By Yue-yuan Li

China has abundant magnesite resource, but the low-grade and powder ores have always been rejected, which influences the comprehensive utilization of resource and often causes circumstance problems. The present work investigated the preparation of magnesia whisker using magnesite tailings as starting materials by preparation magnesium carbonate whisker as precursor firstly in the route of calcination, hydration, carbonation and pyrolysis, follows by second calcination of the precursor. The influence of pyrolysis conditions and additives on morphology of magnesium carbonate crystal as well as the influence of calcination conditions on morphology of magnesia whisker was investigated. The results showed that thermal decomposition products was MgCO3?3H2O. Magnesium carbonate whisker with length of 10~60 µm and the length-to-diameter ratio of 10~20 was prepared when soluble magnesium salt was added. While temperature was elevated at 1°C?min-1, magnesia whisker with length of 10~60µm was obtained.

Jan 1, 2010

By WU Jian-hui

Keywords: metallic material; nickel powder; thermal decomposition; precursor; fibrillar powder; nanometer scale; passivation treatment The precursor thermal decomposition process of fibrillar nanometer scale nickel powder and passivation treatment of obtained powder are investigated, and the composition and morphology of the products are characterized by use of IR, TGA/DTA, XRD and SEM. The results show that the precursor morphology is a decisive factor to the product morphology of the nickel powder. The morphology of the product derived at low decomposing temperature is irregular. The nickel powders produced at the temperature higher than 480 coheres seriously. The product particles are reunited with the decomposition time prolong. The powder prepared under the optimal condition is fibrillar like woolen yarn; the grain diameter is less than 50nm.

Jan 1, 2005

By Xuemei Zheng, Aiyuan Ma, Chao Liu, Guojiang Li, Chenyu Sun, Jinhui Peng, Libo Zhang, Yongguang Luo

In this paper, the removal of fluorides and chlorides from blast furnace dusts by water vapor enhanced microwave roasting was investigated, combined with the advantages of microwave selective heating and based on a thermodynamic analysis of zinc and lead halides. According to proposed reactions in the process, detailed experiments were systematically conducted to study the effect of roasting temperature, holding time, air flow, water vapor flow rates, and stirring speed on the efficiency of the removal of F and Cl. The results show that 97.26% of F and 64.23% of Cl could be separated when the condition of the roasting temperature of 650°C, stirring speed of 80 rpm, holding time at 60 min, air flow of 350 L/h and water vapor flow rate of 8 mL/min was optimized.

Jan 1, 2016

By A. M. Ramalho

In the synthesis and sintering processes to obtain superhard materials, such as diamond and cubic boron nitride, deformable ceramic capsule is used as gasket to transmit and support the required high pressures and high temperatures, HPHT. The ceramics materials for these capsules should have special physics and chemical characteristics such as refractoriness, shear strength and compressibility. In this work, Bridgman?s anvil made of hard metal or speed steel was used to characterize some ceramics materials in terms of their maximum compressible thickness. Tests were also performed with different resin polymers used as binding mixture with ceramics powder. Chemical analyses and investigations through scanning electronic microscopic (SEM), X-ray and real tests for the synthesis of diamond were also performed. The results showed that local Brazilian calcite can be successfully used in the manufacture of HPHT gaskets.

Jan 1, 2006

By Dongok Kim

Regardless of the advantages of the Friction Stir Process (FSP), for age-hardened aluminum alloys, the mechanical properties such as hardness in the stir zone decreased after FSP due to the growth or dissolution of strengthening precipitates. Here, as a new technique, FSP was introduced to alloy copper nanopowders in Al7075 T651. Mechanical properties of copper nanopowder- alloyed Al7075 T651 together with micro and nanostructures were compared with those of as-FSPed Al7075 T651 using SEM, TEM, and Vickers hardness testing to understand structure-property relationships. It was observed that Vickers hardness of the stir zone in copper nanopowder alloyed Al7075 T651 increased by 20% compared to that of the heat affected zone, while the as-FSPed samples did not show a noticeable increase in hardness in the same zone. Xray mapping showed traces of copper nanopowder after the process. TEM is being used to verify if there was CuAl2 formed in the copper alloyed sample.

Jan 1, 2006

By Frank R. Field, Randolph E. Kirchain, Elisa Alonso

"There are a number of environmental incentives for increasing recycling, including the reduction of waste, energy and resource use. Recycling can also be advantageous for manufacturing firms in both the short and long term. Secondary material can substitute for primary material, potentially dampening primary material price increases and reducing the pressure for greater primary extraction. This paper examines the potential for and dynamics of recycling for the case of platinum using a dynamic, behavioral simulation model of the primary and secondary markets. Since the secondary supply of platinum depends on a supply chain separate from primary extraction, recycling can diversify the risks of primary supply instabilities. Over time, recycling can cut primary consumption, reduce overall costs to firms, and possibly reduce the impact of price fluctuations upon firms.IntroductionThe benefits of recycling, from the perspective of the environment, are many, and the environmental benefits of increased recycling are considered a step towards increased sustainability [1, 2]. Life cycle assessments indicate that obtaining materials from secondary sources generally requires less energy and has fewer environmental impacts than extraction and refining of primary materials [3]. Analyses of materials flows show that, in addition to landfill volume reduction, recycling reduces primary material consumption, affecting long term materials scarcity [4, 5].The benefits of recycling are not limited to the environmental. Firms can benefit from the lower energy costs of recycling, especially that of metals whose primary extraction and refining are particularly energy-intensive (e.g., aluminum). The routine participation by firms in secondary materials markets (e.g., www.recycle.net) shows that this advantage has not gone unnoticed.Recycling can also benefit firms whose costs can be significantly affected by changes in material prices resulting from material shortages and material scarcity, with potentially permanent effects upon firms [6-8]. This paper focuses on the impact of recycling in the face of platinum scarcity for supply chain downstream firms."

Jan 1, 2008

By M. S. Borges

The need for the waste management industry to reach environmental patterns, technological innovation, and a technological demand of the productive sector is covered by this study. The environmental care and responsibility in the industrial sector and the necessary cultural changes for companies and entities is also emphasized. A collaborative tool was developed to help all partners involved in the environmental administration. This tool focuses on the interaction among residue generators in the productive chain. It was developed for a vehicle assembler company supported by entities or institutions with emphasis in the research, development and innovation, with expertise and capacity for new products creation, as well as reuse, recycling and reduction of by-products generation. The work aims to establish a tool for socio-environmental management, focusing on promotion and interaction between industrial waste generators sectors.

Jan 1, 2010

By Jiann-Yang Hwang

Microwave heating has been proved an effective method to rapidly heat iron oxide. This offers an opportunity to apply microwave heating in the steelmaking process. The reduction reaction of iron oxide is traditionally achieved at high temperature with reducing gases such as H2 and CO generated from various sources, including coke, coal, and natural gas. This study investigates the differences in iron oxide reduction using conventional and microwave heating under H2 and CO atmospheres. A special microwave thermal gravimetric device was designed and built to facilitate the investigation. With this device, iron oxides can be heated by electric resistance heating, microwave heating, or a combination of methods. The incoming CO and/or H2 also can be preheated to simulate a potential utilization of recovered heat. The iron oxide weight and temperature can be monitored during an entire reduction period. A series of reduction experiments have been conducted. The results are presented and discussed.

Jan 1, 2006

By Alberto Oalvez, Lucya Yunus, Pengfii Tan

"Laboratory flotation tests of slow cooled converter slag have showed that 92.5% copper recovery at the copper cut-off grade of 24 - 25 % can be achieved by using a 50:50 ratio of DSP330 and SIBX (sodium isobutyl xanthate) at the natural pH of 7 and with a grinding time of 18.5 minutes. 70ìéç is the P80 achieved at this grinding time. MIBC is the frother and the solid content of the flotation feed was 46%. In the plant trials, two types of collectors at two different feed particle sizes for both the normal and slow cooled slag were operated. The particle size was controlled by the feed rate. The P80 of 75 ìçé at a feed rate between 32 - 36 t/h were tested. The plant trials have demonstrated that the copper recovery in the milling and flotation process of the slow cooled slags was improved by 3%. IntroductionIt is proposed to float the slow cooled converter slag, in the auxiliary circuit of the copper concentrator at Mount Isa, by using the processing conditions identified from several laboratory flotation tests. Among these laboratory tests, one produced a copper recovery of 4 % higher than those achieved from a normal cooled slag with the same slag feed grade and the same copper content (24 - 26 %) in the concentrate. These test conditions were selected for further studies.Laboratory Test Work and Plant TrialsThere has been a lot of work conducted under laboratory and plant conditions [1]. However, the achieved results did not justify their total implementation in the Mount Isa Copper Concentrator. Initially, the lab trials were carried out with slag cooled 100% in air; then it was changed to combined cooling for 12 h with air and 2.5 days with water sprays. The reason for this change was the shortage of space when the slag was cooled 100% in air, as it takes several days to achieve safe temperatures for its removal. The San Manuel Copper Smelter has reported that their slag was left for air cooling in pits for 8 h and then was followed by water cooling for 2-3 days [2]"

Jan 1, 2012

By Murat Baydogan

Effect of retrogression and reaging treatment on hardness and stress corrosion cracking resistance of 7075 aluminum alloy was investigated. As received 7075 alloys in T6 temper condition were retrogressed at 170, 220, 240 and 380°C for different durations between 15 s and 60 min. Subsequent reaging was made at the T6 aging condition. Treated materials exhibited higher hardness and better stress corrosion cracking resistance than T6 temper in a wide range of retrogression temperature and time. The highest hardness was obtained after retrogression at 170°C for 210 s followed by reaging, corresponding to 20% hardness improvement. Improvement in stress corrosion cracking resistance of the alloy by as much as 85% was also observed. In this paper, improvements in hardness and stress corrosion cracking resistance are discussed on the basis of the microstructural changes during retrogression and reaging treatment.

Jan 1, 2006

By Javier Enrique Basurco Cayllahua

In this work, a gram-positive bacteria was used as biosorbent to elucidate the aluminum load capacity under different conditions related to metallurgical and chemical plants. The sorption data followed the Langmuir, Freundlich, Dubinin-Radushkevich isotherms. In order to determine the best isotherm fit, three error analysis methods were used to assess the data: correlation coefficient (R2), residual root mean square error (RMSE) and Chi-square test. The error analysis established that the Dubinin-Radushkevich model fits better the aluminum biosorption data. The maximum sorption capacity was found to be 41.59 mg.g-1. The maximum removal of aluminum was 95% at pH around 5. The experimental kinetics data was evaluated considering two models (pseudo-second order and pseudo-first order). This study indicated that the R. opacus is an environmental friendly biosorbent.

Jan 1, 2009

By P. A. Olubambi1

Representative samples of the hydrothermal vein deposits of the bulk complex sulphide ore deposit, 10 km south of Ishiagu, in Ebonyin State, South Eastern part of Nigeria were collected from two small scale mining companies. The samples were mixed and successively crushed in a jaw crusher and cone crusher, and ground in a rod mill. Characterization was carried out with SEM, EDX, XRD, XRF and ICP-OES. Mineralogical analysis revealed the presence of sphalerite, galena, siderite, pyrite, quartz and chalcopyrite. X-ray Diffractometry showed that sphalerite mineral in the ore occurs as sphalerite ferrous with varied percentage of Zn and Fe within the various sizes while chalcopyrite occurs as a chalcopyrite group mineral with chemical formula Cu2MnSnS4. Results of the elemental analysis showed variations in elemental composition within the different sizes.

Jan 1, 2006

By Chuanlin Fan

The process of flotation separation and recycling of spent potlining (SPL) was described. On the basis of the laboratory investigations, the effects of influencing factors in froth flotation process, such as grain size, flotation agent dosage, pH value, pulp density, and dissolved components concentration, etc, were carefully studied. And the influence on environment of the process was also discussed. It was found that flotation separation can be used as an environment-friendly method for treatment of SPL residue. Carbon and other compounds (include cryolite, sodium fluoride, calcium fluoride and diaoyudaonite, etc.) from SPL were separated and recycled as flotation products respectively.

Jan 1, 2009

By Zhigang Liang

A carbon free precast block was prepared by using high-alumina fused corundum as aggregate and fused magnesia, and ultra-fine Al2O3 and ultra-fine SiO2 powders as matrix materials. A small linear expansion for the precast block was achieved through spinel formation from the reaction of MgO with Al2O3. The precast block showed a lower apparent porosity, higher hot modulus of rupture and better slag corrosion resistance compared to the traditional Al2O3-MgO-C brick. Moreover, the practical application of the precast block to the ladle lining proved it to possess a better thermal insulation which could effectively prevent the temperature drop of molten steel during the refining process. It can be predicted that the carbon free precast block could possibly be accepted as a new type of ladle lining material for the production of low-carbon and ultra-low-carbon steel.

Jan 1, 2009

By Emma Arakelova

An increase in concentration of a Zn-containing volatile complex for synthesis of ZnO films was investigated when processing their target by ultraviolet radiation emitted by mercury lamp. The experiments were carried out using a flow-type quartz reactor. ZnO tableted target was preliminarily irradiated during 2 to 7 hours. H2O2 (98%) vapor at 25Pa passed through the reactor with ZnO target at 373K. As substrate material, five subsequent quartz cylinders were used at 423K. The experiment lasts 4 hours. H2O2 decomposition on ZnO surface was accompanied by formation of a Zn-containing volatile complex which passed in gas phase and decomposed on the substrates with isolation of final ZnO. The concentration of the Zn-containing volatile complex (N) in gas phase increases with UV pre-irradiation time (t) (without irradiation N = 1.05 1011 particles/cm3; after t=2 hours, N = 5.19 1011 particles/cm3, after t=4 hours, N = 9.95 1011 particles/cm3; after t=7 hours, N = 1.86 1012 particles/cm3.

Jan 1, 2006

By Licheng Zhou

The use of aquatic plants for the removal of heavy metals from wastewater has gained high interest. In this study, batch experiments were conducted to evaluate the adsorption of copper ions in aqueous solution by P. pectinatus L. under various conditions of contact time, initial pH of the solution, metal concentration and adsorbent dosage. The results showed that the maximum adsorption amount of copper ions by P. pectinatus L. was 22.60 mg/g when the initial copper ions concentration was 98.41 mg/L at pH 4.5. The Langmuir and Freundlich models were used to describe the adsorption equilibrium of copper ions on P. pectinatus L. and the adsorption followed the Langmuir isotherm. The adsorption kinetic was well-fitted with pseudo-second-order sorption equations.

Jan 1, 2009

By Qiang Zhang

Hybrid composites are fabricated by adding two reinforcements into matrix materials so that the expected excellent properties can be achieved through the combined advantages of short fibers, and different size particles (micron or submicron), which provide a high degree of design freedom. In this paper, hybrid preforms were produced with the different size reinforcement of the Al2O3 particles and short fibers. The Al-Si alloy-based hybrid composites were fabricated by preform-squeezing casting route. The structure and performance of composite materials were studied with the Transmission Electron Microscopy (TEM), and Scanning Electron Microscopy (SEM). The results show that the reinforcements, both particles and fibers, distribute homogeneously in the matrix materials, and the properties of composites are found to improve in comparison with the matrix Al-Si alloy.

Jan 1, 2009

By Jinhui Li

Silver is a very important metal used in a wide range of applications. It is necessary to recovery of Ag from electronic wastes for increasing of Ag price and circumstance protection. For separating and recycling Ag from Ag-Cu composite materials, thermodynamic data of reaction is calculated and some experiments have been proceeded with Ag-Cu composite material scraps, time, temperature, nitric-sulfuric mixed acid volume ratio and the volume ration of mixed acid vs. water have been discussed. The results show that the optimization conditions is that nitric-sulfuric mixed acid volume ratio 5:95, volume ratio of mixed acid vs. water 10:1, temperature 55?, time 25min. In the conditions, Ag can be selectively leached from Cu-based composite material, Cu base is not eroded nearly.

Jan 1, 2009

By Sergio N. Monteiro

Wastes generated by our society and the question on how to dispose them is, nowadays, a relevant matter of concern. The objective of the present work was to characterize the technical properties of composites made of discarded jute sackcloth with its coarse wove fabric, serving as reinforcement phase, and polyethylene wastes collected from city dumps, as continuous matrix. Different amounts, up to 30 wt.% of jute plain weave, fabric were press molded at 160°Ctogether with sieved polyethylene particles. The resulting composites displayed mechanical properties that could compete with those of low-density wooden board. Both by presenting a solution to, otherwise, disposed wastes and by helping to prevent deforestation, the investigated composite may be regarded as an environmentally correct material.

Jan 1, 2006

By Sergio Neves Monteiro

The efficiency by which an applied load is transmitted through the composite structure depends on the strength of the interface between the matrix and the second phase. In fiber reinforced composites, the interfacial shear stress plays a major role in the composite capacity to support the applied load. This interfacial stress can be obtained by means of pullout tests using the fiber embedded to a certain length in a socket of the matrix material. In the present work, pullout tests were performed to evaluate the interfacial shear stress of ramie, a relatively strong natural fiber, reinforcing polyester matrix composites. The general result permitted to calculate a critical length for the ramie fiber embedded in polyester resin. From this critical length, the value of the interfacial shear stress was calculated. An interpretation of this result together with SEM observation displayed a relatively weak bond between the ramie fiber and the polyester matrix.

Jan 1, 2010