By R. C. Philp, Allan Gibb

INTRODUCTION. THE term matte is applied to smelting-products so extremely diverse in composition and physical properties that it appears impossible to devise any generic formula to represent, chemically, the manner in which the varied proportions of the almost unlimited possible constituents combine with each other. Mattes produced in copper-smelting, in distinction from those produced in smelting-operations in which the recovery of copper is secondary to that of other metals, cover a narrower range in composition. The copper-content of such mattes vary from 20 to 80 per cent., and even this range is much smaller in general practice since it is found advantageous, when possible, to produce mattes with about. 50 per cent. of copper in the first operation. Further, it is unusual that arsenic or antimony occurs in copper-ores in sufficient proportions to form arsenides or antimonides in such quantities that they will separate out from the furnace-products, as is common in lead-smelting. Generally, the mattes produced in copper-smelting are composed mainly of copper (usually greater than 35 per cent.), iron and sulphur, the remaining elements being usually in proportions sufficiently small to allow of their treatment as impurities, rather than as essential constituents of the mattes. In modern practice of smelting copper-ores in blast-furnaces the tendency is to approach pyritic smelting as nearly as pos¬sible, the furnaces being low and the air supplied being largely in excess of that required for complete combustion of the carbonaceous fuel. Hence the atmosphere of the blast-furnace thus used is usually oxidizing or Dearly neutral? and, as a consequence, the reduction of metallic iron that was a necessary evil of former practice is of unusual occurrence in operations where the main object is the recovery of copper. Hearth-accre-

Nov 1, 1905

By William Priestley

The author has shown, by .practical experiments, how the rate of cooling steel in the mold governs ingotism, segregation, the formation of dendrites, and the distribution of intergranular material; and the resulting effect these conditions have on the physical qualities of the steel before annealing, after annealing, and after forging. The paper also describes how the structure of steel is affected by the design of the mold and the method of pouring. It is shown that the various constituents of carbon steel segregate differently under different rates of cooling. For the classes of steel covered in this paper, it is concluded that the best physical structure and the most uniform chemical composition is obtained by pouring the steel at a low temperature and solidifying as rapidly as possible in the mold. MUCH time has been devoted, by metallurgists, to the study of steel after solidification and remarkable strides have been made in the heat treatment of steel, but less knowledge is available of the thermophysical, activity of the constituents of steel prior to solidification in the mold. It is known that certain elements added to steel produce marked changes in physical properties, also that other elements added to steel produce similar changes, but we have only meager knowledge as to how these elements combine in steel under different conditions of solidification. It is not sufficient to know, from chemical analysis, that a certain element is present in steel. We should know how this element is in combination with the other elements and whether the combination is such as will give the greatest physical properties. Certain elements go into solid solution with the iron, while others segregate to the grain boundaries and combine with the impurities collected there. Until it is known where an alloy produces the most beneficial effect and a means, is determined for controlling its physical location by altering solidification conditions, or otherwise, we will not obtain the maximum value from our alloys.

Jan 2, 1924

By Kenneth K. Humphreys, Joseph W. Leonard, Robert L. Llewellyn, William C. McCulloch

INTRODUCTION The particular field of application of machines utilizing air currents as the primary separating medium is in the cleaning of the fine sizes of bituminous coal. Approximately 25,400,000 tons of bituminous coal were cleaned by air machines during 1965. They have not found any application for cleaning anthracite. Since the development and introduction of the first successful commercial pneumatic oscillating machine for cleaning bituminous coal in 19 16, by the Sutton, Steele and Steele Co, Dallas, Texas, and the American Coal Cleaning Corporation, formerly of Welch, W. Va., seven other successful pneumatic coal-cleaning machines have been developed and introduced to the American coal-mining industry: 1. Peale Davis: "Pneumo-Gravity" machine. 2. Arms "Concentrator," oscillating table. 3. Hey1 and Patterson oscillating table. 4. "Stump Air-Flow," pulsating air jig. 5. "Super Airflow," pulsating air jig. 6. Ridge air jig. 7. Phillip air jig. While not all coals can be beneficiated by air washing, the air washing of coals that are easy to clean can be readily proved advantageous. Of all the preparation methods, pneumatic cleaning is the most acceptable from the standpoint of delivered Btu cost. This is based on the premise that a percent of moisture is just as detrimental as a percent of ash. The principle of dry concentration has never been determined with scientific accuracy. To the present time the study has been more of an art than a science. It is possible to forecast the results of wet concentration from a study of the washability characteristics of the raw coal but only after applying rule-of-thumb methods of interpretation to the specific gravity and size distribution can it be ascertained that the raw coal is amenable to dry concentration. Air as a separating medium dates back to biblical times as exemplified in the winnowing of chaff from the grain. However, the same application of air to coal serves merely to blow the dust away and size the remaining particles. Pulsating air was the solution to the problem and largely eliminated the necessity for close screen sizing which was required on early separators. Because of the low density of air, a medium of sufficient density has to be built with the material itself. Hence there must be some device to impart to the bed the necessary mobility for proper classification. Also, the

Jan 1, 1968

By Larry Kaufman, Joan B. Berkowitz-Mattuck, Edward V. Claugherty

The oxidation characteristics of hafnium and zirconiunr diboride were measured between 1200 and 2200'K by a thermal- conductivity method which continuously ttzeasures the rate of reaction of oxygen with the diboride and by a metallographic air oridation method zuhich provides a measure of the total arr7ount of bovide conuerted to oxide for a given time interval. The oxidized specimens obtained from the tl~eritaal-coi~ductitrity method were also examined by quantitatire metal-lographic procedares. The significant results obtained in this investigation reveal that metal-rich compositions of lzafi~iutil diboride proride the most oxidation-resistatzt material up to 2000°K; hafnium diboride is tmre oxidation- resistant titan zirconium diboride at all tempevatures examined; the morphology of the oxide formed on H/B2 and Llie temperature coefficient qi. the oxidation rate constants change at the temperature of ttze monoclinic to tetragonal phase transition] in HfO2; the oxidation of neither HfB2 nor ZrB2, results iN catastrophic Jazlure at lorc. oxygen pressures; and pvefevetztial gvaLti boundary oxidation was not obsevued for either HfBi or ZYB, A comprehensive study of the high-temperature characteristics of refractory transition-metal di-borides is currently in progress. This program has included investigation of the physical, thermal, and thermodynamic properties of TiB2, ZrB2, HfB2, NbB2, and TaB2. In addition, aspects of the synthesis and fabrication of such materials have been studied. In view of the diverse nature of this research, a number of other laboratories have actively participated and contributed specific capabilities for analysis and characterization of these materials. As a consequence, an extensive description of the relevant properties of these compounds has emerged which is central in evaluating their high-temperature (1200" to 2500°K) performance. To date, information on thermodynamic stability, specific heat, and vaporization characteristics,1 hot hardness and electrical resistivity,1, 3 therma1 expansion:'4 and thermal conductivity 1, 5 has been presented. This information has been generated on materials of the highest purity (98.5 to 99.9 wt pct Me + B) and density currently available. Samples fabricated by zone melting6 and high-pressure hot pressing"3'7 techniques have been used to generate suitable specimens for all of the aforementioned studies. dation characteristics of the most oxidation-resistant of these materials, hafnium and zirconium diboride, is presented and a description of the synthesis and the experimental procedures used to prepare and characterize specimens is given. The high-temperature range under consideration (1200" to 2200°K) and the known dependence of oxidation characteristics on sample chemistry, density, and oxidation conditions required a close coupling of the synthesis, fabrication, and evaluation procedures.8 This was accomplished by continual surveillance of chemical composition of starting materials before and after specimen fabrication and by evaluation of density, phase constitution, and microstructural features prior to and after oxidation exposure. I) PROCUREMENT AND CHARACTERIZATION OF STARTING MATERIALS In view of the current state of the art in fabricating refractory boride materials, the methods used in preparing samples for the present study are given in detail as follows: starting materials were purchased in high-purity powder form and fabricated by high-pressure hot pressing into 0.40 by 1.00 in. bars from which oxidation specimens were obtained. The hafnium diboride used in this study was purchased from Wah Chang Corp.; the zirconium diboride from U.S. Borax and Chemical Co. These powders were routinely characterized by quantitative chemical analyses for metal, boron, carbon, oxygen, nitrogen, and iron, by qualitative emission-spectrographic analysis for trace impurities, by X-ray procedures for extraneous phase identification, and by powder densitometry for comparison with X-ray (theoretical) density. Hafnium and zirconium metal and elemental boron were also purchased as high-purity powders and characterized for impurities by emission-spectrographic analyses. The hafnium diboride was procured in three shipments which were designated as HfBl.g7(1), HfB1.88(2A), and HfB2.12(2). The indicated stoichiometry is based on the atomic ratio of total boron to total hafnium; the number in parentheses identifies the shipment number. Shipment 1 was 5 1b, shipment 2A, 1 1b, and shipment 2, 8 1b. The zirconium diboride was procured as a 20-1b shipment and designated as ZrB1.89(1). A small quantity of purified zirconium diboride was also supplied and designated ZrB1, 9(P). The averaged results for chemical analyses which were generally performed according to the procedures set forth in the compilation by KrieGe9 are presented in Table I. Qualitative spectrographic analyses indicated that Ca, Cr, Ti, Si, Zr (in H~B~), and A1 were present at levels between 0.01 and 0.10 wt pct. Other metallic elements were found to be less than 0.01 wt pct. Since it is virtually impossible to purchase these materials in the desired quantities (5 to 20 lb) as single-phase compounds it is necessary to obtain

Jan 1, 1968

By Roger N. Dokken

It is well-known1-4 that Fe-Si alloys from approximately 9 to 27 at. pct Si show an ordered structure of the Fe3Si type at room temperature. Recently Meinhardt and Krisement,' through an investigation of Fe-Si alloys at room temperature by neutron diffraction, discovered that at 10.8 at. pct Si ordering of the FeSi type occurs while above this composition the normal Fe3Si-type superstructure appears. This FeSi type of ordering was also found by Davies8 as indicated by X-ray diffraction measurements on an Fe-8.7 at. pct Si alloy. Meinhardt and Krisement7 extended their neutron-diffraction work and determined the phase-boundary temperatures for both FeSi- and Fe3Si-type ordering. Ordering phenomena can also be studied by resistance measurements.4,8-11 Krivoglas and Maty-sina" carried out a theoretical development of the

Jan 1, 1965

By Benjamin C. Craft

A review of development in North Louisiana during 1936 centers around the Rodessa field, in Caddo Parish. Continued extension of the

Jan 1, 1937

By John V. Beall

Never having done it before, it took us all day and until 11 at night to select and pack for a four-day back- pack trip up Lake Chelan last month. When we were through, we couldn't lift our own pack and Sylvia's, OUT spouse's, we barely managed to budge. Nevertheless, the next morning we were at the dock to board the Laldy of the Lake for the 3 ½ -hr boat trip to Lucerne. Our dress and accouterments creating the appearance of a veritable expedition into the wilderness made a sharp contrast with our fellow passengers, a senior citizens tour group from Spokane. We had come out to Seattle for the SME Fall Meeting and were taking advantage of the occasion for a vacation trip back to Lucerne and Holden where we had lived briefly 25-years ago, and a backpack trip up Railroad Creek from Holden to the Glacier Peak country, weather permitting. No matter what you say, weather is important, and this is one of the ingredients that went into making the SME Fall Meeting and Exhibit in Seattle, September 22-24, a thoroughly delightful experience for the 700 plus persons who attended. Seattle is a beautiful city, but with late September sunshine, which we experienced, it is the best. The second ingredient, is a swinging host committee. Under the leadership of Don Anderson and Tom Van Zandt, co-chairmen, and Mrs. Cecilia Reed, Ladies Program, superb hospitality and fine arrangements were blended. Earl Beistline, from Fairbanks, organized a two-day short course on arctic operations which preceded the meeting and drew an attendance of 44. Dick Robbins, in charge of arrangements, provided Masters-at- arms for technical sessions and a presentation of the colors by the U.S. Coast Guard at the Welcoming Luncheon. Eric Cheney's field trips ranged far and wide with events both before and after the meeting. David (Jeff) Kroft, capably managed audio-visual operations with a group of students from the University of Washington. Charles Hochmuth worked long, hard and effectively before and during the meet- ing on finances. Hank Reed, managed an authentic three-ring circus as Entertainment Chairman. His activities covered two cocktail receptions for all registrants and a dinner-dance. Dolph Campbell and Joe Hackbarth provided publicity by press and TV (see p. 37-40). SME's meetings have certain characteristics and possibly not all of these are known to everyone. The first of these is the deliberate involvement of the AIME Section in the area of the meeting. Most trade shows and conventions are run 100% by a professional staff and although SME staff could also do this, it has been our experience that a more friendly and better meeting results when the local members apply their talents. Actually SME only considers a site for a meeting after it has received an invitation from a Section. The knowledge of local conditions which Section committeemen bring to a meeting is of great value.

Jan 1, 1971

By HENRY M. HOWEL

1. Introduction.-The first part of this papers treats of the causes and the restraining of piping in steel ingots; the second& considers the causes and the restraining of -segregation; and the third proposes certain precautions in engineering specifications concerning these two defects. Into their causes I have looked carefully, with the purpose of arriving at rational methods of restraining them, and at efficient ways of detecting. and measuring the harm which they cause, so as to benefit the public by reducing this harm at once effectively and with the least expense to the manufacturer, and therefore in the end with the least expense to the consumer. In Part I., I infer that the pipe is chiefly due to what I, call the virtual expansion of the outer walls of the ingot in the early part of the freezing. I find that the upper and smooth-faced part of the pipe probably forms while the interior is still molten, but that the lower, steep, and crystal-faced part probably forms in metal which is already firm. Of the five causes which may co-operate to limit the depth of the pipe, I find that three-blow-holes, sagging, and the progress of freezing from below upwards-are usually effective. I find that the pipe may be lessened by casting (1) in wide ingots,; (2) in sand molds, especially if these are pre-heated (this is rarely expedient); (3) at the tops instead of at the bottom; (4) slowly; (5) and with the large end up; (6) by the use of a sinking-head or other means of retarding the cooling of the top; (7) by permitting blow-holes to form; and (8) by liquid compression.) Most of these I consider in some detail, and in particular I dwell on the advantages of casting with the large end up, and I propose certain administrative arrangements to permit this.

Mar 1, 1907

By Salinger, Herbert

WITH the large amount of metallurgical re- search work now being done and the constant effort of the engineer to effect economies of operation, I think it is a safe prediction that the next few years will see a great change in the handling of mine products. The well-managed mine, with sufficient ore reserves to warrant the necessary plants, will increasingly call upon the metallurgist and chemist for the solution of its problems. Shipping sorted ore or concentrate to the nearest smelter will not be the course followed. From ore to metal, or at least to a product directly salable to the consumer, will be the practice followed. As a consequence, mine managers will be increasingly interested in metal trade problems. By metal trade I mean the buying, selling, shipping, handling, and all the practices, forms and customs that go to make up the trade.

Jan 1, 1928

By E. O. Wagner, V. F. Parry

This paper summarizes investigations during 1949 on three pilot plants for drying low-rank fine cool by entrainment in hot gases. Detailed operating results on processing seven coals having moisture ranging from 24 to 62 pct, formulas and data for calculating performance of large units, and general conclusions on the problem of drying fine coal are presented.

Jan 1, 1950

By A. R. Gregory, A. L. Podio, K. E. Gray

Dynamic elastic properties of dry and water-saturated Green River shale samples were computed from compressional- and shear-wave velocity measurements. P- and 5-wave velocity measurements were made in three mutually perpendicular directions with respect to the bedding planes. Measurements were also made in several different directions by varying the angle between the bedding planes and the direction of propagation of the wave for angles of 0, 30, 45, 60 and 909 The oriented samples were subjected to both confining pressure and axial loads, in excess of the confining stress, in the direction of propagation. In general, P- and S-wave velocities increased with increasing stress levels, with a corresponding increase in Young's modulus. Water saturation caused the P-wave velocity to increase and the S-wave velocity to decrease. Elastic moduli decreased upon saturation, except for Pois son's ratio, which increased, indicating some degree of weakening of the material. The samples showed a moderate degree of anisotropy; this was to be expected from the laminated nature and shallow occurrence of Green River shale. INTRODUCTION This paper presents some results of an experimental determination of the elastic coefficients of anisotropic materials (in particular, finely layered rocks and minerals such as Green River shale) from measurements of dilatational and shear-ultrasonic-wave velocities. Ultrasonic techniques have been used extensively in nondestructive testing. Several methods have been proposed by Mcskimmin, 1 and some of these have been used successfully to measure ultrasonic velocities in rocks. Hughes and Cross, 2 Wyllie et al., 3 and Birch 4,5 developed pulse first-arrival techniques for the measurement of dilatational and shear velocities. Williams and Lamb 6 used the method of cancellation of a traveling wave, which was later modified by Myers et al.' and perfected by McSkimmin. 8 Although this method is highly accurate, it has not been used as widely as the pulse-transmission methods recently reported by Jamieson and Hoskins 9 King,10 and Mattaboni and Schreiber. 11 It has been common practice to use some form of crystal transducers, either quartz or ceramic, that has been cut or polarized in different directions in order to generate either compressional or shear waves. However, accurate determination of shear wave velocities has been difficult due to problems that arise in obtaining a pure shear wave from cross-polarized crystals, which usually also generate a small amount of compressional energy. As reported by Gregory, 12 this energy can be seen as a long precursor preceding the sharp break of the shear first arrival. The need for generating pure shear waves led to interest in mode-conversion techniques, which are based upon conversion of the mode of vibration through wave reflection or refraction at a discontinuity. Arenberg13 showed that for certain materials and for certain angles of incidence it is possible to generate pure shear modes by reflection at a boundary. Jamieson and Hoskins 9 used a pyrex glass-air interface for generating pure shear waves, and King 10 used this method successfully for measuring shear-wave velocities in rocks. Gregory l4 arrived at a similar result by refraction of a wave at an aluminum-oil interface. A plane compressional wave, traveling in the oil phase, is incident on the aluminum at an angle larger than the critical angle for compressional waves, and thereby generates a purely transverse, plane-polarized wave in the aluminum. During the last few years methods have been developed that allow the simultaneous determination of shear and compressional velocities in solids.

Jan 1, 1969

By ROBERT. RICHARDS

I. INTRODUCTION The object of this paper is to enlarge the field of settling velocities treated by me in my former papers, Close Sizing Before Jigging, and Sorting Before Sizing.' There seemed need of work both on coarser and on finer sizes. Messrs. A. Sidney Warren and M. L. Nagel undertook the investigation for the coarser sizes, from 12.85 mm. down to 2.05 mm. diameter. Their work, because of the closer spacing and because of the increased number of observations and consequent stronger averages, called for a revision of the former work. Messrs. G., A. Barnaby and Ralph Hayden undertook this part of the work, from 2.49 mm. down to 0.28 mm., which is near the limit of sifting. Their work covers the ground much more minutely and comprehensively than the former papers. There remained to be covered the portion of the field too fine for investigation with the sieves. This part, covering the range of grains from 0.48 to 0.03 mm., was undertaken by Mr. E. S. Bardwell. For it he used the elutriation method. II. THE FIRST, OR COARSEST, SECTION OF THE FIELD. The first desideratum in this investigation was a series of sieves for sizing the sands preparatory to making the tests. It became necessary, therefore, to decide on a sieve-scale for this purpose. A sieve-scale is a series of sieves in which the dimensions of the holes of the successive members form a series increasing by a. definite ratio. There are three natural sieve-scales : 1, progressing by doubling the width of the hole for each suc-

May 1, 1907

By Elmer W. Pehrson

Minerals have played a prominent role in the affairs of man and nations since time immemorial but with the advent of the industrial revolution, expanding use of the products of the mineral kingdom became synonymous with the material progress of mankind. Individuals and business groups have recognized this fact so have been aggressive in searching for and utilizing mineral resources, with notable success. Indeed, their achievements are primarily responsible for the present Machine Age. On the other hand, until recently the body politic has failed to grasp fully the essentiality of minerals although, at times, access to mineral supplies has been an important factor in the political maneuvers of nations. This chapter is concerned primarily with the broader political and economic relationships of mineral resources to the world economy, and with the internal and external actions of nations in the field of minerals. Many factors that condition the mineral economy of regions and the world as a whole, influence the internal and external affairs of individual nations. The more important of these are: 1. The nature of man's dependence on minerals. 2. The problems resulting from the unique characteristics of mineral occurrence. 3. Geopolitical concepts. 4. Minerals and world power. Actions of individual nations affecting their mineral economy seek two basic objectives : 1. Attainment and maintenance of prosperity. 2. Military security. Other objectives may be cited but on careful analysis they become integral parts or extreme phases of the two points noted above. For example, the twentieth century aggressions of the USSR, Germany, Italy, and Japan might be considered as direct bids for world power but they also can be interpreted as exaggerated or mistaken efforts toward military security and peacetime prosperity. Similarly, trade barriers, nationalization of industries, foreign exchange manipulations, taxation, monopolistic prac-

Jan 1, 1959

By C. M. Wayman, J. F. Breedis

The crystallography of the martensitic transformation in the Fe-30 Ni alloy was reinvestigated. The scatter in the habit Plane as determined from measurements on the mid-rib plane was smaller than reported previously, and the orientation relationship was determined from a martensite plate having known direction cosines. From agreement with crystallographic theory and from observations of the morphnlogy of the martensite plates, it is suggested that the mid-rib plane represents the starting region of the transformation. THE crystallography of the martensitic transformation in the iron-nickel system has been the subject of many investigations.&apos;-7 However, for iron alloys containing approximately 30 wt pct Ni, a wide scatter in the reported habit planes exists. In only one instance has a Laue determination of the orientation relationship been made, but the habit plane of the martensite plate studied was not determined experimentally. Because the most successful thermodynamic and kinetic analyses8 of the martensite transformation have been based on Fe-30 Ni alloys, it was considered desirable to reinvestigate the crystallographic features of the transformation in this alloy. Lieberman9 suggested that the most significant information for use in a theoretical treatment involves the determination of all the crystallographic observables from a single plate of the product phase. This was first done in essence by Greninger and Troiano10 for Fe-22 wt pct Ni-0.8 wt pct C, and is the method followed in this investigation. Some theoretical approaches11-13 in describing the martensitic transformation consider the overall transformation distortion to be comprised of a Bain distortion, or lattice deformation (PI, which produces the structure change, and a lattice invariant deformation (G), such as twinning, which together leave the interface or habit plane un-distorted. The incorporation of a rigid body rotation (R) results in a transformation distortion (E) such that the interface plane is left both undistorted and unrotated. In matrix notation, E = RPG where the lattice invariant deformation has "taken place" in the austenite. Bowles and Mackenzie14-16 in formulating a theoretical approach proposed an adjustable scaler quantity, denoted as 6, which represents a uniform dilation in the interface plane. This dilation acts to adjust the lattice spacings of the parent and product structures at the plane of contact. Using the dilation parameter as a variable, these authors were able to account for a continuous variation of habit planes in steels along a curve in the stereogram between {225}A and {259}A. she invariant line strain14 of the transformation is 6 RP, and the corresponding transformation distortion is E/6.) With the dilation parameter known, the invariant line is computed as the triple coincidence of the habit plane, the shear plane of the lattice invariant deformation, and the initial Bain cone.14 The contraction axis for the Bain distortion can be taken9&apos;17 as [010]A, and the correct permutation of the habit plane indices used. Kelly and Nutting 18 have established the shear plane (of twinning) in the tetragonal martensite of Fe-22 Ni-0.8C to be {112)M by means of transmission electron microscopy. The reasonable shear system is then {112}M which is equivalent to {011}A <01l>A. The as-

Jan 1, 1962

Jan 1, 1968

By S. A. Levy, J. D. Wood, J. F. Libsch

A study of the preparation and characteristics of a sevies of Fe-C-N alloys has been conducted. X-ray, microhardness, and metallographic data from a series of single-phase alloys produced by controlled nitriding of carburized foils are reported. The existence of a, y&apos;, and E carbonitride has been confirmed and it has been found that y&apos; is the hardest of these three phases. These results have been used to interpret the structures observed in nitrided steels. ThIS paper represents the second phase of a three-part study concerning combined nitriding and induction hardening. The first part&apos; reports the engineering properties (depth hardness, fatigue, corrosion, and tempering resistance) obtained when seven different steels were subjected to the combined surface hardening treatment. The present paper concerns the nature of a series of single-phase alloys prepared by controlled nitriding of carburized foils. The objective was to simulate the various layers present in the as-nitrided steels. A third paper will report data concerning induction hardening of the foils and will attempt to set forth a mechanism for the high hardness obtained with the combined treatment. Studies of nitriding generally fall into three categories. The first were performed with bars using conventional nitriding procedures, thus yielding a nitrogen gradient and a series of phase layers near the surface.2-6 Such studies were complicated by the presence of the nitrogen gradient, for it was difficult to correlate microhardness and X-ray data with chemical composition. There were always complications due to penetration of the X-ray beam which yielded data influenced by underlying layers. Similar difficulty was experienced in taking hardness readings on a tapered specimen or in isolating various layers by machining. A second group of investigations was primarily concerned with establishment of regions in the Fe-N7,9,10 or the Fe-C-N phase diagram.8 These were performed with powder specimens which were nitrided in am-monia-hydrogen mixtures to produce a series of single-phase specimens. Unfortunately, the powder specimens were not amenable to either microstruc-ture or microhardness study. The third was essentially a compromise of the first two. Bose and Hawkes," using 0.005-in.-thick iron foils, were able to obtain microhardness, microstruc-ture, composition, and X-ray data on Fe-N alloys of eutectoid composition by equilibration in ammonia-hydrogen mixtures at 1290°F. To obtain a better understanding of the nitriding process and the characteristics of the phases in ni-trided plain carbon steels, the present investigation was undertaken. The investigation was patterned after that of Bose and Hawkes with the exception that nitriding was performed at 930°F (below the eutectoid temperature), as in the case of conventional nitriding. In addition to gaining some understanding of the source of high hardness of nitrided and induction-hardened steels, found in a previous study,&apos; this investigation was concerned with the possibility of controlling the phases present in a nitrided case through the use of ammonia-hydrogen mixtures. Knowledge of the properties of each phase and the conditions necessary for its production could make it possible to avoid undesirable surface layers in nitriding. EXPERIMENTAL PROCEDURE Specimen Preparation. A specimen thickness of 0.005 in. was selected to insure that a uniform nitrogen concentration could be obtained in a reasonable length of time by equilibration in an ammonia-hydro-gen atmosphere. The starting material was a vacuum-cast ingot of pure iron, the major impurities of which were: C, 0.003 pct; 0, 0.014 pct; S, 0.004 pct; N, 0.003 pct.* &apos;Compositions are quoted as weight percent except as noted. The ingot was heated to 1500°F in a nitrogen atmosphere and forged to a slab 0.25 in. thick. The material was then reduced to 0.005 in. by alternately cold rolling and annealing in a nitrogen atmosphere at 1600°F. This material was divided into five groups of specimens which, after carburizing, yielded the following carbon contents: 0.003, 0.28, 0.36, 0.46, and 0.74 pct C. The carburizing was performed by the Leeds and Northrup Research Laboratories, using a controlled "carburizing potential" which yielded a uniform carbon concentration throughout the cross section.

Jan 1, 1970

By K. Sallmann

Spurred by a variety of factors, coal flotation is making headway among the preparation plants of West Germany. The author gives some statistics on German coal flotation plants and information on the properties of the feed and quality of the derived products. Types of machines and reagents used, dewatering practices, tailings disposal, and thickening operations are covered. There is special emphasis on the many-sided problems that confront German coal preparation engineers. The coal mining industry of West Germany is concentrated in three coalfields: the first on the Ruhr and the Rhein rivers, the second on the Saar river, and the third near the frontier between Germany and the Netherlands, around the towns of Aachen and Erkelenz. The total run-of-mine production of these three coalfields amounts to 736,000 tpd which come from 145 collieries. There are 121 washeries, 43 of them with a flotation plant. The total throughput of these 43 washeries is 280,000 tpd, out of which 26,000 tons (9.3 pet of the washery feed coal) are cleaned by flotation. The capacity of the individual flotation plants varies within relatively wide limits, the average being 40 tph and the capacity of the largest flotation plant being 120 tph. During the last few years, the number and size of flotation plants have been steadily increasing, although flotation must be looked upon as an expensive and rather complex cleaning process. The considerations which have led to the widespread application of flotation may be summarized as follows: 1) In making coking coal, it is seldom possible to add uncleaned fines to the coke oven charge, as their ash content is too high. If, however, the ash content of the fines is reduced to a maximum of 7 or 8 pet, they can be admixed to the washed and crushed small sizes without difficulty. This means, naturally that revenue is increased since the price of coking fines is always higher than the price for dust or uncleaned wet fines. 2) To prevent silicosis and pneumoconiosis, water infusion and spraying of the coal are practiced much more today than ever before. As a result, moisture content of run-of-mine coal has markedly increased and the washery feed coal contains more and more slurry instead of dry dust. The price of slurry, how- ever, is very low, and in many cases it is impossible to sell filtered raw slurry with a moisture content of 20 to 25 pct and, at the same time, 20 to 25 pct of ash. Reduction of the ash content of these slurries improves the possibility of dewatering them and, in this way, also enhances the marketability of this product. 3) The new severe laws and regulations against pollution of air and rivers make it necessary to de-dust coal better than in the past and to reduce the quantity of the waste water from coal preparation plants and their solids content to a minimum. 4) Even if there were no compulsory reasons to clean the fines, flotation will often lead to an increase in the overall yield. Although not the only application, it appears that the treatment of coking fines is the primary field for the flotation process in coal preparation. It must not be overlooked, however, that a series of arguments may be advanced against flotation: 1) Flotation is an expensive process because, in addition to the cleaning operation itself, the dewatering of the froth and the disposal of the tailings is very costly. 2) Operation of a flotation plant requires well trained personnel. 3) Filtered froth has about a 20 pct moisture content and, therefore, if mixed with the cleaned small coal it causes an undesirable increase in water content of the coke oven charge. For this reason it is necessary to take additional measures for dewatering washed small coal and this, of course, entails additional expense. 4) Disposal of flotation tailings involves very difficult problems, particularly in the highly industrialized regions. An investigation covering 32 flotation plants of Western Germany shows the following composition and properties of their feed:

Jan 1, 1961

By R. F. Mehl, C. E. Birchenall

SINCE Maxwell1 first considered the self-diffusion process in 1872 its importance in the kinetic theory of matter has been recognized. Until the discovery of isotopes in 1913, a direct measurement of this quantity seemed impossible. The only information that could be gathered indirectly was for gaseous systems for which the kinetic theory was well developed. When methods of direct observation be-came available, investigations on self-diffusion were carried out in condensed phases. In metals these data are presumably of potential importance in the study of recovery, recrystallization, creep, sintering, and related phenomena. Following the pioneer work of Von Hevesy2 and his collaborators, who determined the rate of self-diffusion in lead with the naturally occurring thorium B isotope, several metals have been investigated. Pb, Ag³, Au.6,5, and Cu6,7,8,9 are examples of isotropic crystals existing in only one phase modification. Anisotropy of diffusion has been demonstrated in Bil6 and Znll. This paper is a study of a single metal in two allotropic forms and also of self-diffusion in a body-centered cubic lattice. Despite the fact that the measurements in each of the papers cited on self-diffusion in copper seem to be internally consistent to about 10 to 15 pet, the curves reported by different authors differ by factors of 2 to 4 at the same temperatures. This uncertainty may account, in part, for the failure to establish a successful correlation between the self-diffusion rates and other physical characteristics of the metals. No satisfactory theory of metallic self- diffusion has as yet been proposed to account for all the existing data and to permit estimation in other metals. Experimental Part: Two units of radioactive iron were used in these experiments, each a mixture of Fe53 and Fe59 (12). Fe53 decays by K electron capture and the emission of an X ray with a half life of about 4 years. Fe59 emits two beta spectra, one with a maximum energy of 0.26 Mev, the other 0.46 Mev, and gamma rays of 1.1 and 1.3 Mev, with a half life of about 44 days. They were present in nearly equal concentration initially. The composite half life started at about 50 days and increased as the Fe59 decayed, leaving Fe55 relatively more abundant. After aging a year, the half life was too long to measure significant decay in a month. The absorption properties also changed with time. Because of the importance of the absorption coefficient in the diffusion calculations, it was necessary to determine this quantity frequently over the period during which these experiments were carried out. This correction was unsuspected at the time of publication of notesl3 on this work and accounts for the discrepancy in alpha iron and for part of the discrepancy in gamma iron.* * The data in the present paper supersede those given in the notes entirely. In one note the scale of log D was inadvertently reversed. In addition to the correction for the drift in absorption coefficient, the D values for gamma iron at low temperatures were high owing to insuficient correction for diffusion occurring during heating and cooling through the high temperature part of the alpha range at a rate much slower than that employed in the runs reported here. The high temperature alpha rates are much higher than the low temperature gamma rates and correspond to large equivalent times at these temperatures. These experiments were discarded and new measurements taken. Independent experiments with the same activity units indicated a radioactive contaminant in the iron, but exhaustive attempts to isolate and identify it chemically failed. These experiments? indicate † These experiments will be discussed in a later publication from this laboratory. that the contaminant represented only a trace of little importance in the diffusion results. The active iron was plated from an iron chloride solution. Enough of the solution was dropped on a 1% in. square of filter paper to wet it thoroughly.

Jan 1, 1951

By W. J. Schuster

Safety in coal mines depends largely upon adequate training of the foreman. Although management must provide modern and safe equipment and at all times keep mines in first class condition from a safety viewpoint, final results will be determined by the quality of supervision. HANNA COAL CO., Division of Pittsburgh Consolidation Coal Co., operates three large underground mines in eastern Ohio. The section of Pittsburgh No. 8 coal seam in which these mines are located varies in thickness from 52 to 64 in. It is immediately overlain by a stratum of shaly material 12 to 15 in. thick locally known as draw slate, which is structurally very weak and which disintegrates rapidly upon exposure to atmosphere. Immediately above the draw slate as it is normally found is a band of extremely high ash material 6 to 12 in. thick known as roof coal or rooster coal, and above this is a stratum of conglomerate material varying from 4 to 10 ft in depth. Overlying the conglomerate is a relatively thick stratum of limestone, the first stable material above the Pittsburgh coal seam in eastern Ohio. With the method of full-seam mining that has been adopted, draw slate is shot down, loaded with the coal, and removed in the preparation plants. The roof coal then becomes the permanent roof. The major problem in mining the No. 8 seam in eastern Ohio is control of the roof. Since the strata above the draw slate contains no material with a structure firm enough to provide self-support, the roof begins to sag in a relatively short time after the coal and draw slate have been removed. The problem thus becomes one of getting temporary safety posts under this roof as quickly as possible to prevent a break or separation from occurring either in the roof coal or in the conglomerate above it. Haulage System The Pittsburgh No. 8 seam in eastern Ohio is relatively level, with only minor local dips. Throughout the Hanna Coal Co. mines, entries are generally 12 ft wide. Rooms are driven on a 60" angle on 30-ft centers and are 22 ft wide. No attempt is made to extract the 8-ft pillars between. The entire length of main line haulage is gunited in one mine, and a major portion in another. Two of the mines have single-track main haulage roads with passways. The third, a new mine, is double-tracked, and the roof is supported by steel crossbars, 60 lb or heavier, spaced on 4-ft centers and lagged. In recent years timbering on main line and secondary haulage roads has been accomplished by one of two methods: 1—crossbars are supported on a small section of post set in a hitch hole in the rib, or 2—or a hole is drilled in the rib about 12 in. below the roof, of sufficient depth to fasten securely a short length of 40-lb rail, the bottom of the rail facing the roof, on which a short post is set directly under the crossbar. At present the hitch-hole timbering method is favored. At two of the mines the main line haulage locomotives are 26-ton, 8-wheel units. These locomotives are of the axleless type, each wheel being individually mounted on the frame. The motorman&apos;s compartment is encircled by 3-in. armor plate for the protection of the occupants. At the third underground mine conventional 15-ton locomotives are being used. However, these locomotives have been completely rebuilt in the company&apos;s shops. Equipment has been streamlined and quarters have been provided for two people, who are protected by heavy steel plate in much the same way described above. This modernization program has been completed on all secondary haulage locomotives at the three mines, and the company is well on the way to similar equipment of the 6-ton section locomotives. The following additional features have been included in their modernization: 1—additional support for the motors to prevent their falling to the middle of the track and derailing the locomotives should a break occur in the suspension bar support; 2—installation of additional bracing to prevent brake rigging from becoming displaced and causing derailments; 3—enclosure of all electric wiring in conduit or raceway; 4—provision of an enclosed compartment for the storage of re-railers, jacks, and other equipment, so that they need not be carried on the outside of the motor; and 5—redesign of the end of the locomotive opposite the operator&apos;s compartment to prevent anyone&apos;s mounting from that direction. It is interesting to note that some

Jan 1, 1955

By George Krauss, M. Cohen

The reverse martensitic transfomzation (i.e., the conversion of martensite to austenite on heating) was investigated in Fe-Ni alloys containing 30.5 to 33.5 wt pct Ni. The reversed austenite was found to be sufficiently distorted to exhibit marked differences in mechanical properties and to undergo recovery and re crystallization on further heating. In particular, the yield strength of the reversed austenite was as much as 2.5 times higher than that of the virgin austenite: with five cycles of the direct and reverse martensitic transformation, the yield strength was 2.6 times higher. There was an accompanying decrease in strain-hardening capacity and in stable ductility or uniform elongation. The recrystallization was observed to follow sigmoidal kinetics, but was characterized by an abnormal1y large temperature dependence which was evidently due to carbon segregation at the migrating grain boundaries. Upon recrystallization, the strength Properties reverted to those of the virgin austenite, but the ductility did not fully recover until the annealing temperature was further raised to dissipate the carbon segregation at the grain boundaries. The transformation of reversed austenite to produce second-generation martensite resulted in an unusually imperfect structure, thereby leaditg to additional strengthening. Horlleuer, the martensitic phase was much less responsive in this respect than was the austenite. MOST martensitic transformations are capable of undergoing a reverse transformation back to the austenitic phase on heating.&apos; This reaction, like the direct transformation to martensite on cooling, is usually athermal. In analogy with the Ms andMf temperatures for the martensitic transformation (where M, > Mf), the reverse transformation is characterized by the As andAf temperatures (where As<Af). It is well-known that the finish (Af) of the martensite-to-austenite reaction on heating may occur at a temperature where austenite is not stable relative to other phases in the equilibrium diagram.&apos; Reverse martensitic transformations have been found to influence the properties of the parent austenitic phase in a number of ferrous alloys. The austenite thus produced after one or more reversals is significantly altered in strength, microstruc-ture, diffusivity, and annealing characteristics compared to well-annealed, virgin austenite. The first detailed observations of such phenomena were made by Wasserman3 on an Fe-30 wt pct alloy. He found that the reversed austenite (i.e., austenite formed by the reverse martensitic transformation) was much stronger than the original austenite, and the second-generation martensite (i.e., martensite produced from the reversed austenite) was somewhat stronger than the first-generation martensite. On heating the reversed austenite, recrystallization occurred in a manner similar to that of a cold-worked metal; the Laue spots sharpened and the strength decreased.4 In recent years, Russian workers have shown considerable interest in these reverse martensitic transformations. Most of such investigations5-10 have been concerned with the stabilization of reversed austenite relative to subsequent martensitic transformation, and because of its unusual nature, this phenomenon will be discussed in detail elsewhere." On the other hand, the annealing behavior of reversed austenite and the attendant variation in properties have received little attention beyond the experiments of Wasserman.3,4 Gridnev eta1.,8 in one of the few such studies. followed the hardness change of reversed austenite as a function of time at three annealing temperatures. The marked strengthening of austenite achieved by the reverse martensitic transformation has been referred to as "transformation strengthening" by Wasserman3,4 and as "phase hardening" by Malyshev et a1.7,9,10 to differentiate it from hardening produced by cold working. Both groups of investigators noted that further strengthening of the austenite could be attained by repeated or cyclic transformations, but the first cycle resulted in the most pronounced effect. Evidence of the altered microstructure of reversed austenite has been reported by Maximova and Nikonorova6 and by Edmonson and KO.12 The former found that reversed austenite was much more sensitive to etching than the original austenite, and the latter authors observed a (&apos;ghost" structure resembling martensite in certain areas of the reversed austenite. Enhancement of the self-diffusion rate in reversed

Jan 1, 1962