By J. K. Buehler

With the rapid acceleration of the cost of shovel dippers and major standard shovel clipper rebuild components, maintenance management at Kennecott Copper Corp.'s Bingham Canyon mine initiated a dipper maintenance and rebuild program. The program focused on extending the service life of the shovel dipper, reducing field labor in maintaining dippers, and lowering shovel dipper rebuild costs. While comprehensive evaluation of the program is still underway, preliminary benefits of the program indicate: •Reduced field ,gelding for shovel dipper field maintenance, •Fewer dipper rebuild units entering the shop, and •Reduced dipper rebuild costs per unit.

Jan 1, 1979

By Robert S. Williams

On several occasions, when 60-40 brass is first obtained in the beta condition by quenching at about 825" C. and is then reheated, the writers have noticed that reerystallization will take place in the form of twin crystals at the grain boundaries of the original beta crystals. It was, therefore, thought that interesting results would be obtained if this twinning process was studied further, especially as to the temperature at which it first occurs. The material used in the investigation was a bar of extruded muntz metal, 1/2 in. in diameter, and of the following composition: Copper, 60.21 per cent.; zinc, 39.73 per cent.; lead, trace; iron, trace; tin, nil. Specimens 1 in. in length were sawed from this bar and a hole was drilled into the side of each specimen until it reached the center, and the tip of a platinum-platinum rhodium thermocouple was inserted. A small Hoskins' resistance-type electric furnace was used for heating the specimens. The specimens were first heated at 840' C. for 2 hr. and then quenched ' in cold water, in order to get the material entirely in the beta state. In every case, in the reheating process, the furnace was brought to the desired temperature before the specimen was introduced. The time occupied in preheating was from 20 to 30 min. By sawing back 1/4 in. on each side of the hole, two parts were obtained from each specimen and duplicate observations were possible. The specimens were held at the reheating temperatures for periods of 15 min., 30 min., 1, 2, and 4 hr. All specimens were etched with a freshly prepared mixture of equal volumes of concentrated NH4IOH and H2O2.

Jan 1, 1924

By Allan T. Gwathmey, J. Bruce Wagner, Kenneth R. Lawless

Between 250°and 550°C in oxygen pressures of 10 to 760 mm Hg, the relative oxide thicknesses formed per unit time on the (100), (111), (110), and (320), decreased in this order. The predominant oxide orientation was (001)Fe3O4 and [110] Fe304 A small amount of a-Fe2O3 which exhibited a fiber pattern was observed in all oxides except those formed at 250°c in low oxygen pressures. IN order to understand the properties and behavior of thin films, particularly their role in oxidation reactions, there is needed more experimental information on their structure, composition, and kinetics of formation on clean surfaces of known geometry. The present study was undertaken to obtain such information for thin oxide films formed on single crystals of a body centered cubic metal, iron. Crystals in the form of spheres were used in order to expose all possible crystal planes to the reactant gases simultaneously. Using this procedure the relative rates of oxidation of all planes could be estimated, and those exhibiting, maximum or minimum oxidation rates could be selected for a more intensive study of composition and expitaxy. Since the three types of information were obtained from the same experiment using a single crystal substrate, any differences between rate, composition, and expitaxy on the several planes may be attributed to the influence of the substrate structure. EXPERIMENTAL The starting material for this study was Armco iron rods, 6 in. long and 3/8 or 1/2 in. in diam. The analysis was reported to be 99.8 pct Fe, with major impurities listed as carbon 0.018 pct, manganese 0.027 pct, phosphorous 0.005 pct, sulfur 0.029 pct, silicon 0.005 pct, and copper 0.11 pct. These rods were cleaned with ether and heated in an atmosphere of moist hydrogen at 950°C for three days. The purpose of this treatment was to decarburize the iron and to provide a consistent, uniform grain size for the growth of single crystals. Crystals in the form of rods, up to 1/2 in. in diam and 2 in. long, were prepared by a method similar to that reported by Leidheiser and Buck.2 Spherical crystals, 3/8 and 1/2 in. in diam and having a handle about 1/4 in. in diam by 112 in. long, were machined from the single-crystal rods. After machining, each crystal was etched in aqueous nitric acid to remove the cold-worked metal at the surface. Before each experiment, the crystal was polished mechanically with metallographic papers through number 4/0, and electropolished in a perchloric acid-acetic anhydride mixture by the method of Jacquet and Rocquet.3 The crystal was washed in running distilled water for at least 5 min. The excess water was blotted with a soft paper tissue, and the crystal was placed in an all-glass reaction vessel (See Fig. 1). The crystal was heated at 550°C in hydrogen for at least 8 hr prior to the oxidation in order to reduce any surface oxides and to help relieve any stresses in the metal. For the structure and composition studies, flat faces were cut parallel to (loo), (111), and (110) planes on the iron crystal spheres. The orientation of these faces was checked by a back-reflection X-ray diffraction technique. The faces were within 2 deg of the desired orientation. The flat faces were treated as described above except that prior to electropolishing they were given an additional polish on metallographic felt saturated with twenty-minute levigated alumina. After the crystal was heated in hydrogen for at least 8 hr, the temperature was adjusted to the desired value, and the hydrogen was evacuated. Commercial oxygen which had been purified by successively passing through tubes containing magnesium perchlorate, Ascarite and magnesium perchlorate was admitted to the desired pressure as measured by a mercury manometer. A resistance-wound furnace surrounded the oxidation chamber, and a temperature controller maintained the temperature within ±3°C. The furnace was provided with a small window for observing the crystal. The changes in thickness of the oxide films were followed by observing the interference colors. The oxidation was allowed to proceed until the desired oxide thickness was attained on a given crystal plane. The experiment was terminated by evacuating the oxidation

Jan 1, 1962

By L. A. Walker

DURING the past twelve years the underground shaft of the United States mine at Bingham has been sunk an additional 2000 ft. with stations and pockets cut every 200 ft. without interrupting the mining of 600 tons of ore per day and the advancing of 1500 ft. of development per month. Following is a brief description of the way the joint work is conducted. The vertical underground shaft is a three-compartment shaft with outside dimensions of 6 ft. 4 in. by 15 ft. 6 in., and inside dimensions for each compartment of 4 ft. 2 in. by 4 ft. 8 in. The manway compartment of the main shaft is used as the hoisting compartment in sinking operations; it is partially lined with 2 by 12-in, lagging and a bucket is used without guides or crosshead. Preparatory work includes the placing of a bulkhead in the manway compartment, 60 ft. above the lowest station or level, the installation of a hoist, a head sheave, a fleet sheave, a-signal system, air and water lines, and a trap door for handling waste.

Jan 1, 1937

By W.M. Peirce

The present work has been done in an endeavor to correlate and complete the data on the constitution of alloys of zinc with other common metals, dealing exclusively, however, with the zinc-rich alloys in which the zinc content is between 90 and 100 per cent. This investigation has included the systems lead-zinc, cadmium-zinc, iron-zinc, copper-zinc, aluminum-zinc, nickel-zinc, manganese-zinc, cobalt-zinc, tin-zinc, and magnesium-zinc. The important ternary system zinc-lead-cadmium and the zinc corners of other ternary systems have been investigated in connection with this work but will not be dealt with here. Zinc does not form a single homogenous zinc-rich solid solution over any considerable range of concentration with any of the metals mentioned. A limited range of solid solubility is said, by previous investigators, to occur in several cases and certain effects on the properties of zinc are attributed (with varying degrees of consistency among different writers) to the presence of certain other metals dissolved in zinc. The increasing use of rolled zinc and the possibilities offered by zinc as a casting alloy in certain fields have made it essential to determine precisely these equilibrium relationships. In carrying out this investigation reliance was placed chiefly on two methods, conductivity measurements and microscopic analysis. The first method proved valuable in determining the existence and extent of solid solubility. The second method stands alone as a means of determining structural characteristics and supplements the first method in the measurement of solid solubility. The scleroscopic hardness of all conductivity specimens was measured partly for its value from the point of view of mechanical properties and partly as a check on the conductivity curves in indicating the limits of solid solubility. No hardness curves are included in this paper, for in no case were they important in arriving at the constitution of any system. Conductivity measurements were in all cases made on cold-rolled strips 0.020 in. thick and 0.5 in. wide, both as cold rolled and after an

Jan 1, 1923

By W. M. Peirce

The present work has been done in an endeavor to correlate and complete the data on the constitution of alloys of zinc with other common metals, dealing exclusively, however, with the zinc-rich alloys in which the zinc content is between 90 and 100 per cent. This investigation has included the systems lead-zinc, cadmium-zinc, iron-zinc, copper-zinc, aluminum-zinc, nickel-zinc, manganese-zinc, cobalt-zinc, tin-zinc, and magnesium-zinc. The important ternary system zinc-lead-cadmium and the zinc corners of other ternary systems have been investigated in connection with this work but will not be dealt with here. Zinc does not form a single homogenous zinc-rich solid solution over any considerable range of concentration with any of the metals mentioned. A limited range of solid solubility is said, by previous investigators, to occur in several cases and certain effects on the properties of zinc are attributed (with varying degrees of consistency among different writers) to the presence of certain other metals dissolved in zinc. The increasing use of rolled zinc and the possibilities offered by zinc as a casting alloy in certain fields have made it essential to determine precisely these equilibrium relationships. In carrying out this investigation reliance was placed chiefly on two methods, conductivity measurements and microscopic analysis. The first method proved valuable in determining the existence and extent of solid solubility. The second method stands alone as a means of determining structural characteristics and supplements the first method in the measurement of solid solubility. The scleroscopic hardness of all conductivity specimens was measured partly for its value from the point of view of mechanical properties and partly as a check on the conductivity curves in indicating the limits of solid solubility. No hardness curves are included in this paper, for in no case were they important in arriving at the constitution of any system. Conductivity measurements were in all cases made on cold-rolled strips 0.020 in. thick and 0.5 in. wide, both as cold rolled and after an

Jan 1, 1923

By B. R. Queneau

[ ] B. R. QUENEAU-One of the difficulties in metallurgy has always been a lack of precision in measurement, and I think the authors are to be congratulated on developing a method which will give us an accurate and dependable quantitative estimate of the amount of retained austenite. O. ZMESKAL*-As Chairman Queneau said, this is indeed an ingenious and needed determination. We have seen figures presented of 1/2 pct retained austenite determined, and I would like to ask the authors the lower limits of this method. How far down do they feel they can go in improving the technique still more?

Jan 1, 1948

By A. B. Kinzel

SILICON, unfortunately, is not in the same category as some other metals with respect to the absolute value of the highest purity material prepared. Tucker, in England, and Becket, in this country have devel-oped procedures for the purification of silicon, and Becket's process has made industrially available silicon of a purity of 99.8 per cent or better. However, even the term "silicon metal" may be a paradox to some people, although not more so than the term "amorphous" as applied to silicon. These terms come from commerce, and "metal" is used to distinguish industrially high-purity silicon from ferrosilicon, silicon-aluminum, and other high-silicon alloys. Alloys of iron and silicon with 95 per cent Si or less are known as ferrosilicon, with a designation of silicon content where necessary, and the terns "silicon metal" is invariably applied to the grades containing 96 per cent Si and higher. The Becket method of purification was referred to in a monograph on the Alloys of Iron and Silicon, and the Tucker procedure was described in some detail in that publication.1 In order to get silicon of still higher purity, a sample, prepared by the Becket method, analyzing 99.84 per cent Si, 0.020 Fe, 0.016 Al, 0.005 Ca, 0.025 C, 0.033 per cent 02, 0.006 H2, 0.006 N2, and 0.001 per cent Mn, was crushed to pass a 100-mesh sieve said further purified by a modification of Tucker's procedure. This modification differs from Tucker's method in that after treatment the 100-mesh alloy was centrifuged to remove the last traces of acid. Our directly determined analysis of this purified sample shows: Si, 99.952 per cent; Fe, 0.009; Al, 0.012; Ca, 0.003; C, 0.006; or 99.982 per cent. Silicon by difference equals 99.97 per cent. The variation between silicon by difference and silicon as directly determined is important. Although Tucker mentions the amount of insoluble matter in commercial silicon both before and after his treat-ment, he does not mention the existence of carbon in the alloy; neverthe-less, lie reports silicon by difference. Any final figure as to purity obviously results from agreement between direct determination and

Jan 1, 1939

By G. Howell Clevenger

FORMERLY great divergence of opinion existed in regard to the influence of copper in steel, as affecting its various physical properties. More recently the investigations of Stead,1 Breuil,2 Wigham,3 Burgess and Aston,4 Ball and Wingham,5 Miiller,6 Dillner,7 and others have shown fairly good agreement in the major points. Copper steel has been shown by these investigators to possess special properties which make it valuable for certain uses. The general range of composition of the useful alloys of copper and iron, and of copper, iron, and carbon, has been quite definitely established, for the former by Burgess and Aston,8 and for the latter by Breuil 9 and Stead.10 Stead 11 has removed one difficulty in reconciling certain of the earlier data by calling particular attention to the influence of carbon in copper steels. Another point which caused confusion in the earlier investigations, particularly in regard to " red-shortness," was the presence of sulphur. Failure to note the presence of sulphur often led to attributing " red-shortness " to the presence of small amounts of copper. Turner 12 has called attention to the fact that where copper exists in an iron ore it often occurs as the sulphide, so that the presence of copper in steel made from such ores might also, necessarily, mean the presence of sulphur. It is evident that the effect in this case might be quite different than where pure copper was added.

Jan 10, 1913

By L. W. McKeehan, W. C. Elmore

THE magnetic powder method, long used for roughly mapping magnetic fields, has recently been refined 1,2 for investigating the microscopic variations in the surface magnetization of ferromagnetic crystals. Bitter' first discovered regular powder patterns connected with the crystal structure of such specimens. Several other investigators3 have used Bitter's original technique, with slight modifications, to study the variation of the patterns with variations in the magnetizing field applied parallel to the surface, and their dependence upon the state of strain, of polish and of crystal cut. All of the explanations of these patterns on metallic ferromagnetics have been couched in general terms. In a preliminary report we have described an improvement in the powder technique which led us to the discovery of a new effect throwing considerable light on the magnetic secondary structure of alpha iron4 and of nickel' single crystals. We now report additional evidence confirming the existence and stability of a magnetic block secondary structure. SPECIMENS The following list describes the specimens used in the present investigation. DESIGNATION DESCRIPTION A1 Silicon ferrite furnished to us by Dr. W. E. Ruder, of the General Electric Co., for which he gave the following typical analysis: C, 0.05; P, 0.038; 5, 0.026; Mn, 0.15; Si, 3.24. Disk, 0.60 cm. diameter, about 0.05 cm. thick.

Jan 1, 1935

By C. E. Wood, E. P. Barrett, T. L. Joseph

The invention of the Bessemer converter process in 1856 added great impetus to the manufacture of steel and is one of the outstanding contributions to process metallurgy. Although the process of refining pig iron by passing air through the molten metal bears the name of Henry Bessemer, it should be mentioned in passing that William Kelley of Eddysville, Ky., worked on the process as early as 1847. Kelley was granted a patent on the process in 1857, inasmuch as he was able to prove priority in discovery.' After considerable litigation in 1865 the respective interests of Kelley and Bessemer were combined. On Sept. 10, 1856, Robert Mushet of England obtained his first patent on the application of manganese to cast steel. Mushet anticipated trouble in purifying iron by passing currents of air through it: His patent specified that steel made in this way often contained flaws and was red short or cold short. Mushet understood the refining of pig iron into steel well enough to realize the difficulties likely to be cncountered from oxidation of the iron. Mushet was not only an inventor; he was also an investigator. He understood the principle of selective oxidation which takes place in the converter process, and he realized therefore that the remedy for over-oxidation was attainable if a suitable metal could be found at a reasonable cost and in sufficient quantities. His first experiments were made in small crucibles holding a few ounces of metal. Later his work was conducted on a larger scale and with complete success. Manganese had been used in making steel a quarter of a century before the converter

Jan 1, 1927

By Dwight K. Smith, Greg Carter

Studies have been conducted on The properties of many deep well cementing compositions to determine their Strength behavior over curing periods to 180 days at elevated tem-peratures and 3,000 psi pressure. This pressure results in essentially the .vat, compressive strength as that obtained with much higher pressures in ac-cordance with the findings of an API subcommittee ' These different compositions include API C1asses A, E, and F cements containig additives such as retarders, berrtorlite, heavy weight materials and pozzolans. All compositions except mixtures of Poz-zolrrrts and hydrated lime show from mild to severe degrees of strength lass over a temperature rang from -730 to 320" F after setting. Pozzolatl-time compositions actually gain in strength with time at these high temperatures. Other chemical find physical properties evaluated to observe their inter-relation.ship with Strength loss show very little correlation except in per-meability. As retrogression in strength increases, the permeability of set cement increases. X-ray difraction patterns on the set products indicate the formation of certain compounds having little or no strength value in those cementing compositions where strength loss was more severe. INTRODUCTION As a result of the growing trend toward deep well completions, a study has been made on the properties of the various cementing slurries presently in use at elevated temperatures and pressure. The strength of these compositions is of prime importance in selecting the most suitable material for use at high temperatures, to determine WOC time and the proper time to perforate with a minimum of shattering. Of primary interest in this investigation was the strength behavior of various compositions currently in use, and the effect of additives on cement after long periods of curing under severe conditions. Earlier investigators have pointed out that the strength of some cements will increase with increasing curing temperature to about 220 to 340" F, but at higher temperatures a loss in strength occurs at extended time intervals. Studies by the API Mid-Continent District Study Committee on Oil Well Cements' outlined a testing procedure whereby field conditions of temperature and pressure could be simulated in the laboratory.' It was observed that retarded cements undergo changes at elevated temperatures and some lose as much as 50 per cent of their early strength when cured at high temperatures. The scope of these tests was limited to curing periods of 1 to 28 days; additives were not covered in this study. Saunders and Walker' found that the use of additives influenced the strength behavior of cements at high temperatures, but studies were conducted only to a seven-day curing period. Ludwig and Pence' conducted an investigation of two types of cements under elevated pressures and temperatures in an effort to explain the causes of this loss in strength phenomenon. It was observed that with retrogression in strength there were other physical and chemical changes which took place as the cement aged. Today there are a number of cementing compositions available for use at well depths below 10,000 ft. Since all these earlier investigations were limited in curing time as well as the number and type of compositions studied, it was believed that a more extensive study should be conducted on the properties of cements at elevated temperatures, and this work should include those compositions actually in general field use at this time.

By John McDonald

THIS report is a continuation of an earlier one with a similar title,1 to which the reader is referred for such details of procedure as do not appear here. A brief summary will be given of the objects and methods of the research at this time. It was pointed out in the previous paper that properties of magnesium alloys, as re-ported by different workers, often differ. This was thought to be due to differences in the preparation of the specimens tested. The ideal way to compare alloys would be to prepare each of them in so many ways that reasonable assurance would exist that the best properties of each alloy had been developed. The alloys would then be com-pared on the basis of these properties. The treatment actually given the alloys of these studies is necessarily a compromise with completeness. Nevertheless, enough treatments have been given so that a con-siderable degree of assurance exists that the properties obtained are representative of the alloy as such, and not merely of the manner in which it was worked and heat-treated.

Jan 1, 1940

By C. R. Ramachandra, C. C. Patel

Flotation of chalcopyrite from a low grade ore was studied by using different xanthates and dixanthogens as collectors and by conditioning the flotation pulp with oxidizing gaseous systems. The improvement in the recovery of chalcopyrite with the oxidizing systems was mainly due to the auto-activation of chalcopyrite, leading to the enhanced adsorption of xanthates and dixanthogens even when the latter were formed by oxidation of the xanthates. With air or oxygen as oxidizing system, the amount of ethyl xanthate required at pH 8.5 was much less than normally employed in the industry, the recovery being 97-99% of chalcopyrite with a concentrate of 24% copper. With isopropyl and isoamyl xanthates, the recovery was improved but the grade was lowered. By conditioning the pulp with air-CO2 or oxygen-CO2 mixture, the recovery was lowered with ethyl xanthate only, mainly due to the depressant action of bicarbonate formed. Flotation with dixanthogens gave cleaner concentrates of chalcopyrite. because iron pyrite did not float with these collectors. Of the dixanthogens tried, diisopropyl dixanthogen gave the highest recovery, 99% chalcopyrite with a concentrate containing 28.5 to 30% copper, when the pulp at pH 8.5 was condi-tioned with air. Isopropyl dixanthogen was found to be the best collector of all the xanthates and dixanthogens studied. It was found that the adsorbed ethyl, isopropyl and isoamyl xanthates at chalcopyrite surface, activated by cupric sulfate, and at iron pyrite surface were oxidized to the corresponding dixanthogens to different degrees in presence of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture.' The dixanthogen formed at chalcopyrite surface was, however, firmly adsorbed while that at iron pyrite surface was easily desorbed. Since dixanthogens formed have greater hydrophobicity than the corresponding xanthates, as revealed by contact angles,1,2 the former were expected to improve the flotation results. It was, therefore, thought desirable to find out the effect of air, oxygen, air-carbon dioxide mixture and oxygen-carbon dioxide mixture on the selective flotation of chalcopyrite when individual xanthates were used as collectors. The effect of direct use of dixanthogens as collectors on the selective flotation of chalcopyrite was also investigated. For these studies, low grade chalcopyrite ore, received from the Indian Copper Corp., Ltd. (I.C.C.), Ghatsila, Bihar, was employed. At the milling plant of the I.C.C., chalcopyrite is floated at a pH of 8.5, employing ethyl xanthate as collector. EXPERIMENTAL Materials Employed: XANTHATES - Ethyl, isopropyl and isoamyl xanthates of potassium were prepared in a pure state by the methods described earlier.4 A 0.03% aqueous solution of a xanthate was freshly prepared in air-free distilled water for flotation studies. DIXANTHOGENS - Diethyl, diisopropyl and diisoamyl dixanthogens were prepared by the oxidation of xanthates by iodine and purified by extraction with petroleum ether. A 0.03% alcoholic solution of dixanthogen was used as a collector. FROTHER - A 0.2% solution of pine oil in ethyl alcohol was employed. SODIUM CARBONATE - A 0.4 N solution was used. ORE - The composition of the -100 +200-mesh size (Tyler standard) powdered ore, as determined by standard methods of analysis, was: copper 1.57%, iron 10.29%, sulfur 3.15% and acid insolubles 66.10%. Iron present as chalcopyrite (CuFeS2) was 1.38%, while that present as iron pyrite (FeS,) was 1.37%. Both chalcopyrite and iron pyrite were found to be liberated from the gangue minerals and from each other, as observed under a microscope. Flotation of Chalcopyrite with Xanthates in Presence of Different Gaseous Systems: Fifteen grams of -100 + 200-mesh size ore were shaken well with 100 ml of distilled water. The pH of the pulp was adjusted to 8.5 by the addition of sodium carbonate solution. Then 0.1 ml of xanthate solution (0.005 lb xanthate per ton of the ore) was mixed with the pulp, and the latter together with washings transferred to a

Jan 1, 1963

By C. M. Schwartz, A. E. Austin, W. B. Wilson

High-temperature X-ray diffraction studies were conducted with Th-U alloys with up to 10 wt pet U. The solid solubility of uranium in thorium as a function of temperature was determined by the method of lattice parameters. Thorium will dissolve up to 2.5 wt pet U at 950°, 4.5 wt pet U at 1150°, and 7.5 wt pet U at 1250°C. Determinations were made of the temperature of the transition of thorium and of the effect of uranium upon the transition. The a to ß transition for thorium was observed to occur at 1330' ±20°C. Mean coefficients of expansion were calculated for thorium and two alloys, and for ThO2 in contact with the thorium, using X-ray lattice-parameter data. Values obtained at 950° C for thorium and Tho2 were 12.1 and 9.40 X 10-6 per OC, respectively. Impurities obtained during the X-ray exposure were identified by diffraction and were essentially Tho2 and ThC, with two additional unknown phases being detected. The effect of the impurities upon the results is discussed. DIRECT investigation (i.e., high-temperature X-ray diffraction studies) of the phase diagram of thorium-rich uranium alloys has been shown to be necessary since recent work1 - has disclosed the presence of an allotropic transformation near 1400°C in pure thorium with the room temperature face-centered-cubic phase transforming to a body-cen-tered-cubic structure at the elevated temperature. The effect upon the transition of the addition of uranium to thorium and of the solubility of uranium in thorium at high temperatures remained unknown, yet was of interest in understanding fabrication procedures and elevated temperature use. The present work was undertaken to provide information in this area by determining the transition temperature, the effect of uranium on the transition temperature, and the solubility of uranium in thorium as a function of temperature. Experimental Work The high-temperature diffraction data were obtained using a camera especially designed for the purpose3 and capable of reaching temperatures in excess of 2000°C at pressures as low as 1 x 10." mm Hg. Temperature regulation was provided by regulating the power input to ±0.1 pet variation, and by regulating the water flow through the camera jacket to provide a constant thermal load. The X-ray sample was a rod nominally 80 mil diam, which was further turned down to 20 mil and then etched to 18 mil over 1/2 in. of one end. This was placed in the sample holder and mounted on the camera so that the smaller part was surrounded by a cylindrical tantalum-sheet radiation-type heating element. Diffraction from the sample was recorded on film after passing through a slot in the heating element and radiation-baffle shield and through beryllium vacuum windows. The X-ray film mounting was of the Straumanis type4 with a camera diameter of 114.59 mm. Since previous work of Chiotti' indicated that impurities considerably alter the transition temperature, chemical analysis of the arc melted iodide crystal-bar thorium samples was obtained prior to testing. The analysis disclosed the material to contain as low as 0.001 ±0,0002 wt pet H and 0.007 ±0.001 wt pet 0. Carbon was 0.003 wt pet and nitrogen less than 0.002 wt pet. This material was sealed in mild steel in an inert atmosphere and subsequently hot rolled to 3/8-in. diam rods at a temperature of 732°C. Following removal of the jacket, the material was pickled and cold swaged to 1/8-in. rods, from which the diffraction samples were prepared. The alloys were similarly prepared, with the uranium being added during arc melting. The uranium analyses of the alloys prepared appear in Table I. The experimental procedure for diffraction examination of the three samples of high-purity thorium differed from those of the Th-U alloys. The original practice, later modified, consisted of pumping down the camera with the diffusion pump on and then admitting liquid nitrogen to the cold trap of the system. This was modified for the Th-U alloys by maintaining liquid nitrogen in the cold trap at all times before and while the diffusion pump was heated. This minor change produced a reduction in the amount of carbon pickup by the sample during exposure to the diffusion-pump vapors. The sample was brought to the desired test temperature and exposed for 21/2 hr at pressures which were usually 2 x 10-6 mm Hg, or lower. Exposures were made at

Jan 1, 1959

By C. H. Chou, Albert Sauveur

The following experiments were conducted in order to study the influence of the rate of cooling through and below solidification on the dendritic structure (macrostructure) and microstructure of some hypo-eutectoid steel. The steel selected was of commercial grade and had the following composition: C, 0.40 per cent.; Mn, 0.85; Si, 0.70; P, 0.099; S, 0.043. After melting in vacuum in an Arsem furnace, the various samples were allowed to solidify and to cool to room temperature as indicated in Fig. I. Samples were thus obtained representing all possible combinations of slow and fast cooling through the various ranges of temperatures indicated, namely: (I) zone of solidification or primary crystallization, (2) zone of granulation, and (3) zone of secondary crystallization. The location of the different temperature zones in the iron-carbon equilibrium diagram is shown in Fig. 2. The authors adopted Belaiew's notations. The designations of the various samples readily indicate their treatment, as will be apparent from Table 1. Sample SSS.—This sample was slowly solidified and cooled to room temperature in the crucible in which it was melted. The dendritic (macro) structure is shown in Fig. 3. The dendrites an: sharp and dis-

Jan 1, 1930

By James H. Taylor

"Titanium is a widely distributed, dark grey metal1ic element found in small quantities in many minerals. It has no important uses." Happily, this early quotation proved to be wrung; titanium has, on the contrary, found a large number of very important uses. The error in the 1926 quotation illustrates the problems associated with forecasting the future development of any metal. 'The paper will nevertheless attempt to estimate what will happen to the European titanium industry over the coming decade with slightly more accuracy. It was not until 1955 that anything other than pilot plant facilities were installed in Europe. In 1955 IMI's plant in England, two plants in Germany, one in France and one in Sweden came into operation. All the companies associated with titanium installed melting furnaces but only IMI Titanium has forging and rolling facilities devoted solely to the production of titanium. The other firms rely on the use of equipment of their parent steel companies for processing the me1 ted titanium ingots.

Jan 1, 1982

By Richard Moldenke

The paper describes the making of pig iron from the Mayari iron ores of Cuba. The outstanding feature f this pig iron is a considerable content f nickel and chromium. As a marked improvement in the quality of castings has been noted when this iron is used in the foundry mixtures, a series f melting tests f mixtures of great variety of composition was conducted with the idea f getting comparative strengths from which the effect of nickel¬chromium could be seen. These tests, on account of their number, and degree of accuracy desired, were made by the crucible melting method. The paper gives the tables of results, a series f curves showing the inter-relation of the elements involved, and a summary of the conclusions derived. THE presence of nickel-chromium in pig iron made from Cuban ores is so well known that the word "Mayan" is unconsciously associated with it. Since 1904, when exploration of the Mayari deposits of iron ore in northeastern Cuba was undertaken, there has been increasing interest in these ores. The TRANSACTIONS contain numerous references to them. This iron ore, which is shipped to the. United States in the nodulized state, has been thoroughly tested and found very valuable; the deposit covers over 25,000 acres and there is in sight over 500,000,000 tons of ore that, by systematic mining, runs practically constant in composition. With nickel and chromium present, also titanium in sufficient quantities to attract attention, as well as extremely low phosphorus and sulfur contents, the iron founder is naturally interested in the utilization of Mayari ore for pig iron for the better grades of finished iron products. The present point of consumption of Mayari ore is at Sparrow's Point, where Mayari pig iron of any desired composition is made. The com-

Jan 9, 1922

By Orlando Romig

PART I-PREPARATION OP METALLIC SINGLE CRYSTALS WITH ESPECIAL REFERENCE TO SINGLE CRYSTALS OP ZINC? As metals and alloys are composed, of, an aggregate of allotriomorphic crystals or grains, each possessing an individual orientation, the physical characteristics of a metal or an alloy are closely related to the properties of the individual crystals. The preparation and study of single metallic crystals are, therefore, matters of considerable importance. The advent of the X-ray spectrograph as a valuable metallurgical tool has magnified the importance of this subject, because the interpretation of some X-ray spectrographs is difficult unless single crystals are used in these studies. PREVIOUS WORK The first paper, as far as the writer knows, on the behavior or preparation of single crystals of metals is by Baker.1 He describes the behavior of extruded wires of sodium and potassium. These wires, when pulled in tension, instead of I showing the usual conical fracture common to most metals, had a chisel-shaped fracture when they were broken. I and II, Fig. 1, have a similar fracture. Baker checked his results by preparing single crystal wires from molten sodium and potassium and observing their properties. He prepared the wires by filling glass tubes, under oil, with the molten metal. The surfaces of the strained wires showed slip bands of remarkable clearness of which photographs are shown in his paper. He concluded that these wires were single crystals and "that the portions of the metal brought into play are cubes. Such cubes, when placed so that a plane through 'two opposite edges was parallel to the axis of the wire, would allow of lateral contraction by faces gliding over one another in one direction only and not in the direction at right angles."

Jan 1, 1927

By George A. Roche

Investment in growth stocks is the most assured way of achieving superior, long term investment accomplishment. There are many criteria used to select growth companies but the most important is a combination of superior management operating in an industry with above average growth potential. This growth stock approach is the cornerstone of investment strategy for two of the three mutual funds sponsored by the Price organization and for its private clients. However, during the past five years inflation has accelerated due to a variety of factors including the inability of government to meet seemingly unlimited needs with limited revenue sources.

Jan 4, 1972