Search Documents

By J. M. Ross

THE Homestake mine is situated in Whitewood mining district, in the northern Black Hills of South Dakota, in the city of Lead, Lawrence County. The entire property, comprising 557 lode claims with a total area of 3343 acres, is held under United States Patent. The older claims were 300 by 1500 ft. under local regulations, the newer ones 600 by 1500 ft. The Homestake was discovered April 9, 1876, by Moses and Fred Manuel, and Jake Harney, who were drawn into the northern hills, from the Custer placer district, by news of the discovery of rich placer deposits in Deadwood Gulch. They located a number of additional lode claims and, in a short time, the whole country was covered with locations. The Manuel brothers built an arrastre the following winter and took out $5000. The next year the Homestake lode was sold to Senator George Hearst and associates, who organized the Homestake Mining Co. Other companies were formed to exploit other groups of claims and at one time five companies were operating on this deposit, the Father DeSmet, the Deadwood-Terra, the Caledonia, the Highland, and. the Homestake Mining Co. These companies, however, have been merged into the Homestake Mining Company. The first stamp mill, known as the "Eighty Mill," commenced operation on July, 12, 1878, and production has been nearly continuous since that time.

Jan 2, 1925

By H. C. Chang, N. J. Grant

Creep of very coarse grained, high purity aluminum was studied at 400° to 1100°F with an initial stress range of 50 to 1200 psi. The process of boundary sliding and migration was studied. The driving force of boundary migration under creep conditions is shown to be a combination of strain energy migrationand surface energy. A theory is presented regarding the strainenergyrole the grain boundaries play under creep conditions. From this thetheory intercrystalline failure of commercial alloys can be explained. Also from this theory an optimum grain size should exist for good high temperature properties of high purity materials. IN the investigation of the creep of very coarse grained, high purity aluminum previously reported,' the cyclic nature of the process of grain boundary sliding and migration has been established by microscopic observation of the actual creep process as well as metallographically. It was also substantiated by measuring localized strains across the grain boundaries. In addition, it was shown how extensive subgrain and fold formation may result from boundary sliding and how the slid grain boundary may become sharply wavy as a result of subgrain formation. Since the publication of those results, additional information on the process of grain boundary sliding and migration has been obtained. It is the purpose of this paper to report on the direction and driving force of boundary sliding and migration, the effect of grain size, and the effect of temperature. Finally the effect of decreasing purity (alloys 2s and 3s) on the process of boundary sliding and migration is noted. From these results, an explanation is presented for the intercrystalline failure of alloys under creep conditions. The effects of grain size on the creep properties of impure and high purity materials are discussed in the same light. The experimental procedures and technique have been presented elsewhere.' It is only necessary to state how the 2s and 3s aluminum specimens are prepared. Machined specimens were first annealed at 600°F for about 12 hr. In order to produce a large grain size the specimens were then stretched 3 to 8 pct. The specimens were marked with reference marks, electropolished, annealed at 900°F for 24 hr and at 1150°F for 12 hr, and repolished. The grain size of 2s aluminum produced by this treatment is comparable to that of high purity aluminum in the direction of its width of the specimen, i.e., there are 2 to 4 grains across the width of the specimen. However, the grains of 2s aluminum are 3 to 10 times longer in the direction of the specimen axis. On the other hand, the grain size of coarse grained 3s aluminum ranges from 10 to 20 grains across the width of the specimen due to the treatment just outlined and therefore is much smaller than that of both high purity and 2s aluminum. As in 2s aluminum, the grains are about 3 to 10 times longer in the direction of the specimen axis than in the direction of the width of the specimen. The arrangements of the grains in 2s and 3s aluminum were generally irregular; therefore it was difficult to follow the course of the grain boundaries. Results Method of Presentation: In order to show the arrangement of the grains, especially the direction and positions of the grain boundaries, traces of the grain boundaries on the four surfaces of the specimens were unfolded and mapped out after macroetching. Figs. 1 and 2 show the structural development drawings of specimens P-3 and P-8 respectively. The two flat surfaces (of which the front one faces the microscope) and the round-edged surfaces will be called the "front surface" and "back surface" and

Jan 1, 1954

By Arthur F. L. Bell

Prior to 1908 the oil production in the State of California had been almost entirely a heavy fuel oil, with a high flash point, but changed within a short period to a large percentage of refining oil with a low flash, by reason of the heavy production of light oil coming in from the Santa Maria field, the Midway field, and the increased production of the Fullerton field. This is clearly shown in the following tabulation of California's pro- The bringing in of these high percentages of light oil with their dangerous low flash and the increasing demand for the refined products necessitated the devising of some cheap and efficient means of quickly separating the lighter elements either in the field or at the main distributing points; also it became necessary to remove the excessive percentage of water which many of the light oils carried in emulsion. Union Oil Co. Port Harford Plant Probably the first important attempt to top light oil in California by other means than the ordinary stills was tried about 1908 by the Union Oil Co., at its plant at Port Harford, San Luis Obispo County, with Santa Maria oils. The process was the invention of Hubert G. Burroughs who afterward obtained a patent for the process, No. 998,837, dated July 25, 1911. The apparatus used consisted of a series of 12-in. pipes mounted in units of three pipes, one above the other, the crude oil being admitted to the upper pipe and filling it about two-thirds of its

Jan 1, 1916

Aalde, Kaare. ('40) Gen'I Del., Bisbee. Ariz. Aase, Glenn D., ('40) Univ. of North Dakota. Grand Forks. N. D. Abadesco, Enrique A., ('39) College of Engrg.. Univ. of the Philippines. Manila, P. I. Abbott. John L., ('40) Colorado School of Mines. Golden. Colo. Abdul-Ahad, A., ('39) Montana School of Mines. Residence Hall, Butte. Mont. Abreu, Ovidio M., ('38) Univ. of Nevada, Reno, Nev. Acomb, Allen. ('41) Louisiana State Univ., Box 1970, University. La. Acosta S., Gonzalo. ('40) Univ. of Texas, Univ. Sta., Box 1785. Austin, Tex. Adam, Howard W., ('41) Montana School of Mines. Butte, Mont. Adams, Albert, ('381 New Mexico School of Mines, Socorro. N. M. Adams. Charles W., ('39) Michigan College of Min. & Tech., Houghton, Mich. Adams. H. Travis, ('39) 316 South -5th St., Bur¬bank. Calif. Adams, Jack L., ('39) Univ. of Oklahoma, Nor¬man. Okla. Adams. John W., ('41) Colorado School of Mines, Golden. Colo. Adams. Lewis J.. ('39) 402 Del Mar Blvd., Corpus Christi, Tex. Adams, Rob L., ('40) Agricultural & Mech. Col¬ lege of Texas. Box 600, College Sta., Tex. Adamson. Charles R., ('41) Univ. of Utah, Salt Lake City. Utah.

Jan 1, 1941

By A. Rosen, P. Wynblatt, J. E. Dorn

The temperature, strain rate, and structure dependence of the flow stress in a poly crystalline Fe-2 pct Mn alloy was investigated between 77" and 370°K. It was possible to identify the low-temperature data from 77° to 160°K with Dorn and Rajnak's theory of the Peierls mechanism of plastic deformation. Above 160°K one or more thermally activated mechanisms must he operative; however, these were not identified in this investigation. The mechanistic basis for the rapid decrease in the flow stress of bcc metals with an increase in temperature over the low-temperature range is yet being debated. Various dislocation mechanisms have been suggested in the past but the agreement between the various proposed theories and the experimental results have not been definitive. In the present paper, the authors will demonstrate that the plastic behavior of polycrystalline iron containing 2 wt pct Mn plus interstitials agrees excellently with predictions based on the Peierls mechanism from 77" to 160°K whereas from 160" to about 370°K other as yet unidentified thermally activated mechanisms take over. Undoubtedly, the overlap of these mechanisms with the Peierls mechanism contributed to the difficulties of rationalizing the low-temperature behavior of iron and its alloys. I) EXPERIMENTAL TECHNIQUES AND RESULTS Although extensive data are now available on the effect of temperature and strain rate on the flow stress of various bcc metals and alloys, it was, nevertheless, deemed necessary for the objectives of the present study to obtain highly accurate data of the type most pertinent for checking the theories on a series of well-documented work-hardened states. Iron containing 2 wt pct Mn was used in this investigation in order to obtain a lower ductile to brittle transition temperature than that for iron.' The additional elements present were 0.004 pct C, 0.05 pct 0, 0.004 pct S, 0.003 pct P, 0.006 pct N, and 0.001 pct Si. The as-received 3/8 by 3/4 in. bars were cold-rolled to 0.100-in. thickness, recrystallized under argon for 30 min at 1073"~, further cold-rolled to 0.063-in. thickness, and finally recrystallized under argon for 30 min at 1000°K. This treatment gave a stable reproducible equiaxed grain structure having an average grain diameter of about 90 p. Prior to the final recrystallization treatment, the sheet was machined into tensile specimens 1/4 in. wide having a 1.625-in.-long gage section. All specimens were tested in controlled-temperature baths on an Instron Testing Machine. For convenience in the theoretical analyses the data will be given in terms of the shear stress for flow, 7, the shear strain rate, f, and the shear strain, y. A series of three standard strain-hardened states were obtained by prestraining specimens at 300°K and at a shear strain rate of 7.68 x lo-' per sec to three stress levels of 6.89 X l08, 10.3 X lo8, and 14.5 x 10' dynes per sq cm, respectively. Immediately following this prestrain the temperature bath was changed and each specimen was pulled in tension at either f = 7.68 X lo-' or f = 3.06 X 10"3 per sec. In terms of the accuracy that was achieved, the values obtained did not deviate more than *0.1 X 10' dynes per sq cm and * 1°K from the reported values of stress and temperature and not more than *5 pct in the reported values of the strain rate. The tensile stresses were converted to shear stresses using a factor of 1/2. The shear stress for the initiation of flow at the test temperature was determined by taking a y = 6.16 x 10'3 offset. from the modulus line at which point good accuracy could be achieved in determining y and the associated flow stress 7, with only a negligible increase in the pre-

Jan 1, 1965

By Ednlund D. North

Discussion of the paper of Edmund D. North, presented at the Spokane meeting, September, 1909, and published in Bulletin No. 37, January, 1910, pp. 21 to 25. A. SCOTT REID, London, Eng. (communication to the Secretary*) :-As a constructor of several glass mine-models, I have read with much interest the description of the model of the Montana-Tonopah mine-workings by Edmund D. North. As an interchange of ideas and experience is always an advantage, and in view of the fact that such models are coming more and more into vogue, perhaps the following remarks on this subject may prove of interest to mining engineers generally and to Mr. North particularly. In the model of the Waihi gold-mine, New Zealand, which I constructed, a dust-proof case is used. The top, bottom, front, and two ends are of glass; the back only is of wood, painted a dull white, against which the mine-workings show very distinctly. Each mine-level is represented by a horizontal sheet of glass, supported on metal runners fixed to the uprights at each end of the case, in a manner similar to that described by Mr. North. The corner uprights are strengthened by having a metal band screwed to the inside face of each, to which the metal runners or supports for the sheets of glass are screwed in turn. The reason for having this additional strength is that as the mine is developed in depth, and fresh levels are opened, the increasing weight of the glass sheets, added to the model, caused the unsupported wooden uprights to bend slightly, so that the glass sheets-did not fit in with the desired nicety, and co-ordination was, to a considerable extent, lost. Strengthening the uprights in this manner is not important in models of mines in which only a few levels have been opened, or when the sheets of glass are small, but in the Waihi model there are 15 sheets of glass to be supported, and more to be added as development proceeds, and the weight is considerable.

May 1, 1910

By R. J. Sherman, M. R. Achter

Creep rates have been measured for nickel at 1200°F in air and in vacuum, and related to the depth of surface cracks in the specimens tested in the two environments. The surface cracks were observed to grow faster in air than in vacuum in both short-time and long-time tests. Crack depths, however, could be correlated with creep rates only in the short-time tests. Although no cracks were observed in a relatively brittle Ni-Cr-A1 alloy creep tested at 1300°F, the appearance of alloy specimens fractured after interruption in creep indicated that there was a decrease of intergranular cohesion resulting from the diffusion of atmospheric gases into grain boundaries. PREVIOUS investigations1-3 have demonstrated that the effect of atmosphere on the high-temperature strength of nickel and nickel-base alloys may be reversed by changes in the stress or temperature of the test. At high stress and low temperature the creep-rupture life is longer in vacuum than in air, while at high temperature and low stress the relative strengths are reversed. A mechanism to explain this behavior was proposed based on two competing processes. Oxidation hardens and strengthens a metal, but adsorption of gas, by lowering surface energy, reduces the work required to propagate an intergranular crack. The controlling process is determined by temperature and stress. Basic to this mechanism is the concept that environment determines the ease of propagation of intergranular cracks and thus affects creep rate and rupture life. To explore the mechanism in greater detail, this investigation was undertaken to determine the effect of atmosphere on crack initiation and propagation rates in nickel1 and a relatively brittle Ni-Cr-A1 alloy.3 EXPERIMENTAL PROCEDURE The materials were the same as used previously. Nickel of 99.8 pct purity had the following impurity content: 0.02 pct Co, 0.03 pct Fe, 0.02 pct Mg, 0.03 pct Si, and 0.008 pct C. Rods were cold swaged from 1/2 in. to 3/8 in. in diam and machined into speci- mens with gage sections 1/4 in. in diam by 1-1/4 in. long. They were annealed in vacuum at 1600" F for 1 hr to achieve a grain size of 0.07 mm. The alloy was composed of 19.1 pct Cr, 3.6 pct Al, 1.7 pct Si, 0.57 pct Fe, 0.10 pct Mg, 0.027 pct C, 0.004 pct S, and the balance Ni. Sheet specimens of 0.500-in. width and 1.25-in. gage length were machined from 0.033-in.-thick strip and annealed in vacuum at 2000° F for 2 hr, resulting in a grain size of 0.036 mm. Large amounts of an intergranular phase were introduced as a result of the anneal. Creep tests on both materials, using equipment previously described by Shahinian; were conducted in air and in a vacuum of 1 x 10-5 mm Hg. They were continued to rupture and interrupted at various stages of the test. Although extensions were measured from dial gage readings of movement of the lever arm, it is considered that valid comparisons of creep rate may be made in this manner.l Two parameters were measured metallograph-ically* on longitudinal sections of nickel specimens interrupted during creep—the mean depth of surface cracks 2, and the density n as the number of cracks per unit length of surface. They were combined into one parameter by the relation p = n-d [1] As used here, p is equal to the total of crack depths per unit length of surface. RESULTS Nickel. It is well known that the incidence of intergranular cracking is increased with increasing rupture life. Indeed, it is evident in Tables I and I1

Jan 1, 1962

PRESIDENTS DAVID THOMAS 1871 R W RAYMOND 1872-1874 A L HOLLEY1875 ABRAM S HEWITT 1876 T STERRY HUNT 1877 ECKLEY B COXE 1878 - 1879 WILLIAM P SHINN 1880 WILLIAM METCALF 1881 RICHARD P ROTHWELL 1882 ROBERY W HUNT 1883 JAMES C, BAYLES 1884-1885 ROBERT H RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B POTTER 1888 RICHARD PEARCE 1889 ADAM S HEWITT 1890 JOHN BIRKINBINE 1891-1892 H M HOWE 1893 JOHN FRITZ 1894 J D WEEKD 1895

Jan 1, 1923

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

Binary alloys of titanium with silver, lead, tin, nickel, copper, beryllium, boron, silicon, chromium, molybdenum, manganese, vanadium, iron, and cobalt were studied. One-half-pound ingots of the alloys were prepared in an arc furnace, employing a water-cooled copper crucible, an argon atmosphere, and a water-cooled tungsten electrode. The half-pound ingots were fabricated by forging at 1700°F in air to 1/4-in. slab, followed by hot rolling at 1450°F to 0.060-in. sheet. Tensile properties, minimum bend radii, hardnesses, response to heat treatment and aging treatment, and phase relationships were determined for these alloys. EARLY in 1947, as one phase of the evaluation of materials for Air Force Project RAND, Battelle successfully arc melted Bureau of Mines titanium and obtained a few basic properties of unalloyed titanium and several titanium-base alloys. The low density, excellent resistance to corrosion, and high tensile properties of these materials stimulated a great deal of interest among metallurgists and designers seeking better materials of construction. As a result of this early work, Battelle, under contract with the Air Materiel Command, Wright-Patterson Air Force Base, has continued extensive studies of titanium alloys. The result of the first year's work is described in three papers. The present one deals with binary alloys, the second with ternary alloys, and the third paper with quaternary alloys. Melting Method The arc furnace for melting titanium and other refractory metals was developed at Battelle Institute under Air Force Project RAND. During the present work, considerable improvement has been made in the design and operation of this furnace for making small ingots of titanium and titanium alloys. The improved furnace design is illustrated by fig. 1, which shows a cross-sectional view with the dimensions of various parts and their relationship to one another. The essential features of the furnace are the inert argon atmosphere, the water-cooled copper crucible, and the water-cooled tungsten elec- trode. The melting crucible is formed by spinning 0.064-in. annealed copper sheet. A groove for an O-ring seal is spun into the flange of the crucible. A fiber gasket between the crucible flange and the water-cooled brass cover provides electrical insulation. The brass cover is fitted with a sight glass, an opening for the water-cooled electrode, and a tube through which the material is charged. Direct current is used for melting, with the positive electrical terminal connected to the water jacket and the negative terminal to the electrode. A typical heat is made in the new furnace as follows: Approximately, 0.20 lb of titanium under 2 mesh per in. and the alloy addition, if any is to be used, are placed in the bottom of the crucible. The cover is clamped on the crucible so that the O-rings make a tight seal. The remainder of the charge is placed in a glass bottle, and this is connected by a rubber hose to the charging tube of the furnace. The crucible and the charge are evacuated with a mechanical pump to a pressure below 50 mm of mercury, or less if desired, and held at this reduced pressure for 5 min. Hot water is circulated through the jacket during the evacuation period to assist in outgassing the crucible. Following the evacuation, tank argon of 99.92+ pct purity is flushed through the crucible for 5 min and then adjusted to give a positive pressure of 1 to 2 psi. During subsequent operation, an argon pressure regulator introduces only enough argon to compensate for the small leakage which occurs through a mercury trap. Re-evacuation and reflushing the melting chamber with argon produced a negligible reduction in contamination. Two 550-amp generators, connected in parallel, constitute the power source. Normally, about 800 amp are used for melting alloys which are not extremely refractory. The generators are set for 90 v open circuit and 200 amp. The arc is struck and the electrode is withdrawn to produce an arc of 23 to 26 v. This voltage is maintained while the electrode tip is moved slowly around a circle 1 in. smaller than the diameter of the ingot. The current

Jan 1, 1951

By G. S. Cole, G. F. Bolling

A series of Al-Cu alloys has been cast from constant superheat to solidify either with a hot top or with a free liquid/air interface. All the other variables which affect relative fluid motions were kept constant except the imposition of slow rotations m oscillations of the mold. Depending upon the exact circumstances, evi-dence could be found for the nucleation of equiaxed grains from dendrite bits detached from the columnar zone, or from the free surface, or from solid bits induced at pouring; a special experiment showed the solute buildup during ingot solidification and by inference the reality of constitutional supercooling. All methods of grain nucleation are thus supported. When solidification is arranged in a static mold the columnar- to-equiaxed transition occurs by one of these nucleation paths, subject to the natural decay of temperature gradients which promotes nucleation or the survival of nuclei. But when solidification is forced under special fluid flows it may display odd transitions. In one of these the equiaxed zone is synihesized from. dendrite bits detached from the solid/liquid interface. These survive under the concurrent lowering of temperature gradients and eventually cause transition by impeding columnar growth. GRAIN structure control is desired because real experience shows that specific properties are associated with specific cast grain structures. But since control is thus a matter of need and does not require understanding, much of casting remains art. For example, the manipulation of relative fluid motions in simple ingots provides a control of grain structure development,1-4 but theoretical insight is not required in order to broaden its potential applicability. Fortunately, however, once a variable like fluid flow is recognized it can also provide paths toward new insight. New observations using this variable have provided an insight which is curious. All the theories or descriptions of the columnar-to-equiaxed transition (CET) seem to be supported as long as the appropriate experiment is carried out. In order to develop this idea, let us ignore segregation, the chill zone (until a later section of this paper), and the origin and development of the columnar zone.= The details of questioning how equiaxed material forms in a casting may be divided in two. The first part is simply a questioning of the origin for equi-axed grains: are there fresh nuclei from heterogeneous nucleation, or dendrite bits broken off or melted from the columnar zone or elsewhere,6 or other solid bits surviving from the outset of freezing? The second is more complex, a questioning of the CET: does columnar growth slow down and allow the dominance of equiaxed grains, however they are formed, or do equi-axed grains take over and force columnar growth to stop? This "chicken-or-the-egg" second question can be quite useful, especially because it allows us to delineate the ordinary or NATURAL EQUIAXED ZONE and the induced or SYNTHETIC EQUIAXED ZONE. A natural equiaxed zone occurs if solidification proceeds in the absence of disturbances or extraneous forces such as ultrasonics, stirrings, and so forth. Both the CET theory proposed by Winegard and Chal-mers, 7requiring constitutional supercooling, and the CET theory suggested by Chalmers,8 requiring nuclea-tion only on pouring, pertain to the natural equiaxed zone. The best collating evidence to date for both these theories is contained in the work by Biloni and Chal-mers;9,10 the former theory7 is supported by special versions of the unidirectional growth experiment performed by Plaskett and winegardl1 and the latter theory' is supported in detail for the solidification of small ingots. An equiaxed zone can be synthesized when disturbances caused by forced fluid flows2-4 or other artificial means9,10 break off or melt off dendrite tips from an advancing solid/liquid interface,* if (and only if) temperature gradients in the melt are (forcibly) reduced enough to ensure the survival of these bits of dendrites, 2'3 Willful disturbances even so trivial as those produced by rapping a mold might be included here; as will be shown for example, this follows Southin's suggestion that the free liquid/air interface

Jan 1, 1970

By R. W. Kraft, L. D. Graham

The process of' spheroidization, or more properly coarsening, of Al-CuAl,eutectic alloy specimens with various initial microstructures was studied by quantitative metallographic and X-ray diffraction techniques. By measuring the rale at which specimens with a very fine dispersion of phases (produced by quenching molten droplets of the alloy in water) coarsened it uias determined that the rate-controlling mechanism for coarsening was diffusion, probably of aluminum in the aluminum-rich phase. The lamellae in specimens with a high degree of microstructural and cr-ystallog/uphic anisotropy (produced hy unidirectional solidification of ingots) thickened during heat treatment by recession of the CuAl, platelets from jaulted regzons, yet the specinlens retained a very high degree of. anisotropy after prolonged heat treatments at a temperature within 8°C of the eutectic temperature. In such specimens the crystallographic orientation relationship between the phases remained constant and no change in the crystallographic substructure occurred. Based on these observations a model was developed for the coarsening—or rate of' thicken-ing—oj- the lamellar structures which predicts that the rate of decrease of interface area is proportional to the square of lamellar interface area. Experiments with degenerate and very coarse lamellar microstruc -tures preduced by extremely slow unidirectional solidification) indicate that initial microstructure is a most important factor governing the final micro-structure after heat treatment. The particle size and shape of dispersed phases are important parameters affecting the properties of a wide variety of two-phase materials. As is well-known, varietythe dispersed-phase particles tend to coarsen at appropriately high temperatures because the interface energy of the system is reduced by the concomitant reduction in interface area. The phenomenon of

Jan 1, 1967

By G. Krauss, J. M. Thompson, H. Y. Kumagai

Boron-doped p-type and arsenic-doped n-type source materials were used to deposit thin silicon films on amorphous fused quartz substrates by cathodic sputtering in argon atmospheres. All as-sputtered films were found to have high electrical resistivities of about 104 ohm-cm, despite controlled variation of the substrate temperature from 50O to 400°C. The high resistivity of the n-type films persisted even after postdeposition heat treatments as high as 1000°C, while p-type films showed a sharp decrease in re-sistivity to values on the order of 1 ohm-cm or lower after heat treatments above 650°C. X-ray and electron diffraction, together with transmission electron microscopy of the p-type films, revealed that the improved electrical properties resulted from two distinct processes. A primary crystallization or recovery within the pains, which were approximately 200Å diam in the as-sputtered films, accompanied the initial sharp drop in resistivity at 650°C. Following this process, a secondary recrystallization or discontinuous grain growth was nucleated in films heated at 1000°C. The resulting significantly increased size of certain grains and the corresponding decrease in grain boundary area accompanied an additional decrease in resistivity after heat treatment at 1000°C. The properties of thin silicon films are of interest because of their possible application in device technology. Although evaporated silicon films on amorphous substrates1-3 and both sputtered and evaporated germanium films4-' have been studied in some detail, sputtered silicon films have not been widely investigated. It has been observed that evaporated silicon films deposited at substrate temperatures below approximately 600°C are amorphous.1,3,9,10 At substrate temperatures higher than this, the films are polycrys-talline, sometimes exhibiting a fiber texture with the fiber axis normal to the substrate surface.' Similar results have been obtained with germanium films, although in this case the substrate temperature for the amorphous to crystalline transformation is reported to be as low as 150OC.5 The mechanism of film deposition by cathodic sputtering differs markedly from that of thermal evaporation. It might be expected, therefore, that the properties of sputtered and evaporated silicon films would also differ. The purpose of our study was to determine the effects of deposition conditions and heat treatments on the electrical resistivity, structure, and composition of thin silicon films sputtered on fused quartz substrates. EXPERIMENTAL DETAILS Apparatus. A schematic diagram of the sputtering apparatus is shown in Fig. 1. The vacuum chamber was enclosed by an 18-in.-diam by 12-in.-high Pyrex bell jar mounted on a stainless-steel base plate. Access holes in the base plate were used to supply argon gas to the chamber, to allow for various electrical feedthroughs, and to provide mechanical motion to the shutter between the source material and substrate. The chamber was evacuated by a pumping system consisting of a 720 liter per sec oil diffusion pump backed by a 13 cu ft per min mechanical pump. Ultimate pressures of less than 1 x 10-6 torr could be achieved. The substrates were securely mounted on the stainless-steel substrate holder by quartz tabs held in place by stainless-steel screws. Temperatures of the substrate holder were measured by a thermocouple inserted within the holder. A quartz lamp was used to heat the holder and temperatures as high as 420°C could be maintained. Deposition Conditions and Procedure. The substrates used were polished fused quartz slides 116 by 1-12 by 3 in. and were outgassed at 200°C for 1 hr at a pressure less than 1 x 10-5 torr before film deposition. This was followed by a presputtering period of 2 hr during which the movable stainless-steel shutter was so positioned that deposition on the substrate was prevented. At a sputtering voltage of 5000 v dc and an argon pressure of 0.03 torr, the cathode cur-

Jan 1, 1967

By Henry Rawdon

THE RELATION between the course, or path, of the fracture of metals and alloys, produced in service or as a result of certain laboratory tests, and the crystalline units of which such materials are composed is of utmost importance. The fracture of normal material is, in general, intracrystalline, i.e., it consists of a break across the grains rather than of a separation between them. An intercrystalline fracture indicates either that the metal is of very inferior quality or that the break occurred under very unusual conditions, e.g., at a very high temperature. The usual mechanical tests, when applied to metals of the type that breaks with an intercrystalline fracture, merely measure the coherence of adjacent grains for one another and reveal little as to the real properties of the metal itself. Even such a soft plastic substance as lead, under suitable conditions, may be rendered so weak and brittle that the metal can be easily crumbled into powder by the fingers although the constituent grains have lost none of the intrinsic properties of lead. Various erroneous explanations of this behavior of lead have appeared in the scientific literature, the change being described usually as an allotropic one. The importance, in an industrial sense, of a proper explanation of this type of the corrosion of lead justifies the description of the type of metal deterioration that follows.

Jan 2, 1920

P. L. Pratt (University of Birmingham, Birmingham, England)—The author has measured the hardening effect of isolated edge and screw dislocation boundaries in a remarkably elegant manner, and he proposes that the detailed structure of the boundary determines its effectiveness as a barrier to slip although "there are still unknown details of the distribution which may be extremely important." On p. 678 the author states "that for a good crystal (one having a yield of about 30 psi) a change in annealing temperature from 300" to 400 °C resulted in a negligible shift in the level of the stress-strain curve." Is this in agreement with the results of the earlier paper by Li, Washburn, and Parker8 in which such a change of temperature produced notable hardening in crystals with a yield of about 30 psi? Or were these earlier crystals, of the same nominal purity, less perfect than those used in this work? The experiment illustrated in Fig. 15, p. 681, shows that the boundary has sharpened after annealing at 400 °C, the temperature at which the hardening effect first becomes apparent. Did the author verify that no sharpening of the boundary occurred at, say, 300 °C where no hardening was found? This would seem to be an important check on the proposed mechanism, especially since zinc of this purity should polygonize at temperatures well below 400 °C within the annealing times used here. There seem to be at least two alternative explanations which could fit these facts: 1—The boundary may sharpen at 300 °C or even lower temperatures but be unable to contribute greatly to the hardening until jogged by thermal vacancies and other impurity atoms after 400 °C anneal. This mechan- ism, discussed in the earlier paper,' is believed to account for the thermal hardening observed by Blank'" in NaCl, as stated elsewhere: and by results from recent experiments which tend to confirm this view. 2—The dislocations in the diffuse boundary may be locked by impurity atoms at 300 °C and thus only sharpen the boundary at 400 °C with the aid of thermal vacancies. In this case it would be difficult to distinguish between the two sources of hardening (sharpening or jogging), using metal of this purity. Jack Washburn (author's reply)—The author wishes to thank Dr. Pratt for his discussion. In connection with his first comment, it should be pointed out that the temperature of testing in the present series of experiments was —196°C, whereas, in the earlier experiments he referred to,' it was 20°C. Therefore, the yield values should not be directly compared. It is likely that the crystals used in the present work were initially more perfect macroscopically than the large shear specimens used previously. The small size of the test section in the kink specimens made it possible to select regions of the large crystals, from which they were acid-cut, that were free of observable small angle boundaries. The sharpening of a microscopically diffuse boundary such as that in Fig. 15 begins in zinc of this purity well below 300°C. However, it is probably not justified to conclude that because a boundary looks sharp under the microscope it has attained the ideal structure. The author agrees with Dr. Pratt that jogging of dislocation lines is one of the structural features of a small angle boundary that should be important in determining its strengthening effect. More detailed information concerning the changes in boundary structure as a

Jan 1, 1956

By Warren Howes, C. O. Anderson, Robert E. Illidge, M. D. Harbaugh, S. J. Burris

The Tri-State zinc-lead mining district embraces an extensive area, including the northeastern part of Ottawa County, Oklahoma, the southeastern part of Cherokee County, Kansas, and adjacent portions of Missouri, mainly in Jasper County. The Oklahoma-Kansas portion of the district, in the vicinity of Picher, Okla., has been the principal producing area since 1917, and the present milling practice in that section is the subject of this paper. This district is the largest zinc-producing field in the United States. In 1926 it produced 55 per cent of the nation's zinc and 15 per cent of its lead, and in 1933 it produced 35 per cent of the zinc and 10 per cent of the lead. From 1842 to 1933, inclusive, the total output of the district was 18 1/2 million tons of zinc and lead concentrates valued at 818 million dollars. Of this production, the Oklahoma-Kansas, or Picher, field yielded over 9 million tons valued at over 400 million dollars. Mining operations in the Oklahoma-Kansas field near Picher and Baxter Springs began in 1915. The mills built it that time consisted merely of gravity concentration plants employing jigs and tables and the same flow sheets as had proved satisfactory with the free-milling ores such as were mined in the Joplin-Webb City fields in Missouri. The Kansas-Oklahoma ores proved to be much richer but also more refractory to treatment than those in the Joplin area, and contained a considerable percentage of zinc mineral not freed by the amount of crushing usually practiced in preparing the ores for jigging. Thus the old Joplin type of mill, with its usual two or four jigs and a few tables, proved inadequate and resulted in excessive tailings losses sometimes as high as 50 per cent

Jan 1, 1935

By F. M. Morris

A large reserve of thick coal in southwest Virginia was developed by Clinch-field Coal Co. in 1957-1958 to produce a nominal rate of 1500 tph raw coal. Operation features coal cleaning in transit. Refuse removed averages 35 pct. Evolution of plant from initial conception to completion is discussed, selection of means applied is explained, and performance to date us design expectation is described. The long-range plan calls for ultimate handling capacity of 40,000 tpd raw coal with anticipated clean coal capacity of 26,000 tpd on a three-shift basis. From a materials handling viewpoint, the Moss No. 3 operation is principally of interest as an ensemble. Generally speaking, it uses time-tested equipment and ideas but some of these are employed on a scale that may be new in the industry. At present about 20,000 tpd of raw coal are being handled. This is expected to increase to 40,000 tpd as soon as business conditions justify it. The purpose of this paper is to discuss the evolution of the plant as to materials handling practices, to describe briefly the equipment and methods used, and to comment on performance in certain areas. The subject divides itself naturally into four phases: 1) operations at the mines, 2) transportation from mines to plant, 3) raw coal handling into the plant, and 4) transportation of refuse away from the plant. OPERATIONS AT THE MINES The coal reserves for Moss 3 are in southwest Virginia where Dickenson, Russell, and Buchanan Counties come together. This area contains about 15 square miles and over 100,000,000 tons of coal. Here the No. 4 (Tiller) and No. 5 (Jawbone) seams of the Norton Formation lie so closely together that for practical purposes, they constitute one seam of coal. This seam, which is called the Thick Tiller, varies from 10 to 18 ft in thickness and underlies Sandy Ridge, a mountain cresting between 2400 and 3300 ft above sea-level. At 18-ft seam height (which is considered to be the maximum practical mining height) the parting between seams will be about 3 1/2 ft thick and each bench of coal will be about 7 ft thick. Depending on the amount of impurities in the seams Drover. total reject in this height coal may approximate 50 pet by wt. It will average about 35 pet for the property as a whole. The first move in developing this resource was made in 1953 when contour maps of several square miles around Duty, Va., including all the known outcrop, were made by photogrammetry. At this time, it was felt the prospective operation would be served by the Clinchfield Railroad and a photogrammetric route survey was made by this railroad from Haysi to Duty. Study of the resulting maps indicated only one site—adversely owned—which might accommodate the size washing plant to be erected. Water resources of a dependable nature seemed nonexistent. In 1954 bulk washability tests were made on the Tiller Bench at the Moss No. 1 preparation plant. The tests indicated this portion of the seam, mined separately, would wash to 4 pet ash with good recovery. Also in 1954, development of Moss No. 2, south of Sandy Ridge, was begun. This mine is in the Tiller Seam where it is about 100 ft below the Jawbone Seam. The reasons for developing a mine in the normal Tiller Seam before tackling the Thick Tiller seemed compelling: Railroad service could be established quickly, communications were better (though not good!), more was known of the seam (it had been mined in the years 1911 to 19241, and there was no essential property to be acquired. After some legal skirmishing, the Norfolk & Western Railroad was granted the right to serve the new mine. Three decades earlier the old mine had been served by the Clinchfield Railroad. The event which triggered active development of Moss 3 was the Appalachian Power Co.'s decision in 1956 to build a 450,000-kva power plant on Clinch River at Carbo. This solved the problem of marketing the steam coal which inevitably must be a product of a mine in the Thick Tiller. Management promptly decided to build the preparation plant at Carbo where an excellent site was owned; where railroad service existed; where telephone service could be obtained; and where roads, bridges, and water supply were tolerable.

Jan 1, 1961

By I. H. Warren, E. Devuyst

A review of the physical and chemical aspects of the direct leaching of metal oxides has been given and com- pared to recent data of the authors and co-workers. The physical aspects, including the anisotropy of the dissolution, the hydration and the zero point of charge of some metal oxides are discussed first and then the kinetics of the dissolution of metal oxides are considered. A general mechanism of the leaching of oxides which describes most of the observed results is proposed.

Jan 1, 1973

By C. R. Knopp

Gas-oil relative permeability ratio is an important relationship in oil reservoir predictive calculations. A correlation has been developed from 107 gas-flood k/k tests on Venezuelan core samples. The correlating parameter is based on restored-state water saturation tests and' is applicable to both consolidated and poorly consolidated sandstone reservoirs. Data of the correlation show that there are no distinguishah1e differences between the mass-data groupings for the two c1assifications A procedure is recommended for running .sufficient relative. permeability analyses to compute a geometric mean of the sample group. The geometric mean is more representative of the total core, and probably the entire reservoir. For example, while only one in four of the k,,/k,., test curves agreed closely with the resultant correlation of this report, the geometric mean curves of the 16 suites (three samples or more). showed good agreetment ill three cases out of four. INTRODUCTION The gas-oil relative permeability ratio is an important, fundamental relationship in most oil reservoir predictive calculations. Predictive calculations are made to estimate future reservoir production characteristics and ultimate oil recovery. The k1,/k2, relationship is specifically needed to relate the surface gas-oil ratio to the reservoir oil and gas saturation, and to calculate the relative movement of these phases within the reservoir whenever some of the more complex driving mechanisms are present. Laboratory k1/k2, tests are not generally run as a routine analysis. Consequently, k1/k2 data often are not available when needed because the cost of laboratory work could not be justified or the need for such data had not been properly anticipated. When laboratory k1/k2, data are available, they are often very difficult to interpret. For example, wide divergence is sometimes shown in a family of k1,/k1, tests representative of the producing horizon in a single well. With these considerations in mind, a study was made to determine if a relationship might exist between the k1,/k2, curve and some other simple laboratory test criteria. The most probable k1/k2, curve correlation for Venezuela described in this paper is the result of the investigation. The presented correlation defines the most probable gas-flood k,,/k,, curve through the medium of air-water capillary displacement and centrifuge water saturation tests. The laboratory procedures of these tests are. relatively simple, and inexpensive; test data should be. widely available- from routine analysis. DATA AVAILABLE, LABORATORY METHODS The report correlation utilized 107 gas-Hood k1/k2, tests run on sandstone cores of Venezuelan reservoirs. Table 1 is a general tabulation of data pertinent to the tests, while Table 2 summarizes the data. Thetests include 96 from Western Venezuela and 11 from Eastern Venezuela. Eighty-two- of the 107 test samples were sandstones that varied from poorly consolidated to-unconsolidated; 25 were consolidated. The average sample porosity was 26.7 per cent and the average permeability was 1,121 md; these values typify the better sandstone reservoirs of' Venezuela. The Welge gas-flood technique,' based on fundamental Buckley-Leverett frontal displacement theory, was introduced in about 1952 and is widely accepted in the industry. The laboratory procedure is relatively simple, rapid, and can be performed on small core samples. While there have been some minor variations in sample preparation and laboratory procedure in the tests used for the correlation, these tests can be generally summarized as follows. The core sample was first sol vent-extracted and dried. Connate-water saturation was restored by the oil-flushing or evaporation-blow down methods. At the beginning of gas flood the hydrocarbon pore volume was completeiy saturated with the test oil phase. Unsteady-state gas-oil displacement then began with the injection of nitrogen or helium. while the displaced oil and gas phases were incrementally metered at the out-flow face. From the test data, the k,,/k,, curve was calculated by the Welge method.' The individual oil and gas relative permeabilities were also calculated." CORRELATING PROCEDURES In attempting to establish a basis of correlation, we found that broad mid-range sections of 105 of the 107 k,,/k,, test curves could be closely duplicated by a straight line. Only two curves did not show a degree of linearity in this region. Correlation-curve definition parameters were subsequently developed from this observation of consistent mid-range linearity. Possible correlating variables were limited to the physical properties measured on core samples that (1) were widely available as common test data and (2) could be easily and cheaply obtained through future laboratory work. The more obvious possibilities were porosity, permeability and

Jan 1, 1966

By E. W. Dewing

The nature of solid solutions of sodium in non-paphitic carbon at temperatures near 1000°C has been investigated by an electrolytic technique. The activity coefficient is found to vary strongly with the heat-treatment temperature of the carbon, and an analysis of the energy terms involved suggests that this is due to variations in the Fermi level. The diffusion coefficient for sodium is in the range implying that the sodium atoms (or ions) are not bound to specific sites on the carbon, in agreement with lack of evidence for specific compounds in the activity -composition curves. In the light of These results phenomena occurring in aluminum reduction cell linings are dis-cussed. It is concluded that sodium migrates by diffusion through the carbon lallice and not the pores, and that A14C9 is formed within the lining hy The excess of NaF invariably found in used linings is formed by this reaction and by air oxidation: There has recently been much interest in the swelling of carbon which occurs when it is made cathodic in an aluminum electrolysis cell, and there is general agreement that the phenomenon is due to the penetration of sodium atoms, derived from the reaction on the carbon lattice. (NaF and AlF3 are constituents of the fused-salt electrolyte.) The low-temperature lamellar compounds of potassium with graphite are well-known, and one compound between sodium and graphite has been reported.4 There is, however, virtually no information on the basic chemistry of the interaction of sodium with nongraphitic carbon at high temperatures, although Dell3 has made some fundamental studies of rates of penetration. At the time the present work was carried out these were not available. Rapoport and samoilenkol had measured rates of physical expansion in a dilatometer, using the fractional increase in length of a carbon specimen after electrolysis in a cryolite bath for 2 hr as an index of susceptibility to cathodic swelling. Work here with a similar apparatus showed that expansion (of a 1.5-in.-diam cylindrical specimen) ceased in less than 20 hr, and that the final expansion was much more reproducible than the value at some intermediate time. This suggested that an equilibrium was being set up, and that a thermodynamic approach was required. The results obtained are not as accurate as had been hoped, but they are the only ones of their type available and have enabled useful conclusions to be drawn. The experimental work was divided into two parts: an investigation of the activity-concentration diagram for sodium in carbon, and a rough determination of the diffusion rate. For the former, most of the experiments were made with petroleum coke even though this is not a form of carbon used in cell linings. It has the advantages, however, that it is a homogeneous material, that it is low in ash, and that its structure is reasonably well understood. Anthracites and coal cokes gave results of the same type as obtained with petroleum coke, but the reprodu-cibility from specimen to specimen was extremely poor. EXPERIMENTAL 1) The Activity-Composition Diagram for Sodium in Carbon. The petroleum coke was ground, pressed at 40,000 psi into plates 19 by 9 by 2 mm without added binder, and heat-treated. The sodium activities were established by an electrolytic technique. The carbon was made anodic in a cryolite bath with an aluminum cathode, and a controlled potential, E, applied so that the sodium activity at the anode was given by ln Na = 1n asa - EF/RT [21 where as, is the sodium activity generated by Reaction [I]. The relative activity is sufficient for many purposes and is simply given by The value of Na not at present known, but when the thermodynamics of the Na-A1 system have been worked out it can be derived from the equilibrium

Jan 1, 1963

By H. C. Chang, N. J. Grant

Creep of very coarse grained high purity aluminum was studied at 400°, 700°, and 1100°F at initial stresses of 50 to 1200 psi. Local strain measurements were made across the grain boundaries and in different regions of various grains during creep, thereby permitting the drawing of component creep curves. The relative amounts of elongation as measured across a grain boundary and in the grains adjacent to the boundary depend on the temperature of testing. The significance of creep curve equations and activation energies is discussed. THIS paper presents some of the results of a research program devoted to the study of the mechanism of creep in high purity aluminum. Previous publications have dealt with the cyclic processes of alternating grain boundary sliding and migration, and the deformation in the grains caused by these processes;' the direction and the driving force of grain boundary sliding and migration;' the deformation in the grains and the restricting effects of the grain boundaries on this deformation." These previous papers were based mainly on either microscopic observations or X-ray data, or both. Sometimes creep curves across two closely spaced reference marks (about 0.6 to 0.7 mm apart) were also presented with a view to correlating the elongation values with the optical observations in general, and with certain deformation processes in particular. These curves shall henceforth be referred to as component creep curves. No attempts were made, however, to compare either the component creep curves which were obtained in different regions of a specimen, or those obtained from different specimens subjected to different creep test conditions. It is the purpose of this paper to present these component creep curves. Among the factors influencing the behaviors of these curves, those studied were stress, temperature, and grain arrangements in the specimens. It is proposed to show how greatly the deformation can vary from grain to grain and within an individual grain in a coarse grained specimen. The experimental technique and procedure have been presented.' It remains necessary to emphasize that the reference marks were produced by pressing a thin sewing needle into the surface of the specimen before the final annealing at 900°F for 24 hr and at 1150°F for 12 hr. The cold work around the needle indentations was therefore removed. The depth of these holes after electropolishing the annealed specimens was about 0.01 mm. This depth and area were negligible in comparison with the thickness of the specimens, 2.3 mm, and hence would not affect the creep behavior. Results Fig. 1 shows a development diagram of specimen P-8. The dots on the surface locate the needle point reference marks used to obtain the component creep curves. A curve obtained between two dots across a grain boundary measures not only the boundary deformation but also the deformation associated with boundary sliding occurring in the grains in the region between these indents. The original distance between two reference marks was about 0.6 to 0.7 mm. The maximum error of measurement was 0.01 mm, or in terms of percentage elongation, of the order of & 1.5 pct. Whereas the component creep curves shown in the figures to follow were drawn as a gross average of the points, in view of the fineness of some of the steps of grain boundary sliding and migration, as shown in the previous publications,¹,2 it appears logical to expect that some of the finer cycles of movement have not been delineated for the strain sensitivity of the measuring system. It seems justifiable to say that the curves are not as smooth as shown. 700°F Tests: Fig. 2 shows component creep curves across four of the grain boundaries in specimen P-8, tested at 700°F and 85 psi. These curves clearly show alternate cycles of increasing and decreasing

Jan 1, 1954