By John Chipman, Carl F. Floe

A year ago the authors published a paper on the solubility of sulphur dioxide in molten copper.l The data in that paper agreed closely with that obtained by previous investigators, which, however, did not agree with the theoretical predictions for solubility of triatomic gases of this type. It has generally been assumed that the reaction of solution is: 6Cu(l) + SO2(g) = Cu2S (in Cu) + 2 Cu2O (in Cu) [I] _ (CU2S)(CU2O)2 K = (Cu)6(Pso2) [2] Neglecting the slight change in copper concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume of gas absorbed, it follows that this volume should be proportional to the cube root of the pressure. It was found that a plot of the volume absorbed versus the cube root of the pressure gave a straight line, but that this line did not pass through the origin. Calculations of the equilibrium constant for the reaction showed that it was fairly constant for pressures above 100 mm. but that actually it approached zero at lower pressures. The conclusion was made therefore that the solubility as determined could not be expressed by Eq. I or by any other simple equation, particularly at low pressures. Other investigators have concluded that the solubility of sulphur dioxide in copper as well as in several copper alloys is more nearly proportional to the square root of the pressure.* Such a conclusion, however, does not satisfactorily account for the results, even when rather complicated mechanisms for the solution are assumed. The highly improbable speculations of Lepp2 and of Schneider and Esch3 based upon hypothetical dissociation pressures of Cu2O and CU2S dissolved in copper illustrate the type of reasoning that has been used to account for the discrepancy. In the discussion of the previous paper, the authors pointed out that the discrepancy might possibly be due to impurities in the copper, although the purest form available was used. Further consideration of the problem suggested that the impurities likely to have the greatest effect on the solubility of so2 in copper were oxygen, sulphur and carbon. Accordingly, further experiments have been made to show the effects of these elements. Experimental Methods The apparatus used for measuring solubility was essentially the same as that shown in the previous paper. However, since it was desired to make measurements at low pressures, a McLeod gauge was added and 6-mm. glass tubing was substituted for the capillary. This increased the "hot volume" considerably but was necessary in order to obtain good vacuums in a reasonable length of time. A mercury diffusion pump was also installed.

Jan 1, 1942

By W. D. Lowry

As most of the industrial activity of Oregon is centered in the Portland area, the foundries there consume the bulk of the foundry sand produced in Oregon. Although a number of the larger towns scattered throughout the state have gray-iron foundries, the sand used by most of them is of local origin. The yearly consumption of foundry sand of all types for the past few war years in Oregon is estimated to have been approximately 40,000 tons valued at about $285,000, of which an estimated 18,000 tons was shipped in from the Ottawa, Ill., district for use largely by the steel foundries. Until 1945 much of the silica sand consumed by the steel foundries in the Pacific Northwest, approximately 50,000 tons in 1944, came from Ottawa, Ill. and surrounding regions. Although some silica sand was shipped in from Belgium in the past, none is known to have been imported in recent years. Early in 1945, a very promising high-grade silica sand being produced near Eugene, Oregon, was introduced, and all but two of the Portland steel foundries are using this new sand. Until a few years ago, the search for good local (Oregon) foundry sands was carried on largely by the foundry supply houses. Recently the Oregon Department of Geology and Mineral Industries has investigated a number of deposits and has carried on and fostered research on the most bromising deposit near Eugene, about 120 miles south of Portland. High-grade silica foundry sand from this deposit is now being marketed in Oregon, Washington, and British Columbia. The Eugene sand is one of the very few outstanding western steel-foundry sands. Field investigations by the Oregon Department show that there are relatively few deposits of sand in Oregon suitable for foundry use. A knowledge of the geology of the state makes this readily understandable. The only major primary sources of the quartz present in sandstones in Oregon are the intrusive masses of granite, granodiorite, and quartz diorite of late Jurassic or early Cretaceous age found in the Siskiyou Mountains of southwestern Oregon, a part of the old Klamath Mountain highland, and in the Blue Mountains of northeastern Oregon. Transportation militates against the development of any possible deposits of foundry sand found east of the Cascade Mountains in central and eastern Oregon because few railroads traverse that area. East of the Cascades, which separate western from eastern Oregon, many of the older sediments of Paleozoic and Mesozoic age have either been metamorphosed or contain much volcanic eruptive material, and even if some of the Mesozoic sediments are highly quartzose in places, they are in relatively inaccessible areas. All the Tertiary sediments there are of continental origin and contain much ash and other volcanic debris, for there was great volcanic activity during much of that period. In western Oregon much the same is true of the Paleozoic and Mesozoic rocks

Jan 1, 1948

By Kenneth C. Vincent, A. M. Gaudin

In a study1 of the action of amyl xan-thate on chalcocite in water suspension, it was found that if the xanthate is added in relatively large quantity the xanthate group can be accounted for in three forms: (1) as xanthate ion remaining in water, (2) as benzene-soluble cuprous xanthate on the chalcocite, (3) as a benzene-insoluble coating on the chalcocite. Reduction in the amount of xanthate added leads to disappearance of form I then of form 2. With minute quantities of added xanthate, substantially all the reagent is of the "unleachable" kind. Yet this unleach-able xanthate can be dissolved by pyridine to form a soluble cuprous xanthate complex, and it is sufficient in effectiveness to make chalcocite flotable even if insufficient in quantity to form a complete mono-molecular film on the mineral. In that study it was also found that chalcocite abstracts cuprous xanthate from benzene so1ution, in what may (or may not) be a case of molecular adsorption. It seemed desirable, therefore, to study further the "unleachable" xanthate on the chalcocite, and particularly to ascertain whether it is formed as a result of the benzene leach or is actually formed during the conditioning of chalcocite in aqueous xanthate solution. A 'splendid tool to make such studies has recently been perfected; that is, the use of radioactive spies or tracer atoms. With this tool, it was thought possible to answer the problem stated above, but, unfortunately, this did not prove to be true. Answer to the flotation question was clouded by the existence of rapid and selective diffusion of copper atoms in the solid mineral—a phenomenon that was totally unexpected yet remains interesting and perhaps important. Method of Radioactive Spies The method of radioactive spies is discussed in many places. Two convenient references are the article by Evans2 and the book by pollard and Davidson.3 The method was first developed by van Hevesy and paneth in 1013, when only natural radioactive isotopes were available. These isotopes are few in number, and so the method remained limited in scope. Recently the synthesis of over 350 active isotopes of all the known stable chemical elements4 has opened widely expanded possibilities for the method, A fundamental tenet of the method is that a radioactive atom and a nonradio-active atom are exactly alike until disintegration of the radioactive atom. Then, by its sudden death, the spy reveals its location. The relative abundance of spies at various locations makes it possible to ascertain the relative abundance of the corresponding nonradioactive atoms at the same times and locations. A second fundamental tenet of the method of radioactive tracers is that the radioactivity lies in the nucleus of the atom: transfer of radioactivity from one

Jan 1, 1947

A discussion at a joint meeting of the New York Section of the American Electrochemical Society and the American Institute of Mining Engineers, Nov. 20, 1913. Chairman Lawrence Addicks:-Our program this evening represents an attempt to set before you the present situation and outlook in the metallurgy of zinc. It is a time-honored custom to throw bricks at the zinc man. The accusation is that he has borrowed a lime kiln and a gas retort and part of a sulphuric acid plant, hitched them together, and spent the last 50 years in regarding with holy veneration the reactions which take place in that retort. The copper man, who thinks of zinc as something with which copper is adulterated to make brass, and the iron man, who regards it as a sort of paint for corrugated sheets, and the lead man, whose opinion as to zinc is not fit for publication, have long felt that, when two or three of the minor details of their respective metallurgies were put in order, they would take a few clays and fix up zinc on a modern basis. But somehow there still seem to be some unsolved problems at home, and while we are waiting it seems only fair that the case for the defense should be adequately presented. There is probably no man in this country to-clay better able to do this than Mr. George C. Stone, of the New Jersey Zinc Co., on whom I have pleasure in calling to talk to us on "Progress in the Metallurgy of Zinc." George C. Stone:-It is frequently stated that there has been no change in the metallurgy of zinc since the first Belgian furnaces were built in the early part of the last century. It is true there have been no such spectacular and radical changes as were worked in the metallurgy of copper and iron by the introduction of converters; but, in the essentials, I believe the progress in zinc metallurgy has been as great as in that of the other common metals. The main reason that there have not been revolutionary changes is that the chemistry of zinc differs radically from that of the other metals and these differences control the type of apparatus that can be used. The differences are: 1. The temperature at which zinc is reduced by carbon is much above the volatilizing point of the metal and it is therefore always produced as a vapor.

Jan 1, 1914

By W. C. Maurer

Although millions of feet of rock are drilled annually, the basic drilling mechanisms involved are not well understood. The primary reason for this lack of knowledge is because the basic principles of rock failure are not well understood and rock failure is the primary mechanism in drilling. A better understanding of the drilling mechanisms would enable a more scientific approach to the design and use of drills and bits. The paper reviews several models which have been proposed to explain various aspects of the different drilling methods. These models are described and their limitations and areas of application are discussed. Drilling rate relationships are developed and related to the basic rock failure mechanisms. TYPES OF MECHANICAL DRILLS There are three basic methods of mechanically attacking rock: 1) percussive action, 2) rotary action, and 3) combined rotary-percussive action. A percussion drill applies a force perpendicular to the rock surface and the bit moves into the rock perpendicular to the surface, forming a crater beneath it (Fig. 1). A rotary drill applies a constant thrust to the bit while a torsional force moves the bit parallel to the rock surface, breaking the rock ahead of it. A rotary-percussive drill applies both a rotary force and a percussive force to the bit which moves into the rock at an angle to the surface. The commonly used drills can be classified as: rotary-drag, diamond; percussive-hammer, piston, churn; and combination-rotary-percussive, roller.

Jan 1, 1967

By John E. Latz

QUICKSAND far below the surface, stopped two attempts by the Potash Co. of America to sink a third shaft to a potash bed that lies 1000 ft below the southern New Mexico desert. Virtually all methods of grouting were employed in the two failures without any indication of consolidation of the flowing sand. Sinking the South Shaft at the Carlsbad potash mine seemed an almost insurmountable task, until freezing was employed as a final resort. This process that proved to be the answer may be defined as "the sinking of a shaft by freezing, consists of the formation, in the water-bearing strata, of a large block of frozen ground in which it is possible to sink a shaft without danger of an influx of water, providing the ice-wall between the water outside and the shaft itself is strong enough to resist the hydrostatic pressure." Freezing Method Used Extensively in Europe Successful frozen ground shaft sinking projects had been completed in Europe, and Russel G. Haworth, resident manager of the Potash Co. of America, went abroad in search of the know-how needed for the New Mexico undertaking. The freezing process, with a history of two failures at the time, was first successfully employed by Poetsch in 1885 at the Houssu Collieries near Haine St. Pierre, Belgium. Poetsch contracted to sink the remaining 64 ft of an uncompleted shaft through water laden strata from a depth of 190 ft to a depth of 254 ft. This work was in progress until 1887. The freezing and sinking consumed more than two years. As a result of early failures, the process was not favorably received until soon after the turn of the century. The accurate prediction of success in a given application was made possible by the concerted effort and study of a group of European engineers. Means of accurate deviation measurement and control were devised, the nature and properties of frozen water laden soil (the ice wall) were investigated, a thorough and rational basis of refrigeration load calculation developed, and concurrently the efficiency and dependability of refrigeration machinery was greatly advanced. Numerous shafts in Germany, Belgium, France, and England today testify to the reliability and economical surety of the freezing method. Applied to the South Shaft, which is circular in cross-section and 15-ft diam, the freezing method consisted of drilling holes 350-ft deep, through the water bearing strata into impervious ground-the freeze hole pattern being concentric with the shaft and 31-ft diam. The holes were cased with pipe closed on the bottom end. Smaller tubes were placed inside these casings and connected to a header supplying chilled brine from a refrigeration plant. The brine descended in the tubing to the bottom of the hole and ascended through the annular space between the two pipes to the top of the casing; flowed into the return header and back to the refrigeration plant. Under these conditions, each of the freeze hole casings became surrounded by a cylinder of ice

Jan 1, 1952

By W. D. Lowry

As most of the industrial activity of Oregon is centered in the Portland area, the foundries there consume the bulk of the foundry sand produced in Oregon. Although a number of the larger towns scattered throughout the state have gray-iron foundries, the sand used by most of them is of local origin. The yearly consumption of foundry sand of all types for the past few war years in Oregon is estimated to have been approximately 40,000 tons valued at about $285,000, of which an estimated 18,000 tons was shipped in from the Ottawa, Ill., district for use largely by the steel foundries. Until 1945 much of the silica sand consumed by the steel foundries in the Pacific Northwest, approximately 50,000 tons in 1944, came from Ottawa, Ill. and surrounding regions. Although some silica sand was shipped in from Belgium in the past, none is known to have been imported in recent years. Early in 1945, a very promising high-grade silica sand being produced near Eugene, Oregon, was introduced, and all but two of the Portland steel foundries are using this new sand. Until a few years ago, the search for good local (Oregon) foundry sands was carried on largely by the foundry supply houses. Recently the Oregon Department of Geology and Mineral Industries has investigated a number of deposits and has carried on and fostered research on the most bromising deposit near Eugene, about 120 miles south of Portland. High-grade silica foundry sand from this deposit is now being marketed in Oregon, Washington, and British Columbia. The Eugene sand is one of the very few outstanding western steel-foundry sands. Field investigations by the Oregon Department show that there are relatively few deposits of sand in Oregon suitable for foundry use. A knowledge of the geology of the state makes this readily understandable. The only major primary sources of the quartz present in sandstones in Oregon are the intrusive masses of granite, granodiorite, and quartz diorite of late Jurassic or early Cretaceous age found in the Siskiyou Mountains of southwestern Oregon, a part of the old Klamath Mountain highland, and in the Blue Mountains of northeastern Oregon. Transportation militates against the development of any possible deposits of foundry sand found east of the Cascade Mountains in central and eastern Oregon because few railroads traverse that area. East of the Cascades, which separate western from eastern Oregon, many of the older sediments of Paleozoic and Mesozoic age have either been metamorphosed or contain much volcanic eruptive material, and even if some of the Mesozoic sediments are highly quartzose in places, they are in relatively inaccessible areas. All the Tertiary sediments there are of continental origin and contain much ash and other volcanic debris, for there was great volcanic activity during much of that period. In western Oregon much the same is true of the Paleozoic and Mesozoic rocks

Jan 1, 1948

By Carl F. Floe, John Chipman

A year ago the authors published a paper on the solubility of sulphur dioxide in molten copper.l The data in that paper agreed closely with that obtained by previous investigators, which, however, did not agree with the theoretical predictions for solubility of triatomic gases of this type. It has generally been assumed that the reaction of solution is: 6Cu(l) + SO2(g) = Cu2S (in Cu) + 2 Cu2O (in Cu) [I] _ (CU2S)(CU2O)2 K = (Cu)6(Pso2) [2] Neglecting the slight change in copper concentration and considering that the concentrations of sulphur and oxygen are both proportional to the volume of gas absorbed, it follows that this volume should be proportional to the cube root of the pressure. It was found that a plot of the volume absorbed versus the cube root of the pressure gave a straight line, but that this line did not pass through the origin. Calculations of the equilibrium constant for the reaction showed that it was fairly constant for pressures above 100 mm. but that actually it approached zero at lower pressures. The conclusion was made therefore that the solubility as determined could not be expressed by Eq. I or by any other simple equation, particularly at low pressures. Other investigators have concluded that the solubility of sulphur dioxide in copper as well as in several copper alloys is more nearly proportional to the square root of the pressure.* Such a conclusion, however, does not satisfactorily account for the results, even when rather complicated mechanisms for the solution are assumed. The highly improbable speculations of Lepp2 and of Schneider and Esch3 based upon hypothetical dissociation pressures of Cu2O and CU2S dissolved in copper illustrate the type of reasoning that has been used to account for the discrepancy. In the discussion of the previous paper, the authors pointed out that the discrepancy might possibly be due to impurities in the copper, although the purest form available was used. Further consideration of the problem suggested that the impurities likely to have the greatest effect on the solubility of so2 in copper were oxygen, sulphur and carbon. Accordingly, further experiments have been made to show the effects of these elements. Experimental Methods The apparatus used for measuring solubility was essentially the same as that shown in the previous paper. However, since it was desired to make measurements at low pressures, a McLeod gauge was added and 6-mm. glass tubing was substituted for the capillary. This increased the "hot volume" considerably but was necessary in order to obtain good vacuums in a reasonable length of time. A mercury diffusion pump was also installed.

Jan 1, 1942

By J. A. Collins

THE process of plastic extension of face-centered cubic single crystal-line rods is so well understood, since the notable studies of Taylor and Elam,1 that the change in orientation of any crystal by slip and rotation may be predicted from the measured elongation. It is customary to assume a very homogeneous deformation, wherein gliding lamellae are free to rotate so that their slip direction continually approaches the axis of the rod, until a second slip system comes into operation; whereupon conjugate slip proceeds quantitatively to an end adjustment with the [112] direction in the axis of the rod. This process has been checked in many face-centered cubic materials and readily permits the preparation of specimens that have been sub-jected to various determinable amounts of shearing action. It is clearly of interest to study in such measurably strained specimens the development of a recrystallized structure on annealing and if possible detect the source of nuclei from which the new crystals grow. Strain-annealing experiments of this character have been performed by others but not in detail sufficient to permit a study, for example, of the number of recrystallized grains vs, the amount of shear. In the experiments now reported, this was done with a wide variety of orientations covering nearly the entire range of slip on a single system and corresponding to amounts of shear (ratio of shearing distance to distance between lamellae) at the conclusion of a test of from 0.08 to 0.57. A particular point was made of determining the crystallite rotation, or small angular range assumed by the octahedral slip plane after these various amounts of shear. The mechanism of recrystallization and the magnitude and effect of recovery on the recrystallization process was investigated.

Jan 1, 1940

By Arthur E. Bousu, C. T. Eddy, L. W. Eastwood

The recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received considerable attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coalescence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presentcd in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are untenable. A paper on the theory of recrystallization, with additional data, will be completed in the near future by the writers. Since the literature on the subject has been adequately and frequently reviewed, the only referenccs to it in this paper will be those necessary in the discussion of the data presented.

Jan 1, 1935

By B. F. Fackenthall

The Durham Iron Works of Messrs. Cooper & Hewitt, near Riegelsville, Pa., occupy a site which has been almost continuously the scene of iron-manufacturing industry since 1727. Doubtless if Anthony Morris and his thirteen associates, who in that year erected a blast-furnace on the Durham Creek, a short distance above where the Durham Iron Works now stands, could have had a vision of the improved and enlarged apparatus of their successors, they would have been not less astonished by the huge stack, the hot-blast ovens, and the blowing-engines of the modern blast-furnace, than by the railroad which now follows the bank of the river on which their clumsy " Durham boats " once floated pig-iron to Philadelphia. In one particular, posterity must confess their snperiority. We are told that in November, 1728, they shipped three tons of Durham iron to England. The proprietors of the Durham Iron Works are not now shipping iron to England. The present Durham furnace was built (in place of two smaller ones) in 1874 and 1875, and made its first blast in 1876. A description of it, with other works of the same proprietors, at Trenton, N. J., by A. L. Holley and Lenox Smith, was published in London Engineering for January 31st, and February 21st, 1879. Since that time, a number of improvements, dictated by experience, have been made in the details of the furnace and fittings; and the recent roilclusion of a long and successful blast presents a convenient opportunity for a description of the works and a statement of the results of practice. The accompanying drawings will show the general arrangement of the works. The furnace, Plate I., Figs. 1 and 2, is 75 feet high by 19 feet bosh. The hearth is 11 feet 4 inches in diameter, with seven tuyeres 5 feet 6 inches above hearth-line. The tuyeres project 9 inches into the furnace, making the interior tuyere-circle 9 feet 10 inches in diameter. The front is a modification of Luermaun's

Jan 1, 1886

By Ingvar Janelid

13.7-1. General. Iron ore mining in western Europe is mostly carried out underground and only a minor part is mined by open pit methods. Actual open pits of importance in this connection are, among others, Svappavaara in Sweden, Mo i Rana and Sydvaranger in Norway, Corby Mines, Colsterworth, and Scunthorpe in Great Britain, and in western Africa, Nimba and Bong Range in Liberia, and Kedia d’Idjil in Mauritania. The open pit mines of western Africa are of great interest in this connection as they are designed according to European practice and have accepted the same techniques, methods, equipment, etc. as the European mines. In the surface mining of limestone, granite, shale, etc., the technical conditions generally are similar with those in the iron ore mines. Some information will therefore be submitted from typical quarries. The geological conditions at the various iron ore mines and limestone and other quarries vary extensively. In Scandinavia the iron ores occur exclusively in Precambrian rocks. The ore is hard, mostly magnetite or hematite, folded and steep dipping, and hence accessible to surface mining only in the shallow sections. In the mines referred to, open pit mining will last for another 10 to 30 years, whereupon mining has to be continued by underground methods. In France the Minette iron ore has previously been mined in open pits but, because of increased overburden, mining underground with room and pillar methods now dominates. The iron ores are Jurassic, flatlying strata of oolitic type, containing chamosite, siderite, and brown hematite. The British iron ores are mostly of the same origin and appearance as the French deposits, but despite heavy overburden they are preferably mined from the surface. In western Africa, the iron ores are of the same type as in Brazil, i.e., itabirites with high-grade portions resulting from silica-leaching and weathering. The ore contains mostly brown and blue hematite and magnetite. Nimba and Kedia d’Idjil are very similar regarding ore quality and geology. Bong Range is a deposit of low-grade ore which has to be concentrated.

Jan 1, 1968

By J. L. Wyatt

The electrical resistance of titanium as a function of purity and temperature was measured from —325" to 2800°F. Two points of inflection in the data plots were found, and an increase in resistance with increase in temperature above the transformation was observed. IN 1948 Greiner and Ellis' reported on the thermal and electrical properties of titanium, including a study of the effect of temperature on the electrical resistance. The materials used in the research were obtained from the United States Bureau of Mines, where powder metallurgy techniques were being employed for consolidation purposes. These authors found a decreasing resistance with increasing temperature above 1625°F, and concluded that the latter temperature represented the point of transformation from hexagonal close-packed to body-centered cubic structure on heating. They reported a specific resistivity value of 55x10-6 ohm-cm, and showed that dp/dt was positive, decreasing with increasing temperature above ambient. In one of his early texts Hume-Rothery2 mentioned that certain metals, including titanium, exhibited minima in plots of resistance vs temperature. He indicated that this occurred at 212°F. Reporting many years ago on the effect of temperature on the electrical resistance of zirconium, de Boer and Fast³ showed that phase transformation in this sister metal occurred over a range of temperatures, the extent varying with its purity. Graphs of resistance vs temperature, showing transformation effects over a range of several hundred degrees, were presented for relatively impure metal. In the latter case the resistance decreased with increasing temperature throughout the region of partial phase transformation, thereafter increasing as predicted for normal metals by modern theories of the solid state. Since the quality of metal used in previous studies was substandard compared with iodide-type titanium, and in view of the fact that there seemed to be some rather unusual observations in the reported literature, it was decided to undertake a more extensive study of the thermal effects using high purity titanium, and to include temperature ranges beyond those which had been studied in order to ascertain whether or not the characteristics of zirconium would be duplicated. Experimental Materials Materials used in this investigation included commercial quality titanium (Ti-75A produced by the Titanium Metals Corp. of America) in the form of ¼ in. diam rods, and high purity iodide titanium (produced by the Foote Mineral Co.) in the form of crystal bar of irregular size. The latter was cold-swaged into rod form and machined to the desired size. Lead wires to all specimens consisted of 18 gage Ti-75A. Chemical analyses of the stock materials are given in Table I. Experimental Procedures Specimens 2½ to 3 in. in length were prepared with diameters nominally 0.15 to 0.20 in. Two holes,

Jan 1, 1954

By Kenneth C. Vincent, A. M. Gaudin

In a study1 of the action of amyl xan-thate on chalcocite in water suspension, it was found that if the xanthate is added in relatively large quantity the xanthate group can be accounted for in three forms: (1) as xanthate ion remaining in water, (2) as benzene-soluble cuprous xanthate on the chalcocite, (3) as a benzene-insoluble coating on the chalcocite. Reduction in the amount of xanthate added leads to disappearance of form I then of form 2. With minute quantities of added xanthate, substantially all the reagent is of the "unleachable" kind. Yet this unleach-able xanthate can be dissolved by pyridine to form a soluble cuprous xanthate complex, and it is sufficient in effectiveness to make chalcocite flotable even if insufficient in quantity to form a complete mono-molecular film on the mineral. In that study it was also found that chalcocite abstracts cuprous xanthate from benzene so1ution, in what may (or may not) be a case of molecular adsorption. It seemed desirable, therefore, to study further the "unleachable" xanthate on the chalcocite, and particularly to ascertain whether it is formed as a result of the benzene leach or is actually formed during the conditioning of chalcocite in aqueous xanthate solution. A 'splendid tool to make such studies has recently been perfected; that is, the use of radioactive spies or tracer atoms. With this tool, it was thought possible to answer the problem stated above, but, unfortunately, this did not prove to be true. Answer to the flotation question was clouded by the existence of rapid and selective diffusion of copper atoms in the solid mineral—a phenomenon that was totally unexpected yet remains interesting and perhaps important. Method of Radioactive Spies The method of radioactive spies is discussed in many places. Two convenient references are the article by Evans2 and the book by pollard and Davidson.3 The method was first developed by van Hevesy and paneth in 1013, when only natural radioactive isotopes were available. These isotopes are few in number, and so the method remained limited in scope. Recently the synthesis of over 350 active isotopes of all the known stable chemical elements4 has opened widely expanded possibilities for the method, A fundamental tenet of the method is that a radioactive atom and a nonradio-active atom are exactly alike until disintegration of the radioactive atom. Then, by its sudden death, the spy reveals its location. The relative abundance of spies at various locations makes it possible to ascertain the relative abundance of the corresponding nonradioactive atoms at the same times and locations. A second fundamental tenet of the method of radioactive tracers is that the radioactivity lies in the nucleus of the atom: transfer of radioactivity from one

Jan 1, 1947

Jan 1, 1947

By G. S. Cole, G. F. Bolling

A series of Al-Cu alloys has been cast from constant superheat to solidify either with a hot top or with a free liquid/air interface. All the other variables which affect relative fluid motions were kept constant except the imposition of slow rotations m oscillations of the mold. Depending upon the exact circumstances, evi-dence could be found for the nucleation of equiaxed grains from dendrite bits detached from the columnar zone, or from the free surface, or from solid bits induced at pouring; a special experiment showed the solute buildup during ingot solidification and by inference the reality of constitutional supercooling. All methods of grain nucleation are thus supported. When solidification is arranged in a static mold the columnar- to-equiaxed transition occurs by one of these nucleation paths, subject to the natural decay of temperature gradients which promotes nucleation or the survival of nuclei. But when solidification is forced under special fluid flows it may display odd transitions. In one of these the equiaxed zone is synihesized from. dendrite bits detached from the solid/liquid interface. These survive under the concurrent lowering of temperature gradients and eventually cause transition by impeding columnar growth. GRAIN structure control is desired because real experience shows that specific properties are associated with specific cast grain structures. But since control is thus a matter of need and does not require understanding, much of casting remains art. For example, the manipulation of relative fluid motions in simple ingots provides a control of grain structure development,1-4 but theoretical insight is not required in order to broaden its potential applicability. Fortunately, however, once a variable like fluid flow is recognized it can also provide paths toward new insight. New observations using this variable have provided an insight which is curious. All the theories or descriptions of the columnar-to-equiaxed transition (CET) seem to be supported as long as the appropriate experiment is carried out. In order to develop this idea, let us ignore segregation, the chill zone (until a later section of this paper), and the origin and development of the columnar zone.= The details of questioning how equiaxed material forms in a casting may be divided in two. The first part is simply a questioning of the origin for equi-axed grains: are there fresh nuclei from heterogeneous nucleation, or dendrite bits broken off or melted from the columnar zone or elsewhere,6 or other solid bits surviving from the outset of freezing? The second is more complex, a questioning of the CET: does columnar growth slow down and allow the dominance of equiaxed grains, however they are formed, or do equi-axed grains take over and force columnar growth to stop? This "chicken-or-the-egg" second question can be quite useful, especially because it allows us to delineate the ordinary or NATURAL EQUIAXED ZONE and the induced or SYNTHETIC EQUIAXED ZONE. A natural equiaxed zone occurs if solidification proceeds in the absence of disturbances or extraneous forces such as ultrasonics, stirrings, and so forth. Both the CET theory proposed by Winegard and Chal-mers, 7requiring constitutional supercooling, and the CET theory suggested by Chalmers,8 requiring nuclea-tion only on pouring, pertain to the natural equiaxed zone. The best collating evidence to date for both these theories is contained in the work by Biloni and Chal-mers;9,10 the former theory7 is supported by special versions of the unidirectional growth experiment performed by Plaskett and winegardl1 and the latter theory' is supported in detail for the solidification of small ingots. An equiaxed zone can be synthesized when disturbances caused by forced fluid flows2-4 or other artificial means9,10 break off or melt off dendrite tips from an advancing solid/liquid interface,* if (and only if) temperature gradients in the melt are (forcibly) reduced enough to ensure the survival of these bits of dendrites, 2'3 Willful disturbances even so trivial as those produced by rapping a mold might be included here; as will be shown for example, this follows Southin's suggestion that the free liquid/air interface

Jan 1, 1970

By Shiou-Chuan Sun

THE fact that coals of different ranks and even of the same rank differ greatly in their amenability to iroth flotation is well known. In recognition of the need for an explanation of this phenomenon, two hypotheses have been suggested. Wilkinsl reported that the floatability of coals increased with an increase of the carbon content or rank. This postulate is handicapped by the fact that bituminous coals that possess moderate carbon contents are actually more floatable than anthracite coals that have high carbon contents, as shown in columns 6 and 9 of Table I. Taggart and his associates' implied that the difference of floatability between bituminous and anthracite coal was caused by the variation of carbon-hydrogen ratio. This is not applicable to the relative floatability of other coals and carbons. For example, column 11 of Table I shows that the carbon-hydrogen ratios of low-floating lignitic coal and non-floating animal charcoal are not only smaller than the moderate-floating anthracite coal, but are also similar to the high-floating bituminous coal. Furthermore, according to this hypothesis, high temperature coke-A (464), Ceylon graphite (1238), and lamp-black (357), all possessing extremely high carbon-hydrogen ratios, should be less floatable than other substances having much lower carbon-hydrogen ratios such as high volatile-B bituminous coal (11.9 to 22), anthracite coal (35.7 to 60.5), lignitic coal (15.6 to 33.6), and charcoal (13 to 26.2). However the former group is actually more floatable than the latter group. In this paper, a surface components hypothesis is Proposed to explain the different floatabilities of coals, carbons, and hydrocarbon minerals. The validity of the hypothesis is experimentally supported by the actual floatability, natural floatability, wettability, and adsorbability for neutral oils of coals, carbons, and hydrocarbon minerals tested. The combustible recovery of the flotation results, as used in this paper. was calculated from Eq. 1: P (100-Ep) 100 RWCP Rc= [1] F (100-E,) C, where R, is the percent combustible recovery; F and P are, respectively, the weight of feed and the weight of concentrate or product; E, and Ep are, respectively, the total percent of ash plus moisture in feed and in concentrate; Ru. is the percent weight recovery: and C, and C, are, respectively, the percent of combustible in feed and in concentrate. Except for ash and moisture content, all chemical components of a coal are assumed combustible. The experimental work included studies on flotation, ultimate and proximate analyses, contact angle tests, extractions of bitumen-A with benzene, adsorptions for liquid hydrocarbons, and wetting tests. Most of the flotation experiments were performed in a laboratory Fagergren machine; others were tested in a small Denver machine. The solid feed for the former was 300 g and for the latter was 30 g. The solid materials used for flotation were crushed to —48 mesh. After the mineral pulp in the flotation cell was agitated for 6 min and the pH was adjusted to 7.5 & 0.2 with sodium hydroxide or hydrochloric acid, a petroleum light oil having a viscosity of 5.73 centipoises at 77 °F was added and conditioned for 2 min. Finally, pine oil was introduced and the froth was collected for exactly 3 min. The weight ratio of petroleum light oil to pine oil was kept constant at 1.5 to 1. Tap water was used for all flotation tests. Contact angles were measured with a captive bubble machine. For each coal sample, three specimens were mounted in transoptic mounts and polished with levigated alumina, first on a sheet glass, then on a cloth-covered metal polishing wheel. The polished specimen was first washed with distilled water and wiped thoroughly on a cleaned linen pad, then transferred into the pyrex cell of the captive bubble machine and conditioned for 6 min., and finally measured for contact angles at three or more points. Except where otherwise stated, the induction time for each measurement was 1 min. The contact angle representing each material was obtained by averaging the measurements of three specimens. The linen pad was first washed with warm distilled water, then boiled 30 min in a 2N sodium hydroxide solution, and finally washed with distilled water until no trace of sodium hydroxide could be detected in the decanted solution. The cleaned linen pad was stored under distilled water. Immediately before using, the pad was rewashed and transferred into a clean pyrex petri dish partly filled with distilled water. The glassware and rubber gloves used were cleaned by soaking in sulphuric acid-potassium dichromate cleaning solution, followed by rinsing with distilled water. The polished specimens were handled only by glass forceps. The ultimate and proximate analyses were made in accordance with the ASTM standard procedures for coal and coke. The extractable bitumen-A was determined by weighing 1 g of —100 mesh sample and placing it in a desiccated and weighed ASTM aluminum-extraction thimble. The thimble was placed in condenser hooks and inserted into an extraction flask containing 100 cu cm of benzene. The flask was heated and the benzene vapor was condensed by water coils. At the end of 24 hr of percolation, the thimble was removed, desiccated, and weighed. Loss in weight of sample was taken as bitumen-A and calculated to dry and ash-free basis.

Jan 1, 1955

By J. D. Livingston, H. E. Cline

The lamellar-dendritic transition in Sn-Pb alloys near the eutectic composition has been studied at high growth rates. Lamellar structures were found over a substantial range of tin-rich compositions, and this range extended to increasingly tin-rich concentrations as growth rate increased. These results are discussed in terms of stability and competitive-growth arguments. Various experimental and structural limitations to the rate of directional solidification are discussed. The rate of heat removal at the heat sink is the major experimental limitation. ReCENT interet1,2 in the use of fine composite structures produced by directional solidification of eutectic alloys makes it important to determine the range of composition and growth conditions that yield such microstructures. Because increasing growth velocities produce increasingly finer microstructures, it is particularly significant to determine the factors limiting the rate of solidification. Mollard and Flemings3 have shown that composite structures, free of primary dendrites, can be obtained in Sn-Pb alloys of off-eutectic composition. The composition range of composite structures was found to increase with increasing values of G/V, where G is the temperature gradient and V is the growth velocity. These results are in good quantitative agreement with an analysis of the stability of a planar eutectic interface.4 This analysis specifically predicts that over a small range of compositions stable lamellar structures will be obtained even for G/V = 0, hence, even at very high growth rates. The lamellar-dendritic transition in Sn-Pb alloys has also been analyzed with a model based on competitive growth between dendrites and the composite structure.576 This treatment, based on earlier work on organic eutetics,7 predicts that the composition range yielding composite structures in Sn-Pb will increase rapidly at high growth rates. An increase in the composition range of composite structures at high growth rates was recently observed in Cu-Pb alloys near the monotectic composition.8 In view of these results, and the predictions of the stability and competitivegrowth analyses, it was decided to study the lamellar-dendritic transition in Sn-Pb alloys at high growth rates. EXPERIMENTAL Using 99.999 pct pure materials, a series of Sn-Pb alloys were prepared containing 16.8 at. pct to 27.6 at. pct lead. (Eutectic composition is 26.1 at. pct Pb.) Ingots were extruded to 0.175 in. rod, and some rod was drawn to 0.070-in. wire. Directional solidification was accomplished in two different ways, Fig. 1. For growth rates up to 2 x 10-1 cm per sec, a 0.175 in. diam sample was placed in a graphite crucible 5 in. long with 0.250 in. OD and 0.035 in. walls. Samples were melted under flowing argon in a vertical, platinum-wound furnace, and solidified by driving the crucible downwards through a \ in. hole in a water-cooled copper toroid, Fig. l(a). An insulated chromel-alumel thermocouple was imbedded in the center of a representative sample, and moved with the sample during solidification. The local temperature is plotted against the distance travelled by the sample in Fig. 2. As the growth rate increased, the solid-liquid interface moved closer to the water-cooled toroid and the temperature gradient increased. At growth rates above 10-1' cm per sec, heat was not removed fast enough and the sample moved into the toroid in the liquid state. The curve for V = 2 x 10-1 cm per sec shows a plateau caused by incomplete removal of latent heat from the interface, a problem which will be discussed later. To improve the heat removal, the toroid was cooled by nitrogen gas precooled in liquid nitrogen. This allowed successful solidification at rates up to 2 x 10-1cm per sec. Higher solidification rates required still more effective heat removal. Samples 0.070 in. in diam were placed in graphite tubes 0.125 in. in diam with 0.020 in. walls. Instead of cooling by sliding contact with a cooled toroid, these thinner samples were sprayed or directly immersed into water, Fig. l(b). After solidification, samples were stored in liquid nitrogen until they could be examined metallographic-ally. The surface was prepared with a diamond-knife microtome, followed by a light etch. The presence or absence of tin dendrites, Fig. 3, or lead dendrites, Fig. 4, was noted by optical microscopy, usually of a transverse section near the center of the sample. Replicas of the surface were prepared and examined in an electron microscope to resolve the fine lamellar structures, Fig. 5. The structures observed at various compositions and growth rates are summarized in Fig. 6. Composite structures were observed at increasingly cin-rich compositions as growth rate increased. This transition from dendritic to composite structure with increasing growth rate was also demonstrated by solidifying half a sample at a slow rate and then suddenly increasing the growth rate by lifting the furnace and quenching the sample with a water spray. A longitudinal section of this sample, Fig. 7, shows that the tin dendrites, which extended ahead of the slow-moving composite interface, were bypassed by the composite when the growth rate was increased. The range of composite structures at high growth rates was limited by the appearance of primary lead dendrites on the tin-rich side of the eutectic composition. Observation of representative longitudinal

Jan 1, 1970

By A. J. Hendron, D. U. Deere, F. D. Patton, E. J. Cording

In the design of structures founded in the near-surface rock, a distinction may be made between those problems that are related to the strength of the rock mass, and those that are related primarily to the compressibility of the rock mass. The mining engineer deals almost exclusively with problems involving strength in the design of open-pit slopes and underground openings. The civil engineer is similarly concerned with strength problems in the design of vehicular and water tunnels; underground power plants; cut slopes in rock for highways, canals, and spillways; and in the study of the sliding resistance of the foundations of gravity dams and the abutments of arch dams. Moreover, the civil engineer encounters problems in which the compressibility of the rock becomes the key element in the design. These problems include settlement of heavy structures supported on rock, deformation of the abutments of arch dams, and deflection of pressure tunnel linings. The design problems listed above are still solved largely on the basis of experience and rule-of-thumb. However, recent developments in rock mechanics give promise of providing more realistic approaches to certain aspects of the design. This paper, presents some of the more important recent developments which contribute to an understanding of rock behavior and which aid in design of rock structures. Typically, four steps are involved in the design of a structure, whether it be a machine element, a structural member of a building, or a structure in rock. These steps are listed below:

Jan 1, 1967

By AIME AIME

AS director of Battelle Memorial Institute and as Chairman of the important O.P.M. advisory committee on metals and minerals, Clyde E. Williams numbers his acquaintances in the mineral industries by the thousands and h because his principal hobby is liking human beings, most of his acquaintancs are also his friends. Clyde is one of the many outstanding metallurgist, in the United States who started as a chemist. After graduating from the University of Utah in 1915 he was successively chemist for U.S. Smelting Refining and Mining Co., and at the Bureau of Mines station at Ithaca, N.Y. He then got into, metallurgical work and in 1920 he was appointed superintendent of the Northwest Station of the Bureau of Mines at, Seattle. Subsequently he was assistant to H. Foster Bain in metallugical work for the

Jan 1, 1942