By R. F. Hollis, C. K. McArthur

PRIOR to the application of anion exchange, all recovery of uranium from acid leach liquors precipitated an impure product requiring further upgrading before it could be refined. The ion exchange process, on the other hand, provides excellent selectivity for extracting soluble uranium from leach liquors, so that high grade concentrates can be produced directly. The discovery that uranium is readily adsorbed by anion exchange resins, together with the experience of resin and equipment manufacturers in water treatment, led to rapid development of ion exchange in a multiple column operation. Many processing plants using fixed bed ion exchange are in operation or under construction in Africa, Australia, and Canada. There are a limited number in the U. S. Although the fixed bed process has been highly successful, the feed to the ion exchange columns must be a clear solution, which is obtained by filtration or by countercurrent decantation of leached pulps. With some ores, poor filtration or settling characteristics make production of a clear solution difficult. Most processing plants in the U. S. receive their ores from a number of small mines, and there is considerable variation in the settling and filtering behavior of the ores. An ion exchange process was therefore desirable in which the uranium could be recovered directly for the leached pulp by adding ion exchange resin, which could be then separated from the pulp by a screening operation. The process would thus resemble the cyanide-charcoal process in which gold is adsorbed from cyanide pulp by means of activated charcoal. Preliminary tests in which leached pulps were directly contacted with resin beads led to the development of the RIP process.

Jan 4, 1957

By C. S. Blair

THE development of a geological department as an integral part of the Tennessee Coal, Iron & Railroad Co. in the Birmingham district, Ala-bama, in 1908 was an innovation probably unique for any mining organ-ization south of the Ohio River, At that time a few of the oil companies were starting geological departments, but there were no geologists among the larger industrial organizations. The Tennessee Coal, Iron & Railroad Co. had been a substantial producer of pig iron for many years and was just getting a start in the manufacture of steel products from the pig iron. It had large acreages of coal land, ore land and timber land, but there was lacking the detailed knowledge of the possible mineral resources of much (of its territory, and this territory at that time covered an area in the neighborhood of 500,000 acres in the states of Alabama, Tennessee and Georgia. Those responsible for the operations of the mining properties, not being familiar with the kind of help that might be expected from geologic work, were decidedly skeptical of the utility of the work. Therefore it was necessary to develop cooperation with the mining organization, by not infringing upon its functions, and by developing the work in such a manner as to demonstrate to the mining department its practical utility. In the first instance the man responsible for a mining operation is apt to assume the attitude that the geologist is a blockader, because the geologist, unfortunately, is obliged to point out difficulties in the carrying out of mining operations in the way originally planned. He points out the dangers of mining out one coal or metal seam at the ultimate expense of an upper or lower seam, and he develops structural features, such as faults and folds, which call to the attention of the mining operator diffi-culties in his future operations, which the latter had not anticipated. Eventually, however, -the value of having these data became ap to the Tennessee Coal, Iron and Railroad Co., and the operators not only welcomed the geological work and cooperated fully in its acquisition of essential information, but reached the point of asking assistance and advice; and complete coordination of the two activities has existed for many years.

Jan 1, 1933

E. E. THUM,* Salt Lake City, Utah (written discussion?).-While the present paper is confined exclusively to the microstructure of fusion welds, it may be of interest to draw attention to certain appearances existing in resistance welds such as spot or butt-welded joints produced by the Thomson process. For instance, a butt weld between two pieces of carbon tool steel (carbon about 0.90 per cent.) will show concentric ellipsoids of the various materials from pearlite to martensite. The surfaces of demarcation are quite well defined, the center of the ellipsoid being at the intersection of the axis of the piece and the plane of the weld. Often these unannealed welds show a troostitic center; evidently this core was not quenched as rapidly as the surrounding shell. Such specimens are beautiful samples for instruction purposes. An annealed butt weld of this kind will show a very well defined central ellipsoid of decarburized, materials. It is interesting to consider the reason why this change takes place. It must be understood that the heat is on the metal for a very short time, possibly 30 sec. It is therefore evident that the decarburization, or migration, of the carbon takes place with extreme rapidity. Since no blowholes are evident in a well-made butt weld, the deoxidizing air and the products of combustion must migrate with the highest speed; second, the carbon might migrate back into the stock; or, last, a large proportion of the pearlite may be extruded with the hot metal, which forms a fin at the plane of weld. Examining these possibilities in detail, it is not probable that such deep-seated decarburization, extending with maximum effect to the very center of a 2-in. round bar, is done by reaction with the oxygen of the air. This would postulate entrance of oxygen and egress of carbon oxides in large quantity without leaving behind traces in the form of oxides or

Jan 5, 1919

By T. L. Loucks, E. T. Guerrero

Pressure drop characteristics in a system composed of two adjacent concentric regions of different permeability were studied. The differential equations for continuity of mass flow in the two regions were solved using the Laplace transformation and the necessary boundary conditions to give the pressure distribution in the composite reservoir, the resulting equation for pressure drop at the inner boundary was evaluated for a variety of composite reservoirs and compared with the results for a uniform reservoir. From this study it was found that under certain conditions the permeability in both zones, as well as the size of the inner zone, can be determined from the pressure drop curve. INTRODUCTION The theory for the pressure distribution and pressure build-up behavior of a well producing a single, slightly compressible fluid from infinite and finite homogeneous reservoirs was presented by Hornerl and Miller, Dyes and Hutchinson.2 Extensions on this original work to provide improved and extended interpretations and better agreement between theory and observed results have been made by Matthews, et a1,3 van Everdingen,4 Gladfelter, et al5 Stegemeierand Matthews,6 Hurst and Guerrero,7 and Perrine.8 More recently Lefkovits, et al,9 studied pressure build-up behavior in bounded reservoirs composed of stratified layers. Houpeurtl0 has suggested various approaches to the general problem of variable permeability and porosity but presented no analytic solutions for particular permeability variations. Albert, Jaisson and Marionll studied the finite composite reservoir and presented numerical solutions to the unsteady-state case and an analytical solution valid only for large times. They also studied the so-called pseudo-steady state for several examples of radial permeability variations. Very similar examples have been treated in the unsteady state with application to pressure build-up by Loucks in an unpublished manuscript. More recently Hurst12 has presented the complete point-sink solution (valid for all times) for the infinite composite reservoir. He applied these solutions to interference between oil fields along with an even more elegant application of his explicit solution to the material-balance equation including water influx. Mortada 13 approaches the same application by avoiding the point-source limitation but gives the solution for the aquifer region which is valid only for large times. Hopkinson, Natanson and Temple14 have treated both the finite and infinite composite reservoir obtaining the pressure distribution for the inner zone valid for large times. This paper presents a theoretical study of the pressure distribution in an infinite composite reservoir composed of two adjacent concentric regions of different permeability. The object was to determine the manner in which pressure drop at the inner boundary of a composite reservoir depends upon time, the permeability of each zone and the size of the inner zone. Expressions for the pressure distribution in both zones are developed which take into account the radius of the sink and are valid for small times as well as large times. It was felt that an understanding of the pressure drop behavior in various composite reservoirs would be of assistance in the interpretation of some pressure build-up curves which do not behave according to the theory derived for uniform systems. Often the region surrounding the wellbore is either more permeable or less permeable than the reservoir because of the various drilling and completion practices. The effects of reduced permeability due to drilling-fluid invasion and of increased permeability due to fracturing or acidizing need to be more carefully defined. Therefore, an equation for the pressure drop in a composite reservoir was developed, and the effects of both the permeability in each zone and the size of the inner zone were studied. STATEMENT AND SOLUTION OF PROBLEM BOUNDARY CONDITIONS AND ASSUMPTIONS The physical system studied was a composite

By R. N. Upadhyay, M. Maleki, I. Fatt

Conventional laboratory core analysis tests on samples of two limestone reservoir rocks indicate that about 20 per cent of PV is in dead-end pores. These tests (electric logging formation factor, mercury injection capillary pressure and miscible displacement) were carried out on 1/4-in. diameter test plugs. Test results show a clear dilference between these samples and sandstone or homogeneous limestone reservoir rock. Although the amount of dead-end pore space can be only roughly estimated, the presence of such pore space seems clearly indicated. Pressure transient studies also show presence of deadend PV. Although they do not give quantitative results, pressure transient data yield a reasonable estimate of the size of the neck connecting dead-end pores to the main flow channels. INTRODUCTION Equations conventionally used to describe reservoir flow behavior contain the implicit assumption that all connected pore spaces contributed to both porosity and permeability. Several authors3-7 have pointed out the changes in pressure transient behavior and in electric log interpretation that may result if this assumption is incorrect and, instead, dead-end or cul-de-sac pores are present. There is a need for laboratory tests that can detect presence of dead-end pores in core samples. With such information on hand the petroleum engineer can make more rational use of the mathematical tools now available for analysis of reservoir flow behavior. This paper describes laboratory studies designed to detect and, if possible, give a quantitative measure of dead-end PV in laboratory-size core plugs. Three reservoir rocks were used, two of which were limestones suspected of having deadend pore spaces and a well-known sandstone, used as a comparison standard, in which there is believed to be little or no dead-end pore space. All the studies were designed to measure the natural dead-end PV; i.e., the pore space which is dead-ended because of rock structure. During multiphase flow in a rock without dead-end pores, some parts of one of the phases can become surrounded by the other, thereby giving (for certain flow behavior) an effective dead-end pV8,9. Such behavior will not be described here.

Jan 1, 1967

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world's annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months' to several years' duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1'2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis' method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By C. M. Loeb, T. E. Norman

The use of ball, rod and tube mills for grinding ore, cement and other materials has grown so rapidly during the past forty years that the world's annual consumption of ferrous grinding media for these mills is now estimated to be between one half million and one million tons per year. Ferrous grinding balls constitute the major portion of this tonnage. Obviously they represent suficient value to justify thorough studies of the factors governing their performance. The selection of grinding balls is governed principally by: I. Quality (wear resistance, impact resistance, soundness, and the like). 2. Sources of supply and delivered cost. 3. Grinding characteristics or efficiency in the ball mill. This paper deals principally with the quality of ferrous grinding balls. In the study of these factors certain data relative to the fundamental nature of ball wear in ball mills have been obtained. These data are also presented and discussed briefly. The Development of a Suitable Wear Test A study of the fundamental factors governing the quality of grinding balls has been hampered seriously by the fact that a competent test has, in the past, involvetd the purchase of several hundred tons of halls of a specific type which were then run in one or more ball mills for a period ranging from several months' to several years' duration. Often, during the period of test, it became necessary to change operating conditions or the character of the ore fed to the test mill with the result that the rate of ball consumption changed and the test figures became of little value. Under such circumstances, progress in the development of better grinding balls, has been necessarily slow. Economic factors and variations in the quality of balls produced by different sources of supply generally make it necessary for each mill operator to determine for himself the most suitable type of balls for his mills. In our own ball mill grinding operations at Climax, Colo., we were faced with this problem. After we had run a few large scale wear tests at considerable expense we decided to investigate the possibilities of a small scale wear test which would be capable of testing numerous types of balls within a relatively short time. The most important requirement of any test is, of course, that it give results which can be used to predict accurately the wear in full scale operations. It was known that Ellis and his associates1'2 had developed a method of testing grinding balls by small scale tests run at the Ontario Research Foundation. Ellis' method of testing was used as a starting point in our investigations. In the course of our tests a number of modifications of the original method were found to be desirable so that, by an evolutionary procedure, a method of small scale

Jan 1, 1949

By Hugh M. Roberts

In the spring of 1915, then a 30-year old geologist in the employ of the E. J. Longyear Co., of Minneapolis, Minn., I accompanied prospectors to ex- amine outcrops of supposed nickel ore situated a mile or two in from the shore of a lake in the Kenora district of northwestern Ontario. The deposit proved to be bog iron ore containing traces of nickel. We were stormbound there for three days, a circumstance which gave rise to a tale that was told at our fire one night. It seems that Sandy and Jock, two prospectors, were crossing the bay of a large lake in a canoe. They were bucking headwinds; the waves grew higher. Jock called out from the stern, "Sandy, can ye na pray a little." Sandy pressed his knees a little closer into the bow and, between strokes of his paddle, sought for words, which came haltingly, "Save us this time . . . Oh Lord . . . and we promise . . ." when Jock, peering through the spray sang out, "I would na commit yourself, Sandy, I think I see lond ahead."

Jan 1, 1965

By AIME

The Taconites Are Ready, the editorial appearing on P. 933 of the September issue, has provoked comment from several informed engineers to the effect that the indicated profit margin was considerably exaggerated. The cost figures in the editorial, taken from the Congressional Record, were characterized as inaccurate by some correspondents. The theme of the story was, however, substantiated in the announcement (P. 1023, October) that Republic and Armco had joined forces in a $160 million project for taconite development. Chief among the dissenters was E. W. Davis, , Director of the Mines Experiment Station at the University of Minnesota. Mr. Davis has worked up the following set of cost figures:

Jan 1, 1950

By W. F. Holbrook, C. E. Wood, E. P. Barrett

The Blast Furnace Studies Section, Metallurgieal Division, Bureau of Mines, has been working for several years on the mechanism of desulphurization of iron and steel by slags. The usual assumption that desulphurization takes place by diffusion of FeS from metal into slag and subsequent reaction of this FeS with CaO to produce CaS has seemed to us inconsistent with a number of experimental results we have obtained. We undertook, for example, to determine the proportion of sulphur in a slag present as FeS. An entirely satisfactory method of doing this has not yet been evolved. The results of extraction with metallic antimony led to an interesting conclusion, however. FeS is readily soluble in metallic antimony, either physically or by chemical reaction. On the other hand, CaS was found to be insoluble. Hence it would appear that by rapid extraction of the slag with antimony we might expect to determine the distribution of sulphur between iron and calcium. The results showed that much of the sulphur was present as FeS. In some instances the extraction of sulphur as FeS was almost quantitative. For example, in a slag containing 3.8 grams Fe and 3.7 grams S, extraction removed 1.18 grams S and 2.12 grams Fe. If all the iron present in the antimony had been FeS, 1.21 grams S would have been extracted. In another slag with 8.6 grams Fe and 0.06 gram S present, 0.14 gram Fe and 0.08 gram S were extracted. This was obviously extraction of sulphur as FeS within the analytical error and showed that FeS was present either in solution or as a dispersion. Attempts to determine the solubility of FeS and CaS in slag by quenching and ultramicroscopic investigation have indicated that the solubility of FeS is very low, and that reactions in the slag are probably not to be considered as homogeneous. A more detailed report on these theoretical considerations will be made at a later date.

Jan 1, 1940

By W. F. Holbrook, C. E. Wood, E. P. Barrett

The Blast Furnace Studies Section, Metallurgieal Division, Bureau of Mines, has been working for several years on the mechanism of desulphurization of iron and steel by slags. The usual assumption that desulphurization takes place by diffusion of FeS from metal into slag and subsequent reaction of this FeS with CaO to produce CaS has seemed to us inconsistent with a number of experimental results we have obtained. We undertook, for example, to determine the proportion of sulphur in a slag present as FeS. An entirely satisfactory method of doing this has not yet been evolved. The results of extraction with metallic antimony led to an interesting conclusion, however. FeS is readily soluble in metallic antimony, either physically or by chemical reaction. On the other hand, CaS was found to be insoluble. Hence it would appear that by rapid extraction of the slag with antimony we might expect to determine the distribution of sulphur between iron and calcium. The results showed that much of the sulphur was present as FeS. In some instances the extraction of sulphur as FeS was almost quantitative. For example, in a slag containing 3.8 grams Fe and 3.7 grams S, extraction removed 1.18 grams S and 2.12 grams Fe. If all the iron present in the antimony had been FeS, 1.21 grams S would have been extracted. In another slag with 8.6 grams Fe and 0.06 gram S present, 0.14 gram Fe and 0.08 gram S were extracted. This was obviously extraction of sulphur as FeS within the analytical error and showed that FeS was present either in solution or as a dispersion. Attempts to determine the solubility of FeS and CaS in slag by quenching and ultramicroscopic investigation have indicated that the solubility of FeS is very low, and that reactions in the slag are probably not to be considered as homogeneous. A more detailed report on these theoretical considerations will be made at a later date.

Jan 1, 1940

By Y. H. Liu, G. W. Powell

Thin foils made from the gold-rich region of- short (0.15 mm)Au-Ag diffusion couples annealed at 880°C for 1 hr were examined in ax electron microscope and the structures were compared with that of pure gold subjected to identical heat treatments. The couples underwent Plastic deformation (bending) during the diffusional anneal. The foils prepared from the diffusion zone have a higher dislocation density and incidence of subboundaries than pure gold. The plastic bending of the couple can be interpreted in terms of the climb of edge dislocations, which are pavallel to the bend axis, along the direction of diffusion. THE interaction of lattice defects during interdiffu-sion between two metals has been considered by several investigators. In particular, da Silva and Mehl,1 Barnes,' and Bardeen and Herring3 have proposed models based on interactions between point and line defects to account for the Kirkendall effect (marker movement). Each of these models is based on dislocation climb, which can either add or remove lattice planes, induced by an under- or supersaturation of vacancies. A theoretical treatment of the nucleation and growth of voids by the condensation of vacancies has been presented by Seitz.4 Stresses can arise in a binary diffusion couple as a result of the vacancy flux and the gradient in the lattice parameter. rinkmman' has investigated the effects of diffusion-induced stresses on void formation; the results of his analysis suggest that voids can form and grow under the influence of these stresses in the absence of an excess vacancy concentration. The relationships between vacancy supersaturation and diffusion-induced stresses and void formation have been elucidated also by Balluffi and seigle6 who concluded that the stress generated by a vacancy supersaturation aids the growth of voids. Experimental evidence which indirectly shows that stresses are produced by chemical diffusion has been obtained by several researchers.2,7-9 This evidence consists in part of the observation by light microscopy of the formation of subgrains, a process characteristic of the high-temperature deformation of some metals during creep.'0 More striking, however, is the plastic bending of short (0.2 mm) Cu-Ni couples observed by Barnes2 and of boron-doped silicon crystals reported by Queisser.9 Diffusion-induced dislocations in iron and silicon have been investigated by Ainslie et a1.11and Schwutte and Queisser,12 respectively, the former using transmission electron microscopy and the latter an X-ray transmission technique. Matthews and Crawford13 observed the formation of boundaries by the climb of interfacial misfit dislocations in thin, vapor-deposited Au-Pd couples diffused in situ in an electron microscope. In order to obtain additional information on the phenomena associated with defect interaction and diffusion-induced stresses in binary couples, an electron transmission study of foils prepared from the diffusion zone of short Au-Ag couples was undertaken. The initial objective was to investigate the processes occurring at various points of the diffusion zone. Subsequent research demonstrated that foils could be prepared only from the gold-rich region of the diffusion zone using the technique described herein. EXPERIMENTAL PROCEDURE Preparation and Annealing of the Diffusion Couples. The couples were made from annealed, high-purity (99.999 pct). polycrvstalline gold and silver sheets (0.075 mm thick). Shall (0.075 by 5 by 17 mm) elec-tropolished coupons of gold and silver were pressure-bonded by heating the two metals in a graphite device to 770°C and holding at this temperature for approximately 30 min. The quality of the bond was ascertained by metallographic examination at 150 times. Each couple subsequently was annealed at 880°C for 1hr; under these conditions, the extreme portions of the

Jan 1, 1968

By John Devine

DURING the past few years the Bureau of Mines has been studying hydrogen-sulfide corrosion in the petroleum and natural-gas industries. Early work was confined to investigating the various practical, or operat-ing, factors that control the corrosion reaction when ordinary mild steel is being attacked. In that work it was shown that, if the optimum operating conditions1 are obtainable, . gas containing hydrogen sulfide can be handled at ordinary temperatures without serious corrosion resulting. However, frequently "sour" gas must be handled under other than optimum operating conditions, and combating corrosion then becomes a problem to be considered more during the construction of a system than during its subsequent operation. That is, where economi-cally practicable in such cases the designer will seek to substitute for mild steel other steels or ferrous metals more resistant to corrosion by hydro-gen sulfide. The comparative resistance of various commercial steels and alloy steels to corrosion by hydrogen sulfide at elevated temperatures has been reported systematically by previous investigators,2 but similar information for corrosion at ordinary temperatures is available only from scattered sources, representing different methods of testing. As the value of comparative corrosion tests depends largely upon the use of a

Jan 1, 1934

By R. Schuhmann Jr., P. J. Ensio

As a first step in a study of the physical chemistry of copper-smelting slags, experimental measurements were made of the oxygen pressure of simple iron-silicate slags in equilibrium with solid iron. The experiments consisted in bubbling CO2-CO mixtures through the slags in iron crucibles and in finding the equilibrium ratios of CO2 to CO. From the data, activities and partial molal heats of solution FeO and SiO2 in the slags were calculated. THE ternary system FeO-Fe,O,-SiO, is the simplest system which can represent adequately the important chemical properties of the slags formed in matte smelting and converting. Accordingly, the experimental study of slags in this system was started as the first step in a general research program on the thermodynamics of copper smelting. A recent paper by one of the authors' outlines this general research program and shows in some detail how information on thermodynamic properties of iron-silicate slags, especially information on oxygen activities, is essential to a full understanding of the chemistry of copper smelting. The FeO-Fe,O,-SiO, system also is the basis of slags produced in other processes, such as acid steelmak-ing processes, and is important in relation to the behavior of silicious refractories. In addition, data on the physicochemical properties of iron-silicate slags should contribute to a general understanding of the nature of slags, since at present such data for all kinds of slags are relatively meager. The principal quantitative information already available on iron-silicate slags consists in Bowen and Schairer's constitution diagram for slags in equilibrium with metallic iron,' Darken and Gurry's complete and precise thermodynamic study of the Fe-0 system,",' and Darken's study of the phase equilibria in the Fe-Si-o system. From the results of this previous work, it was clear that a complete thermodynamic study of ternary iron-silicate melts was a major undertaking which would have to be broken down into parts, including the working out of the ternary equilibrium diagram as well as extensive activity measurements on slags. The experimental measurement of oxygen activity, using CO-CO, and other gas mixtures as yardsticks of oxygen activity, was the basis of Darken and Gurry's study of the Fe-0 system. From the experimental measurements of oxygen activities over a large range of temperatures and compositions, they were able to calculate the activities of other species such as Fe, FeO, Fe,O,, etc., and also the other important thermodynamic properties in the Fe-0 system. At the start of the present investigation, it appeared that the same approach would be fruitful for the study of iron-silicate melts. Also, the experimental measurement of oxygen activities seemed particularly attractive because oxygen activity itself is a quantitative measure of oxidizing or reducing power, which is an important variable in copper-smelting slags. The slag compositions in equilibrium with yFe appeared most suitable for the first investigation of this kind, for the following reasons: 1—Good constitution data2 were available. 2—An iron crucible could be used, thus affording a simple solution to the refractory problem without introducing contarnination. 3—With Fe activity fixed, at unity with respect to a standard state of solid Fe, measurements of 0 activity could be followed by simple calculations of activities of FeO and other Fe-0 complexes and of SiO,. 4—This starting point afforded several possibilities for cross-checking with previous work,

Jan 1, 1952

By Daniel R. Hull

In 1926 Gendersl reviewed the existing theories of this subject and stated his views in support of the gas-pressure theory. Again, in 1937, the subject was thoroughly reviewed by N. B. Vaughan3 and by Phillips and Brick,2 so that no résumé is called for here. The purpose of this paper is to describe certain observations made in the course of mill work, and to point out that they mostly tend to confirm the gas theory of Genders. Vapor Segregation There is, however, one type of inverse segregation that can be accounted for by considering the volatility of one of the constituents of an alloy. The most familiar case is ordinary brass, which is subject to a zinc enrichment of a few tenths of a per cent at the surface of a chill casting. This has been noted in 70-30 brass by Genders, and a typical example of it is given in Table 1, which represents a cylindrical billet 7 in. in diameter by 55 in. long. After lathe-turning 1/32 in. from the surface, the remaining distance to the center was sampled at six equally spaced intervals. the lead, which is essentially the same throughout, will be mentioned later. Consider a brass-mill mold, either round or rectangular in cross section, standing several feet high. It may require a minute or two for pouring. Before it is full, the metal in the lower end has partly solidified and contracted somewhat away from the mold. The initial shell of solidification follows not far behind the top of the column, even if the central portion is liquid for a long way down. There is, then, a space between metal and mold that is filled with zinc vapor. The vapor has no exit, because the liquid at the top of the rising column is not only in contact with the mold but keeps UP a fresh supply of zinc vapor, which has, perhaps, already begun to condense in the lower portion. The cycle is short. Within a minute or two after the mold is full the bar has cooled enough to condense all the zinc. Some of it may condense on the mold; it might be expected that most of it would condense there, but the mold at that time is well coated with a velvety carbon residue from the oil dressing, overlain by fluffy zinc oxide that commenced covering the inside of the mold as soon as pouring began. The clean skin of the freshly cast brass offers a preferred surface for condensation. Reabsorption is quick and inevitable. A simple experiment indicates that a surprisingly large quantity of zinc vapor is trapped in the space between mold and

Jan 1, 1941

By Daniel R. Hull

In 1926 Gendersl reviewed the existing theories of this subject and stated his views in support of the gas-pressure theory. Again, in 1937, the subject was thoroughly reviewed by N. B. Vaughan3 and by Phillips and Brick,2 so that no résumé is called for here. The purpose of this paper is to describe certain observations made in the course of mill work, and to point out that they mostly tend to confirm the gas theory of Genders. Vapor Segregation There is, however, one type of inverse segregation that can be accounted for by considering the volatility of one of the constituents of an alloy. The most familiar case is ordinary brass, which is subject to a zinc enrichment of a few tenths of a per cent at the surface of a chill casting. This has been noted in 70-30 brass by Genders, and a typical example of it is given in Table 1, which represents a cylindrical billet 7 in. in diameter by 55 in. long. After lathe-turning 1/32 in. from the surface, the remaining distance to the center was sampled at six equally spaced intervals. the lead, which is essentially the same throughout, will be mentioned later. Consider a brass-mill mold, either round or rectangular in cross section, standing several feet high. It may require a minute or two for pouring. Before it is full, the metal in the lower end has partly solidified and contracted somewhat away from the mold. The initial shell of solidification follows not far behind the top of the column, even if the central portion is liquid for a long way down. There is, then, a space between metal and mold that is filled with zinc vapor. The vapor has no exit, because the liquid at the top of the rising column is not only in contact with the mold but keeps UP a fresh supply of zinc vapor, which has, perhaps, already begun to condense in the lower portion. The cycle is short. Within a minute or two after the mold is full the bar has cooled enough to condense all the zinc. Some of it may condense on the mold; it might be expected that most of it would condense there, but the mold at that time is well coated with a velvety carbon residue from the oil dressing, overlain by fluffy zinc oxide that commenced covering the inside of the mold as soon as pouring began. The clean skin of the freshly cast brass offers a preferred surface for condensation. Reabsorption is quick and inevitable. A simple experiment indicates that a surprisingly large quantity of zinc vapor is trapped in the space between mold and

Jan 1, 1941

By F. Forward, H. Veltman, A. Vizsolyi

Activities of oxides in the ternary FeO-MnO-SiO system are calculated from data on the binaries, using the Gibbs -Schuhmann method. These activity data are used, together with thermodynamic relations, to calculate the contents of oxygen, silicon, and manganese in liquid iron, and the composition of the corresponding oxide phases in equilibrium with it. Excellent agreement was found between calculated and experimental metal compositions, indicating that thermodynamic methods, such as those presented, can supply useful data on slag-metal equilibria, and are therefore capable of wider application. When molten steel containing oxygen is treated with a deoxidizer, the product of the reaction is composed of the oxides of the deoxidizing elements together with more or less iron oxide. This assemblage of oxides is presumably very close to equilibrium with the melt since it is formed directly from elements dissolved in it. Therefore, it is likely that metal analyses corresponding to a given oxide phase composition are calculable with considerable precision where sufficient information is available on activities in both phases. The present study was made to test this hypothesis in the case of deoxidation by silicon and manganese. Here experimental data on the relationship among oxygen, silicon, and manganese in the metal phase are available, as are activity data for the MnO-SiO2, FeO-SiO2, and FeO-MnO binary systems. A further objective was to demonstrate in a specific example how gaps in the data may be filled by judicious interpolation, and how the Gibbs-Schuhmann method is applied to obtain activities in ternary systems. The rigorous derivation of the latter, requiring considerable facility in handling partial differential equations, tends to mask the real simplicity of the method, and repel the very engineers and experimenters who would benefit the most from its use. I) GENERAL PROCEDURE Deoxidation of steel with silicon and manganese results in the formation of two phases, metal and oxide. The number of components is four—Fe, Mn, Si, and 0. The phase rule then gives the number of degrees of freedom: If temperature and pressure are fixed, 2 deg of freedom remain. Consequently, it suffices to fix the concentration of two of the components of the system for all the concentrations to be determined and, at least in principle, calculable. The practical problem is then to discover a straightforward method of calculation with a minimum of trial and error solutions. The type of reactions to be dealt with are like the following: Si (in steel) + 2 O(in steel) = SiO2(in oxide phase) The standard free energy of this reaction is readily obtained from the literature, so that the equilibrium constant can be calculated by the expression: Since the metallurgist is concerned with percentages rather than activities, a real solution requires information that will permit activities to be converted to concentrations. This information is fairly adequate for the elements dissolved in molten steel, but is not available for the FeO-MnO-SiO2 oxide system. Therefore, the first step in this study was to find the relation between activity and concentration for the three oxides making up the system. The next step was the calculation of slag and metal compositions that are in equilibrium with one another. As shown by the phase rule, it is sufficient to assume the values of two composition variables in order to calculate the rest. But which two are picked makes a vast difference in how difficult the calculation turns out to be, so that it is necessary to make preliminary trial of several routes to find the easiest one. A convenient method is to begin with the slag, and to pick FeO concentration and that of one of the other oxides. Starting with the relation between oxygen dissolved in the liquid steel and FeO in the slag permits a good first estimate to be made of the oxygen content of the steel in equilibrium with FeO, because the iron content being fairly close to 100 pct, Fe has an activity close to unity. Using this first estimate of oxygen activity, approximate values of the manganese and silicon contents of the melt are readily calculated from the appropriate equilibrium constants. A minor correction for the depar-

Jan 1, 1963

By W. C. Roberts-Austin

The subject with which the Council of the American Institute of Mining Engineers has entrusted me is one of much interest. It has been so admirably treated in America by Prof. Carl Barus* that I should have hesitated to deal with it had not the adoption of pyrometric methods in England recently occupied much attention, especially in relation to metallurgical industries and research. I shall endeavor to show what is the present state of our knowledge of practical pyrometry by briefly tracing the history of the efforts which have been made to measure high temperatures. This paper will, therefore, be limited to the consideration of those forms of appliance which have either marked distinct stages of advance, or have remained in use with more or less modification through a considerable range of time. The earliest pyrometers were essentially thermoscopes, and although their graduation presented great difficulties, their importance as affording a means for the measurement of high temperatures has been recognized for centuries. It would be difficult to illustrate this better than by a brief record of the testimony which has from time to time been offered by those who have had to apply the heat of furnaces in research or in industry, and it is mainly for the sake of the light incidentally thrown on the progress of both that the following historical notes are offered. In the eighth century, Geber, the chemist, wrote a treatise on furnaces, and showed that he was familiar with many and varied means of applying heat; but he points to the difficulties that are met with in conducting operations at high temperatures, which he attributed to inability to measure heat, his actual words being: " sed quoniam non est res ignis, quae mensuari possit." t

Jan 1, 1894

By A. K. Mukherjee, J. E. Dorn

A modified Peierls model is Presented for the rationalization of the asymmetric plastic behavior of single crystals of bcc metals. The model assumes that the asymmetry of slip arises from a tendency toward asymnetric splitting of the a/2[111] screw dislocation. The approach differs from former theories however insofar as it assumes that the splitting is so minor ttut only the core energy is modified and that no real partial dislocations exist. As a consequence, the concepts of a line energy of a partial dislocation, interaction between partial dislocations, constriction energies, and stacking fault energies are not invoked. Instead the present analysis is based on a specialization of the Peierls mechanism which assumes an asymmetric dislocation core which is modified by the effective stress and permits cross slip. The theoretical predictions on the stress-temperature -strain rate and orientation relationship agree qualitatively with the limited experimental data that are currently available. Additional experimental work over wider ranges of conditions is suggested to provide more complete evaluation of the possible validity of this theory. RECENT experimental investigations on the low-temperature thermally activated deformation of bcc metals have confirmed the existence of several unique orientation effects. These will be described with the aid of the standard stereographic projection shown in Fig. 1. If slip were determined exclusively by crystal symmetry, the deformation characteristics would be symmetrical about X; = 0 and independent of whether the specimen were subjected to a tension or a compression stress, regardless of what combinations of slip planes might be operative. Experiments, however, reveal that neither of these symmetry based predictions are valid. A schematic representation of the commonly observed asymmetry of both the yield stress and the plane of slip is shown in Fig. 2. A reversal of the direction of stressing results in an inversion of the asvmmetric behavior. 1) Asymmetry bf Yielding. A detailed investigation on the asymmetric yielding in an Fe-2.7 pct Si alloy was repoEted by Tabka, Tikeuchi, and Furubayashi,1 Similar trends have been observed by Keh and Nakada on iron,' Stein on molybdenum,3 Bowen, Christian, and Taylor4 on columbium, Sherwood, Guiu, Kim, and pratt5 on Ta, Cb, and Mo. The degree of asymmetry not only depends on the atomic number and alloying but, in all cases that have been examined, it also increases with a decrease in the test temperature. 2) Asymmetry of the Slip Plane. Asymmetric $I-~: curves of the type shown in Fig. 2 have been found for several Fe-Si alloys6-8,1 and columbium.4 There is general agre_ement that near X: = 30 deg slip occurs by the [111](211) mode so that ?1 = 30 deg. As X; decreases it appears that [111](211) to [111](101) cross slip takes place leading to slip band traces on intermediate planes. And as xi approaches 0 deg, sharp

Jan 1, 1970

By A. U. Seybolt, J. L. Walter

The effects of the addition of 0.5 pct ThO2 (by volume) on the grain structure and texture of heavily rolled tungsten sheet were studied. Powder metallurgy ingots were rolled to sheet, 0.001 in. thick, and samples were annealed at temperatures from 1200" to 2500°C. The heating rate to the anneal temperature was varied from 3°C per min to 6500°C per min. The orientations of the largest grains were determined by X-ray diffraction. The disposition and loss of the ThO2 particles were determined by electron transmission microscopy and the activation energy for remozlal of the thorium was measured by mass spec-troscopy. Heating rates below about 800 C per min produced large, highly elongated grains. Higher heating rates produced much smaller, less elongated grains. The grain structure and texture of the slowly heated samples were identical to the structures and textures of heavily rolled tungsten foil conventionally doped with aluminum, silicon, and potassium but the recrystallization temperature was about 200°C lower. There was stringer-like dispersion of larger ThO2, particles superimposed on a uniform dispersion of fine particles. The particles increased in size and decreased in number with time at temperature. The loss of particles was accompanied by formation of grain boundary voids and surface pits. The activation energy for removal of the ThO2 was about 40 kcal per mole. THE addition of small amounts of aluminum, silicon, and potassium to tungsten has a profound effect on the grain structure of heavily rolled sheet1 or drawn wire."4 Thus, "doped" tungsten sheet, rolled to 0.001 in. and recrystallized, develops a structure consisting of large, highly elongated grains of a specific preferred orientation.' It has been shown that the elongated grain structure was caused by a dispersion of particles, identified as mullite (Al6si2O13),1,4 in strings parallel to the rolling direction in sheet or to the wire axis. Identical results were obtained for iron which was doped with glass and rolled to 99 pct reduction of thickness and recrystallized.5 Again, the glass particles were disposed in strings parallel to the rolling direction. The strings retarded boundary migration in the lateral direction but grain growth was able to proceed relatively unhindered along the direction parallel to the strings.1,5 In both the doped tungsten and the glass-doped iron, the particles were highly plastic during the high-temperature deformation. Since mullite melts at about 1800°C and the glass employed melts at about 810ºC, the particles were probably molten during the recrystallization anneals (above 1800°C for the doped tungsten and 850°C for the glass-doped iron). There are indications in the literature that particles not plastic at hot-working temperatures (up to about 1550°C for tungsten) may also impart elongated grain structures by primary recrystallization of worked alloys. Examples are dispersions of tantalum carbide in chromium,6 and ThO2 in nickel where elongation ratios of recrystallization grains of up to 20:l were obtained.7 Strings of ThO2 particles in W-ThO2 wire have been seen by Rieck.8 In view of the available evidence, it was of interest to extend the previous studies of doped tungsten and glass-doped iron to include W-ThO2 sheet materials. Of specific interest was the grain structure, preferred orientation, recrystallization temperature, and disposition of the thoria particles. EXPERIMENTAL PROCEDURE A) Material Preparation. About 380 g of blue tungsten oxide (approximate composition WO3) was wet with a sufficient amount of aqueous solution of Th(N03)4 to provide 0.5 vol pct ThO2. The wet mixture was stirred to distribute the doping material uniformly throughout the powder. Stirring was continued while the mixture was heated until it was completely dry. The dried, doped mixture was then reduced to tungsten powder by heating at 850°C for 2 hr in a stream of dry hydrogen. The doped tungsten powder was hydropressed in a rubber sack at pressures of 50,000 psi to produce an ingot approximately 2 cm diam by about 5 cm long. Next, the pressed cylinder was heated in hydrogen for 2 hr at 1350°C to render it strong enough for machining. The cylinder was machined to a square cross section of 1.6 by 1.6 cm with rounded corners. Finally, the bar was heated for 2 hr at 2150°C in hydrogen to provide a sufficiently dense mate rial to withstand the hot-rolling operation. Prior to rolling, the ingot was reduced in thickness by about 20 pct by forging at 1550°C. This served to increase the density of the material and to widen it slightly for better rolling characteristics. The forged ingot was then rolled at 1550°C to a reduction of 45 pct of thickness, following which the rolling temperature was reduced to 1300°C and the slab rolled, with several reheats, to 0.050 in. Further reduction was accomplished at 800°C in tungsten sheet packs to a total reduction of about 99.85 pct. B) Annealing Treatment and Observation of Structure. Small samples of the rolled foil were annealed in one of two ways. Some of the samples were suspended in a covered tungsten can and annealed at temperatures from 1200" to 2200°C for various times in vacuum of l0-7 to 10-6 mm Hg. The can was heated by induction and temperatures were determined by optical pyrometry

Jan 1, 1970