By R. H. Brown, F. Keller

Because of the extensive use of Alclad 24s alloy sheet in aircraft construction, there is much interest in the metallurgical changes caused by heat-treatment of this product.1, 2 One of these changes is the result of the diffusion of soluble elements from the core into the coating during treatment. This paper deals with the thermal treatments that may influence diffusion and with the practical effects of diffusion on the serviceability of the product. As is well known, Alclad 24s-T sheet has a core of high-strength alloy combined with surface layers of relatively pure aluminum. The microstructure of a cross section of this product is shown by Fig. I. Not only does the relatively high-purity coating have a high resistance to corrosion, and hence serves as a mechanical barrier between the core metal and the corroding environment, but in addition this coating exerts electrochemical protection over areas where the core may be exposed, such as cut edges. In addition, the coating affords electrochemical protection to projecting heads of A17s-T, 17s-T and 24s-T rivets, or attached members made from these alloys. Under some conditions of heat-treatment, however, diffusion of copper into the coating will alter the electrochemical relationship between the coating and the core to the extent that only partial protection will be obtained under some corrosive conditions. The reason for the electrochemical protection lies in the fact that the coating layers of pure aluminum are anodic to the alloy core. The addition of copper to aluminum produces alloys in which the potential is lower than that of the pure metal. Moreover, as the amount of copper in solid solution in 24s alloy is increased, the potential of the alloy becomes more cathodic. When heat-treated at 920°F. and quenched in cold water, 24s-T is about 0.16 volt cathodic to pure aluminum. However, copper will diffuse from the core into the coating, and if it reaches the surface the potential will be altered in a cathodic direction. Thus the potential difference between the core and coating may be less than 0.16 volt, depending uponIthe thickness of the coating, and the time and temperature of heat-treatment. Of the methods available for determining the extent of diffusion of copper from the core into the coating of Alclad 24s-T, two are generally used; namely, the metallo-graphic and the solution potential methods.3 Metallographic Methods Metallographic methods will reveal the progress of diffusion of copper into the coating. For instance, the diffusion zone in the coating intermediate between the coating surface and the core is shown in Fig. I. This photomicrograph is of a polished and etched cross section of 0.040-in. Alclad 24s-T sheet. Diffusion proceeds into the coating more rapidly along the grain boundaries than through the body of the grains. Consequently, the diffusion zone is not of uniform width

Jan 1, 1944

By F. Keller, R. H. Brown

Because of the extensive use of Alclad 24s alloy sheet in aircraft construction, there is much interest in the metallurgical changes caused by heat-treatment of this product.1, 2 One of these changes is the result of the diffusion of soluble elements from the core into the coating during treatment. This paper deals with the thermal treatments that may influence diffusion and with the practical effects of diffusion on the serviceability of the product. As is well known, Alclad 24s-T sheet has a core of high-strength alloy combined with surface layers of relatively pure aluminum. The microstructure of a cross section of this product is shown by Fig. I. Not only does the relatively high-purity coating have a high resistance to corrosion, and hence serves as a mechanical barrier between the core metal and the corroding environment, but in addition this coating exerts electrochemical protection over areas where the core may be exposed, such as cut edges. In addition, the coating affords electrochemical protection to projecting heads of A17s-T, 17s-T and 24s-T rivets, or attached members made from these alloys. Under some conditions of heat-treatment, however, diffusion of copper into the coating will alter the electrochemical relationship between the coating and the core to the extent that only partial protection will be obtained under some corrosive conditions. The reason for the electrochemical protection lies in the fact that the coating layers of pure aluminum are anodic to the alloy core. The addition of copper to aluminum produces alloys in which the potential is lower than that of the pure metal. Moreover, as the amount of copper in solid solution in 24s alloy is increased, the potential of the alloy becomes more cathodic. When heat-treated at 920°F. and quenched in cold water, 24s-T is about 0.16 volt cathodic to pure aluminum. However, copper will diffuse from the core into the coating, and if it reaches the surface the potential will be altered in a cathodic direction. Thus the potential difference between the core and coating may be less than 0.16 volt, depending uponIthe thickness of the coating, and the time and temperature of heat-treatment. Of the methods available for determining the extent of diffusion of copper from the core into the coating of Alclad 24s-T, two are generally used; namely, the metallo-graphic and the solution potential methods.3 Metallographic Methods Metallographic methods will reveal the progress of diffusion of copper into the coating. For instance, the diffusion zone in the coating intermediate between the coating surface and the core is shown in Fig. I. This photomicrograph is of a polished and etched cross section of 0.040-in. Alclad 24s-T sheet. Diffusion proceeds into the coating more rapidly along the grain boundaries than through the body of the grains. Consequently, the diffusion zone is not of uniform width

Jan 1, 1944

By E. N. Silverman

Mixtures of' MnS, ZFeO-SiO,, ZMnO.SiO, FeO, and MnO were prepared synthetically and used to study the planes ZFeO. Si0,-ZMnO.SiO,-MnS, FeO-MnO-MnS, and Fe0-MnO.Si0,-MnS in the quaternary system. Because the oxides and silicates studied flux MnS, inclusions in this system are partly liquid during rolling. Also, oxygen can modify subsurface inclusions through the reaction MnS + FeO—FeS + MnO during the soaking of ingots and the reheating of blooms and billets. NONMETALLIC inclusions in steel have long been a subject of study and conjecture because the properties of many steels are known to be affected by the the kind and amount of inclusions present. In free-machining steels, the type of inclusion present has a direct bearing on their machinability; in other steels, cleanliness is important and metallurgists direct their efforts at reducing the amount of non-metallic inclusions. Thus, the accumulation of knowledge about the formation and behavior of inclusions during all stages of steelmaking and processing should aid in improving the quality of steels and decreasing the production costs resulting from rejections. Previous studies of inclusions have contributed greatly to our understanding. The investigators have generally examined inclusions in finished steel. Boulger, Moorehead, and Garvey1 found that in Bessemer steels, low silicon contents results in globular sulfide inclusions with attendant high machin- ability ratings. Van vlack2 also found that low silicon contents favor inclusion morphology that contributes to high machinability ratings. Boquist and Stoll* found that silicon content affected sulfide inclusions and machinability of blooms, billets and bars more than did the finishing temperature in the range between 1775° and 2075°F. Carney and Rudolphy3 studied the distribution of sulfur, manganese, silicon, and carbon in a commercial ingot of resulfur-ized steel and found that silicon was concentrated near the bottom. This helped to explain why bottom cuts had poorer machinability. Klinger and Koch4 developed techniques for extracting inclusions from steel, and the technique devised by Gurry, Chris-takos, and stricker5 for extracting carbides can also be adapted to the study of inclusions. A different approach to the study of inclusions in steel consists of synthesizing the constituents that form inclusions and determining the phase eauilibria in the system that contains the constituents. The resulting phase diagrams can then be used to determine the effect of the various constituents upon each other. In this way, it becomes possible to under-

Jan 1, 1962

By B. M. Larsen, T. E. Brower

THIS discussion is based on statistical manipulation and evaluation of operating data from several commercial blast furnaces which include rather wide variations in practice. We are concerned here mainly with the effect of manganese on sulphur elimination under operating conditions in commercial blast furnaces, but this effect can be outlined more clearly by including certain other variables such as silicon in iron and slag basicity, which are all in part interrelated. Real progress in understanding all of the smelting-zone reactions in this process requires more laboratory studies of slag-metal melts similar to those in the blast furnace, with careful control of oxygen pressure. Such experimental work is very difficult, however, and in the meantime, with the present scarcity of more fundamental data, such statistical trends and correlations as can be obtained from commercial furnace operating records may help in choosing laboratory test conditions as well as adding to our knowledge of operating procedures. We do not know just why the furnace data are apparently so irregular that statistical treatment of large numbers is needed to obtain accurate trends. It is partly caused, no doubt, by the many simultaneous variables present, but there are perhaps also such factors as: (I) the con- tinual swings up and down so characteristic of the process; (2) difficulty of accurate sampling of co-existing phases, as well as (3) the presence of both equilibrium and rate factors as a result of the fast driving of the process. In desulphurization, for example, the flow of thin layers of slag and metal over solid coke surfaces, plus the contact between droplets of iron falling through the slag layer in the hearth, would lead one to expect a close approach to equilibrium. On the other hand, most of the critical part of sulphur removal may occur in a short time and distance below the tuyeres with perhaps an accompanying decrease in oxygen pressure and the concurrent reduction of much of the silicon and manganese, so its degree of approach to equilibrium may be quite variable. Probable Chemistry of Desulphurization Since there is little evidence that sulphur atoms in the iron solution are aasociated to any appreciable extent in molecules such as MnS, the transfer from slag to metal and back again can be written:* (FeS) ? [FeS], [I] hence the following reactions seem most probable in the slag phase, (FeS) + (CaO) ? (CaS) + (FeO), [2] and, (FeS) + (MnO) ? (MnS) + (FeO). 131

Jan 1, 1949

By B. M. Larsen, T. E. Brower

THIS discussion is based on statistical manipulation and evaluation of operating data from several commercial blast furnaces which include rather wide variations in practice. We are concerned here mainly with the effect of manganese on sulphur elimination under operating conditions in commercial blast furnaces, but this effect can be outlined more clearly by including certain other variables such as silicon in iron and slag basicity, which are all in part interrelated. Real progress in understanding all of the smelting-zone reactions in this process requires more laboratory studies of slag-metal melts similar to those in the blast furnace, with careful control of oxygen pressure. Such experimental work is very difficult, however, and in the meantime, with the present scarcity of more fundamental data, such statistical trends and correlations as can be obtained from commercial furnace operating records may help in choosing laboratory test conditions as well as adding to our knowledge of operating procedures. We do not know just why the furnace data are apparently so irregular that statistical treatment of large numbers is needed to obtain accurate trends. It is partly caused, no doubt, by the many simultaneous variables present, but there are perhaps also such factors as: (I) the con- tinual swings up and down so characteristic of the process; (2) difficulty of accurate sampling of co-existing phases, as well as (3) the presence of both equilibrium and rate factors as a result of the fast driving of the process. In desulphurization, for example, the flow of thin layers of slag and metal over solid coke surfaces, plus the contact between droplets of iron falling through the slag layer in the hearth, would lead one to expect a close approach to equilibrium. On the other hand, most of the critical part of sulphur removal may occur in a short time and distance below the tuyeres with perhaps an accompanying decrease in oxygen pressure and the concurrent reduction of much of the silicon and manganese, so its degree of approach to equilibrium may be quite variable. Probable Chemistry of Desulphurization Since there is little evidence that sulphur atoms in the iron solution are aasociated to any appreciable extent in molecules such as MnS, the transfer from slag to metal and back again can be written:* (FeS) ? [FeS], [I] hence the following reactions seem most probable in the slag phase, (FeS) + (CaO) ? (CaS) + (FeO), [2] and, (FeS) + (MnO) ? (MnS) + (FeO). 131

Jan 1, 1949

THE following employment items are made available to AIME members on a nonprofit basis by the Engineering Societies Personnel Service, Inc., operating in cooperation with the Four Founder Societies. Local offices of the Personnel Service are at 8 W. 40th St., New York 18; 100 Farnsworth Ave., Detroit; 57 Post St., Son Francisco; 84 E. Randolph St., Chicago 1. Applicants should address all mail to the proper key numbers in care of the New York office and include 6c in stomps for forwarding and returning application. The applicant agrees, if placed in a position by means of the Service, to pay the placement fee listed by the Service. AIME members may secure a weekly bulletin of positions available for $3.50 a quarter, $12 a year. MEN AVAILABLE Sales Engineer, 37, seven years experience Europe and Latin America both in underground work and administrative and sales work; speaks fluent Spanish, Portuguese, French. Desires responsible position preferably export in U. S. M-692. Superintendent, 46, married. Experience covers mining and metallurgy as mining engineer and as general superintendent; metallurgy of leaching, flotation, cyanidation; development, construction, operation. Presently available. Prefer U.S.A. M-693-333-E-1-San Francisco. Mine Manager, Superintendent, Consultant, 61, married. Design and erection of mining and mill plants-examinations. Many years as superintendent, manager, consultant, designer and builder of mining plants, flotation mills, concentration mills. Available one month's notice. Prefer U. S. but foreign acceptable if good climate. M-695-4211-E-9-San Francisco.

Jan 1, 1952

A Discussion of the papers of James Gayley, on "The Application of Dry-Air Blast to the Manufacture of Iron" (see Trans., XXXV., 746, 1022, also pp. 315 and 745 of the present volume, and of J. E. Johnson, Jr., on "The Physical Action of the Blast-Furnace," p. 454. Chas. B. Dudley, Altoona, Pa.:—I am not a blast-furnace man, and this always puts me at a disadvantage because I cannot go into the details of the making of iron and steel. I have not the experience, and have to take the statements of other people, so what I say regarding the subject of this paper is not in the sense of an expert. When I first heard of Mr. Gayley's experiments, I said to myself, a I fear they will result in failure, since, apparently, Mr. Gayley has forgotten one chemical fact, namely, that carbon does not combine with oxygen in the absence of mater-vapor." This fact which was so astonishing when it was first brought out some years ago, and which those who are interested may find in the Journal of the Chemical Society of London, for 1885, page 349, and 1894, page 611, led me to think that the drying of the air would be a mistake. The general subject of the influence of water-vapor on chemical action is a large one; but the special point in which we are, for the moment, interested, namely, the influence of water-vapor on the combustion of carbon, was especially treated by Mr. H. B. Baker, in the papers referred to. Apparently, however, as the result of Mr. Gayley's experiments, we are to learn that the amount of moisture still left in the desiccated air is sufficient to secure perfectly satisfactory combustion. In thinking over Mr. Gayley's paper, it occurred to me that there were two alternatives, either of which might be chosen, namely, we might dry the air as Mr. Gayley does, or possibly we might, in a very much easier way, simply saturate the air at a constant temperature, and thus get uniform working and

Jan 1, 1906

By B. M. Larsen, T. E. Brower

INTRODUCTION THIS discussion is based on statistical manipulation and evaluation of operating data from several commercial blast furnaces which include rather wide variations in practice. We are concerned here mainly with the effect of manganese on sulphur elimination under operating conditions in commercial blast furnaces, but this effect can be outlined more clearly by including certain other variables such as silicon in iron and slag basicity, which are all in part interrelated. Real progress in understanding all of the smelting-zone reactions in this process requires more laboratory studies of slagmetal melts similar to those in the blast furnace, with careful control of oxygen pressure. Such experimental work is very difficult, however, and in the meantime, with the present scarcity of more fundamental data, such statistical trends and correlations as can be obtained from commercial furnace operating records may help in choosing laboratory test conditions as well as adding to our knowledge of operating procedures. We do not know just why the furnace data are apparently so irregular that statistical treatment of large numbers is needed to obtain accurate trends. It is .partly caused, no doubt, by the many simultaneous variables present, but there are perhaps also such factors as: (I) the continual swings up and down so characteristic of the process; (2) difficulty of accurate sampling of co-existing phases, as well as (3) the presence of both equilibrium and rate factors as a result of the fast driving of the process, In desulphurization, for example, the flow of thin layers of slag and metal over solid coke surfaces, plus the contact between droplets of iron falling through the slag layer in the hearth, would lead one to expect a close approach to equilibrium, On the other hand, most of the critical part of sulphur removal may occur in a short time and distance below the tuyeres with perhaps an accompanying decrease in oxygen pressure and the concurrent reduction of much of the silicon and manganese, so its degree of approach to equilibrium may be quite variable. PROBABLE CHEMISTRY OF DESULPHURIZATION Since there is little evidence that sulphur atoms in the iron solution are associated to any appreciable extent in molecules such as MnS, the transfer from slag to metal and back again can be written:* [(FeS) -, [FeS],[I] hence the following reactions seem most probable in the slag phase, (FeS) + (CaO) = (CaS) + (FeO), [2] and, (FeS) + (MnO) ;:2 (MnS) + (FeO). [31]

Jan 1, 1948

By R. M. S. B. Horta, W. T. Roberts, D. V. Wilson

Evaluation of results obtained by the Harris method for inverse pole figures is discussed. Two existing analyses and a new approach are compared. In the most frequently used analysis, different reflections are accorded equal weight. A second method involves area-weighting of reflections, mainly to take account of nonuniformity of Pole distribution. In the new method, reflections are weighted according to their multiplicity factors. Intensity ratios obtained from a sample of steel sheet by the three methods are compared. INVERSE pole figures offer a convenient method of depicting the proportions of material with various orientations referred to a unique specimen axis. The technique was first applied to fiber textures, but it is now frequently used as a description of texture in sheet metal, the unique axis in this case usually being the sheet normal. The Harris method' for the determination of inverse pole figures has the great merit of simplicity. It suffers certain intrinsic limitations, but provided that these are borne in mind, the results allow useful conclusions to be drawn regarding the effects of texture components on certain mechanical properties. Much thought has been given to alternative methods of texture description, aimed at eliminating the ambiguity in the simpler methods.2"6 Refinements in the method of description are obtained at the price of increasing complexity, and it seems clear that a simple method, such as that of Harris, will continue to find application. The original derivation by Harris1 has been corrected by Morris7 and later by Mueller, Chernock, and Beck.2 Since the latter reference is more accessible, it is referred to more frequently than the work of Morris. Most users of the inverse pole figure method present their results on the basis of the treatment by Mueller et al., and it is the purpose of the present communication to comment on this treatment and to suggest a simple modification to the method of presentation which enhances the meaningfulness of the results. It will be convenient first to summarize the Mueller analysis as follows: The intensity Ihkl of a hkl reflection from a textured specimen is: Ihkl=CI0AL\Fhkl\2NhklPhkl [1] where C is a constant for a given sample I, is the intensity of the incident beam A is an absorption factor. With usual diffrac-tometer geometry and a flat specimen, A is inversely proportional to the density of the specimen. L is the Lorenz polarization factor Fhkl is the structure factor for the hkl reflection Nhkl is the multiplicity factor phkl is the fraction of crystals in the polycrystal-line aggregate with any particular (nkl) plane parallel to the surface. The corresponding equation for a specimen with randomly oriented grains is lR,hkl=CRl°ARL\fnkl\2Nnklk [2] the subscripts R indicating the factors that are different for the random sample, which will, in general, have a density different from that of the textured one. The intensity ratio is hkl , c A Phkl [3] IR,hkl CR AR PR The constants are eliminated by summing over all the measured reflections ^iRMi °R AR PR ljPkkl and from Eqs. [3] and [4] T IR,hkl The only unknown in Eq. [5] is Yj phkl and before this can be evaluated, it is necessary to adopt some form of normalizing procedure. Mueller et al. assume that when a large number, n, of reflections is used, the average value of p as defined by Eq. [6] below will be unity ? = £j**l3l [6] and the final result of their analysis follows: hkl Pkkl = i I&Jf~ [7] ±y* Ihkl ^ in,hki The normalizing procedure used by Mueller et al. involves an unrealistic assumption since it gives equal weight to each of the hkl reflections. Other normalizing procedures can now be examined with a view to selecting a more appropriate one. For an infinite number of reflections, the function p can be averaged over a continuous range of orientations covering the complete solid angle 4p by the integral relation: p =1 jp(a)dQ = l [8] This is the only exact procedure, but in practice a

Jan 1, 1970

By R. E. Grace

WHEN an Fe-C alloy, partially reacted to pearl-ite, is quenched rapidly enough to suddenly stop the growth process, it may be expected that any carbon concentration gradients will freeze in situ in the newly formed martensite. A short tempering treatment should precipitate finely dispersed iron carbide particles in approximately the same distribution in which carbon existed during the growth process. Examination with the electron microscope of areas of tempered martensite adjacent to the pearlite-martensite interface should reveal the existence of preferred areas of precipitation. Fig. 1 is an example of an electron micrograph used in this study. Small sections of a commercial steel (0.9 pct C, 1.6 pct Mn, 0.25 pct Si) were austenitized at 945°C in air for 45 min, furnace-cooled to 697°C, iso-thermally reacted to pearlite for 30 min, and quenched into iced brine. Two samples were tempered 5 and 20 min, respectively, in air at 498°C and were subsequently quenched in water. The samples were mechanically polished and etched in 1 pct picral. Collodion replicas were made by the conventional technique; these were shadowed with chromium at about 650' from the horizontal, and electron micrographs were taken at a linear magnification of 14,200X. Prints were made at a magnification of 44,100X. Lineal analysis of the prints was made as a function of the interlamellar spacing and volume percent of iron carbide. Straight lines were drawn into tempered martensite between adjacent lamellae at a distance S/4 or S/6 apart, where S is defined as the interlamellar spacing measured at the pearlite-martensite interface. The volume percent of iron carbide was measured along each of these traces with a "gage length" of S/10. The results of analyses of two samples are shown in Table I. The area included between the S/2 and S distance from the interface could be considered homogeneous within the sensitivity of the measuring technique. This value was used as a proportionality factor to evaluate an arbitrary carbon content of homogeneous austenite, and also as a parameter by which error in measurements could be evaluated. Results of the lineal analysis are shown in Figs. 2 and 3. Fig. 4 shows the statistical nature of the interlamellar spacing for all lamellae measured in this

Jan 1, 1954

By Homer F. Staley, C. P. Karr

The casting alloy 88 copper, 10 tin, 2 zinc, commonly known in England as Admiralty metal and in this country as Government bronze, gun metal, or Naval Department composition G, has, at its best, many valuable properties. However, its physical properties are known to vary widely with slight changes in method of manufacture of the castings, such as slight variations in composition, variation in pouring temperature, kind of mold used, method of pouring and gating of molds, size and shape of castings, amount and kind of heat treatment, and so forth.' The microstructure of castings made from this alloy is influenced by slight variations of composition, rate of cooling, and kind and length of heat treatment. This is best understood by reference to the equilibrium diagram. The part of the diagram in which we are interested and the effect of the thermal equilibrium relations on the physical properties of the alloy 88 copper, 10 tin, 2 zinc, have been discussed by Hoyt, Campbell, Primrose, and Rawdon.2 In Fig. 1 is given the equilibrium diagram of the copper-tin alloys. Briefly stated, the relations of composition and temperature changes are as follows. Compositions between A and a consist of but one constit ent—the a bronze, which is a solid solution of copper and tin, rich in copper. On cooling from the molten state these compositions gradually crystallize, at temperatures above 790°, into a mass of interwoven treelike crystals or dendrites. The cores of the dendrites are rich in copper and the percentage of tin gradually increases as the surfaces are approached. AS cooling progresses, after a11 the metal has crystallized, no further changes occur in the crystals other than diffusion within the crystals, which tends to erase the dendritic pattern and to render the structure more homogeneous. * Metallurgical Ceramist, U. S. Bureau of Standards, Associate Physicist, U. 8. Bureau of Standards. A. D. Flinn: Iron. Age (1915) 96, 1292-3. C. P. Karr: U. S. Bureau of Standards Tech. Paper 59, Pt. 1. S. L. Hoyt: Enging. (1913) 96, 667-7, 704-5. William Campbell: Trans. Am. Inst. Met. (1912) 6, 158-172. H. S. Primrose: Metal Ind. (1916) 14, 202-4. H. S. Rawdon: U. S. Bureau of Standards Tech. Paper 59, Pt. 11.

Jan 1, 1921

By David B. Reger

Sharp declines of initial production of both oil and gas occurred in West Virginia during 1943. There was only a small decrease in the number of ncw wells, but these wells did not show the quantities of oil and gas that might have been expected. The same situation prevailed both as to routine drilling in old pools and as to exploratory wildcat wells. Out of 42 wildcats drilled, 19 resulted in small commercial gas wells, and 2 in small commercial oil. No new oil pools were discovered, but the proved limits of several old pools were considerably extended, giving 4200 acres of newly proved oil territory. Three new gas pools, resulting from discoveries made in 1942 and former years, came into definite activity. The newly proved gas territory in these and in various extensions of old pools is 39,000 acres or more. It is doubtful whether the newly proved reserves of either oil or gas will balance current withdrawals. The account of operations, as gathered from trade journals and other reporting services, shows that 696 new wells were drilled, resulting in 82 oil wells with 919 bbl. of daily new production; 475 gas wells with 454,735,000 cu. ft. of daily open flow, and 137 dry holes. Also, 57 old wells were drilled to deeper sands, with 3 bbl. and 11,484,000 cu. it. of added production. On the new wells, the oil average was 11.2 bbl. per well per day, and the gas average was 957,337 cu. ft. per well per day. On new wells the ratio of dry holes to completions was 19.68 per cent. On deeper drilling the ratio of failures was 14.03 per cent. The greatly decreased average initial gas-well production in 1943, as compared with 2,270,406 CU. ft. per well in 1942, is directly attributable to the abrupt decline of completions in the Charleston gas field, which reached its peak in 1942. Production of oil for the year was estimated by the U. S. Rureau of Mines as 3,349,000 bbl., as compared with 3,574,000 bbl. in 1942. Production of natural gas for the year is estimated by the author as 210,000, 000,000 cu. ft., compared with the U. S. Bureau of Mines final figures of 215,193,-000,000 cu. ft.* in 1942.

Jan 1, 1944

By David B. Reger

Sharp declines of initial production of both oil and gas occurred in West Virginia during 1943. There was only a small decrease in the number of ncw wells, but these wells did not show the quantities of oil and gas that might have been expected. The same situation prevailed both as to routine drilling in old pools and as to exploratory wildcat wells. Out of 42 wildcats drilled, 19 resulted in small commercial gas wells, and 2 in small commercial oil. No new oil pools were discovered, but the proved limits of several old pools were considerably extended, giving 4200 acres of newly proved oil territory. Three new gas pools, resulting from discoveries made in 1942 and former years, came into definite activity. The newly proved gas territory in these and in various extensions of old pools is 39,000 acres or more. It is doubtful whether the newly proved reserves of either oil or gas will balance current withdrawals. The account of operations, as gathered from trade journals and other reporting services, shows that 696 new wells were drilled, resulting in 82 oil wells with 919 bbl. of daily new production; 475 gas wells with 454,735,000 cu. ft. of daily open flow, and 137 dry holes. Also, 57 old wells were drilled to deeper sands, with 3 bbl. and 11,484,000 cu. it. of added production. On the new wells, the oil average was 11.2 bbl. per well per day, and the gas average was 957,337 cu. ft. per well per day. On new wells the ratio of dry holes to completions was 19.68 per cent. On deeper drilling the ratio of failures was 14.03 per cent. The greatly decreased average initial gas-well production in 1943, as compared with 2,270,406 CU. ft. per well in 1942, is directly attributable to the abrupt decline of completions in the Charleston gas field, which reached its peak in 1942. Production of oil for the year was estimated by the U. S. Rureau of Mines as 3,349,000 bbl., as compared with 3,574,000 bbl. in 1942. Production of natural gas for the year is estimated by the author as 210,000, 000,000 cu. ft., compared with the U. S. Bureau of Mines final figures of 215,193,-000,000 cu. ft.* in 1942.

Jan 1, 1944

By R. W. Bartlett

Hydrometallurgical processes for copper flotation concentrates avoid the SO2 emission problems associated with smelting, but they require oxidation of copper to obtain solubilization during leaching. The resulting copper ions must be reduced to metal, which normally requires large amounts of energy or energy equivalent reagents such as hydrogen or iron. The conventional reduction method is electrowinning which is labor intensive and involves 35 to 40% of both the entire operating and capital cost of the better hydrometallurgical processes. There is considerable incentive to reduce the cost and energy required for producing copper ions from solution. Furthermore, it is thermodynamically possible to do this using sulfur contained in the concentrate itself. In fact, the thermodynamic potential of oxidizing sulfur from S+4 to the S+6 state is greater than required to reduce cupric ion to metallic copper.1 Realization of this potential in a practical process would significantly reduce the cost of hydrometallurgical processing of sulfide concentrates because sulfur would become a cost-free reducing agent. An apparently practical method is to use SO: and HSO3 ions, obtained by ammonia scrubbing of SO2 from a concentrate roaster gas, to reduce leached copper to metal in an autoclave. This reduction step is the Jumau 1907 A series of steps, including sulfite reduction, constituting a crude flowsheet was suggested by Parker in 1976.3 The present paper describes a detailed complete. sulfite process flowsheet based on materials and energy balances, discusses the chemistry, and discusses further work that is required to develop this process. Process materials, utilities costs, and energy requirements are projected to be unusually low because of the utilization of sulfur from the concentrate. Process Description The sulfite reduction process requires a copper concentrate containing approximately as much sulfur on a weight basis as copper. For those few concentrates that are deficient in sulfur, additional sulfur can generally be obtained by allowing more pyrite to float in the concentration process. The process steps, shown in [Fig. 1], are (1) a fluid bed roast of the concentrate, (2) a leach of the roaster calcine using recycled barren liquor from the reduction autoclave, (3) scrubbing of the SO2 gas with ammonium sulfite liquor to produce ammonium bisulfite, (4) reduction and precipitation of copper in an autoclave by combining part of the SO2 scrubber effluent (SO5

Jan 1, 1980

By E. A. Gulbransen, K. F. Andrew

Weight loss measurements were made using a sensitive microbalance operating in a high vacuum system. The Langmuir equation was used to Calculate the vapor pressures of the several metals and alloys. Aluminum lowered the vapor pressure of i9,on in a 5.4 Al-94.6 Fe alloy, and of iron and chromium in a 4.8 Al-21.5 Cr-73.7 Fe alloy. The influence of oxide films formed on the alloys on the effective vapor pressures of the alloys was also studied. These studies were used to aid in the inte9,pretation of the high temperature oxidation of alloys based on iron, chromium, and aluminum. RECENT studies on the oxidation of chromium1 and the heat resistant alloy 5 Al-22 Cr-73 Fe showed transitions in the rate of oxidation at 900o and 1050oC respectively. The transition for chromium occurred at a temperature where the rate of evaporation of chromium from oxide-free surfaces equalled the rate of chromium atoms reacting with oxygen. This paper presents new vapor pressure studies on iron, chromium, and the specially prepared alloys 5.4 Al-94.6 Fe, 21.9 Cr-78.1 Fe, and 4.8 Al-21.5 Cr-73.7 Fe. The ternary alloy is similar in basic composition to the patented heat-resistant commercial alloy known as Kanthal. The binary alloys were studied to show the individual effects of aluminum on the vapor pressure of iron and of iron on the vapor pressure of chromium. The purpose of the proposed studies was to test the influence of metal volatility on the oxidation behavior of heat-resistant alloys based on iron, chromium, and aluminum. Since oxide films formed on the metal may limit metal transfer to the surface, the influence of oxide films on metal volatility was also studied. LITERATURE A) Vapor Pressure. The vapor pressure of iron has been studied by Jones, Langmuir, and Mackay,' Dornte and Nrton. Edwards. Johnston. and Ditmar. and McCabe, Hudson, and Paton. Stull and SinkeT have calculated a heat of sublimation at 298° K of 99.83 kcalper g atom. The vapor pressure of chromium has been reported by Bauer and Brunner,' Speiser, Johnston, and Blakburn, Gulbransen and Andrew,'' Vintaikin,o McCabe, Hudson, and Paton, and Kubaschewski and Heymer.12 Good agreement was obtained except for the early work of Bauer and Brunner.' Stull and Sinke7 calculate a heat of sublimation at 298°K of 95.0 kcal per g atom. Vapor pressure measurements on aluminum have been made by Brewer and Searcy,13 Bauer and Brunner,aand Farkas.I4 Stull and Sinke,7 giving Brewer and Seary's' data the most weight, derive a heat of sublimation of 77.5 kcal per g atom at 298 oK. B) Method. Two methods15 are used for measuring the vapor pressure of metals: 1) The Langhuir free evaporation method, and 2) the Knudsen effusion method, In the Langmuir method, used in the present work, the vapor pressure of the metal P is given by the equation: Here M is the molecular weight of the vapor species. T is the absolute temperature. (dw/dt) is the rate of sublimation in g per sq cm per sec and a is the condensation coefficient. a is a measure of the efficiency of condensation of molecules striking the metal surface from the vapor. If condensation results from each collision a is unity. This coefficient has been found to be unity,a, le for metals. These results establish the general validity of the Langmuir free evaporation method as applied to metals. EXPERIMENTAL A) Vacuum Microbalance Method. A modification of the Langmuir free evaporation method was used. Strip specimens were suspended from a sensitive microbalance operating inside of a high vacuum system. For alloys, microbalance methods17 must be used on large area samples at relatively low temperatures to minimize composition changes. The

Jan 1, 1962

By P. K. Koh

With identical annealing heal treatment the development of major annealed texture component seems to depend primarily upon the degree of cold reduction. Cube texture was evident on annealing- 1/2-, 1,/4- , and 1/8-mil tapes at 760°C, but it dissap-)eared on 927°C annealing of 1/8-mil tape cold reduced 96.9 pct. Some cube texturee remained as tile strongest 927 °C annealed texture component in 1/4- and 1/2-mil tapes cold reduced 93.8 and 87.5 pet, respectively. The switching coefficient increases and the squareness ratio of the hysteresis loop decreases proportionally with increasing cube pole concentration. PREVIOUS studies 1,2 on the 1/8-mil ultra-thin molybdenum permalloy tape established cold rolled and annealed textures and their magnetic performance for switch-core and coincident-current memory applications, The major cold-rolled texture was found to be of {110}<335> which is quite similar to the cold-rolled texture of silver and 70-30 cartridge brass. The major annealed texture components were found to be of {120)-- <001> and {113)<785>. Although the direction for easy magnetization for this type of alloy by the single-crystal technique is not avaliable, knowledge from related studies indicated [Ill] as the easy magnetization direction, similar to that of nickel.&apos; Therefore, a cube orientation, if present in the tape core, would be most detrimental to its magnetic performance.3 In its cold-rolled state the tape had < 111 > directions in the rolling plane 14.5 deg from the rolling direction.&apos; But the coercive force of the tape in such condition will be excessive due to large amounts of internal stresses, and therefore makes its use impossible for memory applications due to long switching time. In lower nickel alloys, suchas 50-50 nickel-iron and 65 pct Ni-Fe sheets, previous investigators4"7 found the presence of cube texture on annealing at 900° to 1000°C. Although no cube texture was found in annealed 1/8-mil tape,"&apos; its presence in some annealed 1,/4-mil tape cores was firmly established a year ago as verified by significant differences in magnetic properties. The present investigation is devoted to the orientation study and related magnetic measurements on three thicknesses of the ultra-thin tape, namely, 1/8 mil, 1/4 mil, and 1/2 mil, cold rolled directly from annealed 4-mil stock in the cold-rolled state as well as after they were annealed at 760°C (1400° F) and 927°C (1700°F). The results obtained might serve to elucidate the development of annealed texture as well as to establish clearly the importance of preferred orientation on the magnetic performance of such memory tape core despite its well-known low magnetic anisotropy exchange energy. EXPERIMENTAL PROCEDURE Samples were taken from one production heat (0.010 wt pct C, 0.004 P. 0.016 S, 0.80 Mn. 0.29 Si. 79.69 Ni. 4.42 Mo. 0.054 Co, 0.002 Ti, 0.12 Al, 0.04 Mg, 14.56 Fe). Annealed 4-mil sheets were cold re-

Jan 1, 1962

By B. A. Cheadle, K. P. Steward

Axial tensile, ring tensile, closed end burst, and free end burst tests were done at room tempe.vature and 300°C on three batches of Zircaloy-2 sheathing zuith different textures. Knoop hardness tests were also done on all batches. The mechanical properties of the tubes were largely dependent on the percentages of cold work, but were also markedly affected by the textures, particularly with respect to deformation behavio&apos;r. The deformation behavior observed confirmed Picklesimer&apos;s predictions, zuhereas Knoop hardness results could be correlated with texture and yield strength anisotropy after the ,method of Wheeler and Ireland. From the mechanical properties, and from efjectiue strain values deterrlzined at the fractures using a photoqid technique, it zuas concluded that tubing witlz a single preferred orientation of radial basal poles best combines strength and ductility for any given deqee of cold work. THE mechanical properties required in collapsible Zircaloy-2 fuel sheathing for water-cooled power reactors are strength to resist wrinkling deformation by coolant pressure and ductility to accommodate a small amount of deformation in service without rupturing. Zircaloy-2 tubing during fabrication develops pre- ferred orientations of the a Zr grains due to aniso-tropic deformation behavior, and these textures markedly affect mechanical properties. Picklesimer&apos; had predicted the deformation behavior of tubes with various textures, but the texture required to provide the optimum strength and ductility for a given degree of cold work has not been reported. To investigate this problem, tests at three transverse to axial stress ratios were done at room temperature and 300°C on three batches of Zircaloy-2 tubing covering a wide range of textures and percentages of residual cold work. Knoop hardness values were also measured to correlate with preferred orientation and yield strength anisotropy after the method of Wheeler and relland.&apos; 1) MATERIAL For this investigation, three batches of tube-reduced tubing were chosen from the Zircaloy-2 sheathing produced for the Douglas Point Reactor. Individual tubes were 191/2 in. long, 0.600 in. OD, and 0.0165 in. nominal wall thickness. The identities of the batches, together with their textures, are shown in Table I. The tubes had the normal Zircaloy-2 composition3 of 1.5 wt pct Sn, 0.3 wt pct Fe, Ni, Cr combined with the following oxygen concentrations: Batch VII 1140 to 1390 ppm 0 Batch VIII 1400 to 1750 ppm 0 Batch IX 880 to 1320 ppm 0

Jan 1, 1968

By T. K. Perkins, R. N. Hoffman, O. C. Johnston

A simplified theory of viscous fingering in miscible systems has been developed. It predicts the correct functional relationship between pertinent variables and permits the calculation of the order of magnitude of fingering behavior for simple systems, such as linear or radial. The theory is based on the following four observations: (1) cross-flow takes place only near the ends of fingers; (2) the relative finger width is about 0.5; (3) fingers can be suppressed by transverse dispersion, the suppression being quantitatively described by a critical ratio of dispersion times; and (4) the widths of extending fingers are close to the minimum size finger that can grow at any stage of displacement. Fingering is studied in two-dimensional linear and diverging radial systems, both theoretically and experimentally. For linear systems, the length of the fingered region is proportional to mean displacement; the finger width is proportional to square root of mean displacement; and there is a small initial region void of fingers because of suppression by longitudinal dispersion. For the radial system, two limiting conditions are recognized. If the mean displacement is small compared with the wellbore radius, the length of the fingered region is proportional to the mean displacement. The width is proportional to the square root of mean displacement. If the mean displacement is large compared with wellbore radius, length of the fingered region is proportional to mean displacement, but the number of fingers approaches a constant value. Also, in the radial case there is a small initial region void of fingers because of longitudinal dispersion. INTRODUCTION The behavior of viscous fingers in miscible systems has been of interest to the oil industry for many years. Previous studies have clearly shown the existence and nature of fingers in small models.1,2,3,4 Engineering techniques for extrapolating to reservoir situations have been proposed. 5,6 Still, because of the lack of a real understanding of the mechanics of fingering, there remains uncertainty and disagreement as to the best way to scale or calculate fingering behavior in the reservoir. In this paper we discuss a study of the mechanics of fingering in miscible systems (i.e., why do fingers behave as they do?). A simplified theory is developed which we believe will (1) predict the correct functional relationship between pertinent variables, (2) permit us to calculate the order of magnitude of fingering behavior for simple systems such as linear and radial, and (3) give further insight into the problem of scaling or otherwise extending the results to more complicated reservoir conditions. The paper includes the following sections: (1) brief summary of the mixing behavior of miscible fluids in linear and radial systems; (2) four fundamental observations of fluid flow (under fingering conditions); (3) based on these four observations, a simplified theory of fingering in linear and radial systems is developed; and (4) the theoretical equations are compared with experimental fingering data measured in laboratory models. A REVIEW OF DIFFUSION AND DISPERSION As will be shown later, the behavior of viscous fingers in miscible systems is controlled in large degree by the mixing between the two fluids. A quantitative description of fingers will first require a quantitative description of mixing. Fortunately, much work has been done to clarify this subject; a fairly comprehensive review has been presented in a previous paper. 7 For present purposes let us (1) briefly summarize the quantitative description of diffusion and dispersion (both longitudinal and transverse) within a differential element; (2) present a simplification of the "width of mixed zone"; and (3) describe the effect of geometry on width of mixed zone. If one fluid is displaced from a porous medium by another miscible fluid (in the absence of fingers)

Jan 1, 1966

By M. Earl Volin, M. Adnan Goksel

The hydro thermal agglomerating process described (U.S. Pat. No. 3,235,371, 1966)* is different from the cotzventional high-temperature processes. Green pellets or briquettes made with mixtures of moist iron-ore concen- trates and burned or hydrated lime fines are hardened in an azttoclave at 198°C and under steam pressure for 112 to 5 hr, with or without previous drying. Under the neutral conditiotzs, oxidation of magnetite does not occur as in the conventional processes. The resulting azzlomerates-- are hard and resistant to abrasion and weathering, and they do not disintegrate in the Under test. The equipment required for the process is not complicated, and favorable operating costs are projected because of the low temperamre and efficient heat recuperation. A low capital investment makes the process attractive even when the annual pellet production is below a million tons.

Jan 1, 1970

Although copper production established a new record, lead and zinc registered gains, and iron production held steady, the mixed trend in metallic and nonmetallic mining and generally lower prices in 1961 resulted in a net decline in the total value of domestic mineral production. According to preliminary estimates from the U.S. Bureau of Mines, the value of metals produced in this country during the year was approximately $1.9 billion, a decrease of $117 million from 1960; the value of nonmetallics was about $3.7 billion, a $14 million decrease. The following report of mining and mineral developments during 1961 is based on USBM and industry sources. Aluminum Output Dips from 1960 Record Government reports indicate that the domestic primary aluminum industry produced approximately 1,880,000 tons, equivalent to 77% of this nation&apos;s capacity. This production is about 6% below the 1960 record output of 2,014,498 tons. Shipments of primary metal ingot slightly exceeded the quantity produced.

Jan 2, 1962