By J. L. Walter, W. R. Hibbard

A GREAT deal of work has been done on the rolling of single crystals of iron. Barrett and evensoon studied end orientations of heavily cold-rolled iron crystals and found that some crystals maintained a sharp single orientation during rolling. Others rotated into two or more orientations, and some fragmented and approached the entire polycrystalline texture depending on the original orientation of both the normal and rolling directions. Barrett, Ansel, and Mehl2 studied iron-silicon alloys and found that the addition of silicon to the iron had little effect on heavily rolled polycrystalline material. Dunn3 has extensively studied the cold-rolling and recrystallization of silicon-iron single crystals. Dunn found that for single crystals having initial orientation between (110) [001] and (111) [112], the principalcomponent of the cold-rolled texture is (111) [112]. Koh and Dunn4 studied the cold-rolled textures of single crystals having initial orientations in the range (001) [110] to (111) [IT01 and found that these are stable end orientations. They also found that all orientations having a [110] direction parallel to the transverse direction rotate to either the (001) [110] or the (111) [112] stable end orientation except for orientations near (112) [11], which divide and produce a final texture consisting of (001) [110]and (111) [112] components. Crystals having a (111) <112>-type texture re-crystallized to a (120) [001] or (110) [001]-type texture. Crystals having orientations with a range of (001) to (335) in the rolling plane and [110] in the rolling direction recrystallized5 to a wide spread of the initial orientations resulting from a multiplicity of 30-deg rotations about several (110) poles. The present study was undertaken to relate other orientations of crystals of silicon-iron to their cold-rolling and recrystallization textures, so that one might rationalize polycrystalline recrystallization data on the basis of the known deformation texture and the behavior of single crystals in these orientations. PROCEDURE Samples were obtained from a cylindrical ingot of 3 pct silicon iron prepared as follows: Armco iron was melted with high-purity silicon flakes under an atmosphere of argon to minimize oxidation. The alloy was poured into a special mold to form an ingot which consisted partially of large columnar crystals. Plates were cut from the columnar portions of the ingot with the longitudinal direction parallel to the columnar axes and ground to 0.040 in. thick. The plates were heavily etched to a thickness of 0.032 in. to remove the cold-worked surface. Orientations of seventeen crystals were determined by Laue back-reflection techniques keeping the mean columnar axis as the reference direction. The plate was then cut in two, parallel to the columnar axis. One portion of the plate was rolled at room temperature parallel to the columnar axis to a reduction in thickness of 84 pct. The remaining portion of the plate was rolled also at room temperature across the columnar axis to a reduction of 66 pct, at which point the crystals began to separate at the boundaries. After rolling, nine individual crystals were removed from the strip by cutting along the crystal boundaries with a jeweler&apos;s saw. Fig. 1 shows the original orientations of the six crystals that were straight-rolled and of the three crystals (4, 7, and 8) that were cross-rolled. Each rolled crystal was carefully etched to approximately 0.002 in. thick. Textures of the cold-rolled crystals were determined by use of the diffractometer with a non-integrating sample holder. The pole figures were made for the (200) poles using molybdenum Ka radiation and were plotted by an automatic stereographic projection recorder.&apos; Spurious poles were determined by rerunning portions of the pole figures using strontium oxide to filter out the Ka radiation. The central portions of the pole figures have not been determined. The pole figures were completed to about 55 deg from the periphery at which point the sample holder interfered with passage of the beam. Following the determination of the cold-rolled

Jan 1, 1959

By Robert Glass Cleland

FROM the time of its organization down to 1917, a period of more than eighty years, Phelps, Dodge & Co. was seldom involved in what could be called a major labor difficulty. Behind this remarkable record lay both a philosophy and its practical application. The philosophy was an attitude toward society called the Golden Rule. That philosophy had been a living principle in the lives of the founders of the company, Anson Phelps, Daniel James, and William E. Dodge. Their successors, William E. Dodge, Jr., and Daniel Willis James, accepted the same philosophy. Dr. James Douglas governed his life by it. All of these men and their families had given tangible expression to that conviction in benefactions of great magnitude and variety-churches, hospitals, educational institutions, libraries, missionary undertakings, and other organizations for human betterment, such as the Young Men&apos;s and Young Women&apos;s Christian Associations, and the development of model communities about their mills and factories. According to the best standards of their generation, they had sought to improve the condition of labor,

Jan 1, 1952

By R. S. Archer

THE binary aluminum-silicon alloys have certain characteristic advantages which are now well known, and these alloys have come into considerable use during the past several years.1 Their field of application has been limited to a certain extent, however, by their low yield point and hardness, low endurance limit, and relatively poor machining characteristics. These properties are improved by the addition of copper, and the ternary aluminum-silicon-copper alloys constitute an important class. The addition of copper decreases the corrosion resistance of the aluminum-silicon alloys and increases specific gravity. Magnesium is a hardening addition which seems to have relatively little effect on corrosion resistance, and which, of course, reduces specific gravity. The object of the work described in this paper was the development of alloys and heat treatments for the production of sand castings and permanent-mold castings having substantially all the advantages of the binary aluminum-silicon alloys together with mechanical properties improved to a degree permitting wider application.

Jan 1, 1930

By L. Adler

A relatively simple and effective technique is proposed to deal with the failure of geologic masses containing weakness planes. This technique, termed irextended" rupture envelope, provides a means to clearly distinguish rock and soil from fractured rock and, on a theoretical level, considers a matrix-inclusion system. It may also constitute the link between Mohr&apos;s and Griffith&apos;s failure theories. Included in the article are five sample problems concerning site location, structural design, strengthening the plane of weakness, changing the magnitudes of major and minor principal stresses and changing the orientations of major and minor principal stresses. Engineers trying to solve design problems in rock and soil mechanics have often assumed an iso-tropic and homogeneous medium. For naturally occurring geologic masses this assumption has always been viewed with regret. The following analysis which deals with the effects of plane anisotropy on failure presents a solution to this. The planes of weakness are joints, faults, bedding planes, fracture and cleavage (natural and induced), foliation and schistosity. The physical properties of these weakness planes include an undulating surface, frictional resistance, discontinuous extent, filling material, tightness and presence of water to cause a hydrostatic pore pressure. All of these properties relating to failure can be summarized in Mohr&apos;s rupture envelope for the plane of weakness. This, along with the geometrical orientation, strike and dip, of the plane of weakness produces what is termed an irextended" rupture envelope. MOHR&apos;S STRESS CIRCLE AND RUPTURE ENVELOPE The significant features of these concepts are listed below.&apos; 1) A point on the u - r coordinate plane represents the normal and tangential stress components on a reference area in the material. This area can have any orientation. (Fig. la)

Jan 1, 1963

By A. W. Fahrenwald

PRACTICALLY all fine grinding is done in a ball mill or some modification of a ball mill. Millions of tons of material are ground each year. The cost varies from, say, a minimum of 10 c. to a maximum of 35 c. per ton. It is thus obvious that even small improvements, which may result in increased grinding efficiency, would be welcomed by mill operators. A review of literature shows that various phases of the subject have been studied independently by many investigators. Also, it is now a subject of investigation at various laboratories in the United States and in foreign countries. Notwithstanding this extensive investigation, ball milling still remains a subject of some speculation. This paper presents the results of an experimental study of some of the factors entering into ball mill grinding.

Jan 1, 1931

By Eric K. Albert, J. Kiusalaas

The paper presents an overview of SPASID (Kiusalaas and Albert, 1983), a new computer program developed under U.S. Bureau of Mines funding for the prediction of surface subsidence caused by under- ground mining operations. The presentation, which is illustrated with two case studies, also re-evaluates the influence function method as a tool of subsidence prediction, arriving at some rather unconventional recommendations. SPASID consists of four modules that communicate through common data bases: (1) Preprocessor. This module prepares and maintains the database for the entire site. The database contains all the information about the site and the mine operation that is necessary for the computation of subsidence. (2) Subsidence Predictor. The influence function method is used to predict the surface displacements that occur in any portion of the site that occur between two given dates. The computations take into account the time lag between extraction and displacement, and the effects of pitching seams and incomplete compaction at the edges of panels. The program contains i not he&apos;s influence function and the Green&apos;s function of transversely isotropic elasticity theory. (3) System Identification. The purpose of System Identification is to determine the optimal values of the various parameters associated with the influence functions in the Subsidence Module. System Identification requires measurements of subsidence from a site with a sirnilar overburden structure. The values of the subsidence parameters are obtained by minimizing the discrepancy between the measured and computed surface displacements. (4) Postprocessor. The Postprocessor is a graphics facility for displaying the data generated by the other program modules.

Jan 1, 1984

By J. Hudy

An investigation has been made to determine the applicability of the Cendrex X-ray instrument for the measurement of the ash contents of washed bituminous coal products. The results obtained for selected products from five preparation plants in the northern Appalachian region are described. Emphasis of the study was placed on low-ash bituminous coals suit-able for utility or metallurgical markets. There was good agreement between the results obtained by conventional ash determination methods and by the Cendrex for all the products tested. A principal disadvantage of coal in competition with other fuels has been its inconsistent quality, especially with respect to ash content. Mine rnechanization and production from coalbeds of inferior quality have accentuated this failing. Present quality control methods in coal preparation plants are inadequate because (1) control samples taken over a production shift only serve to give the average quality of the product, (2) conventional sampling and analysis data are usually not available at the time a shipment is scheduled, and (3) the plant operator does not have the use of such data when the coal is being processed so that operating conditions may be adjusted for correcting variations in quality. Thus, the development and use of continuous-control monitoring instruments is of prime importance. The Federal Bureau of Mines arranged to investigate an instrument using x-rays for rapid continuous ash determinations. Developed by the Dutch State Mines and first described in 1958,&apos; this instrument, which has found widespread acceptance in Europe, is designed to provide ash analysis of any desired coal feed or product stream with only a five-minute time lag between sample collection and analytical results. With limit controls, this unit could be used to feed back signals to preset the separating gravity of coal washers, control the ratio of various coals needed to produce an acceptable blend, and permit the sorting of a washed product into two qualities, one which is below and the other which is above a prescribed ash content. This unit can also be used discontinuously for rapid determination of coal samples taken in the usual manner. THEORY Di jkstra and Sieswerda of the Dutch State Mines studied the effect of chemical composition and ash content on the absorption coefficient of coal with the transmitted radiation method.&apos; They found that with an X-ray wavelength of 1.79 A and values calculated for the absorption coefficients of ash and combustibles, the absorption coefficient of coal gave a linear relationship when plotted against the ash content. Thus, a method of measuring the absorption coefficient of coal could also be used to measure the ash content. However, practical attempts to measure the ash content of coal by comparing the intensities of the transmitted X-rays failed. The absorption coefficient of coal can also be obtained by irradiating a layer of coal with x-rays and measuring the intensity of the diffused reflection (backscatter method). The relationship between the diffused reflection and the ash content is actually hyperbolic but approximates a straight line over a narrow range. A measuring circuit that balanced the difference in intensity of the reflected radiation from a standard surface against that from a coal sample was used. By plotting this difference of reflected radiation against the ash content, a curve which approximated a straight line over a range of 8 percentage points of ash was obtained. DESCRIPTION OF EQUIPMENT The apparatus performs two distinct functions: (1) the preparation of the sample to a suitable size consist and moisture content for delivery to the x-ray element, and (2) the measurement of the ash content by the x-ray element. In a continuous operation the coal sample is delivered to a conditioner where it is dried to a maximum of 1% surface moisture and pulverized in a high speed mill to -48-mesh. This material is fed, at a rate of 250-300 gpm onto a rotating disk, shown in Fig. 1, where it is mixed with material already present. The mixture is rotated on the disk and

Jan 1, 1969

By J. P. Witherow

Mr. BIRKINBINE&apos;s description of the bad working and sudden chilling of the Warwick Furnace last summer, seems to me quite phenomenal in blast-furnace practice. During my connection with the management of blast furnaces for many years, in the anthracite, cake, and raw-bituminous coal districts, such a me has never come under my notice. It seems to me that the scaffold in the zone of fusion could not have established itself (so that the whole power of the engines, with a blast pressure ranging from 12 to 18 pounds per square inch, could not penetrate), unless the furnace was previously badly scaffolded and bridged in some of its upper sections, from 15 to 30 feet above the hearth level, either in the zone of chemical action or the beginning of the zone of fusion. Such a &apos;barrier to the upward gaseous currents would cause a suspension of combustion which may have superinduced the scaffold that is assumed to have existed in the zone of fusion. It is difficult to conceive that an agglomerated mass almost across the section of the lower bosh should have formed all at once, if the furnace was free and porous for the reaction of the gaseous currents, above. Therefore, I think, the Warwick furnace was by no means in as free, open, and fine internal condition at the time the trouble commenced as the description of its regular working would lead us to suppose. I do not question the accuracy of the statements relative to the output of iron, etc I merely claim that the phenomenta, as described, could not have been almost instantaneously developed, unless there had been an incipient scaffold and lodgment above the zone of fusion. I would state my hypothesis to be that the stock lodged or collected in some of its upper sections during fie process of blowing-in, on which, as a basis, more or less accumulations may .have lodged, and thus, indirectly, caused the formation of the suc-

Jan 1, 1881

By V. O. Struebing, K. A. Johnson, F. H. Ellinger, C. C. Land

The system Pu-Ce-(Pu,Ce)Co2 has been investigated by thermal, micrographic, and X-ray diffraction methods. The principal characteristics of this system were found to be: 1) a "eutectic" valley extending across the phase diagram from the 6 Pu/Pu3 Co eutectic at 408°C to the 7 Ce/Ce24Co11 eutectic at 42Z°C, the maximum temperature in the valley being 443°C; 2) three ternary inter mediate phases, each having an appreciable mutual solid solubility for plutonium and cerium; 3) eleven four-phase equilibria comprising one eutectic, four peritectics, and six Class II reactions; 4) a pseudobinary section between the ternary phase A and the y Ce solid solution, and another such section between the 6 Pu solid solution and the 77 phase (Pu3 CO) containing cerium in solid solution. ALLOYS of plutonium that are completely molten at temperatures in the vicinity of 500°C are of interest for use in the liquid state as fast reactor fuels. Since exploratory work1,2 on Pu-Ce-Co alloys had indicated that a "eutectic" valley extended across the ternary system between the Pu-co[6 Pu/n (Pu3co)] and the Ce-CO[? Ce/? (ce24co11)] binary eutectics, thus allowing alloys of any plutonium concentration to be selected within the temperature limitation, the present investigation was begun for the purpose of accurately defining the "eutectic" valley. However, when the existence of three ternary intermediate phases and the consequent complexity of the liquid-solid equilibria were discovered, the investigation was expanded to cover the complete system, except for the corner between the isomorphous series PuCo2-CeCo2 and pure cobalt. 1) EXPERIMENTAL The purities of the alloy components are given in Table I. Alloy buttons, each weighing about 5 g, were prepared by arc melting the accurately weighed components (±0.1 mg) under a purified He-Ar atmosphere. Weight loss as a result of melting was usually less than 1 part in 1000; therefore, the buttons were not chemically analyzed. One half of each button was re-melted by induction heating in vacuo in a magnesia crucible and furnace-cooled, so as to produce a somewhat coarser microstructure than that of the rapidly cooled arc-melted button. About 20 g of each alloy to be examined by thermal analysis were remelted in vacuo in a tantalum crucible of the inverted thermocouple well type. The thermal, X-ray diffraction, heat treating, and micrographic methods used in this investigation were essentially the same as have been described in earlier reports.3,4 Two etchants for these alloys were found to be satisfactory: A) 8 (parts by volume) orthophosphoric acid, 5 ethanol, and 5 glycol; B) 7 tetraphosphoric acid, 36 water, and 57 2-ethoxyethanol. Etchant A was used at 5 to 6 v for 15 to 20 sec, and etchant B was used at 10 v for 10 sec. 2) THE LIMITING BINARY SYSTEMS 2.1) Plutonium-Cerium. The phase relationships of this system have been investigated by Ellinger, Land, and Cramer,5 and by Selle and Etter.6 The over-all agreement of their phase diagrams is good, but there are some discrepancies in the positions of some phase

Jan 1, 1967

By W. B. Mather

GEOLOGICAL studies have revealed the occurrence of hundreds of pegmatite dikes in north- east Brazil, Fig. 1, in the three states of Rio Grande do Norte, Paraiba, and Ceara. Heretofore data have not been available on the possible production of lithium minerals from these areas, and in March, April, and May 1953 the author undertook a reconnaissance survey covering a cross-section of the pegmatites. Sixty-one pegmatites were examined. The pegmatites of Rio Grande do Norte and Paraiba are located in an arid region (Seratao), and except in the most southerly portion there is a mini- mum of vegetation and overburden. The region is easily prospected and relatively accessible by jeep or truck. The pegmatites examined in Ceara are in an area of lush vegetation along the flanks of the Jaqueribe River valley. It is therefore more difficult to prospect, and the dirt roads, as a means of access, leave much to be desired. For all practical purposes rail transportation, except in Ceara, is not available. The rocks of the area1-4 are composed of Pre-Cambrian schist, gneiss, quartzite, and marbles. They have been intruded by granites, monzonites, and diorites and cut by quartz veins and pegmatites.

Jan 9, 1954

By Howbert Van Dyne

THE Presidio mine of The American Metal Co. of Texas is situated 45 miles south of Marfa, Texas, a town on the Southern Pacific R. R., and lies approximately 20 miles north of the Mexican border. Communication with the railroad is maintained over a state highway. All supplies for mine and mill are hauled in by truck from Marfa and precipitates and concentrates are freighted to the railroad by the same means and shipped to Selby and El Paso, respectively. The mill is at the town of Shafter, 1 mile from the mine and at approximately 350 ft. lower elevation. The ore is conveyed to it by an aerial tramway which requires practically no power on account of the difference in elevation. The mill is a countercurrent decantation cyanide and gravity concentrating plant of 200 tons daily capacity. Coarse and fine crushing are done at the mill. Two near-by shallow wells in the bed of Cibolo Creek furnish an abundance of water. Power is generated for the mill and town by a Diesel engine plant.

Jan 1, 1930

By William L. Grube

PECIMEN preparation for electron metallography involves several steps, such as polishing, etching, replicating, mounting, and shadowing. Although each step must be done with care, the operation requiring the utmost attention is etching. Proper etching is important because the relief pattern developed on the surface of the specimen by the etchant, and reproduced as minute differences in thickness of the replica, determines entirely the amount of detail seen in the final micrograph. The characteristic colored stains, sometimes used in light metallography to simplify identification of certain microconstituents, cannot be tolerated because there is danger of introducing artifacts in the replicating operation. It is also quite difficult to remove plastic replicas from stained specimens. A suitable etchant for electron metallography must, therefore, in all cases exhibit a preferential attack upon each of the microconstituents present sufficient to result in a difference in surface elevation. When only two microconstituents are present, it is not too difficult to find a suitable etchant since their physical or chemical properties are generally sufficiently different to result in a marked difference in attack by the etchant. For example, picral (a saturated solution of picric acid in methanol used as an immersion etch) is a satisfactory etchant for the specimen shown in Fig. 1 consisting of iron carbide particles embedded in a ferrite matrix.&apos;

Jan 1, 1952

By Jos. Van Ackeren

Although the Siemens regenerator principle was introduced into byproduct coke-oven design about 40 years ago, many problems of construction, and particularly of heat distribution and pressure conditions, have not been fully solved. Heat should be applied to the walls of a coke oven in such a way that the coking of the charge of coal will be completed everywhere at the same time, and at approximately the same temperature. This means that the application of heat should be uniform from the top to the bottom of the coal mass (except for the thin layer at the top that is purposely kept at a somewhat lower temperature to reduce cracking of the byproducts); also that a little more heat must be applied to the coke end than to the pusher end, because the coal mass is a little thicker at that end. As a modern coke oven is about 40 ft. long and 12 ft. high, a real problem is involved in the proper application of heat to the oven walls so as to secure quick coking time (without endangering the walls through local overheating) and produce coke made at a uniform temperature. Design of Ovens In all regenerative ovens, the points of combustion are arranged in duplicate sets, one set operating in one-half the area of the heating wall and the other set alternately operating in the other half. Because of the reversal of the flow of gases, the points of maximum and minimum temperatures are alternately located at the same places, thus preventing dangerous local overheating. The practicability of the principle of reversal of flow seems to have been recognized at an early date, and has been applied with every conceivable flue arrangement, combustion chamber, and means of air and gas supply. To summarize the various principles that have proved useful for the control of oven-wall temperature, the best practice seems to have resulted from the acceptance of the use of vertical flues; the separate supply of air and gas to the base of these flues, with the resulting flame

Jan 1, 1923

By Jos. Van Ackeren

Although the Siemens regenerator principle was introduced into byproduct coke-oven design about 40 years ago, many problems of construction, and particularly of heat distribution and pressure conditions, have not been fully solved. Heat should be applied to the walls of a coke oven in such a way that the coking of the charge of coal will be completed everywhere at the same time, and at approximately the same temperature. This means that the application of heat should be uniform from the top to the bottom of the coal mass (except for the thin layer at the top that is purposely kept at a somewhat lower temperature to reduce cracking of the byproducts); also that a little more heat must be applied to the coke end than to the pusher end, because the coal mass is a little thicker at that end. As a modern coke oven is about 40 ft. long and 12 ft. high, a real problem is involved in the proper application of heat to the oven walls so as to secure quick coking time (without endangering the walls through local overheating) and produce coke made at a uniform temperature. Design of Ovens In all regenerative ovens, the points of combustion are arranged in duplicate sets, one set operating in one-half the area of the heating wall and the other set alternately operating in the other half. Because of the reversal of the flow of gases, the points of maximum and minimum temperatures are alternately located at the same places, thus preventing dangerous local overheating. The practicability of the principle of reversal of flow seems to have been recognized at an early date, and has been applied with every conceivable flue arrangement, combustion chamber, and means of air and gas supply. To summarize the various principles that have proved useful for the control of oven-wall temperature, the best practice seems to have resulted from the acceptance of the use of vertical flues; the separate supply of air and gas to the base of these flues, with the resulting flame

Jan 1, 1923

By George Otis Smith

In the utilization of natural resources owner, operator, and consumer* should share the attendant benefits. Development needs to be planned under terms recognizing fully the interests of all concerned, for ally undue advantage given to any one of these participants is apt to involve even greater and disproportionate injury to one or both of the others. For this reason it is well to preface any consideration of needed reforms in legislation affecting the disposition of public land with a survey of certain fundamental principles that determine the general conditions of a11 land transfers preliminary to development, utilization, and production. The disposition of any undeveloped natural resource, whether timber, oil, coal, or water power, as a transaction to which land owner and prospective developer are parties, must be based in theory upon a division of expected returns.&apos; Whatever the terms of such disposition, neither party can reasonably ask for anything other than an equitable division of the returns. Under this analysis three and only three questions need to be discussed; namely, what are those profits, how is this division to be accomplished, and what is the equitable basis of division ? The answer to the third question should probably be found by applying to the problem the principles of theoretical sociology, and the question need not be mentioned further at this time, inasmuch as it does not involve the practical considerations to be kept in mind in connection with the other questions, which are concerned with only the measure of returns and their division. That is to say, whether the land owner&apos;s equity is to be stated as 95 per cent, ox as 6 per cent, of the profits attending the development of the particular resource, no change would be necessary in the method to be adopted of arriving at the closest approximation of the prospective total profit. If on this basis we now compare the two methods of disposing of

Jan 1, 1915

By William Blauvelt

Tun technical and engineering problems in the manufacture of coke are today the problems of the byproduct oven. Except in a few special localities, practically no beehive ovens have been built in the United States for the last 5 or 6 years except as renewals of old plants, and during these years the total number of beehive ovens in existence has been steadily falling. On the other hand, the number of byproduct ovens has increased from 4624 in 1911 to a total of about 7660 in operation at the end of 1917; with 2800 building, this makes a total of about 10,460 which will be in operation in 1918, or shortly thereafter. Preliminary Government estimates place the total production of coke for 1917 at 56,600,000 tons, the largest tonnage in the history of the industry. Of this 34,000,000 tons or 60 per cent. was beehive, and 22,-600,000 tons, or 40 per cent. was byproduct coke. Some time in 1918 the production of byproduct coke should pass the beehive output, and when the byproduct ovens now building are completed the total byproduct capacity will be about 40,000,000 tons of coke per. annum, which is over 70 per cent. of the record-breaking total coke production of 1917. The reasons for these changes in the coking industry are familiar to all of us, and need not be discussed here.

Jan 3, 1918

Robert H. Richards, Boston, Mass.: Mr. Goodale calls attention to the difficulty of obtaining clean tailings from the jigs which are fed by the spigots of the hydraulic separator. This difficulty is universally encountered. The Lake Superior copper mills practically overcome it by running the beds of those jigs loose, carrying into the hutch all of the available copper and some sand. These hutches are again jigged upon threesieve Collom jigs, where the treatment is very slow and gentle; and on the successive jigs lighter and lighter bedding is used. The last sieve is run thin enough to let some sand into the hutch. With these precautions most of the free copper is extracted, as well as a fair proportion of the included copper.

Jan 1, 1897

By J. P. Witherow

MR. BIRKINBINE&apos;S description of the bad working and sudden chilling of the Warwick Furnace last summer, seems to me quite phenomenal in blast-furnace practice. During my connection with the management of blast furnaces for many years, in the anthracite, coke, and raw-bituminous coal districts, such a case has never come under my notice. It seems to me that the scaffold in the zone of fusion could not have established itself (so that the whole power of the engines, with a blast pressure ranging from 12 to 18 pounds per square inch, could not penetrate), unless the furnace was previously badly scaffolded and bridged in some of its upper sections, from 15 to 30 feet above the hearth level, either in the zone of chemical action or the beginning of the zone of fusion. Such a "barrier to the upward gaseous currents would cause a suspension of combustion which may have superinducedd the scaffold that is assumed to have existed in the zone of fusion. It is Difficult to conceive&apos; that an agglomerated mass almost across the section of the lower bosh should have formed all at once, if the furnace was free and porous for the reaction of the gaseous currents above. Therefore, I think, the Warwick furnace was by no means in as free, open, and fine internal condition at the time the trouble commenced as the description of its regular working would lead us to suppose. I do not question the accuracy of the statements relative to the output of iron, etc. I merely claim that the phenomena., as described, could not have been almost instantaneously developed, unless there had been an incipient seaffold and lodgment above the zone of fusion. I would state my hypothesis to be that the stock lodged or collected in some of its upper sections during the process of blowing-in, on which, as a basis, more or less accumulations may .have lodged, and thus, indirectly, caused the formation of the suc- * This paper was not presented to the Institute in its present form, but is based on remarks, in discussion, by the author on Mr. Birkinbine&apos;s paper on, a Short Blast at the Warwick Furnace, and Mr. Witherbee&apos;s paper on Two Scaffolds at the Cedar Point Furnace.

Jan 1, 1881

By Bror Nordberg

SAND and gravel are unconsolidated granular materials resulting from the natural disintegration of rocks. The two materials nearly al- ways occur together, variably proportioned in widely available de- posits. A commercial sand comprises the fine granular material, usually less than f in. in diameter (ASTM Designation C58-28), and gravel consists of the coarse, granular material larger than sand (ASTM Designation C125-46T). Gravel falls within the range of 1/4 in. and a top size usually of 3 ½ in. Chemical definition is impossible. Sand and gravel are always of secondary origin. They were formed from various massive rocks through the action of chemical and mechanical forces; then transported, abraded, washed, sorted, and classified by streams, glaciers, waves, or winds, to be redeposited in beds as they are found. Chief disintegrating forces in the reduction of rocks into granular particles were frost, rain, the dissolving action of acid and alkaline ground waters, the mechanical action of streams and waves, and the action of glaciers. Method of formation and deposition have imparted physical properties to sands and gravels that largely determine the commercial value of the materials for particular use and influence the manner of exploitation. In the early days of the commercial industry, purchasing specifications were relatively lenient but in. the past decade much more rigid quality requirements have had to be met for acceptance by all classes of purchasers. The trend to further severity in requirements is a challenge to the industry that commands full knowledge of the nature of raw materials at hand and skillful application of processing into commercial products. Mechanical strength, the ability to resist disintegration, chemica

Jan 1, 1949

Joseph K. Stone, Jr. (Kaiser Engineers, Oakland, Calif.)—I would like to compliment the authors on their clear presentation of the results of their study of the pneumatic processes. We hope that the Inland Management decision to make this information available to all will induce others to release additional valuable fundamental data which they have accumulated in the field. There are two points upon which we would like to comment. In the discussion of Table VII it was indicated that the "oxygen consumptions were about the same as has been reported for other oxygen steelmaking processes". This conclusion is apparently based upon the consumption of 2100 cu ft per ton shown in Table VII. The data in Table IV also permits calculation of 2520, 2280, 2250 and 2700 cu ft per ton in heats 1 to 4, respectively. These figures are in the same general range as those reported for the Kal-Do and Rotor Processes using Thomas iron, but considerably above the following figures for four of the operating L-D Process Plants while using iron which is similar to American basic iron: Donawitz 1760 cu ft per ton Adapted from Cuscoleca&apos; LinZ 1900 cu ft per ton Trenkler & Hauttmann2 Dofasco 1850 cu ft per ton D. O. Davis:3 In addition to the differences between the consumption of gaseous oxygen in the Inland operation and in the L-D Process, there is another closely related difference. The L-D plants for which data are cited are using approximately 1 pct ore while the authors&apos; process used about 7 pct of sinter. Assuming 65 pct Fe in the sinter, the difference amounts to 400 to 500 cu ft

Jan 1, 1959