The following is an incomplete list of members and guests who called at Institute headquarters during. the period Mar. 10, 1919,. to Apr. 10, 1919. F. T. Agthe, Hannibal, Mo. Jay Lonergan,. Denver, Colo. W. F. Almy, Canada. R. R. London, Cebu, P. I. P. G. Bandy, Mexico. W. D. Mainwaring, Philadelphia, Pa. H. R. Bank, Humboldt, Ariz. _ W. G. Mitchell, Montreal, Can. Alan M. Bateman, New Haven, Conn. Francis Nicholson, Joplin, Mo. C. A. Brooks, Lead, S. Dak: C. H. Palmer, Los Angeles, Calif. Louis J. Brunel, Oakland, Calif. D. A. Powell, Columbus, Ohio. W. Burns, Sante Fe, N. M. W. H. Reber, Dallas, Tex. J. B. Carlock, Major, 1st Gas Regt. Capt. J. B. Richards, Spokane, Wash. Louis S. Cates, Hayden, Ariz. T. C. Roberts, E. Orange, N. J. W. M. Corse, Mansfield, Ohio Max Roesler, Washington, D. C. E. 0. Daue, Philadelphia, Pa. C. 0. Sanford, Los-Angeles, Calif. John Davenport, W. Norfolk, Va. Gustave Sessinghaus, Denver, Colo. James T. Dixon, London, England, . E. H. Shriver, Milford Center, Ohio. S. K. Dahl, Messina, Transvaal, S. Af. H. M. Spoor. W. G. Eberhardt, Tucson, Ariz. W. H. Staver, New York. H. S. Emlaw, Grant Haven, Mich. D. B. Sterrett, Washington, D. C. I. W. Farrand, Camp Merritt. W. G. Swart, Duluth, Minn. Oscar Gotsch, Jr., St. Louis, Mo. A. W. Stickney, London, England. James 0. Greenan, Oakland, Calif. E. C. Templeton, Downey, Calif. Gilbert Hart, Philadelphia, Pa. . . R. T. Walker, Pioche, Nev. K. L. Hsueh, China. A. T. Ward, Bellefonte, Pa. Zay Jeffries, Cleveland, Ohio. Joel H. Watkins, Washington, D. C. R. W. Kern, Verde, Ariz. J. Wertheimer, Cleveland, Ohio. H. D..Kinney, Easton, Pa. C. R. Wilfley, Ouray, Colo. E. L. Lasier, Washington, D. C. J. P. Wood, Engrs., U. S. A. Carl Zapffe, Brainerd, Minn. Leland D. Adams has left the employ of the Weedon Mining Co., Ltd., at Montreal, Quebec, and is going to Oakland, Calif., where his address will be 1180 Mandana Boulevard.

Jan 5, 1919

By J. S. Kasper, R. M. Waterstrat, B. F. Decker

THE large difference in the X-ray scattering factors for molybdenum and manganese makes the o- phase in the Mn-Mo system an interesting one to study with respect to ordering of the atoms. Such a study has been carried out using data obtained from a powder sample, and the resulting evidence for ordering in this compound is presented here. It is not possible, of course, to obtain all the details of structure for a u phase from powder data only. Most difficult of all would be the determination of precise atomic parameters. There is reason to believe, however, that the atomic parameters do not vary greatly in the different s'S and that the precise values obtained from one s structure would then allow decisions as to the ordering of atoms to be made when there is a large difference in scattering factors. In particular, the powder intensities for Mn-Mo s are for the most part in good agreement with those observed for Co-Cr, for which single crystal studies have been made by the authors.' There are a few marked discrepancies in the intensity comparison of the two s's, and these cannot be removed by adjustment of the parameters. They are interpreted as resulting from a more pronounced effect of ordering of the atoms. Accordingly, the parameters of Co-Cr s' have been used for the calculations of the Mn-Mo intensities. For Co-Cr, the space group is D4h14-P4/mnm with atoms in the following positions: 1—2 in (b); 11—4 in (f), with x=0.1031; 111—8 in (i), with x= 0.3713 and y=0.0370; IV—8 in (i), with x=0.5662 and y=0.2396; and V—8 in (j), with x=0.3160Y and y — -0.250. The unit cell is tetragonal, with an==9.10A and cn=4.74A for the Mn-Mo u phase studied here.

Jan 1, 1955

By Robert A. Rapp, Ronald L. Pastorek

Solid-state electrochemical measurements by three alternative experimental procedures were made with the cell FeO, Fe3O4 |Zro.85Cao.15O1.85 |Cu| Zr0.85CaO.15O1.85 | FeO, Fe304 to establish the solubility and diffusivity of oxygen in solid copper in the temperature range 800" to 1030°C. The solubility of oxygen in solid copper and the diflusivity of oxygen in solid copper Dgu = 1.7 X 10-2 exp(-16,000/RT) Cm2/sec were determined and confirmed in alternative experiments. The enthalpy of solution of oxygen in solid copper equals —10,000 cal per mole; the partial excess entropy of the oxygen atoms in the Cu-O dilute solution is approximately the same as that found for interstitial atoms in other metals. The diffusivity of oxygen in solid copper is consistent with that expected for an interstitial atom. RELIABLE values for the saturation solubility N(s) and diffusivity DO of oxygen in solid copper have not been unambiguously established in the literature. Following three early determinations by others,1"3 Rhines and Mathewson4 reported that the solubility of oxygen in solid copper increased from 0.007 at. pct 0 at 600°C to about 0.015 pct at 1050°C. Phillips and skinner,, using essentiially the same analytical procedure, reported that the solid solubility increases from 0.0018 at. pct 0 at 550°C to about 0.0075 pct at 1050OC. The only previous value for the diffusivity of oxygen in solid copper was reported by Ransley.6 Ransley deoxidized Cu-Cu2O alloys in an atmosphere of carbon monoxide gas to yield a solubility-diffusivity product. He used the solubility data of Rhines and Mathewson to calculate the diffusivity values. Another method for obtaining the solubility-diffusivity product (N(s) DO) is by measuring the widths of internal-oxidation zones in copper alloys as reported by Verfurth and Rapp.7 However, the calculated N(S)Do products depend upon the alloy content of the specimen, so that the internal oxidation of copper alloys does not follow ideal internal oxidation kinetics. As a result, unequivocal values for the N(s) DO product were not obtained by this procedure. A solid-state coulometric titration technique similar to that employed in this work was introduced by C. Wagner8 to study the dependence on silver activity of the Ag/S ratio in silver sulfide in the temperature range of 160" to 300°C. Similar experiments have been carried out by C. Wagner and co-workers9-11 to study the stoichiometry range of silver and copper tellurides, cuprous sulfide, and cuprous selenide. Numerous authors have carried out electrochemical measurements with a solid oxygen-ion-conducting electrolyte to determine the solubility and/or diffusivity of dissolved oxygen in several liquid metals.12-l6 Rickert and Steiner17,18 have used solid-state electrochemical measurements to determine the diffusivity of oxygen in solid silver from 760" to 900°C. Two different cell geometries were used. In the cell of linear geometry Fe, FeO | ZrO2 + (CaO) | Ag + [0 (dissolved)] [1] oxygen diffused from the interior of the silver electrode to the silver/electrolyte interface where the oxygen activity had been lowered from a fixed initial value to practically zero by the application of voltage to the cell. The diffusivity of oxygen in solid silver was determined from the solution of the diffusion equation and the time dependence of the cell current. However, this determination of the diffusion coefficient depended upon a knowledge of the solubility of oxygen in solid silver. A cylindrical geometry was used for the cell Pt, O2(Po2 = 0.21 atm) | ZrO2 + (CaO) | Ag + [0 (dissolved)] [II] which also allowed the diffusivity of oxygen in solid silver to be determined. These values were in agreement with other available data.l9 Recently, Raleigh20,21 used a method involving the measurement of diffusion-limited currents in a cell involving the AgBr solid electrolyte to determine the diffusion coefficient of silver in Ag-Au alloys at 400°C. Diffusivity values on the order of l0-14 sq cm per sec were measured in the alloy composition range 10 to 60 at. pct Ag in a single experiment. From numerous electrical conductivity and galvanic cell measurements,9'22"26 the solid solution Zr0.85 Ca0.15 O1.85 has been established as an electrolyte with predominant oxygen ion conduction over a wide range of intermediate and high oxygen activities. For interrelating the thermodynamics and the kinetics of the dissolution of oxygen in solid copper in this investigation, a galvanic cell was constructed with FeO-Fe3O4 as the reversible reference electrode, the Zr0.85Ca0.15 O1.85 electrolyte, and a pure copper specimen under-saturated in oxygen as the other electrode. THEORETICAL ANALYSIS Three variations of a high-temperature electrochemical technique were used in this study to provide two determinations each of the solubility and diffusivity

Jan 1, 1970

By D. E. Light, J. Y. Somnay

The use of alkyl acid phosphates and their alkali salts as collectors for the uranium minerals brannerite and uranothorite was investigated. In particular a detailed flotation study was carried out using isooctyl acid phosphate as a promoter. Tests were conducted on an Elliot Lake ore analyzing 0.11% U 3 O 8, chiefly as brannerite, and approximately 9% pyrite. Pyrite was floated with conventional reagents; the flotation of brannerite from the sulfide tails was studied to determine the optimum pH and pulp density to employ with isooctyl phosphate. 4 uranium recovery of over 90% was possible with a selectivity index of 8.95 when these tails were floated at 17% solids and a pH of 1.7. The effect of various modifying agents was also investigated. Aluminum sulfate, lactic acid and sodium silicate improved the selectivity of collection yielding selectivity indices of 9.5 to 11.5. Ferric chloride was found to be a depressant for brannerite. A Bancroft ore which analyzed 0.13% U308, and contained uranothorite was also amenable to flotation using isooctyl acid phosphate. The composite uranium concentrate obtained assayed 0.41% U308 at a recovery of 95.3% and a ratio of concentration of 3.24. Previous investigations1,2 on the flotation of brannerite, pitchblende, uraninite and/or uranothorite from various Canadian ores showed that fatty acids, including oleic acid and tall oils, petroleum sulfo-nates and alkyl acid phosphates, were suitable collectors for these uranium minerals. Additional work carried out by the Mines Branch in Ottawa on brannerite ores from the Elliot Lake area3 used the tall oil Acintol FA-1, or FA-2, as a collector. A recovery of 92% of the uranium in a concentrate which contained about 55% of the weight and assayed 0.2% U3O8 was obtained from a feed of 0.1% U308 in this latter instance. Eigeles et a1.4 carried out flotation on pitchblende ores and found that the most promising results were obtained with alkyl acid phosphates and their alkali salts as collectors. Within the homologous series of alkyl phosphates, the best flotation characteristics were displayed by isooctyl phosphates. Further, isooctyl phosphate derivatives were much less sensitive to hardness forming salts than oleic acid, enabling all flotation tests to be made with tap water. This paper describes tests employing alkyl acid phosphates for the flotation of ores containing brannerite and uranothorite. The flotation work described herein was conducted in conjunction with the development of a leaching process for Elliot Lake, Ontario, brannerite ores. In this process pyrite in the ore was concentrated by flotation and roasted, providing sulfur dioxide which was used to produce sulfuric acid in situ in a liquid-solid extraction process. A 40% conversion to sulfuric acid was indicated at a leaching temperature of 80°C; this resulted in the extraction of 93% of the total uranium after a contact period of 6 hr. A rotary kiln was used as a leaching vessel. Preconcentration by flotation was studied in conjunction with the above process to reduce the bulk of solids for leaching and, consequently, capital expenditure. The materials and methods used in this study will be described initially. Then the results will be presented in two sections, the first dealing with the brannerite ore, and the second with the uranothorite. Finally an economic analysis of the results on the brannerite material will be made. MATERIALS AND METHODS The two ore samples examined were from uranium-producing mines. One was a brannerite ore, a uraniferous quartz pebble conglomerate from the Elliot Lake area, which contained 0.11% U3O8, 4.3% S and 4.5% total Fe. Mineralogical studies of similar samples indicated the presence of quartz, microcline, sericite, pyrite and minor quantities of rutile, pyrrho-tite and zircon. The other ore was from a biotite-rich pegmatite in the Bancroft area; feldspar, quartz and biotite formed the major gangue components. Uranothorite was the principal uranium mineral; the head assay was 0.13% U 3 O 8. Preparation of Feed: The ores were crushed to —10

Jan 1, 1963

By W. R. Bendy

GRINDING is a large and costly part of Portland cement manufacture. Prior to clinkering in the rotary kiln, raw materials are ground to a fineness of 80 to 90 pct passing 200 mesh. Then, after burning and cooling, the resulting clinker is ground to about 92 pct passing 325 mesh. In the cement industry the most favored method of grinding has always been by impact and attrition of a ball charge in a rotating mill. Other types of mills, in which materials are ground between die rings and rollers, or between die rings and large balls, are sometimes used for single-stage grinding and often for preliminary grinding followed by grinding in ball-type mills. Their efficiency is usually high, but maintenance and repair costs are high also, and the ball-type mill continues to be the most widely used. Together with 4 pct gypsum to retard setting time, the kiln run clinker—consisting of hard, semi-fused lumps that may have been crushed to — 1/2 in.—is ground to a Blaine surface area of 3000 sq cm per gram and about 92 pct passing 325 mesh. Approximately 32 kw-hr per ton, or 6 kw-hr per 376-1b barrel, are consumed in the grinding mills alone, not counting auxiliaries. Open Circuit Clinker Grinding: Many early clinker grinding plants employed two-stage, open circuit grinding. Comparatively short mills of large diameter, loaded with balls 4 in. and smaller, first reduced the clinker to 95 pct passing 14 mesh. Tube mills of smaller diameter and greater length, loaded with balls 11/4 in. and smaller, carried out the fine grinding operation. An early development was to assemble two or more stages of grinding in a single mill having two, three, or four compartments separated by division heads. There were difficulties in balancing the compartments, but compartment mills were popular in the 1920's because the layout was simple and there were no elevators and conveyors. Oversize Particles: Open circuit mills, whether separate ball and tube mills or compartment mills, always encountered the problem of tramp oversize in the product. A small percentage of clinker survived passage through the first grinding stage as particles—perhaps 1/16 in. diam—that were too large for the smaller balls in the following stages to reduce to —200 mesh. When the feed rate was lowered to reduce tramp oversize, there were serious losses in grinding efficiency. Many ingenious designs were perfected to incorporate perforated screen plates or wire mesh screens in the ball mills or in the first compartments of compartment mills. Their purpose was to prevent mate: rial passing out of the first stage until it was small

Jan 1, 1958

By N. A. Gokcen, J. Chipman

Aluminum and oxygen dissolved in liquid iron were brought into equilibrium with pure alumina crucibles and atmospheres of known H2O and H2 contents to study the reactions: 1—Al2O3(s) = 2 Al + 3 0; 2—Al2o3(s) + 3H2(g) = 2Al+ 3H2o(g); and 3—H2(9) +O = H2O(g). Aluminum strongly reduces the activity coefficient of oxygen and similarly oxygen reduces that of aluminum. Values of the product [% All" • [% O]3 are much smaller than those found in previous experimental studies and are of the order of magnitude of the calculated values. ALUMINUM is the strongest deoxidizer commonly A used in steelmaking, but the extent to which it removes dissolved oxygen has been debatable. The relationship between aluminum and oxygen has not been determined reliably not only on account of the usual experimental difficulties at high temperatures but also because of uncertainties in the analyses of very small concentrations of oxygen and aluminum. The earliest experimental attempt of Herty and coworkers' was followed by a more systematic study of Wentrup and Hieber.' These authors added aluminum to liquid iron of high oxygen content in an induction furnace and considered that 10 min was sufficient to remove the deoxidation products from the melt. Parts of the melts thus obtained were poured into a copper mold and analyzed for total aluminum and oxygen (soluble plus insoluble forms), assuming that the insoluble parts were in solution at the temperatures from which samples were taken. It is conceivable that the furnace atmosphere in their experiments, consisting of mainly air at 20 mm Hg pressure, was a serious source of continuous oxidation and therefore that their oxygen concentrations were correspondingly high. Scattering of their data was explained to be well within the maximum inaccuracy of 10°C in the temperature measurements and errors of ±0.002 pct each in the oxygen and total aluminum analyses. Maximum and minimum deoxidation values, i.e., values of the product [% All' . [% O] differed by factors of 10 to 15; mean values of 9x10-11 and 7.5x10-9 ere reported at 1600" and 1700°C, respectively. Hilty and Craftsv determined the solubility of oxygen in liquid iron containing aluminum, using a rotating induction furnace. Pure alumina crucibles used in their experiments contained the liquid iron which in turn acted as a container for slags of varying compositions consisting mainly of Al2O3, Fe2O3, and FeO. The furnace was continuously flushed with argon, and additions of aluminum and Fe2O3 were made in the course of each experimental heat. The inner surfaces of their alumina crucibles were covered with a substance other than pure Al2O3, containing both iron oxide and alumina. Although frequent slag additions can change the composition of slag in the liquid iron cup formed by rotation, the inner surface of the crucible must depend upon the transfer of oxygen or aluminum through the liquid iron for any adjustment in composition. It is not clear that their metal was in equilibrium with the crucible wall, but it is clear that it was not in equilibrium with Al2O3. Their deoxidation product, [% A].]" • [% O]3, varied by a factor of more than 50; the average values of 2.8x10- and 1.0x10-7 were selected for temperatures of 1600" and 1700°C, respectively. Aside from the experimental determinations, attempts have been made to calculate the deoxidation constant for aluminum indirectly from thermody-namic data. Schenck4 combined the thermodynamic data for Al2O3 and dissolved oxygen in liquid iron by assuming an ideal solution. His calculated values are 2.0x10-15 and 3.2x10-13 at 1600" and 1700°C, respectively. Later, Chipman5 attempted to correct for the deviation from ideality and derived an expression which led to deoxidation values of 2.0x10-14 and 1.1x10-12 at 1600" and 1700°C, respectively. The errors in these treatments originate mainly from inaccuracies of thermal data and uncertainties regarding the activity coefficients of dissolved oxygen and aluminum. The purpose of this investigation was to study the equilibria represented in the following reactions in the presence of pure alumina: Al2O3(s) = 2Al + 3O K = aAl2.ao3 [1] Al2O3(s) + 3H2(g) = 2Al + 3H2O(g) H2O K2 = aAl2(H2O/H2 ) [2] H2(g) +O = H2O(g) K3 = 1/ao (H2) [3] The experimental method consisted of melting pure electrolytic iron, usually with an initial charge of aluminum, in pure dense alumina crucibles under a controlled atmosphere of H,O and H2 and holding

Jan 1, 1954

By K. Osseo-Asare

The DIAGRAM computer program has been used to develop stability diagrams such as Eh-pH, log [CNI-pH, and log [Me]-pH for the systems Me-CN-H 0 where Me = Au, Ag, Fe, Zn, Cu, Ni, Co. More complex 2 diagrams involving sulfur- and arsenic-containing species are also presented. With the aid of these diagrams, a discussion is presented of the solution conditions (e.g. pH, [CN], [CNS], Eh) vhich influence gold and silver extraction in cyanide solutions. Special emphasis is given to the effects of ore minerals or calcination products, such as pyrrhotite, pyrite, arsenopyrite and hematite on gold-silver dissolution. Application of the stability diagrams to solution treatment operations such as cementation is also indicated.

Jan 1, 1984

LIST OF THE MEETINGS OF THE INSTITUTE AND THEIR LOCALITIES FROM ITS ORGANIZATION Transactions Number Place Date Vol Page 1 Wilkes-Barre, Pa May, 1871 1 3 2 Bethlehem, Pa August, 1871 1 10 3 Troy, N Y November, 1871 1 13 4 Philadelphia, Pa February, 1872 1 17 5 New York, N Y May, 1872 1 20 6 Pittsburg, Pa October, 1872 1 25 7 Boston, Mass February, 1873 1 28 8 Philadelphia, Pa May, 1873 2 3 9 Easton, Pa October, 1873 2 7 10 New York, N Y February, 1874 211 11 St Louis, Mo May, 1874 3 3 12 Hazleton, Pa October, 1874 3 8 13 New Haven, Conn February, 1875 3 15 14 Dover, N J May, 1875 4 3 15 Cleveland, 0 October, 1875 4 9 16 Washington, D C February, 1876 4 18 17 Philadelphia, Pat June, 1876, 5 3 18 Philadelphia, Pa October, 1876 5 9 19 New York, N Y February, 1877 5 27 20 Wilkes-Barre, Pa May, 1877 6 3 21 Amenia, N Y October, 1877 6 10

Jan 1, 1917

By AIME AIME

COMMITTEES. LOCAL COMMITTEE.-R. C. Crawford, Chairman; Harrison W. Craver, Secretary; Julian Kennedy, Taylor Allderdice, E. W. Pargny, Charles L. Miller, W. H. Rea, S. A. Taylor, M. E. Wadsworth, W. A1. Henderon, A. C. Dinkey, W. L, Jones, E. L. Messier, George Mesta, J. H. Jones, G. H. Riley, S. L. Goodale, D. W. McNaugher. LADIES' COMMITTEE.-Mrs. Taylor Allderdice, Chairman; Mrs. Julian Kennedy, Mr. R. C. Crawford, Mrs. E. M. Herr, Airs. J. W. Marsh, Mrs. T. A. Mellon, Mrs. G. P. Bassett, Jr., Airs. D. M. Clemson, Mr. Charles L. Miller, Mrs. V. L. P. Shriver, Mrs. W. A. Bostwick, Mrs. A. C.. Dinkey, Mrs. A. P. Childs, Jr., Mrs. F. R. Dravo, Mrs. Hermon Griffin, Mrs. W. H. Nimmick, Mrs. F. H. Lloyd, Mrs. S. G. Cooper, Mrs. S. H. Church, Mrs. E. N. Ohl. The Institute Headquarters was established at the Hotel Schenley, where a bureau of information was maintained for the benefit of the visiting members and guests of the party during the time of the meeting. TECHNICAL SESSIONS. The first session, held Tuesday evening, Mar. 1, 1910, in the large lecture hall of the Carnegie Institute, was called to order by Harrison W. Craver, Secretary of the Local Committee. Mr. Craver introduced Dr. John A. Brashear, who extended to the members and guests a hearty welcome to the city of Pittsburg, to which David W. Brunton, President of the Institute, responded. The following papers were presented in oral abstract by the authors: Biographical Notice of Dr. Charles B. Dudley, by Dr. R. W. Raymond, New York, N. Y. Biographical Notice of William Metcalf, by Col. II. P. Bope, Pittsburg, Pa. Development of Hindered Settling Apparatus, by Robert H. Richards, Boston, Mass. (Illustrated by lantern-slides.) A Few Mining Districts in the Argentine Republic, South America, by Z. S. Beyl. (Illustrated by lantern. slides.)

Apr 1, 1910

By E. C. Burke, W. R. Hibbard

G. B. Craig (University of Toronto, Toronto, O,nt., Canada)—The advent of pyramidal slip at room temperatures in a magnesium crystal (M2,) and the very low value reported for the critical shear stress are puzzling. Table I1 shows the calculated values (approximate) for sin x cos I in this specimen if all the (10l) planes are considered. If So is the shear stress resolved in the direction of glide, on the glide plane, and U, is the stress operative in yield point tests, then: S,, — 325 (0.169) 55gpersqmm (approximately) for 1101: S,, = 325 (0.465) = 151 gpersqmm (approximately) for (0001): S,, — 325 (0.101) - 32.8 gpersqmm (approximately) Thus, we see the pyramidal plane in which the minimum shearing component operated. Barrett"' stated: "Experiments have repeatedly shown that, when there are several crystallographically equivalent slip systems in a crystal, the one having the greatest resolved shear stress will become active. ..." It does not appear to me that the measurements given are conclusive proof that pyramidal slip operated. E. C. Burke and W. R. Hibbard, Jr. (authors' reply) —Although the low value for the critical resolved shear stress for pyramidal slip may be puzzling, there does not appear to be any basis for questioning the validity of the measurements. Under the influence of constraints, slip systems having decidedly lower shearing components may become operative, e.g., "cross-slip" or the "forced glide" in magnesium reported by Bakarian. Since we believe that pyramidal slip occurred in the specimen because basal slip was inhibited, it is not too surprising to find an operative plane with a lower shear stress. -7 C. S. Barrett: Structure of Metals U94jl p. 2J6. New York. McGraw-Hill Book Co.

Jan 1, 1953

By C. R. Wohrman

A MELT of pure electrolytic iron with about 0.4 per cent. sulfur and 7 per cent. manganese was prepared in connection with a study of inclusions in iron. The alloy darkened rapidly when etched with a 10 per cent. alcoholic solution of nitric acid, and microscopic examination revealed the presence of a semimartensitic, semi-Widmanstättian structure (Figs. 1 and 2) closely resembling the structures found by Benedicks in his artificially prepared "meteoric iron." 1 The structures found by Benedicks were readily explained by the presence in his alloy of the two well known iron-nickel solid solutions, taenite and kamacite, and of their eutectoid (?) aggregate, plessite. By analogy, one would infer the existence of similar phases in the iron-manganese alloy just described, such as inference being strengthened by the similarity displayed in many ways by nickel and manganese in their effects on iron. IRON-MANGANESE ALLOTS ARE REGARDED AS HOMOGENEOUS Heterogeneity of iron-manganese alloys has not been recognized heretofore, judging from the data of standard metallographic books and those of original papers. In fact, iron and manganese are quite generally regarded as completely miscible in the solid state. Dr. Rosenhain,2 for example, writes: Alloys of group (a), of which those of gold-silver, iron-manganese, and copper-nickel are examples, when allowed to crystallize sufficiently slowly to attain their condition of final equilibrium, present a microstructure exactly similar to that of a pure metal-the homogeneous character of the molten solution is in that case so completely maintained that the microscope cannot detect the presence of any second constituent.

Jan 1, 1927

'T. C. MERRIMAN, New Haven, Conn. (written discussion *).-This most interesting paper gives much carefully obtained and valuable data. However, there are two points in connection with the commercial application of such data that might possibly be a source of trouble and mis-understanding. In the first place, the examination of thin sections of annealed brass, subjected to standard Brinell test.(500 kg. on a 10-mm. diameter ball) at thicknesses from 0.075 to 0.150 in. (1.9 to 3.8 mm.) indicates that cold work has been performed on the specimen during the application of the load sufficient to extend way through the section, and have the hardness of the metal affected by the backing. If the usual steel support is used, this effect is very evident. If a piece of soft brass is used as a support, there is an indentation in the surface of the support accompanied by a bulge on the under side of the tested specimen opposite the impression made by the 10-mm. ball. The result is that Brinell specifications (governmental or otherwise) on stock for a certain purpose may not be fair in all cases, since manufacturers, owing to differences in equipment, etc., may not all use precisely the thickness and conditions of stock on which the Brinell specifications were based. This would mean that the government Brinell specification might not give them the temper of stock best suited for their manufacturing methods. The concluding paragraph of this paper, stating that "the hardness of cartridge brass may be determined with greater accuracy by the Brinell hardness measurement than by attempting to judge it from the grain size" appears to be in line with the movement of the last year or so among brass manufacturers toward substitution of the Brinell test for microscopic examination as an acceptance test on cartridge brass. The statement may he strictly true that the Brinell test is the best test for hardness, but it is not, as the statement might readily be construed, a sufficient test of suitable condition. For instance, some cartridge brass might accidentally have been overheated to a point where it would be distinctly unsafe to use for the manufacture of small arms cases and then be so rolled (reduction 3 to 5 per cent.) as to pass perfectly proper Brinell specifications. Under such conditions the microscope would reveal its unsuitability where the Brinell test had failed so to do.

Jan 4, 1919

Jan 1, 1957

By J. Rogers, K. L. Sutherland

THE relationships between collector and mineral, activator and mineral, and activator, collector and mineral will be considered herein. We propose to criticize current theories of flotation but we will not repeat the many pertinent arguments presented by Wark and Cox28 in 1937 in which the "chemical" or more strictly the "solubility" theory proposed by Taggart and co-workers22 is shown to be untenable. Recently Taggart, Arbiter and Kellogg24 have studied the long-chain aliphatic amines as collectors and have attempted to resuscitate the solubility theory for these particular collectors. Dean and Ambrose3 have felt that "we stumble over words" when we distinguish different mechanisms of adsorption. Our view is that nothing is more stultifying to the development of a science than attempts to force widely different phenomena into one classification. This oversimplification leads immediately to difficulties in the interpretation of results. EXPERIMENTAL PROCEDURE The response of minerals to activator and collector was determined by "captive-bubble" tests. The methods of preparation of specimens26 and of testing18 have been previously described. Results from captive-bubble tests were confirmed by flotation tests in glass-stoppered cylinders.25 The full lines shown in the figures relating solution composition to contact (flotation) distinguish solutions in which contact (flotation) is possible from those in which it is not. The curve is derived by successive approximation and the accuracy is ±0.2 pH units and ± 5 mg. per liter of collector or depressant. Solution compositions for which it was shown experimentally that contact or flotation is possible are marked by a circle, those for which it is not possible by a cross and those for which it is doubtful by a cross within a circle. It is assumed that at all other solution compositions within (without) the curve, contact or flotation is possible (not possible). After testing in the collector solution, the mineral was removed, washed, and tested by the captive-bubble method in water, or floated in a cylinder with frother only. In this way the composition of solutions in which a mineral was conditioned but in which properties of the collector solution prevented contact or flotation can be defined. The composition of solutions in which conditioning was possible lie between the full and broken curve, the experimental results being indicated on the figures by a square. The curves show the limits of composition of solution in which flotation in a cell would be possible. Many factors other than those considered in these tests determine recovery or grade of a given mineral in practice.

Jan 1, 1947

By A. L. Mular

Two equations express the integral rate at which fines are produced from a homogeneous material: It has been demonstrated that the Gaudin-Meloy distribution for single fracture is equally applicable to multiple fracture and is related to the Gaudin-Schuhmann distribution at least when the distribution modulus a is close to unity. A, xoY was found to be independent of starting mass over the range studied when particle size was held constant. The equations are related to the input energy to the mill. In an earlier paper,' it was shown that when Mo g of uniformly sized homogeneous material is ground dry in a batch rod mill, the energy-size reduction equation is expressed at any time by the mass of unbroken starting material left at time t, ku is the size modulus of the portion Mo - Mt, and P is a constant that is generally equal to the distribution modulus a. If the power to the mill is constant, Et is proportional to time and Eq. 1 is rewritten where (Mo -Mt)/t is actually the integral rate at which fines are produced from a parent material, and A, is another constant. The size modulus, k,, is determined from the Gaudin-Schuhmann equation:2 where y is the cumulative fraction finer than any size x. Recently, Gaudin and Meloy derived a distribution equation for single fracture on the assumption that the random fracture of a homogeneous material produces daughter particles of similar shape. Their equation is given by where y is the cumulative fraction finer than size X, x, is the size of the unfractured parent, and r is designated the size ratio. Although Eq. 4 is derived for a single event, it should also approximately hold for a series of com-

Jan 1, 1962

By J. O. Betterton, W. K. Noyce

I~JTI HE work on the indium-zirconium system is part A of a larger investigation of zirconium-phase diagrams with solute elements, silver, cadmium, indium, tin, and antimony, which is intended to provide information about the metallic valency of zirconium. The system is an ideal example since the sizes of indium and zirconium atoms are nearly the same, and the solute and the solvent occur in the same row of the periodic table. The only solute from Group III B which had previously been added to zirconium was aluminum' and it was of interest to determine whether indium would dissolve appreciably in alpha zirconium and stabilize this phase in the same manner. Experimental Procedure The experimental methods used in the indium-zirconium work are similar to those described earlier for the silver-zirconium system.' Reactor Grade 1 iodide zirconium of 99.95 pct purity* and indium of 99.99 pct purity were arc cast, and then annealed in silica capsules with protective foils of zirconium and molybdenum. Annealing temperatures and times varied from 1 day at 1300°C to 43 days at 550°C. The compositions of the alloys were detcrmined by an individual chemical analysis of the actual metallographic specimens after two or more sides were examined to insure the absence of solute segregation. Calibrated thermocouples were used throughout, and the uncertainty in the temperatures reported, owing to calibration error, furnace control, and measurement of the small temperature gradients near the capsules, is believed to be well within ±2°C. Typical impurities in the alloys were found by a neutron-activation analysis of four different alloys. The results are given in Table I where the ranges of values will be seen to compare favorably with the usual values for iodide zirconium. With respect to oxygen, nitrogen, and carbon the absence of any unusual amount of these elements compared to iodide zirconium was indicated by the alloy hardness values, since hardness is increased sharply by the presence of these elements. The value for 0 pct In, obtained from the alloys by extrapolation, is 58 2 7 VPN which is in the low part3 f the normal range of hardness found in iodide zirconium. Results of the Experiments The zirconium-rich portion of the indium-zirconium phase diagram from the annealing experiments is shown in Fig. 1. Indium was found to

Jan 1, 1959

By R. M. Genevray, M. B. Bever, E. J. Suoninen

THE martensitic transformation in the ß-phase of the Cu-Zn system has been the subject of several investigations. The transformation is known to be reversible and to be affected by stress. Its temperature range has been determined as a function of composition. In the investigation reported here, the effect of tensile stresses on the transformation was investigated quantitatively. Some information was also obtained on the thermoelastic behavior of the martensite formed in the first stages of the transformation. Most of the experiments were done with alloy E of an earlier investigation;' this alloy analyzed 60.49 pct Cu and 39.51 pet Zn by weight. The methods of shaping and heat treatment were also essentially the same as those previously used. The stress was applied to the specimen immersed in a cooling liquid. The transformation was followed by measuring the electrical resistance with a Kelvin bridge and the elongation with a cathetometer. Fig. 1 shows the M, temperature as a function of stress. Resistance and strain measurements gave essentially identical values. The results suggest a roughly linear relation between M. and in the range investigated, up to 12 kg s mm". At higher stresses, plastic deformation begins to interfere seriously with this relationship. The increase of M, with stress is consistent with published work on the effect of stress on the martensitic transformation. The slope of the curve, 4°C per kg mm ", is of the same order of magnitude as the corresponding value calculated for steel.' Fig. 1 also shows the difference, AM, between the temperature of 50 pct transformation on cooling, as measured by changes in length, and that of 50 pct reverse transformation on heating. This difference, which may be considered a measure of the hysteresis, increases with stress; the decrease at highest stresses is probably associated with plastic deformation. Preliminary work using only resistance measurements was done with an alloy containing 60.15 pct Cu and 39.79 pct Zn by weight. The results indicated higher values o-F M, in agreement with the known variation of M. with composition.' The effect of stress on M, (2°C per kg mm-') was of the same order of magnitude as that shown in Fig. 1 for composition E. An increase in hysteresis with stress was also found. The following experiment was made in order to investigate a partially transformed structure. A specimen of alloy E was cooled to — 85°C under a stress of 4.7 kg mm-'. Under these conditions, the martensitic transformation started but did not go to completion. The stress was then released and the specimen cooled to — 105°C. Fig. 2 shows the measured elongation c. The first change in the slope of the curve indicates the beginning of the transformation under stress. Removing the load at —85°C caused a decrease in length to the value corresponding to the elastic elongation of the parent phase resulting from the applied stress. Hence, the marten-site formed in the first part of the experiment apparently disappears completely and without hysteresis upon the release of the stress. The increase in length on further cooling indicates renewed formation of martensite. These conclusions are consistent with the concept of "thermoelastic" martensite," which has been confirmed by test." Acknowledgments The authors are greatly indebted to Professor M. Cohen for his advice and encouragement. They also thank F. Paxton for assistance. Thanks are due the American Brass Co. which supplied the alloys. References E. Kaminsky and G. V. Kurdjumov: Zhur. Tekhn. Fiziki SSSR (1936) 6, p. 984. A. B. Greninger and V. G. Mooradian: Trans. AIME (1938) 128, p. 337. "J. E. Reynolds, Jr. and M. B. Bever: Trans. AIME (1952) 194, p. 1065; Journal of Metals (October 1952). 'A. L. Titchener and M. B. Bever: Trai~s. AIME (1954) 200, p. 303; Journal of Metals (February 1954). " 3. A. Kulin, M. Cohen, and B. L. Averbach: Trans. AIME (1952) 194. p. 661; Journal of Metals (June 1952). "J. K. Pate1 and M. Cohen: Acta Metallurgica (1953) 1, p. 531. 'C. Crussard: Comptes Rendus (1953) 237, p. 1709. ' G. V. Kurdjumov: Zhur. Tekhn. Fiziki SSSR (1948) 18, p. 999. G. V. Kurdjumov and L. G. Khandros: Dokl Akad. Nouk. SSSR (1949) 66. p. 211.

Jan 1, 1957

Jan 1, 1916

[ARIZONA Established July 10, 1915 ROBERT W. HUGHES, Chairman CHARLES R. KUZELL, First Vice-Chairman GILBERT C. DAVIS, Second Vice-Chairman W. CLARK MASON, Secretary-Treasurer Inspiration Cons. Copper Co., Inspiration, Ariz. LYLE BARKER ROBERT HIGH T. G. CHAPMAN P. D. I. HONEYMAN GEORGE M. COLVOCORESSES WALTER C. LAWSON EDWIN H. CRABTREE, JR. W. H. LOERPABEL WALTER I. GARMS ALBERT MENDELSOHN WESLEY P. Goss CARL E. MILLS H. C. HENRIE JOSEPH A. WILLCOX C. F. WILLIS]

Jan 1, 1946