By A. B. Kinzel

ALTHOUGH the iron-carbon diagram has undergone many changes in the last 20 years, the region below the eutectoid line and up to approxi-mately 1.7 per cent carbon has been little affected. This region is generally considered to consist of cementite and ferrite. Graphite has been noted occasionally in the hypereutectoid steel region, and the ready formation of graphite nodules in malleable cast iron is a phenomenon difficult to interpret in the light of cementite, supposedly stable at sub-eutectoid temperatures. In this case the graphite formation has been partly explained by the presence of silicon, and many have believed that silicon acts to change the stable state rather than to accelerate reactions so as to arrive at the stable state in a briefer period of time. Consider-ation of this phenomenon indicates that cementite is not the stable phase in the temperature composition zone referred to. In the course of examining a low-carbon steel tube taken from a petroleum cracking still, which had been in service for approximately three years at temperatures somewhat below the eutectoid temperature, observations were made that shed light on this entire subject. The tube in question analyzed:1 C, 0.15 per cent; Mn, 0.49; Si, 0.02; S, 0.023; P, 0.015. The microstructure of the tube after service is shown in Figs. 1 and 2. From these it is evident that cementite as such is absent, and that in its place nodular graphite has been formed. In order to check this observation further, samples taken from the tube were heated at 850° C. for varying periods of time. The small samples were put into a large hot furnace, and the total time is recorded. The structure of the

Jan 1, 1934

By A. B. Kinzel

IT is with sincere appreciation and a deep sense of responsibility that I accept the honor of delivering the Howe Memorial Lecture. In our time metallurgical research has delved into phenomena ever more complex in character, so that much of this work must be done by organized teams. We, of the Union Carbide and Carbon Research Laboratories and the Electro Metallurgical Co., are truly a team and the lecture which is to follow is due largely to a few of the outstanding members of that team here cited and well known to you in their own right: John Lamont, whose work deserves special recognition, Walter Crafts, William Forgeng, William Binder, Robert Fowler, and David Swan. Thus it is a fitting pleasure to accept this honor for the research institution which I represent. Henry Marion Howe was truly inspirational and his breadth of view was such that he could use either the method of rigid proof or implied mechanism to further the broad understanding. But perhaps his outstanding characteristic was his sound judgment and his ability to weigh observations. The following is replete with observations and judgment as to their implication. We would like to feel that it is the type of dissertation which Howe, himself, would have enjoyed. Chromium carbides in stainless steel have, in a sense, been a key to the progress of the stainless steel industry. Brearley's first stainless steel, containing approximately 0.30 pct C, was successful because it differed from previous Fe-Cr alloys in that the carbides were present in such amount and form as to provide the stainless and cutting properties. Again, the 12 pct Cr die steels with a carbon content of 1.5 pct or more achieved their properties by virtue of the form and distribution of the chromium carbides. In the straight chromium steels with from 12 to 25 pct Cr, chromium carbide amount and distribution are once more the determinants with respect to physical properties and corrosion resistance. In each of the cases just cited the role of the carbide is in essence similar to that of iron carbide in carbon steel and this story is so well known that we need not dwell on it. In the austenitic stainless steels, the chromium carbide plays only a minor positive role with respect to mechanical properties, and for corrosion resistance the objective is to achieve maximum homogeneity. Thus the tendency has been to ever lower the carbon and correlatively the chromium carbide content of the austenitic steels. Today stainless steels with carbon less than 0.03 pct are beginning to find their true place, and this is being aided in major degree by our Company's introduction of a new type of ferrochromium having negligible carbon. The role of carbon in these austenitic steels has long been recognized, and a truly enormous amount of research has been devoted to the subject. Much has been learned about corrosion resistance, but the attack on the problem from the point of view of carbide precipitation and the nature thereof has left much to be understood. Because of its fundamental importance to the future of stainless steels, further study of the mechanism of carbide formation in austenitic steels is of interest. In the 18-8 Cr-Ni steels, which are typical of the austenitic class of steel, carbon is soluble in the aus-tenite to the extent of approximately 0.15 pct at 1832°F (1000°C). The solubility becomes less with decreasing temperature, so that at 1652°F (900°C) the solubility limit is approximately 0.06 pct, at 1472°F (800°C) it is about 0.03 pct, and at 932°F (500°C) it is approximately 0.01 pct. Obviously this is the ideal situation for the classical precipitation phenomenon. It is true that, in a sense, 18-8 austenite resulting from annealing is in a metastable state, and the phenomenon of ferritic precipitation from this austenite should be considered. However, in a so-called fully austenitic 18-8 steel this is secondary with respect to the carbides and can be neglected. A wide variety of chromium carbides is known. Only one chromium carbide, Cr,,C,,, frequently referred to as Cr,C, has been found in unmodified low carbon 18-8 steel. This, fortunately, simplifies the study of the precipitation phenomena. For this study an A.I.S.I. type 304 stainless steel of commercial quality was selected. Analysis showed C 0.07 pct, Mn 0.49 pct, Si 0.33 pct, Ni 9.34 pct, Cr 18.91 pct, and N 0.033 pct. As expected with this composition the steel was homogeneous after annealing except for a few pools of ferrite, which were disregarded in that their location was not coincident with subsequent carbide precipitation areas. On corrosion testing the steel was normal and typical of good commercial quality. Specimens 1/2xlx4 in. were annealed and subjected to precipitation heat treatment for 100 hr at 100" temperature intervals from 1000° to 1500°F and for ten selected intervals ranging from 5 min to 64 hr at 1300°F. These blocks were then cut into small pieces for metallographic studies. The first problem

Jan 1, 1953

By C. E. Mills

STUDIES of ground movement and subsidence resulting from mining operations cover a broad field. It is also a very important consideration and one that eventually affects nearly every mining operation of any extent. The damage to surface buildings, removal of mine surface plants and replacements of main hoisting shafts must reach an astounding expenditure were these cost figures available over a period of years. Were the subject one of mathematical formula and dependent only on the angle of draw of the walls or country rocks, the problem would be relatively simple. Consideration must be given to depth and extent of workings; structural conditions of the orebodies and enclosing country rock; physical properties of these same rocks, including schistosity, bedding, jointing, slips, dikes, faults, and other structural weaknesses. The method of mining, extent of openings, supporting pillars, and amount of moisture or water underground are other pertinent factors. With such a large number of variable factors, it is apparent that the subject of subsidence is one that must be based largely on experience and results at other mines where conditions are somewhat comparable. In presenting this paper, it is the intent to describe the progressive results of past ground movements at the United Verde, to bring out physical conditions largely responsible for this movement, but to refrain from theorizing on the ultimate extent of subsidence resulting from future mining operations.

Jan 1, 1934

THOSE MARKED THUS * ARE MEMBERS, MARKED THUS ?ARE ASSOCIATES. THESE SIGNS DOUBLED INDICATE LIFE MEMBERS AND ASSOCIATES RESPECTIVELY. THE FIGURES AT THE END OF THE ADDRESS INDICATE THE YEAR OF ELECTION. HEAVY-FACED TYPE SIGNIFIES HONORARY MEMBERSHIP. *AARONS, J. BOYD, Vivian Gold Mining Co., Ltd., Harris, West. Australia. '05 *ABADIE, EMILE R., Cons. and Min. Engr., 214 Union Savings Bank Bldg., Oakland, Cal. '76 ?ABBÉ, MAX F., Prest., Abbé Engineering Co, 220 Broadway, New York, N.Y. '07 *ABBOTT, CHARLES W., Min. Engr. Pioche, Nev. ?08 *ABBOTT, JAMES W., Min. Engr: Ploche, Lincoln Co., Nev. '94

Jan 1, 1917

By L. E. Shiffman

W. J. Parton—Those operators faced with the problem of treating fine coal whether in bituminous or anthracite will find this paper most timely. I would like to take this opportunity of discussing Mr. Schiffman's paper and at the same time express certain views relating to our Tamaqua plant. I would like to ask the author what type of impeller and diffuser is used in the Denver cells? Screen analysis of products from individual cells indicate that coarser material resists flotation and only floats after greater retention time in the last few cells. Also, the need for a scavenger screen to reclaim non-floated coal particles further stresses this point. I have always felt that more efficient means of cleaning coal between 10-mesh and 28-mesh existed than flotation. Reagent and power costs are high for the flotation process. When floating +28-mesh particles, cell capacity is lowered and some of the particles are lost with the refuse. The Tamaqua plant of the Lehigh Navigation Coal Co. floats —28-mesh coal and capacity of recoverable coal is 40 tph for 1800 cu ft of Denver cells; or 0.05 tons per cu ft of cell. At Kimberly 7.75 tph for 600 cu ft of cell gives 0.013 ton per cu ft of cell. At Bessie 14 tph for 800 cu ft of cell gives 0.017 tons per cu ft of cell. It would be appreciated if the author would comment on what he feels is the upper size limit of particle to attain most efficient utilization of the flotation process. The dewatering screw is a very interesting development since it offers a simple way to prepare coal sludge for more complete clewatering by drainage or mechanical dewatering on screen or filters. In other words it could be used to accomplish the same thing as a thickener tank. I would appreciate having the author's comment on how he thinks such a screw dewaterer would work on a froth.* The process as used in floating coal at the Bessie and Kimberly plants may be referred to as more of a bulk oil float in contrast to a froth flotation process. Experiments on increasing capacity of cells is most interesting since we are going through such an experi- mental period at the present time. Recently a double overflow was installed on our No. 30 Denver cells. So far results are not conclusive. In reviewing this paper the following comments are made pertaining to investigation of methods for increasing capacity: Supercharging: Supercharged air in matte flotation or for that matter the use of the normal amount of air drawn in by the impeller would in all probability cause such an aeration in the cell as to destroy the buoyant effect given to the coal particles by the excessive amount of kerosine used. In other words, air creates an agitation zone throughout the cell, creating a boiling and thereby giving a lower recovery in the cell. It would be interesting to know whether the 7 pct increase in recovery was with no air being admitted to the stand pipe. Changing Impeller Speed: The speed of a receded disc impeller for a No. 30 cell as recommended by the Denver Equipment Co. is, I believe, approximately 250 rpm. At this speed and using supercharged air in excess of 8-oz pressure, we have observed a boiling action in the cells. In our flotation we endeavor to obtain some degree of froth flotation using pine oil as a frother. The boiling action as caused by increasing the amount of air added to the cells is detrimental to recovery in froth flotation. It is our belief that to obtain increased recovery from a cell in froth flotation, additional air must be introduced but at the same time this air must be dispersed throughout the pulp in the form of small bubbles and this can only be done by increasing the speed of the impeller. Therefore, if Mr. Schiffman decreased the speed of the No. 30 impellers and at the same time continued to use supercharged air, the boiling action may have been increased because larger bubbles developed. The lower recovery as reported could be due to this factor. Decreasing the impeller speed will definitely decrease the power consumed but may have other disadvantages. First, we believe it will permit "sanding" in the cell and this in our opinion will increase the wear on the impeller and diffuser, especially so, if there is pyrite and/or sand present in the feed. "Sanding" in the cell when air is used, as in froth flotation, will effect the dispersion of this air and cause boiling.

Jan 1, 1951

By L. E. Shiffman

W. J. Parton—Those operators faced with the problem of treating fine coal whether in bituminous or anthracite will find this paper most timely. I would like to take this opportunity of discussing Mr. Schiffman's paper and at the same time express certain views relating to our Tamaqua plant. I would like to ask the author what type of impeller and diffuser is used in the Denver cells? Screen analysis of products from individual cells indicate that coarser material resists flotation and only floats after greater retention time in the last few cells. Also, the need for a scavenger screen to reclaim non-floated coal particles further stresses this point. I have always felt that more efficient means of cleaning coal between 10-mesh and 28-mesh existed than flotation. Reagent and power costs are high for the flotation process. When floating +28-mesh particles, cell capacity is lowered and some of the particles are lost with the refuse. The Tamaqua plant of the Lehigh Navigation Coal Co. floats —28-mesh coal and capacity of recoverable coal is 40 tph for 1800 cu ft of Denver cells; or 0.05 tons per cu ft of cell. At Kimberly 7.75 tph for 600 cu ft of cell gives 0.013 ton per cu ft of cell. At Bessie 14 tph for 800 cu ft of cell gives 0.017 tons per cu ft of cell. It would be appreciated if the author would comment on what he feels is the upper size limit of particle to attain most efficient utilization of the flotation process. The dewatering screw is a very interesting development since it offers a simple way to prepare coal sludge for more complete clewatering by drainage or mechanical dewatering on screen or filters. In other words it could be used to accomplish the same thing as a thickener tank. I would appreciate having the author's comment on how he thinks such a screw dewaterer would work on a froth.* The process as used in floating coal at the Bessie and Kimberly plants may be referred to as more of a bulk oil float in contrast to a froth flotation process. Experiments on increasing capacity of cells is most interesting since we are going through such an experi- mental period at the present time. Recently a double overflow was installed on our No. 30 Denver cells. So far results are not conclusive. In reviewing this paper the following comments are made pertaining to investigation of methods for increasing capacity: Supercharging: Supercharged air in matte flotation or for that matter the use of the normal amount of air drawn in by the impeller would in all probability cause such an aeration in the cell as to destroy the buoyant effect given to the coal particles by the excessive amount of kerosine used. In other words, air creates an agitation zone throughout the cell, creating a boiling and thereby giving a lower recovery in the cell. It would be interesting to know whether the 7 pct increase in recovery was with no air being admitted to the stand pipe. Changing Impeller Speed: The speed of a receded disc impeller for a No. 30 cell as recommended by the Denver Equipment Co. is, I believe, approximately 250 rpm. At this speed and using supercharged air in excess of 8-oz pressure, we have observed a boiling action in the cells. In our flotation we endeavor to obtain some degree of froth flotation using pine oil as a frother. The boiling action as caused by increasing the amount of air added to the cells is detrimental to recovery in froth flotation. It is our belief that to obtain increased recovery from a cell in froth flotation, additional air must be introduced but at the same time this air must be dispersed throughout the pulp in the form of small bubbles and this can only be done by increasing the speed of the impeller. Therefore, if Mr. Schiffman decreased the speed of the No. 30 impellers and at the same time continued to use supercharged air, the boiling action may have been increased because larger bubbles developed. The lower recovery as reported could be due to this factor. Decreasing the impeller speed will definitely decrease the power consumed but may have other disadvantages. First, we believe it will permit "sanding" in the cell and this in our opinion will increase the wear on the impeller and diffuser, especially so, if there is pyrite and/or sand present in the feed. "Sanding" in the cell when air is used, as in froth flotation, will effect the dispersion of this air and cause boiling.

Jan 1, 1951

By A. G. Weber, K. H. Coats, M. H. Terhune, R. L. Nielsen

Two computer-oriented techniques for simulating the three-dimensional flow behavior of two fluid phases in petroleum reservoirs were developed. Under the first technique the flow equations are solved to model three-dimensional flow in a reservoir. The second technique was developed for modeling flow in three-dimensional media that have sufficiently high permeability in the vertical direction so that vertical flow is not seriously restricted. Since this latter technique is a modified two-dimensional meal analysis, suitably structured three-dimensional reservoirs can be simulated at considerably lower computational expenses than is required using the three-dimensional analysis. A quantitative criterion is provided for determining when vertical communication is good enough to permit use of the modified two-dimensional areal analysis. The equations solved by both techniques treat both fluids as compressible, and, for gas-oil applications, provide for the evolution of dissolved gas. Accounted for are the effects of relative permeability, capillary pressure and gravity in addition to reservoir geomety and rock heterogeneity. Calculations are compared with laboratory waterflood data to indicate the validity of the analyses. Other results were calculated with both techniques which show the equivalence of the two solutions for reservoirs satisfying the vertical communication criterion. INTRODUCTION Obtaining the maximum profits from oil and gas reservoirs during all stages of depletion is the fundamental charge to the reservoir engineering profession. In recent years much quantitative assistance in evaluating field development programs has been provided by computerized techniques for predicting reservoir flow behavior. Because of the spatially distributed and dynamic nature of producing operations, automatic optimization procedures, such as those now in use for planning refining operations, are not now available for planning reservoir development. However, present mathematical simulation techniques do furnish powerful means for making case studies to help in planning primary recovery operations and in selecting and timing supplemental recovery operations. A number of methods have been reported which simulate the flow of one, two or three fluid phases within porous media of one or two effective spatial dimensions>-4 However, applying computer analyses to actual reservoirs have been limited mostly to two-dimensional areal or cross-sectional flow studies for two immiscible reservoir fluids. To obtain a three-dimensional picture of reservoir performance using such two-dimensional techniques, it has been necessary to interpret the calculations by combining somehow the results from essentially independent areal and cross-sectional studies. To the authors' knowledge, the only other three-dimensional computational procedure, in addition to those presented here, was developed by Peaceman and Rachford8 to simulate the behavior of a laboratory waterflood. Two computational techniques which may be used to simulate three-dimensional flow of two fluid phases are described in this paper. The first method, called the "three-dimensional analysis", employs a fully three-dimensional mathematical model that treats simultaneously both the areal and cross-sectional aspects of reservoir flow. The second method, called the vertical equilibrium (VE) analysis", is applicable

By F. V. Shallcross

Physical properties of thin films of CdS and CdSe formed by vacuum deposition onto glass sibstrates have been studied as a function of deposition and processing conditions. The crystallinity and surface features of CdS films were examined using electron microscopy and electron and X-ray diffraction techniques. The films were poly crystalline; the preferred orientation and crystallite size increased with film thickness, substrate temperature, and deposition time. The CdS films consisted primarily of hexagonal-phase material, in contrast to similarly prepared CdSe films which have previously been observed to contain mixtures of cubic and hexagonal phases. As-deposited CdS films showed no major dependence of Hall mobility on crystallite size or degree of preferred orientation. Hall mobility and carrier concentration in CdS and CdSe .films were measured at various temperatures; both parameters increased with temperature and yielded activation energies which depended on fabrication conditions. Surface-desorption phenomena and overcoating of the semiconductor with SiO affected the observed electrical properties significantly. THIN films of cadmium sulfide1,2 and cadmium sele-nide3,4 have been employed by various workers as semiconductors in the insulated-gate thin-film field-effect transistor, known as the TFT. These devices are most commonly made by vacuum deposition of all materials onto an amorphous substrate such as glass. A knowledge of the microstructure and electrical properties of semiconductor layers used in the thin-film transistor is essential in order to form a realistic model for the device and to improve its performance, reproducibility, and reliability. This paper will describe studies of the physical properties of vacuum-deposited CdS and CdSe films prepared under various conditions. Structural characteristics examined in- cluded phases present, crystallite size, nature of preferred orientation of crystallites, surface roughness, and structural homogeneity throughout the film thickness. Electrical properties measured were Hall mobility and conductivity and their dependence on temperature and ambient. Thin-film properties are affected by many fabrication parameters including purity and physical form of evaporant, deposition rate, film thickness, design and temperature of the evaporation crucible, geometry of the deposition chamber, nature of the residual atmosphere, composition and temperature of the substrate, and details of postdeposition processing. PREPARATION OF FILMS In this work the semiconductor films were deposited in a conventional oil-diffusion-pumped system with pressures in the 10-8 torr range. The CdS evaporant was obtained from the Eagle-Picher Co. as a high-purity coarse-grained crystalline powder; the CdSe was a high-purity sintered powder supplied by the Harshaw Chemical Co. The evaporation crucible was a resistance-heated molybdenum-wire basket coated with aluminum oxide and filled with a quartz wool plug at the top. The source to substrate distance was usually 10 cm. This region was enclosed by a Pyrex inner cylinder. The substrate was heated with an overlying Pyrex plate coated with tin oxide. The substrate temperature was controlled using a thermocouple attached to the lower side of the heater. This thermocouple was calibrated against another thermocouple attached to a dummy substrate and by observation of melting points of various metal films deposited in the system. The substrates were polished borosilicate glass plates and conventional glass microscope slides. Substrate preparation included cleaning with an ultrasonically agitated detergent bath followed by isopropanol-vapor de-greasing. Film thickness was measured interferomet-rically during and after deposition. STRUCTURE OF CdS FILMS Structural studies were performed on CdS films using electron diffraction, electron microscopy, and

Jan 1, 1967

D EC. 20-The spirit of Christmas and good will toward men has managed a few brief appearances on the front pages, welcome relief from man's usual ill-will toward man. A couple politicos did their best to brighten the scene by well-publicized romances. There was a general exodus to Florida to patch up nervous systems, and even the UNO quieted down as Mr. Vyshinsky departed for home via Eastern Germany. Before going he opened up a preliminary bombardment for the worldwide "communist peace offensive," and it is now the duty of the 600 million (according to the Cominform) ideological converts to press home the attack. In Washington, Mr. Lilienthal resigned as Chairman of the Atomic Energy Commission and demonstrated again the difficulty of government to retain the services of capable men. The President has yet to appoint another victim- possibly someone nicely noncontroversial and timid. So might the critics be appeased, but it would bode ill for the rapid exploitation of peaceful uses of atomic energy, the relaxation of excessive secrecy, wider sharing of developmental work with friendly nations and possible revision of the Acheson-Lilienthal proposals for inter- national control of the atomic bomb.

Jan 1, 1950

By C. S. Finney, John Mitchell

The introduction of ovens for the production of metallurgical coke is believed to be due to L. L. Norton who operated an iron foundry in the vicinity of Connellsville, Pa. Persuaded by his foreman, an English immigrant named Nickols from Durham, L. L. Norton put up a 12-ft square oven which produced coke in 1833. The coal used was taken from a local mine at Mounts Creek. The oven seems to have been used in conjunction with the customary method of coking in mounds. It was in the Connellsville district also, in 1841, that two carpenters, Provence McCormick and James Campbell, formed a partnership with John Taylor, a stone mason, for the manufacture and sale of oven coke. The task of the mason was to construct the ovens, while the carpenters were to build the arks by which the coke could be taken by water to the market at Cincinnati. The following account of the enterprise was given by McCormick: "James Campbell and myself heard in some way that I do not now recollect that the manufacturing of coke might be made a good business. Mr. John Taylor, a stone mason, who owned the farm on which the Fayette coke works now stand, and who was mining coal in a small way, was spoken to regarding our enterprise, and proposed a partnership-he to build the ovens and make the coke and Mr. Campbell and myself to build a boat and take the coke to Cincinnati, where we heard there was a good demand. This was in 1841. Mr. Taylor built two ovens. I think they were about 10 feet in diameter. My recollection is that the charge was 80 bushels. The ovens were built in the same style as those now used, but had no iron ring at the top to prevent the brick from falling in when filling the oven with coal, nor had we any iron frames at the mouth where the coke was drawn. The top and mouth had to be repaired when they fell in. In the spring of 1842 enough coke had been made to fill two boats 90 feet long-about 800 bushels each-and we took them to Cincinnati down the Youghiogheny, Monongahela, and Ohio, but when we got there we could not sell. Mr. Campbell, who went with the boats, lay at the landing some two or three weeks, retailing out one boatload and part of the other in small lots at about 8 cents a bushel. Miles Greenwood, a foundryman of that city, offered to take the balance if he would take a small patent flour mill at $125.00 hi pay, which Mr. Campbell did. He had it shipped here. We tried it, but it was no good, and we sold it to a man in the mountains for $30.00, and thus ended our coke business." So successful did the coke subsequently prove to be in use that the three partners were asked to deliver more. Evidently they had had enough of the coke business, however, for they refused to have anything more to do with it. Few ovens were built between 1841 and 1855, and it is reported that in the latter year, "there were only 26 coke ovens along the river above Pittsburgh". Successful coke makers of these years included Mordecai Cochran, Richard Brookius, and Colonel A. M. Hill. It was the use of coke in 1859 in the Clinton furnace erected by Graff, Bennett and Co. in a plant on West Carson Street, Pittsburgh, that brought the real beginning of the coke-iron era in America. Here the successful use of Connellsville coke as a blast-furnace fuel was demonstrated beyond all possible doubt, and from the year 1859 the coking industry expanded tremendously. The era of beehive coke ovens During the latter half of the nineteenth century and the early years of the twentieth, the major percentage of metallurgical coke produced in the United States came from beehive ovens. It was not until 1893 that the first battery of by-product ovens came

Jan 1, 1961

By R. F. Mehl, C. E. Birchenall

SINCE Maxwell1 first considered the self-diffusion process in 1872 its importance in the kinetic theory of matter has been recognized. Until the discovery of isotopes in 1913, a direct measurement of this quantity seemed impossible. The only information that could be gathered indirectly was for gaseous systems for which the kinetic theory was well developed. When methods of direct observation be-came available, investigations on self-diffusion were carried out in condensed phases. In metals these data are presumably of potential importance in the study of recovery, recrystallization, creep, sintering, and related phenomena. Following the pioneer work of Von Hevesy2 and his collaborators, who determined the rate of self-diffusion in lead with the naturally occurring thorium B isotope, several metals have been investigated. Pb, Ag³, Au.6,5, and Cu6,7,8,9 are examples of isotropic crystals existing in only one phase modification. Anisotropy of diffusion has been demonstrated in Bil6 and Znll. This paper is a study of a single metal in two allotropic forms and also of self-diffusion in a body-centered cubic lattice. Despite the fact that the measurements in each of the papers cited on self-diffusion in copper seem to be internally consistent to about 10 to 15 pet, the curves reported by different authors differ by factors of 2 to 4 at the same temperatures. This uncertainty may account, in part, for the failure to establish a successful correlation between the self-diffusion rates and other physical characteristics of the metals. No satisfactory theory of metallic self- diffusion has as yet been proposed to account for all the existing data and to permit estimation in other metals. Experimental Part: Two units of radioactive iron were used in these experiments, each a mixture of Fe53 and Fe59 (12). Fe53 decays by K electron capture and the emission of an X ray with a half life of about 4 years. Fe59 emits two beta spectra, one with a maximum energy of 0.26 Mev, the other 0.46 Mev, and gamma rays of 1.1 and 1.3 Mev, with a half life of about 44 days. They were present in nearly equal concentration initially. The composite half life started at about 50 days and increased as the Fe59 decayed, leaving Fe55 relatively more abundant. After aging a year, the half life was too long to measure significant decay in a month. The absorption properties also changed with time. Because of the importance of the absorption coefficient in the diffusion calculations, it was necessary to determine this quantity frequently over the period during which these experiments were carried out. This correction was unsuspected at the time of publication of notesl3 on this work and accounts for the discrepancy in alpha iron and for part of the discrepancy in gamma iron.* * The data in the present paper supersede those given in the notes entirely. In one note the scale of log D was inadvertently reversed. In addition to the correction for the drift in absorption coefficient, the D values for gamma iron at low temperatures were high owing to insuficient correction for diffusion occurring during heating and cooling through the high temperature part of the alpha range at a rate much slower than that employed in the runs reported here. The high temperature alpha rates are much higher than the low temperature gamma rates and correspond to large equivalent times at these temperatures. These experiments were discarded and new measurements taken. Independent experiments with the same activity units indicated a radioactive contaminant in the iron, but exhaustive attempts to isolate and identify it chemically failed. These experiments? indicate † These experiments will be discussed in a later publication from this laboratory. that the contaminant represented only a trace of little importance in the diffusion results. The active iron was plated from an iron chloride solution. Enough of the solution was dropped on a 1% in. square of filter paper to wet it thoroughly.

Jan 1, 1951

By W. B. Plank

RETURNS already received from a current survey of the enrolment of students in the mineral technology schools indicate a degree of activity and prosperity in those schools never before equalled. The returns are as yet too meager for accurate analysis, but those at hand point LO considerable increase in the metallurgical and petroleum engineering groups, and indicate that the total of 5011 two years ago in the United States schools will be substantially increased. Generally speaking, the enrolment is not only maximum in quantity but optimum in quality. Better income has sent the boys back to school, but the improved employment conditions have somewhat reduced the number of graduate students. Laboratories are commonly filled to capacity, in some instances overcrowded. Increased enrolment of foreign students from both Canada and South America is noticeable.

Jan 1, 1937

By C. C. Hawes

SILICA is the main impurity in iron ore. It is intimately associated with the iron oxide, sometimes free but more often in the combined state, as a mineral silicate. Its separation and purification sometimes present difficult problems to the analyst. In the absence of any definite knowledge to the contrary, orthosilicic acid. H4SiO4, is supposed to be the only silicic acid made, all other forms, such as metasilicic acid, H2SiO3, representing different degrees of its dehydration. These acids are exceedingly weak but form the most stable compounds found in nature. They are known as the silicate minerals and are formed by the combination of the different metallic oxides

Jan 1, 1936

By J. P. Pritchard, J. T. Pierce, O. G. Slay

This paper discusses the results of a technology-evaluation program to ascertain the feasibility of a piotornask-photoresist technology developed for fabrication of multiple-layer thin-film superconductive circuitry. The uehicle selected for this evaluation was a 120-bil associative data processor requiring a set of nine photomasks to define a similar number of patterned material layers of lead, tin, and polymer insulation. A total circuit area of 4 sq in. involved 2500 actitle and 12,000 passive crossings. Several short-free, electrically continuous specimens were satisfactorily completed under this program. Problems encountered in the preparation and use of the requi-ed set of Photomasks are discussed, as also are the problets of providing suitable external connections. A major retarding factor in the development of the superconducting thin-film cryotron technology for many years was the absence of batch fabrication means yielding necessary device density and count per substrate for practical applications. Early workers in the field desired only limited numbers of devices to permit careful study of discrete devices and representative circuitry integrating logic and memory capabilities. For these purposes mask stencils could be formed to selectively control the placement of materials, sequentially vapor-deposited in vacuum, to form the multilayer structure. In general a distinct pattern was required for each material layer; therefore, mechanical provisions were required to change not only the material source, but the patterning mask as well, before each deposition. All deposition steps were preferably performed in a single evacuation of the deposition chamber. Thus the means for storing, transporting, and registering masks and sources with respect to the substrate existed and were operated within the vacuum environment. In the authors' experience, the approach was and remains serviceable for preliminary device study, but was not extensible to an economical manufacturing method by virtue of the difficulties inherent in mask stencil preparation and use, and the capital investment implicit in the mechanization requirements. Since the commercial attraction of the cryotron technology stems principally from its potential for economical batch fabrication, the authors' program has placed major emphasis on fabrication methods. A highly useful method has evolved through adaptation

Jan 1, 1967

By Charles M. Romanowitz

The motivation for the art of dredging for placer mining can be compared in a slight degree to the spread of civilization which started in the Near East and spread both east and west. Dredging started with the "bag and spoon" dredge in the lowlands of Europe reportedly about 1565, went southeast to New Zealand where designs were developed for a bucket-line mining dredge known as the New Zealand type, and westward to the eastern United States where a dredge was developed and used exclusively for excavating. Then it moved to Montana, where it was first used for mining in 1895. The New Zealand-type dredge was imported into California in 1898 (Fig. 1) and was followed shortly by the Montana design. As today, these early dredges were equipped with continuous bucket- line chains, a treatment plant, and a means of waste disposal mounted on a wooden hull. Both types of dredges are complete mining units: they dig the formation, transport the dug materials, and concentrate the valuable ore. After sizing, the fines containing the ore are passed by gravity to the treatment unit, while the barren materials are discharged overboard. By digging the materials to be treated at the bow and depositing all the waste, at the stern, the dredges automatically advance to new reserves without presenting any transportation problems. The main differences between the two types are in the method of holding the dredge in the digging position and in the disposal of the tailings to the rear. The New Zealand type (Fig. 2) uses the headline system with a bow anchor for holding the dredge in the digging position and long tailing flumes or short stackers off the stern for disposal of the barren materials. The California type (Fig. 3) uses box girder spuds projecting into the ground in a vertical position at the stern of the

Jan 1, 1969

By Charles T. Baroch, Charles J. Baroch

Nuclear energy probably has greater potentialities for changing the world's way of life than any other recent discovery. The atomic-bomb bursts over Hiroshima and Nagasaki suddenly changed the concepts of war. Peaceful uses of nuclear energy are advancing so rapidly that no study of economic trends is complete without giving them consideration. The minerals specialist, especially, must be aware of this new force in our lives, as minerals and metals are essential in harnessing the new force, and atomic energy itself is rapidly improving its competitive position in the energy field. Future historians may chronicle December 2, 1942, as the beginning of the Atomic Age. On that day Enrico Fermi and his co-workers at the University of Chicago produced and controlled the first self-sustaining nuclear chain reaction. Lie many inventions, the first application of nuclear energy was as a weapon of war. However, its potential usefulness in man's work and welfare far outweighs in economic importance its destructive use in war, unless its military effect would be considered so great and all-embracing that no major power will hereafter chance a world conflict. Recognition of this potential has generated a vast international effort to exploit the atom for peaceful beneficent purposes. Like its physical manifestation, the advent of nuclear energy has unleashed chain reactions that have pervaded the political, social, and economic environments of the world. The impact of nuclear developments in one of many fields is exemplified by the uranium mining industry. Uranium was discovered in 1789 and in the next century and a half it found only an insignificant use as a ceramic coloring agent; in fact, in the latter part of that period, it was a largely unsalable by-product of the radium and vanadium industries. Up to 1940 the total quantity of uranium metal produced was not more than a few grams, of doubtful purity. Thus the production of 12,400 pounds of pure

Jan 1, 1964

By Jay A. Carpenter

THIS preliminary report from the Committee to Study Relations Between Students and the Institute is submitted to our member- ship for consideration and discussion before the general subject comes up for action at the Annual Meeting in February. At present, the A. I. M. E. has a dual relationship with mining students, each relationship in no may connected with the other. To the individual student the Institute offers for $2 a year a Student Associateship in the Institute which carries with it a subscription to MINING AND METAL- 'LURGY, a watch fob, and the privilege of becoming a Junior Member after graduation without payment of the -first year's dues, if one's application is accepted. To the student's college society it offers the privilege, upon application, of becoming 'an Affiliated 'Society, which brings with it no specific supervision or aid, and in turn requires no specific conditions as to membership, fees, or rules. This Affiliated Society is distinctly a school organization which Student Associateship in the Institute can he given special status or ignored, is the local .society sees fit.

Jan 1, 1934

By Edward O’Toole

THe Pocahontas district occupies the extreme southern end of West Virginia, principally McDowell, Mercer and Wyoming counties, and a part of Tazewell county, in southwestern Virginia. The first record of the coal field is a report by Prof. J. P. Lesley, of Pennsylvania, about 1880, in which he mentions a coal opening at the upper end of Abbs Valley, Tazewell county, Va. C. R. Boyd, a mining engineer of Wytheville, Va., published a series of articles in 1881, mentioning coal on Indian Creek, Tazewell county, and on Horse Pen creek, which coals, he stated, extended toward the Ohio River. He also mentions the Abbs Valley coal reported by Lesley. In 1881, F. J. Kimball (who became president of the Norfolk & Western R. R. in 1883)) after examining the Scott mine in Abbs Valley, went northward across Abbs Valley Mountain to the place now known as Pocahontas, where he located what has since been called No. 3 vein of Pocahontas coal. In November, 1882, Jed Hotchkiss and others prepared a cross-section of the Flat Top Mountain coal measures, some notes on which were published by Mr. Hotchkiss, between 1880 and 1892, under the title of " The Virginias.' In May, 1881, the Norfolk & Western R. R. was organized through the purchase of the Atlantic, Mississippi & Ohio R. R., an old line running from Norfolk, Va., to Bristol, Tenn., with branches from Petersburg to City Point and from Glade Springs to Saltville. At that time, charters had been granted for three railroads tributary to the New River Valley, but their proposed routes would indicate that the promoters were concerned with minerals, timber, and a connection with the Chesapeake & Ohio R. R., rather than the development of any coal in the Pocahontas district. One of them was projected to extend up Bluestone River a short distance, but not far enough to reach the coal in the Bluestone Valley, and a little grading was done for a narrow-gage road between New River Station and a point in Giles county, Virginia, near the West Virginia line. All charters and railroads in this district were acquired by the Norfolk & Western R.R.

Jan 1, 1925

By R. F. Hollis, C. K. McArthur

PRIOR to the application of anion exchange, all recovery of uranium from acid leach liquors precipitated an impure product requiring further upgrading before it could be refined. The ion exchange process, on the other hand, provides excellent selectivity for extracting soluble uranium from leach liquors, so that high grade concentrates can be produced directly. The discovery that uranium is readily adsorbed by anion exchange resins, together with the experience of resin and equipment manufacturers in water treatment, led to rapid development of ion exchange in a multiple column operation. Many processing plants using fixed bed ion exchange are in operation or under construction in Africa, Australia, and Canada. There are a limited number in the U. S. Although the fixed bed process has been highly successful, the feed to the ion exchange columns must be a clear solution, which is obtained by filtration or by countercurrent decantation of leached pulps. With some ores, poor filtration or settling characteristics make production of a clear solution difficult. Most processing plants in the U. S. receive their ores from a number of small mines, and there is considerable variation in the settling and filtering behavior of the ores. An ion exchange process was therefore desirable in which the uranium could be recovered directly for the leached pulp by adding ion exchange resin, which could be then separated from the pulp by a screening operation. The process would thus resemble the cyanide-charcoal process in which gold is adsorbed from cyanide pulp by means of activated charcoal. Preliminary tests in which leached pulps were directly contacted with resin beads led to the development of the RIP process.

Jan 4, 1957

Philip Argall, Denver Col. (communication to the Secretary): Dr. Raymond claims (Trans., xxiii., 560)) that my statement (p. 557) regarding the crystallization of iron "is beyond question incorrect." He says: "It is not even settled that vibration will crystallize iron under any conditions." While admitting that authorities differ on the possibility of cold crystallization of iron, I believe it is a settled and undisputed fact that vibration in the presence of heat will crystallize iron. Bloxam and Huntington say :* " Vibration assists 'in converting fibrous metal (iron) back into a crystalline state when heated, a lower temperature sufficing than in the absence of vibration." Mr. A. F. Hill, summing up a very exhaustive review upon the crystallization of iron and steel, pronounces against crystallization, but only at temperatures below 900' F. Mr. Howe, discussing ,the breakage of a 20-foot porter-bar with a crystalline fracture, suggests that it was attributable to heat, jointly with the jar. We see, then, that vibration of heated iron bars will induce crystallization and consequent change of structure. Referring to my statement, I wish to point out, that I was discussing the vibration of stamps arid should have said, "vibration under all such conditions," etc. That is, vibration attended with sharp blows, such as a stamp-stem is subjected to, will crystallize iron; yet I believe that intense vibration under any condition will

Jan 1, 1895