By Henry Fay

The erosion of guns is a complex problem which can be solved only by a detailed study of all the factors involved. In the present paper it is proposed to submit the results of observations and experiments which have extended over several years. Certain facts have been established and preliminary reports have been published.' Conclusions have been reached since then which, it is believed, are worth presenting for the purpose of promoting discussion, and with the hope that ultimately the whole truth will be known. The particular phase of the problem which will be presented here is the hardening of the inner surface of the gun tube. It has been known for a long time that after firing a large caliber gun for some time, the surface of the metal becomes hard and brittle, cracks, and wears away.2 The character of this phenomenon may be learned by an examination of some results which are typical, obtained from a detailed study of a 12-in. gun. The gun was trepanned and rings representing various sections of the gun were cut out for examination. The first ring represented the metal at the muzzle end, and the other rings were removed at approximately 120, 240, 325 and 337 in., respectively, toward the breech end. The appearance of the surface of the metal in the different sections is shown in Fig. 1. The greatest amount of wear and maximum amount of hard surface layer was found in section marked E, which is nearest the powder chamber and at the beginning of the rifing; the maximum amount of cracking in D; the maximum amount of copper deposition in C. Section B showed heat cracks on both lands and grooves, and section A showed heat cracks on the driving edge of the lands only. There was much flow of metal in both sections E and D, and there was progressively less effect noticeable toward the muzzle end. The polished cross-section of these same pieces is shown in Fig. 2. The extent of the erosion is greatest nearest the powder chamber, and diminishes toward the muzzle end.

Jan 1, 1917

By Frederick Laist, H. J. Maguire

The ore from the Butte mines of the Anaconda company is quite siliceous; that is, it contains considerably less iron than is needed for the fluxing of the silica. The direct smelting of this ore, therefore, requires the addition of considerable fluxing material. The only flux available in sufficient quantity at Anaconda is limestone containing no metallic minerals. This necessarily makes the direct smelting of the ore so expensive that it is more profitable to subject the ore to a preliminary treatment by concentration. However, as the losses in the concentrator were very high, compared with the losses in the blast furnaccs, it was found, by calculation, more profitable to send ores containing more than a given percentage of copper to the blast furnaces, in spite of the higher costs of treatment. The dividing point was dependent on various factors, the chief of which was the prevailing market price of copper. It was customary, therefore, to segregate the ore as mined into two classes. Ore in the first class generally contained 5 per cent. or over of copper; this was sent directly to the blast-furnace department. Second-class ore contained less than 5 per cent. of copper, and averaged around 3 per cent.; it went to the concentrating department. With the introduction of the flotation process, it mas found possible to maintain an average recovery, as concentrates, of 96 per cent. At the same time, the cost of reverberatory smelting was very materially decreased by the use of pulverized coal. These two changes in practice made the blast furnaces unable to compete with the reverberatory furnaces on a cost basis. The distinction between first- and second-class ore was therefore abandoned, and the ore was treated by concentration. Obviously, on ores as high in iron as the Butte ores, the concentrator produces a product that is self-fluxing; in fact, it is possible to produce a concentrate containing more iron than is necessary to flux the silica. Under these conditions, the amount of basic fluxing materials required for the smelting operations became very srnall and the converter slag lost its former value as a blast-furnace flux. For this reason, a less expensive method of recovering the copper, silver, and gold contained in it than smelting in blast furnaces had to be found. It was not feasible

Jan 1, 1921

By Joseph Singewald

INTRODUCTION FOR a number of years Russia, India and Brazil have outranked .all other countries as producers of manganese ores. During the 5 years immediately preceding the European war, the average annual production of Russia was 844,000, of India 694,000 and of Brazil 200,000 long tons. Since the outbreak of the war there has been a considerable falling off in the Russian and Indian production, particularly in the former, whereas the production of Brazilian ores has been greatly increased, amounting in 1914 to over 250,000 tons and in 1915 to nearly 350,000, with conditions favorable for a still larger production in 1916. Manganese is one of the few industrially important metals that are not produced in the United States in quantity commensurate with our needs, so that we have been compelled to import annually about 300,000 tons, having a value of over $2,000,000, and these ores have been obtained from the three countries mentioned above. Their rank as contributors to our imports of manganese ores was India, Russia, Brazil; and in 1913, Brazil contributed only one-fifth. During the past 2 years Brazil has furnished rapidly increasing quantities to this country, and, with the falling off of imports from India and Russia, has become our principal foreign source. In 1914, Brazil furnished two-fifths of the imports and more than India or Russia, and in 1915 over nine-tenths. The manganese ores of Brazil are consequently of more than usual interest to us at this time.

Jan 10, 1916

By Arthur F. Taggart

The following notes represent significant excerpts from a mass of records of experimental work done in the ore-dressing laborattory at the Columbia School of Mines during the years 1926 to 1928 inclusive. Classification of Experimental Work The experiments performed may be grouped for purposes of description under the following general headings: I. Collecting agents. a. A method for quantifying collecting effect. b. Coating with undissolved collecting agents (oils). c. Action of dissolved collecting agents. II. Frothing agent's. a. A method for quantifying frothing effect. b. Relation between frothing effect and chemical composition. III. Inorganic reagents. a. Methods of studying the effects of these reagents. b. Effect on slime dispersion. c. Effect on sulfides. Summary of the Origins of Present-day Flotation Practice The first practicable, foolproof method of froth flotation was described in U. S. Patent 835120, issued in 1906 to Sulman, Picard and Ballot, and in the equivalent patents in other countries. A number of less simple methods of producing the same result had been described previously in patent publications and otherwise.' The reagents specified in all of these early patents were "oils" and, in addition, some inorganic substance, usually an acid. The quantities of reagents recommended and added were enormous when compared with those used today.

Jan 1, 1930

By Sandip K. Mitra, John E. Dorn

The Basinki-modified Seeger equation for deformation of metals by means of thermally activated intersection of dislocations was used to ascertain the various factors responsible for the strain hardening of poly crystalline aluminum and a series of a solid solutions of magnesium in aluminum. The analyses were based principally on the rate of change of strain rate with stress and the Cottrell-Stokes ratio. From measurements of these quantities on a series of strain-hardened states, the force displacement diagram for intersection, the density of dislocations in the entanglements, and the contributions of the athermal local stress and long-range stress interactions were deduced. Poly crystalline aluminum was observed to have the same force-displacement diagram for intersection as single aluminum crystals, and the corresponding diagram for the magnesium alloys differed in a manner that suggested that small amounts of magnesium may decrease slightly the stacking fault energy of aluminum. Although poly crystalline aluminum had about the same initial density of dislocations as the single crystals, the density of dislocations increased much more rapidly with strain in the polycrystals. This factor and the higher back stresses generated in the poly crystalline aluminum were the major factors responsible for the higher strength of the poly crystalline aluminum, As the magnesium content of the alloys was increased, the initial density of the dislocations also increased. Most of the alloy strengthening arose from this factor; alloying effects due to short-range order strengthening, Suzuki locking, Cottrell pinning, and so forth, were estimated to be quite small. The gveater rate of strain hardening in the alloys was deduced to be due primarily to the greater increase in the density of the dislocations with strain as the magnesium content was increased. It is the purpose of the present investigation to shed additional light on the average plastic behavior of a grain in a polycrystalline aggregate, by analyses, based on dislocation theory, of appropriate experimental test results. These deductions when compared with those from single-crystal data will then serve to illustrate the major items of difference between the plastic behavior of single crystals and the average behavior of a grain in a

Jan 1, 1963

By C. E. Sims, H. M. Banta, S. L. Hoyt

Over the past few years, metallic arc welding has been extended to steels of the hardenable type. As compared with other methods of fabrication, production has been facilitated, service performance frequently has been improved, and the overall results have been so favorable that engineers and production men have placed great emphasis on this application of welding. The metallurgist and welding engineer, however, have been confronted with new problems, since, for one reason, the harder steels are more apt to crack and special precautions must be taken if sound joints are to be procured. Some of the factors that are pertinent to this problem are metallurgical, and it is an object of this contribution to discuss steel manufacture and processing methods and to show how their control assists in reducing the hazard of cracking. By this time, the problem of cracking— specifically underbead cracking, or "hard cracks," or parent-metal cracks-—is well known, and a large amount of work has been published, both here and abroad, dealing with this subject.' The tests described are made under restraint to facilitate cracking and arc so designed that a semiquantitative, or at least a relative, value of the cracking tendency is obtained. As one would expect, it has been reported that the incidence of cracking increases with the carbon and alloy content of the steel. More specifically, the cracking tendency is said to increase with the hardenability of the steel, though it is now recognized that the situation is not so simple. The phenomenon itself, on the other hand, has been but loosely described, and it is in only broad generalizations that this cracking has been related to steel metallurgy. Thus, while it has been abundantly demonstrated that the hardenable aircraft steel, S.A.E. 4130, must tend to crack when are-welded, the problem still remains of why two lots of the same composition and the same hardenability can vary so greatly in cracking tendency, or what it is about the prior metallurgical history that so strongly affects the results. Further, while the efficacy of preheating and postheating in preventing cracking is recognized and utilized in production, the mechanism by which they function seems not to have been described. These points are thought to be significant in the production of steel for fabrication by metallic arc welding and, hence, of interest to mill and process metallurgists and welding engineers. Consequently, it is another object of this paper to discuss the mechanism of parent-metal cracking, including the influence of the condition of the steel and the control of cracking by manipulation of the time-temperature conditions during and after welding. A new method of rating the cracking tendency is also discussed, and the results of the test are related to steel composition and structure or prior history. The work to be described was the outgrowth of work in 1940-41 at Battelle Memorial Institutc on two projects, one

Jan 1, 1945

By Thomas Kesler

THE Cartersville mining district, 35 miles northwest of Atlanta, Ga., has been of varying but continuous importance in the southern mineral industry during the past century. Noted chiefly for its production of brown iron ore, manganese oxide ores, barite, sienna, and magnesian limestone, the district and its environs have produced brick and tile clays, slate, gold, bauxite, and graphitic schist. Minor deposits of serpentine, sericite schist, copper ore, and red iron oxide have been prospected. The obvious deposits of brown iron ore, together with some associated specular hematite, were mined out years ago, although a little ore was left in the workings. Moderately steady production of sienna reached a peak about 1930, then declined rapidly. Manganese mining passed through a relatively active period from the World War to 1931, but has subsided to a small but rather constant output for the Birmingham market. How-ever, the White Manganese Corporation has prepared for possible increased production by constructing a new washer capable of handling about 300 tons of ore per day. Principal activity in the district proper has centered for some years in the production of barite and magne-sian limestone.

Jan 1, 1940

APPROXIMATELY 90 per cent of the steel that is melted and refined in the United States and poured into ingots is made in basic open-hearth furnaces, as shown in Table 1-1. The annual ingot capacity of the steel industry reported January 1, 1950, by the American Iron and Steel Institute3* was 99,040,160 tons, of which the basic open-hearth process accounted for 85,896,580 tons, 86.7 per cent of the .total. The capacity of the individual furnaces varies over a wide range, a large majority falling within limits of 50 to 200 tons (Fig 1-1). Most of the units constructed [ ] since 1942 are in the larger size groups, between 175 and 225 tons capacity.

Jan 1, 1964

By G. Sachs

According to Tammann,' the explanation of the effect of mechanical deformation in producing changes in the properties of metals is one of the most important problems of physical metallurgy, taking rank with the study of the constitution of alloy systems; and this problem has long attracted the attention of practitioner and scientist alike. Its solution was not advanced materially until Tammann2 set up his translation hypothesis with its crystallographic basis, while other hypotheses, such as the amorphous metal hypothesis of Beilby3 and Rosenhain,4 have been shown by more intensive studies to be less and less satisfactory. The principles of the Tammann translation hypothesis have proved to be useful even up to today and in spite of all of the recent accumulation of experimental data, while the differences of opinion which have arisen relate to the extent to which the hypothesis accounts for the observed changes Ïn properties and to what extent further assumptions are necessary. Stimulated by the proposals of Tammann, there soon developed a lively experimental activity which aimed at the elucidation of the structural or crystallographic changes produced by the mechanical deformation of metals. Parallel movements of crystal "blocks" along definite crystal slip planes had already been observed by Ewing and Rosenhain5 in 1900, in metals which had been moderately deformed but without shedding light on the crystallographic nature of the processes accompanying more severe deformation. The solution of this important problem was not advanced until a much later date, or until the methods of X-ray crystal analysis had become available. Shortly after the discovery of the diffraction of X-ray by crystals, symmetrical diffraction effects were

Jan 1, 1931

By L. G. Jones, A. S. Odeh

A theoretical developtment is presented which provides a straightforward method of handling the drawdown analysis for both oil and gas wells flowing at variable rates. In the past our inability to analyze variable-rate drawdowns has been a major obstacle in using them for formation evaluation. This method should permit wider use of these tests in the future. INTRODUCTION Pressure build-up analyses are widely used to obtain reservoir data such as the effective flow capacity of the formation. On the other hand. although pressure drawdowns have been run for a long time, they have not been used extensively to evaluate reservoirs because they are difficult to analyze. One of the difficulties in analyzing pressure drawdowns has been that the theory developed until now has required the test to be run at a constant rate. For both oil and gas wells this is a difficult requirement to satisfy. especially during the early period of a well's life when drawdown tests are usually run. In spite of this limitation, drawdown tests are often run with build-ups as a check. In this paper a theory, which handles the drawdown analysis for variable rates, is presented for both oil and gas wells. Thus, one of the biggest deterrents to running drawdowns is removed, and they should become a much more useful engineering tool in the future. THEORETICAL CONSIDERATIONS 011, RESERVOIRS The general equation used for describing the unsteady-state radial flow of slightly compressible fluids in homogeneous porous media can be written in cylindrical coordinates as where r is the radial distance in cm, t is the time in seconds, p is the pressure at r and t in atmospheres, + is the fractional porosity, p is the viscosity in cp, c is the compressibility in vol/vol/atm, and k is the permeability in darcies. There are a number of solutions of Eq. 1 for various boundary conditions. One of these is the so-called "point-source" solution, which approximates the case of an infinite oil reservoir with a well located at r = 0 and produced at a constant rate. The point-source solution of Eq. 1 is

Jan 1, 1966

By J. D. Ridge

The geologic setting and mineral relationships of seven European massive sulfide deposits that more or less conform to the bedding of the largely noncal-careous sedimentary rocks and/or bedded volcanics in which they are found are considered here. These orebodies consist largely of massive beds or lenses of sulfides usually surrounded by halos of disseminated sulfides and distorted by tectonic activity. The formations containing these deposits have been metamorphosed in varying degrees at times subsequent to their lithification. The ore-forming process is thought to be essentially volcanic, with the ore constituents being brought to the shallow-water site of deposition through tectonic fissures from magma chambers at depth as gases or relatively concentrated hydrother-mal solutions. Certain European ore deposits of base metal sulfide have previously been considered to be of hydro-thermal or magmatic origin, but today a number of European mining geologists consider them to be syngenetically produced. In an effort to provide American geologists with some idea of the reasons behind this change in thought, the geological settings of seven of these deposits have been studied. These are: Ldkken, Meggen, Rammelsberg, Ergani-Maden, Outokumpu, Boliden and Roros. These deposits lie in bedded rocks that have undergone metamorphism from causes not universally agreed upon; most of the formations were originally shales, and may have been intercalated with limey and occasionally quartzitic beds, volcanic tuff, agglomerate, extrusive lavas and usually basic intrusives. Deposits of the conformable type, however, are not confined to these rock types but may be in calcareous and associated igneous rocks or almost entirely in volcanics. These deposits may be closely associated in space with igneous rocks that, again, are usually basic types. Although the ages of the enclosing rocks range from mid-Precambrian (Boliden and Outokumpu) to Eocene (Ergani-Maden), the bulk of them are Paleozoic, with two (Meggen, and eammelsberg) being upper middle Devonian and two (LØkken and RØros) being Cambro-Ordovician. Geographically, two are in West Germany, four in Scandanavia and one in Turkey. Of the seven deposits, six are mined for copper, with three of these also producing zinc, and two lead; one is mined for zinc and minor lead. In the discussions of the seven conformable deposits that follow, I have attempted to present as uniform a treatment as their varying characters will permit. For each deposit, I have considered the stratigraphy of the area, its major structural characteristics, the form of the orebodies, their mineral content, and the origin of the ore. In the last of these subdivisions, I have presented only the viewpoint of those who believe the ores to have been formed by syngenetic processes, processes that went on at the same time as those which produced the beds that enclose the ores but that are not, in the deposits in question, thought to have been sedimentary in the strict sense of the term. The materials of which these orebodies are composed, it is suggested, did actually collect by falling through sea water to the floor of that portion of the sea in which they accumulated. The ore constituents, however, are believed by a considerable number of European geologists to have been added to the sea water from intratelluric sources, probably igneous magma chambers, as exhalations — hydrothermal solutions or volcanic gases. The effect of the encounter with sea water on these ejected gases or water-rich vapors was to precipitate their potentially solid constituents with great rapidity; they were deposited so quickly, in fact, that the amounj of normally accumulated mechanical or chemical sediment deposited over the same period of time was essentially negligible. The ores formed in this manner, however, are generally interbedded with normal sediments or with lava flows, or with any combination of these two types of rock-forming materials. Such departures as these deposits may have from their original mineral content and attitude are thought to be directly related to the degree of dynamic or static metamorphism that they may have undergone after their accumulation. I have not attempted here to present alternate hypotheses to that of so-called exhalative sedimentation although, of course, such exist and, in my

Jan 1, 1963

By George W. Bain

Methods of mining building stone of any sort are planned to produce as few fractures as possible, and present a strong contrast to methods of mining metallic ores, which must be crushed eventually and have fractures produced in as great profusion as possible. Shocks transmitted to a stone invariably make it more porous and more permeable and reduce its effective life, therefore methods of mining building stone involve as This building illustrates the fine detail of workmanship, unprotected sharp corners and thin edges, and tall narrow columns characteristic of marble structures. These features require exceedingly coherent stone, and preservation of these features for decades or centuries demands many special quarrying precautions to keep absorption to 0.14 per cent or less, a detail not essential to stone for coarser architectural types. few shocks as possible. This is singularly true for marble because marble structures are intended to have long life, greater delicacy of line, more gracefulness and fineness of sculpture than those made from any other structural material (Fig. 1). So that delicate lines may remain in almost perfect preservation for decades, or even centuries, it is important

Jan 1, 1938

By George W. Bain

Methods of mining building stone of any sort are planned to produce as few fractures as possible, and present a strong contrast to methods of mining metallic ores, which must be crushed eventually and have fractures produced in as great profusion as possible. Shocks transmitted to a stone invariably make it more porous and more permeable and reduce its effective life, therefore methods of mining building stone involve as This building illustrates the fine detail of workmanship, unprotected sharp corners and thin edges, and tall narrow columns characteristic of marble structures. These features require exceedingly coherent stone, and preservation of these features for decades or centuries demands many special quarrying precautions to keep absorption to 0.14 per cent or less, a detail not essential to stone for coarser architectural types. few shocks as possible. This is singularly true for marble because marble structures are intended to have long life, greater delicacy of line, more gracefulness and fineness of sculpture than those made from any other structural material (Fig. 1). So that delicate lines may remain in almost perfect preservation for decades, or even centuries, it is important

Jan 1, 1938

By J. R. Mihalisin

Phase changes in as-cast alloys in the Ni2 CoCr-Ni, Ti-NSAl system containing 0.1 wt pct C were studied after heat treatment at 1650°F. It was found that a vegion of CrCo-type s was developed in this system after I1000 hr. The tendency for s formation was dePendent upon the aluminum and litanium content, the s -forming tendency generally becoming more pro-nounced as the latter two elements are increased. s lended to form in interdendritic regioues and was associated with solutioning- of- carbide phases. Electron- vacancy computations for prediction of s formation on these alloys mere in sufficient agreement with what was observed experimentally to indicate that the method should be of value in assessing a-forming potential in cast alloys. However, the correlation of electrotz- vacancy numbers may not be as favorable in cast as cormpared to wrought alloys. THE increasing use of high-temperature alloys for longer times at higher temperatures has resulted in a real need for obtaining information on the phase changes taking place in these alloys since these changes often have a direct effect on properties. This paper reports on a study of the phase changes in Ni-Cr-Co-Al-Ti alloys after prolonged heating at 1650°F. The alloys were selected from the pseudo-ternary system Ni2CoCr-Ni3Ti-Ni3Al and this system was chosen because it is the basis of many of the newer cast commercial superalloys. The attempt here was not to define accurately the boundaries of s formation in the NizCoCr-Ni3Ti-Ni3Al system but to delineate the phase transformations taking place upon heating alloys covering a wide range of chemistries in this system. An addition of carbon was made to all alloys to further simulate commercial alloys. It was hoped that the information generated in this manner would be of more direct use to superalloy designers than an equilibrium diagram approach since commercial alloys generally have outlived their usefulness when equilibrium is attained. EXPERIMENTAL PROCEDURE The alloys were vacuum-melted from carbonyl-nickel pellet, vacuum-grade chromium, electrolytic cobalt, high-purity aluminum and titanium, and spec-trographic-grade carbon.

Jan 1, 1968

By W. B. Boggs, J. N. Anderson

An account of the operation of the Noranda smelter covering the period from December, 1927, when the smelter started, until December, 1929, was given in a paper published by the Canadian Institute of Mining and Metallurgy early in 1930.' The object of the present paper is to review matters of interest in the original paper and to describe the present construction and operation of the smelter, with particular reference to the reverberatory-furnace practice. The Noranda smelter was built by Noranda Mines, Ltd., from the designs of A. E. Wheeler, consulting metallurgist of New York, for the reduction of ores and concentrates from the Horne mine and to treat, on a custom basis, ores and concentrates from other mines in the Rouyn district. The smelter is at Noranda, about 330 miles directly north of Toronto. Construction work was started in June, 1926, and copper was first produced in December, 1927. The smelter was built throughout as two duplicate units, each with a rated capacity of 500 tons of ore per day. Operations were started with one unit and after several months it was found that one unit alone could smelt 1000 tons of ore a day. At that time there was only one hoisting shaft, No. 3, and its hoisting capacity and the capacity of the original crushing plant were insufficient to supply ore for the two units at the increased tonnage. Accordingly No. 4 shaft was sunk and a new crushing plant provided to handle the ore hoisted there. Operating two units at capacity also required the installation of two more converters to treat the additional quantity of matte produced. This work was completed in the latter part of November, 1929, and since then both smelter units have been operating continuously. In 1928, a mill to treat 500 tons a day of concentrating ore was completed. Since then the concentrator capacity has been increased twice, and at present 2000 tons a day of ore are being concentrated. The layout of the surface plant of the mine, concentrator and smelter is shown in Fig. 1 and the general plan in Fig. 2. The smelter is shown in more detail in Fig. 3. The original hoisting shaft, No. 3, is now used only for handling men, supplies and waste rock, and the original crushing

Jan 1, 1934

By O. B. Bucklen, P. G. Meikle

INTRODUCTION The trend in the coal industry for many years has been to make every- thing "bigger and faster." This also held true for loading and storage facilities. Where once a million ton per year mine was rare, three to five million ton per year mines are not uncommon today in the bituminous industry. This greatly increased production, made possible through mechanization, required greatly improved loading facilities just to get the coal away from the mine. Also, there is a trend toward combining production from more than one mine and cleaning it in a single preparation plant. In addition to increased loading capacity, this frequently necessitates raw coal storage and blending facilities. The development of the unit train with its attendant economics, more than any other factor, has contributed to the widespread construction of storage and high-speed loading facilities. In the export market, the construction of ever larger coal colliers has contributed to a need for faster and larger loading facilities. In this climate of rapidly changing technology, any written account is faced with the possibility of obsolescence before its appearance. Thus, this chapter seeks to define the common and current practice in coal loading and storage facilities with the full knowledge that this practice is an ever-moving target. FUNDAMENTALS OF COAL STORAGE Storage of coal is becoming an increasingly important part of coal handling systems at mines, particularly since the advent of the unit train concept in transportation. In order to take advantage of reduced transportation rates on trainload shipments of coal offered by unit train movement, operators have found that storage is an economic necessity. In unit train practice large predetermined quantities must be loaded in relatively short periods of time as opposed to conventional practice where coal is loaded at a speed dependent on the production capacity of the mine and/or the cleaning capacity of the preparation plant. Two surveys of storage practices at mines reveal several objectives for storage.1, 2 Raw and/or clean coal storage is generally practiced in order to accomplish one, or a combination, of the following objectives: 1. To improve plant efficiency by distributing plant feed over the entire operating time, or to allow a preparation rate different from the production rate. 2. To limit interruptions of supply, ie, allow mine and plant to function independently with delays in one not affecting the operation of the other.

Jan 1, 1968

By Homer Turner

COALS, other than anthracite, have been so thoroughly studied under the microscope during recent years, that we now know what kinds of plants and what parts of plants form the bulk of lower rank coals from peat to bituminous coal. The microscope has also shown the state of preservation of such vegetation as well as the nature and distribution of products of plant decay. These and further details have been ascertained mainly through the employment of two methods of attack, section cutting and maceration. Anthracite has failed to respond to these methods, so well adapted to the study of lower rank coals and, therefore, has been neglected by investigators to such an extent that there is much doubt as to its microscopical characteristics. The object of this paper is to lift anthracite from its realm of obscurity by demonstrating the wealth of microscopical detail that is revealed when reflected light is used on a properly polished and etched surface and, further, to show the relationship between anthracite and bituminous coal.

Jan 2, 1925

By T. L. Joseph

IT is a distinct privilege to participate in this meeting convened to honor the memory of Henry Marion Howe, a distinguished scientist and metallurgist. Many have added to our rapidly growing fund of metallurgical knowledge but few have made the unique contribution of formulating basic concepts essential to an over-all comprehensive view of the subject of metallography. Of those previously selected to deliver this lecture, several have added a personal touch to their discourse because they were able to refer to their associations with Dr. Howe. It was not my good fortune to know him or to enjoy his inspiring influence. Like most of you, my contact has been with his published works, which are outstanding in that they provide lucid, detailed expositions of the nature and behavior of metals and alloys. His deep understanding and clarity of expression have greatly accelerated our progress in metallography and in the use of metals. The degree to which a man's thinking, experimentation and writing contribute toward an understanding of basic laws and phenomena determines whether his life's work is of transitory or permanent value. This occasion appropriately recognizes the fundamental importance of Dr. Howe's pioneer work in the field of metallurgy. On two former occasions, gray iron was selected as a subject for discussion. The fact that the production of pig iron has not been discussed before does not reflect any lack of interest on the part of Dr. Howe or former lecturers in the process that under- lies the production of steel. Although Dr. Howe's work in his later years centered around metallography, his earlier publications show a considerable interest in the production of iron and steel. He recognized that in the ascending spiral of metallurgical advancement we are not winding a single thread but are weaving a complex fabric. Specific evidence of his interest in the production of pig iron may be found in his book1 on The Metallography of Cast Iron and Steel. In explaining why blast furnaces have been in constant use for about 600 years, he says: "The process is economical because it utilizes with extraordinary completeness the calorific power of the coke due to the thorough transfer of heat from the gaseous products of combustion to the charge." This emphasis on heat transfer, overlooked in many more extended and more recent discussions of the blast-furnace process, illustrates Professor Howe's ability to see the essentials. Other distinct advantages of the blast furnace, such as the removal of much of the sulphur and practically all of the oxygen, were mentioned. It was also stated that although the blast- furnace process is complex in nature, its outward form is comparatively simple, thus permitting large-scale production at small labor costs. All who contemplate the production of metallic iron from its ores by any other process might well consider the

Jan 1, 1946

By Charles Barrett

THE copper-silver system presents several points of special interest in the study of segregate structures. The system is simple eutectic, with limited solid solutions terminal with the pure component metals. The extent of solid solubility decreases with decreasing temperature for both the copper-rich and the silver-rich alloys, thus offering a possi-bility for the formation of Widmanstätten figures and also a possibility for aging after quenching. In contrast to the structures studied previ-ously the structures in this system are unique in their; origin, for one terminal solid solution will precipitate the other, and ice versa. In most of the other systems for which crystallographic data on the precipi-tation (or transformation) process are available, either intermetallic compounds or intermediate phases partake in the decomposition process; the absence of such phases thus distinguishes this system. The lattice structures of the two solid solutions are identical in type, differing in lattice spacing by approximately 10 per cent; because of this it seems difficult if not impossible to predict on the basis of present theory either the outward form of the precipitate or the lattice orientation relationships between matrix and precipitate. The eutectic temperature in the copper-silver system1 is 779°C. At this temperature copper -dissolves 4.3 atomic per cent (7.0 weight per

Jan 1, 1935

By D. K. Crampton

Internal stress and season cracking in brass have been studied for many years and the technical literature contains many data on various phases of the subject. A resume of the literature shows certain fairly well established points upon which various authors are mostly agreed: 1. Season cracking is primarily caused by the presence of relatively high internal stresses, or possibly in some cases by external stresses, or both. 2. A specific corrosion is also essential to season cracking. Certain agents, particularly mercurous salts, mercuric salts and ammonia salts, have such a specific corrosive effect. 3. The tendency to season crack under given conditions increases with increasing zinc content, brass containing less than 20 per cent. zinc being relatively immune. 4. In alpha brass the season cracks are intercrystalline; in alpha-beta brass they lie between the two constituents; and in beta brass they are transcrystalline. 5. The ordinary impurities or added elements in special brasses have little or no effect on the tendency to season crack. 6. Internal stresses can be eliminated, or at least reduced to a safe limit by annealing treatments at temperatures that do not produce visible microstructural changes or appreciable softening of the worked brasses. There are, however, some points in connection with the phenomenon of season cracking which have not been thoroughly investigated, or wherein different authors and investigators are not entirely in agreement. The investigations described in this paper were undertaken to determine: 1. The correlation between mercurous nitrate tests and actual season cracking on long-time atmospheric exposure. 2. The quantitative effect of type and degree of drawing operations on the intensity of internal stress and on the tendency to season crack in brass tubes. 3. The possibility of drawing high-brass tubes in such a manner as to prevent the occurrence of harmful stresses rather than to find a remedy for such stresses once having obtained them.

Jan 1, 1930