By Louise B. Freeman

Kentucky for the first time in its oil history passed the 10 million barrel mark. Of the total 10,019,641 bbl., 8,262,516 bbl. were produced in Western Kentucky, and Union County surpassed all others, with 4,056,142 bbl., or 40 percent of all the production for the state. There were 930 wells known to have been drilled during the year; 510 in Western Kentucky and 221 in the gas-producing area of Eastern Kentucky.

Jan 1, 1946

By John Birkinbine

This piece of Carpenter crucible steel has exhibited a tensile strength of 116,000 pounds per square inch, an elastic limit of 89,170 pounds, an elongation of 25 per cent., and a reduction in area of 42 per cent. The test-specimen had a length of 2 inches between fillets, and was an inch bar reduced to an area of 0.504 square inch. This unusual tensile strength was determined before the bar had been hardened so as to show the remarkably velvety fracture here exhibited; but a piece of the same, tested after hardening, is reported to have stood a stress of 214,000 pounds per square inch. Another test-piece is said to have shown 136,000 pounds tensile strength, 97,300 pounds elastic limit, 20 per cent. elongation in 2 inches, and 40 per cent. reduction of area. Mr. Carpenter claims that this steel, containing 2.27 per cent. chromium and 1.04 per cent. carbon, can be welded like iron, and has proved most desirable,for the highest class of die-steel.

Jan 1, 1895

By F. S. Crawford

IRON and copper are mined in the Lake Superior district. The iron mines of the district have the best safety record for that industry in the country as a whole, while the copper mines of the district rank second in two of the four years recorded (Table 1). In Utah copper comes mainly from open-pit mines, which enables that state to lead easily in safety. All of the Michigan production comes from deep under-ground workings. About 60 per cent of the iron miners in St. Louis County, Minnesota, are employed at open-pit mines; this favorably affects the combined open-pit and underground accident-frequency rate, as this county pro-vides most of the Minnesota-mined iron ore. In Michigan, however, there are few open-pit mines, the bulk of the production coming from underground mines, while all of the Wisconsin production, just across the state line from Michigan, is from underground mines. In spite of the fact that fewer mines in Michigan use the safer open-pit method, the iron-mining industry of that state maintained a consistently low record from 1931 to 1934; however, it was many points behind its nearest com petitor, Minnesota, with its much greater production from open-pit mines.

Jan 1, 1939

By Robert H. Hafner, Irvin R. Kramer

In recent years considerable interest has been shown in surface-alloyed metals, particnlarly those of chromium (chromized steels), which have excellent corrosion resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high tem- peratures of 1200º to 1400ºC. (2200° to 2550°F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- mon salt, and heated for approximately three hours at 930º to 1040°C. (1700º to 1900ºF.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900º to 1000ºC., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a Chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1943

By Robert H. Hafner, Irvin R. Kramer

In recent years considerable interest has been shown in surface-alloyed metals, particnlarly those of chromium (chromized steels), which have excellent corrosion resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high tem- peratures of 1200º to 1400ºC. (2200° to 2550°F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- mon salt, and heated for approximately three hours at 930º to 1040°C. (1700º to 1900ºF.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900º to 1000ºC., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a Chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1943

By Robert H. Hafner, Irvin R. Kramer

IN recent years considerable interest has been shown in surface-alloyed metals, particularly those of chromium (chromized steels), which have excellent corrosion [ ] resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method' employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high temperatures of 1200° to 1400°C. (2200° to 2550 F.) caused excessive grain growth and warpage. Louenstein and Ulmer2 packed iron castings in ferrochromium and com- [ ] mon salt, and heated for approximately three hours at 930° to 1040°C. (1700° to 1900°F.). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900° to 1000°C., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a chromized layer, 0.004 in. thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1942

By D. G. Westlake

Alloys of poly crystalline Nb-H have been tensile tested at 77" and 120°K after slow-cooling and after quenching from room temperature. A rationale has been developed to explain the effect of cooling rate on ductility in terms of microstructure. The inferior ductility of the slow-cooled alloys in this temperature range can be attributed to the precipitation of coarse hydride particles that fracture in the early stages of plastic deformation. Quenching Produced much smaller hydride particles and a decreased tendency for initia-tion and popagation of cracks. Prismatic dislocation loops, punched into the matrix of quenched alloys, eliminate the yield point and may Play some role in the low temperature ductility of the quenched alloys. The difference in ductility between quenched and slow-cooled V-H alloys was even greater than that observed in the N b-H alloys. It is well known that the ductility of Nb-H and V-H alloys decreases with increasing hydrogen concentra-tion and with decreasing temperature.1-l1 The follow-ing are some of the numerous mechanisms that have been adopted in attempts to explain these observations: 1) hydrogen-dislocation interarction,4'6 2) lowering of the crack surface energy by adsorbed hydrogen,9'10 3) localized lowering of the niobium bond strength,9 and 4) exertion of pressure inside voids by molecular hydrogen.6 A recent study1' indicates that, in some way, the embrittlement is related to the precipitation of a hydrogen-rich phase, because embrittlement and hydrogen solubility have the same temperature dependence. Most of the investigators observed that at very low temperatures there was a return of the ductility. Thus, hydrogenated niobium and vanadium may be said to exhibit a low temperature ductility minimum."1'8'9 It has been reasoned by most observers that diffusion is required for the embrittlement mechanism to be operative, and that as hydrogen becomes immobile at very low temperatures, the ductility increases. This investigation of the mechanical behavior of Nb-H al-loys under various conditions is an attempt to gain a better understanding of the low temperature ductility minimum. EXPERIMENTAL Tensile specimens, with gage length dimensions 20 by 3 mm, were machined from sheet stock" and both faces were ground on wet 600 grit Sic paper to obtain a final thickness of 0.5 mm. Annealing as described earlier12 resulted in average grain diameters of 0.3 mm. The recrystallized niobium tensile specimens were electropolished in 90 parts H2S04, 10 parts HF (48.9 pct) by volume, at 287°K and 30 v. Hydrogen, which may have been present in the starting material and/or added during specimen preparation, was removed by annealing at 1073°K in a dynamic vacuum of 2 X 10-6 torr. Hydrogenated specimens (1.15 at. pct H) were prepared by reaction with a known quantity of pure hydrogen (obtained by thermal decomposition of UH3) at 1073oK, followed by cooling at the rate of 100" per hr. These were vacuum encapsulated, homogenized at 573°K for 3 to 5 hr, and furnace-cooled. Tensile tests were conducted on an Instron machine at a strain rate of 4 x l0-5 per sec. The gripping device was such that the specimen was positioned below the crosshead. Thus, subambient test temperatures could be obtained by immersion of the device in a cooling bath of either liquid nitrogen or Freon-12. The temperature of the Freon-12 was controlled within ± 0.1°K of the desired temperature by automatically monitoring the flow of liquid nitrogen through a copper coil in the bath. Slow-cooling to 77°K was accomplished as follows. The testing device was surrounded by a rubber jacket, open at the top and with small holes in the bottom. Liquid nitrogen, brought up to the bottom of the jacket, entered the holes and vaporized quickly. The temperature was monitored at the specimen with a copper-constantan thermocouple, and a constant cooling rate of 2 deg per min was easily achieved by controlling the level of the liquid nitrogen outside the jacket. RESULTS AND DISCUSSION Low Temperature Ductility Minimum. Resistometric studies of both Nb-H12 and V-H13 indicated that at tem-peratures less than 150°K, virtually all of the hydrogen

Jan 1, 1970

By Tasuku Fuwa, John Chipman

Equilibrium data on the reactions of gases with carbon and oxygen dissolved in liquid iron are reviewed and correlated. A source of error in oxygen analysis of graphitic samples is exposed. New experimental data on the oxygen content of high -carbon iron in equilibrium with carbon monoxide indicate that the activity coefficient of oxygen is decreased by additions of carbon. The carbon-oxygen product decreases slightly with increasing carbon content. In recent years a number of investigations have been reported dealing with the equilibria between carbon and oxygen in liquid iron and gases containing carbon oxides. The laboratory study of these reactions dates back to 1931 with the publication of a paper by Vacher and Hamilton' on "The Carbon-Oxygen Equilibrium in Liquid Iron". The principal object of this study was to obtain data on the reaction shown by Eq. [3] below; their data and others by vacherZ permit evaluation of the other equilibrium constants as well. Subsequent studies have been reported by Matoba, Phragmen and Kalling and by Marshall and Chipman.5 The equilibria may be expressed by the following three equations: C + CO,= 2CO;Kl = Pc° [1] 0-+CO = CO,;K2=-P co, "0.PCO c + O = CO; K3 = In the equilibrium constants, ac and a0 are taken as equal to [% C] and [% 0] respectively in the infinitely dilute solution. At finite concentrations an activity coefficient is introduced such that ac =fc [%C], and so forth. It is to be noted that these equations represent only two independent relations, the third being derivable from any two. Richardson and Dennis have determined the conditions of equilibrium in reaction [I] at temperatures of 1560" to 1760°C. Their results have been confirmed by Rist and chipman7 who have shown how the data may be extended to cover the entire range of liquid compositions at temperatures from the eutectic up to 1760°C. An approximate confirmation has been reported by Fuwa and chipman.' These investigations also established the activity coefficient of carbon which was shown to increase rather rapidly with increasing concentration. For the very dilute solutions the value of Kl is expressed in the equation: log^i = - 7280/T+ 6.65 This equation leads to a value of Kl = 430 at 1540° C in excellent agreement with the average value of Marshall and Chipman.5 It is shown as line 1 in Fig. 1 together with the experimental observations. In the case of reaction [2] the direct experimental results can be supplemented by observations on the corresponding reaction with hydrogen, namely reaction [4]:

Jan 1, 1961

By A. G. Metcalfe, A. Siede

The hardening of annealed copper during fatigue testing appears to be independent of the applied stress and to occur largely within the first 4000 cycles. Copper hardened by fatigue is more resistant to annealing than copper hardened by static means, and softens by a multistage process. Creep studies at 300°C show that copper hardened by fatigue also has greater resistance to creep than statically hardened copper. Some theoretical explanations are discussed. RECENT interest in the behavior of metals subjected to fatigue stems from observations of phenomena which could not be explained by current theories of the structure of metals. In 1953 Bullen et al.l showed that the hardening caused by fatigue at low stresses did not cause severe bending of the lattice as did hardening by static methods. This was later confirmed by Wood, 'and Broom and Ham.3 Clarebrough et al4 showed that as the stress level used in fatigue hardening was increased, bending of the lattice was introduced, eventually approaching that of metals deformed by conventional cold-working methods. The type of hardening introduced by fatigue has other interesting characteristics. Kemsley5 showed that copper fractured by fatigue at low stresses resisted annealing as compared to copper hardened an equal amount by static means. The work of Clarebrough etal, shows that the manner of energy release during annealing differs for fatigue-hardened and statically hardened metal in both magnitude and temperature range of release. In addition to hardening of the lattice, fatigue has been shown to cause softening in materials previously hardened by static methods,5 and also in age-hardened alloys.7 The superposition of a small fatigue stress on the static loading of high-temperature alloys has been shown to increase their resistance to creep.' The present work was an attempt to determine the relationship between fatigue hardening, resistance to annealing, and the creep properties of pure copper. EXPERIMENTAL PROGRAM The program described here was designed to answer three questions: 1) Can stress-cycle combinations well below the failure values give significant increases in hardness? 2) Does hardening, under different stress-cycle combinations, give increase resistance to annealing? And if so— 3) Does superior resistance to annealing confer superior creep properties over statically hardened material? Three-quarter hard OFHC copper was annealed in vacuo at 550°C for 1 hr to produce a strain-free material having a fine grain size and uniform hardness. (The standard deviation of the mean hardness of the annealed samples was less than + 1.9 Dpn). Annealing was performed after machining the fatigue specimens so as to avoid work-hardened surfaces. Jigs were used to avoid distortion. The fatigue properties of the annealed copper were determined using an accurately aligned Baldwin-Sonntag SF1-U machine operating at 1800 cycles per min. This limited the minimum number of cycles which could be examined to about 4000 stress reversals. Since failure resulted in specimen damage, hardness increase with number of cycles was measured by testing specimens fatigued to different fractions of the failure values. The results are shown in Fig. 1, and are superimposed on the S-N curve of the copper in Fig. 2. The resistance to annealing of fatigue-hardened material was compared to that of material hardened by uniaxial tensile straining. Specimens hardened to equal values by both methods were progressively annealed for 1 hr at temperature in vacuo. After each annealing treatment the hardness was measured using a Leitz Durimet hardness tester with a 500-g load. At least five tests were made for each hardness determination. The standard deviation for individual specimens varied from 0.26 to 1.48 hardness points. The results are shown in Figs. 3 to 5. The discontinuous nature of the annealing process has been brought out by drawing idealized curves through the data points. This can be justified by the consistency of the results as well as by general agreement with results of Kemsley.5 The creep resistance of fatigue-hardened and

Jan 1, 1960

By H. D. Outmans

The author applies the theory of hydrodynamic stability to fluid flow in porous media and concludes that the displacement of miscible liquids is stable if the stability coefficient, as defined by Eq. 19.2 or Eq. 27.0, is positive. The conclusion is invalid, however, since it is based on a faulty argument. To demonstrate this, the reader is referred to Eqs. 4.1 through 4.5 of the paper which describe, in differential form, the first-order disturbances c, u, v, w and p. In these same equations, cx, cz, gl, g3 and are functions of the stable concentration c. This concentration c is known and depends on x, z and t (the author assumes cy = 0). It follows that cx, cz, gl, g3 and µ are also functions of x, z and t. With this in mind, we turn to Eqs. 8.1 through 8.5 which were derived from Eqs. 4.1 through 4.5 by substituting Eq. 6.0. The significance of this substitution is that the author thereby limits the solutions of Eqs. 4.1 through 4.5 to equations of the form of Eq. 6.0. Eqs. 8.1 through 8.5 represent an infinite linear system with five unknowns: c, u, v, w and p. The coefficients cx, cz, gl, g3 and µ in this system are known at each point and at each instant; the coefficients containing derivatives of f are unknown. If this infinite linear system in c, u, v, w and p is to have a nontrivial solution, then it is indeed necessary (as the author states) that the determinant of the coefficient matrix of Eqs. 8.1 through 8.5, i.e., ( A 1, be equal to zero. This condition, however, is not sufficient. A non-trivial solution exists if, and only if, the rank of the coefficient matrix of the entire infinite system is smaller than five. In other words. all minors of order five must vanish and only if all the coefficients in Eqs. 8.1 through 8.5 are constant is this equivalent to the condition |A| =0. Constant coefficients means that gl, g3 and µ, for instance, are constant; and, since they depend on c it follows that c must be constant. We conclude that the condition I A I = 0, on which the author bases his calculations, is necessary and sufficient for a nontrivial solution only if the concentration c is constant. In other words, the author does not investigate the stability of a miscible displacement but, rather, only the stability of the flow of a homogeneous liquid. Using the initial condition and the fact that the coefficients are constant, we find

By A. E. Zawadzki

A progress report is presented on the development of a process for the removal of sulfur dioxide from flue gases. Catalytic oxidation of the sulfur dioxide in flue gases, with the production of recoverable sulfuric acid, has been demonstrated to be technically feasible. Problems associated with the process are discussed. The need for an inexpensive and efficient process for controlling sulfur dioxide emissions from utility plant stacks has been accentuated by the ever-increasing public demand for elimination of all man-made air pollutants. I would like to describe the results of an investigation of the development of such a process; more important, I would like to present a discussion of the problems associated with the process which remain to be solved. The research work on the BCR catalytic gas phase oxidation process has been jointly sponsored by the Association of Edison Illuminating Cos., Edison Electric Inst. and Bituminous Coal Research, Inc., since 1958. However, work on SO2-pollution abatement was initiated by BCR in 1953. Tieman and Clymer,1 working with ozone and simulated flue gases, evaluated a gas phase oxidation process for removing SO2 from flue gases. Their experimental data indicated that the use of ozone to oxidize SO2 in flue gas concentrations, with subsequent recovery of H2SO4, did not appear to be economical due to the large ratio of ozone to sulfuric acid produced (2.6 to 1). The cost of the ozone would be 6 to 10 times the cost of sulfuric acid produced. As a result of the ozone study, work on a catalytic oxidation process was developed. The following reactions are the basis for the catalytic oxidation process Reaction [I] normally occurs in the combustion of sulfur-bearing fuels. At the high temperature found in the combustion chamber, 95% to 99% of the sulfur in the fuel is oxidized to SO2 and 1% to 5% is oxidized to SO3. The concentration of SO2 in the combustion gases depends on the combustion efficiency and the quantity of excess air used. A commonly used rule of thumb is 0.1 percent by volume SO2 in the flue gas for each 1% sulfur in the fuel. Reaction [2] proceeds at a wide range of temperatures. The rate of the reaction is rapid above l,000°F; however, the equilibrium conversion drops rapidly above this temperature. 2 Reaction [3] occurs rapidly to completion at temperatures below 400°F; above this temperature some SO3 exists in equilibrium with H2SO4. Complete dissociation of H2SO4 occurs above 650°F.3 The simplicity of the proposed process provided added incentive to the development and evaluation of the various component unit operations. The advantages of the process were considered to be as follows: 1) no raw materials were required, 2) the unit operations were not radically new; and 3) a salable product, sulfuric acid, would be produced. The successful development of the process was contingent upon the solution of several major problems: 1) The development of a catalyst which would provide high catalytic activity at reasonable conditions of gas flow and temperature without causing an unacceptable increase in pressure drop. 2) The development of a high temperature dust collection system to provide clean flue gases to the catalytic reactor. 3) The complete recovery of the sulfuric acid produced in the process; the effluent gas must contain less than 20 ppm by volume of sulfuric acid. As of this date, the complete solution to these problems has not been achieved. EXPERIMENTAL Catalyst Development: The use of platinum and vanadium catalysts for the production of sulfuric acid by the treatment of dry gases containing 5% to 20% by volume sulfur dioxide has been known for many years. The application of the basic idea of catalytic oxidation of sulfur dioxide in flue gas concentrations was

Jan 1, 1965

By H. F. Yancey, M. R. Geer, C. L. Allyn, R. H. Eckhouse

W. M. Bertholf—This is an excellent report of a well-conducted investigation, of sufficient scope to provide generally useful information. Some years ago we had occasion to test the Humphreys spiral on the middling from our table plant. The conclusions reached in this investigation come as no surprise to us. In certain applications it is virtually impossible to improve on the spiral from the monetary returns point of view even though its "efficiency" may be low. We have noted that in all successful applications of the spiral the feed is "classified," hence we were somewhat disappointed in the showing the spiral made on the Poplar Ridge coal, the only one of the four which could really be considered the equivalent of a classified feed. As was noted in the paper, however, this coal contained a considerable amount of middle and high-gravity material, apparently more than enough to make up for the theoretical advantage of small particles in these categories. A comparison of particle size in the various specific gravity classes of the four coals is given in table XXV. Table XXV. Comparison of Particle Size in Various Specific Gravity Classes. (Unit size, 150 m to 0.105 mm) Black Eagle Clements Poplar Ridge Rosly,n 1.3 Float 7.47 10.60 8.68 9.66 1.3 x 1.4 7.89 7.96 7.58 8.20 1.4x1.6 7.24 8.36 5.58 6.85 1.6 x 1.8 7.98 8.31 3.42 7.33 Sink 1.8 7.85 7.13 5.09 7.41 Avg 7.69 10.08 7.15 8.38 This tabulation indicates that there was very little difference in the size of the various gravity fractions for three of the coals, Poplar Ridge varying the most. Examination of figs. 3, 6, 7, and 8 reveals a general similarity of behavior for all coals except Black Eagle. Would the authors care to speculate on the reasons for the difference in the distribution curve for the sink 1.60 material in the washed coal of fig. 3 as compared to the others? This difference is particularly noticeable in the 8xl4-mesh size. Was there a "shape effect"? J. D. Price and W. M. Bertholf—The performance data on three of the coals studied appear to be typical, but there are certain departures from the general pattern in the case of the Poplar Ridge coal which are large enough to deserve special consideration. For example: 1. Despite the high proportion of sink 1.60 material in the feed, it was not possible to make a corresponding proportion of high-ash reject. (See table XVI.) 2. Even though approximately 70 pct of the feed was 1.40 float with an ash content of 6.6 pct, and this

Jan 1, 1951

By R. H. Eckhouse, M. R. Geer, H. F. Yancey, C. L. Allyn

W. M. Bertholf—This is an excellent report of a well-conducted investigation, of sufficient scope to provide generally useful information. Some years ago we had occasion to test the Humphreys spiral on the middling from our table plant. The conclusions reached in this investigation come as no surprise to us. In certain applications it is virtually impossible to improve on the spiral from the monetary returns point of view even though its "efficiency" may be low. We have noted that in all successful applications of the spiral the feed is "classified," hence we were somewhat disappointed in the showing the spiral made on the Poplar Ridge coal, the only one of the four which could really be considered the equivalent of a classified feed. As was noted in the paper, however, this coal contained a considerable amount of middle and high-gravity material, apparently more than enough to make up for the theoretical advantage of small particles in these categories. A comparison of particle size in the various specific gravity classes of the four coals is given in table XXV. Table XXV. Comparison of Particle Size in Various Specific Gravity Classes. (Unit size, 150 m to 0.105 mm) Black Eagle Clements Poplar Ridge Rosly,n 1.3 Float 7.47 10.60 8.68 9.66 1.3 x 1.4 7.89 7.96 7.58 8.20 1.4x1.6 7.24 8.36 5.58 6.85 1.6 x 1.8 7.98 8.31 3.42 7.33 Sink 1.8 7.85 7.13 5.09 7.41 Avg 7.69 10.08 7.15 8.38 This tabulation indicates that there was very little difference in the size of the various gravity fractions for three of the coals, Poplar Ridge varying the most. Examination of figs. 3, 6, 7, and 8 reveals a general similarity of behavior for all coals except Black Eagle. Would the authors care to speculate on the reasons for the difference in the distribution curve for the sink 1.60 material in the washed coal of fig. 3 as compared to the others? This difference is particularly noticeable in the 8xl4-mesh size. Was there a "shape effect"? J. D. Price and W. M. Bertholf—The performance data on three of the coals studied appear to be typical, but there are certain departures from the general pattern in the case of the Poplar Ridge coal which are large enough to deserve special consideration. For example: 1. Despite the high proportion of sink 1.60 material in the feed, it was not possible to make a corresponding proportion of high-ash reject. (See table XVI.) 2. Even though approximately 70 pct of the feed was 1.40 float with an ash content of 6.6 pct, and this

Jan 1, 1951

By J. L. Brimhall, R. A. Huggins, M. J. Klein

IN a recent paper1 it was shown that small additions of magnesium, copper, and oxygen decrease the stacking fault probability in plastically deformed silver. Correlation of :X-ray data with measurements of the twinning frequency and metallographic observation of slip lines indicated that this effect may be due to an increase in the relative stacking fault energy. It is the purpose of the present note to report experiments on these alloys of known stacking fault probability that relate to the stacking fault contribution to electron scattering in silver. There has been a considerable amount of disagreement in the literature concerning the contribution of dislocations to electrical resistivity in metals. Calculations relating to the scattering of conduction electrons by the dislocation core, its strain fields, and related effects have been made by several authors.2-5 In addition, experimental work on Cu,3,6-10 Ni,11 and Ni-Co alloys1:! has shown that dislocations in those materials exert an anomalously large effect on resistivity, this effect being related to the presence of extended dislocations. The problem of the scattering due to the stacking fault region between partial dislocations has been treated theoretically using several different procedures.13-'0 The results of these calculations show a wide range of predicted values, from rather large to completely negligible, due to the models and the approximations involved. Almost all of this work has been applied to the specific problem of scattering in copper. The more complete theoretical treatments depend rather critically. on the shape of the Fermi surfaces and the effective mass parameters. The scattering from stacking faults might therefore be expected to vary significantly from one metal to another. Unfortunately, sufficiently accurate information is not available .which would allow one to have any confidence in a theoretical prediction of the scattering in the case of silver. Resistivity measurements were made on small wire specimens of vacuum melted high purity silver and several dilute alloys. These measurements were made at approximately 20°C, with great care being given to temperature measurement and corrections. At such temperatures phonon scattering is significantly greater than imperfection scattering. However, the experimental technique was such that measurements on similarly treated samples were reproducible to better than 2.4 X 10-9 ohm-cm, which was satisfactory for this work. Values of the stacking fault probability and the increase in resistivity after severe plastic deformation are given in Table I. The increases in resistivity resulting from plastic deformation agree quite well with previous work on silver.14,21-26 In addition, it has been previously found that interetitials and vacancies in silver anneal out well below room temperature, so that the residual imperfection scattering in these experiments could be expected to be primarily associated with dislocations;. It is seen from the data in Table I that large changes in stacking fault probability are accompanied by differences in resistivity due to imperfection scattering of only a few percent. If the scattering of conduction electrons by extended dislocations is primarily due to the area of the stacking fault region independent of the stacking fault energy, and not the core and strain fields associated with partial dislocations, the resistivity increase should be proportional to the product of the dislocation density and the stacking fault width, as is the stacking fault probability. Therefore, the imperfection scattering caused by plastic deformation of the alloys should be considerably smaller than that found in the pure silver. Since this was not observed, these results sugegest the possibility that stacking faults do not themselves contribute appreciably to the electrical resistivity of silver deformed at room temperature. An alternative explanation of these observations is that the scattering by the stacking fault is roughly proportional to the stacking fault energy, rather than being determined by the total area of such faults. Sufficient evidence is not yet available to separate these two possibilities. This work was supported by the Office of Naval Research.

Jan 1, 1962

By J. B. DILWORTA

Ix estimating the investment-value of a mining-property or plant, the value of which decreases with operation, it is often necessary to know the sum which must be set aside periodically from earnings either to renew the plant at the end off its life, or to return the capital involved when the earning-power of the investment has ceased. In such cases it is manifestly incorrect simply to divide the total amount to be retired by the number of periods (usually years) during which the investment shall be active, as the sums periodically withdrawn have a certain interest-earning power varying with the length of time they are held and with the opportunities afforded for their investment. But though the interest may be considered to accumulate regularly year by year, yet the rules and tables for compound interest do not apply, owing to the addition of a fixed amount of new money to the total at the beginning of each period. Briefly stated, the problem of sinking-funds is, to find the amount of money which must be periodically set aside at a certain rate of interest, regularly compounded, to yield a certain sum in a given, length of time. In most practical cases the interest is compounded and the fresh amount added at the same time-usually once a year-and on this basis the problem may be solved as follows

Nov 1, 1909

By C. F. Jackson

THE work of, the Mining Methods Committee is now well under way. Following discussions previous to and during the February meeting, an Outline for Papers on Mining Methods was prepared, and over a thousand copies have now been distributed to committee men, to section secretaries and to members who have indicated any interest in the subject. The objective of the committee is to prepare a symposium on mining methods which will be of real practical value to the operator and engineer in the solution of every-day mining problems. It is planned to cover the entire field of mining in such a way that the different branches of mining, such as coal and ore (iron, copper, lead, zinc and precious metal) can benefit from the experience of the others at points where they have problems in common.. It is realized fully that each of these branches of mining possesses its own peculiar problems, but at the same time, there are prob-lems in connection with each, where the experience in others should be of value. The committee proposes to proceed along the following lines: 1. To present a general classification of mining methods, showing their inter-relationship, and at the same time .provide a common language for the discussion of mining methods and a nomenclature that will have the same meaning wherever used. A com-plete set of illustrations will accompany the classi-fication to make clear the terminology adopted and to show graphically the inter-relationship of methods. 2. To show the relationship between the physical characteristic of the deposit, the economic consider-ations and the. mining method., It is not proposed to treat this subject as a mere academic problem, but to secure reports from every mining company of impor-tance in this country, which will show what methods or modifications and combinations of methods have actually been applied and the physical conditions and economic considerations which have led to the adoption of these methods in each case. The Mining Methods Committee has drawn up an Outline for Papers on Mining Methods to be distributed among mining engineers and operators, giving in detail the information desired. This outline is the result of several months of careful thought and is a composite of the suggestions of many engineers and mining company officials from all parts of the United States.

Jan 7, 1922

By Pedro Bolsaitis, Paul M. Sullivan

The activities of zinc in liquid Zn-A1 alloys in the temperature range of 1000' to 1160°K were determined by means of the isopiestic technique. The results are in reasonable agreement with the previous values determined by the radioactive tracer dew point method. Slightly negative excess entropies of mixing were found. The measured activities suggest that the a function for these alloys is not a constant, as has frequently been assumed, but is better represented by two straight line segments of different slopes. THE thermodynamic data of Al-Z alloys have been the subject of investigation by many authors. However, in the recent compilation of such data by Hult-gren et al.,5 the conclusion is reached that none of the previous measurements are reliable or consistent with each other. Since then two new sets of measurements have been reported,2, 8 both laying claim to good accuracies, yet showing very significant disagreement in the measured activity coefficients of zinc in Zn-A1 alloys and in the magnitude and sign of the excess entropies of mixing. Information on the thermodynamics of the system is of particular interest for interpreting results of the Bureau of Mines research on refining of zinc by distillation of die cast scrap. The present study was undertaken as an independent check on the recent values obtained from dew point measurements 8 and electromotive force measurements.' The isopiestic method, first introduced by Herasy-menko,' was chosen because it is one of the few thermodynamic techniques which, in principle at least, is carried out under perfect equilibrium conditions. The disadvantage of the method is that data are obtained at various random compositions and temperatures, which makes the interpretation somewhat cumbersome. The random errors arising from temperature gradients and fluctuations appear to be comparable to those of other techniques, as evidenced by the magnitude of the estimated uncertainties in the calculated integral thermodynamic quantities. An advantage of the method is that each run provides a relatively large amount of data; thus, it is less time consuming than those methods where samples of each composition must be measured individually. EXPERIMENTAL PROCEDURE The activities of zinc in liquid Zn-A1 alloys were measured by the isopiestic method which uses the principle of the tendency toward equilibrium of a series of samples at various temperatures under an imposed vapor pressure of the more volatile component (i.e., zinc, in this case). The basic apparatus is shown in Fig. 1. The small graphite crucibles that contained the metal samples were 15 mm ID and 13 mm deep with approximately 3 mm wall thickness. Each crucible was notched at the top and bottom to allow easy passage of vapor from one to another. At the beginning of an experiment each crucible was weighed on an analytical balance. Zinc and aluminum of spectrographic purity (99.999 pct) were then weighed into the crucibles. The amounts of each metal added were such that initial compositions varied above and below equilibrium values. One crucible contained only pure zinc. After weighing, the crucibles were stacked with the pure zinc on the bottom (corresponding to the lowest temperature in the furnace) and richest aluminum alloys at the top. The entire stack of crucibles was then placed in the silica glass container "E" which was then sealed under vacuum. Sixteen to twenty calibrated Chromel-Alumel thermocouples were attached by wire along the length of the silica tube, one or more adjacent to each sample.

Jan 1, 1970

By CHARLERS R. FETTEE

A slight decrease in drilling activity occurred in the oil fields of western Pennsylvania during 1945 and a considerable decrease in the shallow-gas territory (Upper Devonian or higher). The number of deep tests (Middle Devonian or deeper) completed was two less than in 1944 and these did not open any new reserves of natural gas. Thus far, no commercial oil has been encountered in sands below the Upper Devonian in Pennsylvania. Oil production declined 8 per cent.

Jan 1, 1946

THE CHAIRMAN (F. K. COPELAND,* Chicago, Ill.).-At this particular time conditions existing in this, country, and elsewhere, make all questions of milling or smelting or mining, or anything else, absolutely secondary to the one question of labor. We have always devoted our attention largely to the efficiency of machinery, and to reductions in costs, etc., and have let this tremendous problem of our relation to labor more or less take its own chances. There has never been a time when those who are responsible for the operation of business of different kinds were as com-pletely at a loss as they are now, so that anything that can be brought out that relates to labor is, to my mind, of utmost importance. T. T. READ, Washington, D. C.-This formulation of a method of curtailing forces at the Copper Queen is a notable step in advance of our treatment of personnel in the mining industry. So far as I know, it is the

Jan 12, 1919

By Bernard York, John J. Reed

J. P. Zannaras (U.S. Tungsten Corp., Congress, Ariz.) —In the investigation described in the paper by Bernard York and John J. Reed, the 8x8x8-in. square block was subjected to compressive forces from three sides, top, side, and rear. Let us refer to the stresses set up by these forces as Sz due to top pressure, Sy due to side pressure, and Sx due to rear pressure. At the section across the 2-in. hole (when failure occurred at 317 psi) the compressive stress Sy was equal to 317 x 8/6 = —422 psi, the top compressive stress S; is of the same intensity, —422 psi, and the rear compressive stress S, equals —317 psi. The true stress is T = Sy — S — S Taking as 0.2,* Taking the case when the opening was ½ in. and failure occurred at 517 psi, 8 Sy - 517 x -----= —537 psi 7.5 8 Sz = 517 x-----= —537 psi 7.5 Sx = —517 psi The true stress T = Sy — Sz — S, T - —537 + 0.2 x 537 + 0.2 x 517 = —327 psi. It can be shown that the above fundamental formula holds good not only for the above two examples but for all sizes of openings used, because when this formula is expressed in terms of the external pressure and size of the opening it agrees perfectly with the experimental results obtained by the authors and given in Fig. 12 of their paper. General formula: T = Sy — s: — S....

Jan 1, 1955