By O. C. Ralston, F. Fraas

VIRTUALLY all commercial use of electrostatic separation has employed separators depending on differences of conductance of the broken, solid mixtures treated by them. The two main types of conductance separators have been: (1) Those in which the separating field is as near a static field between two charged electrodes as it is possible to maintain in the face of the usual leakage that takes place between electrodes with some 5 to 50 kv tension between them and spacing of 1/2 to 3 in.; (2) those in which a convective discharge of corona or spray type, but not a spark discharge, takes place between the carrier electrode and a charged electrode facing it, which is of very restricted area, such as a row of needle points or a small diameter wire parallel to the face of the carrier electrode. The present paper deals with this latter type. The principle is usable in separators where the carrier electrode, usually grounded, has the shape of a roller, a conveyor belt, a vibrating table, a sloping chute, or a nearly vertical plate. The innovation studied by us has been the use of the convective field for charging material on the carrier electrode and succeeded by a field between the carrier electrode and an electrode made of a true dielectric which cannot take on a charge by conduction but is charged by being in the radius of the corona discharge. The acquired charge is of the same sign as that of the corona but is not dischargable by contact with a good conductor. However, high-tension charge tends to leak off because of the ionization of the ambient air. The field between this electrode and the carrier electrode is as near static as it is possible to obtain. There are some differences in behavior of this electrode and that of the gas tube electrode used by Sutton, as will be discussed below. Both electrodes cause increased adhesion of nonconductive particles to the carrier roll. The particles are pinned there because they are convectively charged on their outer surfaces facing the corona electrode. The electrodes also cause increased rate of release of conductive particles tending to be pinned by corona charging but conveying the charge to the grounded carrier roll almost as rapidly as it is received by the particles. The sign of the potential on the corona-emitting electrode makes little difference in the separation. An electrode usually emits negative corona somewhat more easily than it emits positive corona, as electrons are then the fundamental particles emitted. With a positive electrode the flow of electrons involved in positive corona discharge is onto the electrode from the ambient gas. Theory In the separator illustrated in fig. 1, the nonioniz-ing electrode is a rotating, nonconductive dielectric cylinder designated as B. The ions emitted by the corona electrode, or wire F, charge both the particles on the carrier electrode, or roll A, and the surface of the dielectric electrode B. Whereas the space between roll A and wire F contains ions, the space between electrode B and roll A is a pure static field free of ions. The dielectric electrode has been described by Bullock.1 However, the corona electrode, which Bullock uses for the purpose of charging only the dielectric electrode, is adapted here to also charge the particles on the carrier roll. In operation the ionic field from the corona electrode is balanced with the static field from the dielectric electrode. The ionic field charges the particle so that it adheres to the roll. The static field intensifies the discharge of the corona charge by interfacial conduction and permits the release of the particle. The ionic and static fields therefore have opposing effects.2 The values of both fields are adjusted so that the poor conductor will adhere and the good conductor will be released.

Jan 1, 1951

By A. F. Witt, A. M. Gaudin, A. K. Biswas

Finite contact angles in the rutile-water-organic liquid system are traceable to contamination or are due to addition of a surface-active agent. Finite contact angles are invariably accompanied by hysteresis.1-7 Besides surfactant concentration and pH, the nature of the organic liquid is found to be a factor influencing the magnitude of contact angle hysteresis. In a recent paper the authors have reviewed principles and applications of measurement methods for contact angles and their hysteresis.22 In this paper, these methods are applied to a system consisting of rutile, an organic liquid (benzene, decane, or dode-cane) and water. Surfactant (dodecylamine hydro-chloride) was used at various concentrations and various pH values. MATERIALS A synthetic rutile crystal supplied by the Linde Co. was used. It is a cylinder 1/2 in. diam, with faces cut perpendicular to the c-axis. The crystal is stated to be alumina-free and to be 99.9% pure. Rutile is a high surface energy solid, its calculated average field strength being 2.7 x 105 e.s.u.,9 its dielectric constant10 is 114. The zero point of charge of rutile was measured11 and found to be at pH 6.0. The atomic distances and bond angles of the tetragonal crystal of rutile have been precisely determined.l2 The organic liquids were specially purified. Reagent grade benzene was repeatedly shaken with concentrated sulfuric acid to remove thiophene, then neutralized with sodium hydroxide solution, rinsed with distilled water, dried overnight over anhydrous calcium chloride and filtered. The refractive index of this chemically purified benzene was 1.4977 (at 25°C) - very close to that of pure benzene (n25 1.4979).13 Both n-decane and n-dodecane were washed with aqueous sodium hydroxide, concentrated sulfuric acid (repeatedly, until the acid layer was colorless) and again with alkali, to free the organic hydrocarbon from fatty acids and unsaturated hydrocarbons. The organic phases were subsequently washed with distilled water and dried over anhydrous sodium sulfate. The filtered hydrocarbons were then distilled under vacuum (9-10 mm pressure). Decane, thus purified, showed traces of unsaturated and of carboxylic compounds. On gas chromatographic analysis the purified n-dodecane showed the presence of two impurities. However, the relative retention times of these components did not change substantially when measured on a polar or a nonpolar column. This indicates that the compounds were probably in the same polarity class, i.e. the components were nonpolar like dodecane. Conductivity water has always been one of the liquids. Conductivity of the water used was 10-6 ohm-' cm". Dodecyl ammonium chloride was prepared from pure amine (supplied by Armour and Co., Chicago), by Li in the MIT Mineral Engineering Laboratory.14 The critical micelle concentration at 25°C is known, 0.0138 mol per liter15 or 3.06 gpl. All our experiments have been done at concentrations lower than the critical micelle concentration. The glass vessels, glass drop holder and the rutile crystal were all cleaned with hot chromic acid followed by distilled water, concentrated hydrochloric acid, and again distilled water, and conductivity water. During the experiments, a nitrogen atmosphere was maintained. For this purpose, commercially purified nitrogen was further purified by passing it over hot copper wire at 450°C, then through columns of acidic chromous chloride solution, concentrated alkali solution and distilled water. APPARATUS AND METHODS Hysteresis was produced by the "captive drop" or constant volume drop method as well as by the "expanding-contracting drop" or variable volume drop method. The image of the drop while it is expanding, contracting or moving is projected on a screen and photographed. The developed film is projected through an enlarger and the contact angles measured with a protractor.

Jan 1, 1964

By John R. Freeman

THIS paper relates entirely to the casting of brass under fluid pressure in steel dies Die castings of metals and alloys of low melting point have been available for many years but the development of brass die castings has been relatively recent, occurring within the past five years The successful development of brass die castings has resulted from the availability of alloy steels that would give satisfactory life as dies and the development of suitable die-casting machines The melting point of copper is 1084° C (1983° F ) and of a high brass about 900° C (1652° F ), as compared to 327 5° C (6215 °F) for lead, 419 4° C (786 7° F) for zinc and 658 7° C (1217 7° F) for aluminum, temperatures that ale indicative of the casting temperatures required for the various types of alloys, of which the melting points are somewhat lower than those of the pure metals TYPE OF DIE-CASTING MACHINE In the well-known plunger and gooseneck types of die-casting machines used for casting the alloys of relatively lower melting point, much of the working mechanism is immersed in the molten alloy For alloys having the relatively high melting point of brass, this obviously is impossible Machines with a separate melting chamber are essential Two rather distinct types are in extensive use at the present time, the Pack and Polak machines, the former designed by Charles Pack and developed at the American Brass Co , the latter developed by Zoseph Polak, of Prague, Czechoslovakia The principles of operation of these machines have been described in articles by Pack1,2,3 and by Sieg 4

Jan 1, 1935

By John R. Freeman

This paper relates entirely to the casting of brass under fluid pressure in steel dies. Die castings of metals and alloys of low melting point have been available for many years but the development of brass die castings has been relatively recent, occurring within the past five years. The successful developnlent of brass die castings has resulted from the availability of alloy steels that would give satisfactory life as dies and the development of suitablc die-casting machines. The melting point of copper is 1084" C. (1983" F.) and of a high brass about 900" C. (1652" F.), as compared to 327.5" C. (621.5" F.) for lead, 419.4' C. (786.7" F.) for zinc and 658.7" C. (1217.7" F.) for aluminum, temperatures that are indicative of the casting temperatures required for the various types of alloys, of which the melting points are somewhat lower than those of the pure metals. Type of Die-casting Machine In the well-known plunger and gooseneck types of die-casting machines used for casting the alloys of relatively lower melting point, much of the working mechanism is immersed in the molten alloy. For alloys having the relatively high melting point of brass, this obviously is impossible. Machines with a separate melting chamber are essential. Two rather distinct types are in extensive use at the present time, the Pack and Polak machines, the former designed by Charles Pack and developed at the American Brass Co., the latter developed by Joseph Polak, of Prague, Czeclioslovakia. The principles of operation of these machines have been described in articles by Pack1,2,3 and by Sieg.4

Jan 1, 1935

By John R. Freeman

This paper relates entirely to the casting of brass under fluid pressure in steel dies. Die castings of metals and alloys of low melting point have been available for many years but the development of brass die castings has been relatively recent, occurring within the past five years. The successful developnlent of brass die castings has resulted from the availability of alloy steels that would give satisfactory life as dies and the development of suitablc die-casting machines. The melting point of copper is 1084" C. (1983" F.) and of a high brass about 900" C. (1652" F.), as compared to 327.5" C. (621.5" F.) for lead, 419.4' C. (786.7" F.) for zinc and 658.7" C. (1217.7" F.) for aluminum, temperatures that are indicative of the casting temperatures required for the various types of alloys, of which the melting points are somewhat lower than those of the pure metals. Type of Die-casting Machine In the well-known plunger and gooseneck types of die-casting machines used for casting the alloys of relatively lower melting point, much of the working mechanism is immersed in the molten alloy. For alloys having the relatively high melting point of brass, this obviously is impossible. Machines with a separate melting chamber are essential. Two rather distinct types are in extensive use at the present time, the Pack and Polak machines, the former designed by Charles Pack and developed at the American Brass Co., the latter developed by Joseph Polak, of Prague, Czeclioslovakia. The principles of operation of these machines have been described in articles by Pack1,2,3 and by Sieg.4

Jan 1, 1935

By E. P. Shoub, J. P. Riott, R. C. Buehl

Pilot-plant tests have demonstrated that it is possible to produce low-sulphur sponge iron (0.03 to 0.0; per cent sulphur) as a continuous process in an internally fired rotary kiln from iron ore or mill scale; a solid carbonaceous reducing agent; and dolomite to control the sulphur content. The proportion of dolomite employed is small, so that it does not add materially to the cost of the sponge iron. The entire operation is carried out at temperatures well below the melting point of iron, so that the product is discharged in granular form. Compared with other methods for the production of sponge iron, the rotary-kiln method has the advantage of simplicity and low cost of equipment and, in addition, requires little labor for the operation of the process. The pilot-plant equipment used for this work was sufficiently large to demonstrate that the production of low-sulphur sponge iron in rotary kilns is feasible and that the costs are not excessive for applications in which sponge iron has distinct advantages over competing materials. This report constitutes a part of a program by the Bureau of Mines under a special Congressional appropriation for studying gaseous and solid fuel reduction of iron ores. Numerous articles on various phases of these investigations have appeared in Bureau of Mines publications or technical journals. Other articles are being prepared and will be published in the near future. The present program, which is under the supervision of Dr. R. S. Dean, Assistant Director of the Bureau of Mines, was initiated in 1942. However, a considerable portion of the work was a continuation of previous research performed by the Bureau. Previous investigators1-4 utilizing the rotary kiln for the production of sponge iron did not develop a suitable method for controlling the sulphur content. A review of the literature shows that the sulphur content in the product usually exceeded 0.1 per cent unless reducing agents with very low sulphur contents were employed. This high sulphur value made the product generally undesirable for use as melting stock in electric or open-hearth furnaces. The production of sponge iron in an internally fired rotary kiln has been described in detail in Bureau of Mines Bullelin 2702; consequently, this article will be confined mostly to new features of the process—that is, means for controlling the sulphur content of the sponge iron. Suitable raw materials include iron ores or mill scale; coal or coke for reducing them, and sized dolomite ( — poi-100-mesh) as the sulphur-controlling agent. A mixture of the raw materials in granular form is fed into the elevated end of the kiln, which is fired axially from the lower or discharge end. In the reducing zone, which is approximately one third the length of the kiln measured from the dis-

Jan 1, 1948

By R. C. Buehl, J. P. Riott, E. P. Shoub

Pilot-plant tests have demonstrated that it is possible to produce low-sulphur sponge iron (0.03 to 0.0; per cent sulphur) as a continuous process in an internally fired rotary kiln from iron ore or mill scale; a solid carbonaceous reducing agent; and dolomite to control the sulphur content. The proportion of dolomite employed is small, so that it does not add materially to the cost of the sponge iron. The entire operation is carried out at temperatures well below the melting point of iron, so that the product is discharged in granular form. Compared with other methods for the production of sponge iron, the rotary-kiln method has the advantage of simplicity and low cost of equipment and, in addition, requires little labor for the operation of the process. The pilot-plant equipment used for this work was sufficiently large to demonstrate that the production of low-sulphur sponge iron in rotary kilns is feasible and that the costs are not excessive for applications in which sponge iron has distinct advantages over competing materials. This report constitutes a part of a program by the Bureau of Mines under a special Congressional appropriation for studying gaseous and solid fuel reduction of iron ores. Numerous articles on various phases of these investigations have appeared in Bureau of Mines publications or technical journals. Other articles are being prepared and will be published in the near future. The present program, which is under the supervision of Dr. R. S. Dean, Assistant Director of the Bureau of Mines, was initiated in 1942. However, a considerable portion of the work was a continuation of previous research performed by the Bureau. Previous investigators1-4 utilizing the rotary kiln for the production of sponge iron did not develop a suitable method for controlling the sulphur content. A review of the literature shows that the sulphur content in the product usually exceeded 0.1 per cent unless reducing agents with very low sulphur contents were employed. This high sulphur value made the product generally undesirable for use as melting stock in electric or open-hearth furnaces. The production of sponge iron in an internally fired rotary kiln has been described in detail in Bureau of Mines Bullelin 2702; consequently, this article will be confined mostly to new features of the process—that is, means for controlling the sulphur content of the sponge iron. Suitable raw materials include iron ores or mill scale; coal or coke for reducing them, and sized dolomite ( — poi-100-mesh) as the sulphur-controlling agent. A mixture of the raw materials in granular form is fed into the elevated end of the kiln, which is fired axially from the lower or discharge end. In the reducing zone, which is approximately one third the length of the kiln measured from the dis-

Jan 1, 1948

By H. P. Reid

PORTLAND cement is manufactured under either of two general proc-esses, the wet or the dry. The raw materials in general consist of limestone, shells, marl, cement rock, clay, shale, blast-furnace slag, etc., so proportioned that when calcined the desired composition will be obtained. In the wet process the combined raw materials are ground to extreme fineness in the presence of water, to a resulting slurry of from 30 to 50 per cent moisture content. The moisture of the slurry may be reduced by thickening or filtering processes for feed to the cement kiln or the slurry may be fed to the kiln with its full percentage of water. The dry process differs from the wet in that the surface moisture of the raw materials is removed prior to grinding. For the drying of these materials heat is required and in most cases is produced by burning of raw fuel either on grates or stokers before the dryers or in suspension in the form of pulverized coal, oil or gaseous fuel. The power required for making the cement is sometimes purchased from outside sources; sometimes it is generated from the heat in the waste gases leaving the cement kilns, or generated at the plants direct from raw fuel. We have, then, as the possible requirements of fuel in the cement industry: (1) fuel for power generation, (2) fuel for drying raw materials, including coal before pulverizing, and (3) fuel for burning the raw materials to cement clinker. There is no essential difference in quality required in fuel for burning the materials by the wet and dry processes.

Jan 1, 1932

By Benj. F. Tillson

To most mine operators, it seems evident that there is a drill-steel problem, although under certain conditions the amount of drill-steel breakage does not appear serious. What is at fault? It may be one or a combination of circumstances. The development of rock drills to the hammer-drill type in place of the old reciprocating piston drill, probably is one important cause for the greater steel breakage. Perhaps the manufacturers of drill steel have failed to realize what alloys are needed for this new service or have overlooked the changes in the art of rock drilling. Although suitable alloys are provided, they may not be SO handled in the manufacturing process as to be in the best condition to withstand the demands of rock drilling. The mine operator may be at fault in desiring to use the smallest possible drill-steel section in order that the gage of the drill bits may be correspondingly small and the amount of footage drilled per unit of labor may be greater; or the black-smithshop practice at the mines may need improvement. The miner who uses the drill steel may also require more intensive supervision and education. Again, the manufacturer of rock drills may have failed to study the types of blows the steel alloys will withstand satisfactorily and which their tools are delivering and so he may not know whether or not a different design of rock drill would equal or excel their present drilling speeds without treating the drill steel so severely. All of these hypotheses probably have their supporters. On the other hand, perhaps we are seeking too much service from drill steel and we need a fuller realization of the fatigue strains developed and should prepare to relieve these by a periodic heat treatment of the steels. However, we do not find any proof that any of these suppositions may be held responsible for the drill-steel breakage attendant to mining. The proposed investigation of this matter by the U. S. Bureau of Mines is fully warranted in the promotion of the conservation of labor and material, and the safety of the workmen. The great range of field conditions, as well as the scope of the research, requires the energetic cooperative support of many interests. Various manufacturers of steel,

Jan 1, 1922

The passing of Benjamin Bowden Lawrence in January, 1921, was a distinct loss to the engineering profession. Mr. Lawrence had a genius for reviving abandoned mines and developing them into substantial producers. A notable example of his work in this line was the Dives-Pelican near Georgetown, Colo. While on an exploring expedition in 1888, he examined this old mine and was convinced that bonanza ore still existed there. He located the owners of the property, and induced them to place sufficient capital at his disposal to enable him to re-open and explore this mine. So confident was he of the outcome that he undertook this work on a profit-sharing basis without salary. Within eighteen months the old Dives-Pelican was operating profitably, and for the following ten years it paid very substantial dividends. The late Theodore N. Vail was one of the owners of this old mine, and many years later, at a dinner given to Mr. Lawrence by the Alumni of Columbia University, Mr. Vail told the story of the resuscitation of the Dives-Pelican by Mr. Lawrence, and declared that the dividends he himself had received provided a large part of the funds that made possible the realization of his dream of establishing the long-distance telephone in this country. The E1 Cobre mines at Santiago de Cuba also owed their renewed life to Mr. Lawrence. Under his management, these mines produced and shipped several million pounds of copper per year. He was for several years consulting engineer for the Kerr Lake and other silver mines in the Cobalt region; the Kerr Lake became famous as a silver producer. Mr. Lawrence spent more than twenty years of his life in the mining camps of the West. He was but twenty-one years of age, and only a few months out of college, when he was appointed manager of the great Chautauqua Lode (a silver mine) located on Glacier Mountain near Montezuma, Colo. Here, isolated in the mountains for several months each year by ice and snow, he worked for five years to make these mines Pay. He possessed unusual breadth of vision and human understanding; he had ''personality plus," and when he opened an office in New York City as consulting engineer he quickly rose to an enviable position in his profession. Young engineers worked with enthusiasm under his guidance. He carefully selected his men, discussed fully with them the plans and policies to be pursued, then left them free to accomplish results in their own way. This attitude developed individuality and resourceful-

Jan 1, 1922

The passing of Benjamin Bowden Lawrence in January, 1921, was a distinct loss to the engineering profession. Mr. Lawrence had a genius for reviving abandoned mines and developing them into substantial producers. A notable example of his work in this line was the Dives-Pelican near Georgetown, Colo. While on an exploring expedition in 1888, he examined this old mine and was convinced that bonanza ore still existed there. He located the owners of the property, and induced them to place sufficient capital at his disposal to enable him to re-open and explore this mine. So confident was he of the outcome that he undertook this work on a profit-sharing basis without salary. Within eighteen months the old Dives-Pelican was operating profitably, and for the following ten years it paid very substantial dividends. The late Theodore N. Vail was one of the owners of this old mine, and many years later, at a dinner given to Mr. Lawrence by the Alumni of Columbia University, Mr. Vail told the story of the resuscitation of the Dives-Pelican by Mr. Lawrence, and declared that the dividends he himself had received provided a large part of the funds that made possible the realization of his dream of establishing the long-distance telephone in this country. The E1 Cobre mines at Santiago de Cuba also owed their renewed life to Mr. Lawrence. Under his management, these mines produced and shipped several million pounds of copper per year. He was for several years consulting engineer for the Kerr Lake and other silver mines in the Cobalt region; the Kerr Lake became famous as a silver producer. Mr. Lawrence spent more than twenty years of his life in the mining camps of the West. He was but twenty-one years of age, and only a few months out of college, when he was appointed manager of the great Chautauqua Lode (a silver mine) located on Glacier Mountain near Montezuma, Colo. Here, isolated in the mountains for several months each year by ice and snow, he worked for five years to make these mines Pay. He possessed unusual breadth of vision and human understanding; he had ''personality plus," and when he opened an office in New York City as consulting engineer he quickly rose to an enviable position in his profession. Young engineers worked with enthusiasm under his guidance. He carefully selected his men, discussed fully with them the plans and policies to be pursued, then left them free to accomplish results in their own way. This attitude developed individuality and resourceful-

Jan 1, 1922

By James C. M. Li

The Petch relation between the flow stress and the gain size is derived from a consideration of gain boundary sources of dislocations without the need of dislocation Pile-ups. Three mechanisms for inierpreting the yield stress: the gain boundary strength, the unpinning of Frank-Read source near a grain boundary, and the generation of dislocations from the grain boundary are compared and the condition of their equivalence is shown. The effect of the average angle of misfit of pain boundaries is found to be sma11 and so is that of the average angle of misfit of subboundaries having impurities. The effect of impurities on the ledge density in the grain boundary is treated thermodynamically and a relatwn is proposed for the variation of Petch slope with impurity activity. The effect of temperature on the Petch slope is interpreted as due to the change of ledge structure in the grain boundary. It is indicated that the effect of annealing temperature may be more important than that of the test temperature and therefore should be studied. The effect of plastic strain on the Petch analysis is deduced from a work-hardening equation in which the generation of dislocations has first-order kinetics and the annihilation of dislocations has second-order kinetics. It is concluded that the Petch slope will decrease with plustic strain if the rate of annihilation of dislocations is sufficiently large. Critical experiments which may shed light on the mechanism for the Petch relation are suggested. THE relation between the yield or flow stress, 0, and the grain size, l, was first proposed by all' and later studied more extensively by Petch and co-workers, who also proposed a similar relation for the fracture stress and deduced from these a grain-size effect of the ductile-brittle transition temperature. The microscopic mechanism used by all' and petch2 involves a pile-up of dislocations of like sign generated from a Frank-Read source. The yielding or flow takes place when the pile-up exerts sufficient stress at the grain boundary so that the plastic deformation can propagate from one grain to another. If the average strength of the grain boundary is ai and the average length of the pileup is lp, the Petch slope, k, is given by" where p is the shear modulus, b the Burgers vector, and v the Poisson ratio. This slope will be independent of the grain size if l/lp is a constant. This is possible, since, if the Frank-Reed source is situated near the grain boundary, lp = 1, and if it is situated in the middle of the grain, Ip = 1/2. cottrell,12 also using the pile-up mechanism, proposed that the stress concentration at the grain boundary will initiate Frank-Read sources near the grain boundary and in this manner a Lüders band can propagate from one grain to another. Assuming that the average distance between the Frank-Read sources and the grain boundary is 1, and the unpinning stress of the Frank-Read sources is op, Cottrell obtained the following Petch slope: This slope will be independent of the grain size if ls is independent of the same, which is not as obvious as the condition, Ip = I for Eq. [2]. In addition to this assumption, the direct relation between the Petch slope k and the unpinning stress, up, was recently questioned by Johnsonon grounds that it is inconsistent with the following observations: the independence of k with temperature and strain rate, and the small k in columbium, which, like iron, has a sharp yield point. As pointed out by ohnson," the most important objection both to the Hall-Petch mechanism, in which the strength of the grain boundary plays the role in yielding, and to the Cottrell mechanism, in which the unpinning of Frank-Read sources plays the role in yielding, is the lack of direct observation of the pile-ups. The dislocation structure in deformed iron has been examined recently in the electron microsope.'-' Dislocations appear to be generated from grain boundaries or other interfaces; they form clusters and tangles within the grain at very early stages of deformation, even in the Lüders band, if the deformation is slow or at normal and elevated temperatures. Although it is still too early to interpret bulk properties from thin-film observations, it does seem worthwhile to look for a mechanism for the Petch relation which does not require dislocation pileup. SUBBOUNDARY SOURCES In order to show that a consideration of grain boundary sources can lead to the same Petch relation as does the consideration of the strength of the grain boundary, we shall first discuss the case of a simple tilt boundary whose elastic properties have been studied in detail.17 The strength of a partially

Jan 1, 1963

By F. B. Sherman, Keros Cartwright

Sanitary land filling has become one of the most widely used methods of disposing of solid refuse. A principal concern of regulatory agencies and the public itself is that landfill operations do not degrade the physical environment, including water resources, and the ground-water reservoir in particular. Knowledge of ground-water and engineering geology can guide landfill operations into suitable terranes or develop measures to compensate for natural limitations at a particular site. Experience and research in Illinois suggest four activities relating to landfill disposal that warrant attention by geologists and engineers: (1) regional delineation of favorable and unfavorable hydrogeologic conditions to facilitate planning and preliminary screening of potential landfill sites; (2) site evaluations, with considerations of geologic materials, topography, water levels, flow systems, and local occurrence and use of water resources; (3) research on aspects of the hydrogeologic environment that control effects of, or are modified by, landfills; and (4) formulation of practices in the siting, construction, and operation of landfills that prevent, mitigate, or isolate deleterious effects. The first two activities are basically in the domain of earth science, requiring the application of fundamental concepts of geology and hydrology and conventional site-exploration methods. The third activity, research, requires contributions from geology as well as other disciplines, including soil physics, sanitary engineering, and chemistry. The fourth calls for policy decisions by regulatory agencies and elected officials, using the contributions of scientists and engineers. Throughout history, man has disposed of unwanted materials by dumping. As urbanization has increased, haphazard dumping practices have given way to disposal under more controlled conditions because of increasing congestion of population and production of waste and greater concern for public health and environmental amenities. Many states and communities have already outlawed open dumping and open burning of refuse. The only practical methods of disposal of large volumes of refuse, therefore, are contained, high-temperature incineration, or burial in a sanitary landfill. In Illinois, regulation of solid waste disposal has been delegated to the Environmental Protection Agency. Each session of the legislature since 1965 has passed increasingly strict laws regulating waste diposal. As a result, the work of evaluating sanitary landfill sites has increased significantly for both the Department of Public Health, now the Environmental Protection Agency, and the Illinois State Geological Survey, which advises the Agency on matters of ground-water geology and pollution. In fact, our ground-water staff spends as much time on studies relating to waste disposal, primarily sanitary landfills, as on ground-water resource studies. Many other geological agencies are experiencing similar demands for increased assistance in solving waste-disposal problems. This paper summarizes some of the salient features of the sanitary landfill concept, describes activities of the Illinois Geological Survey in ground-water and engineering geology relating to landfills, and suggests policies that need consideration. A sanitary landfill is located and operated in such a way that vermin and pests, nuisances, and degradation of air and water are kept at acceptable levels. Some of the physical requirements of a sanitary landfill are all-weather roads for year-round access, fences to retain blowing paper, a daily cover of at least six inches of suitable earth material, and a final cover of at least 2 ft of earth material. Dumping into or adjacent to standing water generally is not allowed. Two common operating techniques are used. In the first, trenches are dug, the refuse is placed in them, and the earth removed from the trenches is used to cover the waste. In the second method, area fill, refuse is placed in low ground and covered with earth from adjacent high areas. The hydrology of the site is a prime consideration in locating sanitary landfills. Putrescible refuse, if saturated above field capacity, produces a leachate that usually has a high concentration of dissolved solids.2 As the leachate also acts as an agent for transporting bacterial pollutants, it constitutes a potential pollution hazard. To reduce the production of leachates, the topography of the landfill area should be such that surface water will not flow into or through the fill. Operations that will result in refuse disposal below or near the highest known water-table elevation may be required to take corrective or preventive measures to protect the ground water. In practice, under humid conditions such as prevail in Illinois, locations where disposal can take place above the water table are relatively few because surficial materials are commonly fine-grained, which permits slow gravity drainage and results in high degrees of saturation (100% moisture content) near the surface. At some sites, although disposal has taken place above the water table, ground-water mounds have developed, resulting in permanent saturation of the refuse. Permeability barriers usually are required to protect the ground-water reservoir from degradation by leachates. The convention in Illinois is to have a minimum of

Jan 1, 1972

By W. V. Green

Creep of tantalum was measured at temperatures from 0.6 to 0.89 of the absolute melting temperature. The creep curves include first, second, and third stages. Steady-state creep rate depends on the fourth power of stress. The activation energy for creep throughout this temperature range is approximately 114 kcal per mole, measured by the aT technique. Subgrain formation occurs as a result of creep strain, and pile-up dislocation arrays are observed in etch-pit patterns. BECAUSE of its high melting point-which is exceeded only by those of rhenium and tungsten—and its high room-temperature ductility compared to most of the other high-melting-point metals, tantalum will undoubtedly be utilized in an increasing number of high-temperature applications. Alloying studies directed toward increased high-temperature strength must use data on tantalum itself as a base line in order to evaluate the effectiveness of the alloying additions. However, to date, no systematic study of creep of tantalum at temperatures above one-half of its melting point has been reported in the literature. Conway, Salyards, McCullough, and Flagella1 have measured linear creep rate of tantalum sheet as a function of stress, but at only one temperature, 2600°C. This paper describes a relatively thorough study of the high-temperature creep of tantalum. METHOD Material Tested. The commercially supplied, l/2-innch-diameter tantalum rod used for this work was electron-beam-melted, cold-forged, rolled, swaged, cleaned chemically, and vacuum-annealed for 1 hr at 1000°C, all by its manufacturer. The vendor's analysis included 60 to 170 ppm C, 3.4 to 4.2 ppm H, 60 to 80 ppm 0, 15 ppm N, and a hardness ranging from 66 to 81 Bhn and averaging 76 Bhn. Creep eimens Used. Two creep-tested specimens are shown in Fig. 1. The 1/4 in.-diameter gage section was 3/4 to 1 in. long, and terminated either at shoulders 5 mils high or at 20-mil-diameter tantalum wires spot-welded to the circumference of the gage section. Both kinds of shoulders served equally well as fiducial marks for optical strain measurements. The spot welding did not alter the creep behavior in any detectable way; the 5-mil- high sharp shoulders did not result in any detectable localized effect on the strain. Before testing, each tensile bar was first mechanically polished -id then electrochemically polished according to the method referred to by Forgeng2 as the "Thompson Ramo Woolridge" method, which was suitable for tantalum after small adjustments of technique were made. Two tensile bars tested at low stresses had 1/8-in.-diameter gage sections and utilized only the weight of the bottom grip for the applied load. Although these diameters were smaller than were desired for other reasons, applied loads were known with high precision in the tests in which they were used. Testing Procedure. Two different constant-load creep-testing machines were employed, one of which has been described by Smith, Olson, and Brown.3 In both, the tensile bar is held vertically on the axis of a cylindrical tungsten tube or screen heater by threaded tungsten grips. The tensile bars and associated grips are heated by radiation from the incandescent heaters, which are heated by their own electrical resistance. Both testing machines use pins to hold the bottom grips in place. The load is applied to a tensile bar through hanging weights, a constant force-multiplication lever, a pull rod sealed to the chamber lid, and a top grip threaded to the pull rod at one end and to the tensile bar at the other. In one machine, the vacuum seal is a bellows with a low spring constant; in the other, the seal involves a rotating "0 ring". With the latter, rotation is converted to translation with a crank shaft, so that elongation of the tensile bar is accommodated with no change of tensile load. The incandescent tensile bar is viewed by an external optical system through slots in the radiation shields and heater, and an enlarged image is projected on a ground-glass screen. Gage-length measurements are made on this image with cathetometers on traveling microscopes. With regard to creep-test results, the two machines were identical. Thorium oxide coatings were applied to the threaded ends of the tensile bars, to prevent diffusion welding of the tensile bars to the grips during testing. Specimen temperatures were measured with an L. & N. optical pyrometer which had been calibrated against a standard carbon arc, and were corrected fir window absorption by calculation from the measured spectral transmittance of the quartz observation windows. Longitudinal temperature gradients in the tensile-bar gage length and temperature drifts during testing were detectable but small, and were estimated to be 10°C or less. Accuracy of temperature measurement was confirmed by comparing the temperature measured on the surface of a special

Jan 1, 1965

By S. S. Shen, M. J. Pool, P. J. Spencer

Heats of solution of silver and copper in dilute Ag-Cu-Sn alloys at 720°K have been determined using a liquid metal-solution calorieter. Values of the se2f-interaction coefficient n AgAghave been calculated at constant copper concentrations and n Cu Cuhas been determined at constant silver contents. The reliability of the experimental data is shown by the very good agreement between nCujAg and ij &$; these interaction coefficients have experimental values of -9100 and - 9590 cal per g-atom, respectively. Certain solution models are shown to be inadequate for prediction of solute interaction coefficients in dilute Ag-Cu-Sn alloys. In a previous publication' the results of a thermody-namic study of dilute Ag-Au-Sn alloys were presented. The present work represents the continuation of a program to investigate dilute alloys of the noble metals with tin and in particular is concerned with solute interactions in the Ag-Cu-Sn system. By determination of the magnitude and sign of the various interaction coefficients in dilute alloys it is possible to gain some understanding of the different types of solute-solute and so lute-solvent bonding changes that occur as the solute concentrations are varied. Hence systematic studies of alloys with similar physical characteristics as regards size, structure, electronegativity, and so forth, of their components can contribute a great deal to present theoretical knowledge of solutions. The recent definition of an enthalpy interaction coefficient, 11, by Lupis and Elliott2 is of particular value in calorimetric studies such as the present one: where j and i are solutes and s is the solvent; Si is the relative partial molar enthalpy of component i and x represents the mole fraction of solute or solvent. Values of ?Hi can be obtained directly by solution calorimetry and data for n are thus easily determined, often with a high degree of accuracy. ?Hi is related to the relative partial molar enthalpy at infinite dilution, ?Hi and to the enthalpy interaction coefficients by the expression: ?Hi?Hi + X;nz+ ... [2] The aim of the present work was to determine the self-interaction coefficients n AgAgand 178: in alloys of different compositions and also to establish values for n Agcg| and ncuAg. Since it is a thermodynamic requirement (resulting from the Maxwell-type relationships which can be applied to partial molar properties) that nAgcu and ncuAg should be equal, a further aim of this study was to demonstrate the agreement between experiment and theory. EXPERIMENTAL A description of the liquid metal-solution calorimeter used in this research has already been published,3 and no further details of its construction and operation will therefore be given here. Copper supplied by the American Smelting and Refining Co. was indicated by them as being 99.999 pct pure, and the silver obtained from A. D. Mackay, Inc., was also quoted as being 99.999 pct pure. A solvent bath consisting of between 70 and 80 g of 99.99 pct pure Sn was used for each series of experimental drops. Its weight was accurately determined and the appropriate amounts of copper or silver were added to give alloys of the desired composition. Approximately 0.00125 g-atom additions were used for determinations of the heat of solution of silver in the bath, while, for copper, specimens consisting of approximately 0.0015 g-atom were used. The heat capacity of the bath was determined at regular intervals during a series of drops using tin or tungsten calibration samples. The heats of solution of silver and copper in pure tin were first determined as a function of their concentration in order to establish the self-interaction coefficients 7AgAg and ncucu Alloys containing a constant 0.01, 0.02, 0.03, and 0.04 mole fraction of copper were then used to study 17:: in alloys of different copper content, while alloys of the same mole fractions of silver were used to determine equivalent data for 178: at constant silver concentrations. The composition of the bath was held at the desired copper or silver concentration by making calculated additions of the appropriate solute throughout the experiment. From the limiting values of ?HAg in the constant copper content alloys it was possible to study ?HAg as a function of xCu and hence to determine 42:. A similar analysis of the re, values permitted calculation of nAgcu. Heat content and heat capacity data from Hultgren et al* were used to calculate heat of solution values from the measured heat effects at the experimental temperature of 720°K. RESULTS AND DISCUSSION Determinations of ?HAg. A preliminary investigation of the heat of solution of silver in pure tin at 720°K was first made in order to establish the value of nAgAg before additions of copper were made and also to compare the value of ?HOAg(l) with that obtained in the previous study of Ag-Au-Sn alloys.' Then the heat of solution of silver in Cu-Sn alloys was investigated as a func-

Jan 1, 1970

By C. M. Smith

PILOTED by Cadwallader, Evans, Jr., as chairman, the Coal Division got under way Monday morning for the first of three consecutive sessions. N. F. Patton started the ball rolling with a paper on the economics of anthracite distribution, which was ably discussed by H. J. Rose, W. S. Blauvelt, and others. Mr. Patton pointed out many incongruities in freight rates, dealers' margins, and other factors which are disturbing the distribution of anthracite, one result being that trucks are hauling at least six million tons of anthracite annually, half of which is stolen. In the discussion of the papers the desirability of greater uniformity in the production and shipment of coal from month to month was urged; with larger summer price concessions as a means toward this end. "Performance Expectancy of Domestic Underfeed Stokers for Anthracite," by Allen J. Johnson, brought this important platter down to date by showing the range in capacities and efficiencies to be expected from well-made stokers, and by detailing other of their operating characteristics. One of his most interesting points is that the efficiency of domestic stokers is practically equal to that of handfiring for good installations and operations of both

Jan 1, 1935

By J. F. Elliott

PRESENT knowledge of the usual metallurgical slags indicates that they are, for the most part, rather complex in behavior and as yet there is no ready means for describing, in a simple manner, the behavior of any one of them. One of the best known slag systems is the iron oxide-silica-lime ternary which is the basic "solvent" in a number of important metallurgical refining operations, the basic open hearth being one of the most important. In this operation, the slag dissolves such components as sulphur, phosphorus, manganese oxide, and magnesia. Considerable study of this slag system and the behavior of these additions has been carried out in the past by a number of authors, as has been summarized in several critical reviews.','2 However, except for determination of the activity of iron oxide, only a limited amount of effort has been directed towards developing, from these data, an understanding of the general behavior of the basic solvent. Reported here are the results from a series of calculations based on data from the literature which permit a semiquantitative evaluation of the activities of iron oxide, silica, and lime (plus magnesia) in the ternary system at 1600°C. The preliminary results, which were reported briefly at a symposium held by AIME in 1953, have been revised and are completed. The steps in the calculation are as follows:* I—establish the activity curves and the curve of the excess molar free energy of mixing at 1600°C for each of the binary systems, 2—construct the activity surface of iron oxide for the ternary from the data on the binary systems and information available in the literature for the ternary area, 3—determine the surface of excess molar free energy of mixing for the ternary system from the activity surface of iron oxide and from the molar curves obtained for the binary system, and 4—differentiate the ternary surface of the molar excess free energy of mixing to obtain the ternary surfaces for the logarithm of the activity coefficients for silica and lime (log rslo, and log rc.~). Si0,-Fe,O: Schuhmann and Ensio have measured the activity of iron oxide in simple iron oxide-silica slags when in equilibrium with y iron. Their data recalculated to 1600°C are shown in Fig. 1. Also included is a point representing a measurement by Gokcen and Chipmana of the activity of iron oxide at 1600°C at the point of saturation with solid silica. For convenience and in accordance with other treatments,' the calculations are based on the hypothetical component, FelO, which is obtained by converting all the analyzed iron in the slag to FeO. In spite of Schuhmann and Ensio's conclusion that the activity of iron oxide in the system does not vary with temperature over the experimental range of 1258" to 1407"C, the data are corrected to 1600°C assuming that temperature does have an effect. It was felt to be most reasonable to assume that the term log rr.10 is a linear function of the reciprocal of the temperature. Reyu has indicated that an effect of temperature on the activities in this system is to be expected from the Schuhmann and Ensio data. In essence, the correction consists of multiplying the experimental value of log rf,,o by the ratio of the experimental temperature in Kelvin to 1873°K. The magnitude of the correction is not large, being approximately 11.5 pct of the experimental value of log rve10. A very minor correction was necessary to compensate for the fact that the slags were in equilibrium with y iron in the experiment, while at steel-making temperatures they would be in equilibrium with liquid iron. Data for the correction were obtained from Darken and Gurry. The standard states established are pure liquid iron oxide (FelO) in equilibrium with pure liquid iron (with the appropriate amount of oxygen in solution) and pure liquid silica. The method of plotting in Fig. 1 is convenient for the calculation of the activity of liquid silica and permits a reasonable extrapolation for the activity of Fe,O in the ranges where no experimental data are available. The uncertainty in the extrapolation to infinity at one terminal where Nvelo = 1 for the usual Gibbs-Duhem integration is reduced considerably by this method. The region of two coexisting liquid phases is estimated to range from 1.8 to 41.7 mol pct Fe,O. The nature of the activity curve for the single-phase region indicates that the activity of iron oxide across the two-phase region is very close to 0.39. Computation of the function log ~F,,o/(1— NF,,o)' for this region (dashed line) in conjunction with the curve through the adjusted experimental data indicate the best probable value of 0.382 for alPe,o in the two-phase area. The line from 0 to 0.018 Nf~~o is obtained by assuming that the component follows Henry's law. In this range, the value for log rveto is 2.59. Appropriate mathematical manipulation of the plotted linet yields the activity curves for the The curve AF", the excess molar free energy of mixing (actual minus ideal), as shown in Fig. 3 is also computed from Fig. 1. This curve is required for subsequent calculations. CaO-Fe,O: The phase diagram for the lime-iron oxide system when in equilibrium with liquid iron is not well known but there appears to be no intermediate compound present. This fact as well as the activity values for Fe,O extrapolated to the CaO-Fe,O binary from Taylor and Chipman' tend to indicate somewhat negative deviations from ideality for the activity curves for the two components. Strong indication of this is evident in Fig. 1 where are plotted the points computed from the estimated activities of Fe,O for the binary system.' It appears that the best line through the data is a horizontal straight line. Because of the general indication of the slight negative departure from ideality, the line is extrapolated horizontally to NF~,o = 0. It is con-

Jan 1, 1956

By Richard McCaffery

CONTENTS PAGE 1. Research on Blast-furnace Slags (A Progress Report). By Richard S. McCaffery 5 2. Determination of Viscosity of Iron Blast-furnace Slags. By Richard S. McCaffery, Clarence H. Lorig, Ira N. Goff, Joseph F. Oesterle and Oscar O. Fritsche 27 3. Effect of Magnesia on Slag Viscosity. By Richard S. McCaffery, Joseph F. Oesterle and Oscar O. Fritsche 55

Jan 1, 1931

DISCUSSION, G. Derge and D. J. Girardi presiding N. A. Gokcen (Michigan College of Mining and Technology, Houghton, Mich.)—While the authors present very interesting results on the effect of sulphur upon the solubility of oxygen, they have not established convincingly the lines of two-fold saturation (the valleys in Fig. 2) and the ternary eutectic point. Their contention that sample S-7, upon melting at

Jan 1, 1954

By E. P. Whelan

A recent investigation1 into the origin of "ghost boundaries" in dilute Cd-Mg alloys has indicated the persistence of a segregated solidification substructure in spite of a homogenizing treatment designed to remove such segregation. Although no grain growth experiments have been reported on these segregated alloys, the homogenizing treatment used in grain growth studies on other dilute alloys2-7 is similar in

Jan 1, 1968