Search Documents

By Masahiro Yoshimura, Sergiy Korablov

"Hydi-othermal corrosion ofTiN, TlAlN and CrN PVD films (3 µm thick) deposited on SUS-304 substrate was studied in 100MPa water in 20-950°C temperature range up , to 750h. The beginning temperature of their reaction was determined as 200°c for TiN and TiAlN and 500°C for CrN films, which are quite low in comparison with that of air oxidation of those powders. Very thin oxide scales. of TinO; n-I homologous series phases were formed above 300°C. TiO2 anatare. is observed for TIN and TiAlN films at 400°C. The· feature of hydrothermal corrosion of CrN films seems to be CrNxOy phase formation.Distinguishable weight changes were observed at higher temperature than 700°C for TiN, 750°C for· TiAlN and 800°C for CrN respectively. Hydrothermal corrosion kinetics .was constructed to calculate the activation energy of hydrothermal corrosions. On the base of obtained data, hydrothermal corrosion resistance was as follows: TiN – TiAlN - CrN. Facetted oxide crystals were formed at higher temperature than 500°C for TiN, TiAlN and 850°C forCrN.IntroductionThe metallic nitride (TiN; TiAlN, CrN) PVD films have high hardness, strength and wear resistance. Therefore these films are widely used in industry for wear resistij.nce application such as cutting tools and die molds. Their performances depend on not only the mechanical properties but also corrosion resistance of coated films. High temperature oxidation of metalliq nitride and nitride films was well studied [1-5]. However there are no reliable data concerning the .corrosion resistance of coated nitride materials. In high-temperature and high-pressure water. There are a few reports on hydrothermal corrosion of nitride films [6,7]. The increase of corrosion resistance of CVD films was observed in following succession TiC - TiCNO - TiCN - TiN at 300-680°C temperature interval and I 00 MPa pressure water according to data of the first report. Kawana et al. [7] have reported about excellent corrosion resistance of CrN films under 290°C and 8, 6 MPa water during I 000 h in the circulating type experimental loop. The films thickness was about 7-10 µm in both cases. However it remains unclear the chemical state of the surface species and especially in-depth distribution, oxide scale thickness and its growth, and defects formation in the oxide film."

Jan 1, 2000

By Akita Ito, Sumio Kato, Mikio Sugai, Shinichi Nakata

"Spark Plasma Sintering (SPS) is a newly developed method for the sintering of metal and ceramic powders, and completes their densification at low temperature and in short period. The SiC powder was synthesized from diatomite and graphite or carbon black by heating at 1 450°C for 1 hr in an argon atmosphere. The synthesized SiC powder was heated at 1500-1800°C, 50 MPa for 15-18 min by SPS. The relative density of sintered SiC body increased with the rise in the temperature. The oxidation of the surface of the SiC particle and impurities in SiC from diatomite greatly influenced the sintering promotion of SPS.IntroductionThe SiC has high hardness because of the covalent bonding, and is also excellent in thermal and chemical stability. However, it is difficult to obtain a dense SiC sintered body by the combustion heating-method. Therefore, the dense SiC bodies have been made by the use of additives and I or the hot pressing (HP) method.In this study, the SiC powder was synthesized by using diatomite of natural products and graphite, and carbon black of reagent as raw materials, and the relationship between the properties of SiC powders prepared at various synthetic conditions and the density of sintered body by SPS was examined."

Jan 1, 2000

By Kazutaka Kunii

It is invariably certain that after punching for IC Leadframes, scrap metal were generated. These seraps were re-dissolved and in order to use as raw material for leadframes, it is necessary to remove the Ni plating. In this study a simple method was developed for the removal of Ni plating by surface oxidation of Ni plating. For this purpose a fundamental study was carried out on the oxidation behavior of Ni plating. Results showed that by controlling the oxidation condition, a considerably high rate of Ni could be removed.

Jan 1, 1996

By Martin Reyes, Juan Hernández, Julio Cesar Juárez, Isauro Rivera, Ma. de los Ángeles Hernández, Francisco Patiño

The dissolution of Ag contained in metallurgical tailings was studied by adding ions Cu2+ and Zn2+ in S2O3 2- medium. Chemical analysis of mine tailings by cupellation revealed a Ag concentration of 71 g/ton. The XRF and XRD analysis confirmed the preponderance of SiO2 in the mineral matrix. The experimental dissolution process was conducted in alkaline solution using six concentrations of NaOH and five of S2O3 2-, at different temperatures, also using five concentrations of Cu2+ and Zn2+ as a catalyst. The results showed similar values for both systems (96.8% and 97.13%). The ion Cu2+ and Zn2+ increases the dissolution of Ag, and decrease the reaction time of dissolution. Under the conditions used, pH and stirring rate did not affect the dissolution of Ag.

Jan 1, 2015

By Yuanbo Zhang, Zhixiong You, Daoxian Duan, Guanghui Li, Tao Jiang, Xiaohui Fan

"Presently, high-grade manganese oxide ores are usually utilized by a coal-based reduction roasting process. However, there were some obvious drawbacks, including serious environmental pollution, high energy consumption, etc. The reduction temperature is relatively high (850-900 °C). In this study, a kind of biomass, pine black charcoal, was used as a reductant to reduce low-grade manganese oxide ores. Under the optimal conditions of reduction temperature of 600~650 °C, roasting time of 30~45 min and ratio of ore to reductant 5:1, the leaching efficiency of manganese reached more than 98%. Compared with the traditional coal-based reduction process, the reduction temperature is reduced by 250-300 °C.IntroductionManganese plays a very important strategic role in the national economy, and it is widely used not only in the metallurgical industry, but also in the light industry, chemical industry, medicine, agriculture, etc [1]. The average grade of manganese ores in China is evenly about 21%, which belongs to typical low-grade manganese ores [2]. Therefore, large quantity of high-grade manganese ores is required to import in order to meet the rapid development of Chinese manganese industry. As reported, the conventional treatment of reduction roasting has been widely applied for processing manganese oxide ores, in which coals or reducing gases (CO, H2 or CHi) were usually used as reducers [3]. However, there were some insuperable problems, such as high energy consumption, poor operating conditions, serious environmental pollution, etc [ 4-9]."

Jan 1, 2013

By Jiann-Yang Hwang

A study on microwave assisted chalcocite leaching was carried out with a microwave hydrothermal reactor. The leaching was conducted with thick mineral slurries (50-100 g/l). The leaching media is a mixed solution of CuCL2 and NaCL The investigation included the effect of leaching temperature, quantities of the minerals per unit slurry volume as well as the initial concentration of cupric ions were investigated. The results were discussed and compared with that using conventional leaching method.

Jan 1, 2003

By R. Gampala

The consolidation of mom matrix composite monotapes occurs by the plastic (time independant) and creep deformation of monotape asperities. Past models of the process used seperate micromechanical analyses of the contact deformation by (rate independent) plasticity and power law creep (i.e steady state creep). These models are now used to simulate consolidation and to optimize/control consolidation process cycles so that the composite's microstructure is "steered" to, a user defined goal state. However, the models do not incorporate the sometimes dominant transient creep process and the instantaneous response of the plasticity mechanism causes finite discontinuities in the microstructure state vector field and therefore eliminates the possibility of using the powerful array of trajectory optimization schemes that all require continuous vector field for optimization and control. To overcome this problem, a inified creep/plasticity constitutive model that results in a continuous state vector field is used to rederive the contact deformation response during monotape consolidation. The contact blunting of a laterally constrained hemispherical asperity is first analyzed and its response represented by two coefficients; one relating the contact area to the blunting strain (C), the second, the mean contact pressure to the blunting rate (F).The C and F coefficients for this unified blunting problem are then obtained by finite element analysis, and detailed results presented for two composite matri-ces of topical interest (Ti-24A1-11Nb and Ti-6Al-4V).

Jan 1, 1996

By S. Tandon

Equilibria studies of selenium distribution for sodium-borate slags were initiated at 1473k under reducing condition as a function of slag composition and alloy composition. The Se distribution coefficient (% Se in slag/% Se in metal) increased from 0.4 to 2.9 with increase in basicity (0.53 to 0.86) for Cu-0.446% Se alloy. However, the results are not very useful from industrial application viewpoint. Therefore, in order to improve the distribution of Se, CaO (10% to 50%) was added to the sodium-borate slag of basicity 0.864. On addition of 502 CaO, the distribution coefficient increased roughly by 100% for slag composition - 44.5% Borax, 22.2% Na2C03, 33.3% CaO and Cu-0.44677 Se alloy. Further, the value of this distribution coefficient has been found to increase by an additional 80% on addition of 20% CaF2 to the above slag for all Cu-Se alloy compositions. Also with increase in initial concentration of Se, the distribution coefficient has been noted to increase.

Jan 1, 1992

By Kazuhiro Asai

Hitachi Refinery of Nippon Mining & Metals Co., Ltd. installed a reverberatory type recycling fumace in 1978 in order to treat the industrial wastes which contain metal elements such as copper, gold and silver. Pyrite and industrial waste materials such as galvanizing sludge, hydroxide slime and dust are smelted. Sulfidized copper, iron and precious metals are transformed into matte and other metallic elements are oxidized into slag This copper matte is transported to Saganoseki smelter and copper and precious metals in the matte are recovered. Recently it is difficult to obtain pyrite economically because of the decrease of pyrite production. Therefore, a new treating process of the liquid waste has been investigated at Hitachi Refinery. In this process, the sulfide or sulfate from the liquid waste are smelted as a source of sulfur.

Jan 1, 1997

By M. Kawakami

In relation to the designing of a new-type blast furnace, the reaction of carbonaceous materials with CO2 is expected to occur at as low temperature as possible. In order to get a highly reaetive carbonaceous material at low temperature, the reaction kinetics was investigated by measuring such quantities as the reaction rate from weight loss, the amount of CO adsorption and specific surface area by BET method. The reaction rates were large in the order of the Bintyo char, metallurgical coke, graphite and glassy carbon. If the rate was converted to the rate per unit area, however, those of the Bintyo char was smaller than that of graphite. Thus, it is suggested that the rate of the Bintyo char is influenced by the pore diffusion of CO2. The rate had a positive relation with the amount of CO adsorption, showing that the rate determining step would be the desorption of CO from the active side on the surface. The rate independent of surface area was derived, combining all the obtained data.

Jan 1, 2003

By Beate Ina Jenssen

Ferric iron removal from the nickel electrolyte at Glencore Nikkelverk AS in Kristiansand, Norway, is achieved by precipitation of iron hydroxide followed by filtration, and it is desirable to improve filtration properties of the precipitated iron hydroxide in order to decrease the filtration time. The effect of increasing the residence time from the current 45 min to 75 min and temperature from 65 °C to 90 °C on the filtration properties of the precipitated iron hydroxide (akaganéite) was studied by simulating the industrial process conditions in a continuous reactor setup operating at steady state, using ferrous-containing process solution as feed material. It was possible to decrease the filter cake resistance by both increasing residence time and temperature, but temperature gave the most pronounced effect and reduced the filter cake resistance by one order of magnitude.

By Laurentiu Nastac, Ruslan Mudryy

"This paper investigates the solidification of cast energetic materials. An active cooling and heating (ACH) technology and a mechanical vibration (MV) technology were applied to achieve unidirectional solidification during casting and to reduce cracks, gas pores, and shrinkage defects. The design parameters of these technologies were developed via Computational Fluid Dynamics (CFD) modeling and thermal stress analysis. Concerning the ACH technology, the number of cooling/heating sections and their temperature profiles and time sequences were optimized based on the thermo-physical properties of the energetic material as well as the riser and mold diameter, thickness and type. The ACH technology will also decrease the thermal stresses during casting of energetic materials and therefore minimize the formation of potential cracks that may form during the casting process. The MV technology will help to remove air entrapped during pouring process and decrease the detrimental gap size between the projectile and the solidified energetic material.IntroductionCasting processes are widely employed in the manufacture of products with intricate shapes and, in particular, in applications where the material of the final product is sensitive to machining. It is especially useful in processing of energetic materials. The cooling conditions applied in the casting process can affect the quality of the final cast in terms of void formation, residual stress distributions, and mold separation. Substantial shrinkage is also observed due to the density change upon solidification [1-3]. Residual stresses are known to be closely related to the formation of cold cracks and hot tears during casting. The formation of a gap between the mold and the cast material is of critical importance due to its deleterious effect on heat removal and on crack formation. In the casting of energetic materials all these defects can significantly impair the detonation velocity, Gurney energy, and insensitive munitions characteristics of the formulation, and lead to catastrophic accidents in explosives handling [ 4-5]. Imposition of carefully controlled cooling condition is thus critical in optimizing the cast quality that could help avoid such destructive effects."

Jan 1, 2013

By Waraporn Piyawit

Grinding sludge from the sintered neodymium-iron-boron (NdFeB) magnets production process was enriched with critical rare earth elements (neodymium, dysprosium and praseodymium), which can be up to 30% in the magnets. The demand of NdFeB magnets are simultaneously growing. Therefore, rare earths recovered from waste residue would reduce the demand of rare earth elements from primary sources. In this study, the feasibility of recycling rare earths through a hydrometallurgical process was investigated. The selective leaching of Nd from grinding sludge can successfully raise the rare earths concentration to 70%. The necessity of an oxidation pretreatment to improve the selectivity between Nd and Fe will be described.

By Pengkai Wang, Huimin Lu, Xiaoxiang Zhang

"In this paper, it was studied an electrochemical reduction process of carbon dioxide in ionic liquids such as 1-n-butyl-3-methylimidazolium hexafluorophosphate ([Bmim] PF6) as the electrolyte. The electrolysis experiments were carried out under current and potential controls. The cathode products contained carbon nanotubes, carbon nanofibers, nanographites, and amorphous carbon. To establish the actual current and potential ranges, the electroreduction of carbon dioxide dissolved in the ionic liquid was studied by cyclic voltammetry on glass-carbon (GC) electrode at room temperature. The electrochemical mechanism of carbon dioxide electroreduction was studied for explanation of all obtained results. Carbon dioxide in ionic liquids was electroreduced, similar to metals oxides being electroreduced in molten salts.IntroductionGlobal warming caused by the increase of carbon dioxide in the atmosphere has become one of the most concerning environment problems, so the solution to this greenhouse effect is very urgent. However, the carbon dioxide is also a cheap and abundant raw material that represents a potential source for the production of chemicals and fuels. Therefore, the development of the technologies that achieve simultaneous reduction and conversion of carbon dioxide to fuels is important. The electrochemical reduction of carbon dioxide is one of the effective approaches to transform CO2. Many investigations have been carried out on the electrochemical reduction of CO2 in both aqueous [1] and non-aqueous [2] electrolyte solutions with different electrodes. The solubility of CO2 in water is very low even under high pressure of CO2, and some investigators have brought focus into the electrochemical reduction of carbon dioxide in organic solvents, because they dissolved much more CO2 than water did. However, the hazardous or toxic properties of organic solvents hinder their use."

Jan 1, 2009

By Deventer Johanna van

Ore bodies around the world are declining in grade, whilst increasing in complexity. The level of impurities relative to the valuable metal is steadily increasing, posing new challenges to existing operations. Ion exchange is widely used in the hydrometallurgical industry for both primary recovery of metals and the removal of impurities. The superior selectivity of ion exchange resins makes them exceptionally suitable for the removal of target impurities to very low levels, thereby saving operating costs, increasing the value of the final product and significantly improving revenue. The ion exchange process in these applications is very simple, using standard ion exchange equipment and acid regeneration. The process can be fully automated, requiring minimal operator interference and supervision Examples of impurities that are successfully removed via ion exchange include iron, antimony and bismuth from copper electrolyte. In the copper electrolysis process, antimony, bismuth and arsenic tend to form slimes which are dispersed in the electrolyte. These slimes contaminate the cathode and/or decrease the quality of the copper deposition. A special chelating resin was developed to remove antimony and bismuth, while at the same time ensuring minimal chloride leakage to the sulphate matrix. The work is described in more detail in this paper. Ion exchange is also used to remove copper, zinc and nickel from cobalt electrolyte. This paper addresses a few of these examples in more detail.

By Juan Patricio Ibáñez

Separation of arsenic and copper from Cu-As-H2S04 electrolytes by electrodialysis has been investigated at room temperature. The effects of current density and pH were studied. An arsenic-free copper solution was obtained for all the tested conditions. The transport efficiency for copper ions was found to be higher than 98% after 3 hours' test. Transport of arsenic and copper through the ion exchange membranes was increased by increasing pH and current density. Solution pH was found to be a key parameter for the separation process, since it controls the speciation of the ions to be transported and the formation of unwanted precipitates which reduce the global efficiency of the electrodialysis process. The main conclusion is that electrodialysis is a promising technique to be used in separating and/or concentrating ions of interest in copper electrometallurgy.

Jan 1, 2003

By Zhigan Deng

Ni–Mo ore is a black shale containing amorphous colloidal sulfides which have highly active. The oxygen pressure leaching behavior of nickel from black shale in aqueous media is presented. The effects of agitation speed, temperature, oxygen partial pressure and particle size on the rate of nickel leaching were determined. The results indicate that at low temperature hydrothermal and excess oxygen presence, the amorphous sulfides are easily oxidized to sulfuric acid and sulfate, and leaching nickel. The mathematical analyses of the experimental data for various experimental conditions indicated that the dissolution process was controlled by the chemical reaction during the early stage of dissolution, and was then controlled by liquid-film diffusion. In the initial stage of leaching, the reaction depends on oxygen partial pressure.

By Huyang Xie, Rishi Raj, Vera A. Versteeg

"A new method for MOCVD has been developed in which a precursor solution is directly injected into a reaction chamber. The vaporization of short pulses of liquid is facilitated by atomization with a piezoelectrically-operated nozzle. The system has been used successfully to grow oriented, thin Ti02 (rutile) films on sapphire substrates with the crystalline relationship (101)[010]R I (1120)[0001]s. A growth rate of approximately 2 monolayers per pulse was achieved at 650°C for a reactant impingement rate of about 800 monolayers per pulse. Also, epitaxial LiTaO3 thin films were grown on (0001) sapphire from a single source, bimetallic precursor, lithium tantalum hexa-t-butoxide as the precursor. X-ray diffraction shows that the LiTaOa c-axis is normal to the sapphire surface. The x-ray pole figure and crosssection TEM diffraction show that the films were also in-plane oriented, with sapphire [1010] parallel to lithium tantalate [1010]. These films are shown to have extremely low optical attenuation, and refractive index that compares well with bulk values.IntroductionMetalorganic chemical vapor deposition (MOCVD) techniques have come into increasing use in recent years, due to the growing versatility and availability of precursors and improved environmental advantages over the halogenated compounds used for conventional CVD. Most commonly, the films are deposited by dissolving the metalorganic reactant (typically a metal alkoxide) in a carrier gas, which is carried through heated lines to a heated substratel . The metal alkoxides decompose by pyrolysis, leaving the films on substrates. While this method has been used to produce excellent epitaxial and heterepitaxial films, it has the disadvantages of complexity: the precursor must be heated to fix its vapor pressure, the gas flow rate carefully controlled, and the carrier lines heated to prevent condensation before reaching the reactor. Additionally, this conventional method cannot be used with certain low-volatility precursors that decompose upon heating."

Jan 1, 1994

By John J. Mortvedt

Application of some by-products of the metals industry which contain plant nutrients to agricultural lands could constitute resource recovery instead of costly disposal. Some industrial by-products contain appreciable concentrations of heavy metal contaminants, such as Cd, Cr, Ni, and Pb. After land application, these metals may be absorbed by plants and enter the human food chain or be leached to groundwaters. Plant uptake of these heavy metals varies with plant species:, soil pH, soil texture, and the particular metal. Certain leafy vegetables can absorb significant amounts of heavy metals, while absorbed metals are usually poorly translocated to cereal grains. Allowable heavy metal concentrations in fertilizers now are not regulated, but EPA is considering such regulations. Heavy metal impurities in animal feed supplements are regulated by the states; so some by-products may not be permitted for this use.

Jan 1, 1992

By S. P. Marsh, D. Banerjee

"Casting processes involve phenomena that occur on widely disparate length-scales. Simulation of macroscopic effects, such as heat transfer and convection, are generally addressed by solving the appropriate equations in discretized form on a finite-element mesh. Microscopic phenomena are described by micromodels that may be empirical or analytical in form. Coupling of phenomena in these two regimes is a critical issue in predicting microstructure and defect formation resulting from macroscopic process conditions. A formalism has been developed for expressing micromodels in a consistent manner using stereological parameters to quantify the geometric characteristics of the developing microstructure. This approach provides a robust and physically consistent method for coupling local micromodels with the macroscopic fields. The macroscopic state variables at each node serve as global constraints on the micromodels that are applied to a local unit volume. An outline of an equiaxed solidification model based on this approach is presented, along with preliminary simulation results. Coupling of convection and enthalpy effects between the micro and macro regimes is also discussed. IntroductionThe primary goal of casting simulations is to improve the reliability of cast parts while minimizing cost and development time. Effective simulations can speed up the mold design process and reduce the likelihood of defective parts by refining a particular casting process on a computer, reducing the dependence on cost- and time-intensive prototype castings. The challenge in developing effective simulations stems from the need to address physical processes that occur over a wide range of length-scales, from microscopic (atomic) and mesoscopic (microstructural) scales to macroscopic distances comparable to the size of the casting itself. Overviews of the various thermophysical phenomena and computational factors that are important in solidification modeling are provided in the literature by Rappaz [1] and Tseng et al. [2].Macroscopically, the solidification process is largely governed by the rate of heat flow from the alloy through the mold wall. Another important effect that occurs on the scale of the casting size is convective flow of the melt, which is driven by density-variations in the melt. Macroscopic calculations employ finite-element or finite-difference methods to solve the sets of equations that govern these effects, and the spatial resolution is determined by the grid spacings used for the calculations. Typical spatial resolutions are on the order of 10-2 to 10-3"" meters. This represents a compromise between the resolution required to simulate the continuum transport processes accurately, and the computational time required to model the entire solidification and cooling process."

Jan 1, 1994