By B. S. Blakeney, E. P. Abrahamson II

The effect of the transition elements in binary solid-solution additions upon the recrystallization temperature of iron has been investigated. All these elements immediately raised the temperature, the majority having their greatest effect in less than 0.10 at. pct. A correlation is noted between the rate of change of recrystallization temperature with atomic percent solute and the electron configuration of the solute element. THE work of Abrahamson and rant' on binary chromium-base alloys indicated that a correspondence existed between the effect of each solute element on the brittle-to-ductile transition temperature of chromium and the ground-state electron configuration of the element added. This was felt to be a bonding phenomenon and would be expected to be observed in measurements of other properties involving the breaking or exchange of atomic bonds. From this work it was postulated that a like correspondence should be found for other properties of binary alloys, such as recrystallization. This study is an effort to check this postulation using binary solid-solution iron-base alloys. Previously, the majority of recrystallization studies were carried out on steels. However, Tammann2 investigated the recrystallization of iron as effected by Co, Ni, Si, Mn, Mo, and Cr and stated that elements with the same crystal structure at room temperature as iron appeared to be more effective in raising the recrystallization temperature. Austin, Luini, and Lindsay3 studied the effects of Ni, Cr, Mn, Co, Si, and Mo on cold rolling and annealing, but noted no trend. Abrahamson and rant,' in their work on the effect of both substitutional and interstitial elements upon the brittle-to-ductile transition of chromium, have shown that the outer electron configuration in the ground state of the solute element appears to be the prime determinant of the transition temperature. PROCEDURE All alloys were made using 99.95 + pct Fe with 0.02 wt pct 0, 0.004 pct C, and 0.001 pct N. All alloying elements were 99.9 + percent pure. Metal-lographically the alloys, out to at least 0.1 at. pct, appeared to be in solid solution. Though several published phase diagrams tend to dispute this.4 All alloys were arc melted six times and cast into square 400-g ingots under an argon atmosphere.

Jan 1, 1961

The Ashanti mine is located in the Gold Coast region of West Africa in Ghana, where gold is found over a wide area of about 105,000 sq km (40,000 sq miles). Ashanti has been the most productive of all the lode mines and has been one of the world's notable gold producers for over 50 years. The mine is located at Obuasi, 113 km (70 miles) north and east of Tarkwa, which is 80 km (50 miles) inland from the coast. The Ashanti lode is worked on 300 m (1,000 ft) of strike length over a width of 12 m (40 ft), and by 1934 it had attained a depth of 700 m (2, 300 ft). The lode is in pre-Cambrian granite intruding a system- of shists, phyllites, etc., containing fragments of the wall rock with quartz, carbonates, sericite and small amounts of pyrite, arsenopyrite, sphalerite, galena, and gold. The shattered quartz fractures carry sulfides and gold, most of which are invisible. (William Harvey Emmons, "Gold Deposits of the World," McGraw -Hill, 1937.) Because the mill treats an ore composed of refractory sulfides - chiefly arsenopyrite and fine free gold - the flowsheet reflects the complex ore characteristics. Plane tables are used in the grinding, circuit for free gold recovery. After roasting the sulfide flotation concentrates, additional free gold is recovered from the calcines with a rotary belt concentrator and the two concentrates are combined for feed to the amalgamation pans, with the resulting gold amalgam being retorted. Following four-stage crushing to minus 9. 5 mm (318 in.) with two stages of grinding, the cyclone overflow is floated for sulfide recovery. The flotation concentrate is roasted with the calcine reground and roughly cyanided to scalp out the gold readily dissolved in one of two cyanidation circuits. The cyanide residue joins the thickened flotation tailing for cyanidation in a complete CCD circuit using filters. The gold precipitates are calcined before melting in pot-type furnaces. The tonnage to the mill of 3,175 mtpd (3,500 s tpd) with a content of over 14.7 g per mt (0.43 oz per st) places the Ashanti production as one of the top producers in the world; and with its past long life, the total production rates it as one of the world's great mines.

Jan 1, 1981

By G. E. Perry, J. F. Bruskotter, D. G. Russell, J. H. Goodrich

The depletion performance of gas wells has been investigated by mathematical simulation techniques. The gas well model which was studied consisted of a single well located in the center of a bounded, cylindrical, homogeneous reservoir. Dependency of gas compressibility and viscosity on pressure was considered in studies of well performance at both constant mass flow rate and constant flowing pressure conditions. To carry out the investigation, the nonlinear, second-order, partial differential equation which describes Darcy flow of a nonideal gas through porous media was solved numerically. Some of the previous investigations of gas well performance have been of limited general use, because assumptions were introduced to simplify either the gas properties or the basic differential equation. Other studies have been rigorous in these respects but have presented a very limited set of calculated results. The present study was attempted to present a rigorous theoretical model and sufficient numerical results to permit meaningful conclusions to be drawn. It was found that all terms must be retained in the partial differential equation to make accurate predictions. The neglect of higher-order terms, e.g., terms of the order of the "gradient squared", leads to serious material balance errors at large times and to conservative estimates of gas well performance. The higher the gas flow rate and/or the lower the permeability-thickness product of the formation, the more pronounced are these deviations. For example, in a well draining 640 acres in a 25-md-ft formation (8,120 MMcf gas in place) at a constant rate of 993 Mcf/D, the rigorous solution predicts a bottom-hole pressure decline from 4,000 to 1,000 psia in 8.7 years. If higher-order terms are neglected in the differential equation, this decline in pressure is predicted to occur in 5.3 years. With the results of the numerical solution of the differential equation as a basis, simple, easy-to-use approximations for predicting gas well performance for Darcy flow conditions have been developed. These simple approximations are based on the familiar equations for flow of a single, slightly compressible fluid. The approximate methods possess a high degree of accuracy and enable the prediction of long-term gas well performance to be made quickly and accurately without the use of a digital computer. Both transient and stable flow period approximations were developed. INTRODUCTION In recent years income from the sale of natural gas and associated products has represented an ever-incre as ing fraction of the industry's total revenue from operations. To meet the surge in demand for natural gas, the industry has depended heavily upon established reserves and has actively pursued development of new reserves. The search has progressively led to reservoirs which yesterday were too tight and/or deep to yield the desired return on invested capital. More than ever before, evaluation accuracy is now required to forecast the criteria upon which engineering recommendations and management decisions are based. Considerable effort has been expended by both research and operations personnel on the development and application of methods for analyzing and predicting the performance of gas wells. Fundamentally, the problem is the familiar one of extracting data during the drilling, testing and early production life of a well and applying these data within an accurate simulation model to predict long-term behavior. During the past 30 or more years a voluminous literature dealing specifically with gas field problems has been generated. A recent book' lists a comprehensive bibliography of published material through 1959. Over 1,200 references are cited. Since then 39 additional articles on natural gas technology have been published in Transactions volumes of the Society of Petroleum Engineers of AIME. Most existing theory for predicting gas well performance requires that one or more idealizations (e.g., steady-state flow, ideal gas of constant viscosity, small and constant compressibility and constant-viscosity fluid) be applied. Although existing theory may apply directly or be adapted by various artifices to describe specific gas well and reservoir behavior, no widely applicable method is available, and existing methods appear to be subject to appreciable error unless better limits of applicability are defined. The objectives of this paper are (1) to present numerical solutions to the partial differential equation describing gas flow under conditions of general interest in gas well performance prediction work, (2) to present solutions which possess a high order of accuracy for both transient and stabilized flow periods of a well producing at constant rate or constant pressure, and (3) to develop and present simplified relationships which can be used as high-order approximations to the exact numerical results for fast and accurate predictions of gas well performance at the operating level. Combined, these objectives are designed gen-

Jan 1, 1967

By Nathaniel Herz

The formula very frequently used for computing the economical size of pipe to transmit compressed air is that of D'Arey, as follows: D = cV w1l Where, D = the volume of compressed air delivered in cubic feet per minute, at the final pressure. c = an experimental coefficient determined for the various sizes of pipe, d = the diameter of the pipe in inches. 1 = the length of the pipe in feet. p, = the initial gauge-pressure in pounds per square inch, p2 = the final gauge-preesure in pounds per square inch. w1 = the density of the air, or the weight in pounds per cubic foot at the initial pressure, p1. The most common case is that in which the given quantities are: the quantity of air required, the length of the pipe, and the initial pressure. The method of solution is to assume a pressure-loss and to compute the remaining factor, cd5, thus giving the size of pipe corresponding to the assumed loss of pressure. It is always desirable to try two or more pressure-drops, in order to find the combination that is most satisfactory, since often a small change in the size of pipe will reduce or increase the loss of pressure several pounds. An alternative method is to assume a size of pipe and calculate the corresponding pressure-drop. Each method involves a series of tedious calculations to arrive at the most economical solution, and also requires the use of tables giving the constant, c, the density of the air, w1, and often, for convenience, a table giving the values of the expressions p1-p2 and c J I hare constructed a graphic chart, Fig. 1, for the solution of

Jan 1, 1913

By Murray F. Hawkins

One problem of reservoir engineering is the early estimation of the size of newly discovered reservoirs. Often these reservoirs are the expansion type in which sizeable pressure drops occur incident to the production of small fractions of the oil reserve, above the bubble point, and a material balance equation may be solved to find the reserve. The early form of this equation' considered only the compressibility of the oil. Later Hall2 showed that the compressible nature of the formation rock is a significant factor in production above the bubble point, and he presented a new equation which includes a formation (rock) compressibility term. This note presents a further extension of the material balance equation as applied to volumetric, unsat-urated reservoirs above the bubble point by including a term for the presence and compressible nature of the interstitial water. DERIVATION OF EQUATION During a decline in average reservoir pressure, ?p ?p, — p1 the initial reservoir volume V,, will decrease to some value V, due to the reduction in pore volume as a result of a decline in the hydrostatic pressure within the formation, and v, = V,, [l — cr ?p]......(1) The formation compressibility c, is expressed in terms of change in pore volume per unit pore volume per psi. Simultaneously the connate water within the formation expands from an original volume V,, = S,V,, to a new volume V,, V, = s,v,, [I + c,npl.....(2) The difference [Vp — V,] is the hydrocarbon pore volume at pressure p and may be equated to the volume of the remaining oil, or [N — N,] B, = V,,, [I - C~A;] - S,.Vpi [l + cwnjl.........(3) But the initial oil in place in terms of the initial reservoir volume, connate water, and formation volume factor is Ilividing Equation 3 by Equation 4 eliminates V,, to give,

Jan 1, 1956

By Stanley Herold

Considerable interest has been shown, during recent years, in the possibilities of developing oil fields in the South American Republics, now that the exhaustion of our present fields can be seen in the not very distant future. The demand for fuel oil and its products has been increasing far more rapidly than our increment of production during the last few years. Increase of consumption has been largely curtailed by the lack of sufficient supply. The main factors that have contributed to our previous neglect of the southern fields have been as follows:, (a) Lack of sufficient demand for the product. (b) Competition with producing fields, having large production, low cost, and better geographical position, such as Tampico, Mexico. (c) Greater interest in home fields with ready market at hand. (d) Our ignorance of southern economic and geologic conditions, clue to the distance between those areas and our financial centers. (e) Economic conditions in the southern countries, necessitating high costs of exploration and exploitation of the fields.

Jan 9, 1918

By AIME AIME

MINERAL production of the United States is valued at over five billion dollars a year at present and the industry employs close to a million workmen, yet such maps as are available that might indicate the geographical distribution of this industry show only the location of coal and oil fields and of other mineral deposits. No recent map is available that shows this distribution in a quantitative way. The purpose of the maps and graphs here presented is twofold: (1) to give the mining engineer a clear conception of the relative value and the pattern of distribution of minerals in the United States; (2) to test the so-called block-pile (or grouped pillar) system of statistical mapping, which makes this presentation possible. (I discussed this method of mapping in an article which appeared in Economic Geology in 1939, Vol. 15, p. 185-188.)

Jan 1, 1941

By S. M. Purdy

Under certain conditions of hot rolling and air cooling from the hot-rolling temperature, bars of a high carbon (0.40 pct C) chrome-nickel austen-itic alloy were found to show magnetism even though no ferrite or martensite could be detected by microscopic or X-yay methods. The appearance of magnetism in such alloys may come from chromium impoverishment of the austenite grains near the precipitated carbide particles. SPORADICALLY, hot-rolled bars of Silchrome 10, an exhaust valve steel, have been found to be magnetic. Because of the analysis of the alloy—0.40 pct C, 18 pct Cr, 8 pct Ni, 3 pct Si —magnetism is unexpected. Preliminary investigation showed neither martensite nor ferrite to be present; only austenite and Cr23C6. Since a literature search was fruitless, a brief study was made of the appearance of magnetism in this alloy. The only basic difference between the two heats is the nitrogen content. Permeability was measured using a Severn magnetic gauge. This instrument consists of a magnet mounted on a counterbalanced arm. A set of calibrated plugs is placed in contact with one pole of the magnet. The specimen is placed close to the other pole of the magnet. If the specimen pulls the magnet away from the plug, it has a permeability greater than that marked on the plug. This technique is swift and reproducible. Previous experience has shown that the permeabilities obtained corresponded to those obtained on a permeater with a field strength of 100 oe. Specimens from both heats were annealed at temperatures between 1700 and 2300°F. One set of specimens was water cooled and another furnace cooled. All the water-quenched specimens were non-magnetic; the furnace cooled ones were magnetic as shown in Table I with no difference being observed between the two heats. Microstructural examination of the specimens showed the expected increase in carbon solubility with increasing temperature. Carbide solution was complete at 2200°F. The specimens heated to 1900°F or below showed some carbide precipitation from the hot-rolled structure. A furnace cooled specimen from a given temperature showed less carbide out of solution than the water-quenched specimen from the next temperature below; e.g., the specimen furnace cooled from 2100°F showed less carbide out of solution than the water-quenched specimen from 2000" F. These studies indicated that the appearance of magnetism was not related to the quantity of carbon in or out of solution and it was related to precipitation at temperatures below 1700" F. A set of samples annealed and water-quenched from 2100° F was aged for 4 hr at temperatures between 1000" and 1600°F; all were non-magnetic. A second set of samples, similarly annealed, was aged 1 to 24 hr at 1200°F with the results shown in Table II. None of the latter set of specimens showed magnetism until they had been aged about 8 hr. Magnetism was quite strong after aging 24 hr. X-ray diffraction studies on several of the magnetic specimens showed that the austenite had a lattice parameter of 3.58A and that the carbide was Cr23C6. Several of these samples were electrolytically digested in 10 pct HCl in ethanol, with a current density of 0.1 amp per sq cm. None of the particles in the residue were magnetic. Accidentally, one cell was run at 1 amp per sq cm; e.g., magnetic particles were found in this residue. After careful separation, the magnetic particles were mounted on a quartz fiber and their diffraction pattern determined using a 5.73-in. Debye-Sherrer camera with CrK radiation. These particles showed a fcc structure with a lattice parameter of 3.57A. Prolonged exposure, up to 16 hr, produced no other lines on the film. The following facts seemed to be established at this time: 1) Austenite was the magnetic phase. 2) Neither ferrite nor martensite could be detected. 3) Magnetization could be produced by aging at 1200°F. One explanation of these data is that the carbide precipitation impoverishes the region immediately around the carbide particle of carbon and chromium and increases the proportion of nickel. All of these serve to increase the Curie temperature of the region around the carbide particle. If the composition change is enough, the Curie temperature will rise above room temperature. If the volume of the affected region is great enough, the magnetism will become detectable. At low aging temperatures, composition changes are great enough but the overall volume of impoverishment is quite small

Jan 1, 1962

By W. C. Winegard, J. R. Carruthers, A. Plumtree, L. R. Morris

The unidirectional solidification of dendrites containing central twin planes was studied in A1-Ti alloys. Once nucleated, the twinned dendrites are a Twore ejficient form for solute redistribution and therefore grow in preference to the normal columnar dendvites. Comparison of these twinned dendrites to adjacent colunmar dendrites by means of decanting experinzents and electron-probe rnicvoarmlysis indicates that these special dendrites grow with less undercooling than normal dendrites. These findings are further supported by the effect of forced convection on the dendrite morphologies. COMMERCIAL semicontinuous cast ingots of most aluminum alloys frequently exhibit large grains which appear to be composed of hundreds of parallel, continuous, thin lamellae. This structure has been termed "basaltic",' "fiederkristall", or, commonly, "feathery grain". The lamellae are 'about 100 p thick, several inches long, and each lamella contains a central (111) coherent twin boundary. The feathery grain has been reported to have a (112) direction2 and a (110) direction4 in the twin plane parallel to the casting direction, in contrast with the usual columnar structure where a (100) direction predominates. Aust et uZ.~ proposed that the twin boundaries were growth twins nucleated by stacking faults on the octahedral planes. chalmers6 has suggested that feathery grain may grow by a re-entrant edge mechanism, as proposed by wagner7 for twinned dendritic growth in germanium. Cahn et ~1.~ have concluded that the occurrence of feathery grain is evidence of some form of lateral layer growth rather than the atomically continuous growth normally observed in metals. The postulates by Chalmers and Cahn would seem to be contradicted by the work of Nakao~"' who showed that feathery grain only occurs when growth rates are high and the aluminum contains some solute. Specifically, Nakao found that in order to obtain feathery grain, in small castings solidified unidirec-tionally upward, the rate of growth must be above 2.4 cm per min and a critical solute concentration must be present. Below this solute concentration the grain structure was totally columnar. The critical solute concentration was found to be approximately: 0.04 wt pct Ti, 2 wt pct Cu or Mg, and 8 wt pct Zn. As pointed out by Chalmers it is not obvious why a twin-plane re-entrant edge mechanism would occur in aluminum which is thought to have a diffuse solid-liquid interface. The present experiments were undertaken to determine the growth mechanisms in- volved and to study the solute segregation in more detail. EXPERIMENTAL PROCEDURES Alloys ranging in composition from 0.05 to 0.23 wt pct Ti* were prepared from 99.9 pct pure Ti and 99.993 pct pure Al. Two-hundred-gram samples of A1-Ti binary alloys were solidified unidirectionally and vertically upward from a water-cooled copper base, in a heated insulated mold. The 1-in.-diam, 6-in.-length mold was made of Marinite (manufactured by Johns-Manville Co.). The mold was attached to a 24-in. pivoted arm such that by dropping a weight the mold was rotated 180 deg, throwing the liquid metal from the solid. In this way, the solid-liquid interface was revealed by decanting. A sketch of the decanting mold is shown in Fig. 1. The alloy was poured into the mold at temperatures ranging from 680" to 750°C, partially solidified by water cooling from the base, and decanted after a measured time interval. Growth rates for each metal-pouring temperature were calculated from solidification-time vs length solidified curves. Temperature gradients in the melt were measured using four No. 34 gage thermocouples which protruded into the mold cavity. Grain orientations were determined by X-ray diffraction using Laue back-reflection techniques. Grain substructures were examined metallographically, using polarized light, by applying a thin epitaxial anodic film to polished sections after the method of Hone and pearson." Titanium micro segregation was measured by electron-probe microanalysis using a NORELCO AMR/~ with a mica crystal and proportional-flow counter. Several of the cast samples exhibited feathery and columnar dendrites growing in the same direction and

Jan 1, 1967

PRESIDENTS DAVID THOMAS 1871 R W RAYMOND 1872-1874 A L HOLLEY1875 ABRAM S HEWITT 1876 T STERRY HUNT 1877 ECKLEY B COXE 1878 - 1879 WILLIAM P SHINN 1880 WILLIAM METCALF 1881 RICHARD P ROTHWELL 1882 ROBERY W HUNT 1883 JAMES C, BAYLES 1884-1885 ROBERT H RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B POTTER 1888 RICHARD PEARCE 1889 ADAM S HEWITT 1890

Jan 1, 1923

By Z. Moser, W. Ptak

The experiments were carried out by the method of measuring the electromotive force of concentration cells having zinc as a reference electrode, the second electrode being the liquid alloy Zn-Sn-Cd-Pb. The electrolyte consisted of liquid chlorides and had zinc ions. The measurements were made for seventy -five alloys of different mole fractions within the temperature range of 714° to 877°K. The experimental results enabled the calculation of the activity of zinc in tested solutions. The activities of zinc were calculated by means of Krupkowski's formulas.3 In addition, the formulas for coefficients of activity of zinc, tin, cadmium. and lead as the function of composition and temperature were given. Activity of zinc was compared with the values obtained from experimental results, and good agreement has been observed. On this basis it can be stated that the theoretical formulas are suitable for determining the thermodynamic properties of liquid quaternary metal solutions. IN the metallurgical processes being carried out at present multicomponent liquid metal solutions take part. For the thermodynamic analysis of these processes it is necessary to know the thermodynamic properties of these solutions. Therefore, many experimental and theoretical papers deal with this problem. The theoretical papers are generally based on the assumption that the structure of liquid metals is similar to their structure in the solid state. In this manner the model of liquid solution, consequently described by means of statistical thermodynamics, has been accepted. This method is being lately developed, especially for solid solutions. Statistical thermodynamics was applied among others by Guggenheim 1 for describing the thermodynamic properties. Unfortunately, the formulas of statistical thermodynamics are often not suitable for the interpretation of experimental results. Attention should be drawn to the relations obtained by means of formulas of phenomenological thermodynamics which always have constants derived with the aid of experimental methods. In the case of the multi-component solutions which contain some additions of impurities besides the basic metal, wagner2 introduced interaction parameters. Equations for the relationship between the activity coefficients and composition were also given by Krupkowski." he application of these formulas requires a good knowledge of the thermodynamic properties of the corresponding binary systems. In these formulas, as in Wagner's, there appear constants which should be determined from ex- perimental data. Nowadays, different experimental methods are applied for evaluating the thermodynamic functions of solutions, for instance: vapor pressure measurements, calorimetric methods, and the measurements of electromotive force of concentration cells. In the present paper this last method for evaluating the thermodynamic properties of four-component systems, Zn-Sn-Cd-Pb, was applied. For instance in the case of Zn-Sn solutions Alabyshev and Landratov, 4 Fiorani and Valenti, 5 and ptak6 performed the investigations. The Zn-Pb system was worked out by Kleppa 7 and Cd-Pb and Cd-Sn by Elliot and chipman.' This method was also applied for determining the activity of zinc in ternary solutions. 1) EXPERIMENTAL METHOD The experimental arrangement with detailed description is given in Fig. 1. It consists of resistance furnaces, one serving for melting samples and the other containing the flat-bottomed, measuring quartz tube with the liquid electrolyte. Liquid metals and alloys are in glass supremax tubes, which have an opening in their lower part above the metal level. This opening allows the filling of the tubes by the electrolyte. In these tubes tungsten wires are placed which by means of suitable conductors are connected with a potentiometer. It is assumed that tungsten dissolves Fig. 1—Schematic diagram of the experimental arrangement for the investigation of the thermodynamic properties of liquid metal solutions: 1, resistance furnaces; 2, autotransfor-mers; 3, galvanometers; 4, regulator of temperature; 5, gas purifier with concentrated H2SOP; 6, U-tube with P2O5; 7, thermostats; 8, steel block for thermostating; 9, supremax tubes for alloys; 10, tungsten electrodes; 11, inlet and outlet of argon; 12, measuring quartz tube; 13, tube for melting samples; 14, tube for thermocouple; 15, cover of quartz tube; 16, rubber seal; 17, bottom cover; 18, outlet of electrodes to potentiometer; 19, outlet of thermocouples to potentiometer; 20, upper view of the quartz tube cover; 21, orifices for cover screws; 22, orifice for argon inlet; 23, orifice for thermocouple; 24, orifices for tubes containing liquid metals; 25, inlet for water-cooling system.

Jan 1, 1969

By Henry J. Sandri

The use of economic models for forecasting purposes is an inexact yet necessary tool for mineral decision making. One method not commonly used is cyclical analysis because of its "non-scientific approach". However, under certain circumstances a modified cyclical approach can provide useful insight to mining companies. The current paper discusses mineral modeling, the type of economic models and the use of cyclical forecasting for mining firms (not speculators) involved in precious metals.

Jan 1, 1984

By Dale A. Vaughan, Oliver M. Stewart, Charles M. Schwartz

A. U. Seybolt (General Electric Research Laboratory)—The authors should be commended for adding some important information to our knowledge of the solubility of interstitial elements in metals. It is becoming increasingly evident that the effect of even traces of such elements have very far-reaching effects upon the mechanical properties of the body centered cubic metals. Those who have worked in this area know that the accurate determination of the small solid solubility limits in systems of the type reported by the authors is a quite difficult task, and it is therefore not surprising that frequently the results of different workers are not in agreement. It is instructive, and usually helpful, to plot the solubility results on log weight or atomic percent -1/T coordinates to find out if a straight line is obtained. A straight line is expected because in systems displaying solubilities of the order of 1 to 3 at. pet or less, Henry's law is usually obeyed—or at least well enough obeyed so that the deviation from linearity is not very appreciable. If Henry's law is obeyed, one canthen use the Van't Hoff Equation in the form In N = ?H/RT + C, where N is mole fraction, at. pet, or wt pet for small values, and AH is the partial molal heat of solution of the solute. R and T have the usual significance, and C is an integration constant. If one plots the reported nitrogen solubility values as indicated above, the three points fall reasonably well on a straight line. The oxygen values for the two upper temperatures fall very closely to the nitrogen values as shown in the authors' Fig. 15. However, the value at 500°C departs widely from the straight line established by the data at 1500" and 1000°C. It is, of course, true that one cannot place too much emphasis on the significance of a line established by only three points, but in the absence of reasons for anticipating deviations, data exhibiting wide departures from linearity should at least be examined closely. Fig. 16 shows the log at. pct -1/T plots for the authors Ta-O and Ta-Ndata including a solid circle point at 500°C and 1.8 at. pet for Ta-O, which is simply extrapolated from the two higher temperature points. In addition, the data of R. P. Elliott9 for Nb-O are shown. These points were picked off his curve and are not very exact, but as can be seen they line up well on a straight line. It is interesting, and probably significant, that the slope of Elliott's results is not far from those of Vaughn, et al. This is probably to be expected because one would anticipate that the partial molal heats of solution of oxyten in these two very similar metals should be not too far apart. AH for Ta-O is about -1900 cal per mol, while for Nb-O it is near -2300 cal per mol. Hence, this lends some support to the thesis that the point at 500°C for Ta-O is much too high. The data of Gebhardt and Preisedanz10 are also plotted, and it is seen that their data while lying on a linear plot, have an appreciably steeper slope. The possible reasons for this will not be discussed here except to point out that their pressure-composition data show anomalies which suggest that they may have been dealing with a different equilibrium from that being discussed. There is another consideration which would also suggest that the solubility at 500°C is lower than shown. The solubility values were obtained by the classic method of first establishing a lattice parameter-composition curve. This the authors did, and there is probably little doubt that it is quite accurate. Such a plot is generally almost error-free because it has a self-correcting feature in that any deviation from linearity makes a data point immediately suspect, and subject to confirmation. Unfortunately, this is not true with respect to the actual solubility values. These are obtained ordinarily by taking an alloy containing more solute than is soluble at some temperature and then thermally

Jan 1, 1962

By AIME AIME

THE report of the united. States Steel Corporation for the' year 1928 gives the, following ,figures of raw materials and' finished products . Raw materials, tons :

Jan 1, 1929

By R. Stickler, A. Vinckier

An optical and electron microscope study was made on a commercial 302 stainless steel heat treated for massive carbide precipitation. Convincirg evidence was obtained that the grain boundary precipitate does not grow away from the grain boundary into the matrix, but grows as a network of large thin dendrites in between the grains. IN austenitic stainless steels the carbon in supersaturated solution precipitates when the steel is heated in the temperature range 450" to 1000°C. During such heat treatments the chromium-rich carbide occurs primarily at the grain boundaries and has adverse effects on the corrosion resistance and low-temperature ductility of the material. It has been shown that the morphology of the precipitated particles differs widely depending on the time and temperature of the heat treatment, the nature of the boundary, the misfit between the grains, and so forth.1"5 It was assumed by Mahla et al.,' Streicher,' and Mc Nutt' that the carbide particles which nucleate in the grain boundary grow in various geometric or dendritic forms away from the boundary into the matrix. However, Kinzel,' Hatwell et a, and Plateau et aL4 found that the particles nucleate in the grain boundary and grow as a network of thin dendrites in the grain boundary interface. We have made a comprehensive studyg of the precipitation occurring in a commercial 302 austenitic stainless steel heat treated for times ranging from 0.15 to 1500 hr at various temperatures from 480" to 1065"~. This study was made to elucidate the influence of heat treatments on both the mechanical and the corrosion properties of this steel. Part of this investigation which is pertinent to the morphology of the grain boundary carbides referred to above is separately reported here. We found that the particles which nucleated in the boundaries grew in the interface of these boundaries, thus supporting the viewpoints of Kinzel,' Hatwell et al.,3 and Plateau et al.4 Furthermore, when carbide particles nucleated in the matrix very close to the boundaries, they possessed a morphology distinctively different from the particles growing in the grain boundaries. MATERIAL A study of metallographic samples and of fracture surfaces of a 302 stainless steel is reported in this paper. The composition and heat treatments are listed in Table I. Polished and etched samples were examined und813r the optical microscope, and carbon extraction replicas of etched micrographic samples and various fracture surfaces3'8'9 were examined under the electron microscope. RESULTS AND DISCUSSION A representative optical micrograph of the 302 steel, condition A, is shown in Fig. l(a). Particles can be seen on the grain boundaries but no traces can be found of particles which grow from the grain boundaries into the matrix. A carbon extraction replica of this sample shows numerous large thin dendrites, Fig. l(b). The lateral dimension of such carbide particles vary up to 100 p, and their thickness estimated from the amoun! of electron penetration i:; between 500 and 1000A. Such large dendrites are extracted from almost all grain boundaries and, if they had grown into the grains, they would definitely be revealed by etching traces in the matrix, Fig. l(a). The reason why these large dendrites on the extraction replica appear to be grown into the grain is due to the mechanism of the extraction replica process. Thus, these dendrites are supported by the carbon replica film only at the edges originally along the grain boundary trace A-A, Fig. l(b), in the polished metal section and have subsequently fallen over onto the carbon replica film during handling. Although such dendrites generally fall only to one particular side of the grain boundary trace, one finds occasionally that parts of a dendrite have fallen to both sides, as shown in Fig. l(b). Further evidence for the growth of carbide in the grain boundary can be obtained from the appearance of fracture surfaces. A small impact specimen of the 302 steel, condition A, was broken at liquid nitrogen temperature. The fracture path follows the

Jan 1, 1962

Henry Louis, Newcastle-upon-Tyne, England (communication to the Secretary): I think very highly of the novel and ingenious device of Prof. Richards for analyzing the movement of the various elements of the jig; it is a method that certainly seems to promise valuable results, if we could only make certain that these various indicator-appliances have no effect upon the action of the jig. I would like, however, to suggest that in future experiments the connection between the plunger indicator-rod and the pencil should be made by means of parallel motions, so as better to reproduce the rectilinear motion of the piston. I should expect, if this were done, that the " curve " of the plunger in the Harz jig, at any rate, would be represented either by straight lines or else by quite regular curves, according to the method by which the plunger is set in motion; the apparent combinatioil of straight line and curve seems difficult to explain. With respect to the water-curve, I am afraid I am completely at fault, but no doubt Prof. Richards can explain my difficulty. In Fig. 2, the areas of the screen-side and the plunger-side of the jig are equal. If the piston be a fair fit and the bottom of

Jan 1, 1897

By C. J. Guntner, R. P. Reed

A commercial 18Cr-8Ni iron alloy (AISI 304L) was examined in tension at 300°, 76°, 20°, and 4°K. Continuous stress-strain recordings were made, X-ray analyses at periodic stress (strain) intervals were obtained, and the magnetic measurements were taken. From this data the percentage of martensitic products [bcc(a) and hcp (E)] was computed as a function of stress (strain). It was found thatup to 15 pct E phase forms at low temperntures. The amount of E formed increases to a maximum at about 5 pct strain, then decreases. This decrease indicates the additional transformation of E to a'. The total amount of E and a' was suppressed at constant stress (strain) at 4°K as compared to 76°K. It is proposed that the suppression of E and a' is associated with the decreased mobility of extended dislocations at very low temperatures. The yield strength decreased as the temperature was depressed below room temperature and then increased rapidly near 4°K. SOME ferrous alloys which are austenitic (fcc ?) at room temperature appear to be unique in that two martensitic products (hcp e and bcc a') may form on cooling to lower temperatures or on application of mechanical stress. The most common room-temperature austenitic ferrous alloys are 18Cr, 8Ni stainless steels. Most aspects of the spontaneous transformations have been previously described for these steels.' Several previous papers have described special aspects of the stress-induced transformations at low temperatures for the stainless steels, such as the existence of the hcp phase (c) after straining at 76oK,2-7 the morphology after straining using electron microscopy,7 and the decrease in E at higher strains at 76oK.4 However, for a complete representation, one must know the stress-strain characteristics and the dependence of both martensitic products on applied stress and temperature. It is the intention of this paper to provide that documentation. To accomplish this, continuous stress vs strain recordings were made at four temperatures: 300°, 76", 20°, and 4°K for annealed AISI 304L (a commercial 18Cr-8Ni alloy). At periodic stress intervals at each temperature the integrated X-ray line intensity of a selected peak for each phase (y, E, and a') was measured. In addition, photomicrographs of the strained surfaces were taken and magnetic measurements were made. The magnetic readings can be directly converted into percent a'.',e With these measurements the percentage of each phase may be plotted as a function of stress (or strain) and test temperature. It was found that up to 15 pct E phase forms upon stressing the AISI 304L alloy at low temperatures. The E percentage increases abruptly after the alloy yields, but then decreases gradually at higher stresses. The rapid increase in e at 76°K is associated with an "easy-glide" portion of the stress-strain curve. The total amount of a' + .G is suppressed below 76°K at a constant stress or strain. The yield strength decreases down to 76°K but increases rapidly below 20°K. EXPERIMENTAL PROCEDURE Tensile test specimens were cut parallel to the rolling direction from 0.1-in.-thick sheet. Continuous stress vs strain recordings were obtained at each test temperature (300°, 76o, 20°, and 4°K) using equipment and methods described elsewhere.' The specimens which were used in the X-ray analysis were stressed to successive increments of strain at each temperature, analyzed at room temperature, then restressed at the test temperature. This procedure was repeated until approximately ten X-ray analyses had been performed with approximately 1.0 pct strain increments. The specimens had a reduced section 1 in. long, 1.2 in. wide, and 0.1 in. thick. They were electro polished prior to testing and after each strain increment. Table I lists the chemical composition, grain size, and hardness for the alloy which was used. This is the same alloy for which extensive mechanical-property tests3 and morphological studies of the spontaneous transformations' have previously been made. For the low-temperature tests (76o and 4°K) below the Ms temperature the specimens were initially cooled to the test temperature, held for 1/2 hr, then warmed and X-rayed at room temperature. The results are listed in Table 11. From earlier work8 it was known that additional transformation on the second cycle would be considerably less (-0.1 pct

Jan 1, 1964

By P. B. Baxendell, R. Thomas

Work on the calculation of vertical two-phase flow gradients by Cia. Shell de Venezuela has been based mainly on the "energy-loss" method proposed by Poett-mann and Carpenter in 1952. The "energy-loss-factor" correlation proposed by Poettmann and Carpenter was based on relatively low-rate flow data. This correlation proved inapplicable to high-rate flow conditions. In an attempt to establish a satisfactory correlation for high rates, a series of experiments was carried out at rates up to 5,000 BID in Cia. Shell de Venezuela's La Paz field in Venezuela, using tubing strings fitted with electronic surface-recording pressure elements. As a result of these experiments a correlation between energy-loss factor and mass flow rate was established which is believed to be applicable to a wide range of conduit sizes and crude types at high flow rates (e.g., above 900 BID for 27/8-in. OD tubing). It is anticipated that the resulting gradient calculations will have an accuracy of the order of % 5 per cent. At lower flow rates the energy-loss factor cannot be considered as constant for any mass rate of flow, but varies with the free gas in place and the mixture velocity. No satisfactory correlating parameter was obtained. As a practical compromise for low flow rates, a modification of the curve proposed by Poettmann and Carpenter was used. In practice this was found to give gradient accuracies of approxirnately ± 10 per cent clown to flow rates as low as 300 B/D in 27/8-in. tubing. INTRODUCTION Production operations in Cia. Shell de Venezuela's light- and medium-crude fields are principally concerned with high-rate flowing or gas-lift wells. Under these conditions the analysis of well performance, the selection of production strings and the design of gas-lift installations are vitally dependent on an accurate knowledge of the pressure gradients involved in vertical two-phase flow. Initially, attempts were made to establish the gradients empirically as done by Gilbert,' but the results were not reliable due to scarcity of data over a full range of rates and gas-oil ratios. Several methods of calculation based on energy-balance considerations were attempted, but the computations were cumbersome and the results cliscouraging. In 1952 a paper was published by Poettmann and Carpenter' which proposed a new approach. Their method was also based on an energy-balance equation. but it was original in that no attempt was made to evaluate the various components making up the total energy losses. Instead, they proposed a form of analysis which assumed that all the significant energy losses for mutiphase flow could be correlated in a form similar to that of the Fanning equation for frictional 1osses in single-phase flow. They then derived an empirical relationship linking measurable field data with a factor which, when applied to the standard form of the Fanning equation, would enable the energy losses to be determined. The basic method was applied in Venezuela to the problem of annular flow gradients in the La Paz and Mara fields" This involved establishing a new energy-loss-factor correlation to cover high flow rates and, also, some adaptation of the method to permit mechanized calculation using punch-card machines. The final result was 1 set of gradient curves for La Paz and Mara conditions which proved to be surprisingly accurate. With the encouraging results of the annular flow calculations, several attempts were made to obtain a corresponding set of curves for tubing flow. Here, unfortunately, little progress could be made. The original correlation of Poettmann and Carpenter was based on rather 1imited data derived from low-rate observations in 23/8- and 27/8-in. OD tubing. It did not cover the higher range of production rates, and extrapolation proved unsuccessful. A new correlation covering high flow rates was required, but this proved to be extremely difficult to establish since tubing flow pressure measurements at high rates did not exist—due to the difficulty of running pressure bombs against high-velocity flow. The necessity for reliable tubing flow data increased with the development of the new concessions in Lake Maracaibo, where high-rate tubing flow from depths of 10,500 ft became routine. Thus. it was decided to set up a full-scale test to establish a reliable energy-loss factor for tubing flow conditions. A La. Paz field light-oil producer with a potential of approximately 12,000 B/D on annular flow was chosen. To obtain full pressure gradients, a special tubing string was installed which was equipped with electronic surface-recording pressure measuring devices,

Among the recent bulletins are the following, which. may be obtained from the Superintendent of Documents, Government Printing Office, Washington, D. C. BULLETIN 127. Gold dredging in the United States, by Charles Janin. 1918. 224 pp;, 63 pls., 23 figs. 50 cents. BULLETIN 161. California mining statutes annotated, by J. W. Thompson. 01918. 312 pp. Paper cover 20 cents. BULLETIN 169. Illinois mining statutes annotated, by J. W. Thompson. 1918. 594 pp. Paper cover 35 cents. The. Potash Situation, by A. W. Stockett. 13 pp. Preparation of Crucible Graphite, by George D. Dub. 27 pp. National Importance of Allocating Low-ash Coke to the Manganese-alloy Furnaces, by P. H. Royster. 4 pp. Production of Ferromanganese in Blast Furnaces, by P. H. Royster. 31 pp. Production of Spiegeleisen in Blast Furnaces, by. P. H. Royster. 19 pp.

Jan 6, 1919

By A. V. UDELL

OF all the metals that have from time to time been called the "Wonder Metal," mercury, often called quicksilver, is probably the most deserving of this designation. A wonder metal it must have been to those workers of an earlier day who named it after that Latin god of commerce and gain, characterized as the fleet messenger of the gods and the conductor of souls to the lower world. The word mercury has been used to indicate a carrier of tidings, a bearer of news, a nimble or clever person, a hawker, and a skillful thief. All of these attributes, and more, are recognizable in this metal, the technical terminology of which is "Hydragyrum," meaning water-silver, and from which the chemical symbol "Hg" is derived. Fickle in its occurrence in nature, simple in its metallurgy, illusive in captivity, it serves man in life or death, in war or peace, in commerce, science and arts, in mining, agriculture, and forestry with a versatility found in no other element.

Jan 1, 1929