By L. L. Brundred

The major portion of the production of the Gulf Coast area, represented by South Texas and South Louisiana, comes from the flanks of well-defined salt domes. This oil, containing an excellent lubricating stock, ranges from 17° to 28° Be. gravity. Some lighter oil is encountered but the life of such fields is, in general, an open question. In fact, there are few light-gravity fields which have proved of much value. In all of the fields water encroachment, or, more properly, water produced with the oil, is a vital factor. After the first head of high-pressure gas is removed, ever-increasing percentages of water appear, and naturally the life of the wells is materially affected thereby. The sands are, as a rule, extremely fine, very soft, and must be carefully excluded from the hole by the use of fine screen to prevent sanding up. All sands are tipped at such extreme angles as to make coring essential for the location of water strata, oil-bearing sands and important shale. beds. Even with modern coring, the correlation of logs is a difficult problem. Due to the fact that the bulk of the oil is refined for its lubricating properties, little attention has been paid to losses by evaporation in the field. This is largely influenced by the fact that the major companies have set a price schedule, showing but two grades, "A" and "B." The average oil company, therefore, does not attempt to use the gas-lift but relies primarily on the air-lift and then only on wells considered to be particularly adapted to its use, namely those capable of producing large quantities of fluid and yet not having sufficient "kick" to flow. Furthermore, as the gas contained in the reservoirs is mostly ricthane such gas being very quickly vaporized and produced in large quantity in the early life of the fields, there is little gas left after the first flush flowing period of the wells. In fact, it is very generally conceded that gas is a precarious fuel to depend on in any of the coastal fields. This situation largely accounts for the fact that air, as the lifting medium, is almost universally used. In the average field, wells are drilled on the flanks of the domes in close proximity to one another, largely on account of the extreme dips of the formation and "town lot" leases, and space to set up machinery and

Jan 1, 1928

By Lester Guttman

THE connection between short-range order and thermodynamic activities in binary solid solutions has been pointed out by Birchenall1 who calculated approximate values of the energy of interaction of Zn and Cu and of the degree of short-range order in alpha-brass at one composition and two temperatures. The purpose of this note is to call attention to a somewhat more accurate theory than that used by Birchenall and to extend the calculations to a wider range of temperatures and compositions as a means of testing its applicability. This is an example of the well-known general method of comparing measured thermo-dynamic functions of a system with those calculated from a microscopic model by means of statistical mechanics. In this case, mathematical approximations must be used which make difficult any decision about the validity of the model. Birchenall's statistical method resembles closely that called by Fowler and Guggenheim2 the "quasi-chemical" method which has been shown to lead in certain cases to results identical with those obtained by the method of Bethe.3 The quasi-chemical method has been extended by Takagi4 to give general formulae for the free energy of binary solid solutions based on several lattices at all compositions and temperatures. Specifically, he treats the four systems typified by: I. ß-brass; 2. a- brass; 3. AuCu3; 4. AuCu. When the temperature is so high that no long-range order exists, these formulae reduce to the same form for all lattice types, namely: [ ] Here the symbols have the following meanings: [F-Helmholtz free energy E-energy S-entropy k-the gas constant per molecule z-coordination number, (e.g. 12 in. a-brass). N-total number of atoms c-atomic fraction of A] VAA, VBB, VAB-energy per bond of the corresponding bonds log means log, throughout The superscript 0 denotes the thermo- dynamic function in the standard state, which has been chosen to be pure A or B with the same crystal structure as the solid solution. The quantity x is the ratio of the number of A-A bonds to the total number and for minimum F satisfies the equilibrium condition [ ] The free energy may also be written in terms of µA and µB, the chemical potentials or partial free energies per atom:

Jan 1, 1948

By A. Lee Barrett

The Maintenance Committee of the Coal Division of the American Institute of Mining and Metallurgical Engineers is presenting as a part of this report the second of a series of maintenance cost comparisons. The committee's purpose is to assemble maintenance costs on all equipment connected with mechanical operations at the face of coal mining and to arrange these costs by districts so that comparisons can be made between districts and within districts. The committee, this year, sent 35 questionnaires to representative coal companies who either reported last year or had advised specifically of the inability to report to last year's questionnaire primarily because of limited time. The response to the questionnaire this year as not as good as last year, only 20 of the 35 selected companies returning a completed questionnaire. This year's data have been compiled and combined with last year's data to present a comparison of the 1945 and 1946 costs of loading machines, shortwall cutting machines, universal cutting machines, service locomotives, shuttle cars, and mine cars. The same tabulation by districts is used as was used for 1945. As was indicated by last year's report there is considerable variation in the in cost of mining machinery in the various coal mining districts and due to this high variability it was not felt practical to attempt to arrive at weighted averages. Consequently, all average figures used in this report are straight averages. An analysis was made of companies reporting both this year and last year in an attempt to determine the trend in maintenance costs for different classes of equipment. Ten representative companies are used in this computation. Table I shows the average cost for 1945 and 1946. It is felt that the negative trend in the maintenance cost of universal cutting machines probably represents the effect of the purchase of a relatively large number of new machines in 1946 with little maintenance cost appearing during the first Year of operation. The grand total figure indicates an upward trend amounting to plus 18.7 pet. However, this figure is viewed with some suspicion because of the effect of the universal cutters decreasing maintenance cost and it is concluded that direct application of percentage increase should be made to types of equipment. In Table 2 covering maintenance costs of various types of mining equipment for 1945 and 1946 the results obtained in Table I indicating trends were applied to those

Jan 1, 1949

F. C. HENDERSCHOTT,* New York, N. Y.-I am going to take, as the text of what I shall discuss, a portion of the second paragraph of Mr. Stanford's paper. It read as follows: "The most vital need of the management is for more brains. The logical course for an engineer ;in charge of an industrial organization is, therefore, to direct whatever forces may be at his command toward the development, training and guiding of-all the brains in his organization. This is easier said than done, for it involves the carrying on toward two objectives, the maximum of productive work and the development of the individuals, who perform it;" and the last sentence of the paper; "Industry has no greater asset than an intelligent workman." The United States of America, at the outbreak of the present war, had the best equipment of any nation in the world. That statement holds not only for our -shops and our transportation systems and our stores and our farms and our homes, but it holds generally.. There was no other nation in. the world that had so good equipment as the United States. There was no other nation in the world that could be called progressive that has such poorly trained workers as the United States. Even Norway, Denmark, Sweden and New Zealand ranked ahead of us. Now that is the, problem, generally speaking, and there was recognition of that fact, a growing recognition which-took form, and one of its forms was what we call the corporation school. Now obviously a corporation has no particular educational functions, but as is said in the closing sentence of Mr. Stanford's paper, or as is implied, an industrial institution is, after all, the reflection of the aggregate of the efficiency of the individuals who compose that organization. There is no way of getting away from that. If your individuals, from your president down, are efficient, if your individual has developed his brains, if he is a trained man, you have got an efficient organization, and if you haven't that condition, you have got weaknesses and your organization is no stronger than those weaknesses. I maintain that the same thing holds for a nation; .a nation is as efficient as the collective efficiency of the individuals who compose the nation, and no more so.

Jan 4, 1918

By Eugene Jablonski

Statistical data on the Polish producing business are available only for the first half of 1939. Because of the invasion of the country during September by Germany and Russia all sources of information have stopped, and it is impossible to get even an approximate picture of the status of the industry after that date. The long declining trend of Polish production, which was finally checked during 1938, kept a further upward tendency during the first half of 1939, and there is good reason to believe that the upward trend would have been maintained. It is true, there was little hope of reviving the slowly dying Boryslaw field, although there still remained a slight possibility for an extension in its southwestern direction. Repressuring plans were still discussed, but. could not be put into effect because of extremely complicated and split-up lease ownership. The Gorlice-Lipinki ficld continued to be the main factor in the increase of the country's production. During the first half of 1939 this field received a further important extension in a southern direction. The Schodnica field continued to use repressuring with success. At the end of June, 21 exploratory wells were drilling, 14 of which were within thc Carpathians and 7 in the Miocene geosyncline of the Carpathian Foreland. All of the wildcat wells drilled within the Carpathians were on the struct,ural cxtcnsion of old established fields, but part of the wildcats of the Foreland were on new geological and geophysical prospects. The Opary gas field of the Foreland discovered last year has been further developed. The Government-owned Polmin completed its third gasser. This well penetrated two sands; the upper one, 118 ft. thick, was found at 1312 ft., with an initial pressure of 570 lb. and capable of produeiring 10 million cu. ft. per day. The second sand, 91 ft. thick, was found at 1690 ft., yielding 20 million cu. ft., with a pressure of 760 lb. The well Mieczyslaw, drilled about 3 miles further north on the flank of the structurc, found the first sand watered. The Pioneer No. 5, at Chodonice near Przemysl, which reported somc gas last year, was 5696 ft. deep at the end of June, still drilling in Miocene. Anothe well in the same vicinity drilled by the Gasolina was 1708ft. deep.

Jan 1, 1940

By Archibald Macmartin

THE Königin-Marien-Hütte is the only works in Germany where the Bessemer process is carried on by the direct method. The Besserner plant there, is arranged after the true English type, and the only resemblance to the Swedish mode of procedure is the dispensing with the use of spiegeleisen at the end of the "blow." In a new department of the establishment, started within three years, each of the converters is turned by means of a very neat and compact reversible engine, the steel shaft of which is an endless screw, which turns against the oblique cogs of a large wheel attached to the shaft of the vessel. An advantage which this arrangement possesses over the ordinary English hydraulic arrangement, is the fact that the endless screw suffices to turn the vessel, in either direction, any number of complete revolutions; while even the latest American improvements, so clearly explained to us by Mr. Holley at the opening session of this meeting, do not secure even one complete revolution without changing the angle of inclination of the hydraulic piston. In the endless screw arrangement, there being no limit to the working of the motor in either direction (no return-stroke necessary), the vessel can always, unless outside reasons demand the contrary, be turned around to any desired position by the shortest cut, whether backwards or forwards. Also, the diameter of the cog-wheel attached to the vessel can be made sufficiently great to avoid all unevenness of motion. In the old department the motive-power still continues to be hydraulic. If reports be true, the new department produces spiegelized steel, for the manufacture of all-steel rails. But the old department is still,' as from the beginning, devoted to the production by the direct method of steel for steel-headed rails. The most remarkable fact connected with this direct steel is the ease with which it welds to the iron' of the rail-packets, although no borax or other fluxing agent is used to facilitate the welding. It is very rarely that an exception occurs, and an ingot or a charge is discarded by the rail-mill. The mixture of pig-iron used for the production of this steel is melted in cupolas of very interesting construction (not to be de

Jan 1, 1874

By G. Thomas, O. Johari

MEIERAN and Richman' have proposed a method for the determination of electron-diffraction patterns from twinned bcc crystals. It is the purpose of this note to present a general method capable of predicting the positions of all reflections from both matrix and twin regions for all possible orientations of cubic crystals. The method has been verified for twinning in explosively deformed copper, and is found to be a very useful tool when used in conjunction with stereographic projection, and dark-field electron microscopy. Let an isometric crystal be twinned in any (hkl) plane. The twinning can be considered either as a reflection in the twin plane or as a 180-deg rotation about the twin axis. In reciprocal space, the 180-deg rotation about the twin axis would place a given point p, q, Y to a new position P, Q,R, such that both will be equally inclined to the twin axis. This is represented in Fig. 1. If the coordinates of three such pairs of points are determined, the matrix of the transformation can be obtained.' It is also seen that such pairs would satisfy another condition, i.e., the vector [p,q,r] plus the vector [P,Q,R] will yield a multiple of hkl, i.e., the indices of the twin plane, because in isometric systems the axis [hkl] is perpendicular to the plane (hkl). This can be simplified by taking the points along the three axes. If a point h2 + k2 + 12, 0, 0 is taken along the x axis, it is seen that its new indices should be so as to yield a sum 2h2, 2hk, 2hl,i.e., 2h(h,k,1). (Also the points h2 - k2 - 12, 2hk, 2h1, and h2 + k2 + 12, 0, 0 are equidistant from the origin and both points make equal angles with the twin axis, i.e., cos-' h/dh2 + k2 + l2.) Similar operations for the points yield respectively, after the 180-deg rotation about the twin axis. Following the method due to Buerger,' the matrix of the transformation is obtained as follows: Using this matrix the indices of any other point in reciprocal space can be determined. This matrix is much simplified for (111) twinning commonly encountered in fcc metals, since are each equal to —1; hence

Jan 1, 1964

By John J. Egan

THE present list of problems relating to the physical chemistry of steelmaking has been prepared by the Committee on the Physical Chemistry of Steelmaking, from answers to a questionnaire Submitted to a number of metallurgists engaged in both industrial and educational work throughout the United States. The purpose of the project is to make available to research laboratories a list of problems, all reduced to their simplest terms, the solution of which would aid in creating a better understanding of the steelmaking process. It is not intended to restrict the problems to practical steelmaking. The list also includes the study of the properties, and their correlation, as well as the physical and chemical reactions, of all Substances that occur or that may be in any way associated with steelmaking operations, Such as metallic substances, refractories, nonmetallic inclusions, and the constituents of slags. Many of the problems can be carried out in university or other research laboratories. Others may be most successfully attacked by cooperation of the research men with the operating personnel. It is the Committee's earnest wish that this cooperation be fostered. It is requested that investigators who are working on any of the problems listed and who anticipate future publication of their results, notify the Secretary of the Committee that such investigation is in progress. Suggested additions to the present list are also requested. The Committee is undertaking to act as a clearing house for information regarding the topics in this field that are being actually studied. Interested persons are invited to correspond with the Secretary. I. Data involved in the state of equilibrium for the various systems (laboratory work, almost entirely). A. SPECIFIC HEATS, HEATS OF FORMATION, ENTROPIES AND FREE ENERGIES OF VARIOUS PURE ELEMENTS OR COMPOUNDS; ALSO CERTAIN TYPICAL SLAGS AND REFRACTORIES. I . Determination of specific heats and entropies of oxides, sulphides, nitrides, etc. over a wide temperature range. 2. Determination of free energies of oxides, sulphides, nitrides, etc. over a wide temperature range. 3. Determination of the heats of formation of the oxides, sulphides, nitrides, etc. 4. Determination of the thermodynamic properties of the more important mineralogical constituents of the basic open-hearth slags such as calcium silicates, calcium phosphates, calcium ferrites, manganese silicates, FeO and Fe2O3. 5. Determination of the specific heats of open-hearth slags, including liquid silicates, if possible.

Jan 1, 1941

By Robert D. Thomson

LISTED among strategic and critical minerals for stockpiling, mica is an important raw material in electronic and electrical equipment industries. Each year large quantities are consumed in the manufacture of television and radio tubes, radar sets, generators, transformers, electric toasters, and irons. Crude mica, which comes from the mine in crystals or in rough books of various shapes and sizes, is known as run-of-mine or book mica. Structural imperfections, impurities, rough edges, and defective laminae are removed by cobbing, rifting, and trimming to produce a marketable block mica or film mica.' After the rough books have been hand-cobbed to remove adhering rock, dirt, and crushed or defective mica they are rifted, or split. In the U.S. a straight-bladed knife is generally used for rifting. Products of this operation are classed broadly as untrimmed sheet mica and scrap. Sheet mica is any relatively flat piece sufficiently free from physical defects to be cut or stamped into specified shapes for industrial use. Sheet mica is classed as block, film, and splittings. Block mica is not less than 0.007 in. thick with a minimum usable area of 1 sq in. Film mica is split from the better qualities of block mica to groups of specified thickness ranging from 0.0012 to 0.004 in. Splittings are sheets with maximum thickness of 0.0012 in. and minimum usable area of 3/4 sq in. As virtually no mica splittings are produced in the U.S., they will not be discussed in this report. Small, low quality block is subdivided as punch and washer. Punch mica is thumb-trimmed material large enough to yield a circular disk of at least 11/2 in. diam for stained quality mica and 1 1/4 to 2 in. for clear quality. Poorer lots, often referred to as washer mica, are also included in the general term punch mica. Trimming, the next step in processing sheet mica, removes broken and ragged edges, loose scales, and other major imperfections. Trimming may be done with a knife, sickle, shears, or fingers. In the U.S. it is usually done with a 3-in. linoleum knife to obtain a bevel-edged cut. If ragged edges are broken off with the thumb and fingers, the mica is called thumb-trimmed. Full-trimmed is rifted mica trimmed on all sides with all cracks, reeves, and

Jan 1, 1957

By M. E. Lombardi

The cost of maintaining the production of an operating oil company is one of the most important, as well as one of the most difficult to estimate, of the various items which go to make up the total cost of producing oil. In the opinion of many operators the cost of drilling and developing new wells, whose, production takes the place of the loss in production through decreased yield of the old wells, is considered an operating expense, for the reason that the total income-producing power of the property is not increased. The cost of these new wells may be added directly to production expense, or it may be charged to capital account, and this account depreciated to the same extent. In either case, after an oil company is on a satisfactory income-producing basis, the money for drilling new wells to maintain production must be taken from the income of the company. Three factors determine the cost of maintaining production: First, the rate of decline in yield of the wells; second, the cost of drilling and equipping new wells in terms of their production; third, the decrease in initial production of new wells as the property is drilled and gas pressure taken off the sands, etc. In order to check theoretical figures for the cost of maintaining production the writer, with the assistance of Reed Bush and Fred Tough, has compiled the following figures. It is necessary first of all to choose a' period of time during which production for the field or territory studied remains fairly constant. The longer the period of time over which this condition prevails, the better. It is also necessary to eliminate or allow for any extraneous condition which may have affected the production returns, such as the shutting down of a large number of wells, the bringing in of a well of exceptionally large yield, the opening up of virgin territory where the flush yield is greater than will be had from new wells in after years, etc. All these conditions are exemplified most simply in the case of the Coalinga field, and perhaps these figures are more truly prophetic than the two other cases given. In applying these figures to the future it is well to assume that the average yield of new wells will constantly de-

Jan 1, 1916

By John C. Smock

THE question of the proper valuation of mines of iron ore was suggested to me by the difficulties experienced in getting answers for the United States Census Office, while I was engaged in the work of collecting the statistics of mines in New Jersey and New York The answers to the questions relating to values of real estate of mine properties varied so greatly that it was necessary to revise them according to some general principles of valuation. Generally the returns of mine proprietors Seemed to be too low. There were, however, examples of what would be termed excessive valuation. The Subject appeared to be of practical importance, and led to the paper here presented. The following table of selected mine statistics is given, prefacing the discussion of the principles of valuation. It is in part made up of census returns and partly of data obtained directly from mine owners and managers. The mines which were Selected for the Several groups and mining districts include nearly all of those from Which the more full and carefully filled returns were received, and are also representative of their respective districts. Hence the averages obtained from them become good types of these groups or districts. The mines of New Jersey appear in Six groups, each containing from three to eleven mines, or, in all, thirty-four mines. The magnetic iron ores of New York are in four well-marked groups, and there are twenty-six mines in them. Then follow the red hematite mines of St. Lawrence and Jefferson counties; and, lastly, the brown hematite groups of Dutchess and Columbia counties, and those of the adjacent parts of Connecticut and Massachusetts. The whole number of mines represented by the table is eighty-eight, of which twenty-eight are hematite mines. The first column gives the value of the real estate; the second that of the plant; the third is the sum of these two, or the capital invested. Then follow the number of men employed, the amount of wages paid during the census year, and the value of materials used in mining and preparing the ores for market.* The seventh column gives the total expendi- * The value of materials is somewhat uncertain in many cases, as royalties are included under this head. Likewise, under wages, the cost of explosives and light is often included. Hence it is impossible to draw the line sharply between these items of expenditure.

Jan 1, 1882

By J. Kittl, D. Arias

THE decomposition on cooling of the high-temperature ß bcc phases in copper- or silver-based binary systems usually takes place by a martensitic. massive, bainitic, or pearlitic reaction depending upon the particular conditions of each system. The AgAl system is one of these systems in which a massive or a martensitic transformation can occur upon cooling from the 3 phase field. Recently Hawbolt and Brown1 observed both massive and martensitic transformation products in a 22.7 at. pct A1 alloy. In the present work the massive and the martensitic transformations were investigated in a number of alloys for the composition range between 23.2 and 27.9 at. pct Al. The alloys were prepared using high-purity silver, 99.999 pct, supplied by ASARCO and aluminum, 99.999 pct, supplied by ALCOA. The metals were melted using a graphite or a sintered alumina crucible which was sealed in quartz tubes under an argon atmosphere. The alloys Were remelted to reduce segregation and homogenized in the 13 phase field for 24 hr. The weight of the alloys after homo-genization compared with the initial weight indicating the alloy composition to be within k0.1 pct of the in- tended composition. Chemical analysis of several samples confirmed the estimated alloy composition. All metallographic observations were performed on samples electropolished with ac current using a 10 pct solution of KCN and a stainless-steel electrode. The samples were cut into -1-mm-thick slices, polished, heat-treated in the ß phase field, and quenched in air, ice water, or iced brine. Some heat treatments consisted of a 2-min anneal carried out in air to allow maximum quenching speeds. Other samples were heat-treated in a vacuum of 10"4 torr and quenched using a helium blast in a quenching apparatus described elsewhere.&apos; In both cases, no appreciable losses of silver or aluminum were noted at the sample surface by sectioning and electropolishing. Table I summarizes the microstructure resulting from the various quenching treatments. The composition of the alloys investigated is also indicated on the equilibrium diagram in Fig. 1. The <, hcp phase, typical of a massive ß — cm, transformation, was observed in all alloys. A minimum temperature of 450°C was estimated for this transformation based on preliminary cooling experiments. the results being included in Fig. 1. In these

Jan 1, 1970

By Ralph E. Grim

THE technology of clay minerals is defined, for the purpose of this review, as- the application of fundamental data regarding clay minerals, and techniques of handling them, to the various industries, arts, and professions concerned with clay materials. The aim of the paper is to narrate recent developments in clay mineral technology. This review does not claim to be complete, and perhaps gives undue emphasis to matters that have been worked on in the author&apos;s laboratory or with which he has some other connection. In the United States in recent years, particularly since the end of World War 11, interest in clay mineralogy has increased greatly. Many laboratories in many different fields have embarked on studies of clay minerals but unfortunately much of this work has not been published. CERAMICS In the field of ceramics, in recent years, a great deal of interest has developed in clay mineralogy. Papers too numerous to be reviewed here have been published portraying the clay mineral composition of substantially all the important types of ceramic clays in all countries. There has been a growing tendency to attempt to solve processing problems on the basis of clay mineral data rather than chemical analytical data. Likewise, there is an in- creasing tendency to control the characteristics of raw materials on the basis of clay mineral composition rather than chemical composition. In the United States in the last few years something like 50 differential thermal analyzers have been set up, and many are for the sole purpose of controlling raw material and processing. The ceramic industry is currently increasing its attention to the influence of exchangeable ions and soluble salts on physical properties. Ion concentration in clay suspensions has long been a matter of interest, but now it is also of interest in clays in the plastic state because of its recognized importance in the plastic, shrinkage, and bonding properties of clays. Students of clay have long recognized that an understanding of the plastic properties of clays is based on an understanding of the character of the water in clay-water systems, the nature of the binding force between individual clay mineral particles, and the factors that control the character of the water and the nature of the bonding force. In the last few years, some extremely important contributions have greatly increased the understanding of the nature of water adsorbed on the clay mineral surfaces. In this connection the work

Jan 1, 1952

By E. T. Turkdogan

The activity of sulfur was determined as a function of composition of ferrous sulfide by equilibrating with hydrogen sulfide-hydrogen gas mixtures at 670° , 800°, and 900". The present results supplement the available data over the composition range from 36.6 to 39.5 pct S. The X-ray lattice spacing measurements made are in accord with the available data and indicate that the limiting composition FeSl.008 may be taken for the iron-iron sulfide equilibrium. The growth rate of ferrous sulfide on iron was measured by reacting iron strips or blocks in hydrogen sulfide-hydrogen gas mixtures. Owing to the slow approach to equilibrium between the gas phase and the surface of the sulfide layer, The sulfidation experiments were carried out for several days. It is shown that the growth rate ullimately proceeds in accordance wilh the parabolic rate law. From the parabolic rate constants and the thermodynamic data on iron sulfide the self-difiusivity and chemical diffusivity of iron in ferrous bisulfide are evalualed. The self-diffusivity of iron thus derived zs found to increase with increasing sulfur content. THE ferrous sulfide known as "pyrrhotite" is a non-stoichiometric phase having a wide composition range from about 50 to about 58 or 60 at. pct, depending on the sulfur activity. RosenQvistl studied the thermodynamics of this phase over wide ranges of temperature and composition. Hauffe and Rahmel&apos; and Meussner and ~irchenall~ studied the parabolic rate of sulfidation of iron in sulfur vapor. By using markers, these investigators showed that the iron cations were the predominant diffusing species in iron sulfide. This is confirmed decisively by the self-diffusivity measurements of condit4 who showed that the self-diffusivity of sulfur in ferrous sulfide is several orders of magnitude lower than the self-diffusivity of iron. Although much has been learned from these studies about the Fe-S system, further research on this subject was considered desirable for better understanding of the physical chemistry of iron sulfide. This work was confined to the study of the kinetics of sulfidation of iron in hydrogen sulfide-hydrogen gas mixtures. The results of this study are given in two consecutive parts. Part I, the present paper, is on the parabolic rate of sulfidation of iron and the diffusivity of iron in ferrous sulfide. The second paper, Part 11, is on the kinetics of the surface reaction between hydrogen sulfide and ferrous sulfide. EXPERIMENTAL Three types of experiments were carried out: i) equilibration of ferrous sulfide with gas of known E. T. TURKDOGAN, member AIME, is Manager,Chemical Metallurgy Division, Edgar C. Bain Laboratory for Fundamental Research, U. S. Steel Corp., Research Center, Monroeville, Pa. Manuscript submitted March 6. 1968. ISD sulfur potential; ii) X-ray studies of ferrous sulfide; and iii) measurements of the parabolic rate of sulfidation of iron. Equilibrium Studies. About 1 g of iron powder or foil. contained in a small recrystallized alumina crucible ind suspended from a calibrated silica spring, was reacted with a hydrogen sulfide-hydrogen mixture of known ratio until no further change in weight was observed. %hen the gas composition was changed and the new state of equilibrium was established after several hours of reaction time. The composition of the sulfide was obtained from the initial weight of the sample and the weight after equilibration. X-Ray Studies. The lattice parameters of some of the equilibrated samples were determined using the General Electric XRD-5 diffractometer with a cobalt tube (no filter) set at 40 kv apd 10 ma; the CoK, radiation was taken as 1.79020A. Observed 220 and 311 diffraction peaks of silicon served as an internal comparison standard to correct for possible misalignment of the goniometer. The lattice parameters of the sulfide phase were calculated from the corrected Bragg angles of the 110 and 102 peaks. Rate Studies. In the initial experiments attempts were made to measure the parabolic rate of sulfidation by measuring the gain in weight of a thin iron strip, -0.05 cm thick, suspended from a silica spring in the reacting atmosphere. The preliminary experiments showed that this technique was not reliable for the measurement of the parabolic growth rate of the iron sulfide layer. In the subsequent experiments the data on growth rate were obtained by measuring, on a microscope stage, change in the thickness of the sample after reaction for a specified time in a hydrogen sulfide-hydrogen mixture of known sulfur activity. For each reaction time a new sample was used. Precision-machined iron blocks, 0.5 by 2 by 5 cu cm, were de-greased and annealed in hydrogen for several hours prior to the sulfidation rate measurements. The experiments were carried out at 670°, 800°, and 900°C in gas mixtures having the ratios, and 1.0 for periods of times from a few hours up to 8 days. Apparatus and Materials. A vertical globar tube furnace with a 3-in.-long uniform temperature zone was used. The glass tube fittings were fused on the zircon reaction tube, 1.5 in. diam. The temperature was measured with a Pt-10 pct Rh/Pt thermocouple placed in the hot zone of the furnace inside the reaction tube (an alumina thermocouple sheath was used). A separate thermocouple was used for the temperature controller which maintained the furnace temperature constant within about 2°C. Anhydrous liquid hydrogen sulfide and oxygen-free dry hydrogen from gas tanks were used in preparing the gas mixtures by the constant head capillary flow-meters. In all cases volume flow rate was 1000 cu cm per min at stp, corresponding to a linear velocity of about 6 cm per sec at 800°C; under these conditions

Jan 1, 1969

By E. T. Turkdogan, L. J. Martonik, R. J. Fruehan

Electrochemical measuretnents of the solid oxide electrolyte galvanic cells CY-Cr2O3 I ZrO2 (CaO) 1 O (in Fe alloy) CY-Cr2O3 I Tho2 (Y2O3)I O en Fe alloy) have been made at 1600°C (2912°F) in order to test the Performance of such cells at liquid steel temperatures. The oxygen pvobe (cell) consists of a disk of ZrO2 (CaO) or Tho2 (Y2O3) electrolyte fused at one end of a silica tube filled with a mixture of Cr-Cr2O3 which is the reference electrode. Upon immersion in liquid steel, the electromotive force readings achieve a steady value within a few seconds, and remain steady for 30 win or more. The perforwzance of the probes has been tested using Fe-O, Fe-Si-O, Fe-Cr-O, Fe-V-O, and Fe-Al-O alloys; the oxygen contents of liquid steel derived from the measured electromotive forces are in satisfactory agreement with those determined by arulysis. Use of the probe in the deoxi-datiorz of steel, in laboratory experiments, is discussed. The results indicate that there is insignificant electronic conductivity in ZrO2(CuO) at oxygen activities down to those corresponding to 10 ppm in steel. At lower oxygen activities, probes tipped with ThOn (Y2O3) disks perform satisfactorily at oxygen activities down to 1 ppm O or less. THE key to the control of deoxidation of steel is a sensing device to measure rapidly the concentration of oxygen in liquid steel in the furnace, ladle or tun-dish at any desired stage of deoxidation. The analysis of the cast steel by the neutron-activation or vacuum-fusion method gives total oxygen as oxide and silicate inclusions. This analysis is important for guidance to steel cleanliness; however, such a postmortem is of little value in the control of deoxidation of liquid steel. At the General Meeting of the American Iron and Steel Institute in New York, 1968, Turkdogan and Fruehan&apos; presented a paper on the preliminary results of the work done in this laboratory on rapid determination of oxygen in steel by an oxygen probe. Details of the work done in this laboratory leading to the development of a galvanic cell for the determination of oxygen in liquid steel, and the results of the tests made are given in this paper. It was through Wagner&apos;s contributions, since the early Thirties, to the physical chemistry of semiconductors in general that it ultimately became possible to construct galvanic cells for application at high temperatures. In 1957, Kiukkola and wagner2 successfully demonstrated the use of several solid electrolytes in measuring the free energies of several chemical reactions, in particular, the use of lime-stabilized zir-conia in high-temperature oxidation reactions. Starting 7 years later, a number of papers appeared in the technical literature3-&apos; demonstrating possible applicability of galvanic cells for the determination of oxygen in liquid steel. In the earliest work, Japanese investigators3j4 experimented with various types of reference electrodes, e.g., graphite-saturated liquid iron at 1 atm CO or Ni-NiO mixtures; the results obtained, though promising, were not of sufficient accuracy. Except for the work of Baker and West,6 all other investigators5,7,8 showed that ZrO2(CaO) electrolyte could be used for this purpose. The main part of the galvanic cell used by Fischer and ~ckermann&apos; and by schwerdtfeger7 (the latter work was done in this laboratory), consisted of a ZrO2(CaO) tube, -1 cm ID, closed at one end, with a platinum contact wire fixed mechanically inside the closed end. The tube was flushed with a gas of known oxygen partial pressure, e.g., air, CO-CO2 or H2-CO2 mixtures; gas along with the platinum lead wire served as the reference electrode. The oxygen contents derived from measured electromotive forces agreed reasonably well with the oxygen contents determined by vacuum-fusion analysis. It is evident from recent investigations that the electromotive force technique using a solid oxide electrolyte is fundamentally well suited for the determination of oxygen in liquid steel. However, it is equally clear that the cell arrangement of the type as commonly used is in need of considerable improvement, as it exhibits several shortcomings for industrial and even laboratory use. 1) Because of its size, the zirconia tube, though stabilized, has a poor resistance to thermal shock. 2) Fine pores and microcracks, which are invariably present in zirconia tubes, are detrimental to the satisfactory operation of the cell, particularly when gas reference electrodes are used. 3) Air or carbon dioxide reference electrodes give rise to high electromotive force readings; as a result, the determination of oxygen in steel becomes less accurate. For higher accuracy, the oxygen partial pressure of the reference electrode should be in the range similar to that of oxygen in steel. 4) Even in laboratory experiments, difficulties are experienced when flushing the tube with gases and maintaining the proper gas flow rate. Fischer and Ackermann,&apos; who used air as the reference electrode, reported that when the flow rate was too low, furnace gases would leak into the electrolyte tube, therefore lowering the oxygen potential and measured electromotive force. The required flow rate in order to avoid leakage depended on the tightness of the electrolyte tube which varied with different tubes, thus making it difficult to predict in advance the required flow rate. However, if the flow rate is too high the inside wall of the electrolyte tube would be cooler than the wall

Jan 1, 1970

By H. C. Fiedler

Heats of high purity iron containing 3.1 pct Si and be -tween 0.0003 and 0.0295 pct N were prepared by vacuum melting ad then pouring while in a nitrogen atmosphere with the pressure between 0 and 90 psi. Strip from a heat with 0.0184 pct N underwent complete secondary recrystallization during the final anneal. Heats with less nitrogen had too few Si3N4 particles to restrain normal grain growth, and the heat with higher nitrogen had too many particles to allow complete secondary recrystallization. In the hot-rolled structure, Si3N4 precipitates only at the grain boundaries, with the consequence that annealing after hot-rolling diminishes the ability to subsequently undergo secondary recrystallization. In contrast to this behavior, ALNprecipitates uniformly in the hot-rolled structure. Under 1 atm of nitrogen, Si3N, in 3.1 pct Si-Fe dissociates between 900" and 950°C; the solubility of nitrogen increases from 0.0010 pct at 900" to 0.0030 pct at 1200°C. The solubility of nitrogen in Si-Fe has been the subject of many investigations. Corney and Turkdogan1 heated a 2.83 pct Si alloy in nitrogen and found the solubility, under 1 atrn of nitrogen, to be 0.0019 pct at 900°C. They claimed that Si3N4 did not form in the alloy above 705°C in 1 atrn of nitrogen. Fryxell et al.2 heated samples of 3.25 pct Si-Fe containing 0.0025 pct N over a range of temperatures and then analyzed for total nitrogen by vacuum fusion and for nitrogen in solution by a modified Kjeldahl technique. At 900°C, they reported the solubility of nitrogen in equilibrium with Si3N4 to be 0.0011 pct. pearce9 found the solubility of nitrogen at 900°C under 0.95 atrn of nitrogen to be 0.0017 pct in a 3.06 pct Si alloy. He reported that Si3N4 does not form above 770°C in 1 atrn of nitrogen. Although internal friction measurements have given somewhat higher values for the solubility,4-6 if the solubility of nitrogen is as low as has been reported by most investigators, and if Si3N4 is stable up to at least 945°C at 1 atrn pressure of nitrogen as reported by Seybolt,7 a small amount of nitrogen in properly processed Si-Fe should be effective in promoting secondary recrystallization. The requirement is that in the final heat treatment there be enough small, well-dispersed particles of Si3N4 to restrain normal grain growth. Fast8 has obtained secondary recrystallization by nitriding high-purity 3 pct Si-Fe after hot-rolling to a thickness of 0.118 in., followed by processing to 0.012 in., and annealing. A large amount of nitrogen, 0.076 pct. was introduced during the nitriding heat treatment, but he has since reported9 that "a few hundredths of a percent" is sufficient. Small amounts of aluminum10 or vanadium" nitride are capable of promoting secondary recrystallization. Heats containing as little as 0.010 pct A1 or 0.042 pct V and from 0.006 to 0.009 pct N underwent complete secondary recrystallization at final gage, whereas heats with lesser amounts of aluminum or vanadium did not.l2 To be reported is the behavior of nitrogen in high-purity 3.1 pct Si-Fe, and the relation of this behavior to the ability to undergo secondary recrystallization. PROCEDURE Ingots weighing 1 lb were made by vacuum melting high-purity electrolytic iron (A104, Glidden Co.) and high-purity silicon (Monsanto Co.). The latter was used in preference to ferrosilicon to insure a low aluminum content. The design of the melting furnace permitted pouring with the furnace atmosphere either below or above atmospheric pressure. Accordingly, at the completion of melting, nitrogen was admitted to the desired pressure and the heat then immediately poured. The ingots were sound, with no indication of porosity. In Table I are listed the heats investigated, the nitrogen pressure at pour, and the nitrogen and oxygen contents as determined by vacuum fusion with a platinum bath at 1850°C, a procedure which insures measurement of the total nitrogen.13 In addition, all heats contained 3.1 pct Si and not more than 0.002 pct C, 0.003 pct S or 0.005 pct Al. It was subsequently found that the quantity of nitrogen contained in the heats in Table I does not necessarily represent that obtained under equilibrium conditions. For example, the ingot poured immediately after 1 atrn of nitrogen was admitted to the chamber contained 0.0093 pct N, whereas an ingot poured 3 min after the nitrogen was admitted contained 0.021 pct N and another poured after a 6-min delay contained 0.029 pct N. While some bleeding of the hot top occurred in the latter instance, the ingot when examined in cross section appeared sound. The ingots were heated to 1325°C in hydrogen and rapidly rolled to 0.080 in. in 3 passes. The roll speed of the final pass was reduced so as to increase the quenching effect of the rolls. The hot-rolled pieces were processed both as-hot-rolled and after heating for 3 min at 900°C in hydrogen. After cold-rolling to 0.026 in., the strips were heated for 2 min at 900°C in hydrogen, then cold-rolled to the final gage of 0.012 in. The loss of nitrogen in going from the ingot to cold-rolled strip was no more than 10 pct. The final heat treatment, which was for the purpose of develop-

Jan 1, 1970

By A. Mitchell

An approximate phase diagram has been developed for the CaF2-CaC2 system, indicating a eutectic point at 1240°C, Ncac2 = 0.13, and no detectable solid solution in either phase. The liquidus line is shown to correspond to a simple c22- ion in solution. A thermo-chemical study of&apos; the reaction between carbon-saturated Ni-Ca alloys and CaC2-CaF2 liquids indicates that lhe Raoullian activity coefficient of CaC2 in dilute solution in Cap2 al 1500°C lies between 8 and 10. Some effects of the stabilily of Cap2-CaC2 solutions at high temperatures on electroslag remelting praclice are outlined. THE alkaline earth acetylides. MIIC2, have a reasonably high thermochemical stability at high temperature in the solid state,&apos; with the exception of magnesium, which forms an unstable acetylide at low temperatures (-500°C) and a carbide, Mg2C3, in the range 700&apos; to 1000°C. The acetylides of calcium and barium have been shown to have limited solubility in their respective chlorides,&apos; and further these solutions contain the acetylide as a C: ion.&apos; The equivalent magnesium solutions have not been studied. Although calcium "carbide" is used as a desulfuriz-ing reagent in steelmaking. and is possibly present as an acetylide-oxide phase in very basic electric arc practice slags, the acetylide ion appears to be substantially unstable in a silicate slag.* As a conse- *This instability arises from equilibria in the reaction: CaC2 + CO = (Ca0) + 3C where the low intrinsic solubility of CaC2 in silicate lattice, and the low activity of CaO in a silicate solution where CaO/Si02 < 1, combine to give a very small equilibrium concentration of CaC2 in solution in such silicate slags at temperatures in the region of I 500°c, even under carbon-saturated conditions. Under highly basic conditions, a liquid CaO-CaC2 phase may separate from the silicate system quence of this, the possibility that reactions involving CaC2 in silicate solutions are of importance to general steelmaking practice is remote. However, in operations involving a slag primarily based on a halide, or alkaline earth oxide, we must take into account the possibility that CaC2 will appear in quantities sufficient to significantly affect both the chemical and physical properties of the slag. The work outlined below presents a study of the CaF2-CaC2 system intended to provide sufficient data to allow an estimate of the importance of this system to electroslag remelting and welding practice. However, we should indicate at this point that there will be other processes, e.g., heat treatment, flux cleaning of castings, fused salt electrolysis, and so forth, where alkaline-earth halide fluxes are in contact with carbon, graphite, or carbides, and where halide-acetylide solutions must be taken into account. EXPERIMENTAL 1) Structural Studies. In view of the difficulty ex-perienced in handling CaC2 prepared from calcium turnings and propane gas at 700°C, it was decided to use solutions prepared directly in the equilibration apparatus, Fig. 1. The starting materials were: a) Ni-Ca-C alloy, prepared by adding calcium to liquid nickel held under calcium fluoride in an induction-heated graphite crucible; b) calcium fluoride, prepared by fusing calcium fluoride powder (British Drug House "EXTRA PURE") calcium fluoride in an induction-heated graphite crucible, in air, followed by electrolysis between graphite electrodes at 1 amp cm-2 density, for 10&apos; coulombs per g CaF2. This procedure decomposes the CaO produced by hydrolysis during the fusion step, replacing it by CaC2; Ca2+ + 2e-Ca*(l) Ca*(l) + 2C(gr)-(CaC2)caF2 O2- -2e-O*(g) O*(g) +C(gr)-CO(g) This results in a composition of between 2 and 5 wt pct CaC2 in CaF2. Fifty grams (in lumps) of this material were placed in a graphite crucible, together with Ni-Ca-C alloy (averaging 20 wt pct Ca), and the equilibration apparatus assembled. The alloy reacted with the crucible at high temperature to give CaC2, which dissolved in the calcium fluoride solution to give the desired composition. Cooling curves were plotted manually for these liquids, with rapid stirring and CaF2 seeding to minimize supercooling, and using a Pt/Pt 13 Rh thermocouple calibrated on the freezing points of nickel and copper. This gave a reproducibility of ±0.l°C. and an absolute accuracy of the thermocouple of ±l°C. An example curve is shown in Fig. 2, with the CaF2 end of the binary system in Fig. 3. The CaF2-CaC2 ingots were crushed, under dry nitrogen, and sampled for chemical analysis and X-ray examination. Analytical details are given in the Appendix. Powder diffraction data indicated that the only phases present in all samples examined were calcium fluoride and tetragonal (Types I and 111) calcium acetylide,4 with no evidence of solid solutions or compound formation. 2) Thermochemical Studies. The apparatus used to obtain activity data on CaC2 in these systems is shown in Fig. 4. It consists of an arrangement whereby the graphite crucible and its contents (CaF2-CaC2. Ni-Ca-C) can be rapidly cooled without exposure to air. Trial experiments to determine an equilibration time by ap-

Jan 1, 1969

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth

IN THE past year, Jaffee and Campbell&apos; and Finlay and Snyder2 reported on the mechanical properties of titanium-base alloys, some of which were in the same ranges of composition as are covered in this paper. In this paper, evidence confirming that given by Finlay and Snyder on the effects of carbon, oxygen, and nitrogen on titanium will be presented; and, in addition, new data will be given on the effects of these elements on the flow properties and phase transformation of titanium. Materials and Preparation of Alloys The preparation and general properties of iodide titanium have been adequately described elsewhere.&apos; , As-deposited iodide titanium rod, prepared at Battelle, of Vickers hardness less than 90 was employed as the base metal in the present work. This was the same material as that used by Finlay and Snyder.2 The probable analysis reported by them for standard quality metal holds here also: N 0.005 pct, 0 0.01 pct, C 0.03 pct, Fe <0.04 pct, A1 <0.05 pct, Si <0.03 pct, and Ti 99.85 pct. Carbon was added in the form of flake graphite supplied by the Joseph Dixon Crucible Co. Oxygen was added in the form of c.p. grade TiO, powder, produced by J. T. Baker Chemical Co. Nitrogen was added in Ti3N4 powder, supplied by the Remington Arms Co. Individual ingots weighed 7 or 8 g. Carbon, oxygen, or nitrogen was added by placing the corresponding powder in a capsule made from as-deposited iodide titanium rods and melting the capsule with the balance of the charge. The charge was are-melted with a tungsten electrode on a water-cooled copper hearth under a partial vacuum of very pure argon (99.92 pct minimum). Melting was practically contamination free. Vick-ers hardness increases of less than 10 points were normal for unalloyed iodide titanium control melts. Nitrogen analyses of are-melted iodide titanium showed a nitrogen content of 0.005 pct, about the same as is present in the as-deposited rod. No tungsten pickup was found in a melt of iodide titanium analyzed for tungsten. Weight losses in melting nitrogen-free alloys were very small and varied consistently from nil to 0.015 g (0 to 0.2 pct). This permitted the use of nominal composition for these alloys. Chemical analyses made for carbon, which can be analyzed conveniently by combustion methods, justified this procedure. Where nitrogen was added, considerable splattering took place. Here it was necessary to analyze for nitrogen by the Kjeldahl method. The ingots were hot rolled at 850°C to about 0.045 in. thick. After hot rolling, the strips were descaled by mechanical grinding, and then given a cold reduction of 5 to 10 pct to insure a uniform thickness throughout the length of the specimen. The edge strips and the tensile strips were annealed in a vacuum of 1x10-4 mm Hg pressure for 3 1/2 hr at 850°C and furnace cooled. Methods of Investigation Hardness Measurements: At least five Vickers hardness measurements were taken using a 10-kg load on each sample in the following conditions: (1) top and bottom of each ingot, (2) top and bottom surface of as-rolled and annealed sheet, and (3) on cross-section of annealed sheet and all quenched specimens. Tensile Tests: Tensile tests were conducted on Baldwin-Southwark testing machines having load ranges of 600 or 2000 lb. Tests were made on 1-in. gauge-length specimens, 3 1/4-in. overall length, 1/2 in. wide, 0.040 in. thick, with a reduced section 1 1/4 in. long and 0.250 in. wide. Two SR-4, A-7 strain gauges, one mounted on each side of the specimen, were used to measure the strain over a limited range to determine the modulus of elasticity. After the modulus of elasticity readings had been taken, load vs. strain readings were taken, using only one strain gauge, at increments of 0.0001 in. until the yield points were passed and then at 0.001-in. increments to the limit of the strain-gauge indicator (0.02 in.). Strain readings above 0.02 in. per in. were taken every 0.01 in., using dividers to measure the strain between the 1-in. gauge marks until the maximum load had been reached. Crosshead speed, when using the SR-4 gauges, was 0.005 in. per min, and, when using dividers, 0.01 in. per min. Flow Curves: Flow curves were determined using the true stress-true strain data obtained during the tension test. The usefulness of this type of information has been dealt with very adequately elsewhere by L. R. Jackson,&apos; J. H. Hollomon,6 and many others. Flow curves of true stress vs. true strain could be converted to the more conventional cold-work curve of 0.2 pct offset yield strength vs. percentage of cold reduction by means of the transformation, 1/1 = 1/1-R, where R is the fraction reduction in cold working. Thus, the true strains corresponding to percentage reduction can be calculated, and the 0.2 pct offset yield strengths scaled off the — 6 curve by taking the true stresses corresponding to the values of 6 + 0.002 strain. Heat Treatment: For the transformation studies, the alloys were heat treated in a horizontal-tube furnace using a dried 99.92 pct argon atmosphere, and quenched into water. Essentially no contamination was found after several hours of heat treatment at temperatures up to 1050°C. Metallography: Specimens were prepared in the

Jan 1, 1951

By E. Breinan, M. Salkind

Al3Ni whiskers were chemically extracted from unidirectionally solidified Al-A13Ni eutectic ingots, bent into loops, and heated for 0.1 to 10 hr at 320°, 415", and 510°C. The initial strains ranged from 0.003 to 0.055. In all cases, permanent plastic deformation was noted after heat treatment. The deformation consisted of relatively uniform bending at low stresses and temperatures and short times and kinking followed by fracture at high stresses and temperatures and long times. After kinking, the whisker segments adjacent to the kinks were found to have straightened, which is evidence of a dislocation condensation mechanism. The range of temperatures and strains at which time dependent plastic deformation was found indicates that creep of whiskers probably plays a role in the creep of A13Ni whisker-reinforced aluminum. WHISKERS may be defined as nearly perfect single crystals which exhibit high strength. Because they can support high stresses at relatively low strains, they have been successfully employed in reinforcing metals at both ambient and elevated temperatures. In studying the creep behavior of A13Ni whisker-reinforced aluminum at elevated temperatures,1,2 it was noted that the composites exhibited measurable creep deformation. This investigation of the creep relaxation of individual A13Ni whiskel, extracted chemically from the composite was initiated to determine if creep of whiskers could con. "bute to the overall creep of the composite material. Many observations of plastic deformation of metal and halide whiskers have been made. Brenner3-8 noted that copper, silver, and iron whiskers exhibited heterogeneous plastic deformation at room temperature when strained beyond their yield points. Gyulai9 and Gordon10 observed plastic deformation of relatively large (>3 µ) NaCl and KC1 whiskers, although the smallest, most perfect whiskers were completely elastic. Eisner" noted plastic deformation and microcreep of iron and silicon whiskers at room temperature after straining beyond the yield point. Whiskers reported to exhibit creep at stresses below the yield point were zinc1&apos;-" and Silicon.15 Cabrera and price" observed some zinc whiskers which crept at room temperature after a short incubation period but then stopped creeping after a short time. Because some of their specimens exhibited no creep, they concluded that those whiskers that crept were relatively imperfect. Pearson, Reed, and Feldman15 observed similar creep behavior of silicon whiskers at 800°C. They also concluded that creep of the whiskers was a result of imperfections in their crystals. Brenner16 observed delayed failure of A12O3 whiskers at elevated temperatures but found no evidence of plastic deformation up to 2030°C (99 pct of E.EREINAN and M.SALKIND,JuniorMembers AIME,are Research Scientist and Chief, respectively, Advanced Metallurgy Section, United Aircraft Research Laboratories, East Hartford, Conn. Maunscript submitted April 5, 1968. IMD the melting temperature). Brenner also noted7 that some copper and iron whiskers exhibited delayed kinking above 350°C while others did not. One can conclude from these observations that small relatively perfect whiskers could exhibit completely elastic behavior during sustained elevated-temperature loading of composites. Since A13Ni whiskers tested in both bending and tension were found to exhibit no evidence of plastic deformation at room temperature&apos;7&apos;18 this study was initiated to determine whether or not creep of A13Ni whiskers occurred at the elevated temperatures at which creep in the composites was observed. Whiskers were chemically extracted from ingots of unidirectionally solidified A1-A13Ni eutectic, constrained in bending to various elastic strains and heat-treated. The bending constraints were removed after heat treatment and the amount of permanent set was taken as a measure of the time-dependent plastic deformation. EXPERIMENTAL PROCEDURES Ingots of eutectic Al-A13Ni containing nominally 6.2 wt pet Ni were unidirectionally solidified at approximately 11 cm per hr using a process described elsewhere.19,20 The starting materials were 99.99 pct pure. Cylindrical sections cut from the center of each ingot were placed in a 3 pct aqueous solution of hydrochloric acid and the whiskers were extracted as described previously.17 The whiskers nearest the surface were blackened somewhat due to overexposure to the acid while the center of the ingot was being dissolved These partially attacked whiskers were discarded. An intermediate zone of silver-gray-colored whiskers was collected and stored in methanol for use in relaxation experiments. Individual long pieces of A13Ni whiskers were placed on Fisher Precleaned Microscope Slides. These normally straight whiskers were bent elastically into arcs or loops of varying radii by manipulating their ends with a slender probe. The mass attraction between the whisker and the probe was sufficient to cause the whisker to follow the probe. The whiskers were retained in the elastic bend by the surface tension of a fine residual film on the slides. By using long whiskers, the action of the surface tension on the unlooped ends of the whisker allowed high elastic strains to be maintained in the loops. After each whisker was bent, a photomicrograph was taken for use in measuring the bending strain. The range of strains studied was 0.003 to 0.055. The bent whiskers were then encapsulated in Pyrex tubes at pressures between 10"6 and 5 x 10"6 mm of mercury and heat-treated at 320°, 415°, and 510°C (respectively 53, 61, and 70 pct of the peritectic decomposition temperature). After each heat treatment, the liquid film on the slides was found to have dried, but the whiskers were held in their original shapes by a residue on the slide. The minimum radius of curvature of each bent whisker was measured before and

Jan 1, 1969

By R. S. Busk

Niels Engel (University of Alabama, University, Ala.)— In this paper it was pointed out that the electron-gas and energy-band theory accounts for the fact that the lattice parameters exhibit a sudden change when the electron concentration (number of bonding electrons per atom) exceeds a certain number around two. This statement is said to support and prove the electron-gas theory. But this theory is not able to account for a series of experimental data. Also several expectations, deduced from this theory, are not found to exist. In Figs. 6 and 7 the energy bands of the second and third periods are given as they must be assumed in order to account for the electrical properties of the elements in these periods. In Figs. 6 and 7 the electron-gas and energy-band theory is compared with the electron-oscillator hypothesis in accounting for the properties of the elements in the second and third periods. Fig. 6 shows the second period, The energy-bands are overlapping and separated to be in agreement with the electrical conductivity of the elements. The oscillator hypothesis explains conductivity due to electron vacancies. In graphite there is a closed s-shell in every other atom and two vacancies in the others. Conductivity is therefore only maintained by migration of s-electrons in graphite. In boron there are no s-electrons. The diatomic molecules of nitrogen and oxygen and the paramagnetism of oxygen can be accounted for by a similar behavior as the s-electrons of the bonding electrons. But this explanation will deviate too much for the purpose of this discussion. Fig. 7 shows the third period. In the energy-band picture about two s-electrons are assumed in magnesium and aluminum, but only one s-electron is assumed in silicon. The diamond lattice is assumed to be controlled by a sp3 hybrid. However the electron distribution develops ideally according to the oscillator hypothesis. Only sodium, magnesium, and aluminum exhibit electron vacancies and conductivity. To account for the insulator properties in Si, P, and S in the third period it must be assumed that the four last added p-electrons must be taken up in bands containing only one electron per band.&apos; (Compare the electron band picture in Hume-Rothery.&apos; Hume-Rothery does not consider the insulator properties of the nonmetals.) In the second period already the first p-electron must have entered a single electron band. Based on the energy-band picture in Figs. 6 and 7, the following questions must be asked: 1—Is it consistent with the energy-band idea that electrons of the same kind (p-electrons) can be divided into separated bands? 2—Is it consistent with the energy band idea that single electron bands can exist? 3—Why are the first two p-electrons (in boron and diamond) separated into two single electron bands in the second period, but overlapping in the third period (aluminum)? 4—Why are s-electrons and d-electrons taken up in continuous overlapping bands, while p-electrons are divided into single electron bands? 5—Why do the peaks and valleys (y and w and further x and z) of the energy band below four electrons per atom not show up in the electrical conductivity of alloys? For example consider the Li-Mg system or the alloys between Mg and three electron metals where the mentioned discontinuity in the lattice parameter is found. 6—Why does the beginning of the p-electron band (x) not show up in the lattice constants similar to the filling up of the s-electron band (z) ? In magnesium alloys the electron-gas theory postulates the first Brillouin zone to be filled at about two electrons per atom. This is claimed to explain the sudden change in lattice spacing and c/a values of several magnesium alloys when the electron concentration exceeds a few percentage points over two electrans per atom. This was emphasized in the paper by Busk. If the electron-gas energy-band theory is correct a sudden change in electrical conductivity and possibly other properties .should be expected when the same electron-concentration or temperature is exceeded. A sudden change in lattice spacing or other properties should also be expected when the filling degree is such that p-electrons are introduced into the p-band, for example at x in Figs. 6 and 7. Such phenomena are at found by experiment. and If the number of electrons should vary with the energy level depending on the average number of bonding electrons per atom, the electrical conductivity should be expected to vary in accordance with the energy band layout (Figs. 6 and 7) caused by different numbers of conducting electrons at different filling up degrees. Nothing indicating such a behavior is observed. In addition to these discrepancies between the electron-gas and energy-band theory and measured data, the theory violates the principles developed along with the Bohr theory of atomic structure. According to these principles a filled shell is saturated and therefore unable to form bonds. Therefore two S-electrons per atom should form a closed or saturated shell, which has been pointed out as accounting for the inability of helium to form bonds. Beryllium, magnesium, or calcium atoms with two s-electrons should be expected to form inert atoms with properties almost like the helium atoms. Several other inconsistencies and disagreements with measured data of the energy-band theory can be mentioned. Some of these are discussed with reference to other papers. 8 Because the electron-gas and energy-band theory seems to fail on several points, I have developed another theory which can account for all the phenomena the electron-gas theory is able to account for. This new theory is further able to account for things which are impossible to explain by the electron-gas theory at the present state.

Jan 1, 1953