluid is withdrawn; it is therefore necessary to specify the future withdrawal schedule before the future pressure behavior can be calculated. Conventionally, the electric analyzer predicts pressure behavior for a specific production schedule. If this schedule is abandoned in favor of some new one, as is frequently the case, either the study must be rerun or results adjusted in some manner. The usual procedure is to predict pressures for several different forecasts covering a wide range of production rates. Pressures for specific rates other than those studied can then be approximated by interpolating between the analyzer predicted curves. However, reliability of this type of prediction is doubtful. This paper describes a technique for predicting future behavior of water-drive reservoirs that retains all advantages of electric analyzer analysis and eliminates the main disadvantage. That is, the analyzer is used conventionally to infer unknown reservoir parameters from the pressure history, but not to predict the future behavior directly. Instead, a derived set of base curves, called influence l'unctions, can be used to calculate future behavior for any production schedule.

By J. Murray Riddell, George A. Morrison

THIS paper is a companion to the one by George A. Morrison on Mining a Deep Limestone Mine in Ohio.[+] Barberton is 8 miles west of Akron, Ohio, and 23 miles south of Cleveland. The underground mining of limestone at Barberton constitutes the world's deepest limestone mine. The stratigraphy is as follows: 0-20 ft. Loam, clay, sand and gravel. Water bearing. 20-40 ft. Fractured. sandstone. Water bearing. 40-110 ft. Sandstone with interbedded shale, slightly fractured. Water bearing. 110-314 ft. Sandstone with interbedded shale, slightly fractured. Water carrying. 314-2197 ft. Shale with occasional seams of sandstone, which varies in thickness from a few inches to 4 feet. Dry. 2197-2247 ft. Limestone. Dry. 2247-2742 ft. Dolomitic limestone. Dry. 2742-2767 ft. Salt. Dry. 2767- Dolomitic limestone. Dry. All of the strata dip to the southeast, about 0.5 per cent from the horizontal. The top 110 ft. of the crust is water-bearing. The rock strata are naturally fractured to a depth of 314 ft., sufficient to allow the passage of water. In the shaft-sinking operations, a stra was encountered at a depth of 520 ft., and flows of methane gas were pierced at depths of 1350 and 1952 feet. Specifications for the mine plant called for, in part, the sinking of two vertical shafts and a hoisting plant capable of producing at the rate of 300 tons per hour. No. I shaft is 550 ft. west of No. 2 shaft. Each shaft measures 8 by 17 ft. outside of steel. General features of the design (Fig. I) are: Principal set members, 6-in. H-section; connecting angles (studdles), 3/8 by 4 by 4-in. angle irons; spacing of sets, 8 ft. centers; spacing of bearer sets, generally, 160 ft.; bearers, of 12-in. I-beams. Each bearing set featured a concrete ring about the periphery of the shaft, steel to rock, and 8 ft. in height; permanent guides, 6 by 10-in. long-leaf yellow pine, 85 per cent heart. THE SHAFT-SINKING OPERATION The preliminary shaft-sinking work consisted of driving interlocked steel piling about the exterior of the shafts to depths of 35 and 32 ft., respectively, and of such horizontal dimensions as to ultimately permit the pouring of a concrete collar 2 ft. in horizontal thickness. Following the pouring of a shaft collar, a temporary wooden headframe for shaft-sinking purposes was erected. The head-frame, while ordinary, featured: (I) a storage pocket of 300 cu. ft. capacity with truck servicing facilities, and (2) pneumatically operated dump doors, which were actuated by the hoistman, thus caring for the dumping of the "ball-and-chain"

Jan 1, 1944

[NORTH AMERICA UNITED STATES ALABAMA Birmingham Cord, Richard H. Dlsmukes, Edward B. Hunter, Robert A. Citronelle Perrin, Huey P. Fairfield Pagel, Herbert Ervin Fairhope Ruffles, William R. Huntsville Eng, Harvard Kelley, Dean W. Waggoner, J. B. Weber, Thomas C. Mobile Hankins, James D. Horner, William L. Petroutson, Peter C. University Cudworth, James R. Jones, Walter B. Mason, William L.]

Jan 1, 1961

By John E. Hockett

The need for basic information about the relationship between resistance to dejormatim (flow stress), temperature, strain, and strain rate, for the solution of metal-fovming problems, is pointed out. Some early attempts to satisfy the need are mentioned. A brief description of a machine called a Cam Plastome-ter is given, including the processing of results of testing in the machine. Next, a program of testing aluminum in compression over a wide range of constant true-strain rates (0.1 to > 200 sec-1) and a modevately broad range of temperatures (223° to 673°K) is described. The results of this program are presented in the form of true-stress us true-strain cuvves. The data in these curves are presented in the form of relationships between true stress and true-strain rate in sermilogarithmic and log-log form, as functions of temperatures—for several true strains. Finally, true stress, for a given true strain, is displayed as a function of log true-strain rate and absolute temperature, i.e., a surface. SINCE the publication of Hill's book1 on plasticity theory, increasingly rapid advances have been made in analytical solutions to forming problems. Methods in common use are the slab method, the uniform deformation energy method, the limit analysis method, the slipline field method, and the semiexperimental method called "visioplasticity". These approaches, and examples of their use, are covered in detail by Johnson and Melloor2 and by Thornsen, Yang, and Kobayashi.3 unfortunately, practically all of the above work has had to rely upon a number of basic assumptions, e.g., homogeneous deformation and Coulomb (sliding) friction; and virtually no dependence of the mechanical behavior of the deforming metal, upon temperature, strain, and strain rate, has been included. It is with this dependency that this paper is concerned. Loizou and sims4 looked at the above relationship for lead using both a constant compression-speed Cam Plastometer and a constant true-strain-rate Cam Plastometer designed by Orowan.5 Alder and Phillips8 investigated the relationships for aluminum, copper, and steel in the same constant true-strain-rate Plastometer. cook7 tested twelve steels at temperatures ranging from 1170° to 1473°K in the same Plastometer over a range of true-strain rates of 1.5 to 100 sec-'. The writer tested commercially pure aluminum at room temperature and depleted uranium at temperatures from 573" to 873°K at strain rates from 10-3 to 1.0 sec-1 in a Cam Plastometer designed and built at Los Alamos Scientific Laboratory.8 During the past few years the Cam Plastometer at Los Alamos has been used for a number of relatively minor experiments on brass, mild steel, duralumin, Armco iron, and depleted uranium. In this time the machine has been continually modified and improved. It was decided to utilize fully the wide range of strain rates now available with the machine by testing a material about which some information was already in the literature. Prior work on commercially pure aluminum6 appeared to deserve confirmation and expansion. So it was decided to explore the resistance to compression of this material over the currently available range of constant true-strain rates and a convenient range of temperatures. This paper is a report of that exploration. I) EQUIPMENT AND PROCEDURE The principal item of equipment is, of course, the Cam Plastometer, the working part of which is shown in Fig. 1. In this figure, an aluminum specimen may be seen between two tungsten carbide platens, in position for a room-temperature test. Above the upper carbide platen is a load cell. Output from the load cell is amplified and applied to a galvanometer in a recording oscillograph. Auxiliary equipment includes the oscillograph, the control console, a counter, and a time-mark generator. The counter is first used in adjusting the time base. Then it registers the count, of sixty pips per revolution generated by the rotating cam, in each second. These pips and the time base are also applied to galvanometers in the oscillograph. Thus, load, time, and cam position are recorded simultaneously. Heating of a specimen prior to compression is done

Jan 1, 1968

By J. M. Eldridge, P. Balk

Phosphosilicate glass films were formed, by reacting gaseous P2O5 with SiO2, over a large range of temperature (800° to 1200°C) and gas phase composition (nearly two orders of magnitude of effective P2Ospressure). The film compositions generally corresponded with the liquidus curve, delineating the maximum solubility of the tridymite Phase of SiO 2 in phosphosilicate liquid solution at the temperature of film formation. It is shown that the P2O5 concentration of the phosphosilicate liquid film tends to decrease by reaction with the underlying SiO 2 layer until the liquidus curve is reached. The validity of the thermodynamic argument used in this explanation is supported by the results of a determination of the composition of borosili-cute films, prepared by reacting gaseous B2O3 with SiO2 at different temperatures. The kinetics of phosphosilicate film formation were described by a model predicated on a steady-state diffusion of P2O5 through the film. UNDERSTANDING of the processes leading to formation of phosphosilicate and borosilicate glasses is of great importance for producing passivating layers on FET devices. Passivating films with optimum characteristics are preferably formed in a separate step, independent of the doping of the semiconductor.' The results of an investigation carried out to gain improved insight into the mechanism of glass formation are presented in this paper. It would be expected that application of the known Pz05-Si02 and B 2 O 3-SiO2 phase diagrams should be useful in extending understanding of the glass-forming processes. However, the question of the propriety of treating thermally grown SiO2 in these binary oxide systems by the methods of equilibrium thermodynamics must be considered when this application is attempted. Although Sah et a1.' and Allen et al. 3 investigated the kinetics of formation of phosphosilicate glass (PSG), they failed to adequately relate their diffusion models to the occurrence of experimentally observed phases in the PSG/SiO 2/Si system. Horuichi and yamaguchi4 investigated the diffusion of boron through an oxide layer and described their results in terms of a model similar to that of Sah and coworkers. More recently, Kooi 5 and Snow and Deal6 reported the compositions of PSG films formed by depositing P2 O 5 onto SiO2. These compositions apparently coincide with those at the liquidus curve delineating the maximum solubility of crystalline SiO2 in phosphosilicate liquid solutions. These authors did not discuss the thermodynamic implications of their results on the structure of thermally grown SiO2 films. The structure of thermally grown Sio2 films and that of vitreous silica are generally thought to be quite similar. Since the solubility of a substance depends on its structure, it is relevant that the solubility of vitreous silica in water7 is highly reproducible, like the solubility of thermally grown SiOz in phosphosilicate liquid. Furthermore, the vitreous silica-water system appears to be in true thermodynamic equilibrium (viz., the same solubility value can be approached from both supersaturated and under-saturated solutions). Sosman7 suggested that a type of two-dimensional lattice may form at the silica/solution interface, resulting in the observed solubility behavior that is characteristic of a crystalline solid. An alternative explanation may be that vitreous silica has a microcrystalline grain structure. Other investigators have suggested that vitreous silica has essentially the structure of B cristobalite,' or is composed of microcrystals of p tridymite or cristobalite, or a mixture of both. Presumably the grain size would be sufficiently large to minimize any appreciable contribution of the grain boundaries to the solubility of the crystalline matrix. The present investigation was carried out to clarify the significance of the boundaries in the Pa,-SiO, and B2O3-SiO2 Systems in determining PSG and BSG (borosilicate) film compositions. Furthermore, the kinetic data for PSG film formation were extended, using a wider range of formation parameters than were previously reported. One model describing the kinetics of film formation will be presented that is compatible with the thermodynamics of the Pa5-Si02 system. EXPERIMENTAL PROCEDURE Glass Film Preparation. SiO2 films (1000 to 8000A thick) were obtained by oxidation of silicon substrates in dry O2 at 1100°C. PSG and BSG films were prepared by exposing these layers to gaseous oxides obtained by reacting high-purity POC13 and BBr3, respectively, with O2. A double-columned saturator was used to ensure complete saturation of the N 2 carrier

Jan 1, 1969

By S. Feuerstein, L. Rice

The effect of low pressures on the flow and fracture behavior of molybdenum is described. For poly crystalline samples, room-temperature tensile tests indicate greater ductility under 10 Torr than under intermediate pressures up to and including atmospheric pressure (760 Torr). In addition, tests conducted at 760 Torr under atmospheres of air, dry nitrogen, and purified argon exhibited no apparent difference in mechanical properties. Critical tests involving baking in situ as well as those involving single-crystal deformation further imply that the ductility effect is a pressure-dependent phenomenon related only to the fracture process. This dependency is discussed in terms of adsorption and diffusion contributions. THE effect of very low pressures on material properties has heretofore been presumed to be important only for substances possessing relatively high vapor pressures at ambient temperatures. Research has therefore been concentrated primarily on organic solids and liquids, and in some instances on metals such as zinc and cadmium. Most vacuum-effect studies' on the mechanical behavior of metals have been performed under conditions of either cyclic loading or creep rupture at elevated temperatures, i.e., over extended time periods. These studies were not restricted to high vapor pressure materials but also encompassed such metals as gold, copper, and nickel. Very little concern, however, was placed upon the importance of a vacuum environment on the mechanical behavior of metals subjected to a simple unidirectional deformation at ambient temperatures. A tension test is generally of short duration as compared to a creep test, and at room temperature vacuum effects if any would be expected to be surface-limited. In early 1963, Kramer and podlaseck2 reported a change in the bulk flow behavior of aluminum single crystals during room-temperature tension tests. The deformations were performed under pressure conditions of 760 to 3.4 X 10-8 Torr and indicated for the first time a vacuum surface effect contributing to the bulk tensile behavior of metal specimens. As a consequence, an experimental program was initiated in this Laboratory to study the effects of ultrahigh-vacuum conditions on the mechanical behavior of metals. The results of a preliminary study on poly-crystalline molybdenum3 revealed, unlike Kramer's observations of changes in the stress-strain behavior, only an increased ductility under ultrahigh vacuum. Flow behaviors were nearly identical for all tests re- gardless of pressure. This paper presents comprehensive results obtained in this area of research. 1) EXPERIMENTAL PROCEDURE Three material categories were used in this study: sintered and are-cast polycrystalline molybdenum of nominal purity 99.93+ pct and single-pass electron-beam zone-refined molybdenum single crystals having a nominal purity level of 99.99+ pct. The interstitial levels (weight percent) as determined by the Materials Testing Laboratories, Division of Magnaflux Corp., were as follows: sintered molybdenum (C— 0.005, H—0.0004, O—0.015, N—0.008); and arc-cast molybdenum (C-0.0038, H-0.0003, O-0.015, N-0.023). Single-crystal molybdenum obtained from Materials Research Corp. had a typical interstitial analysis of C-0.0015, H-0.00007, O—0.00045, and N-0.0001. Tensile specimens having a 5 mm diam by 50.8 mm length were prepared from these materials. An average grain diameter of 0.059 mm was obtained for the sintered specimens following a 4-hr, 1600°C heat treatment. Grain sizes from 0.019 to 0.149 mm were obtained in the arc-cast specimens following heat treatments from 1100° to 1600°C for 1 hr. This series of specimens was used exclusively for the grain-size effect studies. All samples were electrolytically polished in 97 pct sulfuric acid solution prior to testing. Experiments were performed at room temperature in an ion-pumped ultrahigh-vacuum system positioned in an Instron tensile machine, Fig. 1. A constant strain rate of 4.2 x 10-4 sec-1 as derived from crosshead displacement was assumed for the deformations. Starting vacuums ranged from 2 to 0.5 X 10-10 Torr. These pressure measurements were made using corrected values4 of an NRC Redhead gage. Comparative readings were also made against a G.E. triggered dis-

Jan 1, 1967

By David T. Peterson

Calcium metal was found to deoxidize thorizcm at 1000° to 1200° C. The reaction kinetics were determilled and related to the diffusion coefficients of oxygen in thorium. The solubility of oxygen in thorium, the minimum oxygen concentration, and the diffusion coefficient were determined from 1000° to 1200°C. This firocess results in the lowest oxygen concentrations zohich have been reported for thorium metal. FOR many years it has been known that calcium metal will reduce thorium oxide to thorium metal. This reaction has been the basis for several methods of preparing thorium metal. From the equations giv-by Kubaschewski and vans, ' AF" for the reaction Cao, + Tho,(,) - CaO(,, + Th(,) was calculated and found to be -3.4 kcal at 1000°C, -2.5 kcal at llOO°C, and -2.0 kcal at 1200°c. Thorium is very slightly soluble in liquid calcium, and the solubility of calcium in solid thorium is very low. Consequently these metals would be in essentially their reference states. If thorium containing oxygen were equilibrated with liquid calcium between 1000° and 1200°C, the oxygen content of the thorium would have to be below the solubility limit in thorium. Oxygen is one of the impurities most difficult to remove from thorium and is the most abundant impurity in metal prepared by almost all known methods. Fortunately, oxygen does not have a large influence on the properties of thorium because the solubility in solid thorium is very low. EvenT in thorium containing 100 ppm of 0, particles of thorium oxide can be observed in the microstructure. In view of the incompatibility of thorium oxide and liquid calcium and the low solubility of thorium oxide in thorium, the deoxidation of thorium by this method was investigated. For thorium containing an amount of oxygen well in excess of the solubility limit, the reaction should proceed in the following sequence. The oxygen content of the thorium matrix near the surface would be depleted by the diffusion of oxygen to the surface. At the surface, the oxygen would react with calcium to form calcium oxide. To maintain equilibrium within the thorium, thorium oxide would dissolve to keep the matrix saturated. Consequently, the thorium-oxide particles would disappear first at the surface and then the particle-free rim would grow in thickness. If the rate-controlling step were the diffusion of oxygen through this layer of thorium which was growing in thickness in direct proportion to the amount of oxygen removed, the well known parabolic time law should be observed. If the oxygen concentration at the surface of the thorium and at the inner surface of the deoxidized rim were known, the diffusion coefficient of oxygen in thorium could be calculated from the parabolic rate constant. EXPERIMENTAL PROCEDURE The thorium metal used in this study was prepared by calcium reduction of ThF, by the method described by Wilhelm.' The analysis of this metal is given in Table I. The carbon was determined by combustion, the oxygen by the HC1-insoluble residue method, nitrogen by the Kjeldahl method, and the other elements by emission spectroscopy. A section of this ingot was hot rolled at 600°C to 1/4 and 1/8-in. thick plates. Specimens approximately 7/8 in. square were cut from these plates, and all surfaces of the specimens were cleaned and smoothed by filing with a clean file. Individual specimens were placed in 1-in. diam by 2-in.-long tantalum capsules. Approximately 1 g of clean, high-purity calcium was placed in the capsules and an end closure arc-welded in place. The tantalum capsules were sealed in Inconel crucibles to protect the reactive metals from oxidation. The entire loading procedure was done in a glove box filled with pure argon. The loaded crucibles were placed in a muffle furnace, controlled within 2OC of the desired temperature, for a measured length of time. After the specimen had cooled to room temperature, it was sectioned perpendicular to the large faces and through the mid-point of two of the sides. The sectioned specimen was mounted and polished through Linde A abrasive. The rim which was free of thorium-oxide particles could be clearly observed microscopically as mechanically polished. Twenty measurements of the thickness of the rim were made at equally spaced points far enough from the end of the

Jan 1, 1962

By John J. McKetta. Jr., Louis B. Lesem, George H. Fancher

The proration of oil produced in the field frequently is based partially or entirely upon the gas-oil ratio of wells. The measurement of the gas-oil ratio is one of the more important field tests in regulatory and pro-ration work, and the test always should be conducted according to standardized methods and procedure. Obviously, the gas-oil ratio and the volume of gas produced by a well depend upon many factors but should be independent of the method of measurement and of the devices used to measure gas and oil. Consequently, the volume of gas accompanying a barrel of oil produced by a well may be measured by any reliable and accurate device or instrument. Frequently either a critical flow prover or an orifice well tester is used for this purpose, and for a particular well the same rate of flow of gas should be obtained regardless of whether a critical flow prover or an orifice well tester is employed in the test. In Texas, when using either instrument, either Capacity Table 1 or 5' is employed in making the necessary computations. If the tables are used, a discrepancy always is found whenever the two instruments are compared by extrapolation to the same conditions of flow. Clearly, Tables 1 and 5 must be at fault in some respects. The orifice well tester and the Bureau of Mines type of critical flow prover are essentially the same instrument; both devices utilize a square-edged orifice 1/8 in. in di-ameter as the primary element, and both freely discharge gas to the atmosphere. Tables for the orifice well tester' have been published in the ranges of 0 to 15 in, of water and 0 to 40 in. of mercury (Hg) differential in pressure. Coefficients for the critical flow prover have been published for differentials in pressure greater than 75 psia. An extrapolation of either differs from the other set of data as much as 18 per cent at some points. No immediately obvious reasons for the discrepancy was found, and data available from the literature were insufficient to effect reconciliation. Consequently, a series of experiments was performed to check the available data and to determine discharge coefficients for the two devices in an overlapping range of differential pressure. The correlating equation used in preparation of tables such as Tables 1 and 5' is the so-called hydraulic equation, Q = C1 vh .....(1) The tables cover orifice sizes from 1/8 through 1 1/4 in. A second set of tables, for use with greater differentials in pressure, apply only to the 3/4, 1, and 1 1/4-in. orifice plates over a pressure range of 0 to 40 in. of Hg. The correlating equation used in preparation of the tables is Q = C2 vH(29.32 + 0.3H)/G . (2) Each of these equations is valid only for the range to which it has been applied, and neither equation is valid for extrapolation. Theoretical equations for flow through an orifice are based upon assumptions of fractionless flow and an emergent jet the size of the orifice. A multiplier, C,, called the discharge coefficient, is inserted into the theoretical expression to compensate for both frictional losses and the contraction of the jet experienced in the plane of the orifice. Buckingham3 shows that C, should vary with the ratio of upstream to downstream pressure for flow of a compressible fluid at any average linear velocity through the orifice less than the velocity of sound. Work published by the National Advisory Committee for Aeronautics4 indicates that the variation continues into the so-called critical flow region until the vena contracta coincides with the plane of the orifice. The NACA work, however, does not indicate a leveling off of the coefficient. The work of the Bureau of Mines5 for the critical flow prover was based on differential pressures greater than 75 psi and indicates that the discharge coefficient, Cd, is constant in this region at a value of about 0.86.

Jan 1, 1958