By A. L. Mincher, W. F. Sheely

Mechanical properties of columbium have been studied over the temperature range of -196 to 1093oC. The decreased strengthening influence of cold-work at temperatures below ambient has been interpreted in terms of the Peierls-Nabarro effect. Maxima in the rate of strain hardening observed during tensile testing in the range 250-600°C. have been correlated with interstitial impurities to indicate the temperature ranges at which carbon, oxygen, and nitrogen, respectively, are responsible for strain aging. THE growing need for structural materials for use above the useful service temperatures of the iron-, nickel-, or cobalt-base alloys has caused the refractory metals to be considered as potential engineering materials. These metals, which include columbium, tantalum, molybdenum, and tungsten, are called refractory because the lowest melting point among them,that of columbium, is about 1000°C higher than the average melting temperatures of conventional high-temperature alloys. They are all body-centered cubic transition metals and, as such, their mechanical properties have basic characteristics which distinguish them from the face-centered cubic metals. For example, all show a much steeper rise in strength with decreasing temperature below room temperature than do the face-centered cubic metals, and their mechanical properties are strongly influenced by interstitially dissolved impurities. In order that these new metals may be used efficiently, it is necessary that their characteristics of behavior be fully known. In this paper, the mechanical properties of columbium will be examined over a wide range of temperatures. In particular, the influences of cold-work and individual species of interstitial impurity atoms on mechanical properties will be described, and basic mechanisms which may control the observed characteristics will be explored. EXPERIMENTAL The material used in this investigation was Union Carbide Metals Co. columbium roundels consolidated to four 4-in. diam ingots, three by consumable-electrode arc melting and one ingot by electron beam melting. Impurity contents of the ingots and methods of ingot conversion and treatment are summarized in Table I. The only metallic impurity occurring in any significant quantity was tantalum at about 0.1 pct. Iron, silicon, titanium, and zirconium were each less than 0.015 pct; boron was 1 ppm or less. This should have no appreciable influence on properties. The electron beam melted material, being the purest, will be used as the basis for comparison in the discussions to follow. Tensile tests were conducted from-196 to 1093oC, on both cold-worked and fully recrystallized arc-melted and electron-beam melted columbium using standard 1/4-in. diam, 1-in. long gage length test specimens. A strain-rate of 0.005 in. per in. per min was employed until the 0.2 pct yield strength was achieved and then the strain-rate was increased to 0.05 in. per in. per min for the balance of the test. Samples were protected in an inert atmosphere at tests above 300°C. The tensile properties obtained on the electron-beam melted columbium, E, in both the cold-swaged and recrystallized conditions are given in Fig. 1. The yield strength data of Dyson, et al.,' obtained on recrystallized electron beam melted columbium and the tensile strength data reported by Tottle2 on powder metallurgy columbium are included in Fig. 1. The material used by Tottle had been purified by vacuum sintering. There is excellent agreement between Dyson's data and those obtained in the present investigation. The tensile strengths obtained by Tottle were slightly greater than those obtained in this investigation on electron-beam melted columbium but varied with temperature in a similar manner. Tottle's data showed a maximum in tensile strength near 500°C, as did our data on electron-beam melted material, and also showed a small maximum at 300°C. The significance of these maxima will become evident later in the discussion. The tensile properties of cold-swaged and recrys-tallized arc melted columbium are plotted in Fig. 2. It was found that the properties of the recrystallized arc-melted columbium from all three heats showed very close agreement except at temperatures between about 500" and 800°C. A reason for this range of disagreement will be suggested in the discussion. The generally good agreement, however, attests to the ability of cold-working and subsequent recrystal-lization to erase the effects of the three different primary breakdown procedures and to produce nearly equivalent structures in the samples derived from the three different heats. wesse13 reported tensile data on columbium having interstitial impurity contents between those of the

Jan 1, 1962

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

The tensile properties, creep resistance. and thermal stability of highly alloyed Ti-Al-Zr alloys were examined. On the basis of these studies, the Ti-7Al-1ZZr composition was selected for more complete evaluation. The alloy was found to be weldable and free from excessive directionality. In addition, it developed maximum properties without requiring heat treatment other than an annealing operation in the alpha field. The alloy was recommended for scale up and is presently being investigated on a production-level basis. One of the more attractive properties of titanium alloys is their ability to withstand stress at moderately high temperatures, and a considerable amount of effort has been devoted to increasing the maximum service temperature of titanium alloys. This work has suggested that the optimum alloys for high-temperature service will be single-phase a (close-packed hexagonal) alloys containing significant amounts of aluminum. However, the maximum amount of aluminum which can be alloyed with titanium is between 6 and 8 pct,l since at high-aluminum contents an embrittlement reaction occurs in the anticipated service temperature range, 800" to 1100°F. It has been shown that the embrittlement reaction involves decomposition of the high-aluminum a phase to one or more new phases.' Since this reaction does not occur at intermediate or low-aluminum contents, it was felt that intermediate Ti-A1 alloys might be strengthened by a-soluble ternary additions without inducing the embrittlement reaction. The first alloying addition considered was tin, which shows extensive solubility in a titanium and has moderate strengthening tendencies. Unfortunately, it was soon apparent that tin also promoted the embrittlement reaction, and that to obtain a stable alloy, the aluminum content had to be reduced as the tin content was increased. The second alloying addition considered was zirconium, which is similar to tin in its effects on titanium. This element did not contribute to the embrittlement reaction and, in fact, appeared to increase the maximum amount of aluminum which could be alloyed with titanium without inducing instability. This paper describes an investigation of the Ti-A1-Zr a alloy region. Alloys containing from 4 to 12 pct A1 and from 6 to 15 pct Zr were examined. The properties of these alloys are described and the bases for selecting an optimum composition is outlined. This composition, Ti-7A1-12Zr, is presently being scaled up in tonnage quantities, and is being evaluated extensively throughout the industry. In addition to presenting the basis for its selection, this paper presents a description of the properties developed in laboratory material as determined during the alloy investigation. These properties suggest that this alloy can fill an important position in applications requiring light weight, fabrica-bility, weldability, and strength to 1000oF or higher. EXPERIMENTAL PROCEDURES Titanium alloy ingots were prepared by inert electrode arc melting under an argon atmosphere. Alloying elements used were 110 Bhn titanium sponge, high-purity aluminum, and reactor-grade zirconium. Pancake-shaped ingots were prepared weighing approximately 300 g. The composition of the ingots was checked by weight measurements before and after melting. The pancake ingots were forged at 2000°F to approximately half their original thickness to give a flat plate roughly 1/2 in. thick. This plate was then rolled at 1800' to 1600°F to 0.250 in. thick. All of the alloys examined fabricated well. However, alloys containing 15 pct Zr tended to overheat due to exothermic oxidation, and scaling was excessive. As might be anticipated from its effect in decreasing the ß transus, increased zirconium appeared to improve fabricability somewhat, especially during rolling at lower temperatures. Except for a limited study of heat-treatment response, all alloys were examined in the a-annealed condition. Prior to heat treatment the a and ß tran-sus temperatures were determined by metallo-graphic examination of samples quenched after annealing at 50-deg intervals in the transformation region. These data are shown in Fig. 1. Recrystal-lization appeared to occur in about 1 hr in the range 1300º to 1500ºF. Therefore, alloys were annealed for 1 hr at 1550ºF (4 and 5 pct Al), 1600ºF (6 through 7-1/2 pct Al), or 1650°F (8 or more pct Al). This produced an equiaxed a grain structure. In most alloys, a "ghost" structure was visible after the a-annealing treatment, as shown in Fig. 2. This structure apparently resulted from the acicular

Jan 1, 1963

By K. P. Mukherjee, K. P. Gupta, J. Bandyopadhyaya

Even though a lot of work has been done in the past to establish phase equilibrium in the Cu-Si system a re cent investigation casts some doubt about the existence and crystal structure of some of the phases that form in the composition range of 15 to 25 at. pct Si in Cu. The present investigation was carried out using high temperature X-ray diffraction technique along with other standard techniques to study the phases in this composition range. The high temperature 6 phase appears to be tetragonal with parameters a,, = 8.815A, c, = 7.903A, and co/ao = 0.896. The reported bcc E phase exists at room temperature and at least up to 780°C and appears to undergo a transformation near 600°C. The phase appears to be cubic but not of the bcc type. The ? phase appears to undergo a transformation, as has been indicated by earlier investigators, and the low temperature form of .? phase is tetragonal with parameters a, = 7.267A, co = 7.8924, and co/ao = 1.086. THE Cu-Si binary system has been investigated by several investigators1" and several intermediate phases,?,e,?' at lower temperatures and ?,ß,0,e, and ? at higher temperatures, were observed between terminal solid solutions of copper and silicon. Even though the existence of the e phase and the transformation in the ? phase were reported in many early works, in a recent study of this system Nowotny and Bittner6 doubted the existence of the e phase and phase at 550°C. Among the high temperature phases, the 6 phase was reported to have a complex cubic structure with parameter a, = 8.805A.7 Nowotny and Bittner, however, suggested that the structure of the 6 phase might be of CsCl type. In order to check these contradictory reports the present study was taken up to investigate the Cu-Si binary system in the composition range of 17 to 25 at. pct Si. EXPERIMENTAL PROCEDURE Weighed amounts of copper (99.99 pct) and silicon (99.9 pct) were induction melted in recrystallized alumina crucibles under argon gas atmosphere. The alloys containing 17, 18, 20, 21, 21.2, 22, and 24 at. pct Si were annealed in evacuated and sealed quartz capsules at 700°C for 3 days and subsequently water quenched. Other than this annealing, the 21.2 at. pct Si and 24 at. pct Si alloys were annealed at 550°C for 10 days, the 17 at. pct Si alloy was annealed at 750°C for 3 days, and the 22 and 24 at. pct Si alloys were annealed at 780°C for 2 days. All annealing temperatures were controlled to within *l°C. Alloys after quenching were subjected to metallographic and X-ray diffraction investigation. A solution containing 5 g FeC13 + 10 cc HCl + 120 cc H2O diluted with six times its volume with water was used as etching reagent. A 114.6 mm diam Debye Scherrer camera was used for obtaining diffraction patterns. The 17, 21.2, and 24 at. pct Si alloys were subjected to high temperature diffractometry using a Tempress Research High temperature attachment and a GEXRD VI diffractometer. For the 6 phase (17 at. pct Si alloy) powder specimen from a 750°C annealed alloy was reheated to 750°C in the high temperature attachment for 1½ hr before taking a diffraction trace. A 550°C annealed and slowly cooled phase (24 at. pct Si) alloy was first reheated to 550°C. a diffraction trace was made after annealing it for 2 hr, and subsequently it was heated to 716OC and kept at this temperature for 2 hr before taking a diffraction trace. For the e phase (21.2 at. pct Si alloy) a 550°C annealed and slowly cooled specimen was heated first to 425°C and annealed at this temperature for 2 hr before taking a diffraction trace. Subsequently, the specimen temperature was raised to 495", 540°, 603", 635", 682", 720°, and 748°C and homogenized at each temperature for 1 hr before taking diffraction traces. The powder specimen temperature was controlled to within +2oC at each temperature and argon gas, purified by passing it at slow rate through a fused CaC12 column, hot (800°C) copper and titanium chips and finally through a P2O5 column, was used to prevent oxidation of the powder. For all X-ray work copper-radiations at 25 kv, 15 ma (for Debye Scherrer technique), and 40 kv, 20 ma (for diffractometer tech-nique) were used. RESULTS AND DISCUSSION At 700°C the alloys containing 17 to 21 at. pct Si showed two phases while the 21.2 at. pct Si alloy was found to be single phase. The X-ray diffraction patterns of the two-phase alloys were consistent with the phase (ßP-Mn type structure) and the phase (21.2 at. pct Si) patterns. The diffraction patterns of the 17 at. pct Si alloy quenched from 750" and 700°C were identical. According to the accepted Cu-Si phase dia-gram4,5,10 the 17 at. pct Si alloy at 750°C should be in the (k + 6) two-phase region and very close to the -phase boundary. The identical patterns possibly resulted from the decomposition of the 6 phase on

Jan 1, 1970

By R. J. Reynik

A semiempirial small flunctation theory of diff- sion in liquids is presented, which employs a fluctuation energy assumed quadratic for a small atomic or molecular displacement and Einstein's random-iralh model. The resulting diffusion equation is given by In these equations. D is the diffusivity, is the average liquid shite coordination number (at interatomic distance d. cm. T is the absolute temperature, xu. em, is (the diffusive displacement. K, is the quadratic fluctuation energy force constant, and rg, cm, are the radii oj diffusing atoms A and B, respectively. The quantities Xn and K are calculated from the computer-filled values of the slope and intercept. respectively. The radius of self-diffusing atom or radii and of diffusing atoms A and B are eta United and compared with values reported in the literature.. The predicted linear variation of diffusivity with. It tempera lure htm been observed in approximately thirty-iire metallic liquid systems, and in over seventy-fiee other liquid systems, including the organic .alcohols, liquified inert gases, and the molten salts, ALTHOUGH the average density within a macroscopic volume element of liquid is constant for fixed total number of atoms. pressure. and temperature, there exist microscopic: density fluctuations within the respective volume element. As such the microscopic volume available to an atom and its Z first nearest neighbors at any instant of time fluctuates above and below the average volume available to these atoms. If one assumes that liquid state atoms vibrate as in a solid. and further postulates that the mean position of any atom in the liquid state is not stationary. but shifts during every .vibration a distance 0 5 j 5 xo. then every atom in the liquid state continuously undergoes diffusive displacements which vary in the range 0 5 j 5 ro. Mathematically. for a binary liquid system consisting of atcrms A and B. the maximum diffusive displacement. .YO, is defined by the equation: where d is the average liquid state interatomic distance at specified liquid state coordination number Z. and v~ \ and vg are the effective radii of diffusing atoms A and B: respectively. For self-diffusion. r^ equals rg , and Eq. [I.] reduces to: It is interesting to note that Eq. [l] or [2] can be used to compute the radii of the diffusing atoms, provided one had an experimental evaluation of xo. As such. the computed radii could be compared with metallic or crystallographic ionic radii to ascerlain the electronic character of the diffusing atoms. Thus it is proposed that in the liquid state the n~otion of an atom relative to its original equilibrium position of oscillation represents the thermal vibration of any atom and its Z first nearest neighbors. while the small and variable displacements. 0 5 1 5 xc,. of the centers of oscillation represent the complex diffusive motions of the atoms at constant temperature and pressure. This is consistent with data obtained from slow neutron scattering by liquids1 ' and resembles an itinerant oscillator model of the liquid state.'" It is further postulated that the atomic displacements characterizing the liquid state diffusion process are essentially a random-walk process. As such. it nlay be described by Einstein's equation:' where D is the diffusivity. sq cm sec-'. j2 is the mean square value of the diffusive displacement. and i> is the frequency of density fluctuations giving rise to diffusion. FORMULATION OF DIFFUSION EQUATION The effective spherical volume occupied by an atom, as a consequence of a microscopic density fluctuation which enlarges the volume available to any atom, exceeds its average liquid state atomic volume by an amount: where AV is the enlarged spherical volume, v is the radius of the diffusing atom. and j is the elementary displacement distance from the original center of oscillation of the vibrating atom to a new center of oscillation position. For small atomic displacements. where c is a constant whose value depends upon the assumed geometry of the enlarged volume. For a spherical increase in volume, c equals 4nr2. Following the treatment of Furthl' and ~walin." assuming the enlarged volu~nes AL7 for the diffusing atoms are distributed in a continuunl. the probability of finding a fluctuation in the size range 0 5 j 5 xo defined by Where c includes the geometric constant cl and Eij) is the fluctuation energy causing the volume change. But the proposed model assumes all the Z first nearest-neighbor atoms are centers of oscillation. and hence the probability that any of these atoms is adjacent to a fluctuation of magnitude 05j5xo is unity. Thus:

Jan 1, 1970

By B. A. Cheadle, K. P. Steward

Axial tensile, ring tensile, closed end burst, and free end burst tests were done at room tempe.vature and 300°C on three batches of Zircaloy-2 sheathing zuith different textures. Knoop hardness tests were also done on all batches. The mechanical properties of the tubes were largely dependent on the percentages of cold work, but were also markedly affected by the textures, particularly with respect to deformation behavio'r. The deformation behavior observed confirmed Picklesimer's predictions, zuhereas Knoop hardness results could be correlated with texture and yield strength anisotropy after the ,method of Wheeler and Ireland. From the mechanical properties, and from efjectiue strain values deterrlzined at the fractures using a photoqid technique, it zuas concluded that tubing witlz a single preferred orientation of radial basal poles best combines strength and ductility for any given deqee of cold work. THE mechanical properties required in collapsible Zircaloy-2 fuel sheathing for water-cooled power reactors are strength to resist wrinkling deformation by coolant pressure and ductility to accommodate a small amount of deformation in service without rupturing. Zircaloy-2 tubing during fabrication develops pre- ferred orientations of the a Zr grains due to aniso-tropic deformation behavior, and these textures markedly affect mechanical properties. Picklesimer' had predicted the deformation behavior of tubes with various textures, but the texture required to provide the optimum strength and ductility for a given degree of cold work has not been reported. To investigate this problem, tests at three transverse to axial stress ratios were done at room temperature and 300°C on three batches of Zircaloy-2 tubing covering a wide range of textures and percentages of residual cold work. Knoop hardness values were also measured to correlate with preferred orientation and yield strength anisotropy after the method of Wheeler and relland.' 1) MATERIAL For this investigation, three batches of tube-reduced tubing were chosen from the Zircaloy-2 sheathing produced for the Douglas Point Reactor. Individual tubes were 191/2 in. long, 0.600 in. OD, and 0.0165 in. nominal wall thickness. The identities of the batches, together with their textures, are shown in Table I. The tubes had the normal Zircaloy-2 composition3 of 1.5 wt pct Sn, 0.3 wt pct Fe, Ni, Cr combined with the following oxygen concentrations: Batch VII 1140 to 1390 ppm 0 Batch VIII 1400 to 1750 ppm 0 Batch IX 880 to 1320 ppm 0

Jan 1, 1968

By C. G. Dunn

WITH respect to theories of recrystallization in metals plastically deformed, it has been said that the present status of this subject is far from satisfactory.1 It may also be said that before any mechanism of recrystallization for metals and alloys can be set forth in a satisfactory manner, there must be made available considerable data on orientation changes that occur during the deformation and recrystallization processes. Although extensive data have been published on recrystallization in single crystals and in polycrystalline specimens, more results of a type that can be classified according to simple orientation changes would be desirable in this complex field. It might even be said that before classifications are made according to types of orientation changes, it may be possible to classify a considerable amount of data into certain kinds of orientation states if groups of common or nearly common orientation occur. Methods for computing the probability of occurrence for various types of groups have been published2 and it has been pointed out in particular that it should be possible to analyze orientation data for high-order twin relationships between old and new grains even when agreement is not at all exact. In this connection, work on recrystallization in silicon ferrite reported in a paper concerned with complex groups of annealing twins' indicated that some data were consistent with primary nucleation occurring according to a second-order or a third-order twin transformation. However, further work in this latter direction was definitely needed. It is, therefore, the purpose of the present paper to report data and analyses for primary nucleation in silicon ferrite following small deformations that have been carried out at the Pittsfield Works' Laboratory of the General Electric Co. Analyses have been made with the aid of standard groups of twins that are reported elsewhere .4 PREPARATION OF SPECIMENS AND EXPERIMENTAL PROCEDURE The material used in the present investigation was taken' from the same heat of steel as that used in a prior report.3 The finished strip in both cases was made by the Allegheny-Ludlum Steel Corporation according to methods that produce a high degree of preferred crystal orientation. Samples with large grains had the following composition: 3.45 per cent Si, 0.003 C, 0.008 P, 0.020 S, 0.075 Mn, 0.031 Al and 0.072 Cu. Thickness of specimens was 0.012 inches. Plastic deformation was produced by cold-rolling the samples on a mill with

Jan 1, 1945

By Edward Saibel

The various theories that have been advanced to explain or predict the conditions under which a metal fractures may be divided into two categories: First, there are the macroscopic theories generally used in engineering practice. These are empirical in nature and limited in application. For example, the maximum normal stress criterion, which is quite satisfactory for a mild steel in simple tension at atmospheric pressure,' no longer suffices when this steel is pulled under hydrostatic pressure.2 In all of these empirical theories, the critical condition characteristic of the material and of the loading conditions must be obtained experimentally. Secondly, there are the theories based on interatomic forces,3'4 or on the energy required to form new surfaces.5,6 These have all dealt with the theoretical evaluation of the tensile stress necessary to bring about rupture in a purely brittle manner; that is, without plastic flow preceding fracture. All of these attempts have led to values of the tensile strength of crystals or of polycrystalline bodies that are 100 to 1000 times higher than observed values. On this account, it has been thought necessary by some investigators to conceive of a microcrack structure or distribution of flaws throughout the specimen such that the resulting stress concentrations provide the factor necessary to bring about agree- ment between calculation and experiment. It has been pointed out by several observers' that this point of view is highly unrealistic, in that the weakening effect of these flaws or microstructures must be very uniform from specimen to specimen, since the fracture stresses found for various specimens of the same material tested under similar conditions are so nearly constant. Furthermore, since calculations based on atomic forces or atomic energy are for purely brittle fracture, a condition probably never satisfied in tests, agreement is hardly to be expected. Thermodynamic Theory of Fürth In order to resolve this apparent discrepancy between the theoretical cohesive strengths and the observed fracture strengths, Fürth8 advanced a thermodynamic theory of the tensile strength of isotropic bodies based on work of Born relating to the melting of crystals. Assuming an isotropic material free from imperfections and flaws, behaving elastically up to the breaking point, and assuming a connection between rupture and the melting phenomenon, Fürth obtains an expression for the rupture stress a, in the form where Q is the melting energy per unit mass, p is the density, and is Poisson's ratio. Furth compares fracture stresses computed from Eq I with the fracture stresses of metals as given in the Landolt-Bernstein Tables (1927) and in the Hand-

Jan 1, 1947

By Edward Saibel

The various theories that have been advanced to explain or predict the conditions under which a metal fractures may be divided into two categories: First, there are the macroscopic theories generally used in engineering practice. These are empirical in nature and limited in application. For example, the maximum normal stress criterion, which is quite satisfactory for a mild steel in simple tension at atmospheric pressure,' no longer suffices when this steel is pulled under hydrostatic pressure.2 In all of these empirical theories, the critical condition characteristic of the material and of the loading conditions must be obtained experimentally. Secondly, there are the theories based on interatomic forces,3'4 or on the energy required to form new surfaces.5,6 These have all dealt with the theoretical evaluation of the tensile stress necessary to bring about rupture in a purely brittle manner; that is, without plastic flow preceding fracture. All of these attempts have led to values of the tensile strength of crystals or of polycrystalline bodies that are 100 to 1000 times higher than observed values. On this account, it has been thought necessary by some investigators to conceive of a microcrack structure or distribution of flaws throughout the specimen such that the resulting stress concentrations provide the factor necessary to bring about agree- ment between calculation and experiment. It has been pointed out by several observers' that this point of view is highly unrealistic, in that the weakening effect of these flaws or microstructures must be very uniform from specimen to specimen, since the fracture stresses found for various specimens of the same material tested under similar conditions are so nearly constant. Furthermore, since calculations based on atomic forces or atomic energy are for purely brittle fracture, a condition probably never satisfied in tests, agreement is hardly to be expected. Thermodynamic Theory of Fürth In order to resolve this apparent discrepancy between the theoretical cohesive strengths and the observed fracture strengths, Fürth8 advanced a thermodynamic theory of the tensile strength of isotropic bodies based on work of Born relating to the melting of crystals. Assuming an isotropic material free from imperfections and flaws, behaving elastically up to the breaking point, and assuming a connection between rupture and the melting phenomenon, Fürth obtains an expression for the rupture stress a, in the form where Q is the melting energy per unit mass, p is the density, and is Poisson's ratio. Furth compares fracture stresses computed from Eq I with the fracture stresses of metals as given in the Landolt-Bernstein Tables (1927) and in the Hand-

Jan 1, 1947

By James A. Crookston, William D. Fitzpatrick

Committee C-8 of the American Society for Testing and Materials defines "Refractories" as "Material, usually nonmetallic, used to withstand high temperature," and it defines the term "Refractoriness" thus, "In refractories the capability of maintaining the desired degree of chemical and physical identity at high temperatures and in the environment and conditions of use." The ability to withstand high temperatures is critical to classifying a material as a "refractory." However, as the foregoing definition of "refractoriness" implies, the refractory material may be subjected to and is expected to resist not only high temperatures but a variety of other destructive forces incident to its use. These include abrasion, impact, thermal shock, chemical attack, and high level loads at high temperatures. The various industrial applications of refractories represent an infinite variety of combinations and degrees of severity of these destructive forces, including high temperatures. Naturally, such a variety of application conditions leads to a need for a wide variety of refractory products to satisfy those conditions. The number of refractory products available is great enough that some form of classification is necessary to a discussion of refractories. Refractories may be classified in several ways, but the most suitable one is based on their general compositions and to lesser degrees on their physical condition and distinctive properties. The primary types of brick include aluminosilicate brick (fire clay and alumina), basic brick (magnesia and chrome ore, alone and in various combinations), silica brick, insulating brick, and special refractories (carbon, Sic, ZrO,, zircon, borides, and nitrides). Brick are, of course, preformed and are usually heat treated at high temperatures before use, but are in some instances unburned and/or chemically bonded, including the relatively new class of tar-bonded magnesia and/or dolomite brick. In addition to preformed refractories, another broad category includes the so-called specialty refractories, which are usually made in the same types as itemized for brick-bonding mortars and high temperature cements, hydraulic setting castables or refractory concrete, plastic firebrick, and ramming mixes. Refractory grains, such as fire clay and high alumina calcines, dead-burned magnesite and periclase, and dead-burned dolomite are also considered refractory products. Brick are also classified on the basis of physical dimensions, as standard sizes and special shapes. The standard sizes are those which are of definite shape and design and are designated as 9 x 4 ½ x 2 ½ in. and 9 x 4 ½ x 3 in. straights and series. All other brick of non- standard sizes are referred to as special shapes. These come about as a result of a particular need for a given furnace or for a particular application.

Jan 1, 1975

By Edward Saibel

THE various theories that have been advanced to explain or predict the conditions under which a metal fractures may be divided into two categories: First, there are the macroscopic theories generally used in engineering practice. These are empirical in nature and limited in application. For example, the maximum normal stress criterion, which is quite satisfactory for a mild steel in simple tension at atmospheric pressure, no longer suffices when this steel is pulled under hydrostatic pressure.2 In all of these empirical theories, the critical condition characteristic of the material and of the loading conditions must be obtained experimentally. Secondly, there are the theories based on interatomic forces,3,4 or on the energy required to form new surface.5,6 These have all dealt with the theoretical evaluation of the tensile stress necessary to bring about rupture in a purely brittle manner; that is, without plastic flow preceding fracture. All of these attempts have led to values of the tensile strength of crystals or of polycrystalline bodies that are 100 to 1000 times higher than observed values. On this account, it has been thought necessary by some investigators to conceive of a microcrack structure or distribution of flaws throughout the specimen such that the resulting stress concentrations provide the factor necessary to bring about agreement between calculation and experiment. It has been pointed out by several observers7 that this point of view is highly unrealistic, in that the weakening effect of these flaws or microstructures must be very uniform from specimen to specimen, since the fracture stresses found for various specimens of the same material tested under similar conditions are so - nearly constant. Furthermore, since calculations based on atomic forces or atomic energy are for purely brittle fracture, a condition probably never satisfied in tests, agreement is hardly to be expected. Thermodynamic Theory Of Fürth In order to resolve this apparent discrepancy between the theoretical cohesive strengths and the observed fracture strengths, Fürth8 advanced a thermo- dynamic theory of the tensile strength of isotropic bodies based on work of Born9 relating to the melting of crystals. Assuming an isotropic material free from imperfections and flaws, behaving elastically up to the breaking point, and assuming a connection between rupture and the melt- ing phenomenon, Fürth obtains an expression for the rupture stress u, in the form [ ] where Q is the melting energy per unit mass, ? is the density, and µ is Poissons’ ratio. Fürth compares fracture stresses computed from Eq I with the fracture stresses of metals as given in the Landolt-Bernstein Tables (1927) and in the Hand-

Jan 1, 1947

By Richard J. Fruehan

ThE thermodynamic activities of nickel and chromium in liquid Ni-Cr alloys have not been previously reported. There have been several investigations on the solid alloys.1-3 In the present investigation the activity of chromium in liquid Ni-Cr alloys at 1600° C was determined by the use of the following galvanic cell, The use of galvanic cells employing solid oxide electrolytes for determining the activity of metals in solid alloys was first demonstrated by Rapp and Maak4 on Cu-Ni alloys between 700° and 1000°C. Recently Schwerdtfeger5 tested the performance of the ZrO2(CaO) electrolyte at 1600°C and found it satisfactory for oxygen pressures as low as 10"12 atm. He also demonstrated the use of solid oxide electrolytes for determining the activities in liquid metal systems in measuring the activity of manganese in Fe-Mn alloys at 1500°C. Extensive investigations have been carried out in this laboratory, exploring the oxygen partial pressure lower limit at which ZrO2(CaO) electrolyte can be used satisfactorily in oxygen galvanic cells at 1600°C. In a paper to be published at a later date,9 it is demonstrated conclusively that ZrO2(CaO) exhibits insignificant electronic conductivity at oxygen pressures down to about 3 x 10"13 atm which is lower than the oxygen partial pressure in equilibrium with Cr-Cr2O3 at 1600°C. Therefore, the activity of chromium can be related to the measured reversible electromotive force of the cell in the present investigation since no electronic short circulating will occur. Fig. 1 is a schematic diagram of the cell used. The Cr-Cr2O3 electrode was made of equal weights of chromium and Cr2O3 powders which were mixed and packed into a recrystallized alumina crucible. A Pt-wire lead was embedded into the Cr-Cr2O3 compact to insure good contact. A ZrO2(CaO) crucible, supplied by the Zirconium Corp. of America, contained the Ni-Cr melt equilibrated with solid Cr2O3. The ZrO2(CaO) crucible was placed on the Cr-Cr2O3 electrode and additional Cr-Cr2O3 mixture was packed around it. Contact with the Ni-Cr alloy was made with a Cr2O3 tube, which is a weak electronic conductor. A platinum wire lead was attached to the Cr2O3 tube. The galvanic cell was lowered slowly into the hot zone of the furnace tube in order to avoid too large a thermal shock which could break the ZrO2 (CaO) crucible. The furnace was con- tinuously flushed with purified argon during the experiment. The temperature was measured with a Pt-Pt/10 pet Rh thermocouple and maintained at 1600° ± 5°C. The electromotive force was measured with a recording potentiometer. The furnace was turned off when measurements were being made in order to avoid induction effects and the reversibility of the cell was demonstrated in the usual manner. The electromotive force was measured several times over a period of approximately 1 hr. During that period the electromotive force remained constant within ± 3 pet and did not continuously drift in any one direction. After the experiment the alloys were analyzed for chromium in the usual manner. The measured electromotive forces of the cell at 1600°C, (2912°F), are listed in Table I. The activity of chromium, with solid pure chromium as the reference state, (a), was calculated using Eq. [l], , n F E I, n lna RT- U] where E is the measured electromotive force, F is the Faraday constant, and n is equal to 3, the number of equivalents per mole, (nF/RT = 18.59 volts'1 at 1600°C). The resulting activities are listed in Table I. The activity of chromium relative to pure liquid chromium was also calculated. The free energy of fusion of chromium at 1600° C was calculated using

Jan 1, 1969

By W. T. Thom

ALL engineering education is faced by certain basic problems, three of which seem to have particular present importance in geological engineering training in general, and in respect to training for oil field geoexploratory work in particular. PROBLEM I The first of these problems has to do with present and future educational objectives and with the numbers and qualities of the men who should be coming out of our geoexploratory training programs. Before the war we needed ever-increasing numbers of graduates at the Bachelor's level and a very much smaller number of men who had reached the Doctorate degree. Now, with more difficult, more extensive, and more costly exploratory work; with a rapid expansion of company "staff" activities, and with the initiation of many new research organizations and laboratories; it is clear that men of exceptional ability will be more and more in demand, and that the schools will need to carry a greater proportion of their students through to the Ph.D. degree. PROBLEM 2 Assuming that the mineral industries will need an increasing supply of well-qualified Ph.D.s for future geoexploratory work (staff, line and research), can the schools expect to provide this supply of able Ph.D.s merely by expanding the proportion of B.S. and B.A. majors who go on through to the doctorate stage of training? And the answer is definitely "No "-as the situation stands at present. Most A.B. graduates are years short of the preparations in basic science and elementary engineering prerequisite to effective graduate study in the geoexploratory fields (paleontology excepted), and similarly many of the annual crop of B.S. graduates lack adequate training in English; in ancient and modern history; and in the modern principles of labor and public relations. Indeed, several basic problems of undergraduate curricular organization and integration remain to be solved before most recipients of a Bachelor's degree will have that sound and broad educational foundation prerequisite to graduate training on a really effective basis. It is for these reasons that we have continued to experiment with our geological engineering program at Princeton, in an endeavor to provide a pilot-plant demonstration of a suitably broad and flexible undergraduate curriculum. PROBLEM 3 But assuming that the schools can and do get undergraduate curricula set up in proper phase and scale to meet needed enrollment quotas for graduate training, what about the most urgent part of our whole mineral-industry educational problem? What about finding and bringing into mineral-industry training those youngsters of superior ability who are, by potential or known inclination, especially well-qualified for geoexploratory work?

Jan 1, 1947

By W. T. Thom

All engineering education is faced by certain basic problems, three of which seem to have particular present importance in geological engineering training in general, and in respect to training for oil field geo-exploratory work in particular. Problem i The first of these problems has to do with present and future educational objectives and with the numbers and qualities of the men who should be coming out of our geo-exploratory training programs. Before the war we needed ever-increasing numbers of graduates at the Bachelor's level and a very much smaller number of men who had reached the Doctorate degree. Now, with more difficult, more extensive, and more costly exploratory work; with a rapid expansion of company "staff" activities, and with the initiation of many new research organizations and laboratories; it is clear that men of exceptional ability will be more and more in demand, and that the schools will need to carry a greater proportion of their students through to the Ph.D, degree. Problem 2 Assuming that the mineral industries will need an increasing supply of well-qualified Ph.D.s for future geoexploratory work (staff, line and research), can the schools expect to provide this supply of able Ph.D.s merely by expanding the proportion of B.S. and B.A. majors who go on through to the doctorate stage of training? And the answer is definitely "No"—as the situation stands at present. Most A.B. graduates are years short of the preparations in basic science and elementary engineering prerequisite to effective graduate study in the geoexploratory fields (paleontology ex-cepted), and similarly many of the annual crop of B.S. graduates lack adequate training in English; in ancient and modern history; and in the modern principles of labor and public relations. Indeed, several basic problems of undergraduate curricular organization and integration remain to be solved before most recipients of a Bachelor's degree will have that sound and broad educational foundation prerequisite to graduate training on a really effective basis. It is for these reasons that we have continued to experiment with our geological engineering program at Princeton, in an endeavor to provide a pilot-plant demonstration of a suitably broad and flexible undergraduate curriculum. Problem 3 But assuming that the schools can and do get undergraduate curricula set up in proper phase and scale to meet needed enrollment quotas for graduate training, what about the most urgent part of our whole mineral-industry educational problem? What about finding and bringing into mineral-industry training those youngsters of superior ability who are, by potential or known inclination, especially well-qualified for geoexploratory work?

Jan 1, 1949

By Robert B. McCormick

WORLD WAR II has developed a use for the nonmetal mineral quartz crystal that was unknown in World War I. During the interim period of peace, experimental work in the radio field with the piezoelectric properties of quartz crystal resulted in the almost universal adoption of quartz-crystal radio oscillator plates to control frequency in radio broadcasting, police, commercial and amateur communications equipment. Telephone resonators and filters made from quartz crystal also were developed, which vastly improved the frequency control of long distance telephone circuits. EXPANSION OF THE INDUSTRY The sudden war demands of the armed services for radio equipment using quartz crystal for frequency control led to an unprecedented expansion of the manufacturing industry. It is estimated that the 1940 peacetime volume amounted to approximately $1,500,000, while today a vast new quartz-crystal industry supplies more than $150,000,000 worth of quartz oscillator plates to the Army and Navy each year. This demand has caused an enormous expansion not only of American manufacturing facilities but also of Brazilian mining output, virtually our only source of raw quartz crystal. Actual figures of imports and consumption cannot be cited, for security reasons, but certain comparisons have been made, which indicate the transformation of quartz crystal from a minor to a major nonmetal. Lends has shown that the value of quartz-crystal exports from Brazil is now about equal to that of phosphate rock produced domestically in 1941 and actually exceeds the combined value of crude feldspar, gypsum and fluorspar production in the United States in the same year. This great expansion under wartime pressure was not accomplished without some anxious moments, but all the demands of industry have been met and the Government has been able also to accumulate a substantial stock pile of material against future contingencies. INSPECTION AND GRADING OF QUARTZ CRYSTAL The swift growth of the quartz-oscillator industry necessitated the simultaneous evolution of methods and criteria for inspecting and grading quartz crystal. It has been found that, generally speaking, it is economically feasible to cut only crystals that are at least 30 per cent by volume free from major defects such as optical and electrical twinning, cracks and fractures. Blue needles, bubbles, "chuva" and other minor imperfections can be tolerated in the usable portion unless present in great excess. The present marketing system in use in both Brazil and the United States, as far as quality is concerned, depends solely on the "usability" of a crystal, which is defined in the Brazilian-American agreement2

Jan 1, 1945

By Robert B. McCormick

World War II has developed a use for the nonmetal mineral quartz crystal that was unknown in World War I. During the interim period of peace, experimental work in the radio field with the piezoelectric properties of quartz crystal resulted in the almost universal adoption of quartz-crystal radio oscillator plates to control frequency in radio broadcasting, police, commercial and amateur communications equipment. Telephone resonators and filters made from quartz crystal also were developed, which vastly improved the frequency control of long distance telephone circuits. Expansion of the Industry The sudden war demands of the armed services for radio equipment using quartz crystal for frequency control led to an unprecedented expansion of the manufacturing industry. It is estimated that the 1940 peacetime volume amounted to approximately $1,500,000, while today a vast new quartz-crystal industry supplies more than $150,000,000 worth of quartz oscillator plates to the Army and Navy each year. This demand has caused an enormous expansion not only of American manufacturing facilities but also of Brazilian mining output, virtually our only source of raw quartz crystal. Actual figures of imports and consumption cannot be cited, for security reasons, but certain comparisons have been made, which indicate the transformation of quartz crystal from a minor to a major nonmetal. Lundl has shown that the value of quartz-crystal exports from Brazil is now about equal to that of phosphate rock produced domestically in 1941 and actually exceeds the combined value of crude feldspar, gypsum and fluorspar production in the United States in the same year. This great expansion under wartime pressure was not accomplished without some anxious moments, but all the demands of industry have been met and the Government has been able also to accumulate a substantial stock pile of material against future contingencies. Inspection and Grading of Quartz Crystal The swift growth of the quartz-oscillator industry necessitated the simultaneous evolution of methods and criteria for inspecting and grading quartz crystal. It has been found that, generally speaking, it is economically feasible to cut only crystals that are at least 30 per cent by volume free from major defects such as optical and electrical twinning, cracks and fractures. Blue needles, bubbles, "chuva" and other minor imperfections can be tolerated in the usable portion unless present in great excess. The present marketing system in use in both Brazil and the United States, as far as quality is concerned, depends solely on the "usability" of a crystal, which is defined in the Brazilian-American agreement2

Jan 1, 1948

By Robert B. McCormick

World War II has developed a use for the nonmetal mineral quartz crystal that was unknown in World War I. During the interim period of peace, experimental work in the radio field with the piezoelectric properties of quartz crystal resulted in the almost universal adoption of quartz-crystal radio oscillator plates to control frequency in radio broadcasting, police, commercial and amateur communications equipment. Telephone resonators and filters made from quartz crystal also were developed, which vastly improved the frequency control of long distance telephone circuits. Expansion of the Industry The sudden war demands of the armed services for radio equipment using quartz crystal for frequency control led to an unprecedented expansion of the manufacturing industry. It is estimated that the 1940 peacetime volume amounted to approximately $1,500,000, while today a vast new quartz-crystal industry supplies more than $150,000,000 worth of quartz oscillator plates to the Army and Navy each year. This demand has caused an enormous expansion not only of American manufacturing facilities but also of Brazilian mining output, virtually our only source of raw quartz crystal. Actual figures of imports and consumption cannot be cited, for security reasons, but certain comparisons have been made, which indicate the transformation of quartz crystal from a minor to a major nonmetal. Lundl has shown that the value of quartz-crystal exports from Brazil is now about equal to that of phosphate rock produced domestically in 1941 and actually exceeds the combined value of crude feldspar, gypsum and fluorspar production in the United States in the same year. This great expansion under wartime pressure was not accomplished without some anxious moments, but all the demands of industry have been met and the Government has been able also to accumulate a substantial stock pile of material against future contingencies. Inspection and Grading of Quartz Crystal The swift growth of the quartz-oscillator industry necessitated the simultaneous evolution of methods and criteria for inspecting and grading quartz crystal. It has been found that, generally speaking, it is economically feasible to cut only crystals that are at least 30 per cent by volume free from major defects such as optical and electrical twinning, cracks and fractures. Blue needles, bubbles, "chuva" and other minor imperfections can be tolerated in the usable portion unless present in great excess. The present marketing system in use in both Brazil and the United States, as far as quality is concerned, depends solely on the "usability" of a crystal, which is defined in the Brazilian-American agreement2

Jan 1, 1948

By B. S. Tani, R. V. Schablaske, M. G. Chasanov

In the Ti-Cd system two intermediate phases, TiCd and Ti Cd, have been found and characterized by X-ray diffraction powder techniques. An earlier reference' had reported the existence of the compound Tisd. No structural details, however, were given nor was there any indication of the possible existence of other binary compounds. Studies of the solubility of titanium in liquid cadmium2 led to the discovery of both TiCd and Tisd. The solid phase in equilibrium with saturated solutions of titanium in liquid cadmium at temperatures below 620°C is TiCd, whereas TizCd is the equilibrium solid phase above 620°C. Both thermal analysis and X-ray studies show that a peritectic reaction between the y phase (~isd) and cadmium to form the 6 phase (Ti Cd) occurs at 620°C. X-ray diffraction powder photographs of material isolated from the ingots used in the solubility measurements as well as material prepared by a direct heat of the appropriate stoichiometric amounts of titanium and cadmium can be indexed on the basis of a tetragonal unit cell with a = 2.904 ± 0.002A, co = 8.954 * 0.004A, c/a = 3.083. No variation of lattice parameters indicative of a range of composition is evident. With four atoms in the unit cell the calculated density of the intermetallic is 7.05 g per cm3; the observed value is 7.07 g per cm3. The TiCd lattice is primitive as indicated by the fact that there are no systematic absences among hkl reflections. The absence of all hko reflections for which h + k = 2n + 1 is also evident. This systematic absence indicates the following two space groups, C\h — P4/n and D&~4/nmm; both groups, however, have the same two- and four-fold positions. Stoichiometry, symmetry and space group indicate two likely structure types. They are the PbO-litharge3 (B10) type and the Ti CU (B11) type. Spatial considerations favor the B11 structure with atoms placed in the following positions: 2Ti (c) 0, 1/2, Z; l/2, 0, Z 2Cd(c) 0, 1/2, Z; 1/2, 0, Z The TiCd structure may be summarily described as a layered structure in which double cadmium layers alternate with double titanium layers along the c-axis. The best agreement between calculated and observed intensities is obtained for the values ZTi = 0.608 and ZCd = 0.130. Calculated and observed powder intensities as well as other pertinent powder data are recorded in Table I. Interatomic distances for the proposed structure are recorded in Table II and are to be compared with the distances of closest approach for titanium and cad-

Jan 1, 1962

By R. P. Corbett

Since the beginning of operations at the Kelley mine in 1952, Anaconda has emplaced more than 150,000 cu yd of concrete underground. Concreting practices have changed over the years but the net result is still the same- lower costs along the line and more versatility.

Jan 7, 1961

By James M. Schopf

Coal petrology is the study of the lithologic composition and texture of coal and includes megascopic as well as microscopic differentiation. Coal petrography is a quantitative study, principally (but not exclusively) microscopical in nature. The distinction between coal petrologic and coal petrographic studies usually is not important, but it is important to recognize that these studies differ materially from other types of petrology that deal primarily with minerals. The petrologic entities of coal are less clearly distinguished than most minerals and the basis of distinction is not always clearly expressed. The relation of coal petrology to geologic, mining, and technologic problems is most evident when results of coal petrologic studies can be stated quantitatively. The chemical and physical composition of coal and the determination of its quality and properties are continuing problems. The source of these problems lies in the heterogeneity of coal and in its almost complete insolubility in ordinary solvents at normal temperatures.

Jun 1, 1956

By C. D. Jardine, D. G. Patton

Rapidly increasing energy costs and more rigid customer quality requirements necessitate improved control of pelletizing processes. With the introduction of dedicated microprocessor-based controllers, sophisticated control strategies are now possible. An application of this technology at Carol Project has resulted in fuel savings, improved pellet quality, and standardization of operating procedures. This was accomplished with no production loss by using a "building block" approach to design and equipment selection.

Jan 1, 1985