By Edwin B. Johnson

The success of self-fluxed sinter in enhancing the operation of the blast furnace during the past few years has reasonably led to the assumption that the use of self-fluxed pellets might result in even greater furnace efficiencies. A great share of development work in agglomeration has been directed towards techniques related to the production of self-fluxed pellets, but no appreciable tonnage of self-fluxed pellets had been produced on a commercial scale until this past year when The Cleveland-Cliffs Iron Co. produced 35,000 tons of such pellets by the grate kiln system at the Republic mine during the period May 21-June 5, 1962.

Jan 3, 1963

Page Laboratory Methods...........................127 Special Analytical Methods.......................127 Improvements in the Accuracy of the Vacuum-fusion Method for the Determination of Oxygen in Steel....................127 Quantitative Spectrochemical Analysis of Mixtures of Gases.......131 Oxygen Samples from Open-hearth Bath...............133 Rapid Analysis of Sample for Alumina.................139 Accurate Carbon Analyses in Low-carbon Steel.............139 Laboratory Technique for Study of Reactions Involving Liquid Metal. . . . 142 Rotating Liquid Crucibles......................143 Stationary Crucibles.........................145 Jones and Laughlin Experimental Furnace...............148 Vacuum Melting..........................149 Measurement of Temperature of Liquid Iron and Steel;..........149 Pouring and Teeming Temperatures..................149 Bath Temperatures.........................151 Plant Methods.............................154 Methods of Studying Slags.......................154 Sampling Slag in the Open Hearth..................155 Viscosity of Open-hearth Slags....................155 Petrographic Examination of Slag...................156 Statistical Methods Applied to Study and Control of Chemical Relations in Bath...............................166 Rapid Method of -Correlation Applicable to Study of Steelmaking Reactions............................166 INTRODUCTION On Thursday morning, Feb. 16, 1939, a round table discussion was held on the subject of Experimental Methods in the Study of Steelmaking. Dr. John Chipman, Professor of Metallurgy at the Massachusetts Institute of Technology, and chairman of the A.I.M.E. Committee on Physical Chemistry of Steelmaking, presided. In opening the meeting, the chairman said: "The purpose of this round table is to discuss methods of study by which more and better information on the fundamentals of steelmaking can be obtained. It was thought that a round table discussion rather than a symposium would furnish the best opportunity for those actually using various methods of study to get together and discuss their common problems. For this reason attention will be focused upon methods of study rather than upon their results. We want new and current and up-to-date discussion.

Jan 1, 1940

By Russell W. Dayton

The metallurgical polarization microscope has been utilized in several researches in the last few years, thus attaining a fair degree of prominence, but little has been written in a manner suitable to a metallurgist concerning the theory of this instrument. In this investigation the theory was carefully studied, and the results are presented here in a detailed manner, yet as simply as possible. The theory is discussed with particular reference to the three chief functions of the instrument: (1) determination of anisotropy; (2) effect of strain; and (3) identification of inclusions. Each of these is investigated experimentally, with especial attention to the mechanism of producing any effect. Where possible, the discussion is supplemented by photomicrographs. The instrument used had numerous defects as a polarization microscope; these and their remedies are discussed. In the microscopic study of transparent mineral sections (chalcography) the use of polarized light has aided tremendously in the identification of a mineral. The determination of strain in transparent substances (photoelasticity) by the use of polarized light has lately become a commercial process, used in testing finished glass articles. The success of the use of polarized light with opaque materials has not been so great. The magnitude of the effects obtained is much less than that of the corresponding effects with transparent materials, and the mechanical difficulties are much greater. Königsberger,"' i in 1909, was the first to apply polarized light to the microscopic study of opaque substances; Endell and Hanemann(2) were the next, in 1913. In 1919 and 1920, Wright(3,4) prepared two papers on the subject. In the first he developed the detailed mathematical theory from the viewpoint of the electromagnetic theory of light, and in the second described the various methods in use, giving improvements of his own. Schwarz(5)

Jan 1, 1935

By J. N. Maycock, P. W. M. Jacobs

Previous measurements of the thermoelectric power of ionic crystals are reviewed briefly. It is concluded that, while extensive measurerements are available on systems in which the electrode M has a cation in cornon with the sall MX, there is as yet little modern work on systems in which the metal electrode M' does not haue a calion in common with the salt. We haue now measured the thermoelectric power of- single cryslals of KC1 and of KC1 + SrCl2 between plati.nu?n electrodes over a much wider range of temperature than before. individual ionic heats of transport, which, while probably not very accurate, are of a reasonable order of magnitude, are obtained from this data on the basis of an assumption that charge carriers do not cross the electrode/salt interface. RELATIVELY little work has been done on thermal diffusion in ionic crystals. Reinhold and coworkers1-I measured the thermoelectric power and Soret effect in silver and cuprous salts and their mixed crystals. One electrode was kept at constant temperature and electromotive force was measured as a function of the temperature gradient. This is not a satisfactory technique if the results are to be compared with theory; rather should the electromotive force be measured for small temperature differences as a function of the mean temperature of the two electrodes. They used electrodes having the same cation as the salt. Patrick and Lawsons measured the thermoelectric power of AgBr and of AgBr containing 0.25 mole pct CdBr2 using silver electrodes and temperature gradients of 10°C in the temperature range 100° to 400°C. The results were analyzed using the Teltow9 values of the ratio of the mobility of the two types of charge carrier (cation vacancies and interstitials) found from conductance measurements and the wagnerlo estimate of the heterogeneous contribution to the thermopower, Ohet They obtained values of qi = 0.017 ev and q$ = -0.385 ev for the heats of transport of interstitial Ag ions and cation vacancies, respectively. Their data has been reanalyzed by Haga using the corrections to the Wagner formula for ehet given by Howard andLidiard; Haga found ev. Christy et a1.14 have measured the thermopower of AgBr containing 0.01 to 1.0 mole pct CdBr,. They analyzed their results in terms of the theory of Howard and Lidiard and found that excellent agreement with the theory was obtained if q5 + : + hF was set equal to 0.70 ev at 175°C and equal to 0.58 ev at 250°C. Since Teltow's value for hF, the enthalpy of formation of a Frenkel defect pair, is 1.27 ev, this means that qt + q: increases in magnitude from -0.57 ev at 175°C to -0.69 ev at 250°C. This result is in poor agreement with Patrick and Lawson's value of -0.37 ev for pure AgBr (for which the corrections to the Wagner estimate for ehet are very small). christy1' has also reported thermopower measurements for pure silver halides and for the systems he finds that qr + qt for AgBr increases in magnitude from about -0.55 ev at 150°C to about -1.1 ev at 400°C. The temperature dependence of the sum of the heats of transport in AgCl is very similar in magnitude. The sum qi + q cannot be decomposed into the individual interstitial and vacancy heats of transport without a knowledge of the entropy contribution from the change in the lattice vibrational frequencies around the interstitial and vacancy. Despite this it seems an inescapable conclusion from Christy's analysis that and -6 = Q Ag are quite strongly temperature-de pendent and that -q: is much greater in magnitude than the corresponding activation energy for vacancy migration, +0.37 ev. It remains a mystery as to why the data for pure AgBr are fitted so well by the assumption of temperature-independent heats of transport if association of impurity ions and vacancies is neglected.l The values for q$ and q: so obtained are also much more in line with those expected from a simple kinetic interpretation of the heats of transport due to wirtz.17 Christy and Hsueh have also measured the thermopower of CuCl between copper electrodes; 0 for pure CuCl is comparable with that for the silver halides but, owing to the limited solubility of divalent cation impurities it was not found possible to deduce values for the heats of transport. In contrast to these extensive measurements on cells of the type M MX 1 M, there have been relatively few attempts to measure the thermoelectric power of cells of the form M' 1 MX I M'. (We specifically exclude from discussion cells of this type in which the metal electrodes M' are in contact with gas containing a controlled partial pressure of either M or X,, since in these cells the electrochemical reactions are analogous to those of the first type.) The thermoelectric power of Pb12, PbC12, TlC1, TlBr, TlI, NaNO3, and KNO 3 between platinum electrodes was measured by Thie1e.l3 In discussing these measurements Holtan20 asserts that the thermopotential initially fluctuated wildly and even changed sign before approaching a steady value. A high degree of irreproducibility is also evident in the work of Nikitinskaya and Murin21 who first studied the thermopower of NaCl and KC1 between platinum electrodes. Much better reproduci-bility was achieved in our earlier measurements on KC1;22 these were, however, confined to a relatively narrow temperature range and one of the objects of the work reported in this paper was to extend the temperature range of the measurements of the thermoelectric power 8 of KC1. The only other published

Jan 1, 1967

Page Laboratory Methods...........................127 Special Analytical Methods.......................127 Improvements in the Accuracy of the Vacuum-fusion Method for the Determination of Oxygen in Steel....................127 Quantitative Spectrochemical Analysis of Mixtures of Gases.......131 Oxygen Samples from Open-hearth Bath...............133 Rapid Analysis of Sample for Alumina.................139 Accurate Carbon Analyses in Low-carbon Steel.............139 Laboratory Technique for Study of Reactions Involving Liquid Metal. . . . 142 Rotating Liquid Crucibles......................143 Stationary Crucibles.........................145 Jones and Laughlin Experimental Furnace...............148 Vacuum Melting..........................149 Measurement of Temperature of Liquid Iron and Steel;..........149 Pouring and Teeming Temperatures..................149 Bath Temperatures.........................151 Plant Methods.............................154 Methods of Studying Slags.......................154 Sampling Slag in the Open Hearth..................155 Viscosity of Open-hearth Slags....................155 Petrographic Examination of Slag...................156 Statistical Methods Applied to Study and Control of Chemical Relations in Bath...............................166 Rapid Method of -Correlation Applicable to Study of Steelmaking Reactions............................166 INTRODUCTION On Thursday morning, Feb. 16, 1939, a round table discussion was held on the subject of Experimental Methods in the Study of Steelmaking. Dr. John Chipman, Professor of Metallurgy at the Massachusetts Institute of Technology, and chairman of the A.I.M.E. Committee on Physical Chemistry of Steelmaking, presided. In opening the meeting, the chairman said: "The purpose of this round table is to discuss methods of study by which more and better information on the fundamentals of steelmaking can be obtained. It was thought that a round table discussion rather than a symposium would furnish the best opportunity for those actually using various methods of study to get together and discuss their common problems. For this reason attention will be focused upon methods of study rather than upon their results. We want new and current and up-to-date discussion.

Jan 1, 1940

By Russell W. Dayton

The metallurgical polarization microscope has been utilized in several researches in the last few years, thus attaining a fair degree of prominence, but little has been written in a manner suitable to a metallurgist concerning the theory of this instrument. In this investigation the theory was carefully studied, and the results are presented here in a detailed manner, yet as simply as possible. The theory is discussed with particular reference to the three chief functions of the instrument: (1) determination of anisotropy; (2) effect of strain; and (3) identification of inclusions. Each of these is investigated experimentally, with especial attention to the mechanism of producing any effect. Where possible, the discussion is supplemented by photomicrographs. The instrument used had numerous defects as a polarization microscope; these and their remedies are discussed. In the microscopic study of transparent mineral sections (chalcography) the use of polarized light has aided tremendously in the identification of a mineral. The determination of strain in transparent substances (photoelasticity) by the use of polarized light has lately become a commercial process, used in testing finished glass articles. The success of the use of polarized light with opaque materials has not been so great. The magnitude of the effects obtained is much less than that of the corresponding effects with transparent materials, and the mechanical difficulties are much greater. Königsberger,"' i in 1909, was the first to apply polarized light to the microscopic study of opaque substances; Endell and Hanemann(2) were the next, in 1913. In 1919 and 1920, Wright(3,4) prepared two papers on the subject. In the first he developed the detailed mathematical theory from the viewpoint of the electromagnetic theory of light, and in the second described the various methods in use, giving improvements of his own. Schwarz(5)

Jan 1, 1935

By A. A. Dor

Out of nine new major iron ore concentrators put in operation during the last three years, or expected to be commissioned in 1968, seven incorporate primary grinding mills and have a total design capacity of 13,150,000 ltpy of pellets, while only two include conventional rod and ball mill grinding circuits for a total design capacity of about 6,100,000 ltpy (Table I). This evolution in the application of primary grinding to hard, fine grained magnetite ores represents an important development in the technology of mineral processing. It has been the outcome of comprehensive testwork in the laboratory and in pilot plants.

Jan 11, 1968

By W. B. Mather

Arkansas' nonmetalliferous deposits are of many different types. The principal types briefly described in this paper are: clays, shales and slates; silica deposits; limestone and dolomite; barite; gypsum; celestite; nepheline syenite; greensand; phosphate; vermiculite; fuller's earth; bentonite; diamonds; sand and gravel. The future development of these deposits is expected to effect profoundly the industrial development of the state.

Jan 5, 1950

By H. A. Guess

For a number of years I have used for the commercial wet assay of lead generally the ammonium molydate, and occa-sionally the ferrocyanide method. These well-known methods need no detailed description here. In the ore-selling and ore-buying establiahments of the West, 90 per cent. of all wet lead-assays are made by one or the other, and at least nine-tenths of this proportion by the molybdate method. A procedure so well-established must have merit; and, in

Jan 1, 1905

By H. T. Kennedy

The fact that intrusion of water into oil wells can be prevented by treating the sand adjacent to the well seems to have been only recently recognized. Swan1 mentions the process of solidifying naphthalene in strata. R. Van A. Mills2 recommends the use of materials such as sodium silicate and sodium carbonate, which react with oil-field water to form solid plugging agents. When a well is drilled in a new field the oil sands are found essentially devoid of water (Fig. 1). Unless a completely impermeable break exists over wide areas in the field, no water is found above the lower limit of the oil zone and no oil is found below the upper limit of the water zone. After considerable oil has been taken from the well, however, it is almost universal experience that water intrusion occurs. This intrusion may be of two kinds. The water may follow a path parallel to the bedding planes of the producing formation through loose streaks in the pay sand, as shown in Fig. 2, or the water level of the field may rise and enter the well by coning (Fig. 3). Water entering from the side is called "edge water," and that coming in from the bottom is called "bottom water.'' Effectiveness of any method for shutting off water depends not only on the effective treatment of the sand adjacent to the well but on

Jan 1, 1936

By H. P. Allen

The Achotla mill of the Cia. Minera de Penoles is of special interest in that it is one of the few still employing the chloridization process. The ore milled comes from the Suriana mine and consists of both oxide and sulphide, from neither of which can the gold or silver be extracted by a simple cyanide treatment. The mill was built in 1927, after several years of study in the development of the process1, and operated from December of that year until October 1930. Operations were resumed in February 1935, and have been continuous since, treating approximately 5000 tons per month, while the mine is getting up to full tonnage of 6500 tons per month. Transportation of Supplies The property is in Guerrero, Mexico, some 175 km. by airline southwest of Mexico City. The mill site is at Temisco (Fig. I), 8 km. from the Balsas River and 4.8 km. by aerial tram from the mine. At Temisco are the general office, shops, warehouses and laboratory serving both mine and mill. Here sufficient water is available either from a small creek running through the property or from the Balsas River, also convenient and ample storage space for the tailings. With the exception of the mine timber and a few native building materials which may be obtained locally, all supplies for both mine and mill are brought down the Balsas River from Balsas, the terminal of a Mexican National Railway line out of Mexico City. The method of transportation on the river is interesting. Rapids with very fast water are numerous, prohibiting the use of mechanically propelled boats. Those used resemble large, flat-bottomed rowboats some 22 ft. long by 8 ft. wide (Fig. 2). They are manned by two oarsmen sitting in the bow, each handling one large oar, and usually another man in the stern who, with his oar, assists in steering the boat, especially when the rapids are run. From 3 to 7 tons of freight are carried on each boat, depending upon the stage of the water, which governs also the time

Jan 1, 1939

By S.S. Clarke

The sheet-ground deposits of the Tri-State district, because they are fairly uniform in thickness (7 to II ft.)—rather flat, with an easy dip to the west—and cover a large acreage, offered a problem of improved transportation. Heading advance in this kind of mine is very rapid and track haulage requires a larger crew of trackmen than do other mines, and a heavy investment in track. The use of some type of rubber-tired truck equipment for underground haulage was under consideration for some time by the Eagle-Picher Mining and Smelting Co. The nature of some ore bodies made them not adaptable to truck haulage and some mines that did offer possibilities were equipped with other types of haulage, and the expected savings by the use of trucks did not offset the loss of investment that would be incurred in discarding other equipment. The decision was made to sink a new shaft, designed for skip hoisting, on the Blue Goose ore body, and then develop truck equipment. Developing Tractors and Trailers A study was made of internal-combustion engines for power units in the tractors, but the extreme difficulty of controlling air circulation, and the heavy cost of drilling large churn drill holes for blower installations, led to the adoption of a tractor with a storage battery. The storage-battery tractor that was on the market for mine haulage was impossible to obtain because all were needed for defense work. Several standard electric-truck chassis were purchased and rebuilt in the Eagle-Picher shops. The steering wheel was shortened and set vertical, permitting the driver's seat to be moved forward, and the frame was shortened enough to take the battery box and the fifth wheel support that carried the gooseneck of the dump trailer. The fifth wheel, or turntable, is of the ball and socket type. Tig. I shows the ball fastened to the gooseneck. The socket is split to permit introduction of the ball and is held by through-bolts, and the socket is welded to a ½-in. plate, which in turn is attached to the tractor frame. Smaller wheels and tires were put on to reduce over-all height. If it had been necessary, the spring: could have been reversed, or taken off entirely, to gain additional clearance. The tractors are equipped with 48-cell, 23-plate, 400-A.H. batteries. With the initial tonnage and mileage, the batteries were about 50 per cent down at the end of a shift. Tractors have truck tires 7.50 by 20, 8-ply, front and rear, the rear being dud. After four months of use, the .tires are beginning to show signs of failure.* In

Jan 1, 1943

By Raymond Ward

Jan 1, 1945

By Alan Morris

SEASON cracking of brass has received wide attention and there is a wealth of technical literature on the subject. Its causes are fairly well understood and means for its prevention are inexpensive and effective, .so that the frequency of failures from this source has diminished of recent years. But its sister phenomenon, the failure of annealed brass by reason of applied tensile stress plus a certain type of corrosion, has received less attention, though it has been responsible for occasional more or less troublesome cases of cracking of brass in service. The work described in the following pages was undertaken about two years ago to determine the relative resistance of various commercial brass mixtures to stress-corrosion cracking, and to learn something of the controlling factors. By stress-corrosion cracking we mean the cracking of brass free- from internal stresses by reason of applied tensile stress and simultaneous attack by certain corrosive agents. Rogers,1 in discussing a paper by Hatfield and Thirkell, says : "He had also applied a solution of mercuric salt to tensile test pieces of brass whilst they were under stress in the testing machine. At very moderate stresses such test pieces cracked, and very readily broke." Moore, Beckinsale and Mallinson2 subjected test pieces to simultane-us corrosion and tensile stress. In order to determine the minimum stress detectable in brass by the mercurous nitrate test, tensile samples were placed under stress and treated with mercurous nitrate solution. They found that brass stressed below a minimum did not crack.

Jan 1, 1930

By C. F. Nagel

THIS paper is written primarily for those who are familiar with the processes mentioned but who desire a further insight into some of the fundamental principles. It does not give a complete description of the various practices employed in the working of aluminum and its alloys, but presents a few illustrations of the essential respects in which aluminum differs from other common metals, and emphasizes the controlling factors of the processes under consideration. HEAT TREATING Certain aluminum alloys are capable of having their mechanical properties greatly altered by a heat-treatment process. The degree of this improvement may be illustrated by some typical properties of duralumin (Table 1). It is essential that the material be in the wrought condition in order to obtain maximum heat-treatment effects. [ ] In the case of duralumin, the process consists of heating the metal to a prescribed temperature and then quenching it. Immediately after quenching, the material is relatively soft though not as soft as in the annealed state. If allowed to stand at room temperature, the material changes, increasing in hardness and strength without loss of elongation, but at the expense of the plasticity. This action is very rapid at first, gradually diminishing in intensity and to all practical purposes being completed in about four days. This process of hardening is termed

Jan 1, 1928

By H. P. Allen

The Achotla mill of the Cia. Minera de Penoles is of special interest in that it is one of the few still employing the chloridization process. The ore milled comes from the Suriana mine and consists of both oxide and sulphide, from neither of which can the gold or silver be extracted by a simple cyanide treatment. The mill was built in 1927, after several years of study in the development of the process1, and operated from December of that year until October 1930. Operations were resumed in February 1935, and have been continuous since, treating approximately 5000 tons per month, while the mine is getting up to full tonnage of 6500 tons per month. Transportation of Supplies The property is in Guerrero, Mexico, some 175 km. by airline southwest of Mexico City. The mill site is at Temisco (Fig. I), 8 km. from the Balsas River and 4.8 km. by aerial tram from the mine. At Temisco are the general office, shops, warehouses and laboratory serving both mine and mill. Here sufficient water is available either from a small creek running through the property or from the Balsas River, also convenient and ample storage space for the tailings. With the exception of the mine timber and a few native building materials which may be obtained locally, all supplies for both mine and mill are brought down the Balsas River from Balsas, the terminal of a Mexican National Railway line out of Mexico City. The method of transportation on the river is interesting. Rapids with very fast water are numerous, prohibiting the use of mechanically propelled boats. Those used resemble large, flat-bottomed rowboats some 22 ft. long by 8 ft. wide (Fig. 2). They are manned by two oarsmen sitting in the bow, each handling one large oar, and usually another man in the stern who, with his oar, assists in steering the boat, especially when the rapids are run. From 3 to 7 tons of freight are carried on each boat, depending upon the stage of the water, which governs also the time

Jan 1, 1939

By W. B. Coleman

Considerable discussion on the effect of iron and steel scrap in blastfurnace burdens was presented in the January, 1927, issue of Mining and Metallurgy. Therein the question is asked as to what causes the difference in physical properties of pig irons where the chemical analyses are practically the same. This point no doubt has been noticed by a number of furnace operators, but several years ago very little thought was given to it. The foundries purchased pig iron, had it analyzed and found it to be within their specification. The castings made from this iron at times would be satisfactory and at other times hardness and shrinkage would occur. Since the iron was chemically correct the foundries generally were at a loss as to what to do. They changed their method of melting in the cupola and in some cases this corrected the trouble. In some instances the foundry would continue eliminating a brand of iron until the castings produced were satisfactory. Through this process of elimination they would finally arrive at the conclusion that a certain brand of iron was causing the trouble. During the course of this elimination minor changes might have been made in the melting and in the end satisfactory castings were secured without discovering any definite reason for the trouble. Frequently the foundries blamed the manufacturer of the pig iron although the seat of the trouble was in their own method of melting. I have in mind one foundry in particular that was using three brands of pig iron for producing their castings and their losses were rather high. Three entirely new brands of iron were substituted in the charge and still the losses continued. Even after using six brands of pig iron the management felt that the pig iron was the cause. The difficulties encountered in the melting of iron in the cupola, over the past several years, reflect in a great many cases on the operation of the cupola. At different times certain brands of iron were unsuitable for producing a certain class of castings, but at the same time one could see no reason why the iron should be considered abnormal. Irons from furnaces where production and low cost are the main factors that are being used in foundries produce in most cases harder cast-

Jan 1, 1927

By C. G. Rhodes, D. Kramer

High-field critical transport current density (J) measurements at 4.2 °K as a Junction of applied magnetic field (H) were made on samples of cold-rolled and annealed columbium with H parallel to J. Microscopic examination of the samples revealed a well-defined planar fiber structure produced by the cold rolling. J was found to he lower when fibers are parallel to the direction of magnetic field penetration than when they are perpendicular. This effect may he a consequence of the interaction of flux movement with fiber boundaries. THE severe changes in microstructure brought about by cold working superconductors leads to profound changes in their superconducting behavior. In particular, the ability of a superconductor to carry a transport current with zero resistance (the maximum value of this current density will be called "J" in the presence of large external magnetic fields (to be referred to as "H") is greatly influenced by the microstructure. In the case of columbium, LeBlanc and Little1 and Autler et a1.2 have observed an increase in J due to cold work. LeBlanc and Little also observed an anisotropy in J in cold-rolled columbium strips, which Hake et al.3-6 have shown to depend upon the angle between H (H ? J) and the rolling plane. An increase in J due to cold work has been found in a variety of high-field superconducting alloys3'4'7-9 as has the anisotropy effect.10 First explanations of why cold work raised J invoked the idea that dislocations carried the high-field supercurrents,8,11 since cold working drastically increases the dislocation density and presumably the number of supercurrent paths. However, recent ideas on the nature of high-field superconductivity together with new experimental evidence reveal that the bulk of certain superconductors can remain superconducting in high fields while carrying high transport currents. These later developments have been discussed by Berlin-court and Hake12 and a comprehensive review has been prepared by Berlincourt.13 According to the ideas of Gorter14 and Anderson,15 one would expect that the influence of microstructure on high-field supercurrent density will depend on tine interaction between microstructure and penetrating flux and on the direction of the Lorentz

Jan 1, 1965

By George Frederick Kunz

The manifold inconveniences resulting from the absence of a uniform standard of mass for determining the weight of precious stones have long been obvious. This lack has been keenly felt in commercial transactions, and those who have devoted time and research to the study of historic diamonds and precious stones have had frequent occasion to deplore the absence of such a standard in the past. In a paper read in Chicago in 1893, before the International Congress of Weights and Measures, held in connection with the World's Columbian Exposition, the writer suggested dividing the carat into 100 parts, and constituting a standard international carat of 200 mg.; that is, 5 diamond carats or 20 pearl grains to a French gram, making 5,000 carats or 20,000 pearl grains to a ki1ogram. He also called attention to the fact that while this would depreciate the present diamoiid carat or pearl grain only about 2.5 per cent., it would abolish the troublesome discrepancies between the various carat-weights now in use, and could be easily explained and understood everywhere.' The subject of the various diamond carats, their incongruity, and the resulting confusion as to the correct weights of historic gems when definite records of them are searched for, has been fully treated by me in an extensive study of this subject in The Book of the Pearl2 To the earnest and unremitting efforts of C. E. Guillaume, Director of the Bureau Internationale des Poids et Mesures at Sévres, is largely due the eventual success of this eminently desirable reform, which he has constantly urged both by articles on the subject and by addresses delivered in Paris before the International Committee for Weights and Measures.3 The general adoption of a uniform standard for dealings in pre-

Jan 1, 1914