Search Documents

By Cyril Stanley Smith, Earl W. Palmer

A study of the precipitation-hardening of copper steels1 led the authors to investigate malleable iron containing copper, for the low-carbon ferritic matrix in malleable iron should lend itself admirably to precipitation-hardening. It was soon found that in addition to rendering malleable iron susceptible to improvement by precipitation-hardening treatments, copper has another potentially useful effect as an accelerator of graphitization. Brief mention of these effects was given in a general paper by Lorig and one of the present authors2; the present paper gives further details on the graphitization and precipitation-hardening effects only. After the completion of this work a paper by L. Lykkin3 appeared, confirming the authors' conclusions regarding graphitization. Material Used After some preliminary heats had been made in the laboratory to determine the effect of copper, several castings from commercial air-furnace heats were obtained, and data from these alone are given here. Part of the metal was poured directly and part was treated in the ladle with the desired amount of copper before pouring. Green-sand molds were used, each holding two tensile test pieces of the form adopted by the Malleable Iron Research Institute, or two bars for graphitization studies, 5/8 in, in diameter and 9 in. long, fed through two enlarged sections equidistant from the middle and ends of the bars. Risers of suitable size insured sound castings. Tensile tests were made on the castings after commercial mallealleizing and after special heat treatments to be described. The analyses of the white irons are given in Table 1.

Jan 1, 1935

By H. LeChatelier, B. Bogitch

Page Introduction........................... 134 Methods of Investigation....................... 135 The Tridymite Network...................... 137 Independent Variables....................... 146 Manufacturing Operations..................... 153 Introduction Silica brick are indispensable in the manufacture of steel because they alone are able to withstand the high temperature of regenerative furnaces. All attempts to replace silica brick by other refractory materials for this purpose have failed, but the reason for this failure has remained obscure; we shall give an explanation later in this paper. Before the war, silica brick employed in France came principally from abroad, for which reason, since the beginning of hostilities, certain French steel works have been seriously handicapped. Our attention was first directed to the question by M. Bied, Engineer of the Teil Works. With him, we began certain investigations, at first using our laboratory and the furnaces of neighboring steel works. The larger part of our experiments, however, have been made in the laboratory of the Faculty of Sciences at the Sorbonne. For the heating of our samples, we are deeply obliged to MM. Charpy, Yeatmann and Guerineau. In undertaking these studies, our first aim has been to render assistance to French industry, by indicating, as precisely as possible, the necessary conditions for the manufacture of high-grade brick; but at the same time me have

Jan 1, 1919

By P. R. Sperry

In an investigation of the decomposition of the solid solution in a cold worked high-purity aluminum alloy containing 7 pct Mg, aged at temperatures from 30o to 82°C, the nucleating sites at the earliest stages of precipitation were observed to be of two types. Nucleation occurred at the high angle grain boundaries both when the alloy was initially cold worked and when solution annealed. Nucleation also occurred at certain unique deformation markings which began to appear in abundance at approximately 30 pct reduction in thickness by cold rolling. These deformation markings were identified as deformation (kink) bands rather than as the usually assumed "slip planes." Zn material that was cold rolled 15 pct, only the grain boundary Fig. 2—A1-7 pct Mg alloy, cold worked 60 pct and heated at 230° C for 5 min. Etched with Perryman's reagent. X500. Reduced approximately 25 pct for reproduction. (a) Bright field illumination, precipitate deeply pitted. (b) Phase contrast, showing slip markings.

Jan 1, 1962

By H. F. Moore

Jan 1, 1936

ALABAMA. Anniston.-Noble, A. E., 20th St. and Wilmer Ave. Auburn.-Brown, R. L., Box 0. Belle Ellen.-Hutcheson, W. C. Bessemer.-Abbott, C. E., T. C., I. & R.R. Co Dobbs, G. G., Box 97. Ferguson, V., U. S. C. I. Pipe & Fdy. Co. Williams, E. P., Tenn. C., 1. & R. R. Co. Birmingham.-Aldrich, T. H. Aldrich, T. H., Jr., 406 Woodward Bldg. Allen, A. W., 1616 S. 14th Ave. Bowron, J., 1401 S, 20th St. Burbidge, T. A., Brown-Marx Bldg. Coxe, E. H. Tenn. C., I. & R. R. Co. Crawford, C. G., Tenn. C., I. & R. R. Co. Crockard, F. H., Brown-Marx Bldg. Ellis, E. E.,1515 Brown-Marx Bldg. Fairbairn C. T., Woodward Bldg. Fies, M. H., 2316 Highland Ave. Geismer, H. S., Keiser-Geismer Engrg. Co.

Jan 1, 1917

By H. F. Moore

Jan 1, 1936

Jan 1, 1959

By T. E. Leontis

The importance of magnesium alloys in the manufacture of aircraft engines has been realized for many years. A concentrated effort has been exerted in the laboratories of the Dow Chemical Co. to develop magnesium-base alloys with improved properties at elevated temperatures whereby greater advantage can be taken of the inherent lightness of these materials. In an earlier publication, attention was called to the superior tensile properties and resistance to creep of cerium-containing magnesium alloys at temperatures up to 700°F. More recently, additional data on magnesium-cerium alloys have been furnished by Murphy and Payne. The present paper deals with the mechanical properties of sand-cast magnesium alloys containing zinc, at temperatures up to 500°F. The study includes binary Mg-Znt alloys containing up to 10 pct zinc and several ternary and some polynary alloys based on the Mg-~Zn,f Mg-jZn, Mg-4.4211, Mg-6Zn, and Mg-roZn binaries. The compositional variation in the tensile properties, hardness, and creep at room and elevated temperatures, and in the electrical conductivity at room temperature has been determined. The results of these tests show that many zinc-containing magnesium alloys exhibit resistance to creep at elevated temperatures significantly higher than that of present commercial magnesium alloys, but lower than that of alloys of the magnesium-cerium type. In addition, they have high tensile properties at room and elevated temperatures and high conductivity. This combination of mechanical properties and conductivity indicates that these alloys should be given serious consideration for commercial applications involving exposure to temperatures higher than those to which present commercial magnesium alloys can be taken safely. Literature The properties of sand-cast magnesium alloys containing zinc as a principal alloying element have not been investigated very extensively, especially at elevated temperatures. The following remarks, which are confined to sand-cast alloys, will serve as a summary of the most important references on this phase of magnesium metallurgy. The first recorded determination of the tensile strength of binary Mg-Zn alloys as a function of zinc content was reported by Aitchison. Similar studies, including the measurement of elongation and hardness, have been performed by Gann and Winston,' Dumas and Rockaert, Haugh-ton and Prytherch,6 and by Spitaler, the last being reported by Beck.' A slight superiority in the tensile strength of chill-cent Mg + 8 es alloy Over the sand-cast alloy was noted by Maybrey.8 That alloys of magnesium containing 5 to 12 pct zinc

Jan 1, 1949

By Robert F. Mehl, Edward L. McCandless

Oriented overgrowths and intergrowths among both metallic and nonmetallic substances have been recognized and studied for well over a century. The work of Widmanstätten in 1808 on the geometrical structure in meteorites, a structure known by his name, demonstrated that oriented intergrowths can occur in purely metallic systems. This fact led to much of the early microscopic study of alloys, contributing greatly to the advance of physical metallurgy. The problem has been attacked again in recent years in a comprehensive fashion, with the object of discovering what atomic movements may occur during phase changes in alloy systems. Much of this work has appeared in the A.I.M.E. Transactions in a series of papers published by Mehl and coworkers beginning in 19311. Although many aspects of this general problem remain unsolved, it may be said that the orientation of a new phase forming by precipitation from solid solution or by transformation invariably bears a unique relationship to the orientation of the phase from which it formed, and that similarity in atomic patterns on atomic planes in the two phases play an important part in determining the orientation relationship. Analogous orientation relationships exist in oriented intergrowths in nonmetallic systems—mineral or inorganic. In 1827 Haidinger2 discovered natural intergrowths of hematite and magnetite, and demonstrated that the rough form of the magnetite octahedrons was delineated by small crystals of hematite, of which the basal (00.1) planes lay parallel to the octahedral cleavage planes of the magnetite. The description of this orientation relationship was later completed by von Rath3, who showed that the edge (00.1): (10.1) in hematite lies normal to the [Ill]

Jan 1, 1937

By H. M. Howe, Levy A. G.

Four aspects of flow in the plastic deformation of steel by overstrain, such as punching, wire-drawing, tensile rupture, etc, are…

Jan 1, 1915

By George S. Rice

Ten years ago: October, 1914, the author had the privilege of giving an illustrated address on investigations of coal-dust explosions1 to this Institute at one session of its fall meeting in Pittsburgh, Pa,. On the following day, the members had the opportunity of seeing a large-scale explosion test at the Experimental Mine near Bruceton, in which the explosion was made to follow a predetermined path by means of rock-dust barriers of various types, which had prevented the explosive waves from reaching the outlets of the mine by the shortest paths.2 There was also shown a ((home-made" rock-dusting machine discharging the dust from a flexible nozzle, and a cement gun operated for the quick erection of a fire or ventilation stopping, such as might be put up after an explosion. Following that paper, there was presented a paper by J. Taffanel, Director of the Lìévin testing station in the Pas de Calais, which reviewed the French coal-dust investigations.3 A paper4 by Howard N. Eavenson contains lists of explosions that occurred in North America and Great Britain, from early in the 19th century to 1912; in France to 1903, and Belgium to 1909. Although explosions still occur, we are hopeful that we have entered a happier freedom from these visitations, as the result of increased knowledge of the causes and means of prevention. Looking back over coal-dust investigations, there appear to have been periods of advance and of stagnation. Coal-dust Investigations From the earliest times of coal mining, which chiefly affected Great Britain as the first nation to take up coal mining on a large scale, to the beginning of the 19th century, no one thought of coal dust as an explosive agency; firedamp was the cause dreaded. It was believed, when Sir Humphrey Davy invented his safety lamp in 1815, that a solution had been found for the prevention of mine explo-

Jan 1, 1925

By E. M. Wise, T. E. Kihlgren, N. B. Pilling

SYSTEMATIC data are presented on the relation of composition of nickel silvers to color, tarnish resistance, hardness and liquidus temperatures, for alloys containing up to 30 per cent nickel and 50 per cent zinc, further modified at certain nickel and zinc contents by 0 to 8 per cent of tin and 0 to 10 per cent of lead. Attention has also been directed, using a still more limited range of alloys, toward a study of tensile properties and such casting properties and characteristics as fluidity, shrinkage and pressure tightness. In some of these, rather broad ranges of composition are dealt with; in others, it has been expedient to focus attention on the Federal Specification 20 per cent nickel silver casting alloy, WWP-541.

Jan 1, 1935

By Richard H. Mote

The endlessly changing pattern of mineral supply and demand offers opportunity to the alert and can bring disaster to the unwary. The discovery of ore bodies, the invention of extractive processes, the provision of new transport facilities, the political stabilization of underdeveloped areas, and many other changes can increase supply dramatically. Such new outpourings of mineral wealth from ore bodies bring fortunes to their developers, and consumers frequently find their competitive positions decidedly improved by new and cheap sources of supply. On the other hand, operators of marginal properties can find competition from newly opened high-grade mines intolerable. Consumers that have depended on the products of nearby, high-cost mines may find new, remote, low-cost supplies advantageous only to their competitors. The invention of new prospecting methods can have spectacular effects. Shortly after World War I the discovery rate of petroleum pools began to decline. The leading prospecting technique of that day, the projection downward of surface reflections of geologic structure, was proving less rewarding. Prophets foretold an oil shortage in the near future. But at that very moment scientists were perfecting the application of seismic waves to reveal underground oil-bearing geologic structures. As these geophysical methods were put into commercial use the whole outlook changed-the problem of the 1930's became how to cope with the surplus from discovery, not how to meet the ever rising demand. Many lead mines were being abandoned as unprofitable about this same time because the penalties charged by smelters for the zinc in the ores and concentrates more than counterbalanced the payments for lead and silver. Then selective flotation (at the time called differential flotation) appeared,

Jan 1, 1964

By N. M. Langdon

Spokane Meeting, September, 1909.) THE following corrections to the paper of Mr. Langdon (Bulletin No. 34, October, 1909, pp. 919 to 940), received after the publication of the paper in the Bulletin, will be incorporated in the paper as finally published in the forthcoming Vol. XL. of the Transactions, but are here presented for the information of members:' Page. 921. Table I., furnace M2, item 11. For " 8801 " read "0.8801." 922. Table II., furnace C, item 2, under gas. For " 0.011 C " read " 0.011 0." Furnace G, item 13, under gas. For " 5.074 air " read " 3.074 air." Item 15, 114.269 " should be " 4.289." Furnace H, item 2, under iron. For " 0.04 " read ".0.01." 923. Table II., furnace J, item 1, under iron. For " 0.95 " read " 0.93." Furnace N2, item 6, under gas. For " 0.66 CO," read 0.066 C02." 924. Table III., furnace C, item 17. For " 379 " read " 397." 927. Table IV., furnace C, item 4. For " 0.0124 " read 0.0424." Furnace G, item 15.. For " 4,060 " read " 4,066." 928. Line 2. Items 19 and 20 of heat-supply, should be items 20 and 21. 930. Line 3. Expunge remainder of paragraph after the word " supplied," and substitute the following : "As compared with the fusion-zone, the loss by radiation n C was 25.5 per cent. of the total (2,278 units) supplied to that zone, while in D it was 22.5 per cent. of the total heat (1,824 units) supplied to that zone. Finally, as compared with the reduction-zone, C lost by radiation 36.8. per cent. of the 1,580 units supplied to that zone,

May 1, 1910

By H. W. Maynor, C. J. McHargue

DURING the course of an investigation of materials suitable for use as thermocouples at elevated temperatures by one of the authors, several nlolybdenum-rhenium alloys were prepared. Micrographs of an annealed alloy containing 25 pct Re (intended concentration; analysis not obtained) showed a number of twins, Fig. 1, suggesting a face-centered cubic structure. This note reports the structure and recrystallized wire texture of an alloy containing 25 wt pct Re. Alloys were prepared from 99.9 pct Mo (Fansteel Metallurgical Corp.) and rhenium obtained from the University of Tennessee (purity unreported). Powders were combined and briquetted at 56,000 psi and sintering was carried out at 2400°C for 5 hr in vacuum. Ingots so prepared were swaged at 982.2" to 1037.8oC into wires 0.036 in. diameter, a reduction in diameter of 85.6 pct. These wires were vacuum-annealed 1 hr at 2000°C. A North American Philips 114.59 mm powder camera and nickel-filtered copper radiation were used for structure determination. For the texture determination a Laue-type camera was used with zirconium-filtered molybdenum radiation and, because of the high background, aluminum foil was mounted next to the film. Exposures were taken with the wire perpendicular to the X-ray beam and tilted by 10". It was found that the X-ray pattern could be indexed on the basis of a face-centered cubic structure. Because of difficulties associated with obtaining a good X-ray pattern for this material, accurate parameter determinations were not made. An indicated parameter value of 3.70A was obtained. The X-ray data are given in Table I. The annealed wire texture was observed to be a sharp [111] texture. The spread about this fiber axis was k8" at the surface of the 0.036 in. wire. The annealed wire textures of aluminum have been reported as retention of the [Ill] deformation texture for anneals below 500°C and a new [1121 texture for anneals above 600°C.1 In copper wires, with a [Ill] plus [loo] deformation texture, results indicate a retention of this texture for annealing at lower temperatures and new components or the disappearance of components for annealing at higher temperatures.' The presence of the strong [I111 texture in the molybdenum-rhenium alloy after a 2000 °C anneal suggests that the deformation texture was the same. Acknowledgment The wires used in this study were prepared and heat-treated at the Institute for Atomic Research, and Ames Laboratory, Iowa State College, and the authors wish to express their thanks to the Institute for allowing the use of the material and permission to publish the results.

Jan 1, 1954

By Henry M. Howe

Jan 1, 1909

PRESIDENTS DAVID THOMAS 1871 R W RAYMOND 1872-1874 A L HOLLEY1875 ABRAM S HEWITT 1876 T STERRY HUNT 1877 ECKLEY B COXE 1878 - 1879 WILLIAM P SHINN 1880 WILLIAM METCALF 1881 RICHARD P ROTHWELL 1882 ROBERY W HUNT 1883 JAMES C, BAYLES 1884-1885 ROBERT H RICHARDS 1886 THOMAS EGLESTON 1887 WILLIAM B POTTER 1888 RICHARD PEARCE 1889 ADAM S HEWITT 1890 JOHN BIRKINBINE 1891-1892 H M HOWE 1893 JOHN FRITZ 1894 J D WEEKD 1895

Jan 1, 1923

On the following pages are abstracts of papers published by the Institute during the year 1936 as TECHNICAL PUBLICATIONS and CONTRIBUTIONS, papers in bound volumes appearing for the first time, and papers in MINING AND METALLURGY For abstracts of papers that appeared in bound volumes in 1936 but that were published as TECHNICAL PUBLICATIONS in 1935, see the YEAR BOOK dated January 1936.

Jan 1, 1937

By G. R. M. Del Giudice

A survey of the flotation literature of the past 10 years indicates an increasing use of the microscope as a tool for investigation. Thus, the metallurgical microscope has been used by Tucker and Head;' Taggart, Taylor and Ince;2 Ince,3 and del Giudice4 to examine mineral surfaces that had been subjected to the action of various flotation reagents and to the action of slime pulps. It has also been used by Gaudin, Groh and Henderson;5 Martin;6 Morrow and Griswold;7 and others to examine bakelite briquets of mill products. The microscope with transmitted light, both with bright-field and dark-field illuminations, has been used by Taggart, Taylor and Knoll8 and by Ince9 to observe Brownian motrement and flocculation in flotation pulps. The use of the microscope at low-power magnifications with incident illumination for the examination of mill products has been known for years.10 Finally, del Giudice11 has used a relatively new type of illumination, the Ultropak, for the examinntion of slime-coatings.

Jan 1, 1935

Aalde, Kaare. ('40) Gen'I Del., Bisbee. Ariz. Aase, Glenn D., ('40) Univ. of North Dakota. Grand Forks. N. D. Abadesco, Enrique A., ('39) College of Engrg.. Univ. of the Philippines. Manila, P. I. Abbott. John L., ('40) Colorado School of Mines. Golden. Colo. Abdul-Ahad, A., ('39) Montana School of Mines. Residence Hall, Butte. Mont. Abreu, Ovidio M., ('38) Univ. of Nevada, Reno, Nev. Acomb, Allen. ('41) Louisiana State Univ., Box 1970, University. La. Acosta S., Gonzalo. ('40) Univ. of Texas, Univ. Sta., Box 1785. Austin, Tex. Adam, Howard W., ('41) Montana School of Mines. Butte, Mont. Adams, Albert, ('381 New Mexico School of Mines, Socorro. N. M. Adams. Charles W., ('39) Michigan College of Min. & Tech., Houghton, Mich. Adams. H. Travis, ('39) 316 South -5th St., Bur¬bank. Calif. Adams, Jack L., ('39) Univ. of Oklahoma, Nor¬man. Okla. Adams. John W., ('41) Colorado School of Mines, Golden. Colo. Adams. Lewis J.. ('39) 402 Del Mar Blvd., Corpus Christi, Tex. Adams, Rob L., ('40) Agricultural & Mech. Col¬ lege of Texas. Box 600, College Sta., Tex. Adamson. Charles R., ('41) Univ. of Utah, Salt Lake City. Utah.

Jan 1, 1941